By Hugh O?Neill

IN PREVIOUS papers,1 the author has reported the results of experiments on the straining in tension of a single crystal test piece, about 0.6 in. long, of vacuum-melted electrolytic iron containing 1.8 per cent. of silicon. The crystal was originally in the "as cast" condition, and was stressed slowly along a tetragonal axis so that slipping along conjugate gliding planes finally transformed the original cylindrical portion into a pair of fracture wedges. One of these fracture wedges was sectioned along the stress axis in a plane at right angles to the edge of the wedge. A metallographic study of this plane of -section led to the conclusion that slip had taken place in the (111) direction along (112) planes making a V shape with the stress axis. The present paper describes the results of scratch-hardness tests conducted on the same section, in order to determine the distribution of strain hardness therein, followed by annealing, and considers the resulting variations in hardness. These observations supplement those made by Krivobok2 on similar material reduced 25 per cent. by hammering (i. e., by impact) in the cold. In order to investigate ageing effects, two small crystals of the same alloy were also tested.

Jan 1, 1928

By O. F. Walker, W. C. Hahn, V. A. Johnson, J. D. Wood

The diffusion coefficients of zinc in single-crystal zinc and carbon in single-crystal and poly crystalline nickel were measured by means of radioactive tracer techniques both with and without the application of ultrasonic vibrations under conditions such that the temperature of the sample was closely controlled. The results of this investigation indicate no enhancement of diffusion in any of the samples. It is suggested that previously reported enhancement may have been due either solely to temperature increases caused by ultrasonic vibrations or in combination with changes in the boundary conditions. A number of observations have been reported in the literature in which it has been implied or inferred that the application of ultrasonics enhances diffusion (see, for example, Refs. 1-5). The present study was undertaken in an attempt to observe this effect under carefully controlled conditions, particularly with regard to measurement and control of the temperature of the sample. Two different types of systems were studied; these were the self-diffusion of zinc and the diffusion of carbon in nickel. EXPERIMENTAL For diffusion with ultrasonic energy applied, the samples were included as part of a resonant ultrasonic system operating at 58.5 kcps. The ultrasonic generators used were rated at 100 and 250 w and could be tuned over a frequency from 10 to 100 kc. A PZT (lead titanate/lead zirconate) ceramic transducer provided the driving vibration. This system requires no metallurgical joining of the specimen to the acoustical transmission line since the ultrasonic driver and the follow-up section clamp the specimen in position by means of a constant pressure of 50 lb developed by an air cylinder. The ultrasonic driver and follow-up section, both made of titanium, were 4 in. in length from clamping point to the end in contact with the specimen. Using the relationship given by Mason,6 A = V/f, the resonant wavelength, A, in titanium is calculated to be 3.3 in. at a frequency, f, of 58.5 kc, taking the velocity of sound in titanium, V, as 1.95 X 105 in. per sec. The 4-in. driver and follow-up section, therefore, are each 4.0/3.3 =1.21 times the resonant wavelength. Clamping pressure must be applied at stress nodes of the transmission line in order to preserve resonance. Therefore, a specimen length of 0.58 times the wavelength in the specimen was required to place the clamping pressure application points at stress nodes exactly three wavelengths apart. A stress antinode was contained in the center 3 in. of the specimen. A small PZT ceramic disc attached to the follow-up section provided an output voltage proportional to the intensity of the standing wave. This output voltage was monitored on an oscilloscope and the ultrasonic system was tuned to resonance by varying the frequency until the output signal was a maximum amplitude. The amplitude of the output signal was maintained constant throughout the diffusion anneal. A split cylindrical stainless-steel chamber, which was purged with argon prior to and during the runs, was placed around the specimen. The chamber in turn was surrounded by a movable furnace whose temperature could be controlled to 7C. Heat exchangers were used to cool the driver, follow-up section, and ultrasonic transducer. Great care was taken to obtain the true specimen temperature in all cases. Several different methods were tried; the most successful was that in which the thermocouple was held in contact with the midlength of the specimen by means of an asbestos insulating pad and wire straps. In the case of zinc, single-crystal specimens of 99.999 pct purity were used. The samples were 0.25 by 0.25 in. square and of the proper length for resonance, that is 1.1 in. long with the c axis parallel to the long dimension of the specimen for the case of diffusion perpendicular to the c axis and ultrasonic motion parallel to the c axis, and 1.9 in. long with the c axis perpendicular to the long dimension of the specimen for the case of diffusion parallel to the c axis and ultrasonic motion perpendicular to the c axis. In each case, one of the rectangular faces was electroplated with a thin film of zinc containing Zn The constant pressure used to clamp the specimen in place in the ultrasonic system caused some deformation in some of the samples. For these samples the deformation was concentrated in either end of the specimen; thus, for all samples (both zinc and nickel) the center in. was cut from the specimen after the diffusion anneal to be used for sectioning and counting. The nickel single-crystal samples, of 99.999 pct purity, were used in the form of rods 0.25 by 0.187 by 2.07 in. long with the (100) direction parallel to the rod axis. The polycrystalline nickel samples of 99.97 pct purity had an average grain diameter of 0.007 in. and were used in the form of rods 0.25 by 0.125 by 1.87 in. long. The direction of ultrasonic motion was parallel to (100) direction (bar axis) for the single-cqstal samples and parallel to the bar axis for the polycrystalline specimens. A thin film of c14 suspended in methanol was applied to the diffusing face of the specimen. Two specimens were butted together lengthwise for each diffusion anneal to minimize oxidation. After diffusion, a precision lapping device similar to the one described by Goldstein7 and a radiation detector were used to obtain a plot of specific activity vs penetration distance for each specimen. (A scintil-

Jan 1, 1969

By Stanley Rajnak, John E. Dorn

The saddle-point activation energy for the nu-cleation of a pair of kinks is estimated as a function of the applied stress, the lattice constants, and the height and shape of the Peierls' hill by employing the line-energy model of a dislocation. The kinetics of disloration motion by the Peierls' mechanism are discussed and the microscopic dislocation velocities and macroscopic strain rates are formulated by the Arrkenius type of approach in terms of the activation energy for the formation of pairs of PEIERLS was the first to illustrate that a straight-dislocation line has its lowest energy when it lies in a potential valley parallel to lines of closest packing kinks. The log of the dislocation velocity is found to be approximately proportional to the log of the local applied stress. It is also shown that the low-temperature mechmical properties of several bcc metals might be explained in terms of the Peierls mechanism, good agreement being obtained between theory and experiment for the flow stress us ternperature, activation energy vs stress, and activation volume us stress curves for these metals. of atoms on the slip plane. When such a straight dislocation is moved rigidly from one valley toward the next, the atoms in the vicinity of the core of the dislocation change their positions and bond angles, causing the energy of the dislocation to increase. Midway between two adjacent valleys, the disloca-tion energy reaches a maximum value and any additional small displacement will cause the dislocation to fall down the hill into the next valley. The maximum shear stress necessary to promote such

Jan 1, 1964

By V. Patarini, M. Salkind

BECAUSE of its high strength and stiffness coupled with low density, continuous boron filament is showing great promise as a potential reinforcement for both metals and nonmetals. Of primary consideration for structural applications is the fatigue behavior of boron fiber composites. Composite fatigue behavior is dependent upon three factors: 1) fiber fatigue behavior, 2) matrix fatigue behavior, and 3) the effect of the interface and fiber ends. The purpose of this note is to describe the behavior of boron filament in rotating beam fatigue. The filament, described by Talley' and Galasso, Salkind, Kuehl, and Patarini,' was made by the hydrogen reduction of boron trichloride on a hot tungsten filament. Testing was performed using a commercial rotating beam wire fatigue tester* described by Votta.~ One end of the test sample is held in a chuck in a synchronous motor. The sample is bent around in a "U" shape, and the other end inserted into a carbide bushing. The maximum strain occurs at the bottom of the "U" where the radius of curvature is a minimum. The strain is adjusted by adjusting the length of the specimen and the location of the bushing. Samples were rotated at 3600 rpm and an automatic shutoff device used to determine the number of cycles to failure. The measurements were accurate to the nearest 360 cycles. The fatigue behavior is summarized in Fig. 1 for fifty-one samples of 4.8 x 10"3 in. diam fibers and ten samples of 3.2 X 10"3 in. diam fiber. The two sample groups represent two different filament production runs and two different nominal size groups. Both groups exhibited nominal tensile strengths of 400,000 psi. No significant difference in the fatigue behavior of the two sample groups is apparent. The scatter in the data is not unexpected for a brittle filament which exhibits a tensile strength distribution with a standard deviation of 10 to 15 pct. Because the test procedure provides a known outer fiber strain in the sample, the maximum stress was calculated assuming a Young's modulus of 58 x 10' psi. This value was selected as being representative of several nominal fiber sizes.2 All of the samples which failed exhibited sudden, catastrophic fracture, and no permanent deformation. One sample was stopped after 1.66 x lo8 cycles at *200,000 psi. The fiber exhibited no apparent damage or deformation. It is apparent that the fatigue resistance of boron filament is quite good. It can therefore be speculated that the fatigue behavior of boron fiber composites would be controlled by the "weaker links", namely matrix fatigue resistance and interface behavior. In fact, preliminary investigations have revealed that this is true for boron-reinforced aluminum? It should be noted that the data presented herein may not necessarily reflect the tensile fatigue behavior of boron filament. It is well-known that boron filament has a radial residual stress pattern with the outer surface in ~om~ression.~ Because of this fact, tensile failure is normally nucleated in the interior of the filament.5 Since the data presented herein is for a rotating beam test in which only the outer surface of the fiber is stressed to the maximum value, it would be incorrect to assume that the failure mechanism and fatigue behavior would be the same if the fiber were tested in tensile fatigue. The fact that many of the data are well above the nominal 400,000 psi tensile strength would tend to support this argument. The authors would like to express their appreciation to the United Aircraft Research Laboratories for supporting this investigation and for permission to publish the results. A portion of this effort was supported by the Air Force Materials Laboratory under contract AF33(615)-2125.

Jan 1, 1968

By G. Abowitz, R. B. Gordon

The velocity of sound, mass density, and thermal expansion coefficient were measured in dilute lead, tin, zinc, bismuth, cadmium, indium, and potassium amalgams as a function of composition. Measurements in the Hg-TI system extended ovev the wider range of composition, 0 to 40 at. pct TI. The sonic velocity was measured as a function of temperature. The calculuted adiabatic compressibility in all cases was found to decrease much more rapidly than would be expected on the basis of a linear variation with composition. An interpretation of the results is given in terms of changes in the Debye characteris -tic temperature of mercury on alloying and a possible change in the bonding of mercury itself. If a liquid is considered as an isotropic elastic medium, the phase velocity of a longitudinal elastic wave traveling in the liquid is given by where K is the bulk modulus, G the shear modulus, and d the mass density. G can be neglected for liquids of ordinary viscosity, i.e., approximately 1CT2 poise, because the shear stress component is relaxed essentially at once. That is, for liquids of ordinary viscosity and at frequencies of the applied stress up to several hundred megacycles, the relaxation time of the shearing process is much shorter than the period of the applied stress. Eq. [I] then reduces to The adiabatic rather than the isothermal compressibility is measured at the megacycle frequencies used in ordinary ultrasonic velocity measurements. The sonic velocity and compressibility have been determined for many organic liquids and aqueous eletroltes,' and the results have been interpreted in terms of existing theories for these fluids. The velocity of sound and compressibility are important parameters in theories of the liquid state. For example, equations of state have been proposed relating the free volume of liquids to the acoustic velocity.3 Comparatively very little work has been done on the acoustic properties of liquid metals and alloys. leppa,' orddon, and several other investigators

Jan 1, 1963

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

IN THE past year, Jaffee and Campbell&apos; and Finlay and Snyder2 reported on the mechanical properties of titanium-base alloys, some of which were in the same ranges of composition as are covered in this paper. In this paper, evidence confirming that given by Finlay and Snyder on the effects of carbon, oxygen, and nitrogen on titanium will be presented; and, in addition, new data will be given on the effects of these elements on the flow properties and phase transformation of titanium. Materials and Preparation of Alloys The preparation and general properties of iodide titanium have been adequately described elsewhere.&apos; , As-deposited iodide titanium rod, prepared at Battelle, of Vickers hardness less than 90 was employed as the base metal in the present work. This was the same material as that used by Finlay and Snyder.2 The probable analysis reported by them for standard quality metal holds here also: N 0.005 pct, 0 0.01 pct, C 0.03 pct, Fe <0.04 pct, A1 <0.05 pct, Si <0.03 pct, and Ti 99.85 pct. Carbon was added in the form of flake graphite supplied by the Joseph Dixon Crucible Co. Oxygen was added in the form of c.p. grade TiO, powder, produced by J. T. Baker Chemical Co. Nitrogen was added in Ti3N4 powder, supplied by the Remington Arms Co. Individual ingots weighed 7 or 8 g. Carbon, oxygen, or nitrogen was added by placing the corresponding powder in a capsule made from as-deposited iodide titanium rods and melting the capsule with the balance of the charge. The charge was are-melted with a tungsten electrode on a water-cooled copper hearth under a partial vacuum of very pure argon (99.92 pct minimum). Melting was practically contamination free. Vick-ers hardness increases of less than 10 points were normal for unalloyed iodide titanium control melts. Nitrogen analyses of are-melted iodide titanium showed a nitrogen content of 0.005 pct, about the same as is present in the as-deposited rod. No tungsten pickup was found in a melt of iodide titanium analyzed for tungsten. Weight losses in melting nitrogen-free alloys were very small and varied consistently from nil to 0.015 g (0 to 0.2 pct). This permitted the use of nominal composition for these alloys. Chemical analyses made for carbon, which can be analyzed conveniently by combustion methods, justified this procedure. Where nitrogen was added, considerable splattering took place. Here it was necessary to analyze for nitrogen by the Kjeldahl method. The ingots were hot rolled at 850°C to about 0.045 in. thick. After hot rolling, the strips were descaled by mechanical grinding, and then given a cold reduction of 5 to 10 pct to insure a uniform thickness throughout the length of the specimen. The edge strips and the tensile strips were annealed in a vacuum of 1x10-4 mm Hg pressure for 3 1/2 hr at 850°C and furnace cooled. Methods of Investigation Hardness Measurements: At least five Vickers hardness measurements were taken using a 10-kg load on each sample in the following conditions: (1) top and bottom of each ingot, (2) top and bottom surface of as-rolled and annealed sheet, and (3) on cross-section of annealed sheet and all quenched specimens. Tensile Tests: Tensile tests were conducted on Baldwin-Southwark testing machines having load ranges of 600 or 2000 lb. Tests were made on 1-in. gauge-length specimens, 3 1/4-in. overall length, 1/2 in. wide, 0.040 in. thick, with a reduced section 1 1/4 in. long and 0.250 in. wide. Two SR-4, A-7 strain gauges, one mounted on each side of the specimen, were used to measure the strain over a limited range to determine the modulus of elasticity. After the modulus of elasticity readings had been taken, load vs. strain readings were taken, using only one strain gauge, at increments of 0.0001 in. until the yield points were passed and then at 0.001-in. increments to the limit of the strain-gauge indicator (0.02 in.). Strain readings above 0.02 in. per in. were taken every 0.01 in., using dividers to measure the strain between the 1-in. gauge marks until the maximum load had been reached. Crosshead speed, when using the SR-4 gauges, was 0.005 in. per min, and, when using dividers, 0.01 in. per min. Flow Curves: Flow curves were determined using the true stress-true strain data obtained during the tension test. The usefulness of this type of information has been dealt with very adequately elsewhere by L. R. Jackson,&apos; J. H. Hollomon,6 and many others. Flow curves of true stress vs. true strain could be converted to the more conventional cold-work curve of 0.2 pct offset yield strength vs. percentage of cold reduction by means of the transformation, 1/1 = 1/1-R, where R is the fraction reduction in cold working. Thus, the true strains corresponding to percentage reduction can be calculated, and the 0.2 pct offset yield strengths scaled off the — 6 curve by taking the true stresses corresponding to the values of 6 + 0.002 strain. Heat Treatment: For the transformation studies, the alloys were heat treated in a horizontal-tube furnace using a dried 99.92 pct argon atmosphere, and quenched into water. Essentially no contamination was found after several hours of heat treatment at temperatures up to 1050°C. Metallography: Specimens were prepared in the

Jan 1, 1951

By F. W. Jessen, N. Mungan

The plastic flow characteristics of clay water suspensions were first recognized by Binghaml in 1916 and further studied by Ambrose and Loomis&apos; in 1931-1932. Many physical and chemical properties of clay suspensions are deeply influenced by particle size distribution as well as by the exchange cation. Separation of a number of fractions is particularly helpful in making a detailed study of a suspension. A limited amount of work has been conducted on the effects of particle size on specific properties of mud drilling fluids. A knowledge of particle size distribution is essential for a better understanding of fundamental properties of clay suspensions, particularly viscosity and gel strength. The purpose of this investigation was to study the effect of particle size on the viscosity and gel properties of clay suspensions and to determine any changes in mineral composition accompanying variation in size. EXPERIMENTAL PROCEDURE Numerous methods may be used to fractionate a poly-dispersed clay suspension into nearly mono-dispersed systems. Particles larger than 44 micron (325-mesh) may be obtained by wet screening. For sizes from 44 to 1 micron, the fractionation may be accomplished by sedimentation, elutriation plus microscopy,&apos; or turbidimetry.6 When dealing with systems which contain a major portion of particles below l-mi-cron size, slit ultramicroscopy,7 centrifuge methods of Svedberg,5 eams,9 and McBain,l0 and X-ray methods" may be employed. The Sharples super centrifuge has been proved suitable for the economical separation of suspended particles of submicron range.12,13,14 Three-hundred and forty-five gal of 1 per cent by weight Aquagel suspension was mixed in a high-speed 5-gallon mud mixer and the suspension was allowed to stand in 5-gal glass bottles for 30 days to assure full hydration. All particles larger than 44 microns were removed by wet screening. Five fractions in the range of 44 to 1 micron were obtained by sedimentation. The Sharples super centrifuge method described by Hauser and Reed.13 Norton and Speil,14 Ha user and Lynn,15 and Hauser and Schachman,10 as employed to yield five fractions of submicron size. A super centrifuge operation chart prepared by Fancher, Oliphant, and Houssierre12 was used to determine operating conditions for the desired particle ranges. The clay suspension, after removal of all material above 1-micron size, was centrifuged. During rotation of the bowl, the particles were deposited on a thin plastic liner which fit closely inside the bowl. After passing 5 gal of suspension through the centrifuge, the liner was removed and the particles on the liner were scraped off, remixed and recentrifuged. This was repeated five times. Thus, Fractions H, I, K, and L were obtained. The finest fraction, M, remained in an approximately 0.4 per cent suspension. Water was evaporated under reduced pressure from this suspension to yield the finest particles. Results of the fractionation are included in Table 1. In order to achieve proper orientation and humidity conditions for X-ray diffraction analysis, the following procedure was employed. The dilute suspensions were placed on glass slides and allowed to dry at room temperature. This was repeated several times. Previous to measurement each sample first was placed in a water desiccator for half an hour and then allowed to stand for 15 minutes at room temperature. thus yielding an equilibrium condition of about 52 per cent relative humidity. The relative humidity of the room in which the X-ray diffraction was carried out was maintained at approximately 50 per cent so that there was no change in the spacings during the X-ray examination. Samples

By S. K. Asunmaa, W. D. English, N. A. Tiner, W. A. Cannon

This paper discusses the reaction of metal surfaces with fluorine. Fluorination reactions result in the formation of metal fluoride films which are "passive" toward further reaction of the metal with fluorine. These films are very adherent, and do not easily detach from the substrate metal by mechanical flexing or thermal shock. Exposure of passive films to a humid atmosphere produces hydrated metal fluorides which cause secondary fluorination reactions upon reexpo-sure of the metal surface to fluorine. The surface films formed range from 10 to 30A in thickness and they pow at the expense of surface oxide films. The apparent film formation is completed rapidly in 15 to 30 min on stainless steel and nickel surfaces. On copper and on Monel surfaces, the film at first grows rapidly, then increases slowly over an extended period of time. Passive films are formed at all fluorine pressures in the range from 0.1 to 1.4 atm at room temperature. ALL metals react when exposed to fluorine. These reactions generally produce surface films which consist of metal fluorides. The rate of reaction is largely determined by the extent to which these films are protective. Although there is an extensive literature concerning reactions of oxygen with metals, there are very few investigations reported concerning fluorine-metal reactions. Brown, Crabtree, and ~uncan&apos; investigated the kinetics of the reaction of gaseous fluorine with copper metal which had been freshly reduced in hydrogen. The reaction rate was independent of pressure over the range from 6 to 60 torr. A logarithmic rate law was obeyed in the temperature range from 25" to 300" ~. There was some deviation at higher temperatures which could have been the onset of a parabolic law. The calculated film thicknesses ranged from about two molecular layers, 10A, for 5 hr exposure at room temperature to thirty-five molecular layers for 5 hr exposure at 200" . The authors concluded that no single mechanism could explain all the observations. O7Donnell and spatkowski2 studied the reaction of fluorine with copper at 450°C at pressures from lo to 133 torr. The reaction was found to be pressure -dependent and followed a logarithmic rate law. It was not entirely diffusion-controlled, and fluorine was thought to be the migrating species in the reaction. Miscellaneous metal-fluorine reactions were investigated by Haendler et ~1.~ Reaction products were identified but no rate data were determined. Air Prod- ucts and Chemicals, Inc., have conducted an investigation of reactions between fluorine and various metal powders at room temperature and 85° C. Fluoride film thickness as a function of time of exposure was reported on the assumption that the reaction takes place between fluorine and metal to form the normal metal fluoride. Surface areas of the powders were only estimated so the relative film thicknesses may not be exact. The data showed reaction rates which were generally logarithmic in character, the rate of film growth virtually ceasing after a few hours exposure time for some alloy powders. The effect of moisture on fluoride films was also investigated by measuring additional reaction with fluorine after exposure of passivated powders to atmosperic moisture. The fluorination of iron was studied by 0&apos;~onnell~ at temperatures from 225" to 525" ~ and at pressures ranging from 20 to 200 torr. In all ranges, the reaction followed a logarithmic rate law and was dependent on the square root of the gas pressure. The author concluded that fluorine gas passes through pores in the film. As the film grows, the blocking of pores leads to a rapid decrease in reaction rate; hence a logarithmic rate law is observed. Jarry, Fischer, and Gunther&apos; investigated the mechanism of the reaction of fluorine with nickel at about 600" to 700°C. On the basis of the metallographic examination of fluoride scales growing on the nickel and from separate radioautographic data, it was claimed that fluorine is the migrating species in the reaction. This is in sharp contrast to the growth of oxide films on nickel where it has been shown that nickel ions migrate through the scale to the gas-solid interface to react with oxygen. Few investigations have been reported of the reaction of fluorine with metal oxides. Such investigations should be of great significance for a better understanding of passivation in view of the ubiquitous oxide films on technical alloys. Haendler et al.3 studied the reaction of fluorine with oxides of copper, tin, titanium, zirconium, and vanadium. Copper (I) oxide reacted as follows in the temperature range 150" to 300"~: temperature above 300" ~ was required for the CuO to react to form additional copper fluoride. Ritter and smith7 also investigated the reaction of fluorine with copper (11) oxide. An oxide powder comprised of spherical particles with a fairly high surface area was reacted with fluorine, starting at room temperature and increasing to 100° C over a period of 3 or 4 hr. The initial reaction was slow until the fluoride film thickness reached about to or 15R at which time the reaction rate accelerated, then decreased again. Most of the kinetic data was obtained during this final phase of reaction. The authors conclude that the film grows slowly at first until the stresses developed in the distorted lattice are sufficient to rupture the initial

Jan 1, 1969

By E. S. Wheeler

The conversion plant of the Clirnax Molybdenum Co. is at Langeloth, Washington . County, Pennsylvania, approximately 30 miles west of Pittsburgh. The molybdenite concentrates converted originate in the company&apos;s mine and mill at Climax, Co1orado.l They are delivered to the Langeloth plant by rail packed in 175-lb. bags. War production of concentrates at the mill started in 1918 but it was not until about 1920 that any peacetime uses of the metal began to develop. Early conversion of Climax concentrates was mainly into ferromolybden um, produced for the company by a custom smelter. Chronology of Plant Development In 1924 a small hand-rabbled roaster was built at Langeloth, the roasted concentrates being used principally in the production of calcium molybdate by a conventional wet method. The size of the original plant is indicated by the fact that during 1925 about 400,000 lb. of molybdenum was converted. In 1925-1926, a multiple-hearth roaster was erected (12-ft. 0.d. 8-hearth Nichols-Herreshoff); also the first experimental ferromolybdenum was produced at Langeloth. At this time sa.1cium molybdate was produced in the furnace by a process to be described. With continued interest in and increased use of molybdenum, it was necessary to arrange for enlargement of plant facilities. Although only one 12-hearth 16-ft. 0.d. roaster was erected at this time (1929), plans were prepared for a duplicate unit, which was completed in 193 5, giving a potential roasting capacity of some 16,000 lb. Mo per day under the then prevailing roasting practice. Shortly after this second unit had gone into production, increased demand overtaxed the plant, and as a result two 12-hearth 18-ft. 0.d. roasters were placed in operation in 1936 and 1937. This gave the plant a potential roasting capacity of 40,000 to 50,000 lb. Mo per day, and necessitated major changes in auxiliary handling equipment as well as improved facilities for producing ferromolybdenum. Following the introduction (1938) of a new product—molybdic oxide briquets— and because of the constantly growing demand for molybdenum, plant facilities were again enlarged in 1940 and 1941 by the erection of two 16-hearth 18-ft. 0.d. roasters. These two new units, along with a change in roasting practice, brought the potential roasting capacity to 150,ooo to 190,000 Ib. Mo per day, based on about 15 lb. per sq. ft. of hearth area. Other departments of the plant have necessarily grown, until today the plant is modern throughout and completely mechanized, with equipment geared to produce marketable products as follows:

Jan 1, 1944

By T. A. Rickard

The history of this State is that of one generation. Thirtysix years only have elapsed since the birth of that beneficent industry whose footsteps were the first to traverse the wilderness of the prairies and penetrate the solitude of the mountains. So soon is history made. The men who halted on the rolling plain where Denver now stands and gazed westward at the snow-clad ranges in eager questioning of their possibilities of golden wealth, have lived to see a noble city built where once their camp-fires burned, and have participated in the discovery of a magnificent series of productive mines amid the mountains which seemed at that time the Ultima Thule of their pilgrimage. To those who investigate the workings of our complicated mining and metallurgical industries, the story of their evolution from humble beginnings will appear an instructive romance. The record that tells it presents features common to the growth of modern mining regions, but also bears aspects peculiar to

Jan 1, 1897

By T. V. Philip, Paul A. Beck

IN a previous note1 it was pointed out that the available information suggests a distinct correlation between the occurrence of the CsCl-type ordered structures formed in equi-atomic binary alloys of transition elements and the location of the components in the periodic table. A definite increase in the bond strength between unlike atoms, as compared with that between like atoms, is indicated when, in binary alloys of iron group elements, the other component is changed from chromium to vanadium or tantalum, to titanium. Laves and Wallbaum,2 eported a CsCl-type ordered structure for the stable intermediate phase at the equi-atomic composition in the Ti-Fe system (and also in the Ti-Ru and Ti-Os systems). On the other hand, Tagaya, Nenno, and Nishiyama8 found no ordering of this kind in the body-centered-cubic solid solutions in the Cr-Fe system. It was concluded&apos; that the occurrence of a CsC1-type ordered phase of intermediate stability may be expected in the V-Fe system. Preliminary results were described: suggesting that at least some degree of order does exist in the equi-atomic alloy VFe, annealed at 1200° C and quenched in cold water. Using CrK radiation, at least one weak superlattice line was found in the X-ray diffraction pattern which could be indexed as (100). and which disappeared, as expected, when FeK radiation was used. It was found more recently that the impurity phase (presumably VN), previously giving rise to additional X-ray diffraction lines and thus preventing definite indentification of the (111) superlattice line,&apos; can be eliminated by preparing the alloy by arc melting in a helium atmosphere. The alloy specimen melted in this manner had clean surfaces and showed very littte, if any, nitride phase in the microstructure after annealing in vacuum at 1250°C and quenching. The relative intensity of the (100). superlattice line with CrK radiation was greatly increased and, in addition, a fairly strong (Ill) , superlattice line and even a detectable (210) , super- lattice line was obtained, when the powder produced by filing from the 1250°C annealed and quenched specimen was reannealed in vacuum at 625°C for 1 hr. By using a cellulose acetate film as a filter in front of the photographic film in order to absorb the soft radiation resulting from air fluorescence, the background intensity could be reduced considerably in relation to the intensity of the diffraction lines. All three superlattice lines, (100),, (111)., and (210)a, disappeared, as expected, when a radiation other than CrK, was used.1 For the powder reannealed at 625ºC, the strongest lines of the s pattern also appeared weakly, indicating that during an: nealing at 625°C a small amount of transformation took place from the body-centered-cubic to the u phase. However, since all superlattice lines to be expected in the 0 angle range used were actually very clearly present, it was evident that the high temperature body-centered-cubic phase had transformed into a CsCl-type ordered structure before much s phase could form. Reannealing filings for 1 hr at 700°C resulted in complete transformation into the u phase. After 1 hr at 650°C the transformation into IT was not quite complete, the strongest body-centered-cubic diffraction lines were still present, although fairly weak, and only the (100), super-lattice line was detectable (extremely weak). These findings not only confirm the previous conclusionsL as to the existence of a CsCl-type ordered structure in the Fe-V system, but they also indicate that this metastable ordered structure forms at about 600°C preceding the formation of the stable s phase, while at 1250°C the disordered body-centered-cubic phase is stable. The faint (loo) , super-lattice line previously observed in specimens quenched from 1200°C was probably due to the fact that the quenching of the powder in an evacuated fuse:! quartz capsule was not fast enough to prevent completely the ordering reaction on cooling. The present results conform with the suggestion that the A-B bond, in relation to the A-A and B-B bonds, increases in strength from CrFe to VFe to TiFc. It is, therefore, of interest to compare the measured values of the average atomic diameter for these three alloys with the corresponding average atomic diameters calculated from the atomic radii of the elements concerned. ASSUming A-B contacts

Jan 1, 1958

By G. Thodos, R. B. Grieves

A method has been developed for the accurate calculation of the cricondentberm and cricondenbar temperatures of multicomponent hydrocarbon mixtures of known composition. The mixtures may contain any number of components including paraffins and isoparaffins, olefins, acetylenes, naphthenes and aromatics. This approach is based upon the mole fraction of the low-boiling component in the mixture and graphically presents the ratios of the cricondentherm and cricondenbar temperatures to the pseudocritical temperature as {unctions of a boiling-point parameter. The only requirements are the critical temperature, normal boiling point and the approximate vapor pressure behavior of each component. For mixtures of more than two constituents a stepwise calculation procedure is necessary where the pseudocritical temperature is based upon the critical temperature of the pure low-boiling component and upon the actual cricondentherm or cricondenbar temperature of the mixture of all the remaining higher-boiling components. From an analysis of 22 binary systems (123 compositionsl, the average deviation of calculated cricondentherm temperatures from reported values is 0.87 per cent, based on degrees Rankine; and for 10 multicomponent mixtures containing from three to six components, the average deviation is 0.98 per cent. From an analysis of 18 binary systems (104 compositions) the average deviation of calculated cricondenbar temperatures from reported values is 0. 79 per cent; and for 15 multicomponent mixtures, 1.47 per cent. Equations, derived from the graphical relationships, are presented which enable rapid calculations for both binary and multicomponent systems. INTRODUCTION With the increasing tendency towards the use of high pressure processes, the need for an accurate method of calculation of the properties of a multicomponent hydrocarbon mixture in the critical region is becoming more essential. Critical region phase relations are also significant in gas condensate reservoirs, for which a knowledge of the fluid phase boundaries and regions of retrograde condensation make it possible to evaluate optimum operating conditions. The possibility of liquefaction in the underground structure may be established, and information on the feasibility of the use of repressurizing may be determined. A typical phase diagram for a multicomponent hydrocarbon mixture is presented as Fig. 1. This figure also shows the regions of retrograde behavior encountered by following lines AB and AC. If accurate methods of calculating the temperatures and pressures at the critical, cricondentherm (maximum temperature) and cricondenbar (maximum pressure) points of multicomponent hydrocarbon mixtures of known composition were available, it would be possible to estimate closely the entire phase diagram of any mixture. Several methods have been presented in the literature for the estimation of the critical temperatures and pressures of multicomponent mixtures containing all types of hydrocarbons and including the fixed gases.4-8,21 Considering the cricondentherm and cricondenbar points, the work is more limited. Etter and Kay5 have developed rather complex equations for

By W. B. Morrison

The principal factors influencing the total percent elongation of a lead-tin eutectic and several low-alloy steels which exhibit superplasticity were investigated. These factors are: a) Strain-rate sensitivity of the stress (m). b) Specimen geometry; in particular, diameter-to-length ratio (d0/l0), and surface irregularity (e.g. notches). A feature of the tensile deformation of a superplastic alloy is the early appearance of a neck which continues to extend throughout the test. As a result the total elongation is directly related to the diameter-to-gage-length ratio. The strain-rate sensitivity of the stress varies during extension, mainly because of microstruc-tural changes. A satisfactory correlation exists between the minimum strain-rate sensitivity and total elongation, as indicated in the equation shown below. Notches cause a considerable reduction in total elongation and their effect is greatest at high values of strain-rate sensitivity. An initial notch depth exists below which there is no appreciable effect on elongation. An equation relating elongation to strain-rate sensitivity and specimen geometry is proposed, THE total percent elongation of a tensile specimen is usually regarded as a measure of superplasticity. However, little attention has been given to the fact that total elongation is also a function of specimen diameter and gage length, even though the importance of geometry has long been recognized in the tensile testing of materials in which elongations are relatively small.* In the present study, the effect on superplas- tic extension of the ratio of specimen diameter to length was investigated and an analysis was made of strain distribution along the gage length. Superplastic alloys are characterized by having a flow stress sensitive to strain rate but relatively insensitive to strain.2"&apos; In an earlier study,5 it was found that the strain-rate sensitivity of several low-alloy steels changed during the test and that the minimum value correlated best with total elongation. In the present study, the variation of strain-rate sensitivity during the straining of a lead-tin alloy was investigated. EXPERIMENTAL PROCEDURE Lead-tin eutectic alloy (32 pct Pb 68 pct Sn), made from high-purity lead and tin, was cast in the form of 1-in. diam rod. The rod was cold-rolled in stages to 0.25 in. diam and then swaged to 0.125 in. diam. Samples were cut from the rod at various stages of the mechanical working process. Tensile test specimens were then made by attaching threaded steel ends to the rods by an epoxy-base thermosetting adhesive which required a setting treatment of 2 days at room temperature. The rods were seated in the steel ends in holes approximately 0.01 in. oversize. The test pieces thus made were of various diameters and gage lengths. These were stored at a temperature of about -70°C (-94°F) until required for testing. The distribution of strain along the gage length of a specimen was determined at various stages of the tensile test. The lead-tin alloy was superplastic at room temperature and direct observations during testing were simple. The gage length was divided by reference marks into five initially equal units. These reference marks were made with ink and were reinforced during the test when the initial marks became faint. Photographs were taken, at intervals, of the deforming specimen and measurements of the elongation in each of the gage units were made on these photographs. Tests were also done on several superplastic low-alloy steels whose properties were described earlier.5 The chemical compositions of these steels are given in Table I. A diagram of the notched tensile specimen used in the steel tests is shown in Fig. 1. The specimens were tested at 900°C (1650°F) in a furnace through which a mixture of He + 2 pct H was continuously circulated.5 RESULTS Strain Distribution. Approximately 20 tests on lead-tin alloy specimens were conducted to determine the strain distribution during the test. An example is shown in Fig. 2 of the strain distribution in the gage

Jan 1, 1969

By A. T. Yu

On March 18, 1964, the 52,000 dwt ore carrier M/S Houn Maru called at the port of Coquimbo, Chile, on its maiden voyage to take iron ore to Japan. This marked the first time a vessel of this size ever arrived at Coquimbo, and the event promises to drastically accelerate henceforth iron ore exports from Coquimbo province. This was made possible by the use of a versatile shiploading system recently installed by Cia. Minera Santa Fe. Coquimbo has no mechanized loading facilities other than six conventional 5-ton cargo cranes. Limited space on shore further complicates the stocking problems. To make the best of what is available, a meticulously organized semi-hand-loading system has been developed through the years.

Jan 5, 1964

By Oswald J. Heinrich

(with figures on plate V.) THE origin of spontaneous combustion in collieries is, of course, chiefly due to bad system in laying out the pits, unclean workings, insufficient ventilation, and neglect in damming off works after they are exhausted of the main coal. This is particularly indispensable in the Richmond field, because it is difficult and dangerous here, on account of the inferior roof, to remove the last vestiges of coal ; and we are compelled also to retain all the slates and bands, as far as possible, in the pit, to help fill up, although such material is liable to fire. This, however, can be prevented to a great extent, as men¬tioned below. I am satisfied that the only system of working this thick coal is by cross-cutting ( Querbau, ouvrage à travers) or working in benches, as practiced in France (Creusot, Rive de Gier, St. Etienne), in Sile¬sia (Königsgrube), which I have used as far as it is practicable in an old pit, almost torn to pieces by former workings. Modifications may, of course, be needed, even in the same pit, on account of irregu¬larities in the seam. I am also satisfied for economical reasons (on account of the heavy cost for timbering) that pits here ought to be worked upwards, even if it requires a longer period of time to win the coal, and a greater outlay of capital to commence with. The various saddle-shaped "troubles" making natural minor basins in the main basin aid in the execution of this plan. A pit worked once ought to be worked out clean, given up, and dammed off forever. If sections of proper height are assumed, according to the required amount of production for a certain period of time, they ought to be worked out and filled in as much as possible, dammed off, and ulti¬mately allowed to fill up with water, in order to protect the tipper works in future from fire in the gob below. This I consider indispen¬sable, because we may not be able profitably to fill in all the ground. To do so we have to use the waste of the mine, although it is liable to fire in time. In using this stuff, it ought to be surrounded by walls of rock not liable to take fire, laid firmly in clay, the gob being in the middle, and firmly covered and packed with clay on top. In

Jan 1, 1873

COUNCIL OF ECONOMICS OF AIME Formerly Mineral Economics Division Established as a Division December 15, 1948 Established as a Council February 26, 1957 Douglas Donald, Chairman Sheldon Wimpfen, Vice-Chairman (Mining) A J Phillips, Vice-Chairman (Metals) E Connaughton, Vice-Chairman (Petroleum) J S Vanick, Contact AIME Director A H Lindley, Jr Secretary-Treasurer Lehman Brothers 1 William Street New York 4, N Y COUNCIL OF EDUCATION Formerly Mineral Industry Education Division Established as a Division January 15, 1932 Established as a Council February 26, 1957 L E Shaffer, Chairman J D Forrester, Vice-Chairman O Cutler Shepard, Past Chairman , Contact AIME Director

Jan 1, 1959

COUNCIL OF ECONOMICS, AIME Formerly Mineral Economics Division Established as a Division December 15, 1948 Established as a Council February 26, 1957 Sheldon P Wimpfen, Chairman John D Ridge, Vice-Chairman (Mining) A J Philips, Vice-Chairman (Metals) Warren B Davis, Vice-Chairman (Petroleum) COUNCIL OF EDUCATION, AIME Formerly Mineral Industry Education Division Established as a Division January 15, 1932 Established as a Council February 26, 1957 James D Forrester, Chairman Charles V Kirkpatrick, Vice Chairman (and Chairman-elect) Lysle E Shaffer, Past Chairman Truman H Kuhn, Secretary-Treasurer Colorado School of Mines Golden, Colorado John S Bell, Contact AIME Director

Jan 1, 1960

By GEORGE D. RAMSAY

WHEN the Ironton blast furnace of the Columbia Steel , Co. was first put into operation the iron ore was mined frol11 the deposit near Iron Springs, Utah. This is principally a hematite with 12 to 20 per cent of magnetite finely disseminated throughout the ore. It varies from a fairly soft broken rock structure to that which is hard and compact. In the broken form it will weigh about 150 lb. per cu. ft., and in place the density is approximately 250 lb. per cu. ft. The first ore received for the blast furnace was crushed so as to pass through approximately a 4-in. square opening screen. A typical screen test of this ore is shown in Table 1.

Jan 1, 1935

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The kinetics of crack propagation in a hydrogenated high-strength steel at subzero temperatures indicated that cracking progressed in a discontinuous fashion. The delayed failure process thus involves a series of crack initiations rather than the continuous growth of a single crack. The incubation time required for the initiation of delayed failure was controlled by the diffusion of hydrogen. The activation energy for the process was 9120 cal per g-alom. As the test temperature was lowered the incubation time constituted a greater percentage of the total tinze to fracture, and al -50°F the incubation and fracture times were essentially coincident resulting in instantaneous, catastroplzic fracture. A unique feature of hydrogen embrittlement is the delayed failure process in which the material fails under the action of a sustained load even though it is capable of supporting a higher load for a finite period of time.&apos;)&apos; Delayed failure of steel and titanium is characterized by an incubation time, preceding the initiation of a crack in a highly localized region, and the subsequent growth of the crack to ultimate failure.3-5 The kinetics of crack growth in hydro-genated high-strength steels have been studied through the use of resistance measurements and have an important bearing on the mechanism of delayed failure. Delayed failure is believed to be merely a facet of hydrogen embrittlement in which sufficient time is allowed during a test for hydrogen diffusion. The current theories employed to explain hydrogen em-brittlement can be grouped into two types. one6-8 explains the embrittlement on the basis of the pressure exerted by molecular hdrogen in lattice voids or defects while the other9-10 attributes the embrittlement to the influence of hydrogen in the lattice. The mechanism used to explain the nature of the crack kinetics in delayed failure is based on the stress-induced diffusion of hydrogen to the area of maximum triaxiality.3 When the hydrogen concentration in this region reaches a critical value, a crack is nucleated. This initial crack propagates instantaneously until stopped by the higher fracture stress of the adjacent material of lower hydrogen content. The continuation of cracking must then await the further diffusion of hydrogen to the new region of triaxiality near the base of the crack where another initiation will occur. From this mechanism it follows that crack propagation is nothing more or less than a series of initiations with limited fracture. The purpose of this investigation was to examine the kinetics of crack growth in an effort to determine whether or not the process was discontinuous. Studies of crack propagation were conducted at low temperatures to retard the diffusion of hydrogen which is presumed to be the rate controlling process in delayed failure. MATERIALS AND PROCEDURE Specimen Preparation—A commercial heat of air-craft quality SAE-AISI 4340 steel, designated as Heat G, was furnished by the Republic Steel Co. in the form of %-in. hot-rolled bars. The material had the following chemical analysis: Composition of 4340 Steel—G Heat C Mn Si Ni Cr Mo 0,395pct 0.82pct 0.29pct 1.76pct 0.85pct 0.25pct Notched tensile specimens with less than a 0.001 in. radius, Fig. 1, were used throughout the investigation. The specimens were heat treated to a 230,000 psi strength level according to the following sequence: a) Normalize bar stock at 1650°F for 1 hr, b) Stress relieve at 1200°F for 4 hr and furnace cool,

Jan 1, 1960