Search Documents

By D. J. Blickwede

WHEN iron is dipped in molten zinc at temperatures in the range 840" to 930°F, the two metals react to form layers of Fe-Zn compounds which adhere to the iron. At the galvanizing tem- perature, the successive layers are:' y (Fe5Zn21), 61 (FeZn;), and 5 (FeZn13), in conformity with the Fe-Zn constitution diagram. There is no quantitative information in the literature on the rates of growth of the individual alloy layers over the temperature range 840° to 930°F. Rather all the past experiments have studied the loss in weight of iron as a function of galvanizing

Jan 1, 1954

By I. Cadoff, J. P. Nielsen

The Ti-C phase diagram exhibits a peritectic point at 1750°C and 0.8 pct C, and a peritectoid point at 920°C and 0.48 pct C. The maximum solubility of carbon in a titanium is 0.48 pct. The 6 region containing the Tic compound (20 pct C) extends to 11 pct C at the peritectic temperature. THE interest in the Ti-C alloy system stems from the fact that carbon occurs as an impurity in titanium alloys when graphite electrodes or graphite crucibles are used in their melting. Since titanium-base alloys are still in the development stage, some virtue may be found in carbon addition to titanium. The Tic compound is currently emerging as an important powder metallurgy base constituent similar to the WC compound. Ehrlich' identified the phases and structures present in the Ti-C system. The peritectoid region of the phase diagram was investigated by Jaffee et al." A preliminary diagram based on theoretical considerations was proposed at the outset of this research." The Tic compound has been investigated extensively and has been reported on in a large number of papers. Experimental Procedure Arc-melted alloys of 24 compositions in the range 0 to 20 wt pct C were investigated using metallography, X-ray diffraction, and, for the liquidus and solidus regions, incipient and complete melting. All alloys were prepared from iodide titanium (New Jersey Zinc Co., 99.95 pct Ti minimum) and spectroscopic grade carbon (National Carbon Co.). To prevent carbon spattering during arc melting the carbon was encapsulated in titanium. For alloys containing less than 1 pct C the powder was inserted into a capsule formed by drilling a hole in the as-received rod. For higher compositions, capsules were formed from titanium sheet. Arc Melting: The charges were melted in the copper-hearth cold electrode furnace shown in Fig. 1. This furnace is similar in principle to the all-metal unit adapted for titanium melting at Battelle Memorial Institute.' The transparent pyrex walls giving unlimited visibility during operation and the multiple-

Jan 1, 1954

By R. M. Brick, F. L. Vogel

THE elementary mechanism of deformation in the body-centered cubic metals has been a subject of dispute for many years. If the problem were merely that of designating the crystallographic plane or planes of slip, the solution would have appeared long ago. However, there must be greater differences in the deformation behaviors of the body-centered and face-centered types than the differences in their lattices would suggest. The lines of slip formed on the polished surface of a strained face-centered cubic metal conform to glide over a single plane of the crystal. Slip in body-centered cubic iron, however, is frequently observed as curved and forked lines which could not possibly define a single plane of atoms. This alone is sufficient reason to expect different modes of deformation to operate in the two lattice types. The literature in this field now has generally accepted the proposition that {110), {112), or (1231 planes will act as slip planes in iron. It is essential that the experimental evidence supposedly supporting this proposition be critically examined. Taylor and Elam1 in 1926, using relatively small single crystals, determined the operative slip systems by measurements of the distortion of a grid engraved on the specimens prior to deformation. Their results indicated that shearing had taken place in the close-packed direction on a plane adjacent to or coinciding with the plane of maximum shear which contained the slip direction. This led the authors to propose a theory of noncrystallographic or banal slip. The authors considered an alternate rationalization of banal glide. Slip on two (1101 planes or possibly two {112} planes containing the same <1ll> direction could produce the wavy slip lines. By employing plane segments of varying widths, the integrated plane could take any position in the <111> zone. They rejected this explanation, however, feeling that the preponderance of evidence was against it. Taylor&apos; continued the investigation of the plasticity of the body-centered cubic lattice on ß brass. He reasoned that the resistance to shearing of a given plane in the zone of the slip direction was a function of the angle between the glide plane and the closest (110),: P F=—cose sine cos(X —?) [1] where F is the resistance to shear; P, the axial load at yielding; A, the cross sectional area; e, the angle between slip direction and load axis; x, the angle between plane of maximum shear containing the slip direction and the (101) pole; and ?, the angle between observed glide plane and the (101) pole. Differentiating Eq. 1 and rearranging, dF — = tan(x-?) d? [2] F which expresses the variation of the shear resistance with the angle $. Integrating this equation between the limits 0 and ? yields In F/F0 = ?0?tan(x— ?) d? [3] Here, F, is the resistance to shear of the (110) plane and F is the resistance to shear of a plane $ degrees from the (110). Thus, the variation of shear resistance with $ can be calculated from an experimentally measured x vs $ relationship. Fahrenhorst and Schmid8 sed several methods, none of them involving direct observation, to determine the glide system in ferrite. They determined the variation of critical resolved shear stress with

Jan 1, 1954

By G. S. Farnham, D. A. Scott

Partition of certain elements, particularly nickel, was determined for slowly cooled steels, the greater number containing from 0.30 to 0.35 pct C. Approximately 3 pct of the nickel, 18 pct of the manganese, 33 pct of the molybdenum, and 35 pct of the chromium occur in the carbide phase. Partition of one element is not much affected by the presence of another. THE object of this investigation was: 1—to determine the partition of nickel between cemen-tite and ferrite in a medium and high carbon series of annealed steels; 2—to evaluate the effect of chromium and/or molybdenum or both on the partition of nickel in medium carbon annealed steels; 3— to determine the partition of chromium between ferrite and carbide in a series of medium carbon annealed steels; and 4—to study the chemistry of the carbides formed in an AISI 2330 steel during both isothermal transformation, and quench and draw experiments at 1150°F (620°C). The partition of alloying elements between ce-mentite and ferrite in annealed steels has been the subject of many investigations, a summary of which has been given by Austin1. However, there is no satisfactory data available concerning the partition of nickel. It has generally been assumed that virtu- ally all of the nickel concentrates in the ferrite phase in annealed steels. Two investigators"." have reported the finding of nickel in extracted carbide residues. Recently, it has been shown4 that nickel substitutes up to 40 pct for iron in the lattice of cementite produced by the low temperature carburization of iron-nickel powders. In addition to the lack of data on nickel partition, the literature also fails to make reference to the effect of other elements on the nickel content of the carbide in nickel-bearing steels. The partition of molybdenum between ferrite and carbide has been reported"-&apos; for hypoeutectoid steels, isothermally transformed at 1300°F (705°C) and

Jan 1, 1954

By D. J. Carney, R. L. Stephenson

A sampling technique has been developed for procuring a sample of sinter representative of the entire depth of the sintering bed. The sampling method involves the use of an open-bottom metal basket that rides on the grate of the sintering machine and when removed contains a sample of the sintered product. Additional data have been obtained to indicate that the tumbler test is a suitable means of measuring sinter strength. IN the last few years additional sintering facilities have been installed in both the Pittsburgh and the Chicago district of the United States Steel Co. Since the construction of these sintering plants made possible the use of higher percentages of flue-dust sinter in our blast-furnace burdens, it became important to study means of controlling the quality of sinter to obtain optimum results in the blast furnace. For controlling an operating process, it is necessary first to establish standards by which the quality of the product can be judged. For sinter, it appeared that an important property was its strength or its resistance to degradation during transportation and charging into the furnace. Consequently work was undertaken to establish a standard for sinter strength that could be used both for controlling sintering-plant operations and for correlating sinter quality with blast-furnace performance. The first problem in setting up a standard was that of procuring a sample that would be representative of the sinter made under any particular set of conditions at the sintering plant. Since the United States Steel Co. sintering plants discharge the finished sinter either into a large pit or onto a rotary cooler, the sinter becomes inseparably mixed with material sintered 2 hr before or 2 hr afterwards. For this reason the exact identity of the sinter is lost. A sample selected as the cooler is discharged, or as the sinter is removed from the pit, cannot be said to be truly representative of the sinter made at any specific time. Sampling The first attempt to procure a sample that would be representative of a specific sinter mix and of specific operating conditions was made by stopping the Dwight Lloyd sintering machine and removing an entire pallet full of sinter. This method, however, proved very difficult to perform and interfered considerably with the operation of the plant. To overcome this difficulty, a sampling method was devised by technologists at South Works enabling them to secure, without interrupting the sintering operation, a sample of about 1 cu ft of sinter, representative of sinter for the full depth of the sintering bed. The South Works method involves the use of a steel-frame-work basket. A typical basket is shown in Fig. 1. The basket has been used both with and without crossbars along the bottom. As long as the crossbars are in the same direction as the grate bars on the sintering machine they do not interfere with the sintering process. The basket is set on an empty grate of the Dwight Lloyd sintering machine before it passes under the swinging feed spout, see Fig. 2. When the basket is removed after it has travelled the length of the sintering machine, it contains the sample. Just before the basket is removed, the sinter is scored and chipped to facilitate removal of the sample from the sinter bed. A view of the basket after its removal is shown in Fig. 3. Although the sampling method was originally designed for use on a Dwight Lloyd sintering machine, it can also be used on the Greenawalt type of machine. When used on the Greenawalt-type machine, the basket is placed on the sintering grate before the charging car passes over it, and finally it is removed just before the pan is dumped. Testing After a method of obtaining a representative sample of sinter had been developed, the next step was to select a method of measuring its strength. The irregular shape and size of the sinter pieces precluded the use of a simple compression test for determining strength; consequently, the shatter test and tumbler test were investigated. To perform the shatter test, a sample of sinter, approximately 5 lb, is dropped from a hinged-bottom box at a height of 3 ft onto a steel plate. The broken sinter is sieve-analyzed after a specified number of drops. The tumbler test is performed with the use of a standard ASTM coke-tumbling drum. The drum is 3 ft in diam and is equipped with two lifter bars diametrically opposite one another on the inner periphery of the drum. The drum is rotated at a speed of 24 rpm for 200 revolutions, and after tumbling the sample is sieve-analyzed. To express as single numbers the results of sieve analyses after shattering or tumbling, the method suggested by R. E. Powers1 was employed. This method involved plotting the size of the sieve openings on a logarithmic scale and the cumulative per cent larger than each sieve on a probability scale as described by J. B. Austin.&apos; By interpolating from the plotted data, which in most cases approximated

Jan 1, 1954

United Engineering Trustees, Inc James L Head, &apos;55, E C Meagher, &apos;56, Gail F Moul¬ton, &apos;57 Advisory Committee to Real Estate Committee Cleveland Dodge, Herbert Hoover, Paul D Merica The Engineering Foundation W M Peirce, &apos;56, A M Gaudin, &apos;58 Research Procedure Committee A M Gaudin, March &apos;54 Engineering Societies Library Board Frank T Sisco, &apos;54, E M Wise, &apos;56, James L Head, ex officio Engineering Societies Personnel Service Board of Directors E J Kennedy, Jr, E H Robie

Jan 1, 1954

By J. Washburn, R. Drouard, E. R. Parker

Temperature dependence of the rate of recovery in zinc single crystals after a simple shear deformation at low temperature was investigated. Some tentative suggestions regarding the annealed and strain-hardened states of a crystal are discussed. RECOVERY may be defined as the gradual return of the mechanical and physical properties of strain-hardened metal to those characteristic of the annealed material; an increase in temperature increases the rate of recovery. The annealing process in strain-hardened polycrystalline metals is complicated by the inhomogeneity of strain which always exists in aggregates. Polygonization in bent regions of the crystals and growth of new almost strain-free grains starting at points of severe local distortion1-:&apos; make it almost impossible to isolate and study the recovery process. Homogeneously strained single crystals, however, do not polygonize or re-crystallize and hence they can be used advantageously to study recovery. In such crystals strain hardening is completely removed by recovery alone. Since recovery is a process whereby certain lattice disturbances introduced by plastic flow are gradually reduced, a knowledge of the rate and temperature dependence of this process for various conditions of prestrain might be helpful in formulating a model of the strain-hardened state. For simplicity it seemed desirable to limit the type of prestrain to the simplest obtainable, i.e., simple shear strain. In the experiments to be described, recovery was studied by observing changes in the stress-strain curve of prestrained zinc single crystals held for various times at temperatures above that employed for straining. Single crystals were grown from the melt by a modified Bridgeman technique from Horse Head Special zinc 99.99 pct pure, and from spectrographically pure zinc 99.999 pct pure. They were grown as 1 in. diameter spheres and acid-machined&apos; to the final specimen contour. The test section was a cylinder about 1/8 in. high and 3/4 in. in diameter. The conical sections adjacent to the test section were cemented into the grips so the load could be transmitted to the crystal as uniformly as possible. The specimens were oriented so that in testing the maximum shear stress was applied along one of the slip directions, [2110], in the (0001) plane. Details of the production and testing of such specimens have been presented.&apos; Each test was carried out according to the following schedule: 1—The crystal was strained at — 50°C until it reached a maximum shear stress, ,,,. The strain rate was approximately 5 pct per min in all cases. 2—After straining, the crystal was unloaded before the temperature was changed. Unloading required about 3 min. 3—The temperature of the specimen was then increased from — 50°C to the temperature, T, of recovery. This change in temperature was completed in a time of less than 2 min. The specimen remained at temperature, T, for a time, t, which differed for the various specimens. 4—Thereafter the temperature was again reduced to — 50 °C in approximately 3 min. 5—While at —50°C, the stress-strain curve after recovery was obtained. 6—The specimen was then unloaded and annealed for 1 hr at 375 °C in a helium atmosphere to bring about complete recovery. Cooling to room temperature after anneal required 90 min. 7—The same crystal could be re-used for another test because the plastic properties after annealing closely duplicated those of the original crystal. The specimen was immersed during the test in a bath of methyl alcohol which, through a system of tubes, could be pumped through either of two heat exchangers to regulate the temperature; this was accomplished by circulating the liquid through coils immersed in a bath of acetone and dry ice for cooling or in a bath of warm water for heating. Test temperatures were thus maintained constant within ±1°C. The — 50°C temperature was low enough so that no measurable recovery occurred during unloading and reloading. The stress-strain curve continued after recovery along a path below, but approximately parallel to, the path of a curve obtained in an uninterrupted test. Fig. 1 shows some of the results from a specimen of 99.999 pct Zn. The amount of downward displacement of the curve due to recovery was a

Jan 1, 1954

By W. J. Houk, F. C. Hull

To clarify interpretations of grain structures and to assist in calculations of spatial grain size distributions, plane distribution curves have been determined for random sections through four regular polyhedrons approximating the shapes of metal grains. The characteristics of the distribution curve for the average metal grain are predicted. IT was realized early in the history of metallurgy that metals are polycrystalline aggregates and that the size and shape of crystals affects the properties of the material. Reaumur1 in 1722 employed the microscope to examine the fractured surfaces of steel and of white and gray cast iron and suggested a polyhedral arrangement of the crystals. The first extensive investigation of the form of crystal grains was carried out by Desch.2 He examined the disintegrated grains from a ß brass sample and noted that the number of faces per grain ranged from eleven to twenty and that the number of edges per face varied from three to eight and the maximum occurred at five. While it has been found practical to examine isolated grains only in exceptional cases, it is always possible to make a plane section through the metal and examine the shape of the grain sections on the plane of polish. Desch2 tried to determine the relation between the form of a polyhedron and that of its plane sections for comparison with distribution curves of numbers of sides per grain section of actual metal samples. The polyhedrons investigated were the rhombic and pentagonal dodecahedrons and the orthic tetrakaidecahedron. However, the frequency distributions of the number of sides of plane intersections were not sufficiently characteristic to decide which polyhedron most closely approximated the average grain in a metal. Determination of Statistical Shape of Grain in Space Scheil3 was interested in the problem of calculating the distribution of grain sizes in space from the easily measured distribution of grain section sizes on the plane of polish. Assuming that the grains were spheres and using the plane distribution curve for a sphere shown in Fig. 1, he employed a successive subtraction method to calculate the spatial distribution. In order to evaluate the accuracy of these calculations, Scheil and Wurst4 determined the actual distribution of grain sizes in space in their sample of ingot iron by polishing off successive layers and following every individual grain in a series of micrographs. From curves of mean radius of intersection of a given grain vs thickness of metal removed in polishing, Scheil and Wurst attempted to derive the statistical shape of a grain in space. Their calculated plane distribution curve for this shape is compared with the distribution curve for a sphere in Fig. 1. A table of values based on this curve was prepared for calculating spatial distributions of grains. The calculated and measured spatial distributions of their sample then agreed much better than when a spherical shape had been assumed. In the present paper, an attempt has been made to learn something about the average metal grain by studying in detail the effect of the shape of regular polyhedrons on the plane distribution of areas and shapes of areas produced by random sections through them. From the data presented below, it can be concluded that the plane distribution curve for the average metal grain differs in three fundamental respects from the curve derived by Scheil and Wurst. Polyhedrons Selected for Study The polyhedrons selected for the statistical study are illustrated in Fig. 2 and consisted of a cube, a figure formed by cutting off the corners of a cube at the midpoints of the original edges, a tetrakaidecahedron, and a pentagonal dodecahedron. The length of edge on any one figure is a constant. For the above models the edge lengths were 3.50, 4.00, 2.00, and 2.08 in., respectively. A cube was selected for one of the polyhedrons because of its simple geometry, because it is a form that by repetition can completely fill space, and because it represents a convenient degree of departure from compactness beyond which the shape of

Jan 1, 1954

By P. M. Aziz, I. Markson, C. S. Barrett

The abnormal after-effect in twisted wires that occurs when untwisting is interrupted by etching con be brought under control and used to study the mechanical properties of thin surface films and how they are effected by reagents and heat treatment. Results are given of studies of oxide films on high purity aluminum. IF a wire is subjected to plastic deformation by torsion and then released, it untwists in the normal after-effect, but under certain circumstances the untwisting is abruptly lessened or reversed by the application of an etchant to the wire.1,2 This abnormal after-effect may occur, for example, if there is a coherent oxide film on the surface of the wire which is removed by the etchant. Following a suggestion of A. H. Cottrell that predicted this effect, it is attributed to dislocations that had piled up beneath the oxide layer and represents the rapid release of residual stresses caused by these dislocations. When the layer is removed, the stress relief may be by escape of piled-up dislocations from the metal, or by an activation of latent sources of dislocations located at the surface, together with rebalancing of elastic stresses to compensate for the loss of stressed material, as in a residual stress analysis determination, these mechanisms acting singly or in combination.&apos; The slower the attack of the reagent, the more gradual is the stress relief and the smaller the change in strain rate when the reagent is applied. A study has been made of the factors that influence the magnitude of the normal and abnormal after-effects with the object of developing techniques suitable for a quantitative investigation of the influence of various surface films on dislocations in wires, and of the rate and extent of the attack on the films by different reagents. It was found that reasonable sensitivity and reproducibility could be achieved if a suitable choice of variables was made and if these variables were held constant through a series of experiments. The method was then applied to a study of oxide films produced and treated in different ways on the surface of high purity aluminum wires, and to a study of the damage to these films caused by various reagents. Experimental Procedure The material used throughout this work was prepared from 99.9968 pct Al. This high purity aluminum was melted, cast into 1/2 in. diameter ingots, and then swaged and drawn without intermediate annealing to 0.040 in. diameter wire. A sketch of the apparatus employed for twisting is shown in Fig. 1. The test wires were mounted into the apparatus by cementing one end of the wire to the beaker and the other to the tube with laboratory wax of high melting point. The length of the wire between the waxed joints was 4.2 & 0.2 cm. Extreme care was taken during mounting to avoid cold-working the wire. The wire was twisted through 335" in 2 to 4 sec by rotating the pinion on the gear box until the vertical post on the rotating table, which was initially touching the horizontal stop, was arrested by the stop. All the tests were conducted with apparatus and reagents at the same temperature (about 25°C). In all tests, except those where the duration of the initial torque was investigated, the torque was applied for a period of 2 min. At the end of this time the table was rotated back a few degrees away from contact with the stop and the wire allowed to untwist. The after-effects were measured by reflecting a beam of light from the mirror shown on the apparatus. After the wire had untwisted for 6 min, a reagent was carefully poured into the beaker and thereby applied to the surface of the wire.. In some tests the liquid in the beaker was removed after a few minutes and replaced by an-

Jan 1, 1954

By C. S. Barrett

The torsional after-effect in polycrystalline cadmium is interrupted by an abnormal twisting when the film is removed by etching. This is accounted for by the pile-up of dislocations beneath anodic or other oxide films during the original twisting, and the relief of the residual stresses from these by elastic and plastic processes during etching. WHEN an iron or zinc wire coated with oxide is plastically twisted and then released, it untwists according to a law of equal increments in equal intervals of log time, but if the oxide is suddenly removed by etching this normal after-effect is interrupted by a transient, and thereafter the untwisting is slower.&apos; Etching may even reverse the strain temporarily. Related effects caused by hydrated oxide films on cadmium in creep tests have been observed by Phillips and Thompson:&apos; definite transient strains caused by the removal of the film from single crystals of cadmium were observed; however, negligible effects were obtained with polycrystalline wires. Pronounced effects of both transient and steady nature were observed by Phillips and Thompson when anodic films 10-4 cm thick were etched off, and weak effects, transient only, occurred with hydrated oxide films 3x10 cm thick such as were formed by standing in water for 10 min. It was estimated that 10.&apos; cm films, formed in water in 1 or 2 min, could be detected in the apparatus of Phillips and Thompson. Since abnormal after-effects were observed by the torsion method equally well with polycrystalline and monocrystalline iron and zinc wires,&apos; it was anticipated that the torsion method would also disclose them in polycrystalline cadmium, in spite of the fact that analogous effects had not been observed in tensile creep tests on polycrystalline zinc by Pickus and Parker3 r on polycrystalline cadmium in tensile studies by Andrade and Randall." Because of its high sensitivity, particularly its sensitivity to surface conditions, the torsion method was thought to merit further study as a method of investigating thin films of various types and the action of various reagents on these films. Materials and Methods Cadmium wires were cold-drawn to a diameter of 0.039 in. from a stock that was determined spectro-scopically to contain 0.05 pct Bi, 0.005 pct Cu, 0.008 pct Pb, and 0.007 pct Si. The wires were cut to about 17/8 in. lengths and were annealed 1 hr in air at 290°C, after which the grain size was such that there were 5 to 7 grains across a diameter. The wires were then mounted as indicated in the insert in Fig. 1, one end being fastened with laboratory wax into a small diameter brass tube and the other end being waxed to a thin glass fiber which supported, on its upper end, a small galvanometer mirror. The wires were waxed with care to avoid straining or annealing, for it was found that the after-effect rate was sensitive to prior cold work in a wire. The assembly was then clamped above a beaker into which the reagent could be poured. The lower end of the wire was held in the hand while the wire was twisted 180"; it was then released immediately. Since precision timing of these manipulations was not attempted, the different wires cannot be compared as to exact rates of untwisting. The length subjected to plastic strain was 15/8 in. The surface coatings studied were those produced by the annealing in air, by anodic treatment of

Jan 1, 1954

By G. A. Moore

A brief review is given of methods designed to produce metallic iron of high purity, and typical results are listed. A recent method, utilized at the National Bureau of Standards, consists of the extraction of ferric chloride by ether, reduction of this ferric chloride to ferrous chloride, further purification of this chloride, and the subsequent electrolytic deposition of metallic iron. iron produced by this procedure apparently is softer than, and otherwise different in properties from, any iron previously prepared and contains appreciably smaller amounts of impurities. THE history of attempts to produce "pure" iron reaches to antiquity and it may be presumed that each ancient armorer who succeeded in making a better steel concluded, correctly, that he had done a better job of removing the "base metals," and incorrectly, that he now at last had a "pure" metal. Early metallurgical papers mentioned use of "pure iron" in making alloys—this "pure" iron in most cases being inferior to some commercial stocks of the present time. Improvement has been continuous, and usually at a sufficient rate to convince each succeeding group of workers that they, at last, were using the really pure metal (until the analysts also improved their techniques to again discover the impurities). These adventures were reviewed in some detail by Cleaves and Thompson.&apos; Although the ores of a metal may be abundant, difficulties in extracting it may make the pure metal very rare. When impurities are restricted to a total of a few parts per million, nearly all pure metals become rarities. Lead, copper, gold, mercury, silver, zinc, aluminum, bismuth, and the six platinum metals are claimed to be available with total impurities ranging from 2 to 50 ppm. The present small and scattered world supply of so-called "pure" iron holds an unimpressive place in another group of 16 metals having approximately 100 ppm of foreign material. Of about 20 less rare metals, only the platinum metals are more costly to prepare. While the production of such rare varieties of iron may appear insignificant in the presence of thousand-ton operations with 95 to 99 pct metal, it must be emphasized that all researches on commercially interesting irons and steels are in fact studies of the modifications of the properties of iron by additional materials. Until the properties of high purity iron are directly measured, all ferrous research must operate without known base values. Traces of impurities may affect the properties of a metal in many ways. Infinitesimal traces of solutes, by disturbing the electronic configuration, greatly change the electrical properties of transistors and semiconductors2-3 and slightly larger traces might alter these quantities in iron. Soluble impurities which disturb the perfection of lattice arrangement not only may alter the magnetic constants and electric properties, but by their close association with dislocation phenomena probably control the very existence of the "yield point"; determine the value of yield stress; and perhaps control the selection of slip and cleavage planes. It has been speculated that impurities might even cause the allotropic transformation in iron, but in any case their rearrangement must contribute to the unreliability of heat capacity and other thermodynamic measurements. Impurities which do not remain in solution may cause even greater effects on the properties. Microscopically visible amounts of phases other than ferrite can be found in all high purity irons which have come to my attention. It can be calculated that from 50 to as little as 2 ppm of an insoluble material might be sufficient to completely film all grain boundaries in irons having grain sizes from ASTM Nos. 10 to 1. Should this occur, such films, even though invisible, may be very important in fracture problems, especially at extremes of temperature:&apos; Studies of grain growth and diffusion normally imply consideration of a single-phase system, hence, in the presence of insoluble impurities they can be expected to give ambiguous data." High purity iron is also in demand for use as chemical and spectro-chemical standards; for work in classifying the lines of the iron spectrum; for biological work in nutrition; and for work in nuclear physics. where the presence of some sensitive

Jan 1, 1954

By Shiou-Chuan Sun

THE fact that coals of different ranks and even of the same rank differ greatly in their amenability to froth flotation is well known. In recognition of the need for an explanation of this phenomenon, two hypotheses have been suggested. Wilkins1 reported that the floatability of coals increased with an increase of the carbon content or rank. This postulate is handicapped by the fact that bituminous coals that possess moderate carbon contents are actually more floatable than anthracite coals that have high carbon contents, as shown in columns 6 and 9 of Table I. Taggart and his associates&apos; implied that the difference of floatability between bituminous and anthracite coal was caused by the variation of carbon-hydrogen ratio. This is not applicable to the relative floatability of other coals and carbons. For example, column 11 of Table I shows that the carbon-hydrogen ratios of low-floating lignitic coal and non-floating animal charcoal are not only smaller than the moderate-floating anthracite coal, but are also similar to the high-floating bituminous coal. Furthermore, according to this hypothesis, high temperature coke-A (464), Ceylon graphite (1238), and lamp-black (357), all possessing extremely high carbon-hydrogen ratios, should be less floatable than other substances having much lower carbon- hydrogen ratios such as high volatile-B bituminous coal (11.9 to 22), anthracite coal (35.7 to 60.5), lignitic coal (15.6 to 33.6), and charcoal (13 to 26.2). However the former group is actually more floatable than the latter group.

Jan 1, 1954

By J. F. Henderson

Stable mining operations commenced in the Northwest Territories in 1933. Pitchblende from Great Bear lake and gold from the Yellowknife district are the main minerals produced. The value of pitchblende products produced from 1933 to 1941 was nearly $6; 000; 000; data on subsequent production are not available. The first gold was produced from the Con mine at Yellowknife in 1938. Other properties that later came into production include the Negus; Slave Lake; Thompson Lundmark; and Ptarmigan mines. The annual gold production reached $3; 862; 000 in 1942 but due to the war and consequent labour shortage fell to $333; 218 in 1945. The only producing mines at present (May; 1947) are the Con and Negus; but several promising properties are under development; including that of Giant Yellowknife Gold Mines where large tonnages of ore are being blocked out. With the reopening of former producing mines and new production from properties now being developed; gold production should rapidly increase and exceed its former peak within the next few years.

Jan 1, 1954

By H. Carroll Weed

By caving a block into the workings of its open pit and using the block as an ore transfer, the lnspiration Consolidated Copper Co. has solved a transportation and sizing problem, making possible a great expansion of open-pit methods as applied to Inspiration ore-bodies. FROM 1915 to 1948 the entire production of Inspiration Consolidated Copper Co. was supplied from underground mining. The sole method used was block caving. Underground haulage and hoisting facilities were designed and geared to large-scale production. Beginning in 1948 open-pit mining was substituted for block caving in a portion of Inspiration&apos;s Live Oak orebody. The idea proved so attractive that before the Live Oak pit had come into production, another pit on the Colorado orebody (now the Thornton pit) had been laid out and stripping started. It should be noted that these orebodies were not new and the entire program was one of changed methods of mining. Since part of these orebodies had already been mined by block caving methods, it must be recognized that haulage levels had been established under the area or adjacent to it. The orebodies lay on the south side of Inspiration Ridge, while the shafts, crushers, and treatment plants are all on the north side of this ridge. The existing main crushing plant was designed to take a maximum of 12-in. material, and all ore was sized to this dimension by passing through grizzlies in the stopes. In the original planning for open-pit work much thought was given to the transfer of ore to existing underground levels for haulage and hoisting from the regular shafts. If this could be done the necessity of crossing the ridge could be eliminated. Final decision called for cutting a road through the ridge, installation of a primary crusher at an elevation of 3968 ft on the north side of the ridge, and railroad haulage with existing facilities to the main coarse crusher. This decision was brought about by the difficulties of properly sizing and transferring to underground haulage large tonnages of coarse breaking oxide which lay on the upper benches of the proposed pit. Trucking over the ridge on a 7 pct grade would give a cheaper and more flexible operation in handling this material. The benches in the pits are laid out at 50-ft inter-vals and designated according to elevation above sea level. The lowest bench in the original pit was laid out at 3500-ft elvation. All haulage roads are on a 7 pct grade and a vertical lift of 468 ft was considered about the maximum economically possible from a cost standpoint. After 2 years&apos; operation the advantages of pit mining, both from the standpoint of costs and flexibility of operation, became more and more apparent. Studies were then started to develop the extension of open-pit mining to more of the ore reserve than had been planned originally. The idea of transfer raises was again explored. Obviously, as elevation of the pit was lowered, shorter transfer raises would be needed to reach the main haulage levels. Transportation from the lower elevations to the rim of the pit by belt conveyor or skip hoisting was also considered. However, it was recognized that sizing would be required both for conveying and regulation of feed size to the main crusher plant. This would necessitate a fixed or portable crusher located somewhere in the pit. It was known that the sulphide ore at the lower elevations was softer and easier to break than the overlying oxide of the upper benches. This sulphide ore is very suitable for grizzly sizing. Calculations indicated that for ore mined on 3650 elevation, costs for trucking to the primary crusher, crushing, and delivery by railroad to the coarse crusher would equal costs for dropping the same material to the 600 level, hauling underground, and hoisting directly to the coarse crusher bins, provided a suitable method of sizing and transferring could be developed. Above 3650 elevation costs would favor surface haulage; below they would favor underground haulage. The idea of caving an underground block from the 600 haulage level directly into the bottom of the pit

Jan 1, 1954

COUNCIL OF SECTION DELEGATES F J Meek, Chairman H A White, Vice-Chairman H R Gault, Secretary Division of Earth Sciences National Research Council 2101 Constitution Avenue Washington 25, D C

Jan 1, 1954

By J. Chipman, N. J. Grant, J. C. Fulton

This paper contains data on the distribution of silicon between liquid iron-silicon-carbon alloys saturated with respect to graphite and CaO-SiO2-Al2O3 slags under 1 atm of CO at 1600°C. The ranges of slag compositions studied were extended from the dicalcium silicate saturated liquidus composition up to silica concentrations at which Sic appeared as a stable phase. IN blast furnace operation it is not to be expected that slag and metal reach equilibrium with one another. Nevertheless, the silicon content of the metal varies with slag composition and with temperature in a manner which would be predicted from equilibrium considerations. Similarly, the distribution of sulphur between slag and metal does not attain an equilibrium state, yet the influence of slag composition is strongly analogous to its effect on the distribution equilibrium. The desulphurizing power of metallurgical slags has been shown to be highly dependent upon the FeO content of the slag. Moreover, the rate of removal of sulphur from slags is influenced by the oxygen potential of the slag-metal system. Thus it was shown by Grant, Kalling, and Chipman1 that the presence of MnO in slags which are low in FeO causes a marked slowing down of the transfer of sulphur from metal to slag. This led to the hypothesis that the slow removal of sulphur by blast furnace slags of more acid composition might be due in part to the effect of SiO2 on the oxygen potential of the system. This was verified in the work of Grant, Troili, and Chipman,&apos; who found that the desulphurizing power of the more acid blast furnace slags could be markedly improved by an increase in the silicon content of the underlying metal. Their explanation of this improvement was that the higher silicon content of the metal decreased the rate of transfer of more silicon and, along with it, of oxygen from the slag to the metal. The slowness of the transfer of sulphur from metal to slag was the result of the slow reduction of SiO2 from slag to metal. Attempts to study the rate of sulphur removal had in the past resulted in very slow rates corresponding to the rates of silica reduction. It has become evident on the basis of these studies that further experimental studies on the rate of removal of sulphur must take these factors into consideration if there is to be a clear understanding of the rate of sulphur transfer under conditions simulating those existing in the blast furnace. It will be necessary, at least in a part of such study, to employ combinations of slag and metal in which the disturbing effect of silica reduction has been eliminated; in other words, to employ slag-metal combinations which are already in equilibrium with respect to the transfer of silicon. In preparation for such studies of desulphuriza-tion, a preliminary program of research on the distribution of silicon between slag and metal has been undertaken. This will ultimately include a comprehensive survey of the effects of temperature and slag composition on the equilibrium distribution of silicon between slag and metal. The present paper is a report on experimental methods employed and on

Jan 1, 1954

By John D. Price

COAL blending, in the preparation of coal before coke making, is so commonly practiced as to be almost universal. But the reasons underlying this practice, the benefits resulting from it, and the materials used in blending vary widely. This paper will outline the various phases of the subject and present information which may be correlated with work that has been done elsewhere. It will deal entirely with work done on the high-volatile coking coals of the western part of the United States, special emphasis being given to the coals of Colorado and Utah. A surveyL of the 86 coke plants in active operation in the United States during 1949 indicates that only 9 plants, or 10.5 pct of the total, charged one single rank of coal into their ovens, while the remaining 89.5 pcl made use of blending in some form. This report indicated that of these total plants 5 used straight high-volatile coal, 4 used straight medium-volatile coal, 47 used blends of high and low-vola-tile coals, 25 used blends of high, medium, and low-volatile coals, 2 used blends of high and medium-volatile coals, 3 used blends of medium and low-volatile coals. The fact that certain plants operated on a single kind of coal should not be interpreted to mean that no blending was practiced there, for invariably such plants secure their coal from more than one source and in the interest of uniformity do blend the coals as received. The general term coal blending covers two fields, the first of which is the mechanical mixing of a number of coals to secure uniformity. Often it is found necessary to secure coal for coke production from a number of different mines; these coals, though of the same general type or rank, may differ in their chemical composition or in the physical qualities they impart to coke made from them. Again, it is not unusual to find that coal from different sections of the same mine may show variations in quality. Under such conditions it may be necessary, in the interest of a uniform final product, to introduce a system of blending bins, a bedding yard, or other mechanical methods of securing a uniform mixture. Unfortunately this form of blending has received very little attention up to the present time; it has not received the consideration its value merits. The second type of blending, while also for the purpose of coke improvement, deals more particularly with the use of a blending agent differing in character from the base coal: it is this form of blending that will be discussed here. To consider only the western coals, for blending may be found necessary for other reasons with other coals, blending has been practiced experimentally or commercially under the following conditions: 1—When a single coal or mixture of coals of the same rank does not produce a satisfactory coke. For example, a high-volatile coal when used alone is likely to contract when coked so that a comparatively weak coke is formed. Or, if of very low rank, the coal may be deficient in the necessary bitumens required for good coke production. 2—When a product of some special quality is required, for example, when a plant ordinarily producing blast furnace coke must operate at slow coking rate to produce a high-grade foundry coke. Under this condition the reduced daily production of all products which accompanies slow coking time may be undesirable, and the use of some blending agent to increase the size of coke made at faster coking rates may be necessary. 3—When greater yield of coke or its coproducts is needed. Depending upon economic values of the products it may be found desirable to increase the yield of one or the other. 4—When supply of a particular coal must be used, either to protect reserves of high quality coking coal or to utilize a surplus or inferior product not otherwise usable. Many materials have been used for blending purposes, the exact agent to be used depending both upon the condition to be corrected and the nature of the base coal. No universal blending agent that can

Jan 1, 1954

By B. E. Blair

Accelerometers of various types, velocity gages, and a displacement meter are shown to give reliable date when measuring seismic pulses generated in rock by the detonation of explosive charges. Displacement and velocity records are differentiated and shown to compare with velocity and acceleration records. Velocity and acceleration records are integrated and shown to compare with displacement and velocity records, respectively. The experimental data are shown to satisfy the scaling laws developed by dimensional analysis. Propagation laws are developed for peak amplitudes of the first pulse of displacement, velocity, and acceleration. These propagation laws are shown to be independent of the gage used to obtain the data. As a result, the usefulness of the various gage types can be extended. For example, accelerometers, because of their high frequency and amplitude limits, can be employed near the shot to measure acceleration and/or velocity (by integration), Velocity gages, because of their higher sensitivity, can be employed at relatively larger distances from the shot to measure velocity and displacement or acceleration (by integration or differentiation).

Jan 1, 1954

By H. C. Cooke

"The Eustis mine, which was discovered in 1865, lies about 6 miles southwest of the city of Sherbrooke, Quebec, in lots 2, 3, and 4, range 9, Ascot tp. The mine was operated almost continuously from 1865 to 1937, under vanous owners.The ore was pyrite with varying amounts of chalcopyrite, a small amount of zinc blende and galena, and a low content in gold and silver. Parts of it ran quite high in copper, but the mine average would probably have been between 3 and 4 per cent. The high percentage of pyrite made it profitable to separate the ore into a copper concentrate and a pyrite concentrate. The latter was shipped away for manufacturing sulphuric acid, or was treated in a plant erected in 1887 at Capelton by the Nichols Chemical Company.The ore is a replacement of mica schist, which in turn was formed by the shearing of rhyolite flows. Ore also replaces the 'green rock', a term locally applied to carbonatized mica schists. The ore contained numerous 'horses' and smaller fragments of country rock, in all stages of replacement, ranging from those whose character was quite distinct to those whose ancestry could only be detected by an indefinite banding preserved in the sulphides."

Jan 1, 1954

By A. M. Bell

"Hallnor mine is in the township of Whitney, Porcupine district. To date, its production of gold has been second largest in the east Porcupine field. Ore was discovered in the property in 1936 by diamond drilling in overburdened country. This drilling was undertaken by Noranda Mines following the discovery of ore in conglomerate at Pamour 1 mile to the east.Milling commenced at the Hallnor in June 1938, and to the end of 1945 432,000 oz. gold had been produced from 889,000 tons of ore, giving an average recovery of 0.49 oz. a ton.The West mine of Pamour, the Broulan orebody, and the veins on the Hallnor and Bonetal are all parts of a mile long vein system that has been separated into three sections by cross faulting. In consequence, they could well have been described in one paper. In treating them individually the viewpoint obtained from each may lead to conflicting opinions, and any conclusions advanced in this paper on the general structure should be modified by the conclusions advanced in papers on the neighbouring properties.GENERAL GEOLOGYRock FormationsThe Hallnor orebodies occur within 400 feet of the contact between lavas and sediments, and may lie in either lavas or sediments. The lavas near the ore consist of flows of pillowed andesite and one flow of more acid and less sheared and chloritized lava locally named trachyte. These flows strike east-west and dip steeply. At the surface on the east side of the property the volcanics have been intensely altered to a massive carbonate rock having a north-south thickness in excess of 1,000 feet . This carbonate body extends west across the property with a plunge of 45° (Fig. 1)."

Jan 1, 1954