By George A. Roberts

The development of an alloy system, high-speed steel, is used as an example of the progress of physical metallurgy. Tracing the history of men and their thoughts as they studied and invented and modified these materials, the story of high-speed steel since the 1890's is seen to be a long, slow, but steady progression of achievements. Today's multiplicity of high-speed steels are the result. Data are presented on quantitative metallography of carbides in high-speed steel with high vanadium content using the QTM instrument. Grindability as well as mechanical properties are related to the content of excess MC and M6C carbides in a series of high-speed steels and the newer matrix steels. These emphasize the present state of knowledge and show the current stages of thought that may affect the development in succeeding years. It is a great thrill for me, an ex-research metallurgist and ex-practicing metallurgical engineer, to speak to an audience currently engaged in both pursuits on the occasion of the 43rd Howe Memorial Lecture before the Iron and Steel Division of the AIME. I shall not review Henry Marion Howe's distinguished career, so adequately reviewed in Maxwell Gensamer's contribution in the 1965 AIME History of Metallurgy, except to point out that, while leading the life of an intellectual, he worked as a practicing research metallurgist and a practicing metallurgical engineer for significant periods of time and contributed greatly in both areas. For those of you who believe, as I do, that in the intellectual activity of metallurgy we are blessed with an intimate mixture of science and engineering (see Mehl's 1960 Howe Lecture), we might recall that Howe, while pursuing a life of writing and teaching in later years, served as the first Chairman of the Division of Engineering of the National Academy of Sciences. That metallurgists were called upon then to lead an engineering recognition movement is perhaps related to the strong part played by the AIME and its members in the recent establishment of a National Academy of Engineering and to the fact that a metallurgist is its head, 47 years after Howe served. I stress these engineering aspects for I wish to talk about a metallurgical engineering subject today. Alloy systems, physical metallurgy, and steel blended with an historical perspective and a report on new techniques to improve the old will, I trust, be of sufficient interest to bring these lectures back to the physical-metallurgy banner from which they have departed for 4 years. Those process metallurgists, open-hearth fiends, and physical chemists among you will just have to be patient. The development of an alloy system is the engineering application of scientific thought and fact. There are many interesting alloy systems, developed to a high degree of technology and sophistication over the past 40 to 70 years. These systems are bound together and related by a similar set of characteristics. For example, stainless steels are a system in which the members are related by a high chromium content which gives a corrosion-resistant characteristic. A subfamily in this system would be austenitic steels

Jan 1, 1967

By Mark J. Klein, A. H. Clauer

The Snoek peak induced by solute nitrogen in chromium was studied. A rapid quenching rate is required to maintain nitvogen in solution in sufficient concentrations to be detectable by internal-friction techniques. An expression for the tertninal solubility, c, of nitrogen in weight pevcent is log,,c = -4130/T + 1.05. The diffusion of nitrogen in zhromium determined by internal friction is SNOEK&apos;S theory1 of the stress-induced ordering of interstitial solute elements in the bcc lattice has been used to deduce information on the behavior of interstitials in a number of bcc metals. Under the proper conditions, internal-friction studies of "Snoek peaks" permit a determination of diffu-sivities, solubilities, and precipitation kinetics of interstitial elements. Internal-friction studies of this type have been reviewed by Nowick,&apos; Wert,= Powers and Doyle,4 and others. The behavior of interstitial atoms in Group V-A metals and iron has been rather extensively studied in this way, and results are reasonably self-consistent. However, the study of interstitial elements using internal friction in the Group VI-A metals—tungsten, molybdenum, and chromium—is much less clear. Thus far, internal-friction studies have revealed a peak in tungsten tentatively attributed to carbon5 and a peak in chromium associated with nitrogen. In chromium, Bungardt and Preisendanz6 observed a peak at 180°C for a frequency of -1 cps which they associated with nitrogen. More recently, de Morton7 determined the diffusivity of nitrogen in chromium from studies of a nitrogen peak at 160°c for a frequency of -1 cps and from elastic aftereffect measurements. The objective of this investigation was to study the nitrogen peak in greater detail, to obtain information on the behavior of nitrogen in chromium. This information is of interest because nitrogen is known to have an embrittling effect on chromium. However, efforts to deduce the role played by nitrogen in influencing the mechanical behavior of chromium are handicapped by lack of information on its behavior and distribution in chromium. EXPERIMENTAL PROCEDURES The chromium wires used in these studies were drawn from arc-melted iodide-chromium stock that had been extruded, swaged, and centerless-ground to 0.25 in.-diameter rods. Internal-friction measurements were made in an evacuated torsional pendulum similar to the one described by Kê,8 utilizing wires 0.048 to 0.030 in. in diameter. A series of analyses of the fabricated wires showed that the major impurities were approximately 100 ppm Fe and a combined interstitial content of 50 to 100 ppm C, O, N, and H. A typical interstitial analysis of the wires after processing is 15 ppm C, 2 ppm H, 50 ppm O, and < 5 ppm N. Interstitial concentrations were determined by vacuum-fusion, combustion-conductimetric, and micro-Kjeldahl analyses. In general, vacuum-fusion analysis yielded a lower nitrogen concentration than did micro-Kjeldahl analysis. For consistency, the nitrogen concentrations reported in this investigation were determined by the former method. Heat treatments were carried out by encapsulating the specimens in quartz tubes containing argon. The fabricated wires were annealed at 1150°C for 1 hr to produce uniform recrystallized grain size of about 0.015 mm. Nitrogen and carbon were added to the fabricated wires by encapsulating them in a quartz tube containing ammonia or methane, and annealing them at 1150°C for 48 hr. In some instances, carbon was also introduced by coating the wires with carbon black prior to annealing.

Jan 1, 1965

By N. S. Stoloff, J. N. Mushovic

Age hardening response of a Mg-Th-Zr alloy has been studied at temperatures in the range 60° to 450°C. Transmission microscopy revealed clustering of thorium atoms at low aging temperatures, supporting a previous report of GP zone formation. Peak strengthening, which is observed at 325°C, is due to the formation of a coherent, ordered, DO19 type superlattice structure, of Hobable composition Mg3Th, as plates parallel to the matrix prism planes. These plates later reveal a Laves phase structure of composition Mg2Th. The equilibrium Mg4Th phase begins to precipitate in two different forms at an early stage, competitively with the Mg2Th plates. RECENT work on the Mg-Th system indicated that, unlike most magnesium-base alloys, complex precipitation phenomena may be occurring. The partial phase diagram of the Mg-Th system indicates that an equilibrium phase, Mg5Th, is the sole intermediate phase.&apos; sturkey,&apos; however, has reported, using X-ray and electron diffraction techniques, that a metastable fcc Laves phase, Mg2Th, precedes the formation of the equilibrium compound, which he identified as closer in composition to Mg4Th. Murakami et al.3 reported that the equilibrium phase precipitates preferentially on grain boundaries and dislocations in a Mg-1.7 wt pct Th alloy; Kent and Kelly4 aged a more dilute alloy, Mg-0.5 wt pct Th, for 4 days at 220°C and found similar results. In addition, they reported that a platelike phase with a structure close to that of the magnesium matrix forms perpendicular to the basal plane and is probably ordered. Research on a Mg-4 wt pct Th alloy by electrical resistance measurements and transmission electron microscopy has suggested that GP zones may form at low aging temperatures.3 However, the electron micrographs purporting to show this phenomenon were not conclusive. In view of the fragmentary evidence concerning the nature of the precipitation processes in the various Mg-Th alloys, an aging study was undertaken to clarify the characteristics of the various precipitates which form and to correlate the mechanical properties of the system with the direct precipitate-dislocation interactions. The latter results are presented elsewhere.&apos; The purpose of this paper is, therefore, to discuss the precipitation sequence in this system. EXPERIMENTAL PROCEDURE Sheet stock (0.060 and 0.010 in. thick) of a commercial Mg-3.93 wt pct Th-0.42 wt pct Zr alloy (designated HK3lA) similar to that studied by sturkey2 was supplied through the courtesy of Dr. S. L. Couling of Dow Metal Products Co. Zirconium does not enter into any precipitation reactions,&apos; but is present primarily as a grain refiner. The alloy was chill cast, warm rolled to 0.090 in. thick stock, and then finally reduced by a combination of hot and cold rolling. The alloy chemistry is given in Table I. This material was solution treated at 580°C for 4 hr in a dry CO2 atmosphere, and then water quenched. Material in this condition was fairly clear of precipitate particles and was fully recrystallized. Aging at temperatures less than 200°C was accomplished by immersing the alloy in a silicone oil bath; for higher temperatures, aging was done in a salt pot. Age hardening treatments were conducted at 60°, 80°, 105°, 135°, 160°, 250°, 325°, 350°, and 450°C for times ranging from 5 min to 400 hr. Hardness tests were performed on chemically polished 0.060-in.-thick blanks of solution treated material which were aged at the various temperatures for increasing lengths of time. For aging temperatures above 150°C the Rockwell Superficial 30T scale was employed, while samples hardened at temperatures below 150°C were monitored with the 45T scale. Each data point consists of at least three separate readings. Yield stresses also were measured at room temperature on both 0.060 and 0.010 in. sheet specimens aged at 325°C. The aged foils were thinned by the window method in a solution of 80 pct absolute alcohol and 20 pct concentrated perchloric acid (70 pct) maintained at 0°C. A stainless steel cathode was used and the applied voltage was 10 to 15 v. Thinned samples were rinsed in distilled water and pure methanol. After the me-thanol rinse the thin foils were quickly dried between filter paper. Foils prepared by the above method were examined in a Hitachi HU11B electron microscope operating at 100 kv. RESULTS A) Hardness. The hardness data are depicted in Figs. 1 and 2. Peak strengthening occurs at 325°C after aging about 6 min, see Fig. 1. Significant strengthening is achieved also at 350°C, but aging at 450°C produces only softening. The stepped curve at 250°C indicates that a complicated precipitation process may be occurring at that temperature. Fig. 2 suggests that at least two hardening mechanisms exist since the lowest temperature hardness peaks are displaced to the left of the peaks obtained at 135° and 105°C. A great deal of scatter is observed at long times in all cases due to magnesium surface degradation caused by the silicone oil bath. B) Identification of the Strengthening Precipitates. The structure formed atlowagingtemperatures (c10O°C) was not clearly resolvable by transmission microscopy. The only bright-field evidence for a change in structure was a mottled appearance which could be observed at extinction contours, as shown in Fig. 3(a), and the disappearance of this effect when dislocations produced under the influence of the electron beam passed through the matrix, as noted in

Jan 1, 1970

By N. J. Sather

The history of the Bunker Hill mine dates back to August 26, 1885, when Noah S. Kellogg found the outcrop of the Bunker Hill orebody on the hillside of Milo Gulch above the present town of Wardner, Idaho. A small concentrator was erected in 1886, and before the railroad came, the mine output was transported by mule teams to the head of navigation on Coeur d&apos;Alene Lake. After ten years of production, an interest was purchased in the Tacoma smelter at Tacoma, Wash., to which the entire output was shipped. In 1916 and 1917, a modern lead smelting plant and refinery was erected, and a modern electrolytic zinc reduction plant was built in 1927-1928 by the Sullivan Mining Co. which was 50 pct owned (and now totally owned) by the Bunker Hill Co.

Jan 6, 1961

By H. B. Probst

Mechanical twins were produced in zone-refined tungsten single crystals by explosive working at room temperature. These twins are parallel to (112) planes and have irregular boundaries rather than the classical plane twin boundaries. These boundaries aye grooved surfaces in which the grooves themselves are parallel to a <111> direction and the sides of the grooves appear to be par-allel to (110) planes. TWINS were produced in tungsten single crystals by explosive working at room temperature. These twins differ in character from any previously reported for tungsten; however, they are similar to those found in molybdenum after compression at -196°C.1 Deformation twins "resembling Neumann bands in ingot iron" have been observed in tungsten by Bech-told and Shewmon.2 This observation was made with sintered polycrystalline tungsten pulled in tension to fracture at 100°C and using a strain rate of 2.8 x 10-4 sec-1. More recently Schadler3 found deformation twins in zone-refined tungsten single crystals pulled in tension at -196"&apos; and -253°C. These tests were conducted using a strain rate of 3.3 x l0-4 sec-1, and the twin bands were found to be parallel to a (112) plane. Deformation twins in tungsten&apos;s sister metal, molybdenum, were observed by Cahn.4 These twins were produced by compressing small (0.7 mm) vapor-deproducedposited molybdenum single crystals at -183°C. The compression was performed &apos;by impact." By the use of precession X-ray techniques, Cahn was able to identify the twin plane as {112} and the shear direction as <1ll>. Mueller and Parker1 produced deformation twins in polycrystalline electron-beam-melted molybdenum by compression at -196°C. Their "loading rate" was 5000 psi per min which, judging from their stress-strain curve, corresponds to a strain rate of approximately 0.3 x 10-4 sec-1. These twin bands were found to be parallel to (1 12) planes; however, they differed in appearance from previously observed twins. In place of straight and parallel twin boundaries they were found to be irregular, jagged, and sawtoothed. The sides of the saw teeth were identified as (110) planes and irrational planes of a (111) zone. The twins observed in the present work in tungsten single crystals are similar in appearance to those of Mueller and Parker in polycrystalline molybdenum. The starting material used in this investigation was 3/16-in. diam commercial tungsten rod produced by powder-metallurgy techniques. This material was converted to a single crystal by the electron-bombardment floating-zone technique.= The process was carried out in a vacuum of 10-5 mm of Hg using a traversing speed of 4 mm per min. Segments (=2 in. long and 3/16 in. in diam) of two crystals (A and B) produced in this manner were studied. Crystal A received one zoning pass, while crystal B received two passes. The two crystals were explosively worked at Bat-telle Memorial Institute in the following manner. A 1/2-in.-thick layer of plastic was applied to the crystals to serve as a buffer in an attempt to prevent cracking. The composite, crystal and buffer, was then wrapped with 1/8-in.-thick DuPont sheet explosive EL506A2 and detonated in water at room temperature. Metallographic samples of the worked crystals were prepared, and back-reflection Laue X-ray patterns were obtained using unfiltered molybdenum radiation. RESULTS AND DISCUSSION Blasting the crystals as described above failed to prevent cracking. The crystals fractured into several fragments about 3/16 to 1/2 in. long; however, the fragments were of sufficient size to be useful for the subsequent study. The diamond pyramid hardness of the crystals after blasting was in the range 430 to 450 as compared with 340 for the as-melted material, which shows a definite hardening resulting from plastic deformation. These hardness values were obtained using a 1000-g load and taking readings only in sound portions of the crystals free of cracks. The crystals exhibited profuse twinning as shown in Fig. 1. No such structure is present in the as-melted condition. Most of these twins have jagged twin boundaries and are similar in appearance to those found in molybdenum by Mueller and Parker. The twins in both crystals were found to be parallel to {112} planes. This identification was made by using the conventional two-trace method. Subsequent efforts to describe these twins more fully were carried out on crystal A. If the longitudinal axis of crystal A is placed in the (001)-(011)-(Il l) basic triangle of the standard cubic stereographic projection, as in Fig. 2, then the two sets of twins shown in Fig. 1 are parallel to the (112) and (121) planes. Fig. 3 shows a schematic representation of a twin with jagged boundaries. This type of twin with a <111>

Jan 1, 1962

By C. S. Finney, John Mitchell

On December 31, 1959, there existed in the United States 15,993 slot-type coke ovens capable of producing 81,447,700 net tons of coke. These ovens were concentrated in 74 coke plants in 21 different states. As of the same date, there were 7448 beehive ovens in existence at 45 plants in the states of Pennsylvania, Virginia, West Virginia, and Kentucky. Total annual capacity of the existing beehive ovens was 4,368,800 net tons, but only 5148 ovens with a capacity of 3,131,600 tons were in operating condition. It is interesting to compare the average dimensions of slot-type ovens built during recent years with the 30 ft x 5 ½ ft x 16 ½ in. ovens erected at Syracuse, N. Y. in 1892. A composite oven built according to the average dimensions of all those erected between 1954 and 1958, for instance, would be 39 ft long. 12 ft high, and 18 in. in width. The coal capacity would be 16 tons as against the 4.4 tons which could be charged to the Syracuse ovens. Of the 15.993 slot- type ovens in existence at the end of 1959, by far the greater number were built by the Koppers Co. whose total of 11,280 ovens included 7891 Koppers- Becker and 3389 Koppers ovens. Of the remainder, there were 3260 Wilputte, 1350 Semet-Solvay, 63 Otto, and 40 Simon Carves ovens. By-product coke oven plants are usually classified either as furnace or merchant plants. According to the definitions used by the US Bureau of Mines, the former are "those that are owned by or financially affiliated with iron and steel companies whose main business is producing coke for use in their own blast furnaces. All other coke plants are classified as merchant. They include those that manufacture metallurgical, industrial, and residential heating grades of coke for sale on the open market; coke plants associated with chemical companies or gas utilities; and those affiliated with local iron works, where only a small part (less than 50 pct of their output) is used in affiliated blast furnaces." The annual coke capacity of the merchant plants during 1959 was 10,393,000 tons. However, the by-product oven of today is essentially an appurtenance of the iron and steel industry, rather more than 87 pct of total by- product coking capacity being concentrated at furnace plants. This was not always so. There was a time when the merchant plants played a much greater part in meeting the US demand for coke and gas. High noon for the merchant plants was reached during the early 1930&apos;s. By 1932 there were as many by- product oven installations being operated by the merchant sector of the industry as by the coke divisions of the iron and steel industry (44 of each), and in the same year the merchant plants produced 46.5 pct of all by-product coke made in the country. Since that time their contribution has drastically declined. In 1940 merchant plants were responsible for only 23.2 pct of total US production, and by 1950 their number had decreased to 30 plants which turned out 18.5 pct of the total by-product coke made. At the end of 1959 only 20 of the 74 existing by-product oven installations were merchant plants. They ac- counted for 12.5 pct of the year&apos;s production, or 6,849,786 net tons. This percentage has remained fairly constant since 1954. There are several reasons for the decline of the merchant coking industry. For example. On the grounds of economy, quality control, continuity of supply, and so on, the iron and steel industry usually prefers to control its own mines and carbonize its own coal at or near to the blast furnace rather than rely on independent operators for metallurgical coke. As the steel companies have enlarged their own coking facilities, so has the need for coke obtained from other sources declined. Furthermore, not only has the steel industry increased in self-sufficiency by building mare coke ovens during recent years, but it has also progressively improved the fuel efficiency of its blast furnaces. During the years 1947-49 the average coke consumption per ton of pig iron was 1892.8 lb. During 1958 the corresponding figure was 1613.4 lb. There are many individual furnaces where still better results are being obtained, and further reductions in the average may be expected. Perhaps the greatest threat to the merchant coking plant has been the fantastic increase in the use of natural gas and petroleum products for purposes which manufactured gas once served. So deadly has the com- petition from natural gas and oil been that it has almost eliminated by-product oven installations owned by public utilities. In the peak years of the early 1930&apos;s there were 23 such public utility plants. In 1960 only two were left. One of these, owned by the Citizens Gas and Coke Utility, was at Indianapolis, Ind.; the other was the plant operated by the Philadelphia Electric Co. at Chester, Pa. The non-utility merchant plants have also been sorely hit. With gas sales revenues reduced, domestic

Jan 1, 1961

By H. M. Otte, A. L. Esquivel

A new leasl-squares method is Presented for determining lattice parameters of hexagonal or tetragonul structures. The method is adapted for use on electronic computers and involves a reiterative procedure. The correction factor employed raries linearly with the lattice parameter, a (determined from the Brag, angle). In contrast, Cohen&apos;s method and recent modifications of it use a correction factor that varies incersely as the squure of the lattice paramneter, a. While the recent modifications attempt to improve the precision of the extrapolated lattice parameter, a, (or-cu). by stressing the importance of the weighting factor. the present approach emphasizes the need for choosing the correct extrapolation function. A comparison between the present method (the Linear method) and Cohen&apos;s method indicates that the Linear method may be more appropriale in certain cases. through a priori no critertion appears to he available for making a chorce between the methods. The size of hexagonal and tetragonal crystal lattices is determined by two parameters, a, and c,. Although in principle the two lattice parameters can be determined independently from reflections for which h - k = 0 and 1 = 0, respectively, in practice this may be inconvenient (because of the angular positions at which these reflections may occur) or not easily possible (because of low intensity). Furthermore, if a high precision or accuracy is required, the limited number of reflections of this type available, particularly in the high-angle region, is not sufficient for the necessary corrections (mainly due to absorption) to be determined with accuracy. Several methods1-7,11-13 have been proposed employing all reflections, to obtain the optimum values, a. and co, either by a trial and error procedure or a least-squares fit. Of the latter method, cohen&apos;s5 is the best known one since it provides explicit expressions for the optimum a. and c,. However, Cohen&apos;s method is only strictly valid if an extrapolation function is used that varies linearly with l/a2 or lie2 (see Section 3), a requirement that does not appear to be generally appreciated. On the other hand, all the better known and more widely used A recent trial and error method was proposed by Massalski and King8,7 who computed extensive auxiliary tables of axial ratios vs the functions A = [(4/3)(h2 + hk +k2) + l2+(a/c)2] and C = A(c/a)2 used in computing a and c values from the observed Bragg angles. These values of a and c were then plotted against a function which permitted linear extrapolation. As a criteria; for the "optimum" values, Massalski and King rely upon a visual fitting of the line through points representing reflections of low 1-index points to compute the extrapolated value of ao and high 1-index reflections to obtain CO. The successive computations and graphical plotting required to reach the "optimum" value are quite lengthy and tedious even on a desk calculator and no quantitative assurance is obtained of having in fact selected the optimum value.* If the method of Massalski and King is used on an electronic computer, then their published tables become redundant and a least-squares fit becomes a natural selection for the choice of optimum values. Such an approach will be called the Linear method. For work now in progress on the effect of certain physical variables on the lattice parameters of hexagonal crystals, it has become essential to determine the confidence limits of small changes in the lattice parameters. Since extrapolation functions that varied linearly with a and c actually also appeared to vary linearly with l/a2 or l/c2 when tested against published as well as our data, a comparison of Cohen&apos;s method and the Linear method was considered desirable (Sections 3 and 4). For the latter method an electronic computer was required since a reiterative procedure to obtain the optimum ao and co values had to be employed. The purpose of this paper is to describe the principles of the Linear method, illustrate its application, and compare it with Cohen&apos;s method. 1) THE LINEAR METHOD The standard practice in obtaining the lattice parameters in the Debye-Scherrer method is to

Jan 1, 1965

By R. K. Iyengar, G. C. Duderstadt

An investigation was carried out to determine the effect of Ca-Si additions on the dissolved oxygen content of liquid steel. An apparent equilibrium was reached after holding the melt for some time when the total oxygen content of the melt was identical with the dissolved oxygen. Results of the investigation show that for deoxidation with silicon and manganese the apparent equilibrium is reached after 8 to 12 min and the oxygen content of the melt is in good agreement with values reported in the literature for similar steel compositions. Ca-Si additions decrease the dissolved oxygen content appreciably below that obtained with Si-Mn deoxidation. It is postulated that some calcium dissolved in liquid steel at the time of its vaporization combines with dissolved oxygen to form CaO which then fluxes the manganese silicate, thereby lowering the activity of the deoxidation products. Slow flotation of calcium silicate inclusions is attributed to their slower growth rate. An addition of aluminum (to yield <0.005 pct Alsol) prior to introduction of Ca-Si improves the kinetics of removal of resulting deoxidation products. WITH the introduction of continuous casting of billets and blooms, application of calcium-containing alloys for deoxidation purposes has gained new interest. More so than in conventional ingot casting, the degree of control of the dissolved and total oxygen contents in steel for continuous casting can determine the success or failure of the operation because these affect both surface (pinholes) and internal quality of the billets. Of the available deoxidizers, only silicon has so far found wide application. However, in the typical range of application (0.20/0.30 pct Si), it is too weak a deoxidizer to suppress pinhole frequency to the level desirable for all but the least demanding appli-cations (approximately 10/50 pinholes per sq ft, de-pending on degree of subsequent reduction). On the other hand, Vincent&apos; has shown that it requires ap-proximately 0.007/0.008 pct A1 soluble in the steel to suppress pinhole formation to <10 pinholes per sq ft. In view of the difficulty of consistently maintaining this aluminum level and the associated problem of tundish nozzle constriction2 when aluminum is added to the ladle, steelmakers have searched for other de-oxidation alloys to circumvent the problem. Calcium-containing alloys offer such a possibility. When employed as a partial substitute for silicon, CaSi (30 pct Ca/60 pct Si) additions are reported to yield adequate pinhole contro1.3 Its use simultaneously preserves the "fluidity" of the steel and ensures good castability.4 Oxygen contents as low as 0.007 to 0.014 pct have been obtained with CaSi additions varying between 3 to 8 lb per ton.5-7 Due to the high degree of vaporization of calcium at the temperature of molten steel and the different methods used to introduce it into the liquid, the reported results show considerable scatter and lack of consistency. According to several investiga- deoxidation tors, the flotation characteristics of CaSi products are not as favorable as those found for alumi-num but are similar to those established for silicates with low alumina content.678 Thus, cleanliness ratings were improved when CaSi was replaced by a com-bination of Si + A1 followed by CaMnSi additions.5,9 In view of the lack of a comprehensive description of the deoxidation potential of CaSi alloys, a study was undertaken of the effect of CaSi additions on oxygen content in comparison to Si + Mn and Si + Mn + Al. The alloy chosen for this study contained 63 pct Si, 32 pct Ca, <3 pct Al, and 2.5 pct Fe. EXPERIMENTAL PROCEDURE The experiments were divided in three groups as shown in Table I. In each group, the CaSi addition was increased successively while maintaining the melt composition constant. The experiments in the third group were designed to determine the effect of prede-oxidation with small amounts of aluminum. Ingot iron, containing 0.02 to 0.03 pct C and 0.03 to 0.05 pct Mn, was melted in a 100-lb magnesia crucible. Pig iron was added to the melt under air in an induction furnace to attain the desired carbon content of 0.05 to 0.15 pct and thereby control the initial oxygen content of the melt between 0.04 and 0.015 pct. After removal of the slag, the furnace was sealed and argon was introduced through an opening in the graphite cover, Fig. 1. When the desired temperature was reached, electrolytic manganese was added to the melt and pin samples were taken (7 mm silica tubing) to establish initial oxygen content. To obtain maximum efficiency, CaSi and metallic silicon were introduced in a sealed steel pipe into the bath. This procedure assured minimum loss of calcium through vaporization as the deoxidants were always released at the bottom of the melt. Samples were taken at regular intervals and quenched in water. Temperature of the bath was measured with a Pt/Pt-10 pct Rh thermocouple. Portions of the pin sample were used for oxygen analysis; five determinations per sample were made to obtain average oxygen content. Oxygen analyses were made by the inert carrier gas fusion method with frequent cross checks with the vacuum fusion method.

Jan 1, 1970

By F. C. Foshag, P. E. Wingrove

The Kayford, Boone and Nicholas Division of Bethlehem Mines Corp. operates a modern coal preparation plant in Van, WV. Since start-up of the Van plant in 1976 until the summer of 1980, the refuse handling system proved to be a costly maintenance problem and a material handling bottleneck. During the 1980 two-week miners&apos; vacation, the original system - which included two screw conveyors and a drag conveyor - was replaced by an installation using two Flexowall steep angle belt conveyors. This paper describes the technical and economic analysis that led to the new installation and reviews its first year operating performance.

Jan 1, 1983

By R. M. Brick

A PREVIOUS publication 1§ has described the effect of quenching stresses on the lattice parameter values of high-purity aluminum-copper alloys particularly with reference to the solution and precipitation of CuAl2. A similar study has been made of the aluminum-rich aluminum-mag-nesium alloys. Attention has been directed in the present investigation to the magnitude of the quenching stresses as affected by the specimen size and shape, the number of solute atoms and the quenching rate. The effect of cooling stresses in causing plastic deformation or cracking has been considered in relation to the physical properties of the alloy. On reheating alloys in the two-phase field, the time required for pre-cipitation to occur has been observed in connection with the degree of supersaturation, the rate of diffusion of the solute atoms as a function of the comparative atomic radii, degree of strain, temperature of reheating and grain size. A few qualitative comparisons on the relative effect of these factors have been drawn between the aluminum-copper alloys and the aluminum-magnesium alloys.

Jan 1, 1935

By David E. Fogelson, James J. Olson

Rock mechanics as a guide to a safe underground operation is gaining importance as more is under- stood of rock behavior under stress and of the competency of rock after blasting. The U. S. Bureau of Mines&apos; Twin Cities Mining Research Center and White Pine Copper Co. personnel undertook a joint research program recently to define how the rock adjacent to a newly opened underground working could be left as undisturbed as possible. The goal was to leave a competent structure which would tend to limit rock falls and thus decrease the incidence of fatalities from this greatest of all underground hazards. High-amplitude stress waves and borehole gases create a crushed zone in the rock, the thickness of which is about equal to the borehole radius. Beyond the crushed zone, additional structural damage occurs to the rock from the microstructural level up to visible fractures that may extend several feet. This type of rock damage near the final excavation lines reduces rock strength and increases the possibility of failure of the openings from subsequent vibrations or stresses.

Jan 9, 1969

By H. Hanemann

Discussion of the paper of H. HANEMANN and PAUL D. MERICA, presented at the New York meeting, February, 1916, and printed in Bulletin No. 108, December, 1915, pp. 2371 to 2385. JOHN A. MATHEWS, Syracuse, N. Y.-I should like to ask the authors if there is any evidence of chemical change resulting information of, alpha iron from the gamma crystals found in nickel steel of high nickel content when stressed beyond the elastic limit, similar to the effect produced by drastic cooling. Would the stresses mentioned and the drastic cooling both result in an increase in magnetic induction? I would also like to ask the authors if they have made a test of the hardness. It would be very interesting to see whether the hardness decreased under the conditions of stress, as might be the case if alpha iron were produced. PAUL D. MERICA, Washington, D. C.-While it is impossible to state absolutely, it is my belief that the effect of deformation is approximately the same as, that of -drastic cooling, but we did not make a test, of the hardness.

Jan 5, 1916

By H. M. Howe

The chief purpose of this note is to call attention to the triaxial diagram as a convenient means of illustrating the properties of slags, and by this example of its use to commend it to those inclined to graphical studies having other possible applications. Explanation.—In the common or di-axial diagram, the properties corresponding to any point are determined by its perpendicular distance from each of two axes. For example, in an ordinary stress-strain diagram the properties of a given point in the curve are, first, a stress cd so many pounds per square inch, because its perpendicular distance from the horizontal axis of the diagram corresponds by the vertical scale to that stress; and second, a strain or elongation of so many per cent., because its perpendicular distance from the vertical axis corresponds by the horizontal scale to that elongation. It happens that, as a matter of convenience, we habitually place these two axes at right angles to each other; so that our measurenieilts happen to be made not only at right-angles to

Jan 1, 1899

By R. R. Nash, W. F. Sheely

Experiments were conducted on magnesium monocrystals in order to collect quantitative information on the mechanisms which limit the rate of basal slip. Using critical shear stress and creep data, activation energies for creep at low aid at high temperatures were derived. The activation energy at low temperatures is the same as that for jog formation and the activation energy at high temperatures agrees with that for climb. COTTRELL has suggested that at low temperatures, the expansion of dislocation loops under stresses near the yield strength is limited by the rate at____ which the expanding loops can cut the "forest" of dislocations passing through the glide planes.&apos; On the basis of this mechanism, seeger2 has derived expressions for low-temperature creep and for the relation of flow stress of single crystals to temperature. In the work reported here, the authors have performed experiments designed to obtain quantitative data on the physical properties of the dislocation intersection mechanisms operating during basal slip in pure magnesium monocrystals. Above a critical temperature, dislocations thread-

Jan 1, 1961

By R. H. Thielemann

THE conventional short-time tensile test provides a reliable means of predicting the sustained load-carrying capacity of steels only when the temperature is such that continuous plastic flow does not occur. At elevated temperatures, stresses considerably less than the short-time rupture value may produce continuous flow, with fracture occurring only after long periods of time. The amount of flow or creep accompany-ing failure varies for different steels, and depends, to a large extent, on the temperature and the duration of the test. Service records of cracking stills, steam superheaters and high-temperature boilers have shown that brittle fractures sometimes occur with little or no warning. In installa-tions of this type, localized stresses are often encountered, and steels must be capable of withstanding a certain amount of deformation without fracture. The sustained-load rupture test determines the expected life and corresponding ductility of steels at various stresses and tempera-tures. It also yields additional information regarding the effect of micro-structure and metallurgical stability on the high-temperature properties.

Jan 1, 1939

By H. E. Cline

Solidification of Pb-Sn alloys ranging in composition from 1.2 to 56 at. pct Pb ws observed with polarized light. Lamellar structures were observed over a larger range of compositions in alloys containing excess tin than excess lead, as expected from constitutional supercooling. The occurrence of pools of supercooled liquid surrounded by lead is explained by the difficulty in nucleating tin. Cells and dendrites weve observed in tin-rich alloys. Evidence was found that the degenerate structure formed at low growth rates, the formation of faults, and abrupt changes in composition and structure can be attributed to non-steady-state growth. The apparent interface shape was observed to have deep grooves at the interphase boundaries. HUNT and Jackson have observed the shape of the interface during growth of organic eutectics. They observed the formation of lamellar faults and shape instabilities upon changes in growth rate. The lamellar structure in these organic eutectics was not restricted to the eutectic composition. Recent work by Mollard and Flemings2 indicated that Pb-Sn alloys from 12 to 26 at. pct Pb could be solidified with a lamellar or rodlike structure if a sufficiently steep temperature gradient was used at a slow growth rate. Observations of the solid liquid interface of the Pb-Sn eutectic were made by Davies3 using polarized light. Photographs were at too low a magnification to determine the interface shape, but he has concluded that tin was the leading phase. In the following experiments, solidification of a range of Pb-Sn alloys from 1.2 to 56 at. pct Pb was observed using polarized light, to determine the factors controlling stability of the lamellar structure. EXPERIMENTAL Procedure. One hundred-gram ingots of alloys prepared from 99.999 pct pure Pb and Sn were cast into graphite molds under argon. The compositions of the alloys were 1.2, 6, 12, 26, 36, 46, and 56 at. pct Pb. Two-gram pieces were melted between two cover glass slides which were squeezed into a 1-mm separation. Samples were then observed under polarized light in a hot stage shown in Fig. 1. A long working distance objective designed for viewing at 500 times was used. Photography was made difficult by the lack of illumination and contrast at these high magnifications. By using an elliptical polarization compensator, as suggested by A. Holik, the contrast and illumination could be optimized. Photographs could be taken only at slow growth rates to avoid excessive interface motion during the 15-sec exposure used. The solidification rate was varied by increasing or decreasing the power to the heater. It was found that insulation was necessary to avoid undesired growth rate fluctuations. The temperature gradient, as measured with two thermocouples 1 cm apart, was 80" ± 20°C per cm during all the experiments reported here. The advantage of this procedure is in being able to observe solidification while it is occurring. However, the observations are restricted to the glass-metal surface and may be influenced by this surface. Also, one has no knowledge of the interior of the sample, in contrast to studies of the freezing of transparent organic eutectics.&apos; Observations. The alloy near the eutectic composition (26 at. pct Pb) solidified in a lamellar structure when the growth rate was uniform. If the growth

Jan 1, 1968

By Jean-Jacques Prompsy, J. S. Rinehart

Some time ago a study was initiated at the Colorado School of Mines in an effort to arrive at a better understanding of the stress fields developed within drill bits under dynamic loading and the influence that these stress fields could have on the failure of the bits. Particular emphasis has been given to the influence that bit shape has on the establishment of highly localized, potentially destructive stress inhomogeneities within the bit. The study has been divided into three phases involving three velocity regimes: impacts at very low velocities, 0 to 20 ft/sec, a velocity range in which dynamic effects are just beginning to be found; impacts at velocities ranging from 20 to several hundred ft/sec, a range commonly encountered in practical drilling operations; and impulsive loading through the detonation of explosives, a region in which the dynamic effects are greatly exaggerated and made more identifiable. The ultimate objective is to provide basic data which will enable the mitigation through judicious design of the frequency and severity of these transient concentrations of intense stress, thereby prolonging and increasing drill efficiency. This paper presents results of the third phase of this study — the development of a better understanding of the dynamics and mechanics of failures caused by transient stress-wave interactions. The impulsive loading or transient waves in these experiments were generated by detonating small explosive charges placed on the ends of Plexiglas cylindrical rods terminating in truncated cones. Under such intense loading, dynamic effects are greatly exaggerated and, hence, made more identifiable. The explosion generates a high-intensity transient stress disturbance which moves through the rod, reflects from surfaces which lie in its path, and establishes momentarily narrow regions of high concentrations of stress where failure of fracture may occur. The peregrinations of these waves, their interactions and their effects have already been described in the literature (see, for example, Refs. 1 and 2). The locations and extent of the regions quite apparently are strongly dependent on specimen shape, making it possible through judicious shaping of specimens to relocate the highly stressed regions, minimize their extent, or eliminate them entirely. These experiments were designed, first, to identify more clearly the vulnerable regions in geometries relevant to drill-bit design and, then, to modify these regions in a predictable way by changing specimen shape. Through this latter process, it is anticipated that better bit design might evolve. The specimens used in the experiments were cylindrical rods, 1 1/2 and 1 1/8 in. in diameter, ended by a truncated cone, with the cone angles ranging from 45° to 130°. Upper cone face diameters were 1/2, 3/4, or 1 in. A small plastic-covered electric blasting cap detonated on the axis of the specimen produced the spherical shock wave. The detonators used were Olin Mathieson No. 6, which induced into the rod a transient saw-toothed stress disturbance of about 3-microseconds duration, corresponding to a wave length of 0.3 in. in the Plexiglas. Five distinct systems of fracture were observed: (1) along the axis of the rod, a lower system of fractures, the cracks focusing around one point for specimens having cone angles of 80° and 90° and, as the cone angle was increased, spreading downward; (2) just above these fractures, an upper system of fractures composed of horizontal cracks observable in some specimens but not of any appreciable extent; (3) a third system of axial cracks still above the latter, observable in the small cone-angle specimens; (4) in the upper part of the specimen, a system of radial fractures extending from the blasting point; and (5) circular spalling due to reflection of the wave on the boundary of the cylinder. Only the first three systems, the axial fractures, are examined here. LOWER TENSILE FRACTURE SYSTEM The first, lower system of tensile fractures, shown in the photograph of Fig. 1, was observed in almost all of the specimens. It was due to the reflected tensile wave coming in from the boundary of the cylinder as shown in Fig. 2. The reflected wave was cylindrically convergent and focused

By Tibor Stefansky, John E. Dorn

MOTT and Nabarro1-5 were first to illustrate the importance of the flexibility of dislocations in accounting for the strengthening that metals undergo due to the presence of internal-strain centers. Such strain-centers might arise from a number of causes such as radiation damage, the presence of semicoherent and coherent precipitates and clusters, as well as individually dispersed interstitial and misfit substitutional solute atoms. Each strain-center induces positive and negative shear stress fields on the slip planes of the surrounding alloy matrix. In order to effect plastic deformation, therefore, the alloy must be subjected to sufficiently high applied shear stresses to push dislocations past all such internal stress fields. If dislocations were inflexible and moved as rigid lines, they would be equally pushed and pulled by internal stress fields. At this extreme the strengthening would be vanishingly small. Dislocations, however, are not rigid; they are flexible and extensible. They wiggle between positive and negative strain-centers, thus increasing their line energy at the expense of their interaction energy with strain-centers. cottrel16 and Friedel7,8 have independently presented lucid reviews of the significance of the Mott-Nabarro dislocation-flexibility concept to the strain-center strengthening of alloys. Their analyses however were only semi-quantitative. There is evidence in the recent literature of renewed interest in a more rigorous analysis of flexibility. Thus, Gleiter9 and Gerald" have shown that the calculated strain-energy interaction between a dislocation and the stress fields of coherent precipitates can be seriously in error if the flexibility of the dislocation is not taken into account. This report will be concerned with a more detailed analysis of the problem based on the following approximations: 1) Although many types of strain-centers exist, the following analysis will be limited to the case of solute-atom strain-centers in fcc substitutional alloys. 2) To facilitate the analysis by avoiding statistical considerations, the strain-Centers are assumed to be in regular arrays on the slip plane. Although the quantitative results are somewhat dependent on the type of array that is assumed, the qualitative trends are similar for various arrays that were studied. 3) An adjustment of the results from those for square arrays to those for the more realistic case of a random distribution of strain-centers is accomplished by adopting the interesting statistical theory first introduced by Kochs,11,12 elaborated on by Dorn, Guyot, and stefansky,13 and analyzed by Foreman and Makin14 in their computerized experiments. 4) For simplicity the dislocation lines are taken to wiggle about their edge orientation and no correction is applied to their line energy for deviations from edge configurations or for the elastic interaction between segments of the now curved dislocation. It will be shown that for extremely low concentrations of atomic strain-centers the strengthening increases with the square root of their concentration. For slightly higher concentrations the strengthening rate becomes less rapid. At a critical concentration a maximum strength is obtained and a decrease in the strengthening takes place as the concentration of solute atoms is further increased. These trends are a direct consequence of dislocation flexibility. They arise from changes in the amplitude of the waviness of the dislocation line at the yield stress with solute atom concentration. Despite the simplifying assumptions that were made, the results agree qualitatively with appropriate experimental data. I) STRESS FIELDS ON SLIP PLANES Internal stresses are introduced in a lattice whenever a host atom of radius ro is replaced by another that has a different atomic radius. According to the classical theory of linear elasticity,15 the stress field about a solute atom at the origin of a spherical coordinate system is given by arr=-4G€(?_0)3 ffflfl ="W =2G€{t) f°rr^ro(l+e) UJ where G is the shear modulus of elasticity and Y, = ro(l + E) is the radius in situ, of the substituted atom. As shown by ~shelb~,&apos;~ this approximation assumes that the bulk modulus of elasticity of the substituted atom is identical with that of the host species. ~abarro&apos;~ suggested that the strain E can be deduced

Jan 1, 1970

By T&apos Ke, ing-sui

NUMEROUS investigators have observed that internal friction accompanies cold-working of metals and the effect of annealing is to reduce this internal friction.1,2 However, - most of the experiments were made at high stress amplitudes and the principal purpose was to study the increase of internal friction as a result of the applied cyclic stress during measurement. In order to study the internal friction introduced by cold-working applied prior to the measurement, the stress level applied during the measurement of internal friction must be sufficiently small. The results of measurement are significant and can be used for a base of comparison only when the applied cyclic stress is so small that the internal friction is independent of stress amplitude. Internal friction of cold-worked metals under small stress level has been studied by a number of workers8 -" he internal friction was measured around room temperature with a frequency of vibration of the order of kilocycles per second. The purpose of this paper is to report a study of the change of internal friction when severely cold-worked aluminum was annealed at successively higher temperatures until it was completely recrys-tallized. The measurements of internal friction were made over a range of temperature extending from room temperature up to the temperature of prior anneal. The frequency of vibrations used was about one cycle per second. The apparatus used for the internal friction measurements to be reported in this paper was a torsion pendulum with the specimen in wire form as the suspension fiber. The description of this apparatus and the method of measurement have been previously given.7,8 The applied stress was sufficiently small SO that the magnitude of internal friction is independent of stress level at each temperature range concerned. Corresponding to this stress the maximum shearing strain on the surface of the specimen is of the order of l0-5 and lower. The in- ternal friction (Q-1) is reported as 1/p times the logarithmic decrement. Internal Friction Versus Temperature of Anneal: Fig. 1 shows the internal friction measurements performed upon 99.991 pct aluminum subjected to 95 pct reduction in area. The final diameter of the wire is 0.033 in. This figure gives a general survey of the effect of temperature of anneal and of temperature of measurement. The internal friction of the cold-worked specimen was first measured at room temperature. It was then annealed at 50°C for one hour and the internal friction measured at 50°C and at room temperature. The same wire was successively annealed at higher temperatures for one hour and measurements were taken at the annealing temperatures and lower temperatures as before. Such a procedure was followed in order to stabilize the internal friction at the temperature of measurement so that during the measurement which generally takes about half a minute, there is no detectable change in internal friction. This series of measurements .was made up to 450°C. After each annealing a short test piece of the specimen, which had received the same past thermal and mechanical treatments, was taken out for metallographic examination. It is seen from fig. 1 that up to the annealing temperature of 250°C we have the following observations: for any given temperature of measurement, the internal friction is lower the higher the temperature of prior anneal. When the annealing temperature is 290°C or higher, the internal friction at the annealing temperature drops abruptly to a value which is much smaller than that for the previous curve. Metallographic examinations showed that the recrystallization of the specimen was completed after the annealing at 290°C. Fig. 1 shows that, as far as internal friction is concerned, there is no abrupt transition between the processes of recovery and recrystallization. Averbach has also reached the conclusion that recovery may be a process analogous to recrystallization on the basis of X ray extinction measurements in brass." The effect of annealing temperature upon the internal friction at room temperature is shown by curve I of fig. 2. In this figure the internal friction at room temperature was plotted as a function of annealing temperature. It is seen that the internal friction decreases rapidly at first with an increase

Jan 1, 1951

By N. S. Stoloff, R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-Co and Fe- V alloys containing up to 25 pct solute have been studied in the temperature range 25° to - 196°C. The microyield stress is independent of temperature for all alloys studied, while the temperature dependence of the ordinary yield stress is large and comparable to that for unalloyed iron. An alloy-softening phenomenon is observed for many alloys relative to unalloyed iron, and appears to be a consequence of removal of inter-stitials from solution and their subsequent agglomeration. The ductile to brittle transition temperature is increased markedly by both cobalt and vanadium. Transmission electron microscopy observations reveal that cross slip and cell formation are restricted with increasing solute, which can account for many aspects of yielding and fracture behavior. IRON and other metals of bcc structure slip on many planes of the (111) zone at moderate and elevated temperatures, giving rise to wavy glide. At low temperatures, however, there is a tendency for slip to be restricted to planes of only one or two crystallographic types; in the case of Fe-Si alloys for example, (110) glide predominates, giving rise to planar slip bands."&apos; Restriction of cross slip at low temperatures in iron has been linked by Brown and Ekvall3 to increased strain hardening in the preyield microstrain region, leading to an apparently large temperature dependence of the yield stress. Support for this view has been provided by Lawley and Gaigher4 from a transmission electron microscope study of molybdenum. They concluded that dislocations at lower temperatures, by virtue of their inability to change planes readily, are unable to interact and annihilate, leading to an increase in internal stress and work-hardening capacity. Restriction of cross slip at low temperatures has also been suggested to be an important factor in determining the ductile to brittle transition of single-phase solids, including metals of bcc structure.5 It is pertinent to note that most solute elements tend to raise the ductile to brittle transition temperature of poly crystalline ferrite,6,7 although in some cases, e.g., Fe-Cr7 and Fe-Al,8 the dilute alloys may actually yield at lower stresses than unalloyed iron. It appears, therefore, that solute elements may have an effect analogous to lowering the test temperature with regard to restricting cross glide. Such an effect has indeed been observed in the ionic alloy system KCl-KBr,9 in which bromine atoms, although causing little misfit and consequently little effect on the yield stress of KC1, have a pronounced effect in restricting wavy glide and inducing brittleness. The purpose of the present investigation was to determine the effects of selected solute atoms on the yield stress and fracture behavior of iron, and to elucidate in turn how the slip character was related to these properties. Since it is known that interstitial atoms exert a strong influence on the mechanical behavior of iron, the solute elements chosen for study were vanadium, which reacts strong with interstitials,10 and cobalt, which does not form highly stable interstitial compounds." EXPERIMENTAL PROCEDURE Four-pound ingots of each of the following alloys were vacuum-melted in zirconia crucibles: Fe-1, 5, 10, 25 at. pct Co, and Fe-1, 4, 10, 20 at. pct V. An ingot of unalloyed iron from the same original stock as that used for the alloy was remelted under similar conditions to eliminate variations in interstitial content arising from differing thermal histories. Chemical analyses of the iron, cobalt, and vanadium melt stock are listed in Table I. All ingots were rolled and swaged, commencing at 850°C, to 1/4-in.-diameter bar. The bars were then annealed at 850°C for 1 hr (except that the 10 and 20 pct V alloys were heated for 2 hr) to give a uniform equiaxed grain size of about 0.05 mm. Tensile samples of 0.125 in. diameter by 0.8 in. gage length were utilized for studies of the ductile to brittle transition. A second set of tensile samples were utilized for microstrain experiments in which strain sensitivity of 1 x 10"6 was achieved by a capacitance method.3 Cylindrical compression samples 0.250 in. diameter by 0.4 in. long also were prepared to study the influence of composition on the macroscopic yield stress, and for metallographic analyses of defor-

Jan 1, 1965