By Cem Colakoglu

In this study, nickel containing iron alloys were produced by carbothermal reduction of lateritic nickel ores obtained from Manisa - Caldag region of Turkiye in order to investigate the reaction mechanism of nickel and cobalt. In the experiments, the lateritic ore containing 1.58 wt.% Ni and 0.12 wt.% Co was calcined in a semi-pilot scale rotary furnace at 1100°C for 1 hour. Then, a mixture of calcined ore and metallurgical coke was reacted in sintered alumina crucibles using a graphite resistance tube furnace at different time (0- 60 min) and temperature (1500-1600°C).

Jan 1, 2009

By NRMR Bhargava

With the increasing use of lead-free solder alloys, low melting point alloy is often required due to the heat- sensitive parts or substrates in modern electronic devices. For such demand of low melting point, the nanostructure lead- free solder alloy, having excellent metallurgical characteristics and a melting point of <215oC, were developed by mechanical attrition of conventional lead free solder alloys (Sn-Ag-Cu, Sn-Ag and Sn-Cu). The decrease in melting point due to nanosize effect was calculated theoretically as function of particle size and the theoretical results were compared with experimental values measured by differential scanning calorimetry. The newly developed alloys have eutectic composition of Sn-3.5Ag-0.7Cu, Sn-3.5Ag and Sn-0.7Cu and the melting point depression found to be 5.10C, 4.10C and 6.20C when the bulk alloys reduced to 80 nm, 92nm and 96nm sizes respectively.

Jan 1, 2009

By Alicia Esther Ares

The family of Zn-Al (ZA), Zn-Ag and Zn-Al-Ag (ZINAG) alloys offers high mechanical properties, ease of finishing, the advantage of low energy and pollution-free melting. Also, present alternatives to the well developed alloy systems, such as brasses, bronzes, cast irons and aluminum alloys. The main objective of this paper is to measure thermal parameters in ZA, Zn-Ag and ZINAG hypoeutectic and hypereutectic alloys directionally solidified which present columnar, equiaxed and columnar to equiaxed transition structures (CET). Also, estimate the mechanical properties, such as microhardness and tensile parameters and correlate these with the thermal (cooling rate) and structural parameters (grain size and dendritic spacing). The different types of structures were analyzed with optical and scanning electron microscopy. The results showed the influence of concentration, microstructural arrangement and thermal conditions during solidification on the mechanical properties. The results of the present investigation are compared with previous experiments.

Jan 1, 2010

By Ovidiu Pasca

The Phelps Dodge Miami Smelter utilizes four Hoboken converters to process molten matte from the Isasmelt vessel. This paper presents past and present improvements in operation, maintenance and process optimization, based on data collection, which has led to increased converter campaign life and copper throughput.

Jan 1, 2005

By Y. Zhoa

The surface morphology of materials is of fundamental importance to many surface related applications, such as wetting, friction, reflection, drag, and adhesion. Various approaches for micro/nano patterning atop polymer surfaces have been proposed in recent years. However, a cost effective technique is still highly in demand. In this paper, we demonstrate a novel but rather simple and generic approach for surface micro/nano patterning using shape memory polymers (SMPs). Different types of novel patterns are realized and their 3-D surface features are quantitatively analyzed by a PLµ Confocal imaging profiler.

Jan 1, 2010

By J. M. Tannenbaum

A depth-sensing micro-indentation technique is developed for evaluating mechanical properties of materials at elevated temperatures (to 1200°C). System description and design considerations of the test apparatus are described. Based on Hertzian spherical indentation approach, the micro-indentation test apparatus is capable of determining Young?s modulus and creep strength of test materials with flat, tubular, or curved architectures from room to 1200°C under either air or controlled gaseous environments. Calibration tests were conducted on a H13 Tool Steel coupon from 22°C to 500°C and single crystal Haynes 230 alloy at 1000°C with excellent agreement to the literature values. Indentation creep tests of Haynes 230 alloy were carried out at 1200°C with preliminary results showing good correlation to creep exponents. Further system refinements will be investigated, and additional testing will be conducted.

Jan 1, 2010

By Liang Sha

In this study, adsorption of copper by chemically modified orange peel was investigated. A conspicuous change occurs in the surface morphology of the biomass due to modification, which is depicted by SEM images. Equilibrium isotherms and kinetics were obtained and the effects of various factors, including solution pH, contact time, initial metal ions concentration and temperature, were studied by batch experiments. Kinetics was found to be best-fit pseudosecond- order equations. Equilibrium was better described by Langermuir isotherms rather than Freudlich isotherms. At 25?, pH5.30, the maximum adsorption capacity was 70.67mg?g-1 . With increase of temperature, adsorption efficiency decreased. The biosorbent was suitable for repeated use for more than five cycles.

Jan 1, 2009

By A. Barba, M. P. Gómez, F. Puertas, M. Palacios, M. F. Gazulla, S. Martínez-Ramírez, I. García-Díaz

"The present study explores the reactivity and burnability of cement raw mixes containing fired red or white ceramic tile wastes or combinations of the two as alternative raw materials. The results showed that the new raw mixes containing these wastes are technically viable. The reactivity and burnability of the new raw mixes have been evaluated; confirming very good results when the particle size of wastes was less than 90 µm. The chemical and mineralogical compositions of the new clinkers were comparable to clinker manufactured with conventional raw materials. The mix of red and white ceramic tile waste was found to perform as well or better than each type of waste separately, a promising indication that separation of the two would be unnecessary for these purposes.IntroductionPortland cement clinker production consumes large amounts of energy (850 kcal/kg clinker) and has a considerable environmental impact. This involves massive quarrying for raw materials (limestone, clay etc), as it takes 1.7 tonnes to produce one tonne of clinker, as well as the emission of greenhouse and other gases (NOx, SO2, CO2) into the atmosphere. Around 850 kg of CO2 are emitted per tonne of clinker produced.The cement industry is looking for solutions to these problems, to attain sustainability and comply with the Kyoto Protocol commitments [1,2]. For that reason, experimental ways are being explored to develop cements whose manufacture is less energy-intensive, less damaging to the surrounding environment and with lower tendency to emit polluting gas. One of the reach this objective is the use of industrial waste and by-products as alternative materials for cement manufacture. Such alternative materials may partially replace fuel [3,4], conventional raw materials [5-8] or clinker in the final composition of the cement [9]."

Jan 1, 2008

By P. N. Anyalebechi

The effects of solidification rate on the cast microstructures of aluminum alloys 6009 and 6016 have been investigated with directionally cooled laboratory-size ingots, at 0.2-10.1 K/s and 0.4- 23.1 K/s, respectively. These ranges of solidification rate are within those observed in commercial-size ingots. In both alloys, the average dendrite cell size and second phase particle size decreased with increase in average solidification rate and with a decrease in average local solidification time. However, at comparable solidification rates, the dendrite cells and second phase particles are finer in the shorter freezing range alloy 6009 than in the longer freezing range alloy 6016. This is provisionally attributed to the earlier formation of second phase intermetallics at higher temperatures during solidification and to the formation of greater amount of the relatively coarse plate-like ß -phase (Al9Fe2Si4) phases in alloy 6016. In general, in both alloys, the types and relative amounts of the second phase particles in both alloys are independent of solidification rate.

Jan 1, 2006

By Jacques J. Eksteen

Any effort to improve the metallurgical control of industrial furnaces employed in the primary extraction of high carbon ferroalloys are bound to fail unless the variability of the melt is not fully accounted for. A number of sampling campaigns were performed on both 3phase AC submerged arc and single phase DC open arc furnaces at different smelter sites in South Africa where High Carbon Ferrochrome is produced. It was found that the heterogeneity between multiple samples during a single taps were much higher that for heterogeneity found within a sample. Moreover, this heterogeneity (as quantified by the relative standard deviation per tap) varied with the operating conditions of the furnace, the element monitored and the type of furnace. A relationship was found between the relative standard deviation of certain elements and the degree of subcooling of the melt.

Jan 1, 2006

By Timo Kankaanpää

Keywords: Solvent extraction, dispersion, phase separation, CFD The liquid-liquid dispersion phases are separated by gravity in a solvent extraction settler. This separation step is made more effective by picket fences. The picket fence geometry and its physical placement have a significant effect on the separation process, because the purpose of a fence is to smoothen and control organic-aqueous dispersion flow in the first part of the settler and achieve a deep and dense dispersion layer in the front end of the settler resulting in a clean phase separation. In this study, physical phenomena in the solvent extraction process and phase separation in a solvent extraction settler with and without picket fences have been examined using a commercial CFX software package. It can be concluded that the used CFD-approach proved to be a complementary tool for optimizing and designing the solvent extraction settler.

Jan 1, 2005

By W. M. Cross

Bubble attachment time measurements for the rare-earth phosphate minerals monazite and xenotime were made as a function of oleate concentration, sodium fluoride addition, and temperature. Results indicate that the rare-earth phosphates behave similarly to other phosphate minerals, notably collophanlte and fluorapatite, which have been studied previously. The addition of sodium fluoride yielded a modest decrease in bubble attachment time with fluoride additions below the apparent fluoride surface precipitation point, while at fluoride additions greater than the apparent precipitation point a significant decrease in attachment time occurs. Increasing the temperature or the system gave a slight decrease in bubble attachment time in the absence or sodium fluoride. With sodium fluoride addition and below the apparent fluoride surface precipitation point, an increase in temperature actually increased the attachment time. For sodium fluoride additions above the apparent fluoride surface precipitation point, a temperature increase significantly decreased the attachment time.

Jan 1, 1989

By M. I. Brasileiro

The use of experimental design to the study of mixtures has found a wide range of applications, even in laboratory scale or in industrial development works. The aim of this work was to maximize granite sawing waste content in ceramic tiles using experimental design. Based on the raw materials, specific formulations were developed using the experimental design. The raw materials were mixed and sample bodies were produced using uniaxial pressing. The sample bodies were fired and characterized in terms of water absorption, mechanical strength and X-ray diffraction. Regression models were adjusted relating the water absorption and mechanical strength with the amount of raw materials. The results showed that the methodology of experimental design maximize the content of wastes incorporated in ceramic tiles formulations. Formulations containing up to 40% of waste can be used for the production of ceramic tiles.

Jan 1, 2009

A molten metal granulator was designed and fabricated at the U.S. Dept. of Energy, Albany Research Center, for granulation of precious metal-bearing alloys and slags. The system was designed to safely granulate a metal alloy at a temperature of up to 1,600°C at a rate of roughly 50 kg of alloy per minute. The primary water jet was supplied by a 18.6-kW, 600 liter per minute pump which provided approximately 600 kg of water per minute through the primary jet. Two 3.7-kW, 150 liter per minute auxiliary pumps provided additional wash water to wet the granulation trough through 4 secondary jets, which were placed at either side of the primary jet. The water supply was closed-loop, including a 37,850-liter supply tank and 22,710-liter recovery tank. Magnetic separators and particulate filters were included for collection of the finest fraction of the granulation product, which cleaned the water sufficiently for continuous recycle.

Jan 1, 2006

By Napisporn Memongkol

Syntheses of Al-TiC-Al2O3 and Al-SiC-Al2O3 composites were obtained in situ by carbothermal reduction of mixtures of Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders. The reductions were carried out in a horizontal tube furnace under flow of inert gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of aluminum reinforce with titanium carbide and alumina and aluminum reinforce with silicon carbide and alumina. The effect of the reaction temperature (1000 o C ? 1200 o C) and condition of precursors on the Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders were investigated using XRD and SEM method. The synthesized products showed those composites with aluminum matrix and titanium carbide and alumina as reinforced phases and aluminum matrix and silicon carbide and alumina as a reinforced phase was formed.

Jan 1, 2006

By Qingwei Wang

This study focused on acidic wastewater from producing sulfuric acid system in zinc smelter containing mercury 21.48mg/L, zinc 55.85mg/L, lead 38.50mg/L, copper 1.68mg/L, cadmium 10.25mg/L, As 29.86mg/L treated by biologics. The factors of pH value, the ratio of biologics to mercury, complexing time, hydrolytic time and temperature were studied in this paper. Experimental results indicated that at pH value 10, quantity of biologics to mercury ratio was 16, complexing time 30min, hydrolyzation time 20min, temperature at 40?, concentration of mercury in treated water was removed to 22.15µg/L. At same time heavy metals such as Zn, Pb, Cu, Cd, As was removed by biologics, the remained concentration in treated water was Zn 0.53mg/L, Pb 0.12mg/L, Cu 0.01mg/L, Cd low to 0.01mg/L and As 0.023mg/L. According to EDAX analysis, mercury content in complexing sediment reached 28.49% easily to recycle as raw material and low concentration of heavy metals in hydrolytic sediment easily to dispose and treat.

Jan 1, 2009

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

Achieving continued economic growth with social equity within the natural limits of the Earth&apos;s &apos;eco-systems is the major issue facing the world today. The material and energy needs of the world cannot be met with the current ways of addressing this issue. The need for metals, an important class of materials, will continue into the future because their unique properties make substitution by other materials impossible in many applications and this need will continue to be met from primary metal production and recycling. However, the recycling rate will increase and the usage pattern of metals will change to reflect the environmental impact of their production and use. Pyrometallurgy has an important role in meeting the metal needs of the future since some metals can only be produced pyrometallurgically; the energy required to produce some metals pyrometallurgically is significantly less than by other methods; most metals are most efficiently recycled pyrometallurgically; and the release of harmful and toxic elements into the biosphere can sometimes best be controlled through pyrometallurgical processing. The development of strategies for pyrometallurgical processing for the future lies in the recognition that sustainable development calls for large step improvements in value delivered per unit of environmental impact over the entire supply chain. Pyrometallurgists can respond to this challenge by contributing to reducing the environmental impact of meeting metal needs using three broad strategies: "end-of-pipe" approaches to convert emissions into benign materials for storage or disposal; flowsheet redesign to limit or eliminate emission production; and improved recycling technologies. A number of examples are discussed to illustrate how the sustainability driver is already influencing the technological development of pyrometallurgical processes, and how these will develop further as the sustainability driver strengthens.

Jan 1, 2003

By A. J. Sideris

It is known that Mg can act as a catalyst/solvent in the high pressure high temperature diamond synthesis. However, above pressure levels of the order of 7 GPa, and temperatures from 1700 ? 1800oC, it was not possible yet to use Mg for the industrial production of diamond. A possible alternative is the use of MgNi based alloys. However, owing to the great Mg reactivity, it was consider, so far, a difficult task to deal with such alloys. The present work presents successful results regarding the production of MgNi alloys, with different composition, at high pressure conditions. The behavior of the alloys and their microstructural characterization is analyzed.

Jan 1, 2006

By G. N. Shannon

Keywords: inclusions, slag, modeling, interfacial energy, capillary force, particle flotation, particle separation A previously introduced model of inclusions separating across a steel-slag interface, developed by Nakajima/Okamura and Bouris/Bergeles, is expanded to include different inclusions shapes (octahedral and plate-like, besides spherical) as well as comparison between model ladle-, tundish-, and mold-slags. Investigation of the relation of these shapes with the interfacial capillary force ? which arises due to the dynamic interfacial energy during separation ? has shown that the force has a significant effect on whether the inclusion separates rapidly or settles at the interface. For the slags considered, the most significant physical property is found to be viscosity, which resulted in fast separation times for inclusions in the mold and ladle slags, relative to the more viscous tundish slag. Particle dissolution (using experimental data) is included in separation modeling.

Jan 1, 2005