By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2 versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By D. A. Meyn, R. L. Holtz, C. S. Pande, M. A. Imam, D. J. Singh

"Various theoretical and experimental techniques used to search and develop new metal hydride systems suitable for hydrogen storage are described. The main theoretical technique under study makes the use of electronic structure of the candidate materials. Microstructural characterization techniques like transmission electron microscopy are being used to study the hydride formation. Novel processing techniques for material preparation such as those needed to produce thin films or amorphous phases are also being utilized. The techniques are illustrated with results from Pd, FeTi and Mg2Ni systems.IntroductionOf the four methods of hydrogen storage, compressed gas, cryogenic liquid, metal hydrides, and gas-solid adsorption, the metal hydride storage method is more attractive from the point of view of high volumetric density and safety. Compressed gas storage has disadvantages of extreme pressure, weight, and volume requirements, whereas storage of hydrogen as cryogenic liquid is unattractive due to the requirements of extremely low temperatures and high consumption of primary energy. Moreover, the number hydrogen atoms present in a volume of 10- 22 Cm3 (nH) in liquid hydrogen state (- 20K) is 4.2 whereas number of hydrogen atoms that can be accommodated in a free volume of 10-22 cm3 of various hydrides are as follows: LiH--5.9, TiH2--9.2, ZrH2--9.2, VH2--l0.2. High hydrogen concentration is usually associated with a large H/Metal atomic ratio but is also a function of structure."

Jan 1, 1994

By Roger W. Lee

The commissioning of the prototype Imperial Smelting Furnace (ISF) in 1950 was a technological breakthrough in the pyrometallurgical smelting of zinc and provided significant advantages over the existing retort processes. However, for most zinc concentrates the electrolytic zinc process continued to be more economic. Therefore, the Imperial Smelting Process (ISP) specialised in smelting zinc and lead concentrates that were less amenable for treatment by either the electrolytic zinc process or the lead blast furnace. Subsequently, improved mineral processing techniques led to a decrease in the availability of these concentrates so the treatment of secondary materials in the ISP assumed greater importance. This was facilitated by the development of techniques such as hot briquetting and tuyere injection. In 2002 over 1 million tonnes of zinc and 400,000 tonnes of lead were produced by the ISP. However, in the 2002-3 the economics of the Process became extremely difficult because of low metal prices and increased operating costs. This resulted in the closure of four ISP smelters in 2003 and two in 2005. Nevertheless, two new ISP smelters are scheduled for commissioning in China in 2006 where local economic conditions continue to favour the process. The economics of the process are examined particularly in respect of smelter margin and operating costs. The need to increase the smelter margin means that the future of the process will be closely linked to its ability to consume secondary materials and an examination will be made of its potential for conversion to 100% secondary operation. Apart from a reduction in raw materials costs, a substantial reduction in operating costs would ensue from not operating sinter and sulphuric acid plants.

Jan 1, 2006

By KAGAN BENZESIK, Onuralp Yücel, Mehmet Bugdaycı, Ahmet Turan

ZrB2 and B4C are one of the most significant advanced ceramics. They are being used in various industrial areas from space technology to nuclear industry owing to their physical properties such as high melting point, high thermal/electrical conductivity and low density. Present study was conducted in two main stages: Self-propagating high-temperature synthesis (SHS) reactions and leaching. ZrO2, Carbon black, B2O3 were used as starting material to produce ZrB2-B4C powders by SHS. Also Mg powder was used as the reductant. The reaction mixtures (approximately 100 g) were mixed thoroughly 15 minutes in a turbula mixer and charged into Cu crucible and compacted. W (tungsten) wire was placed at the top of copper crucible and the reaction realized by passing current through the wire. After initiation, a highly exothermic reaction became in a self-sustaining mode and propagated throughout the SHS mixture. The samples were characterized by using AAS and X-Ray Diffraction.

Jan 1, 2016

By Rong Yang, Qijie Zhai, Wenbin Xia, Changjiang Song

"Tills paper focus on the influence of carbon content and cooling rate on the microstructure and phase formation of Fe-Mn-C alloys under near-rapid solidification. When manganese content is about 11wt.%, more s-martensite can be obtained with cooling rate increasing when carbon content is 0.14wt.%, the formed phase changed from a phase to y phase when 0.74wt.% carbon is added to the samples, and when carbon content up to 2.1wt.%, carbide can be obtained in the sample. A host of stacking fault, which attributes to the strain-induced martensite, can be observed in the sample. The microhardness increased with cooling rate increasing, and under the same cooling rate, the microhardness of samples with 0.14wt.% carbon is highest.IntroductionTo obtain high performance materials is eternal pursuit of material science research. Material scientists have explored many new ways to obtain high performance materials from long time ago. Rapid solidification is one of most popular ways to produce advanced materials by obtaining metastable phases, because it is widely known that the solidification of metals in metastable phases gives access to a whole range of materials with novel properties [1]. Furthermore, nowadays metastable materials have been extensively used in many fields, for example, many of our modem high performance materials such as steel products or aluminum alloys for aeronautical applications are in the form of metastable rather than stable phases [1]."

Jan 1, 2012

By Henk Dijkman

Existing metallurgical operations can be optimized by implementing engineered bioreactor systems in the process configuration. For instance, metals can be recovered safely and economically from process and waste streams using biogenic sulfide. This paper focuses upon possible applications of high rate biotechnology in metallurgy and mining. Metal recovery from liquid streams (process bleed streams, leach water, waste streams), integrated removal of (fugitive) SO2, treatment of acid blowdown and other options will be described. Practical examples are given. A large-scale application of biotechnology at Pasminco's Budel Zink refinery is described. Here, acid plant blowdown is treated together with electrolyte magnesium bleed. Concentrated zinc sulfide (10 tpd) is produced biologically, eliminating the production of gypsum and closing the refinery sulfur cycle. Recovery of metals from solution at Kovehute Pribram in the Czech Republic is the second practical example. In this case, H2S is produced on-site for metal removal from an alkaline slag dump leachate. At the Caribou mine in New Brunswick, Canada, acid mine drainage is treated with biogenic sulfide. This plant is situated upstream of a lime neutralization plant. As a result, reusable ZnS is produced, the volume of the sludge (gypsum and hydroxides) from the lime plant is reduced by 50%, the sludge is free of heavy metals and the final effluent concentration of heavy metals is in the ppb range. In the second phase of this project, metals will be recovered from stored tailings, resulting in significant revenues.

Jan 1, 2002

By Stanko Nikolic

Ferrous calcium silicate slags are potentially important for future practice in copper converting operations and processes and can be described by the ?Cu2O?-FeO-Fe2O3-CaO-SiO2 system. Despite its industrial importance the phase equilibria in this system have not been fully investigated. Characterization of this slag system is necessary to improve the design and optimization parameters of new processes, including fluxing and operating temperatures. Experimental methods have been developed to investigate the phase equilibria of these slags at copper saturation and without copper. This technique involved equilibration of samples at a fixed oxygen partial pressure, rapid quenching, and analysis of the compositions of phases using electron probe x-ray microanalysis (EPMA). Liquidus and solidus data are reported for the primary phase fields of spinel, wollastonite and tridymite at 1250oC and an oxygen partial pressure of 10-6atm. The resulting data has been used to construct liquidus isotherms in the ?FeO?-CaO-SiO2 system both in equilibrium with and without molten copper. The experimental results were compared with the predictions of a thermodynamic computer package utilizing a self consistent thermodynamic database. The predictions of the model were in good agreement with the experimental isotherms when projected onto the FeO-CaO-SiO2 section, however the copper concentrations in the liquid phase at copper saturation were lower than predicted using the current database of the model.

Jan 1, 2006

By John G. Reid

When the paper "Operations at the Greenvale Nickel Project Mine and Refinery" was delivered at the 1st International Laterite Symposium in February 1979, the Yabulu Caron plant had been operating for four years and production had just stabilized. The design had been based closely on the Caron plant at Nicaro, Cuba, built in 1944, also by Freeport. Yabulu had 10 Herreshoff ore roasters and production in 1978 was 18,682 tonne nickel as impure oxide sinter and 763 tonne cobalt in a mixed sulphide with a cobalt to nickel ratio of 1 :2.5. In the 25 years since the 1st Symposium, two more roasters have been added, but dry ore processing rate has remained relatively unchanged at 2.4M Uyr to allow a lower feed rate per roaster with associated higher recovery. The ore source has changed from the domestic Greenvale mine to imports from New Caledonia, Indonesia and the Philippines. Nickel production between 1978 and 2003 has risen by 67%, cobalt has risen by 146% and the products have changed to high purity nickel compacts and "ChemGrade" cobalt salt. The plant changes that have contributed to the increased recovery, production and product value are discussed. Keywords: Caron, Yabulu, nickel, cobalt, ammonia

Jan 1, 2004

By J. E. Sallee

An experimental study has been conducted on the level of arsenic contamination in samples of zinc oxide when the zinc oxide is contacted with gas mixtures containing As4O6(g). This contamination has been determined as a function of A4O6 saturation pressure, temperature, zinc oxide sample surface area, impurities, and oxygen level in the gas mixture. The results indicated a rather clean separation can be achieved between condensed zinc oxide and gaseous arsenic oxide as long as attention is given to temperature control, and the final zinc oxide surface area. For a 300°C operation temperature and an AqOg saturation pressure of 0.38 TORR (or 0.05% As406 by volume), the contamination level is expected to be approximately 100 ppm. This suggests that arsenical dusts can be treated in the HRD flame reactor process and a reasonable purity zinc oxideproduct produced. The results also show no evidence of zinc arsenite or zinc arsenate formation.

Jan 1, 1994

By K. C. Liddell, B. Dou

"In producing multilayer films for magnetic data storage applications, the interfacial roughness must be controlled in order to obtain high quality materials with reproducible properties. The present understanding of the effect of roughness on multilayer properties such as magnetoresistance is sketchy, particularly for electrodeposited films. In this study, quantitative atomic force microscopy was used to characterize surface morphology before and after Ni films of varying thickness were deposited on Cu cathodes. A multinuclear multilayer growth mechanism is supported by both the deposition conditions and the AFM images, and a multinuclear multilayer model gave a satisfactory fit to measurements of the density of peaks on ultrathin Ni films between 0 and 8 nm thick.Alloys consisting of alternating ferro-and paramagnetic layers have begun to replace Permalloy in the sensing elements of magnetic hard drives. The operating principle of the new read heads is giant magnetoresistance (GMR), and they are smaller and more sensitive than previous inductive heads (1). Experimental studies on sputtered multilayers have emphasized the role of layer thickness and interlayer roughness in determining the presence and size of the GMR effect (e.g., 2,3,4,5,6). However, roughness in electrodeposited multilayers has rarely been measured, even though read heads are likely to continue to be made by this process for some time to come. Cu/Ni can be considered a model system for understanding processing-microstructure-property relationships in electrodeposited multilayers and is the most widely investigated of all such systems (e.g., 7,8,9,10,11,12). Nevertheless, the roughness of the interfaces in Cu/Ni electrodeposits has not been systematically characterized by quantitative techniques, and in all studies reported so far, the total deposit thicknesses were considerably greater than the 10 nm needed for most sensor applications (1). The thinnest such films were about 50 nm (7)."

Jan 1, 1998

By D. P. Cook, M. I. Bloch, J. A. Dantzig

"In this article, we describe a combined experimental and computational program to study the filling of automotive wheels during low pressure die casting. Experiments are performed by placing thermocouples into the mold walls of a production caster for the Ford F 113 wheel to measure the temperature profiles in the die during processing, and to infer the filling pattern. Computational models are also developed using a 36° section of the wheel pattern, taken directly from CAD data files. We use these models to simulate the filling and heat transfer processes. Comparison between experimental and computational results are presented, demonstrating the viability of this procedure.IntroductionAutomotive companies are using increasing amounts of aluminum in production vehicles: While the main driving force is improved fuel economy through weight reduction, replacing steel wheels by aluminum also offers the potential for improved vehicle performance by reducing unsprung mass. For these reasons, many new vehicles are now supplied with cast aluminum alloy wheels, and the aftermarket for these wheels continues to grow.The most common production process for these wheels is low pressure die casting. The process is subject to numerous defects, including microporosity, cold shuts, cold folds, misruns and inclusions. Scrap rates at the caster of the order of 10% are not uncommon. Many wheels also have large production runs, into the hundreds of thousands of wheels per year. Thus, the cost savings from even small reductions in scrap rate have the potential to be quite significant.Most of the defects are associated with the filling and solidification processes in the mold. The molds are air cooled, and the placement and sizing of cooling passages is currently as much art as science. The ultimate goal of this project is to improve that situation, by implementing simulation procedures that enable engineering design methods to be used in die and process specification."

Jan 1, 2000

By Jose Castro

The growing demand of scrap to supply the electric arc furnace has driven to search for new alternatives of raw material. The DRI produced using self-reducing pellets has become competitive due to the potential use of a wide range of carbonaceous materials such as coal, charcoal, biomass etc. In this context, the rotary kiln process using improved technologies such as post-combustion and self-reducing burden is a promising source of high quality raw materials. This paper presents a mathematical model of the rotary kiln process designed for self-reducing pellets and post-combustion. The model is based on the transport equation of two-phase flow, energy and mass transfer. The solid material is composed of a typical self-reducing pellet. The model considers the solid phase (C, volatiles, Fe2O3, Fe3O4, FeO, Fe, H2O, SiO2, Al2O3, MgO, P2O5, K2O, Na2O, FeS, CaO and gangue) and the gas phase (N2, O2, CO, CO2, H2, H2O, SO, SO2 and SiO). For each of the above components a conservation equation is solved and the mass and energy transport is accounted. The set of differential equations are coupled by the rate equations describing the kinetics of the several reactions, which take place within the rotary kiln. All the conservation equations are solved based on the finite volume method applied for a three-dimensional cylindrical coordinate system. Simulation results are presented for global parameters such as metallization degree, productivity, gas utilization ratio and calorific value. Inner conditions such as three-dimensional gas and solid temperature patter and compositions are discussed.

Jan 1, 2006