By Toshiaki Tsuru, Takeshi Ohgai, Hisaaki Fukushima, Shigeo Kobayashi, Tetsuya Akiyama

"Electrodeposition behavior of Zn-Cr alloys from the methanol baths was investigated. In the methanol baths of low Cr3+ concentration, Cr (III) compound was incorporated in the deposits and no lusfrous Zn-Cr alloys was deposited. However, Cr was existed as metallic state in the deposits obtained from the baths of higher Cr3+ concentration. With an increase in water content in the baths, the chemical state of Cr in the deposits changed from metallic to trivalent state. Under the condition that metallic Cr can be electrodeposited, Zn deposition was significantly polarized to the potential of Cr deposition.INTRODUCTIONAn attention has been paid to Zn-Cr alloy plated steel sheet because of its excellent properties for body panels of automobile and electrical appliances [1]-[4]. This plating process can be operated using the sulfate solutions containing Cr3+ ion [1] - [6].In decorative single Cr plating, on the other hand, many attempts have been made to electroplate Cr from trivalent electrolytes, which is motived by environmental deficiencies of the presently used hexavalent process [7]. [8]. However, it has been reported that in the aqueous solutions the behavior of the electroreduction of 0 3+ is atypical due to the complicated nature of the chemistry and electrochemistry of cr3+ species [9]-[11]. Even in Zn-Cr alloy plating, it is difficult to codeposit metallic Cr with Zn in simple sulfate electrolytes [l]-[4], [12]. Therefore, it can be expected that the electrodeposition behaviors of Zn-Cr alloys as well as Cr are significantly changed when the electrodeposition is conducted in non-aqueous plating solutions.In this study, the electrodeposition of Zn-Cr alloy was conducted from methanol solutions to clarify the electroreduction mechanism of Cr3·-Cr0 in the alloy deposition process."

Jan 1, 2000

By M. Soltanieh

The liquidus surface? and tie-lines in the nickel-cobalt-sulphur ternary system have been determined between 1<273-1573 K. The experiments were conducted by equlibrating the liquid sulphide with the metallic alloy phase. The liquid sulphide phase was sampled and chemically analyzed. The alloy was analyzed by electrol} microprobe. Combining the present results with the.avai1abl~ literature data, the thermodynamic properties of this system were calculated.

Jan 1, 1998

By T. H. Courtney, B. R. Murphy

"Nominal room temperature mechanical alloying (MA) has been used to synthesize the high melting temperature NbC and Cu-NbC composites. Elemental powders of Cu and Nb were alloyed in the presence of either graphite or hexane to form nanocrystalline NbC or a Cu-NbC composite. Through control of hot-isostatic-pressing (H/Ping) parameters, we have been able to minimize microstructural coarsening during densijication, and have processed fully dense bulk compacts of both single phase NbC and two-phase Cu-NbC while maintaining a nanocrystalline or near-nanocrystalline structure. These materials generally exhibit high strength and low fracture toughness. However, mechanical properties vary significantly depending upon the Cu content and the method of NbC synthesis (graphite or hexane).INTRODUCTIONMechanical alloying (MA) has been recently used to synthesize a variety of inorganic solids; sulfides (1-2), nitrides (3), borides (4), and carbides (3, 5-8). One advantage of this processing route is that synthesis of fairly high melting temperature materials takes place at what is nominally room temperature. Another advantage is that the structures generated are often nanocrystalline in scale, with attendant interesting properties. The consolidation of these fine structures into near fully dense or fully dense materials while limiting microstructural coarsening is a challenge that has just recently seen limited success (5, 9). We report here on some recent studies of ours dealing with crystallite size and structural analysis of NbC and CuNbC composites consolidated to full density from mechanically alloyed powders. Bulk mechanical properties and their dependence on milling parameters are also presented."

Jan 1, 1994

By Debbie Marshall

Nickel and cobalt in lateritic ores can be extracted by either a hydrometallurgical or a pyrometallurgical route. The high-iron limonitic fraction of a deposit is best processed&apos; hydrometallurgically while the magnesium-rich transitional and saprolitic fractions are more suited for pyrometallurgical processing. During hydrometallurgical processing, it may be attractive, for economic reasons, to blend the limonitic component with transitional and saprolitic ores, which contain higher nickel levels. However, blending increases the concentration of magnesium in the feed, leading to increased acid demands. The decision on how much ore to process then becomes an economic one. Ore samples with different magnesium contents were prepared for the leach test program by blending limonitic and transitional ores. The ore samples were slurried in seawater and tested in the Falconbridge Hydrometallurgical Pilot Plant. As expected, acid consumption increased with increasing magnesium content of the ore. For target extractions of 95% nickel and 92% cobalt, the required residual free acid concentration increased from 30 g/L at 1.7% magnesium to 50 g/L at 2.7% magnesium. When the magnesium content was raised to 3.8% and 4.6% in subsequent pilot plant testing, the final free acid requirements did not increase beyond what was observed at 2.7% magnesium. Thus, the cut-off ore composition to maximize nickel units and minimize acid requirements is between 1.7- 2.7% magnesium. Keywords: high pressure acid leaching, laterites, magnesium

Jan 1, 2004

By Yeliz Demiraya, Onuralp Yucelb

"Production of strontium metal from its oxide was studied under the pressure of 1-5 mbar by methalothermic process. SrO with 99 % purity was used in the experiments. Effects of Al powder addition (100, 200, 300 % of stoichiometric ratio) and time were investigated on recovering of metallic strontium. Effects of BaO addition (100 %, 200 %, 300 %) was also investigated. The final residues were examined for their chemical composition. XRD, AAS and Flame Photometer were used for chemical analysis. More than 96 % of strontium metal recovery can be obtained.IntroductionStrontium is an element which is used in many advanced technology applications. Barium strontium titanat, strontium bismuth titanat, and strontium bismuth tantalat thin films are promising materials in ferroelectric and Schottky-based microelectronics technologies, especially for memory applications. Physical vapor deposition (PVD) techniques as magnetron sputtering, thermal evaporation and molecular beam epitaxy (MBE) are the most widely used methods for growth of these thin films [1-3]. In these techniques high-purity of Sr metal is used as evaporation sources and sputtering targets. Furthermore, metallic strontium is used as a ""getter"" in electron tubes, and as an alloying elements in aluminum alloys [4].The most used Sr compound is SrCO3 and widespread process used in production of SrCO3 is the hydrometallurgical carbonation of celestite. Although there are considerable amount of Selestite reserves, SrCO3 and strontinum metal are not being produced in Turkey, yet [5].Concentrated celestite (SrSO4) is conversed to SrCO3 in carbonate media. Black ash and direct conversion processes are currently used methods. There are many satisfactory studies about hydrometallurgical carbonation of celestite and decomposition of SrCO3 [6, 7]. Since strontium metal is produced from it’s oxide (SrO), SrCO3 needs to be decomposed to SrO."

Jan 1, 2011

By Hua-qing Li

Electromagnetic stirring process effectively improves the casting quality of metals. In this paper, the physical simulation experiment, in which the molten copper is displaced by mercury, was designed. The factory test parameters were determined according the simulated data. The flow behavior of the mercury to be stirred as well as the relations between the microstructure of plate blanks and the current parameters were analyzed. With an appropriate electromagnetic stirring, the inverse segregation of tin for C51900 alloy plant blank reduces from 15 % ~ 30 % to about 5 %, and the proportion of equiaxed grain rises to larger than 30%.

Jan 1, 2009

By Y. H. Liu

Several foaming aluminum samples of different density were prepared in a semi?industrial scale experimental system, Their properties such as the energy absorption characteristics, mechanical properties, heat conductivity and acoustical properties were measured. The results showed that the foaming aluminum with a density of 0.5 to 0.6 g/em3J has the best energy absorption and this makes it suitable as the ensuring bar of the automobiles and also as a cushion material for the engine. The foaming aluminum with a density of 0.25 to 0.4 g/em3 has the best acoustical properties and heat conductivity resistance, which is suitable for the door filling material, the ceiling and the partition or the car engine.

Jan 1, 2003

By Xue Sun, Dengfu Chen, Yuting Chen, Mujun Long, Song Xu, Helin Fan

In order to seek an effective extraction process for vanadium, the recovery of vanadium from a high Ca/V ratio vanadium slag was studied by sodium roasting and ammonia leaching. In the present paper, the oxidation and leaching process of vanadium slag was investigated by X-ray diffraction (XRD), scanning electron microscopy and energy dispersive X-ray spectrometry (SEM/EDS) techniques. The effects of ammonium carbonate concentration, leaching temperature and leaching time on the leaching ratio of vanadium were discussed. As indicated in the experimental result, the optimal (NH4)2CO3 concentration was 120g/L, leaching temperature was 60°C and leaching time was 20 min. Approximately 92% of the vanadium was recovered under the optimal conditions. Furthermore, by means of X-ray diffraction analysis, the phase transformations of the vanadium slag during roasting and leaching processes were analyzed and discussed.

Jan 1, 2014

By Orlando C. Rojas

The Potrerillos Smelter commissioned a new El Teniente converter in 1985. As a result of the use of this technology, the Peirce-Smith converters have been processing only high grade matte or white metal. These operational changes resulted in damages to the converter shells, excessive splashing and cold dope generation and very short refractory campaigns. The paper shows the modifications to the tuyere angle, mouth design changes and new techniques for mouth cleaning and gas handling. Operational results up to 1991 are also shown.

Jan 1, 1993

Studies of electric pulse (EP) disintegration were conducted on ores of disseminated precious minerals, &apos;on platinum-bearing chromitites of the Konder Complex, Russia, on diamond-bearing impactites of the Popigai meteoritic crater, Russia, and on and diamond-bearing metamorphic rocks of Northern Kazakhstan. It was shown that EP disintegration ~s a technology that achieves ideal liberation of disseminated minerals, and is a new efficient method to study accessory minerals.

Jan 1, 1991

By N. Ono, H. Fujiwara, S. Otsuka-Yao-Matsuo, T. Omata

"The electrical conductivity and the oxygen release and uptake of sintered indium tin oxide (ITO) upon heating and cooling under the condition that P(O2)/P*=4.9X10-4 (P* = atmospheric pressure), :when P(O2) was approximately 50Pa, were simultaneously measured by using a closed-system oxygen-gas analyzer. A large increasing in -the electrical conductivity - upon the· oxygen release detected in 1130<T<1273K was observed. Quantitative relationship between the number of oxygen atom released from ITO and the conduction electron density in ITO was studied. The release of one oxygen atom agreed with the generation of two conduction electrons, i.e., the efficiency-carrier-generation for the oxygen release from the ITO was almost one. The oxygen atom released must be originally at the quasi-anion site in the C-type rare-earth lattice, i.e., the 16c site in the space group of Ia3, as an interstitial excess oxygen, Oi"". It was concluded that the mechanism of conduction carrier generation and compensation upon SnO2 doping into In2O3 can be expressed by the defect equation, 2SnO2-2Sn1n +2(1-z)e'+zOi""+3O0 x+(l-z)/2O2, and that the oxygen release bringing the increase in the electrical · conductivity can be expressed by the equation, Oi""-1/2O2+2e'.IntroductionThin films of SnO2-doped In2O 3 (generally designated as ITO, for indium tin oxide), which have high optical transparency for visible light and high electrical conductivity, have been used as transparent electrodes for liquid crystal and electrochromic displays. It is well known that the electrical conductivity of ITO depends on the content of SnOi-dopant and oxygen. However, a reliable relationship between electrical conductivity and the absolute oxygen content in ITO has yet to be reported. The elucidation of such a relationship is one of the important clues for realizing extremely highly conductive ITO electrodes."

Jan 1, 2000

By Ragnhild E. Aune, Shahid Akhtar, Reza Beheshti

"The potential use of Black Dross (BD) as a raw material for the production of refractories, fluxing agents and glasses is the main motivation of the present study. Heat treatment experiments were carried out in Ar, and under reduced pressure (20 Pa), to evaluate the salt removal efficiency. The chemical composition of the BD after heat treatment was investigated by SEM-EDS and XRD analyses. Based on the present results, it is established that the salt starts to evaporate at ˜1273 K in Ar, and under reduced pressure. The salt removal efficiency in a 20 g sample was found to increase in both cases as a function of time and temperature. Moreover, in Ar the chlorine concentration was lowered to 0.3 wt% after heat treatment at 1523 K for 10 hours. Under reduced pressure, however, 0.2 wt% residual chlorine was obtained after 8 hours at 1473 K.IntroductionIt is believed that aluminum recycling in the near future will become the main route of aluminum production [1]. Black dross (BD) that is produced during this process contains, among other things, high amount of salts like NaCl and KCl [2, 3]. Almost 800,000 tons of BD is annually land filled in United States and this number continues to grow with the increase in aluminum recycling [2]. The BD should be dumped in controlled land field and it is costly procedure [4, 5].The water-soluble compounds in BD react with water or environmental humidity and release chlorides into the water and/or generate toxic gases such as H2, CH4, NH3 and H2 S [6-8]. In the Europe, BD is considered as toxic waste and its disposal as landfill is forbidden [8, 9]. After salt removal, the BD is considered to be non-hazardous and can be buried under ground [10].On the other hand, BD do also contains many relatively valuable compounds that may be changed in to useful materials as a result of further treatment [11, 12]"

Jan 1, 2012

By Michael S. Moats, Jan D. Miller, Wlodzimierz W. Zmierczak

"For many, hydrogen in a pure hydrogen economy would be like natural gas in today’s energy economy. Unfortunately, hydrogen’s physical properties are unsuited to the energy market’s requirements in terms of packaging, storage, transfer, and delivery. In this paper, a hybrid energy economy that packages hydrogen chemically on carbon atoms from various sources including recycled carbon dioxide is introduced and discussed. For this new hybrid energy economy to become a sustainable reality, the ability to recycle carbon dioxide and use hydrogen to create an appropriate energy product, such as dimethyl ether (DME), is needed. DME is recognized as a potential next generation, “beyond-petroleum”, environmentally benign commodity for energy storage and distribution. It is expected that to maximize the sustainability of the proposed hybrid energy economy, “green” hydrogen will be utilized. The “green” hydrogen would be created by the electrolysis of water powered by renewable energy sources, such as solar, wind or geothermal heat.IntroductionWith the growing concerns surrounding trends in global warming and increasing concentrations of “greenhouse” gases, such as CO2 and CH4, efforts to mitigate the emission of these gases from industrial sources are growing. With respect to CO2, the demonstrations of various capture and sequestration methods are underway around the world.The sequestration of CO2 is mainly focused on storing the gas underground or deep in the ocean. The Intergovernmental Panel on Climate Change (IPCC) estimates that 2000 Gtonnes of CO2 can be stored underground in depleted oilfields, un-minable coal beds and other geologic features [1]. Additionally CO2 may be stored at the bottom of the ocean. The lure of storing carbon dioxide in depleted oilfields or un-mineable coal seams is that an economic benefit (enhanced oil or methane recovery) can offset the costs of gas capture, transportation and storage. Unfortunately, all of these storage methods have potential for the release of CO2 or CH4 back into atmosphere or creating environmental damage (mobilizing heavy metals, disrupting deep sea ecology)."

Jan 1, 2008

By D. I. Davidov, D. A. Shishkin, M. B. Rigmant, E. P. Romanov, N. N. Stepanova, N. V. Kazantseva

The Co-19 at.%Al-6 at.%W alloy was prepared by two methods of casting. We used arc melting under an argon atmosphere with casting into a copper water-cooled casting mold and induction melting furnace with casting into a ceramic Al2O3 mold. According to the X-ray and SEM analyses, phase compositions depend on the cooling rate of the ingot after melting. After arc melting, the cast alloy has a three-phase structure, consisting of  cobalt (FCC), intermetallic phases CoAl (B2) type, and Co3W (DO19) type. After the induction melting, the alloy has a three-phase structure, consisting of  cobalt (FCC), intermetallic phases CoAl (B2) type, and Co7W6 () type. All phases in the investigated ternary alloy at the room temperature are ferromagnetic. Curie temperatures of all obtained phases were defined. It is shown that the magnetic properties of the studied alloy are typical for soft magnetic materials.

Jan 1, 2015

By Sedef Pinar Basag, Onuralp Yucel, Ahmet Turan

Niederschlag process is commonly used to produce metallic antimony. The process is a metallothermic process which is conducted in one step for metallic antimony production. Using this method Sb2S3 is mixed with coal and metallic iron and subjected to reduction. During heating, antimony sulfide is decomposed and sulphur combines with iron to form the matte phase. Metallic antimony is collected at the bottom of the crucible. In this study, evaluation of Sb2S3 concentrate, extracted and obtained from West Anatolian Region of Turkey was investigated by using Niederschlag process. The reductant stoichiometry, reduction temperature and duration were carried out in the experiments. Chemical analysis methods by using atomic absorption spectrometry (AAS) and X-ray diffraction spectrometry (XRD) techniques were used for the characterization of the concentrate, metallic nuggets and matte phases.

Jan 1, 2016

By E. A. Werner, W. Liebfahrt, J. Blaha

"The influence of the composition and the microstructure on the plane strain fracture toughness of five cold work tool steels all processed via the powder metallurgical route is investigated using 3-point bending specimens. The steels differ in composition and therefore possess different volume fractions of carbides. The amount, size and distribution of the carbides in the matrix are estimated by quantitative image analysis on a plane parallel to the fracture surface without discrimination of the carbide type, since the carbides are always much harder [1,2] than the matrix, irrespective of their composition. Due to the production of the steels via the powder metallurgical route almost all carbides are spherical in shape. The mechanical in-situ properties of the matrix are characterized by indentation tests performed with an ""UltraMicro"" -indenter in a scanning electron microscope.IntroductionCold work tool steels are used as tools in applications where excellent wear resistance and high hardness are required. Examples are cutting, woodworking, thread rolling, wire and deep drawing, cold extrusion and pressing of parts at process temperatures below 200°C. For such applications the steels must show an optimum combination of hardness, wear resistance and toughness while offering good machinability. Hardness and wear resistance are controlled by the amount of carbon and carbide forming elements such as molybdenum, tungsten, vanadium, chromium and niobium. These elements are present in the MC-, M6C and M7C3-carbides and are also responsible for the precepitation of secondary carbides during tempering. In this report attention is paid to the influence of the primary carbides only, while the very small ~~nm) secondary carbides will be treated as constituent of the homogeneous matrix. Increasing the amount of carbides (alloying elements) usually results in a decrease of the material's toughness which is caused by the presence of clusters and/or bands of carbides. To achieve an optimum combination of hardness, wear resistance and toughness many of the today's cold work tool steels are processed via the powder metallurgical (PM) route, which helps to prevent non-uniform element/carbide distribution because of the rapid solidification of the powders used. The resulting microstructure of the tool steel then consists of a tough matrix with uniformly distributed hard carbides· of globular shape. This shape of the carbides is also desirable instead of blocky carbides present in non-PM tool steels, since they improve the machinability of the steel. An additional advantage of PM-steels lies in the possibility to produce near net shaped tools thus lowering the costs of machining."

Jan 1, 2000

By Nathalie Neveux

For the first time, dehydrated ferrous sulfate was successfully used for the dry synthesis of potassium ferrate. In addition, ferrate ion is stabilized as a solid solution where hexavalent iron is partially substituted by S(V1) leading to a sulfato-ferrate having the following formula K2(Fe,S)04. This substance has an efficient life time of about six months. Ferrate ion is a powerful oxidant ( EO = 2.2V ), a bactericidal agent and possesses coagulant, flocculant properties. Its reduction generates nascent oxygen, hydroxyl groups and Fe(OH)3. Alkali metal ferrate is probably the future global agent for water treatment. Applications of this material in the field of urban and industrial effluents treatment have been investigated. Heavy metals cations such as Cu, Cd, Mn, Ni, Pb, Zn, ... were successfully removed. The results of sulfato-ferrate use for cyanide destruction, decrease in COD, soil, discoloration of pulp and paper effluents will be summarized.

Jan 1, 1999

By G. C. Yao

Branch and needle-shaped intermetallic compounds of iron, silicon and aluminum normally exist in the molten aluminum. If a suitable amount of manganese metal is added into molten aluminum, the shape of the intermallic compound particles may become lumpish and spherical. According to the difference in electric and magnetic properties of these impurity particles and molten aluminum, these impurity intermetallic compound particles can be separated by applying an alternating magnetic field. In this experiment the alternating magnetic field was formed by a "c" type loop with AC (50Hz) current. The inner vacuum of the fireclay refractory separator is 25xl5xl30mm3 with a lateral baffle inside. The separator was put into the interspace of the "c" type loop. It was found that the longer the separation time, the larger the amount transferred of impurities. The amount of transferred impurities increases with the increase of separation time and intensity of magnetic field. The addition of manganese metal enhances significantly the efficiency of impurity separation

Jan 1, 2003

By M. Vondersaar, B. Bulnes

Quemetco, Inc.,. as a subsidiary of RSR Corporation, operates one of RSR's three secondary lead smelters in the City of Industry, California, next to a residential area within Los Angeles County. The Reverberatory furnace serves as the main reactor for melting lead grid and paste recovered by the battery crushing system. Feed material is introduced via screw conveyor after drying in an upstream rotary kiln. Slag produced by the Reverb flows directly to an electric arc furnace. Products from this one-pass furnace system consist of soft lead bullion from the reverb, hard lead bullion from the arc furnace, and a non-hazardous slag from the arc furnace. Furnace bullion is processed into finished product in a six-kettle refinery. An overview ·of plant operations is presented. Where applicable, references will be made to changes that have taken place during the last decade.

Jan 1, 2000

By Amir Rehmat

The Institute of Gas Technology has developed a fluidized-bed process for recovering direct reduced iron from blast furnace flue dust a material currently considered to be a waste from the iron and steel industry. In the process, a portion of the carbon in the flue dust is combusted to supply energy for the endothermic reaction between carbon and steam. The reaction produces reducing gases comprised of carbon monoxide and hydrogen both of which react with iron oxides to produce reduced iron. Up to 95 percent of the iron oxides contained in the waste stream can be reduced to elemental iron. The vitiated reducing gases emanating from the process can be used as fuel in the plant. The yield of iron depends upon the quantity of iron oxide present in the flue dust and generally ranges from 20 to 30 percent of the waste stream. The investment cost estimated for a single processing train dedicated to one steel plant can be recovered in less than one year.

Jan 1, 1996