Search Documents

By E. S. Rowland, J. Welchner, R. H Marshall

This paper presents results on an extension into the realm of high-carbon steels of some work recently published1 on the effects of time at temperature, quenching temperature and prior structure on the hardenability of one 0.20 and four 0.40 per cent carbon alloy steels. It was shown at that time that unless the conditions of time, temperature and prior structure are substantially the same in performing the hardenability test as in conducting hardening of parts in production, the correlation of hardenability information with the hardness and properties of production parts is often not of satisfactory accuracy. The general effects of these variables on the austenitic grain size, distribution of excess carbides and critical cooling rate have been known for many years and one or more have been investigated by Shepherd,2,3 Davenport and Bain,4 Digges,5,6 Digges and Jordan,' Post and associates8 and Roberts and Mehl,9 to mention only a few. There has been no systematic investigation, however, into the quantitative variations produced on the hardenability of commercial high-carbon steels by changes in these factors of time, temperature and prior structure. Procedure A plain carbon hypereutectoid steel, S.A.E. 52100 and Graph-Mo, a molybdenum-bearing high-carbon steel containing some graphite, were chosen for this investigation. The chemical analyses of these electric-furnace steels are given in Table I. The procedure used was exactly that reported previously,' hence the details will not be repeated here. Normalized (165o°F.) and spheroidized prior structures were utilized on all steels with hot-rolled and quenched (I600°F. oil) prior conditions added for the plain carbon steel. The end-quench test developed by Jominy10 was sclected for use in this investigation and, with the noted exceptions, the American Society for Testing Materials standard procedure was followed. The effect of time at temperature was examined at intervals of o, 10 and 40 min. and 4 hr., and a few 16-hr. tests were run. Salt-bath heating of the specimens was employed to control and minimize the

Jan 1, 1944

By Herbert H. Uhlig

Although the mechanical properties of high-carbon manganese-iron alloys, particularly the Hadfield manganese steels, have been established, the literature discloses discrepancies in the reported properties for the low-carbon alloys. Hadfieldla summarized the existing data up to 1927, including the investigations of Guillet, Arnold, Strauss, Burgess and Aston, and reported his own values for alloys containing for the most part from 0.06 to 0.I5 per cent carbon. He noted: From these comparisons it wil! be seen that while there is a broad and general agreement as to the character of the alloys at the different manganese percentages, there are disparities in individual cases, especially as regards the degree of toughness or brittleness displayed by an alloy with certain percentages and with particular types of treatment. These differences are not always readily explainable.lb His data showed that alloys containing 4 to 10 per cent manganese water-quenched from Iooo°C. were brittle and hard with maximum brittleness at about 7 per cent. Slight improvement in ductility was obtained with compositions from 10 to 17 per cent manganese. Alloys containing up to 17 per cent manganese slowly cooled rather than quenched from 87o°C., he found, were slightly improved in ductility with significant improvement in alloys analyzing 4.1 and 4.8 per cent manganese. Recently Walters, Kramer and Loring2 reported mechanical properties for alloys made up from electrolytic manganese and ingot iron and containing from 0.02 to 0.04 per cent carbon. They showed that a tempering treatment at 54o°C. (Iooo°F.) for one hour significantly improved the ductility of compositions ranging from 6.7 to &apos; 20.7 per cent manganese. The differences of these compared with Hadfield&apos;s results they considered to originate in this tempering treatment plus the fact that Hadfield&apos;s alloys contained higher carbon and phosphorus (0.06 to 0.I5 per cent C; 0.06 to 0.07 per cent P compared with 0.02 to 0.04 per cent C, <o.ooI per cent P). In this paper it is shown that of the low-carbon alloys (0.02 to 0.03 per cent) containing from 3.3 to 21.5 per cent manganese moderately or rapidly quenched from IOOO°C. some are brittle or ductile, depending on presence or absence of hydrogen. Hydrogen is readily absorbed at high temperatures, and much of it is retained when the alloys are cooled to room temperature. The presence of hydrogen in the range of composition from 10 to 18 per cent manganese is a major factor in determining relative ductility. At 22 per cent manganese, and also at compositions below 10 per cent manganese, factors other than or in addition to hydrogen play a role. These are discussed. Also data are presented to show that hydrogen absorbed by the high-carbon alloys of Hadfield composition is without effect on their mechanical properties.

Jan 1, 1944

By J. R. Low, M. Gensamer

During the course of an investigation into the drawability of automobile-body sheet steel, it became apparent that certain advantages would be possessed by a deep-drawing steel with a very low yield strength, but almost normal tensile strength, provided a reduction in yield strength could be accomplished without sacrifice of ductility and fine grain size. It would also be desirable to have this steel free from strain-aging; that is, free from the tendency for the yield point to return after it had been eliminated by straining. It was known that, wet hydrogen treatment acted to eliminate aging, but as carried out by other investigators, at relatively high temperatures, this treatment resulted in grain coarsening. It has been established by some of the experiments reported in this paper that all of these objectives can be accomplished by treatment in wet hydrogen at a low temperature, in the neighborhood of 72o°C. The time of treatment is relatively short (about 3 hr, to completion with 20-gauge sheet) if the water content of the hydrogen atmosphere is made fairly high, say aimost 30 per cent by volume. At this temperature. the grain size remains fine in the time required. After this treatment sheet reduced the usual amount by cold-rolling has a grain size of about A.S.T.M. No. 7. The yield point is completely eliminated, and the yield strength is reduced to a very low value, in the neighborhood of 15,000 lb. per sq. in. The stress-strain curve departs gradually from the straight-line elastic part after the fashion of nonferrous deep-drawing alloys. This elimination of the yield point is accompanied by a verv low indentation hardness; for example, 32 Rockwell B or even lower. There is no aging as measured by increase in the yield strength upon aging at room temperature or for 3 hr. at 200°C., after stretching about 10 per cent in tension. Tensile strength is only slightly less than the box-annealed sheet, seldom dropping much below 40,-ooo lb. per sq. in. Elongation is practically unchanged, or increased slightly. The term yield point, as here used, refers to the phenomenon of heterogeneous deformation occurring at a substantiallv constant load, observed principally in annealed low-carbon steels. If such a steel is loaded in tension, the load increases steadily with elastic strain, suddenly falls, fluctuates slightly about some constant value for a time and then begins to rise again as deformation proceeds. The maximum initial load before the sudden drop is generally called the "upper yield point"; the value of the load where deformation proceeds at a

Jan 1, 1944

By H. A. Schwartz, W. Kenneth Bock

In this paper it is shown that when the tensile strength of a given steel in various states of heat-treatment is plotted against its elongation, a straight line results. The equation of this straight line can be computed with considerable accuracy from its chemical composition. The appropriate equations are given. The logarithm of the slope of the tensile-strength locus is shown to be proportional to the cumulative effect of the total alloy addition and the vosition of the line to be directly proportional to the cumulative effect of the alloy content. It is further pointed out that heat-treatment is more effective than composition in determining yield ratio. The latter enters mainly by its effect on hardenability, which is briefly discussed. Reduction of area and Brinell number are given some incidental attention. The data are applicable only to steels that have been normalized and/or quenched. The steels, if normalized, may or may not have been tempered. If quenched they must have been tempered at or above 4oo°C. (75o°F.). Introduction Cast steels vary in composition and frequently are used in various states of heat-treatment. It is obviously important to be able to predict the compositions that might accompany specific engineering properties by suitable selection of heat-treatments. For cast steels, which are of necessity produced heat by heat in accordance with the particular requirements of the castings to be poured, there has been, happily, much less tendency to standardization than for rolled products, whose destination is not necessarily known when particular ingots are made or rolled. It is of distinct advantage to the steel foundry-men to be able to make steel of given properties, using alloys that can be recovered from scrap, or most conveniently or cheaply bought, rather than a particular formula adopted in the interest of standardization. The heat-treatment appropriate to securing a given result in a given steel is well known to be closely related to composition. For example, molybdenum steels are not much softened by tempering except at rather high temperatures. Highly alloyed steels are "air-hardening," and on cooling in air behave like carbon steels that have been quenched. With these matters, we do not concern ourselves in this paper, although we recognize their importance. The entire picture evidently will be very complex and can be brought within accurate understanding only if our knowledge of test results can be coordinated in terms of general principles.

Jan 1, 1944

By Myron A. Pugacz, Frank S. McKenna, Clarence E. Jackson

The notched-bar impact test has proved worth while in certain applications as a test for control of the quality or the heat-treatment of steel. In view of the serious thought that even so simple a test as the tensile test has evoked during the past years, it is not surprising that the notched-bar impact test should have inspired much experimental work. The correlation of the great number of data has not been successful, although steady progress has been made toward a better understanding of this test. Progress has been made, especially, in the isolation of the effects of the many variables that control the results. The stress system imposed on a specimen with a notch is so complicated and unpredictable that no simple evaluation of the test has been possible. Because of this uncertainty, many engineers hesitate to use the notched-bar impact test, and this attitude may well continue until a better understanding of the effects of the variables in the test are available. Without doubt, any additional data that may be presented should be accompanied by as complete a description of the - details of test as possible, so that it may be added to the general fund of information that is to serve as the basis for the theory of the notched-bar impact test. The many factors that may control the test results have been pointed out repeatedly. The importance of the effect of the type and dimensions of the specimen has been recognized. Most of the work reported by American investigators has been limited to small-size (Charpy) specimens tested as a simple beam; two types of notches (Fig. I) have been commonly used. Considerable data have also been presented by many investigators using a small specimen tested as a cantilever beam; this commonly being called the Izod test. Here, however, a shear component of stress makes the stress system even more complex than that present in the simple beam type of test, hence a critical analysis is difficult. Much work has also been reported by investigators using the tension type of specimen. A second variable that must be controlled is the testing temperature. An indication that the tests were performed at room temperature is not sufficient, since in many steels a variation of a few degrees in the actual testing temperature may be sufficient to give an entirely different range of results. Other factors, such as the composition and condition of the material being tested and the speed of test, should also be considered. Many investigators have contributed data and theoretical discussions on the problems encountered in notched-bar test-

Jan 1, 1944

By John H. Hollomon, C. Zener

It is commonly recognized that a given material may be described as ductile or brittle only with reference to the conditions of test. Thus under the usual test conditions quartz is brittle, but under high pressures it is ductile. Salts that are brittle at room temperature become ductile at elevated temperatures. Pitch, brittle with respect to rapid loads, flows at low rates of loading. Pearlitic steel, ductile under the usual conditions of test, may be embrittled under the proper conditions of combined stresses, temperature, and rate of loading. Earlier Investigations A clear analysis of the conditions necessary for plastic flow and for fracture was first given by LudwikI1 who introduced two types of stress, the "flow stress" and the "stress at fracture." These stresses may refer to tensile or to shear stresses, or, in fact, to any type of stress. Ludwik considered these two stresses to be independent of one another, functions of the conditions of test and of the prior history of the material. For the purpose of analysis. both a Flow stress and a stress at fracture can be envisaged as functions of strain over the entire range from zero to infinite strain. Thus, the material is brittle if the stress at fracturc is less than the flow stress and ductile if the reverse is true. According to Ludwik&apos;s analysis, the problem of determining the effects of combined stresses, of temperature and of strain rate upon the behavior of metals reduces to a problem of determining the effect of these variables upon the flow stress and upon the stress at fracture. In the present paper, methods are described for determining the effects of two of these variables, temperature and strain rate, and examples are given of the dependence of tlow stress and stress at fracture, upon these two variables. The effect of combined stresses will be discussed in a succeeding paper. The flow stress may be determined from a load-diameter curve. Load-diameter curves were obtained over a wide range of temperature and over the limited range of strain rates obtainable with the lever-type Riehle machine used. The curves were then converted to an extremely wide range of strain rate by making use of the equivalence of the effects of changes in strain rate and changes in temperature, previously proposed2 and demonstrated3 by the authors. According to this principle of equivalence, strain rate e and temperature T affect the flow stress only through a single parameter-p of the form: p = eeQ/RT 111 In this equation, R is the gas constant (2 cal. per gram mol per deg. C.), and Q is a heat of activation, which varies from material to material, and may depend upon the strain, but not upon the strain rate or the temperature. There is associated with every value of p a flow-stress curve. article of strain rate and of temperature that give the same p have the same flow-stress curve. Therefore, merely by changing the temperature of test, the effect of changing the strain rate may be obtained. Thus, under isothermal conditions, the material will behave the same at

Jan 1, 1944

By John H. Hollomon

The interpretation of notched-bar impact results has been a matter of controversy since the introduction of more or less standard tests by Fremont,&apos; Charpy2 and others at the turn of the century. Many investigators3-l1 have contributed to the understanding of the significance of such tests. Several symposiums12,13 have been held with the express purpose of discussing the significance and interpretation of the impact tests. It is not the purpose of this paper to review all these contributions to the development of the knowledge on this subject, but rather to present an interpretation of notched-bar impact tests that appears to be in agreement with the available published data. Fundamentally, the interpretation discussed in this paper of the brittle failure of some steels in notched-bar impact test is similar to the qualitative analysis presented by Ludwik3 in the I92o&apos;s. Essentially, Ludwik stated that the function of the notch was to increase the tensile stress necessary for yielding, and that brittle failure occurred when the stress necessary for yielding exceeded the normal stress required for fracture (with no plastic deformation). Ludwik, however, had no means of measuring this normal stress necessary for failure of a plastically* undeformed metal, therefore he could not extend his interpretation beyond the qualitative stage. Kuntze14 and recently Mc-Adam15 attempted to determine the effect of deformation on the stress necessary for fracture by testing, in tension, specimens notched to various depths and angles. Because of the uncertainties in Kuntze&apos;s (and McAdam&apos;s) analysis of the stresses (which have been pointed out by Sachs16) and the inherent nonuniformity in the stress distribution in notched bars, the results of such investigations are difficult to interpret. A more direct method of measuring the effect of deformation on the fracture stress was suggested in previous papers"-18 and has been utilized in the present investigation. The present paper concerns itself primarily with the behavior of notched impact specimens. The effects of strain rate, temperature, and stress distribution, which are discussed with reference to the impact specimen, apply just as well to the behavior of metal at the bases of notches in any engineering structure. All that is necessary is to determine the stress distribution in the structure at the base of the notches.

Jan 1, 1944

By Nicholas Kowall, K. L. Clark

Maximum furnace efficiency and close control of final steel composition demand that the steel melter be able to follow closely the variations in the carbon content of the bath. For many years, the fracture test has been used by melters for estimating carbon, because it requires only a very short time to pour a sample into a chill mold, cool it in water, break it with a sledge hammer, and observe the fracture. After long experience gained from the observation of such fractures, most melters are able to estimate the carbon content of steel with amazing accuracy, particularly in the lower carbon ranges. Notwithstanding the utility of the fracture test, there has been widespread interest in other methods for rapid carbon determination to supplement it and to ensure against possible errors in human judgment. Several methods, based upon measurement of magnetic properties as functions of carbon content, have been described in the literature1-6 and have been found to give reasonably reliable results in plant practice when scrap composition is known and controlled. A difficulty encountered in the use of analyzers of the magnetic type is that alloying elements do change the relationship between carbon content and magnetic properties and it becomes necessary to establish calibration curves for all the expected combinations of alloy residuals that are not oxidized in the bath. The work reported here is of an investigation of a method that is independent of alloying elements normally present in constructional steels, being based upon the relatively well-known fact that in plain carbon and low-alloy steels martensitic hardness is a function of carbon content alone. Work oF Other Investigators In I938, Burns, Moore and Archer published & curve? that showed that the hardness of martensite is a function of carbon from 0.10 to 0.50 per cent and is independent of grain size or alloy content, at least within the rallge found in construc-tional S.A.E. compositions. Some of the deeper hardening types investigated, however, contained carbon to a maximum of only o.2o per cent. Using this principle, Kern8 developed a method of rapid carbon determination for S.A.E 43xx steels, His procedure consisted of chill-casting a test bar that was large enough to give a a that could be prepared for Brinell indentations. The test piece was quenched immediately after solidi fication was complete and hardness readings were taken, so that the carbon content could he read from an experimentally determined curve giving the relationship between as-quenched hardness and carbon. Experimental Work Although Kern&apos;s work had been done with a relatively deep-hardening steel, it

Jan 1, 1944

By Eugene F. Poncelet

This paper attempts to analyze the phenomena involved in the fracture of brittle solids by simple compression. Glass squares standing on edge, and compressed between two parallel steel jaws, developed jagged fractures, roughly parallel to the compression. Polarized light disclosed the presence of high local stress concentrations indicating poor contact all along the contact surfaces with the steel jaws. Teszar has shown that partial contact between the jaws and such a compressed solid causes tensile stresses in the free surfaces of the solid normal to the compression. Furthermore, Scoble has shown that in brittle solids fractures are caused by, and develop normally to, a sufficient tensile stress. It follows that such "partial-contact" cracks must be expected. With optically flat jaws and specimens, no "partial-contact" cracks developed. Instead, very smooth cracks vertical to the compression appeared &apos;upon release of the pressure. Investigation showed that the friction with the rigid steel opposed the return of the glass to its original width, after creeping on the steel as compression built up, thus setting up tensile stresses in the glass surfaces. It was not found possible to eliminate these "release" cracks. Compressed to destruction, such specimens flew to dust. A Microflash photograph taken during the explosive disintegration revealed: (I) oblique parallel fragmentation cracks, 30" off the direction of the compression; (2) transverse forking fragmentation cracks, normal to the former; (3) release cracks parallel to the compression; (4) a disintegration cloud. Given a distribution of submicroscopic cracks of random orientation throughout the glass, Griffith has shown the highest tensile stresses to be located at the tip of the cracks 30" off the direction of the compression. Although the preexistence of such cracks or flaws in unstressed glass is doubtful, they can be generated by the distorting forces set up by the compression itself. Atoms, in a structure held together by Morse-type forces or bonds, have under tension both a stable and an unstable state-of equilibrium. The difference in energy level between these two states is a function of the tension, and this difference must be borrowed from the thermal energy level of the bonds to reach the unstable state and result in a broken bond. As the fraction of the bonds having at any instant a sufficient thermal energy level is a known function of that level, it is possible to determine, in function of the prevailing tension, the fraction of the bonds that are broken. Upon breaking of the bond uniting two atoms at the tip of an advancing crack, the two atoms accelerate away from each other, causing in the solid propagation of a

Jan 1, 1944

By Carl L. Shapiro, Jerome and Strauss

This is a critical examination of the theory that the amount of carbon necessary to form the iron-carbon (carbide) eutectoid is lowered by the addition of any carbide-forming element. Although this theory has been built up over a long period of years, it appears, in the light of recent published investigations upon the ternary constitutional diagrams of iron with carbon and other alloying elements, to be no longer tenable. A survey of these new results, summarized below, shows that (as is known) some metals lower the carbon content of the iron-carbon (carbide) eutectoid, whereas others raise it, but (as not heretofore clearly set forth) some first move the eutectoid in one direction and then, at higher concentrations, shift it in the opposite direction. Moreover, these differences in behavior exist even among the common alloying metals classed as carbide formers. PART I Influence of Body-centered Cubic Elements The effects of the various body-centered cubic metals (chromium, tungsten, molybdenum, vanadium, columbium and tan. talum) are reviewed individually. Iron-carbon-chromium System.—In the monograph on Alloys of Iron and Chromium, Kinzel and Crafts1 concluded that the carbon content of the eutectoid is lowered by increasing the chromium content. The quantitative influence of chromium on the eutectoid point of iron-carbon alloys was shown by Monypenny2 (Fig. I) and no data have been forthcoming to refute his findings. Iron-carbon-tungsten System.—Gregg,3 in the monograph on Alloys of Iron and Tungsten, accepted the data showing that tungsten decreases the amount of carbon required to form the eutectoid. The influence of tungsten on the eutectoid percentage of carbon as determined by Oberhoffer and Daeves4 is shown in Fig. 2; these results have received general approval. , I ron-carbon-molybdenum System.—In the monograph on Alloys of Iron and Molybdenum, Gregg5 reviewed the work of Guillet,6 Swinden,7 and ReedI8 all showing that molybdenum lowered the carbon content of the eutectoid, whereas Takei9 contradicted this conclusion. Svetchnikoff and Alferova,10 a little later, showed that large additions of molybdenum shift the eutectoid to the right. These last-named investigators found that molybdenum, up to 1.2 per cent, shifts the pearlite point and the point of maximum solubility of cementite in the gamma phase only slightly in the direction of lower carbon content; on the other hand, increasing amounts of molyb-S

Jan 1, 1944

By James K. Stanley

Preferred orientation, particularly in irons and low-carbon steel, is a phenomenon that is both of considerable importance and theoretical interest. At times it is a liability and at other times an asset. In deep-drawing operations, preferred orientation is extremely undesirable because it necessitates trimming operations and increases scrap loss. Furthermore, oriented metals are likely to crack more easily than randomly oriented material because the forming of symmetrical and unsymmetrical shapes out of preferentially oriented metals and alloys increases the probability of rupture in regions of high stress, owing to differential ductility.&apos; In the electrical industry, on the other hand, preferentially oriented silicon irons are in demand for transformer application because of the improved magnetic permeabilities in the rolling direction.2 This phenomenon of preferred orientation in soft magnetic materials has been responsible for the tremendous improvement in transformer design and construction in recent years. Directional properties in metals have received a great deal of attention in the metallurnical -literature,3-9 in which much of the information reported about orientation has been obtained by conventional methods, mechanicai properties and X-rays. A wealth of data has been obtained and often at a great expenditure of time. The recent introduction of the magnetic torque measurements on ferromagnetic materials provides a very simple and rapid method of evaluating orientation. The judicious use of the method can supply important information, but it should be borne in mind that such studies must be supplemented by X-rays, optical methods,10 and etch and pressure figures" to get a rational understanding of the orientation phenomena. No claims are made that the magnetic torque of evaluating orientation will reveal the behavior of the metal in deep drawing. For this purpose the accepted tests for deep-drawing quality must be used. For a good drawing stock, which must have low impurities, desirable grain size, ductility, strength, hardness, good surface, random orientation, and good recrystallization behavior, it cannot be expected that any simple test will be satisfactory for appraising all the factors. The only factor on which the magnetic method can be used is orientation, which is, of course, of considerable importance. When directionality can cause a 10 to 15 per cent change in tensile strength and a IOO to 300 per cent change in tear length,12 it goes without saying that a reliable as well as rapid method for detecting these changes would be desirable. There are certain inherent advantages in testing orientation by the torque method: The method is rapid with the proper type of equipment; no elaborate preparation of specimens is required—it is only necessary to punch or machine a I-in. disk of the sheet material and insert it into the testing device.

Jan 1, 1944

By C. G. Dunn

Many investigations have been made concerning the nature of plastic deformation and recrystallization of metals either in the form of polycrystalline materials or in the form of single crystals. However, similar work on strip materials composed of large grains as thick as the strip and having a high degree of preferred crystal oricntation has not been carried out extensively. Such materials are ideal not only for studying changes in single crystals under conditions where neighboring grains exert their influences but also for obtaining the complete change in orientation of a grain or group of grains during the course of plastic deformation and subsequent recrystallization. It is well known that first-order twins in the form of Neumann bands may be produced during the plastic deformation of ferrite crystals, particularly silicon ferrite crystals.l--3 Furthermore, it is believed that high-stress regions exist in the vicinity of these bands4. and it has been said that these banded regions would be active in recrystallization processes.5 Evidence to that effect in silicon ferrite had already been presented with photomicrographs showing recrystallization among Neumann bands during the early stages of recrystallizati~n.5,6 Similar evidence has been published for nonferrous metals5 Merging of fine parallel deformation bands during annealing to form twin bands of ordinary appearance in alpha brass has been offered not only as evidence of an active role being played by mechanical twins but also as evidence that such twins cxisted prior to recrystalli~ation.5 Proof that such new structures are actually first-order twins, or even twins at all, must be considered inadequate except for those cases where X-ray or optical data have been obtained to confirm the necessary oricntation relationship.7,8 A. B. Greninger has obtained excellent iliustrations of annealing twins in alpha iron.9 Since his material was previously deformed by sharp hammering, a process that generally induces Neumann bands, the existence of twins following annealing might suggest that they grew from mechanical twins. In connection with transformation twins in alpha iron, Greninger reported that grains containing three twin orientations occurred rarely and none occurred with three sets of well-developed bands.9 The work at the Pittsfield Works Laboratory on silicon ferrite in the form of large-grained strip steel deformed a small amount and annealed to partially recrystallize the grains indicates that the deformation and recrystallization processes that lead to annealing twins involvc more complex processes than the formation of Neumann bands and the growth of such bands. Some groups of annealing twins are obtained which contain not only three well-developed twin structures, but also contain more than one order of twins. It is also shown, in one case, that an interrelated group of twins did not arise within one single parent grain and, furthermore, orientations of grains in the group

Jan 1, 1944

By G. V. Smith, C. O. Tarr, R. F. Miller

Metallurgists have long recognized that the Fe3C type of carbide is not a stable phase in steel and that, given sufficient time, it will decompose with formation of graphite, at least at temperatures below about 205o°F.l This slow graphitization has never been of much concern to users of hypoeutectoid steels, for in such steels it occurs only during prolonged exposure at elevated temperature. In I935, Kinzel and Moore2 reported complete graphitization of the carbide of a 0. I5 per cent carbon steel that had been in service for about 26,000 hr. at a temperature of about IIOO° to 12oo°F. In discussing this paper, both Mathews and Sauveur reported graphitization of slightly hypereutectoid steels. In an extensive investigation of graphitization of high-purity iron-carbon alloys, Wells1 produced graphite at 7oo°C. (I29o°F.) in an alloy containing as little as 0.13 per cent carbon, and showed that graphite may precipitate either directly from austenite or from decomposition of Fe3C, also that the rate of graphitization tends to increase with increase of temperature, at least up to a certain point, and with the presence of graphite nuclei. Jenkins, Mellor and Jenkinson,3 studying the structural changes in carbon steels ranging from 0.17 to 1.14 per cent carbon during stress-rupture tests at elevated temperature, observed graphite in an aluminum-killed 0.40 per cent carbon steel after fracture in 4340 hr. under a stress of 17,900 lb. per sq. in. at 840°F. and in many of the steels after stress-rupture test at 12oo°F. Unstressed samples of 0.60, 0.86 and I.I4 per cent carbon steels graphitized almost completely in 360 hr. at I200°F., while samples of 0.90 and 1.10 per cent carbon steels were somewhat graphitized, and steels containing 0.24, 0.40 and 0.57 per cent carbon showed no sign of graphite. Their results indicate that graphite precipitates the more readily the higher the carbon content, though this tendency is influenced to some extent by deoxidation practice, and that graphitization is accelerated by plastic deformation. In a recent study of the graphitization of 0.4 and 0.6 per cent carbon steel strip, made by M. A. Hughes,4 it was found that at I2oo°F. graphite appeared after 72 hr. in aluminum-killed but not in silicon-killed steel, and that the rate of graphitization was increased by slow cooling from I6oo°F. and by cold-working prior to annealing. In creep tests of normalized 0.15 per cent carbon steel killed with 2.5 Ib. of aluminum per ton, at the U. S. Steel Corporation laboratory at Kearny, spheroidization and some graphitization were found after 3000 hr. at Iooo°F. under a stress as low as 1500 lb. per sq. inch. .

Jan 1, 1944

By Taylor Lyman, E. P. Klier

The structures formed when austenite is quenched to subcritical temperatures and allowed to transform isothermally have been the subject of intensive study since the work of Davcnport and Bain.&apos; Isothermal transformation diagrams summarizing the results of many of these studies have become widely familiar to metallurgists. Of particular interest to metallographers are the dark-etchingl acicular products of transformation formed by isothermal reaction below the temperature of maximum velocity of the austenite to pearlite reaction. These products, the bainite structures, can he formed in a wide variety of steels. However, the constitution of bainite is not well understood and divergent views have been expressed as to its mode of formation. In this investigation a combination of dilatometric, microscopic and X-ray methods has been brought to bear upon the problem in the hope of some elucidation of the bainite reaction as it occurs in hypo-eutectoid steels. Mechanism OF Bainite Formation Davenport and Bainl considered the mechanism of bainite formation to consist of two steps—an allotropic transformation followed by precipitation of carbide. The separation in time of the two processes was considered to be very slight in the upper temperature range and very marked at temperatures just above the martensite range. This concept has been restated by Vilella, Guellich and Bain2 in the form of a definition of the acicular mode of transformation as: The successive, abrupt formation of flat plates of supersaturated ferrite along certain crystallographic planes of the austenite grains; this supersaturated ferrite begins at once to reject carbide palticles, (not lamellae), at a rate depending upon temperature In effect, this is the acicular mode of transformation, even though the temperature be such as to limit the actual life of the quasi-martensite to millionths of a second. The investigation of isothermal decomposition of austenite in certain alloy steels (notably those containing chromium or molybdenum) has revealed that there may be a range of temperatures between the pearlite and bainite reactions in which the austenite decomposes at a relatively low rate.3-6 Further, it is characteristic that in the second region of fast reaction the decomposition of the austenite is incomplete by one reaction but goes to completion by a second reaction. These observations led Wever7 to a description of the bainite reaction as follows: I. The reaction takes place by initial precipi. tation of a martensitic intermediate structure. 2. In the upper temperature range this structure readily decomposes into ferrite and cementite. In the lower range carbon separates in an unknown form. 3. In the upper temperature range the precipitated carbide nucleates the precipitation

Jan 1, 1944

Jan 1, 1944

Jan 1, 1944

By E. C. Skinner

Cardox, which consists essentially of a steel tube containing carbon dioxide compressed to the liquid state, is a trade name designating a device used principally in coal mines to break down coal. The use of Cardox to break down coal was developed in the Middle Western coal fields around 1927 or 1928. At first, a large, heavy tube was used, requiring many parts. Through experimentation and technologic improvement, the weight of the tube has been brought down from 88 lb. to 20 lb. and the new, light tube makes use of larger volumes of CO2 at lower pressures than formerly was thought possible. This blasting method is extensively used today in coal mines and probably one tenth of the bituminous coal produced in the United States is prepared with Cardox. Construction and Application As used in the coal mine, Cardox looks like a piece of steel pipe 2 to 3 in. in diameter and 3 to 5 ft. long. When it is necessary to fire a shot, the tube is wired with two leg wires that are long enough so that when the tube is pushed the desired distance into the hole the wires will protrude 5 to 6 in. It has been found that No. 18 insulated copper annunciator wire is the best material for leg wires. A two-conductor rubber-covered shot-firing cable of sufficient length is then attached to the leg wires. A 2 to 6-volt current is applied, either by means of shot-firing batteries or the standard type of shot-firing generator. Upon the application of the current, the charge in the cartridge is set off. Because the breaking action upon the coal is supplied by the relatively slow physical expansion of the carbon dioxide gas rather than by the rapid chemical formation of gases as in more familiar explosives, the result is a slow heaving action, somewhat similar to that produced by black powder, rather than a shap detonating effect. Permissible powder does its work at roughly ten times the pressures in use with Cardox. The escaped gas from a Cardox shot apparently works along the planes of weakness in the coal face, such as the coal cleats, the edges of the cut, and along the top of the seam, breaking off the coal toward the free faces and heaving the mass of coal outward. Cardox tubes are manufactured in various sizes to take care of variable conditions of seam size, undercut depth, cleatage, coal hardness, and so forth. The tubes range in diameter from 2 to 3 in. (Table I) and the normal CO2 charge is from 24 to 96 oz. For any one tube size, several sizes of shear disks are available, thus excellent control of the type of shooting desired is possible. In general, local experience and experimentation dictate the size of tube chosen for any particular job. For high coal, and deeper or wider cuts, a larger size is chosen to start with, and the opposite is true for low coal, softer coal, or small cuts. After the tube size has been experimentally selected, tests are run in the mine to determine how many shot holes are needed and where the holes should be placed. The size of the disk,

Jan 1, 1944

By H. P. Greenwald

THIs paper brings forward a discussion that was prepared for the meeting of the Coal Division in Chicago in 1938.1 War in Europe less than a year after that meeting, followed by our defense preparations and entry into the conflict, caused general cessation of large-scale experimentation on the subject, and it is best to confine this paper to events in the United States during the five-year period since the preceding paper was written. The views of members of the Coal Division&apos;s Committee2 on Rock-dust-ing for 1943 were obtained before this paper was written and the manuscript was reviewed by them. Extent of Rock-dusting Statistics on the use of rock dust in the United States during the years 1930-1933, appearing on page 97 of Volume 139 of the Transactions are extended in Table I herein through the year 1941. The results through 1933 did not appear encouraging, but there has been improve-ment since that date. It has always been true that the larger operations were the ones that used rock dust. In 1941 only 10 per cent of the mines in the country used rock dust, but they produced 57 per cent of the coal, employed just under 50 per cent of the miners, and accounted for 52 per cent of the man-hours. Unfortunately, collection and compilation of these statistics are slow procedures, and figures dealing with the tremendous war expansion of the industry are not likely to be available for a year or more. In 1941 the five leading states in regard to percentage of man-hours worked in mines using rock dust were: Utah, 92.1; Wyoming, 79.3; Alabama, 77.4; New Mexico, 72.5; West Virginia, 65.3. The first four states were the same as in 1933, but West Virginia displaced Washington in fifth place. On the basis of pounds of rock dust used per ton of coal, the five leading states in

Jan 1, 1944

By Raymond Mancha

The use of blower fans and tubina- for auxiliary face ventilation is a somewhat controversial subject. Most authorities agree upon the advantages of this system over the maintenance of line brattice for dead-end ventilation. They also recognize the system&apos;s disadvantages. However, there is considerable disagreement as to the proper relation of the advantages to the disadvantages. It is the purpose of this report to present the opinions of four authorities of diversified occupation and permit the reader to form his own opinions on the subject. ORsErvers Carel Robinson is a mining engineer consultant of wide repute, who has a background of operating experience. Thomas G. Fear is a mine operator whose present position is that of chief engineer for the Hanna Coal Co. at St. Clairsville, Ohio. E. H. Denny is chief of the Coal Mine Inspection Division of the U. S. Bureau of Mines, and is a very able engineer whose past experience well qualifies him to appraise this problem. Cloyd M. Smith, editor of the periodical Mechanization, is a ventilation consultant. For a number of years he was a member of the Mining Department of the University of Illinois and has studied mine ventilation for many years. It is Mr. Robinson,s opinion that closely spaced breakthroughs, although conducive to low gas accumulation past the last open crosscut during the driving of entries, are difficult to maintain and are constant Sources of fugitive air. Jute or canvas brattice is suitable for entry driving with

Jan 1, 1944

By C. E. Brown, D. C. Helms, O. W. Shimer

The early history and progress of anthracite stripping, from the first known operation at Summit Hill in 1821 through 1917, was covered in 1917 in a paper by J. B. Warriner,1 then chief engineer, now president of the Lehigh Navigation Coal Co., and stripping methods between 1917 and 1931 were the subject of a paper in 1931 by H. H. Otto,2 of the Hudson Coal Company. . The present paper is confined to methods used today on pitching beds in the western middle and southern anthracite fields. The anthracite industry, not unlike other large industries, had been affected for more than a decade by the adverse economic conditions of the country. High development and operating costs and the competition of other fuels caused some collieries to be closed temporarily, while others were permanently abandoned. In order to obtain a larger tonnage at a lower development cost, a larger stripping program was put into effect by many companies. In 1932, stripping operations accounted for 3½ million tons, or 7 per cent of the total anthracite production of the year, and in the next 10 years this increased until more than double that amount, or over 14 per cent of the total production, was from stripping operations. These figures represent the total production of the entire anthracite region; unfortunately, the figures have not been separated from the different fields. There are some operations in the southern and middle western fields where the tonnage obtained from stripping amounts to more than 30 per cent of the total colliery production. Stripping operations on pitching beds present difficult problems. Owing to the various geological formations, a different situation is encountered in nearly every stripping pit; and because of the proximity of an overlying bed, it is very often necessary to load the entire overburden into trucks and haul it out of the pit to the dump area, although back filling and casting is done whenever possible. Beds in the areas described in this paper pitch from 20" to 90 and some are on the invert in many sharp folds and faults. Planning The more successful strippings have had adequate engineering analysis. Some work is being done without much preliminary planning, but many strippings would have failed completely if close supervision by the engineering department had not been . maintained. Locations of stripping areas are determined as follows: I. By constructing cross sections over the areas and drilling sufficient diamond-drill or well drill holes to study the strata and to determine the location, thickness

Jan 1, 1944