By W. C. Leslie, R. M. Fisher, K. G. Carroll

J. S. Bowles and J. K. Mackenzie (Commonwealth Scientific and Industrial Research Organization, Mel- bourne, Australia)—The authors are to be congratulated for giving the first direct experimental proof that the observed macroscopic strain accompanying marten-site transformations is not necessarily a shear. We

Jan 1, 1953

Vatukoula, the Fijian equivalent of gold rock, is the name of the community embracing the gold mines owned and operated by Emperor Gold Mining Company Ltd., Loloma (Fiji) Gold Mines, N.L., and' Dolphin Mines Ltd. It is situated in the Tavua Goldfields approximately five miles from the northern coast of Viti Levu, the largest island of the Colony of Fiji.The climate is sub-tropical, there being a definite wet and dry season. The wet season is somewhat variable in length but usually extends from December to March, during which time most of the rainfall for the year is recorded.Although the average annual rainfall is 71 in., more than twice this amount has been recorded. Precipitation at the rate of 5 in. per hour is not uncommon and 15 in. of rain has been registered in 24 hours. The mining methods adopted, therefore, had to suit these wet conditions.The occurrence of gold in the Tavua area has been known since 1872, but it was not until 1932 that discoveries were made which led to the formation of the present operating companies. In 1934 the Emperor Gold Mining Company Ltd. commenced operations, followed in 1935 by the Loloma (Fiji) Gold Mines, N.L., and later by the Fiji Mines Development Ltd., now known as the Dolphin Mines Ltd. Up to the end of 1951 these three mines had produced 2,501,688 tons of ore from which 1,277,881 oz. of fine gold and 347,429oz. of silver were obtained, realizing in Fijian currency £13,025,153.The three mines are situated close togeth.er on contiguous mining leases, and, although under common management, are operated as separate en,tities. Since 1944 all the...

Jan 1, 1953

By Alfred L. Ransome

GOLD output in Alaska in 1950, following a 2-year decline, increased to the highest point since 1942. Tills unexpected gain in production of the Territory's greatest value commodity was largely responsible for the increase in the over-all value of mineral output in the Territory to $17,852,000 from $15,549,000 in 1949. Although coal continued to rank second to gold in value of output, production was slightly less than the record production of 1949. The mining of platinum continued to be an important factor in the mineral industry, with production of crude platinum metals exceeding that of 1949. The output of lead was three times the 1949 production, and silver gained 46 percent over the previous year's total. Copper and zinc production-entirely as byproducts from other ores-showed an increase, but remained minor. Production of tin was relatively small, but substantially above the total for 1949.

Jan 1, 1953

"THE CONCEPT of energy as a commodity, while not entirely new, is not as widespread as the importance of the idea to this modern world would lead one to expect. The growth in the supply and use of energy over the past years has been tremendous, but our very closeness and familiarity have somewhat distorted the viewpoint, particularly of the younger generation. To many of us who remember the wonderful satisfaction of our first responsibility for directing two horsepower hitched to a farm cart or hay wagon, there still arises a feeling of some awe at the casual flick of the switch with which our sons and daughters summon to their convenience the service of some one hundred or more horsepower.Energy is the vital component of our existence and, no matter what contempt our day-to-day familiarity may •breed, it is wise to .pause from time to time and consider our national energy standing. Have we still capital in the bank? Are our expenditures wisely •conceived and well directed? Is provision being made for the years •ahead for the needs of our children and our children's children?"

Jan 1, 1953

By R. R. Morral, F. M. Krill, K. T. Aust

THE occurrence of twins in aluminum ingots cast under certain conditions has been well established. For instance, Herenguel and Lacombe1,2 have observed a twinned columnar structure in 99.5 and 99.9 pct Al, solidified by continuous or semicontinuous casting. The structure, which they termed "basaltic," appears in the form of elongated crystalline fibers of alternating luster. Herenguel and Lacombe2 found sections of flat crystalline plates composed of twin crystal plates, in which the twin plane (111) and a [I121 direction contained in the twin plane are parallel to the principal heat gradient. This orientation relationship is different from the usual orientation texture observed in cast face-centered cubic metals, where the [100] direction is approximately parallel to the long columnar axes lying in the direction of growth." A large amount of twinning has also been observed by the present authors in semicontinuous cast aluminum of 99.2 pct purity, Fig. 1. Mondolfo4 has suggested that the twinned cast structure forms by a deformation twinning process as the result of uneven cooling stresses within the ingots. This suggestion appears to be inconsistent with the large amount of twinning observed in the semicontinuous cast ingots and with the large difference of dendritic

Jan 1, 1953

By K. C. Li

ARSENIC and antimony are always grouped together by chemists, since they are both members of group V of the periodic table of elements and exhibit a general similarity in the formation of compounds. Metallurgists generally think of them as less closely related because they do not have similar uses. In metallurgical operations, especially lead and copper smelting, arsenic tends to go off as a vapor phase and collect as fume in the flues, while antimony tends to remain with the bullion. Broadly speaking, the frequency of occurrence, practical utility and the effects on associated metals of arsenic and antimony are such that the metallurgist is inclined to think of arsenic as a troublesome impurity in ores, but of antimony as a valuable constituent that is recovered either as a byproduct or through the metallurgical treatment of antimony ores. Estimating the world production of arsenic as about 40,000 tons annually, probably not more than about 200 tons yearly is produced and used in metallic form, whereas one half of the approximately 40,000 tons of antimony produced annually is metallic. ARSENIC The modern uses of arsenic differ little from ancient ones. Though it has been known from early times, its poisonous quality is almost the only one that yet finds extensive use. The shift in the past century from its utilization in poisoning people to the poisoning of insects, beginning in 1860, has not only led to a considerable increase in

Jan 1, 1953

By J. J. Gilman

RECENT experiments have shown that the mar-tensite reaction in a standard tool steel is influenced by the history of the reacting austenite. The martensite reaction proceeds to a given extent at a higher temperature in austenite formed from an annealed spheroidal structure than it does in austenite formed from tempered martensite: that is to say, a prequench lowers the temperature range of the martensite reaction in this steel. Furthermore, a prequench alters the appearance of the martensite as compared to martensite formed from "virgin" austenite. The steel used for this work was a manganese nondeforming tool steel of the following composition: C, 0.85 pct; Mn, 1.43; Si, 0.23; Ni, 0.12; Cr, 0.59; and W, 0.59. A piece from a rolled bar was forged to Vz in. sq and annealed to a spheroidal structure. Disks 1/8 in. thick were used in the experiments. Several sets of the specimens were prepared and austenitized in lead at 1475°F. Three sets were held at 1475°F for 15 min, quenched in water, and immediately reheated to 1475°F. After this quench the three sets were held for 5 min, 30 min, and 3 hr, respectively, at 1475°F and then the individual specimens in each set were quenched in molten baths to 325", 300°, and 275ºF, respectively, and held for 15 sec. Immediately after the quenching treatments? the specimens were tempered at 600°F for 30 sec to darken the martensite and then were quenched in water. The holding times were short enough to avoid isothermal transformation. Three other sets of specimens were given the same final quenching treatments as the first three, but they were austenitized at 1475°F for 20 min, 35 min, and 3 hr and 15 min, respectively, without an intermediate water quench. The two individual specimens from each set were quenched together in order to eliminate quenching errors. Several experiments were run in this way but only the six sets referred to are described in detail because they all yielded essentially the same results. By means of the stated heat treatments the martensite reaction was investigated for: 1—austenite formed from an annealed structure, and 2— austenite formed from tempered martensite. The martensite reactions of the two types of austenite differed significantly. This is shown by Figs. 1 and 2. Comparison of the photographs on the left in Figs. 1 and 2 with those on the right shows that less martensite was formed by a quench to a given temperature from prequenched austenite than from austenite formed from an annealed structure, that is, the prequench suppressed the martensite reaction. The effect was observed for specimens austenitized 20 min, 35 min, and 3 hr and 15 min. A comparison of Figs. 1 and 2 shows that the martensite reactions in both sets of specimens occurred at lower temperatures with increased austenitization time. This was caused by the increased dissolution of residual carbides with time at 1475°F. However, the difference in amount of martensite formed in prequenched austenite as compared to virgin austenite was approximately the same for all three austenitization times. One further observation should be noted. The needles of the martensite formed from virgin austenite are somewhat longer on the average and show less of a tendency to cluster than those of martensite formed from prequenched austenite. This causes the martensite on the right in Figs. 1 and 2 to have a more acicular appearance than the martensite on the left. Since the sets of specimens used in this work were austenitized for identical total lengths of time and the effect of a prequench on the martensite reaction existed for specimens held at the austenitizing tem-

Jan 1, 1953

By William P. Jones

THE consumption of sulphuric acid, one of the most important commodities in our modern industrial world, is often used as a barometer for industrial activity. The economics of acid manufacture are largely dependent upon the location of the place of consumption and the availability of raw materials in that locality. Sulphuric acid is made from SO,, oxygen from the air and water. Therefore the sulphur dioxide is the only raw material to be considered in an economic study. SO, can be obtained from almost any material containing inorganic sulphur, such as elemental sulphur, pyrites, coal, sour gas and oil, metallurgical gases, waste gases, or gypsum and anhydrite. Many tons of acid can also be reclaimed by the recovery and concentration of spent acids. The aim of this paper is to present a guide to the economic aspects to be considered when the installation of an acid plant is contemplated. It must be remembered that 1 ton of elemental sulphur produces 3 tons of sulphuric acid and that the shipping of sulphuric acid by tank car is very costly. The size of the plant must also be given careful consideration. For instance, operation of a plant producing 5 tons of acid per day might be warranted in Brazil or Pakistan, whereas economics usually favor buying quantities up to 50 tons per day for use within the United States. Elemental sulphur, when available at the low price of 1M4 per lb delivered at an acid plant, has always been the raw material most frequently used for sulphuric acid. All conditions favor its use at this price. The so-called sulphur shortage has been the subject of so many technical papers, magazine articles, and newspaper items during the past y6ar that it hardly seems necessary to mention it again, but a very brief review of the matter will serve as a foundation for the discussion that follows. There is no shortage of sulphur. Only a shortage of low-cost Frasch-mined brimstone exists today. Other more expensive sulphur-bearing materials are plentiful, both in the United States and abroad. The low cost of Frasch-mined brimstone has discouraged the development of higher cost sources. However, the approaching depletion of Gulf Coast dome deposits and the greatly increased demand for sulphur here and abroad have made it necessary for industry to prepare for conversion to utilize sulphur in other forms. For future planning this situation must be considered permanent and not temporary. This conclusion is based on the fact that although sulphur demand will continue to rise, the production of Frasch-mined sulphur probably will not increase greatly beyond its present level of about 5,000,000 long tons per year. The International Materials Conference in Washington estimates 1952 requirements of the free world at nearly 7 million long tons; and the Defense Production Administration has recently set a new goal for 8,400,000 long tons annual domestic production by 1955. The total sulphur equivalent produced in this country in 1950 was 6 million tons. What, then, are the alternatives for the manufacture of the vital chemical, sulphuric acid? Today about 85 pct of this country's sulphur, and nearly 50 pct of the world supply, comes from our Gulf Coast salt domes and is extracted from the earth by Frasch's hot water process. The Gulf Coast salt dome deposits have been the most important known natural deposits in the world, producing 90 million tons of sulphur during the past 50 years. However, at the present rate of extraction these deposits cannot be expected to last indefinitely. Pyrites Pyrites are, and have been for many years, the source of more than 50 pct of the world's sulphur requirements. The principal use, of course, is in the manufacture of sulphuric acid. The use of pyrites in the United States has diminished greatly because of the availability of low cost native sulphur, but pyrites have continued a major source of sulphur in many other countries. The most available pyrites for use in this country are in the form of lump pyritic ore and in mill tailings from flotation of other minerals such as lead, zinc, copper, gold, and silver. An important factor, when the use of pyrites for acid manufacture is being considered, is the disposal of calcine. A ton of sulphuric acid requires approximately ton of high-grade pyrite and results in 1/2 ton of calcine. If the calcine is a fairly pure oxide, free of harmful impurities, it can be used, after sintering, in an iron blast furnace burden. Its value might be as high as 15d per unit of Fe at the blast furnace; or possibly $10.00 per ton of sinter, if it assays 65 pct Fe. This might result in a credit of $4.00 per ton of acid if the sintering plant and blast furnace are both located adjacent to the acid plant. On the other hand, several factors must be considered before this credit can be realized, i.e., freight to blast furnace, availability of sintering facilities, methods of eliminating impurities, and the removal of valuable metal values. In some locations it would be most economical to dump the calcines.

Jan 1, 1953

By L. B. Ticknor, M. B. Bever

An isothermal calorimeter suitable for measurements of heats of solution in liquid tin as solvent is described. Measurements of the heats of solution of gold, silver, copper, and a gold-silver alloy are reported. The heat of formation of this gold-silver alloy is also reported. HEATS of solution in liquids can be determined directly, but few such data have been published for metals as solvents. Knowledge of heats of solution is desirable because it contributes to the general understanding of energy relations in metallic solutions. Thermochemical measurements of this type also furnish answers to specific problems: For example, from the heats of solution of an alloy and of a mixture of its constituent elements in a given solvent, the heat of formation of the alloy may be found. Similarly, differences in the energy content of samples of the same metal in two different states, such as the annealed and cold worked states, may be determined. In the work reported here, gold, silver, and an alloy of gold and silver were dissolved in liquid tin at 240°C and gold, silver, and copper were dissolved in tin at 300 °C. The experiments yielded the heats of solution of these metals in tin. The heat of formation of the gold-silver alloy was also determined. The same calorimetric method is being used to measure the energy stored in metals during cold working and preliminary results have been published.' Equipment and Experimental Procedure The isothermal calorimeter used in this work, Fig. 1, consisted of a Dewar flask completely immersed in a constant-temperature salt bath. A long neck provided space for thermocouple leads and a stirrer shaft and permitted the injection of solute samples. The metal bath in the calorimeter flask was stirred at about 100 rpm by a small glass impeller driven by a constant-speed motor. The shaft of the stirrer passed through a Wilson vacuum seal.2 All measurements were made under vacuum in order to eliminate temperature disturbances resulting from gas convection and to prevent the oxidation of tin. The calorimeter flask was joined by an all-glass connecting line to a gas-control system which made possible the use of a protective atmosphere of deoxidized and dried hydrogen. At the operating temperature of the calorimeter tin oxide was not reduced by hydrogen, presumably because the reaction rate was too slow. Part of the closed system was a removable side tube through which the solute sample could be introduced and in which it was held at a temperature of 0°C prior to injection into the metal bath. The salt bath containing a mixture of sodium, lithium, and potassium nitrates was similar to that described by Beattie3 and was equipped with a stir-

Jan 1, 1953

By F. W. Glaser, Benjamin Post

A LTHOUGH most transition metals form a wide variety of boride compounds, the existence of only one zirconium boride, ZrB2, had been established prior to this investigation.' The crystal structure and some properties of a hitherto unreported zirconium boride, ZrB12, are described in this paper. Only one other dodecaboride of a transition metal, UB12, has been reported up to the present.' Chemical analysis of the new compound showed 44 pct Zr and 56 pct B, compared with 41 pct Zr and 59 pct B computed for ZrB12. The difference is within the range of error of the analytical method employed. ZrB12 shows marked metallic properties. It is obtained as a fine black powder. Measurements of electrical resistivity were made at —79°C, + 22°C and +64°C. At 22°C the electrical resistivity is approximately 60 microhm-cm. Over this range the temperature coefficient of resistivity is +0.00162. The thermal conductivity at room temperature is 0.122 watts per cm per "C. The product of the electrical resistivity and thermal conductivity is therefore 8.05, which is not far from the normal Wiedemann-Franz ratio (approximately 7.5 at room temperature). These measurements were made on hot pressed samples which were not always high density specimens. The hardness of ZrB12 on the Rockwell A scale varies between 92 and 92.5. Crystal Structure Determination Single crystals of ZrB12 of a size suitable for X-ray diffraction analysis could not be obtained and powder samples had to be used. Filtered Cu radiation was used throughout. Powder diagrams were indexed on the basis of a face-centered cubic unit cell. After correction for film shrinkage, a Bradley and Jay extrapolation³ to ? = 90" indicated that a, = 7.408 ±0.002A. The volume of the unit cell is 406.5A.V he assumption that there are four "molecules" of ZrB12 per unit cell leads to an X-ray density of 3.63 g per cc. The measured density is 3.7 g per cc (as measured by the immersion method). Relative intensities of reflections were determined by integrating the intensities of diffraction peaks using the count register of a North American Philips wide range spectrometer. Intensities measured in this way showed good agreement with photographic intensities estimated visually using multiple film techniques. The usual Lorentz, polarization, and multiplicity corrections were applied to the observed intensity measurements. There are striking similarities between ZrB12, and UB12. The unit cell of the latter is also face-centered cubic and contains four molecules. a, = 7.473, compared with 7.408 for ZrB12. The radius ratio rB/rU is 0.57; rB/rZr is 0.54. In both ZrB12, and UB12 the four metal atoms in each unit cell are in special positions; only the boron positions need be determined. The latter may be inferred from the extent to which diffraction of X-rays by the 48 boron atoms reinforces or weakens the diffraction by the metal atoms. This effect is relatively much greater in the case of the zirconium compound. In their determination of the crystal structure of UB12, Berthaut and Blum' assumed holohedral symmetry (space group Oh5 , Fm3m) and reported that the U atoms are in positions 4(a): 000; 01/2 1/2; ½ 0 ½ ; ½ ½; the boron atoms were reported to be in positions 48(i) with x = 1/6: ½xx; ½xx; x½x; x½x; xx½; xx½; ½xx; ½xx; x½x; x½x; xx½; xx½

Jan 1, 1953

By C. R. Breck

THERE has been a running discussion over the-past several years with respect to the life and adequacy of our natural gas reserves.. Some of the experts agree on one phase of the subject at least--that eventually it will be necessary to augment deliveries of natural gas in the northern markets by the development of a more or less comparable synthetic gas made from coal. The purpose of this paper is to point out: 1. It may be later than a good many people think-the demand for additional domestic and commercial pipeline gas in at least one section of the North will probably be felt rather keenly before an adequate synthetic pipeline-gas project, developed on economic lines, could be completed, even if ' initiated in the near future. 2. The evidence is considerable that such a project would be technically sound and economically self-supporting, although the margin of profit at first might be so small and the magnitude of an economic enterprise so great that financing would be impossible without Government aid in some form or other. The part of the country referred to is the heavily populated section in the northeast of the United States. To simplify an examination of the situation, let us take the potential marketing areas within range to the north and east of the three pipelines: 1. Tennessee Gas Transmission Co. as it enters Erie County, New York state. 2. Texas Eastern Transmission Corporation just before the tap that supplies the general Philadelphia area. 3. Transcontinental G& Pipe Line Corporation as it enters the state of New Jersey The sources of gas for these three pipelines are in Texas and Louisiana. The ultimate maximum combined capacity of the three lines at the points stated is approximately 1,200,000,000 cu ft per 24 hr at the maximum load factor probable of attainment in normal operation. The areas supplied by the three lines north and east of the points stated, or assumed as eventual markets, are: 1. Central New York state, from Buffalo to Albany (both inclusive).

Jan 1, 1953

By Strathmore R. B. Cooke, Emert W. Lindroos, Norman F. Schulz

DURING the course of an investigation of the effects of various starch products on hematite and quartz in regard to their separation by flotation, it was found that whereas most starches flocculated suspensions of hematite in water, they did not flocculate similar suspensions of quartz. However, a derivative of whole corn starch containing approximately one tenth aminoethyl group (-—CH,CH2NH2) per glucose unit proved to be an exception. This aminoethyl starch was a very good flocculant for both hematite and quartz, and also possessed the property of depressing both minerals in cationic flotation tests. In view of the widespread use of starch as a flocculating agent of solids in tailing water, pulps, and for coal slimes, ore and various other purposes in sulphide and nonsulphide flotation, attention is called to the effective surface activity of aminoethyl starch in flocculating suspensions of the two minerals investigated. Test Materials The starch products employed included Globe Pearl starch No. 144 and fresh aminoethyl starch, both supplied by the Corn Products Refining Co. Dr. A. L. Elder" has kindly furnished a description The minerals used in the various tests are listed in Table I. Their specific surfaces were determined by the air permeability method, which gave results reproducible to within plus or minus 3 pct. Surface areas obtained by krypton adsorption were greater than the air permeability values by a factor of 2.0 for quartz and 62.4 for hematite. Starch Adsorption on Mineral Surfaces Starch adsorption data were obtained by agitating for 1 hr measured volumes of neutral starch solutions of known concentrations with weighed quantities of finely divided mineral of measured specific surface. The mineral then was separated from the pulp liquor by centrifugation and the residual starch content determined by chemical analysis. The analytical procedure consisted of oxidizing the starch with an excess of dichromate in acid medium at elevated temperature and titrating the excess dichromate by the ferrous ammonium sulphate—potassium permanganate method. Analytical results were reproducible to within less than 1 pct. Adsorption data obtained in unbuffered solutions near the neutral point are plotted in Fig. 1. The adsorption on either mineral was far greater for the aminoethyl starch than for the Pearl starch. Flocculation The degree of flocculation was determined for a given pulp by measuring the time required for the supernatant liquid to reach a certain degree of clarity. This was accomplished by passing a standard light beam through the pulp, contained in a glass settling tube, and measuring the time required after agitation ceased for the intensity of the transmitted beam to reach a predetermined value. Starch reagent was added to each pulp in small uniform increments, and the settling time was determined after each such addition. Increase in pulp liquor volume due to the added starch reagent was ignored in these tests. Pulps were maintained at or near neutrality. of the preparation of the aminoethyl starch: "Three hundred and sixty grams of powdered unmodified corn starch was slurried in 3 liters of water and stirred during gelatinization. Eighty-six grams of ethylenimine was added slowly during reflux which was continued for 4 hr. The yellow solution set to a gel upon cooling. This was broken up and neutralized with HC1. The thick paste was dried on hot rolls. Adsorbed polyethylenimine and salts were removed from the yellowish products by washing first with acidified aqueous '60 per cent' alcohol. The white product contained nitrogen corresponding to about one aminoethoxy group per ten glucose residues." Only laboratory samples of this starch derivative have been prepared. The starch reagents for use in flocculation, flotation, and adsorption tests were made up by dispersing the appropriate quantities of air-dry starch in cold water, adding boiling water, and heating for 30 min at 120°C under pressure. When used ip adsorption tests, the starch solutions first were cleared of insoluble matter by centrifugation.

Jan 1, 1953

By F. H. Wilson, E. W. Palmer

The solid solubility of iron in 2 to 10 pct cupro-nickels increases with temperature and nickel content. Property changes accompanying various heat treatments indicate typical precipitation hardening behavior. Iron content also affects softening temperature and sub-scale formation. These factors, as well as impingement corrosion resistance, influence the optimum iron content of commercial alloys. FOR many years Cu-Ni alloys have been used extensively in the form of tubes, pipes, and plates for the construction of salt-water lines and surface condensers on shipboard and in tidewater power stations. The 30 pct Ni alloy has been considered more resistant to rapidly flowing sea water than alloys of lower nickel content, and has been standard on ships of the U. S. Navy. Some ten years ago, the still better corrosion resistance obtained by modifying the 30 pct Ni alloy with approximately 0.5 pct Fe was recognized, and the iron-bearing alloy rapidly superseded the plain alloy as the standard material for severe service. In 1945, Tracy and Hungerford1 published a study of the effect of iron on the corrosion of various cupro-nickels in sea-salt solutions, and their data indicated that the 10 pct Ni alloy containing about 0.75 pct Fe was equivalent to the 30 pct Ni alloy containing 0.5 pct Fe. This was confirmed by LaQue in discussion of the above paper, and by results in an experimental condenser set up at the Kure Beach marine test station of The International Nickel Co., reported by Freeman and Tracy.' The 10 pct Ni iron-bearing alloy is now being very widely used in applications where the 30 pct Ni iron-bearing alloy was formerly considered standard. While this "substitution" has undoubtedly been stimulated by the present extreme shortage of nickel, it must be emphasized that it involves no loss of service performance, and would have occurred anyway in the course of time, for economic reasons. In view of the increasing use of the 10 pct alloy, it seems desirable to make generally available the results of several investigations of Cu-Ni-Fe alloys carried out in the Metallurgical Research Laboratory of The American Brass Co. in recent years. The present paper, deals with the constitution of these alloys in the copper-rich corner of the system, and with the variations in hardness and tensile properties resulting from the heat treatment of alloys containing various amounts of iron. Most of this work is concerned with alloys containing 10 pct Ni. With over about 0.75 pct fe, the 10 pct Ni alloy is suscep- Alloys Several series of cupro-nickel alloys containing iron were used in these investigations. Most of them were prepared in the laboratory, but two samples of commercially fabricated alloys were included. Series A—Nominally 2 and 5 pct Ni, each with 0 to 1.5 pct Fe. Series B—Nominally 10 pct Ni with 0.1 to 0.4 pct Fe. Series C—Nominally 1.0 pct Ni with 0 to 2 pct Fe. Series D—Nominally 10 pct Ni with 3 to 5 pct Fe. Series E—Nominally 10 pct Ni with 1 and 1.5 pct Fe.

Jan 1, 1953

By H. C. Doepken

Wrought Hadfield steel was tested in axial tension at from 100° to —196°C, to determine flow and fracture stresses as well as conventional properties. Ductility and related properties, such as fracture stress, decreased continuously with temperature. Peculiarities during straining indicated possible martensite formation or mechanical twinning. THE mechanical properties of austenitic manganese steel have been summarized by Avery and Day,' including the low temperature tensile properties reported by Hadfield and coworkers2,3 " These data show the material to be brittle at both liquid oxygen and liquid 'hydrogen temperatures. Avery and Day report considerable ductility measured by Charpy V-notch tests at —100°F (-73°C). Since the review of low temperature properties by Seigle and Brick' show face-centered cubic structures, other than Hadfield steel, to be ductile at low temperatures, it was felt that a study of tensile properties, between the reported intervals, should show whether the decrease in ductility was a gradual decline or an abrupt drop beginning at some intermediate point. X-ray examinations were made in an attempt to shed further light on the mechanism of work hardening of austenitic manganese steel. The presence of a magnetic constituent has been found by Hall" and by Avery, Homerberg, and Cook." Krivobok7 demonstrated the growth of magnetic constituents on reheating cold-worked specimens. Hadfield2,3 ' and Goss found no a iron. The steel from which the specimens were taken was commercial hot rolled % in. diam rod of electric furnace steel. The ladle analysis was as follows: C, 1.40 pct: Mn, 12.11; P, 0.060; S, 0.012; Si, 0.120; Ni, 0.080; and Cr, 0.090. Fifteen specimens, 6 in. long, were cut from a

Jan 1, 1953

By David Moskowitz, Ira Binder, Robert Steinitz

THE hard refractory borides of the transition elements of the 4th, 5th, and 6th groups of the Periodic System have been the subject of a number of recent investigations.'-' It is well known now that most of these elements form several different borides, and Kiessling8 has summarized the rules which govern to some extent the arrangements of the boron atoms in the various structures. Melting points of a few borides have been published." The systems Fe-B, Ni-B, and Co-B have been reported," but, as these borides are rather low melting, they are outside of the groups of boron compounds considered here. Brewer' has tested the stability of various borides and estimated a number of eutectic temperatures between different borides, but in no case was the complete system of a transition metal and boron investigated. The phase diagram becomes of special importance if the preparation of the borides from the elements in powdered form is considered; the lowest eutectic temperature will determine the first appearance of a liquid phase. Also, the knowledge of high temperature phases, if they exist, is important for the preparation of bodies from these borides by hot pressing or sintering. During the investigation of various metal borides,7 it was found that there were more boride phases existing in the Mo-B system than reported by Kiessling." They occur, however, only at temperatures above 1500°C and were, therefore, not found by him. This led to a study of the equilibrium diagram of the Mo-B system. ranging from 0 to 25 pct B and from room temperature to the liquidus. Part of this investigation was reported during the "Research in Progress" session at the 1952 Annual Meeting of the AIME.11 Raw Materials and Preparation of the Borides The raw materials used were commercial molybdenum and boron powder, both supplied by the Molybdenum Corp. of America. The molybdenum powder was 99+ pct pure? while the boron powder contained about 83 to 85 pct B. A large percentage of the impurities in this powder was oxygen, with the rest formed by iron, calcium, and unknown substances. The low purity of the boron used was, however, not considered detrimental to the final product, as most of the impurities evaporated at the high temperatures at which the borides were formed. The final product always had a minimum purity of 96 to 98 pct (figured as molybdenum and boron), with carbon, iron, and probably oxygen being the remaining products. Carbon is usually present as graphite. The chemical analyses always confirmed the compositions which corresponded to the crystallographic structures as determined by X-ray diffraction, and the boron content of the finished product agreed closely with that of the starting mixture; no boron was lost during the boride preparation. The chemical analysis methods employed for molybdenum and boron were previously described by Blumenthal.12,13 The powders were mixed by hand in the desired proportions, compressed at room temperature under low pressure, and then heated under hydrogen to about 1500" to 1700°C in a graphite crucible to form the borides. Usually, the three well-known borides Mo,B, MOB, and Mo,B,, which are stable at room temperatures, were prepared in this way, and all other compositions were made by mixing these borides in various ratios or by the addition of molybdenum or boron powders for the very low or very high boron contents. Preparation of two-phase compositions directly from the elemental powders was tried only occasionally to check whether equilibrium could be reached in this way. Experimental Procedures The stable borides were mixed in the desired ratios and heated under hydrogen in graphite crucibles to various temperatures. The well insulated crucibles were heated in a high frequency induction furnace. Special care was taken to obtain exact temperature measurement, which proved much more difficult than originally anticipated. It is believed that individual temperature measurements have an error of less than ±25ºC, while melting or transformation temperatures are accurate within ±50°C. The temperatures were measured with an optical pyrometer which was aimed at the closed end of a graphite tube extending down into the crucible. close to the samples. Attempts to measure directly through the hydrogen exit stack failed. The crucible arrangement is shown in Fig. 1. Heating was done at a slow rate to be sure that the temperature inside the crucible was uniform. The specimens were kept at the final temperature for about 30 min. For the investigation of high temperature phases, some samples were quenched. They were heated, without atmosphere protection, in a very small graphite crucible which could be rapidly removed from the high frequency coil, and dropped into water. These quenched samples were afterwards annealed to establish the equilibrium at lower temperatures. The melting points or the positions of the solidus and liquidus lines were determined by heating the specimens to various temperatures and examining them at room temperature for evidence of a liquid phase. These results were checked later on by thermal arrest curves, especially to determine the exact position of the eutectic temperature line. For this purpose about 200 g of the boride were melted in a graphite crucible, in an arrangement similar to Fig. 1. Slow cooling was assured by very good

Jan 1, 1953

By Paul W. Richardson

"Introduction And AcknowledgmentsTHIS PAPER outlines the geology and discusses the geological problems of the Mindamar mine. It is impossible to acknowledge the contributions of ideas of all the geologists who have worked in the area. Among the more important contributors are K. DeP. Watson, W. S. James, B.S.W. Buffam, and L. J. Weeks, and John MacPherson, the resident geologist at the mine.A mineralogical and chemical study of the ore and country rock is being carried •on by Dr. Watson at the University of California, Los Angeles.General InformationThe Mindamar mine is on Cape Breton Island, forty miles south-west of Sydney (Figure 1). The nearest railway stations are at St. Peters, which is thirty-two miles southwest of the mine, and at Sydney. Good gravel-surfaced roads connect the mine to the railways.The mine is producing at the rate of 600 tons a day of ore containing zinc, lead, copper, and minor amounts of silver and gold. At the present time the mill feed averages 9 .per cent combined metals, of which zinc makes u:p 7 1per cent and lead and copper each 1 per cent.General GeologyThe ore being mined ,by Mindamar occurs in a shear zone parallel to a northeasterly striking, vertically dipping, series of rocks consisting of rhyolite tuff, rhyolite, minor more basic flow rocks, and diorite (Figure 2). In the vicinity of the mine, these rocks have been termed the Mine Series. They belong to the Bourinot group, which has been assigned by L. J. Weeks to the Middle Cambrian. At the latitude of the mine, the Bourinot group is bounded on the northwest by the Stirling fault and extends eastward for two miles."

Jan 1, 1953

By Henry A. Stiff, J. P. Hammond, A. B. Westerman, H. C. 195-000-000-014 Cross, and Lawrence E. Davis

The phases in Cr-Fe-Mo alloys have been investigated with homo-genization, aging temperature, composition range, and alloy addition as variables. Metallography, three X-ray methods, and hardness were used as methods of study. The behavior of s, M23,C8, and Z phase are reported for cornpasition range 60 pct Cr-15 to 25 pct Fe-15 to 25 pct Mo-<0.005 to 0.36 pct C with aging at 1400º to 2000°F. With 2 pct Ti, Tic and TiC-TiC are formed; with nitrogen Cr2N. THE recently developed class of chromium-base heat-resistant alloys shows appreciably higher strength than commercially used high temperature alloys. However, further developmental work is required to impart needed shock resistance and some degree of room-temperature ductility to these alloys. Extensive exploratory work on chromium-base alloys was begun in a program initiated by the War Metallurgy Committee of the National Defense Research Council at the Climax Molybdenum Co. in the early part of 1942.&apos; Alloys were sought for gas-turbine blades for use at 1600°F. A minimum of 5 pct elongation in the stress-rupture test was a requirement. From the Climax work, ternary alloys of chromium, iron, and molybdenum appeared to show the greatest promise as materials for gas-turbine blades. The composition line in the ternary diagram joining the 60 pct Cr-15 pct Fe-25 pct Mo and 60 pct Cr-25 pct Fe-15 pct Mo alloys was indicated as representing the most useful combination of strength and ductility.&apos; Strength increased while ductility decreased as molybdenum was raised in this composition range.&apos; The 60 pct Cr-15 pct Fe-25 pct Mo type alloy was thought to have the most suitable properties for gas-turbine blades.&apos; Concurrent with the study reported here, other investigations were being made on Cr-Fe-Mo alloys. The liquidus temperatures on a series of low carbon, ternary alloys were being determined, and isothermal sections drawn at 2370°, 2010°, and 1650°F (1300°, 1100°, and 900°C).2 Also, various methods of preparation and some mechanical and physical properties of chromium-base alloys, particularly the 60 pct Cr-15 pct Fe-25 pct Mo type, were being investigated., At the inception of the present program, only a limited study had been made of etchants for developing the microstructures of chromium-base alloys; X-ray analysis of the microconstituents had not been made. A review of the literature revealed that no phase-diagram work had been reported on the Cr-Fe-Mo system. Scope of Work The work on chromium-base alloys includes the following: 1—The development of etching methods for differentiating between the microconstituents; 2—The identification of microconstituents by X-ray diffraction methods; and 3—A comprehensive metallographic and hardness study after various heat treatments. The phases were studied by three standard X-ray techniques: 1—The block-sample focusing-camera method; 2—The powder-diffraction method on elec-trolytically separated residues; and 3—The powder-diffraction method on cold-worked aggregate samples. The results by the first two methods were correlated with the metallographic data. The third method was used largely to study conditions approaching equilibrium, since cold working prior to heat treating accelerated precipitation. Seven types of alloys were investigated: 50 pct Cr-50 pct Fe, 40 pct Cr-40 pct Fe-20 pct Mo, 55 pct

Jan 1, 1953

AN economist at MIT provided Americans with myth destroying information which should prove effective against the gentlemen of the extreme left. For a number of years they have charged that a small number of companies in each industry has been grabbing more and more of the industry&apos;s business. M. A. Adelman has shown that the concentration of business in the hands of big corporations has not shown any sign of growth during the last 50 years. Quite the contrary, there has been a slight decline in this concentration, according to Adelman. There are more small companies per thousand population than ever before. Bearing this out is the fact that International Harvester is now doing 41 pct of the possible market against a former 85 pct; American Can Co. has dropped from 90 pct to 50 pct; American Smelting is down to 31 pct compared with 90 pct; and lastly, U. S. Steel which has plummeted from 65 pct to slightly more than 30 pct of the steel market. Declines of the same proportions have hit big companies in other industries. Price cuts on Detroit&apos;s 1953 automobiles indicate that even among the biggest competition is still one of the most important household gods. Big business is still slugging it out for the attention of the American consumer. It&apos;s a battle which can only have one result-benefit to the man who buys.

Jan 1, 1953

By Manuel Gomez

This report presents experimental work conducted on a number of coals found within the boundaries of the Missouri River Basin, which were, to an extent, a selection of coals typical of that region. In the min, the laboratory work falls into three general classifications: (1) Laboratory distillation assay of coal to establish yields on carbonization; (2) chemical analyses of the coal samples before drying or carbonization; and (3) chemical analyses of the products of carbonization. It will be seen in the following discussion that these data derived from the small-scale laboratory apparatus are useful in predicting yields from pilot plants or industrial units. Coal is produced in about 48 general areas or mining fields in the Western States, of which approximately 18 fall within the limits of the Missouri Basin.3/ Beginning with the Northern Colorado field, through the Central and Western Wyoming fields, the coal is principally bituminous and subbituminous rank. The western Montana coals are also of these ranks. Progressing northeast from central Wyoming the coal decreases in rank, as shown by the subbituminous C coals of the Gillette field in northern Wyoming and the lignites of eastern Montana and North Dakota.

Jan 1, 1953

By N. J. Grant, C. F. Flo, F. B. Cuff

An investigation of the Ti-Cr system has shown the presence of a complete series of solid solutions in the ß phase, with a minimum in the solid us near 50 pct Cr. An intermetallic compound, TiCr2, forms during cooling from the ß solid solution. There is a eutectoid reaction at the low chromium side of the system. IN view of the recognition of the potentialities of titanium and its alloys as important structural materials there has arisen a need for a systematic investigation of various titanium binary diagrams. Of these, the Ti-Cr system was of particular interest because of the improved properties imparted to titanium by small chromium additions. A literature survey disclosed a partial constitution diagram that had been suggested by Vogel and Wenderott,¹ This diagram, shown in Fig. 1, is the result of work done on the Fe-Cr-Ti ternary system. Alloys containing less than 43 pct Cr were not investigated. In addition to this, a study of alloys in the Ti-Cr system was reported by McPherson and Fontana.² Adenstedt3 furnished a number of dilato-meter curves obtained from specimens containing 5, 10, and 15 pct Cr. Very recently, McQuillan4 submitted a proposed diagram covering the complete range of compositions between titanium and chromium. This diagram was in general agreement with the one described here. Experimental Procedure Sponge titanium (99.7 pct) and electrolytic chromium (Bureau of Mines analysis: 99.03 pct Cr, 0.40 pct Fe, 0.53 pct O2) were used for the initial determination of the system. Subsequent refinement of points, particularly for the low chromium side of the diagram, was accomplished by using iodide titanium and high purity chromium (National Research Corp. analysis: 0.050 pct C, 0.045 pct O2). The Ti-Cr alloys were prepared by melting 25 g charges in an enclosed, water-cooled copper crucible using a movable tungsten electrode. The atmosphere was helium, prepurified by first passing it through a drying agent and then through sponge titanium heated to 850°C. Particular care was taken to avoid any large scale segregation resulting from insufficient mixing of the components. Each charge was melted and kept molten for approximately 1 min, allowed to cool, inverted, remelted, and kept molten for an additional minute. In order to ascertain the amount of impurity pickup (oxygen and nitrogen) during the melting procedure, three iodide titanium specimens were melted in sequence and then checked for increased hardness. The specimens in the as-cast condition showed a relatively large hardness increase over the hardness of the as-received iodide titanium. The scattering on these readings was large. However, after the specimens had been homogenized at 840 °C for 2 hr and slowly cooled, the measured increase in hardness over the as-received titanium was small with a corresponding decrease in scatter. The reason for this hardness change is that in heat treating these specimens below the transformation temperature (885°C) there was a conversion from the as-cast structure to the more nearly equilibrium structure of the annealed specimen. The alloys were analyzed for chromium content and although the actual percentage was invariably low the deviation from the nominal composition never exceeded 0.6 pct Cr.

Jan 1, 1953