By R. S. Dean

"It has long been recognized that the properties of polycrystalline substances are not the same as those of single crystals. These differences are especially marked in metels and metallic minerals, and are of greatest practical importance in metal working and ore treatment. The property changes encountered in passing from a metal single crystal to a poly-crystalline aggregate are the same as are produced by cold-working a metal or by the precipitation of a disperse phase. Hence, we may logically assume that the property changes are all due directly or indirectly to the formation of interfacial area or internal surface. Our problem, then, is to ascertain the physicochemical state of the metal atoms at such internal surface and show how this physicochemical condition accounts for the pronounced changes of mechanical, magnetic, and electrical properties that accompany increased internal surface.GENERAL CONCEPT OF INTERNAL SURFACEIn 1678, Huyghens attempted to explain the double refraction of calcite by postulating that crystals were built from a regular arrangement of ellipsoidal particles. Over 100 years later, Abbé Hauy concluded from his studies of cleavage that crystals might be built from small units, but the units were of the same shape as the entire crystal. This idea, which was prevalent in mineralogical thought before the advent of X-ray spectrometry, was discarded when the great success of Bragg made it appear that the chemical atoms were in reality the elements of structure. In the further development of X-ray technique, however, C. G. Darwin, in England, and P. P. Ewald, in Germany, found it necessary to postulate crystal units con¬taining many atoms. The latter gave the name of mosaic crystals to those so constituted. The individual units are supposed to Possess the ideal atomic arrangements revealed by the X-ray but are not oriented with respect to one another."

May 1, 1938

By H. H. Schrenk, Carlton E. Brown

"INTRODUCTION The question as to whether or not the flow of water through pneumatic rock drills commonly used in this country keeps to a minimum dust disseminated into the air during drilling arose during a study of the dust-in-air conditions in Butte mines from February to July 1936 and December 1936 to June 1937 made by the Bureau of Mines in cooperation with the Anaconda Copper Mining Co., Butte, Mont, The purpose of this report is to describe the study, including some experimental work on the subject, and to give test results.ACKNOWLEDGMENTSThe help of the ventilation department of the Anaconda Copper Mining Co. in planning the study and collecting the data is gratefully acknowledged.EXPERIMENTAL CONDITIONSTests were conducted in an untimbered 6- by 8-foot crosscut in medium-hard granitic rock near the shaft station on an inactive level of one of the active Butte mines. Figure 1 shows the plan and section of the test location. Air was drawn from the shaft at the station, through the crosscut, and up through another shaft. The flow of air through the crosscut was decreased by a brattice downstream from the sampling location, so that relatively high, easily measurable dust concentrations would be obtained in the tests. Impinger samples for determing concentration of dust in the air were collected in an opening 51 inches wide, 29 inches high, and about 4o inches from the top of the rails in a wooden stopping about 16 feet downstream from the place where the test holes were drilled."

Apr 1, 1938

By A. U. Miller

Definite progress has been made in accident prevention in Illinois during the past few years; the State Department of Mines and Minerals is receiving excellent cooperation from coal companies and employees, the companies are making greater effort to maintain their mines in good condi- tion, and the employees are eliminating more unsafe practices. As a result, some coal companies have made commendable safety records that prove that coal can be mined with a comparatively low accident rate. However, there is need for further improvement, as the accident rate of the State as a whole is much higher than it should be. During the 55-year period 1882-1936, in- clusive, reports of the State Department of Mines and Minerals show a total of 7,005 (an average of 127.36 per year) men killed in and around the coal mines. Of this number, 6,425 (91.7 percent) were killed underground, 346 (4.9 percent) in the shaft, and 234 (3.3 percent) on the surface. Of the fatalities underground, 3,300 (51.3 percent) were killed by falls of roof, sides, or face coal, 1,167 (18.1 percent) by haulage, 639 (9.9 percent) by handling explosives, 579 (9 percent) by explosions, 151 (2.3 percent) by electricity, and 589 (9.1 percent) by other means. Of the fatalities in the shaft, 171 men (46.5 percent) were killed by falling down the shaft, 14 (41.6 percent) by the cage, and 31 (8.9 percent) otherwise. On the surface, 113 (48.2 percent) of the fatalities were due to railroad cars, 51 (21.7 percent) to machinery, and 70 (29.9 percent) to other causes. The fact that 7,005 lives (an average of 127.36 per year) were lost during 1882-1936 is sufficient evidence that in the past too little interest has been taken in safety by either the management or workers. A realization of this deplorable loss of life should act as an incentive to the industry to make greater effort to prevent accidents in the future. After an accident occurs, the facts pertaining to it become history, and anything that may be done afterward cannot change in any way the damage that has already been done, such as loss of life, personal injury, and destruction of property. The main benefit that can be derived from an acci- dent is that suitable procedure may be adopted and some lesson may be learned to aid in preventing a similar accident in the future. All accidents, par- ticularly serious ones, therefore should be investigated and an effort made

Apr 1, 1938

By Ellis S. Hertzog, James R. Cudworth

Tremendous interest has been evidenced in the subject of dewatering and drying ooal for the past 10 years, and yet little effort has been made to summarize the literature, at least so far as this country is concerned. Only a few published articles have dealt solely with dewatering and drying coal. In most cases the subject has been discussed briefly, either in general terms or as to specific installations. It is desirable that a compendium be prepared collecting in one place information on the dewatering and drying of coal, the needs for this process in various fields, the available equipment, and the current American practice in regard to it. This work was underta..lten by the :Bureau of Mines in cooperation with the University of Alabama. New coal-washing plants in which various types of dewatering and drying equipment were in operation were visited in-Pennsylvania; Ohio, India...~a~ and Illinois. The dewatering·and drying of coel has .been studied in this coimtry by the Surface Preparation ·Committee of the ·coal Operato~s• Committee of the .American Mining ·Oongress. In GermaIJY .it has received the special attention of the Reichskohlenr·at, and in Great Britain of the Utilization of Fuel Commi-t-tee of the Insti ti.ite of Min"ing Engineers.

Apr 1, 1938

By L. C. IlsLey

A list of permissible mine equipment, tested and approved prior to Jan 1, 1937, was published in Bureau of Mines Information Circular 6942 • .ll The present list inc ludes additional equipment approved during the calendar yea r 1937. The ma terial has been listed und er the same. headings as th ose used. in Information Circular 6942. The number that appears at the beginning of each it em represents the number o f this type of ma.chine appr.oved including the machine in questi on; for instance, the miing ma.chine numbered 70 was the seventiet h co al cutting ma chine design for which approval has been isnued. All of the equipment listed represents new designs except that covered by the first item, that is, 57 under the • heading nLoading Machines and Conveyors. 11 This item covers the approval of the 500-volt design of a machine the 250-v olt design of which was approved on January 17, 1935. The system under wich these devices were tested permits the manu-. facturer., after his equipment has passed certain tests prescribed by the 'Ui"eau of Mines, to mark his equipment with a seal showing that it has been approved by the Bureau. These tests are designed to insure t hat equipments hav,e the minimum requirements for safety in use. The only object of the :Bureau in making such tests and publishing lists of permissible equipment is to help decrease the hazards of mining.

Apr 1, 1938

By F. G. Miller, H. C. Miller

Petroleum technologists and progressive operators constantly are striving to increase the percentage of oil that may to recovered from reservoir rocks through wells. The exhaustive studies that have been made of the function of natural as in the production of oil, for example, have aided operators greatly in increasing the quantity of oil recovered from reservoirs. Natural gas dissolved in and otherwise associated under pressure with oil in reservoir rocks, however, is not the only source of energy available for moving oil through sands to wells. In becoming "reservoir—energy conscious" engineers have learned that in many petroleum reservoirs the edgewater flanking the oil accumulation constitutes a potential source of energy capable, through proper control, of increasing oil—recovery efficiencies materially. No longer is the encroachment of water into the oil— and gas—filled tart of the reservoir considered as an evil to be combatted by devious methods but rather a natural consequence, incident to the withdrawal of nil and as from the wells, that may be used advantageously in lengthening the flowing life of wells and increasing the economic recovery of oil and gas.

Mar 1, 1938

By H. H. Schrenk, Carlton E. Brown

"INTRODUCTION The angle at which a hole is drilled has long been thought to affect the amount of dust disseminated into the air during wet drilling. The amount disseminated has been reported as increasing rapidly with the approach of the angle of the hole to the vertical (up) position. 4/ This has been explained commonly as being caused by a decrease in contact of water with the face of the drill hole; increase in amount of sludge dropping through the air; and increase in amount of sludge running down the drill steel and being thrown into the air by the rotation of the drill steel and by leakage of air from the front head of the drill.The steep up angles of the holes drilled are responsible, at least partly, for the higher dust concentrations found in such places as raises, compared with those at level faces, where most of the holes are drilled at angles farther from the vertical (up) position. The mining industry is coming to realize more and more the importance of the angle of the drill hole as a contributing cause of the high dust concentrations found in some raises. Much work is being done to counteract the effect of the angle of the drill hole on dust dissemination. The rate of rater flow through drill steels is being increased by the use of water tubes of larger diameter or by higher water pressures to obtain better contact between water and the face of the drill hole. Traps are being developed to catch the sludge from the drill hole and allow it to drain down through a special pipe before it drops through the air or runs down the drill steel. Drills that permit little or no air to leak from the front head along the drill steel are being designed and used. Care is being taken to prevent the exhaust from the drill dispersing the sludge into the air."

Feb 1, 1938

By H. P. Greenwald, H. C. Howarth

There was reported in Bureau of Mines Technical Paper 5754/ a series of tests to determine the compressibility and bearing strength of specimens prepared from blocks of potash salt obtained from a mine near Carlsbad , N. Mex . The events leading up to the investigation were sketched in a foreword by George S. Rice , then chief mining engineer of the Bureau ( retired September 30 , 1937 ) ; this foreword also gives a discussion of the possibility of increasing the ultimate total recovery of the potash salt by " second mining" of pillars or by use of a longwall system . In June 1936 , Rice and the senior author visited Carlsbad with H. I. Smith , chief of the mining division of the Geological Survey , to observe mining then in progress and to discuss with the management of one of the mines records of convergence of roof and floor which they were obtaining . It developed that serious thought was being given to the possibility of roof failure resulting from shear at the faces of pillars . There was envisioned the danger of such cracks extending upward to water - bearing strata . Obviously , the simple compression tests of the potash salt then being made would throw no light on this question , and tests of assemblies of potash and roof salts would have to be made . In this connection it is to be remembered that in the mine no sharp division exists between the potash salt being recovered and the nearly pure halite which forms the roof . The interlocked crystalline structure is continuous , and there is merely a very rapid decrease in the proportion of sylvite in a short distance vertically . Figure 2 of Technical Paper 575 shows that two samples near the top of the salt being mined contained , respectively , 51 and 65 percent potassium chloride . Contrasted with this is an analysis of the roof salt given on page 24 of that publication , which showed only 3.6 percent potassium chloride . As the data given in Technical Paper 575 show , the roof salt is much less plastic than the potash salt . The immediate roof may then be thought of as a more rigid stratum of indefinite extent resting on and continuous with yielding supports and loaded uniformly at the rate of 900 to 950 pounds per square inch . Just what thickness of the salt should be considered as immediate roof is uncertain .

Feb 1, 1938

By Leonard C. Grimshaw

Diffusion of carbon from gases into iron has been the object of much research, because of its long recognized importance in carburizing processes, but the direct diffusion of carbon from steel into iron has received relatively little attention. Because of the increasing use of clad metals in industry, direct diffusion from steel into iron is becoming of practical importance. Therefore, the object of this investigation was to study the diffusion of carbon from several different kinds of steel directly into relatively pure iron, realizing that elements in the steels other than carbon might influence the rate of carbon diffusion. The previous work on diffusion of carbon into iron has been considerable, and includes many reports in foreign languages. This work has recently been well reviewed by Mehll and Krynitsky12 and the reader is referred to their excellent bibliographies. Methods of Study There are two main methods by which the direct diffusion of carbon from steel into iron may be studied. In one method, steel is first decar-burized in part, and diffusion of carbon then allowed to take place from the steel into the decarburized steel. This method is open to two serious objections: (1) the decarburized steel is not iron, but contains elements such as manganese, silicon, chromium or tungsten, which may be an essential part of the steel under study, and which may seriously influence the diffusion of carbon into the decarburized area; (2) there is from the start of diffusion an unknown carbon-concentration gradient between the steel and the decarburized area. Another method, which possesses neither of these disadvantages, is to study diffusion from steel into a thick plating of electrolytic iron. Herc the chief difficulty is to secure an electrolytic deposit of iron upon steel without introducing an oxide film at the interface that will interfere with diffusion. The author is able to deposit iron upon any kind of steel without introducing an oxide film at the interface, so that diffusion of elements from the steel into the iron is free to proceed unhindered.

Jan 1, 1938

Jan 1, 1938

The Thirty-sixth, Regular Meeting of the Rocky Mountain Coal Mining Institute was called to order at the Shirley-Savoy Hotel, Denver, Colorado, Thursday, June 23, 1938, at 11:15 o'clock a.m., by Thomas Allen, Vice-President for Colorado, who announced that owing to the serious illness of Fritz Nyman's father, Mr. Nyman would be unable to attend the convention. Vice-President Allen welcomed the convention as a representative of Governor Ammons. Owing to the overlapping of a previous engagement, Mayor Benjamin F. Stapleton regretfully arrived too late to welcome the gathering in behalf of the City of Denver. Vice-President Allen selected Mr. F. W. Whiteside to preside at the morning session. On motion made, seconded and carried, the reading of the minutes of the Thirty-fifth Regular Meeting was dispensed with, inasmuch as they are printed in the proceedings. Chairman Whiteside suggested that the appointment of the personnel for the Committee on Resolutions, Nominating, Membership and Auditing be deferred until later in the meeting, and on motion made by Mr. Oliver, duly seconded and carried, this suggestion was adopted.

Jan 1, 1938

By Frederic Benard

THE Ontario Refining Company, Limited, wholly-owned subsidiary of The International Nickel Company of Canada, refines the entire blister copper output of the latter's Copper Cliff smelter. Prior to 1936, the blister was cast in 460-lb. cakes at the smelter, loaded on open cars, and transported by rail to the refinery, a distance of approximately 1 1/4 miles. Here the cakes were transferred to the plant narrow-gauge system, charged to furnaces, and re-melted. This procedure necessitated the operation of holding furnaces and casting machines at the smelter -extensive re-handling-and melting down of a cold charge at the refinery. Transfer of the copper in molten form direct from converters to anode furnaces promised a considerable reduction in costs, and this possibility was investigated. As a result, a portable holding furnace, or hot-metal car, was designed and constructed. It was placed in operation in July, 1936, to be followed a year later by three additional units of slightly modified design. Figure 1 shows the original car, and Figure 2 the lacer type. With four cars in service, operations were placed on an all 'hot-metal' basis.

Jan 1, 1938

[ ]

Jan 1, 1938

By Morris Cohen

WITHIN the past two years, a number of publications have called attention to the double peaks, or stages, that appear in the hardness and strength curves of certain aging alloys. The author has shown the existence of double hardness peaks during the aging of a high-purity silver-copper alloy;' and on the basis of electrical resistance, microscopic, dilation and lattice-parameter measurements, he concluded that the initial hardness peak occurs prior to precipitation while the secondary hardening is due to precipitation. It was suggested that the general mechanism of age-hardening involves two consecutive processes, the first consisting of nucleus or knot' formation, and the second consisting of actual precipitation and particle growth. It was further held that the two stages are interdependent, but because of nonuniform precipitation they may overlap each other to an extent that increases as the aging temperature is raised. At high aging temperatures, the effect of the first stage cannot be detected because of the rapid occurrence of precipitation. . The general theory of age-hardening recently presented by Dr. M. L. V. Gayler3 is in close agreement with the picture outlined above. With reference to work done on duralumin, copper-beryllium and copper-silver alloys, Dr. Gayler also concluded that age-hardening takes place in two consecutive steps: first, diffusion (in which the solute atoms migrate to certain crystallographic planes), and then precipitation. However, W. L. Fink and D. W. Smith4 have shown that the double aging peaks that appear in the strength curves of high-purity aluminum-copper alloys may be explained without recourse to pre-precipitation phenomena. By means of very careful metallographic technique, Fink and Smith demonstrated that during aging the precipitation takes place at an accelerated rate along the grain boundaries and slip planes as a result of the plastic deformation caused by the drastic quench from the solution heat-treatment temperature. † The general precipitation occurs at a

Jan 1, 1938

By John E. Dorn, Oscar E. Harder

The phenomenon of diffusion, according to the most prevalent conceptions at the present time, undoubtedly played an important part in the formation and distribution of metals and minerals in the earth's crust. Apparently there is good evidence that in the geological rate of cooling diffusion caused numerous materials to separate into individual masses or into duplex structures. As is well known, the early steels were made by cementation; that is, by heating wrought ferrous metal in contact with carburizing materials so as to produce a relatively high carbon content on the surface. If the process was continued long enough, the carbon diffused throughout the piece. A more homogeneous product depended upon further heating and forging, so that the carbon diffused to a fairly uniform concentration throughout the metal. In the modern metallurgical industry, diffusion is the basis for many operations; for example, the production of hard surfaces on steels by carburizing, nitriding, cementing with chromium, silicon, boron and beryllium. Castings or ingots as they solidify do not have homogeneous structures, but these structures are made largely homogeneous by suitable process of heat-treating and the resulting diffusion. It is in modern physical metallurgy, however, that we become greatly concerned about the mechanism of the phenomenon of diffusion. The rates of diffusion, effect of temperature and time on diffusion, and the relation of diffusion to the many properties of the parent metal and the diffusing metal have become important; also, we are concerned with the diffusion of a single metal into a complex alloy. For example, what is the mechanism whereby carbon and nitrogen travel into steel? What is the effect of alloying elements in the ferrous material on the rates of diffusions? What is the effect of simultaneous diffusion of carbon and nitrogen? How does chromium, beryllium, boron, or the like, diffuse into the steel, and what are the effects of alloying elements in the steel previous to the cementation process? These inquiries are by no means limited

Jan 1, 1938

By Frederick N. Rhines, Robert F. Mehl

It has been shown elsewhere1 that the data on the rates of diffusion in solid metals are fragmentary and in many cases unacceptable. As a result, relatively little is known concerning the factors determining rates of diffusion and the variations in these rates with temperature. The first form of Fick's law (equation 1 below), in which the diffusion coefficient D is assumed invariant with composition, has been recognized for many years as only an approximation. The differential equation representing the second form of Fick's law (equation 4 below) has only recently been integrated by Matano,2 and unfortunately only in cases where a full diffusion-penetration curve (concentration-distance curve) has been obtained can the Matano solution be applied. The proper analysis of diffusion data is thus confined to the data of Grube and Jedele and of Jedele. 8 These data are essentially for one temperature alone and do not furnish any information on the variation of the activation heat of diffusion, Q, with concentration: no information exists on the variation of Q with concentration within a single solid solution field. 11 Much of the argument concerning the properties of metals that determine D and Q has been drawn from data in which variations of the quantities with concentration are unknown, for these data have been taken from experiments that could not furnish this information. Speculation concerning the properties of metals that may be effective in determining D and Q on the basis of data in which the chosen D and Q values are averages over wide concentration ranges of values at particular concentrations, ranges often of 100 per cent, is likely not to be fruitful.

Jan 1, 1938

By William L. Fink, Dana W. Smith

In parts I1 and II2 of this series, there were presented results of investigations on the age-hardening of an aluminum-copper and an aluminum-magnesium alloy. It was shown that the simple precipitation theory of hardening3 adequately explained the aging phenomena, including certain so-called "anomalous" behaviors which had caused other investigators to reject or modify the precipitation theory. However, these papers did not discuss the double aging peaks, which have been stressed in recent articles by Dr. M. Cohen4 and Dr. M. L. V. Gayler.6 The present paper is devoted to an explanation of this "anomaly." Fig. 1 is a generalized schematic representation of aging curves at different temperatures. Curve A corresponds to the aging at the lowest temperature, and D at the highest temperature. Certain previous investigators have explained curve A and the initial peaks

Jan 1, 1938

By Arthur S. Coffinberry, Ralph Hultgren

We have studied the gold-aluminum system by X-ray diffraction and by the microscope over the entire range of composition for temperatures between 300° and 500° C. Results obtained are shown in Fig. 1, combined with the work of Heycock and Neville1 at higher temperatures. The diagram differs in important details from that given by Hansen2 in his critical compilation of the literature of binary alloy systems. This work was undertaken both because of the intrinsic value of a knowledge of the phase diagram of this system and because of the need of theoretical metallurgy for precise and accurate data, particularly X-ray diffraction data. Systematic studies of equilibrium diagrams, particularly by Hume-Rothery,3 have shown regularities that yield a certain insight into the nature of alloying forces. It has been shown, for example, that solid solubility depends on the concentration of free electrons in the alloy, on the relative radii of solvent and solute atoms, on the forces of attraction between atoms, and on the relative stability of intermediate phases. The well-known Hume-Rothery rule states that the crystal structures and compositions of many intermediate phases depend on the electron-to-atom ratio. This has been confirmed and extended by wave mechanical calculations.4 A knowledge of the forces between atoms in alloys, even an imperfectly developed empirical one, should be a valuable guide in the preparation of technological alloys of desirable properties. Furthermore, such information is basic in such problems as rate of diffusion, age-hardening, phase transformations, and others. The most valuable data for this purpose are furnished by X-ray diffraction studies. Unfortunately, work has been

Jan 1, 1938

By C. H. Mathewson, H. M. Day

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By J. T. Eash, E. M. Wise

Many of the platinum metal alloys are hot-forged in the early stages of reduction from ingot and substantial quantities of platinum alloys are commercially employed at very high temperatures in ammonia oxidation units, orifices for forming glass rods and fibers and as cathodes in long-life thermionic amplifiers. They are used also for electrical heating resistors, safety blowout disks, thermocouples and crucibles. The tensile properties at elevated temperatures are important in many of these situations but data on the subject are limited. Creep data also are important, but will not be covered at this time. Scope and Conclusions Tensile tests were carried out at room temperature and elevated temperatures up to 1100" C. on previously well annealed samples of platinum. palladium and several of their important alloys with compositions shown in Table 1. The results are presented graphically in Figs. 1 to 4. The tensile strengths of platinum and the platinum-base alloys (with the exception of the 10 per cent rhodium-platinum alloy) at 1100" C. are from 16.6 to 18.8 per cent of the strengths of the same alloys (well annealed) at room temperature. The strength ratio of the 10 per cent rhodium-platinum alloy is 22.3 per cent, which is appreciably higher than that of the other materials tested. The tensile strengths of palladium and the palladium alloy at 1100" C. are from 10 to 11.2 per cent of the room-temperature values. The elongations of platinum and its alloys tend to increase at temperatures above 600" to 800" C., while the two samples of pure palladium show a maximum at 600" C.

Jan 1, 1938