Search Documents

By I. U. Onyenanu, C. E. Ilochonwu, E. I. Nwonye, C. O. Nwajagu

This work shows how pure silica was derived directly from rice husks ash (RHA) in different temperatures for reduction to Silicon (Si). The processes to form Si materials are usually complex, costly and energy-intensive. The silica in the ash undergoes structural transformations depending on the conditions of combustion. A high purity silica was produced at 650oC after burning the rice husk (RH) for up to 7 hours. The purity of the silica was determined by dissolving the RHA with alkali solution to form sodium silicate solution of pH 11.0. This was added to hydrochloric acid of pH 1.5 which lowered the pH of the solution to 4.0 to form silica gels. The silica gels produced were washed and dried to powder and then characterized using XRD and EDX techniques. This study was done to reduce energy waste and environmental pollution in Nigeria as silica is used to develop many materials.

Jan 1, 2015

By Alicia Esther Ares, Carlos Enrique Schvezov, Alejandra Silvina Roman, Claudia Marcela Méndez

In this paper the structure of aluminum based alloys and their corrosion behavior by using different electrochemical techniques as characterization methods are considered. Currently, it becomes imperative to know the role of the Al2Cu against the susceptibility to corrosion of these alloys. The present work aims to studying the electrochemical behavior of aluminum base alloys with the following compositions: Al-1wt.%Cu, Al-4.5wt.%Cu and Al-15wt.%Cu (with different grain structures), in 1M NaCl solutions, at room temperature. Cyclic potentiodynamic polarization tests were performed and were found that the alloys with more than 1wt.%Cu in the matrix have an unstable behavior and without tendency to reach passivity. The equivalent circuits derived from electrochemical impedance spectroscopy technique (EIS) generally showed two capacitive contributions. The susceptibility to corrosion becomes a complex function, not only of copper concentration and structure, but also with interdendritic spacings and distribution of phases in the alloys.

Jan 1, 2015

By Min Chen, Cui-huan Huang, Zhen Tian, Jian-hong Dong

"The present work studied the production of Fe-Si-Mn alloy from adjusted converter slag by thermodynamic analysis. The results showed that solubility of SiO2 in the molten slag increased with increment of temperature, and it is about 80% at 1800 ?. With increment of SiO2 content, a(MnO) and a(CaO) decreased, and a(FeO) increased to the maximum when w(SiO2) is about 30%. As a result, the reduction of the slag was in the order of Fe?Mn?P before SiO2 reduction, the reduction order was Fe?P?Mn?Si when SiO2 content in the slag was from 46.4% to 54.2%, and changed to Fe?Si?P?Mn when SiO2 content exceeded 54.2%. The mass fraction of Si in the alloy phase increases with increasing of w(SiO2) in the slag, and the mass fraction of Si in the alloy reached to 62.2% at 1800 ?.IntroductionFerroalloy production is a high energy consumption and high pollution industry[1-2]. If ferroalloy production could be produced from molten slag by addition of carbon-reducing agent, the valuable metal and oxide in the slag can be recycled, most importantly, if the high-temperature resource carried by molten slag can be made full use in the field of ferroalloy production, the power consumption of ferroalloy production could be cut down greatly.Converter steel slag is a kind of byproduct in steelmaking processing increasing rapidly with the increment of crude steel, but the utilization ratio is low. Most heat recovery research is still in the experimental stage except the heat recovery of blast furnace slag by water quenching method, at present[3-4]. It is of great significance for enterprises to energy saving and emission reduction if the molten steel slag could be utilized directly. Not only the reuse methods of liquid steel slag material can be promoted, but also the use of heat carried in the slag could be achieved. The basicity of converter slag is high and the activity of SiO2 is low so the reduction of SiO2 in the slag is little. The compositions of slag and metal phases were calculated by Factsage program on different conditions to explore the reduction of converter slag for recovery of valuable metals and an efficient new way to use the high-temperature heat combining with the current reuse and research status of converter slag. Further, the improvement of components activity in slag and the increase of Si concentration in the metal were also dicussed."

Jan 1, 2012

By Marco Pasetto

The possibility to re-use marginal materials (by-products) deriving from industrial activities in the construction of road infrastructures, as total or partial substitution of natural aggregates, successfully combines demands for economy and environmental sustainability. The paper presents the results of a laboratory study, conducted at the Experimental Road Laboratory of the University of Padova, to verify the suitability of a particular type of electric arc furnace slag to be recycled in the lithic skeleton of high-performance asphalt mixes (porous asphalt, high modulus mixes, stone mastic asphalt, nonskid surfacings) for road and airport flexible pavements. the process of transformation of iron and steel slag into a product that can be used in road building is described, along with the characterisation of the mixtures, plus an analysis of the results of a wide battery of mechanical-performance tests. This study forms part of wider theoretical ? experimental research being done at the University of Padova in order to improve knowledge of the characteristics of succedaneum materials and check their possible applications in road and airport construction.

Jan 1, 2006

By Nan Wang

Based on the commercial computational fluid dynamics software, Fluent, a three dimensional finite-volume model has been established, and the fluid flow and heat transfer in the super-wide slab mold (cross section 3250mm×150mm) of Nanjing Iron and Steel Company has been simulated. The basic feature of flow and temperature field in a super-wide mold has been analyzed, and the effects of mold width, the submergence depth of SEN, outlet angle of SEN, casting speed, superheat and cooling rate on the flow and temperature field have been investigated. The results by comparing several simulated calculations for 3250mm×150mm slab show that a more proper fluid flow and temperature field in the super-wide mold can be obtained with 15°outlet angle, 120~150mm submergence depth of SEN and 1.2~1.4m/min casting speed. The results through numerical simulation provide a theoretical basis for optimizing the configuration design of SEN and choosing reasonable processing parameters for the continuous casting mold of super-wide slab.

Jan 1, 2009

By M. C. Ruiz

The leaching behavior of chalcopyrite concentrate in acidic CuC12-NaCI-O2 solutions was investigated. Experiments were conducted under continuos flow of oxygen at atmospheric pressures. The results indicated that among the variables temperature has the largest influence on the dissolution of chalcopyrite in this medium, and high copper extraction can only be obtained at temperatures near the boiling point of the solution. It was also found that the stirring speed did not influence appreciably the dissolution of chalcopyrite. An increase in the oxygen flow rate up to 0.1 1/min increased the copper extraction. The total chloride concentration affects the dissolution of chalcopyrite up to about 4 M. Copper extraction of 93 % was obtained in leaching chalcopyrite of size fraction -400 # Tyler at 105 OC in 2 hours.

Jan 1, 1997

By Weng Fu

In this study, Resin-in-Pulp (RIP) technology is used to separate Pb from a chalcopyrite slurry. Solvent-impregnated resin, Lewatit® VP OC 1026, which contains di(2-ethylhexyl) phosphoric acid (D2EHPA) in a macroporous polystyrene matrix was used, as the functional group exhibits selectivity for Pb over Cu. Adsorption pH, kinetics, as well as resin and CuSO4 concentrations were investigated. The results show that the kinetics of Pb and Cu loading are fast, reaching the adsorption equilibrium within 30 min. The equilibrium pH of 2 was chosen as optimum for operation in order to achieve a high Pb extraction rate and extent as well as selectivity for Pb over Cu. High Cu(II) concentration in solution results in Pb(II) requiring a larger amount of resin for the same degree of extraction. Regeneration and reuse tests show that the loss of adsorption capacity happens in the 1st and 2nd cycles and then the adsorption capacity stabilises for the 3rd cycle.

By L. -C. Lai

A series of LaNi5-based alloys, with partial substitution of Ni by Al, Co, or V, were prepared The gas-phase hydrogen absorption kinetics and pressure-composition-temperature curves were measured The activation became easier and the plateau pressure was reduced as Ni was partially substituted by Al Substitution with Co reduced the hysteresis as well as the hydrogenation capacity, but enhanced the absorption kinetics Vanadium is often considered as a hydride former, but when it was added to LaNi5, it was found that V occupied the B site. A small amount of substitution of Ni with V led to a higher hydrogenation capacity and faster activation rate Based on these properties, an alloys LaNia 25CO0.5V0.1Al0. 15 was fabricated as an electrode. Compared with LaNi4.85Al0.15, it was found to exhibit faster activation, higher discharge capacity, and longer cycle life. The variation of the hydrogenation characteristics is discussed based on the physical and chemical properties of the alloying elements.

Jan 1, 1997

By Wang Dawan

During the process of arsenic bearing gold concentration biooxidation, the content of chloride ion in water is a very important factor to the activity of bacteria and the oxidation of sulfide minerals. In this paper, the influence of underground mine water with different chloride ion content to the biooxidation of arsenic bearing gold concentration and the limit of chloride ion content to bacteria were summarized. These results indicated if the content of chloride ion was less than 1.2g/L, the bacteria?s ability to oxidize sulfide minerals was little affected, and if the content of chloride ion were increased to 2g/L or more, the activity of bacteria was seriously restrained, and if the content of chloride ion were increased to 4g/L, the activity of bacteria was absolutely restrained. So, as the content of chloride ion in water was cumulated to 2g/L or more in biooxidation plant, the water must be refreshed to maintain normal production.

Jan 1, 2008

By Y. W. Miao

Along the south-west coast of Taiwan is about 550,000 metric tons of heavy sand deposit containing about 10 % black monazite. The Institute has developed a separation process to recover the individual rare earths and the developed process has been commercialized by a local private company. The decomposition of the local black monazite by sodium hydroxide through hydrothermal and fusion methods has been investigated. In the hydrothermal process 4.5 wt. % of aqueous alkali solution was used in an autoclave. In the fusion process, caustic soda (9.8% NaOH) was employed in am open cylindrical reactor. The same product of hydrous rare earth oxides were obtained and then dissolved by hydrochloric acid and the p-H adjusted in order to separate the thorium from the rare earths. After filtration, the filtrate contained rare earth chloride and the cake contained mainly the silica and thorium hydroxide. Both methods give a yield of 90 % with respect to the rare earths recovery. A detailed description of operation and comparison of the two methods are given.

Jan 1, 1989

By R. E. Molnar

A number of flowsheets have been designed and operated, or are currently being considered, to extract copper from leach solutions having much more copper than the 4 g/L levels typically found in heap leach liquors. Dealing with these solutions has required that the envelope for ?normal? copper solvent extraction be pushed beyond the usually considered limits. Others have published information on flowsheets to recover copper from leach liquors containing over 25 g/L copper. Secondary solvent extraction circuits are often required to attain satisfactory overall recoveries. This paper reviews some of the issues faced in three pilot plant circuits that were operated by SGS Lakefield Research to produce cathode copper from solutions containing 8 to 20 g/L Cu. The primary objective was to maximize copper extraction using one solvent extraction circuit. The role of feed acidity and the disposition of impurities such as iron and chloride are considered. The challenges of running short SX piloting campaigns are discussed.

Jan 1, 2003

By Jin Zuomei

The kinetics of dissolution of nickel matte in the presence of manganese dioxide with silver ions was investigated. The catalytic silver ions enchanced the leaching rate up to a factor of 17. The effects of stirring, temperature, particle size, concentrations of Mn02, silver and ferric ions, and the experimental procedures were studied. Solid residues at various levels of nickel extraction were examined by SEM, TEM, electron micoprobe and X-ray diffraction. These results indicated that the dissolution reaction was topochemical and fits a surface reaction control model. The activation energy was calculated to be 39.15 KJ/mol. The leaching rate of Ni3S2 was independent with stirring rate, but the reaction rate constant was inversely proportional to the initial particle diameter. The order of the reaction rate are 0.41, 0.69, 0.33 with respect to Ag+, Mn4+ and Fe'+ con-centration respectively. Thus a kinetic rate equation was developed. Moreover, we propose a mechanism of silver catalyzed leaching of Ni3S2'

Jan 1, 1990

By Joachim Lemke

The stainless steel sheets of permanent cathodes at Norddeutsche Affinerie (NA) were damaged by corrosion after nearly 11 years in operation. The necessary raising of the strength for stripping the copper had increased the deformation of the stainless steel blades. Current efficiency declined. After investigating the possibilities, like buying new cathodes or treating the steel surface, i.e. by sliding, a repair process was developed whereby the stainless steel sheet was exchanged. Special laser technology for cutting used blades und welding new stainless steel sheets underneath the used hanger bar was applied because the energy input into steel is the lowest of all welding methods. The new stainless steel sheet was welded with the rolling line in a horizontal direction. The achieved flatness of the repaired cathode blades amounted to less than 4mm per meter. During 11 months NA repaired nearly 36,000 permanent cathodes and put them back into operation. Repair costs were much lower than the costs of buying new ones and current efficiency increased again to more than 96% with a current density of 340 A/m².

Jan 1, 2006

By Alex I. Kociubczyk, Wilky Desrosin, Lucía Mabel Boycho, Alicia E. Ares, Carlos E. Schvezov

In the present research, commercially pure Sn and Zn, and Sn-Zn alloys (Sn-1wt.%Zn, Sn- 2wt.%Zn, Sn-4wt.%Zn, Sn-8wt.%Zn and Sn-8.9wt.%Zn, weight percent) were obtained by a horizontal directional solidification process with two opposite senses and heat extraction. The solidification process was realized using a horizontal furnace with two heat extraction systems at both ends. The temperature was measured using eight K-type thermocouples and an electronic recorder of temperature data. The resulting structures were analyzed using optical microscopy. From the solidification process the thermal and metallographic parameters were determined in all samples. The presence of defects in the solidified pieces was observed. Internal defects pretended to be dependent not only on the composition of the alloys under consideration but also on the size of the structures formed, also, on the velocities and accelerations of interphases, and on the variation of thermal gradients. A model of the phenomenon from the first principles is presented.

Jan 1, 2015

By Y. F. Jia

Arsenic constitutes a major contaminant for the hydrometallurgical industry. Its removal and immobilization from process effluents typically involves lime neutralization and co-precipitation with ferric iron (Fe (III)/As(V)>3). Alternatively, precipitation of scorodite (FeAsO4?2H2O (cr)) may be applied to arsenic fixation. The mechanism of arsenic fixation in the former process has been suggested to be surface adsorption. Unequivocal characterization of these products is difficult because of their amorphous nature hence a variety of methods need to be applied including the particularly powerful method, extended x-ray absorption fine structure (EXAFS) spectroscopy. In this study, we have investigated the preparation of arsenate-adsorbed ferrihydrite with the purpose to compare its structure to that of Fe(III)-As(V) co-precipitates and scorodite (both amorphous and crystalline). Furthermore the solubilities of these Fe(III)-As(V) solids are measured as a function of pH. Their structures are elucidated and correlated to their solubilities and thereby the application of these findings to the practice of arsenic removal and disposal is assessed.

Jan 1, 2003

By Toyohisa Fujita

The effect of variables on the gold extraction with ammonium thiosulfate was investigated on sponge gold and ore samples. The Effects of CUS04, (NH4hS203, NH40H, (N~hS04' pH, stirring speed and retention on gold leaching rate and thiosulfate oxidation (consumption) have been studied. Almost 100% of gold was leached from sponge gold and over 96% from ore sample at optimum conditions. Trioctylmethyl ammonium chloride was used to recover gold from thiosulfate pregnant solution. It was found that more than 99% of gold was recovered by the extractant diluted with n-octane at 01 A ratio of 1: 1 without the re-adjustment of pH or others. Also, the gold cementation was conducted without de-aeration by using zinc, copper and aluminum powders. The result indicated that the gold was effectively recovered from a solution of low ammonia and copper concentrations and higher thiosulfate concentration. The gold recovery process by using ammonium thiosulfate is an environmental friendly method comparing to conventional cyanidation process.

Jan 1, 2003

By Haotian Xue

A new process to extracted antimony directly from stibnite concentrate by reductive sulfur-fixation smelting in sodium molten salt has been presented. The influences of sodium salt content and composition, ferric oxide addition, temperature and time was investigated, respectively. The optimum conditions was determined as follows: W????: ??concentrate=40%, W??alt: ????concentrate =88.75%, WFe2O3 :Wconcentrate =55.13%, W??aCl: ????alt=40%, 1123K, 1h. Under above-mentioned optimum conditions, the average direct recovery ratio of antimony can reach 91.48%, and the main chemical composition of obtained crude antimony is Sb 94.31%, Fe 4.436%, Pb 0.502%, Au 0.0236%. In comparison to traditional antimony pyrometallurgical process, the smelting temperature of present process is reduced from 1423~1473K to 1123~1173K. During the smelting operation, SO2 emision can be avoided completely due to sulfur-fixation as FeS. Furthermore , S0 can be obtained when the molten slag is handled by water leaching with conditions of 323K, L/S=5/1, 2h.

Jan 1, 2014

By Marcela Morvová, Mário Janda, Morva Imrich

"The possibilities of greenhouse gas mitigation using various methods are brought out. The special case of utilization of mixture of CO2 with other greenhouse gases in a synergetic way inside non-thermal plasma based system is described in detail.Measurements on pilot system comprising pyrolysis chamber as alternative energy system (production of hydrogen and liquid tar) were made for various biomass and waste as the input material. The exhaust from this system was treated with non-thermal plasma gap suitable for up to 650Nm3/hour of exhaust gas flow. Condensable portion of exhaust is liquefied in distillation unit; produced hydrogen is stored on-line inside nano sized carbon of our own production.The CO2 removal efficiency varies depending on exhaust composition between 45 to 98%. Other oxides as CO, NOx, SOx and several hydrocarbons and VOC are also removed. The main product connected with CO2 removal is a solid powder of proteinoid nature. There exist strong probability, that precursor of the origin of life on the Earth from primary atmosphere were formed in the similar way as it is present in the electric discharge system used. Our system is equipped with on-line as well as ex-post analysis of all forms of products. We have also developed a system for recuperation of all forms of produced heat. It is stored inside as latent heat of waxes.IntroductionNatural greenhouse effect on the Earth is caused mainly by water vapour with the average absolute concentration about 4%. Other gases able to absorb long-wave radiation and thus this causing greenhouse effect are CO2, CH4, N2O, halocarbons and as precursors ozone and NOX. Some of them we produce and introduce into atmosphere in large quantities during production of energy and in transport. This factor leads to permanent increase of average temperature of air, sea and oceans, so called global warming.Nowadays large amount of data exists showing that the temperature of Earth in the last 150 years has been continually increasing. It represents about 03°C per ten years and the most of climatologist believe, that the increased concentration of greenhouse gases in the atmosphere is responsible for this effect.The most important greenhouse gas is carbon dioxide CO2. Majority of CO2 emissions comes from electric power stations working with fossil fuels, cars and industry. Burning of fossil fuels contribute up to 80% to world wide anthropogenetic emissions of CO2."

Jan 1, 2010

By Mahmood Alemrajabi

When LKAB processes their iron ores in northern Sweden, they generate apatite as a by-product. The apatite has been recovered by flotation and the concentrate contains about 0.4 wt% rare earth elements (REE). Both phosphate rock and REE are listed as critical raw materials for the European union. In the present study, the recovery of REE within the nitrophosphate process of fertilizer production has been studied. In the first stage, the REE are precipitated and isolated as a phosphate concentrate. For further purification and individual separation of REE by solvent extraction, removal of phosphorous from the concentrate to enhance the dissolution of REE in mild acidic solutions is essential. In this study, thermal treatment of the concentrate with sodium hydroxide at elevated temperatures followed by water leaching has been studied in order to separate the phosphorous and thereby facilitate dissolution of the REE. The results show that 95% of total phosphorous initially present in the REE phosphate concentrate is removed after thermal treatment with NaOH 1:1 mass ratio, at 400 °C.

By Adegbenjo Adewale Oladapo, Ibitoye Simeon Ademola, Ladiipo Olufemi Akinbiyi, Adegbola Adekunle Amos, Adeboje Taiwo Bode, Raji Fatai Olasunkanmi

The combined effects of the addition of Silicon (Si) as alloying element and low temperature annealing on the tensile properties of 70/30 brass with Nickel (Ni) and Iron (Fe) contaminants is investigated in this paper. Melts of cartridge brass were made to which 0, 0.5, 1, 2, 3 and 4 wt % of Si was added. These were sand cast into rods of 600 mm by 10 mm diameter and were thereafter machined into standard tensile test samples. Some of these samples were annealed in a muffle furnace at temperatures of 250, 300, 350, 400 and 450 oC respectively and the others were used as control. Subsequently, all the heat treated and non heat treated samples were subjected to tensile tests on a Hounsfield Extensometer and the load – extension plots retrieved were analyzed. Microstructural characterizations of the samples were carried out using Accu-Scope Optical Microscope. The results showed that cartridge brasses subjected to alloying and annealing treatments had improved tensile and yield strengths. However, the tensile properties were increased and maintained within acceptable limits at stress relieve annealing temperatures.

Jan 1, 2015