Search Documents

By S. F. Reiter, R. W. Guard, J. H. Keeler

DURING the last several years the authors have been conducting tests on a tensile machine that autographically records load-elongation data. In certain tests at elevated temperatures on face-centered cubic, hexagonal close-packed, and body-centered cubic materials (binary alloys of nickel, zirconium, and iron), the load-elongation curve as shown in Fig. 1 reaches a maximum load (Pmax,) at relatively small amounts of strain and a large amount of elongation occurs subsequently with a continuously decreasing load, until finally localized necking and fracture take place. This early maximum load behavior has been found without the accompanying evidence of localized necking as has been assumed by some, or of evidence of cracking as observed by others.' This behavior has also been observed by Nadai and Manjoinez whose results are in good agreement with ours. The prior strain, strain rate, test temperature, and crystal structure affect the observations. The influence of prior strain was observed in tests on unalloyed zirconium at 300°C in which specimens containing large amounts of prior strain (cold work) exhibited the type of curve shown in Fig. 1. No localized necking was observed after strain as much as that of point B. Annealed and recrystallized specimens of the same material showed a load-elongation curve with maximum load occurring after considerable strain hardening and at the beginning of localized necking. Interrupted tests (Fig. 2) show no loss in strength because of recovery or recrys-tallization during an interval at temperature without load. Recovery under stress such as found by Wood and Suiter3 in aluminum is now being investigated as one possible explanation. The strain rate is a contributing variable as shown in Fig. 3, a test on high purity nickel. Here the strain rate was decreased by a factor of ten during a test in which the maximum load was reached at a small strain. The slope of the true stress-true strain curve was positive with the more rapid strain rate and negative with the slower strain rate. In many binary ferrites an added effect of temperature has been observed. Fig. 4 shows the load-elongation plots for a binary ferritic alloy containing 2 pct Mo. The slope of the small portion of the stress-strain curve obtained at a strain rate of 0.01 mhr1 changes sign from negative to positive on going

Jan 1, 1955

By A. R. Troiano, R. F. Hehemann

The influence of partial decomposition to high temperature bainite on reaction kinetics at a lower temperature has been studied in two alloy steels. Reaction at the lower temperature is retarded by the prior treatment, and the extent of decomposition may be reduced. Interpretation of these results is based on a mechanism involving a limitation in the nucleation and growth of bainite plates. OF the major transformations in steel, the characteristics and general behavior of the bainite reaction are probably the least understood and appreciated. Limitations of space preclude a critical evaluation of the present status of the bainite transformation in this presentation; however, such a treatment will shortly appear elsewhere. Only the salient features pertinent to the present investigation will be introduced briefly here. Although the reaction curve for the formation of bainite is similar to that for a nucleation and growth process, other kinetic features are more in keeping with the martensitic mode of transformation. A definite temperature exists above which austenite will not transform to bainite.1-5 his temperature, which has been designated B., is determined by the composition of the austenite. Unlike other nucleation and growth processes, the amount of austenite transformed to .bainite is a function of reaction temperature. The extent of decomposition increases from 0 at H. to 100 pct at some lower temperature.' , This lower temperature will be designated B1 and appears to be relatively insensitive to austenite composition.% 5 The similarity in the effect of reaction temperature on the bainite and martensite transformations serves to emphasize the close connection between these two decomposition processes. Austenite decomposition in the bainite range proceeds without partition of the alloying elements.8-11 Partition of carbon has been proposed" primarily on the basis that partial transformation to bainite lowers M, and increases the amount of austenite retained at room temperature. Carbon enrichment resuslting from such partition has been employed to explain the influence of reaction temperature on the extent of decomposition.'" It should be noted, however, that no enrichment has been detected experimentally in high carbon steels.1,14,15 Lattice-parameter measurements of retained austenite in steels containing 0.3 to 0.4 pct C have indicated carbon enrichment, 3,10-18 although the split indicative of a high carbon martensite has not been reported. Carbon enrichment, if it does occur, must be highly localized around the bainite plates. Therefore, carbon enrichment does not account for the influence of temperature on the progress of the bainite reaction."' Thermal history is known to influence the martensite transformation through stabilization.20,21 No similar phenomenon in the bainite transformation has been reported. Materials and Procedure Two triple-alloy steels were chosen for this investigation. Their compositions were as given in Table I. These steels were chosen because the pearlite reaction did not interfere with the bainite reaction. Steel K was received in the cast condition and forged from 2 in. square bars to 1/2 x1 3/4 in. plates. The 4340 was received as 11/4 in. hot-rolled rounds. Both steels were homogenized in vacuum for one week at 2300°F in order to minimize segregation. A quenching dilatometer similar to that described by Flinn, Cook, and Fellows" was employed for the kinetic measurements. Dimensional changes were detected by a differential transformer coupled with a high speed recorder. The dilatometer was mounted so that it could be transferred to any one of three furnaces: a nitrogen-atmosphere austenitiz-ing furnace and two salt-bath furnaces for isothermal transformation. Dilatometer specimens were 1/32 x 1/4x 1/2 in. with a gage length of 1.4 in. All specimens were nickel plated in order to minimize decarburization during austenitizing. The austenitiz-ing conditions consisted of 10 min at the temperatures given above. Austenitizing temperatures were controlled to 210°F and transformation temperatures to ±3ºF. The precision of the dimensional measurements was estimated to be ± 5 x105 in. per in. Results and Discussion Isothermal Transformation: The characteristics of the isothermal bainite reaction will be described

Jan 1, 1955

By H. P. Holmes

Tonnage quantities of hafnium metal have been prepared in Kroll-process equipment designed for producing zirconium. Some slight process modifications have been necessary, but overall operation is the same as for zirconium. Hafnium oxide is chlorinated in the presence of carbon and the resultant hafnium tetrachloride reduced by magnesium metal. Byproduct magnesium chloride is removed in a high-vacuum distillation step and the hafnium sponge metal crushed for further use. Arc-melted metal can be forged and rolled to sheet, but the best material produced to date would not be considered cold ductile. INTRODUCTION This investigation is part of the program for the production of pure metals from domestic and foreign ores that has been underway at the Bureau of Mines for several years. It was done in cooperation with the Atomic Energy Commission and the Bureau of Ships.

Jan 1, 1955

By C. S. Matthews, P. Hazebroek, F. Brons

A method has been developed for calculating the average pressure in a bounded reservoir. The reservoir is first divided into the individual drainage volumes of each well, by using the criterion that at steady state each individual drainage volume is proportional to a well's production rate. The average pressure in each drainage volume is then calculated by a method developed in the report. By volumetrically averaging these individual drainage volume pressures, the average pressure in the entire reservoir is obtained. To calculate the average pressure in each drainage volume, a correction is applied to the ordinary extrapolated pressure, i.e., the pressure obtained by extrapolating to infinite time the linear portion of the graph of closed-in pressure versus log[?t/(t + ?t)], where At is the closed-in time and t the production time. The correction, which is a function of the production time, is presented in graphical form for different shapes of the drainage area (horizontal cross section of the drainage volume). INTRODUCTION It is important to be able to find the volumetric average pressure in a reservoir so that the size of the reservoir may be determined from material balance calculations. It is also desirable to be able to find the approximate distribution of pressure within a reservoir for detection of fluid movement. 'The purpose of this paper is to present a method for calculating both the average reservoir pressure and the approximate distribution of pressure within a bounded reservoir — that is, a reservoir with no water drive. In reservoirs where the pressure builds up rapidly after wells are shut in, the determination of average pressure generally poses little problem, for one often need only average the final buildup pressures. It is when pressure buildup is slow that difficulties arise. For practical and economical reasons, the time allowable for closing in wells is limited. If at the maximum allowable closed-in time the pressure has not reached a con- stant value (and this is more often the case than is generally realized), calculation of average pressure presents difficulties. One method which has been used in the past for obtaining an "average" pressure involves the extrapolation to infinite closed-in time of curves of pressure as a function of closed-in time. Contour maps of these extrapolated pressures are used in arriving at an average pressure. In some cases wells are shut in for arbitrary Lengths of time, and contours of these arbitrary shut-in pressures are used for calculation. All these methods are somewhat arbitrary and suffer from lack of fundamental theoretical basis. For example, no precise meaning can be given either to the extrapolated or to the arbitrary shut-in pressure. Furthermore, there seems to be no reason why either set of pressures should be contourable. It was because of the vagueness of these old methods and their lack of a sound theoretical basis that, the present method for determining average reservoir pressure was developed. SYMBOLS A = drainage area of a well, cm' A, = drainage area of well j, cm2 A , = total drainage area of all wells in a reservoir, cm2 c = coefficient of compressibility of fluid at reservoir temperature, atm-1 f = hydrocarbin-filled porosity, fraction h = net thickness of formation, cm k = permeability of formation, darcy p = pressure at a well, atm p0 = initial reservoir pressure, atm p* = pressure obtained by straight-line extrapolation of linear portion of plot of p versus log [At/(t+ At)] p = volumetric average pressure inside drainage volume of a well q = volume flow rate at a well, cc/sec a: prevailing reservoir conditions q, = total volumetric flow rate from a reservoir, cc/sec at prevailing reservoir conditions rw = radius of well bore, cm T = kt/fµcA t = corrected time of production of a well, seconds, defined by

Jan 1, 1955

By T. T. Campbell

A survey of the literature eras made covering the use of aqueous non-aqueous, and fused-welt systems for the electrowinning or electroplating of molybdenum metal. The survey was prepared in order to provide background for further investigations directed toward the electrodeposition of pure molybdenum metal from either aqueous or nonaqueous mediums. While a thorough effort was made to cover all available references, a critical review was not attempted nor does this survey pretend to be exhaustive in nature.

Jan 1, 1955

By J. L. Eakin

Systematic flooding was introduced into Nowata County, Okla., in May 1931. The results of this means of stimulating the nearly depleted Bartlesville reservoir in the county has been the subject of four Bureau of Mines Reports of Investigations.2-5/ This report presents a discussion of four full-scale water-flooding projects in the Delaware-Childers field and 1 pilot project in the Curl Creek field (fig. 1). All five plants have been in operation for only a few months. Although substantial increases in the rates of oil production have been obtained 1 by the injection of water, the projects are of particular interest at this time because of the novel methods of operation and new equipment that are being employed. One project utilizes a portable "package" plant designed for a pilot operation. All of the controls for this project are centrally located. The design makes it possible to remove the test plant to another location if the project is unsuccessful or if the unit is to be replaced by a larger plant. This project also utilizes diatomaceous-earth filters successfully for the first time and makes use of plastic pipe. Another novel feature of the operation is the aeration of Arbuckle limestone water through an airlift in the supply well.

Jan 1, 1955

By E. E. Harton

Bureau of Mines Information Circular 16, Bibliography of Investment and Operating Costs for Chemical and Petroleum Plants, was published in October 1949 as an aid in making estimates of investment and operating costs of processes for manufacturing synthetic liquid fuels. Development of such processes by the Bureau of Mines was authorized by Public Law 290, 78th Congress. This bibliography included refer¬ences to and abstracts of publications appearing from 1930 to September 1948 on all processes in general use in the petroleum refining and chemical industries. Publications in this field have been numerous since compilation of the above bibliography, and the present report was prepared to cover the field from September 1948 through June 1952.3/

Jan 1, 1955

By G. A. Pinsky, Pickard M. K

"IntroductionTWO METHODS of mucking have been used in sinking C shaft, the five-compartment production shaft of the Yellowknife property of Giant Yellowknife Gold Mines, Limited:(a) Band mucking during the original sinking in 1949 and 1950 (l); and(b) Mechanical mucking with the Cryderman shaft mucker during the recent deepening in 1954.This paper briefly describes the recent deepening and compares the performance figures of the two sinking operations.PlanningProduction planning in 1952 showed that it would be advisable to deepen C shaft in 1954 to provide for three new production levels and the installation of an underground crusher. To complete the required shaft work it would be necessary for a shaft crew to deepen the shaft about 500 feet, to partly excavate three level stations and a crusher station, and to cut a station for the loading pocket. Figure 1, a vertical section of the lower part of the shaft, shows the details of the deepening programme.During the planning period, Giant had a rather small supervisory staff and at the same time was experiencing a heavy labour turnover. As it was obvious that production would suffer if the sinking crew were recruited at the mine, it was decided that the merits of contracting-the shaft sinking to an independent contractor should be investigated."

Jan 1, 1955

By Elmer R. Kaiser

G. A. Vissac (Consulting Engineer, Vancouver, B. C.) —Some of the data presented in this paper, in connection with cost studies of washed coals, should be clarified and qualified. Washing a raw coal down to a low ash content may mean higher losses in refuse, but the cost of the operation may be more than compensated by the increased value of the resultant product. However, careful engineering and accurate machinery are required to insure maximum profits. Washing at a low gravity separation demands a very accurate automatic process, chiefly when the small sizes of coal are being handled. Coal consumers today are buying mostly on a Btu basis, cognizant of the fact that low ash contents result in lower installation costs and in savings in handling and transportation charges. The attached Table X gives the actual balance sheets of the various cleaning operations corresponding to various ash contents for the two coals presented in the paper, using the old technique of a two-products separation. or the new technique, now commonly used in Europe, of a three-way separation made possible by new methods and new equipment. Savings in capital costs, handling, and transportation have been calculated on the basis of a delivered cost f.O.b. plant of $10.00 per ton of coal at 16.5 pct ash (actual 1953 average price reported by Consolidated Edison, N. Y.), and of $3.50 at the mine also for 16.5 pct ash coal. In both cases this corresponds to values of 126 and 4.26 per 1 pct of combustible and per ton, respectively, on delivered and on at the mine prices. As an example, the middle western coal at 16.5 pct ash, raw, washed down to 4 pct ash in a two-way process will give 53.75 pct of clean coal at 4 pct ash and 46.25 pct of refuse at 31 pct ash. The value of the losses will be 0.4625x(100—31)x0.042 = $1.34. Add the cost of washing, capital, and operation, which is $0.35. The total cost will then be $1.69. But with a three-ways separation we will have 53.75 pct of first-grade coal at 4 pct ash, 37.25 pct second-

Jan 1, 1955

Jan 1, 1955

By J. Fageant, W. C. Ellis

All major regions in a progressively solidified germanium ingot were related through successive orders of octahedral twinning. The occurrence of lineage structure and the generation and survival of orientations are discussed. WHEN metals solidify in a temperature gradient a preferred orientation, or casting texture, usually develops. For example, in face-centered and body-centered cubic metals, most of the solidifying crystals have a cube axis, <loo>, aligned approximately in the freezing direction.&apos; In the solidification of diamond cubic metals this is not the case, since there is a natural tendency to form twin orientations.&apos; . In this paper, twinning relationships in cast germanium are described; some conclusions with respect to nucleation and survival of new orientations are discussed. In the first experiment, an ingot of high purity germanium, % in. in diameter and 1 % in. in length, was formed by progressive solidification4 from the bottom. The ingot was cut into 21 slices, each circular and about 0.030 in. thick. The top surface of each slice was polished and etched to reveal the regions of different orientations. Orientations were determined by the Laue X-ray back-reflection method. The uncertainty in the determined orientation relationships was l" or 2" when separate slices and films were involved. Frequently, however, advantage was taken of illuminating across a boundary when the patterns of the two orientations were recorded on the same film. The uncertainty then was less than 1". Often the twin relation was evident from common zones or individual reflections. Twin relationships were recognized through comparison of the values of the nine angles between cube poles of the two orientations with those calculated for successive orders of octahedral twinning. The birth and survival of each region can be reconstructed by visual examination of the etched slices shown in Fig. 1. In slice 21, where solidification began, many regions are present; these regions were found to be twin-related. Solidification appears to have started from one nucleus formed probably at the wall of the crucible.* Subsequent ori- entations were developed by nucleation on existing solid surfaces, and only in the twin relationship. This is an example of a general process of nucleation on a surface of existing solid and may be descriptively termed oriented nuc1eation.t In germanium, and other diamond cubic substances, the orienting habit is that of twinning on an octahedral plane.&apos; " The prevalence of straight traces in the polished surfaces of succeeding slices (Fig. 1) suggests that the twinning observed in the first slice persisted throughout solidification. This was confirmed by X-ray determinations. The schematic diagram of Fig. 2 shows the twinning relationships of the major regions throughout the ingot. Since all observed relationships are describable as twinning, it is reasonable to conclude that no random nucleation occurred in the freezing of the ingot. An alternative possibility would be that nucleation of a random nature occurred, but only those nuclei in twin orientations survived in subsequent growth. This is unlikely for there would be as good a reason for the growth of randomly oriented nuclei as for the growth of the many different orientations present after several orders of twinning. The many twin components contain a wide distribution of orientations, and did grow. In fact, they are the only ones found in the solid. The conditions of solidification of this ingot were such as to discourage nucleation of crystals wholly in the liquid. The rate of solidification was 0.125 in. per min. This slow rate of heat removal afforded but small opportunity for supercooling within the liquid —a condition needed to provide enough decrease in free energy for such nucleation. When nucleation occurs on an existing solid surface, the interfacial energy between the existing and forming regions is important in determining the new stable orientation. The new orientation is expected to be one which minimizes this energy. In the diamond cubic structure, the interface for the

Jan 1, 1955

By Frank Doxley

"FIRST OF ALL I should like to express to the members my sincere thanks for having had the privilege of serving them as President during the year now ending, to the Council for their guidance, and to the Secretary-Treasurer for his untiring efforts on both the Society's and my behalf during my year of office.During the .past five years the Canadian •Coal picture has changed considerably. In the West, production has been almost halved and many mines have been closed, due to the development and expansion of oil and natural gas industries, which, with some imported residual oil -on the Pacific coast -have provided competition which has been impossible to meet. The two major railway companies have embarked on an oil-burning and dieselization .programme and with this has .been lost one of the largest available markets for coal. Natural gas pipe-line installations still further threaten the remaining outlets for Western coal.In the East, retention of markets has also been a •problem, due to the intense competition provided by imported American •coal and the importation of residual oil.Because of cost it is impossible for central industrial Canada to be supplied with .coal from the Maritimes and markets are, therefore, restricted to fringe areas in Ontario and Quebec, and the Maritime Provinces.The dieselization programme of the Canadian National Rail ways has meant the loss of a large market for Nova Scotian coal and it is fair to assume that within a comparatively short time the market will be completely lost."

Jan 1, 1955

Jan 1, 1955

By A. L. Titchener, M. B. Bever

FROM their investigation of the martensitic transformation in Cu-Zn alloys, Greninger and Mooradian&apos; concluded that there was no critical temperature at which martensite formation began in this system. Recent unpublished work by Gen-evray With two compositions of brass revealed the existence of a critical temperature, which is a function of composition and stress. In the work reported here the temperature range of the martensitic reaction was studied as a function of composition in high purity Cu-Zn alloys. The specimens were about 4 in. long with a diameter of 1/16 in.; their compositions are given in Table I. They were heated under vacuum for 5 min at 5" to 10°C below the temperature of incipient melting, and quenched into brine at about — 10°C. Specimens of alloys C, D, E and F were obtained with little or no precipitated a phase. Many attempts yielded only three usable specimens of alloy B, and even these contained appreciable amounts of a. All efforts failed to preserve metastable p in alloy A (containing 38.02 pct Zn and 0.002 pct each of Pb and Fe). The transformation was studied by measuring the electrical resistance during continuous cooling and heating of each specimen at similar rates. The cooling media were alcohol with dry ice from room temperature to — 78°C and a bath of petroleum ether and methyl cyclohexane (75:25), cooled by liquid nitrogen, from —78" to about —150°C. Readings were also taken at —195 °C in liquid nitrogen. Fig. 1 illustrates a typical experiment. The relative resistance is obtained by assuming the known

Jan 1, 1955

By J. Visman

A simplified method of assessing the characteristics of a cleaning unit, including washability curves, yield figures, ash error, separating gravities, and error curve. FOR more than 25 years evaluations of coal cleaning units have appeared in many publications, and during this time considerable progress has been made in developing the theory and techniques of calculating washery results. A variety of characteristics have been defined over the years, many receiving general recognition during the first post-war Coal Preparation Conference in Paris in 1950. Coal preparation has become a science, and the approach to preparation problems is being revolutionized. Formerly, for example, if a coal operator wanted to know the performance of a given cleaning unit for a particular grade of his run-of-mine, he either shipped a carload to the manufacturer for a test run or relied on a report of a test carried out on a coal similar to the one he intended to clean. In modern practice the expensive, time-consuming test work generally can be avoided if the washability curves of the coal in question and the error curve of the cleaner are known. Normally a guarantee can be given on the strength of this information. General acceptance of modern standards has thus reduced the need for pilot-scale models of existing types of coal cleaners. Needless to say, the method requires exhaustive and accurate information on the cleaning unit and on all the additional circumstances affecting its results, information that ultimately can be secured only from actual tests made in the laboratory or in the washery. It is not the purpose of the present discussion to compare the merits of various characteristics, but to describe the general method of calculation, including a method of obtaining data with a minimum of laboratory work. All data presented here were derived from tests made at the plant with portable field equipment, using small quantities of varsol, carbon tetrachloride, and bromoform. It will be explained later that the use of standard fractional ash contents designated normalized ash contents aids considerably in reducing the routine testing of coal cleaners. Like any other statistical procedure, this method has limitations, and it is not recommended for any work in connection with guarantees. Even a varying commodity such as coal, however, will follow the law of large numbers, which is the basic law of statistics, thus allowing simplification of test work without appreciable loss of accuracy. The characteristics needed for evaluating cleaner performance are normally derived from a float-sink analysis of samples of the clean coal and the refuse, followed by ash determinations of the various fractions. Usually a sample of feed is also collected to find its ash content and to make a single specific gravity cut, both in connection with determination

Jan 1, 1955

By R. W. Bruce, K. W. Downes

"IntroductionSULPHUR production in Canada from all sources for the year 1953 amounted to about 375,000 tons. Except for 16,000 tons of elemental sulphur derived from natural gas, this production was in the form of by-product pyrites, liquid sulphur dioxide, and sulphuric acid. In the same year, Canadian industry imported 359,000 tons of elemental sulphur from the United States. The cost, including transportation charges, to Canadian consuming plants ranged from $35.00 to $45.00 per long ton, depending upon location.Although most of the sulphur consumed is used in the oxidized form it is often most convenient to buy sulphur in the elemental form, and convert it to sulphur dioxide or sulphuric acid in situ as required. This is because elemental sulphur is easily shipped and stored, weighs only half as much as an equivalent quantity of sulphur dioxide and one-third as much as the corresponding quantity of sulphuric acid, and is readily converted to these forms in a sulphur burner. A process, therefore, which could economically recover elemental sulphur from sulphide ores would be most attractive.Since the turn of the century, notable improvements have been made in extractive metallurgy, but until recently only limited attention has been paid to the possibilities of elemental sulphur recovery. This has been due to the plentiful supplies of cheaply mined Frasch sulphur which have been available on the world markets."

Jan 1, 1955

By Shiou-Chuan Sun

THE fact that coals of different ranks and even of the same rank differ greatly in their amenability to iroth flotation is well known. In recognition of the need for an explanation of this phenomenon, two hypotheses have been suggested. Wilkinsl reported that the floatability of coals increased with an increase of the carbon content or rank. This postulate is handicapped by the fact that bituminous coals that possess moderate carbon contents are actually more floatable than anthracite coals that have high carbon contents, as shown in columns 6 and 9 of Table I. Taggart and his associates&apos; implied that the difference of floatability between bituminous and anthracite coal was caused by the variation of carbon-hydrogen ratio. This is not applicable to the relative floatability of other coals and carbons. For example, column 11 of Table I shows that the carbon-hydrogen ratios of low-floating lignitic coal and non-floating animal charcoal are not only smaller than the moderate-floating anthracite coal, but are also similar to the high-floating bituminous coal. Furthermore, according to this hypothesis, high temperature coke-A (464), Ceylon graphite (1238), and lamp-black (357), all possessing extremely high carbon-hydrogen ratios, should be less floatable than other substances having much lower carbon-hydrogen ratios such as high volatile-B bituminous coal (11.9 to 22), anthracite coal (35.7 to 60.5), lignitic coal (15.6 to 33.6), and charcoal (13 to 26.2). However the former group is actually more floatable than the latter group. In this paper, a surface components hypothesis is Proposed to explain the different floatabilities of coals, carbons, and hydrocarbon minerals. The validity of the hypothesis is experimentally supported by the actual floatability, natural floatability, wettability, and adsorbability for neutral oils of coals, carbons, and hydrocarbon minerals tested. The combustible recovery of the flotation results, as used in this paper. was calculated from Eq. 1: P (100-Ep) 100 RWCP Rc= [1] F (100-E,) C, where R, is the percent combustible recovery; F and P are, respectively, the weight of feed and the weight of concentrate or product; E, and Ep are, respectively, the total percent of ash plus moisture in feed and in concentrate; Ru. is the percent weight recovery: and C, and C, are, respectively, the percent of combustible in feed and in concentrate. Except for ash and moisture content, all chemical components of a coal are assumed combustible. The experimental work included studies on flotation, ultimate and proximate analyses, contact angle tests, extractions of bitumen-A with benzene, adsorptions for liquid hydrocarbons, and wetting tests. Most of the flotation experiments were performed in a laboratory Fagergren machine; others were tested in a small Denver machine. The solid feed for the former was 300 g and for the latter was 30 g. The solid materials used for flotation were crushed to —48 mesh. After the mineral pulp in the flotation cell was agitated for 6 min and the pH was adjusted to 7.5 & 0.2 with sodium hydroxide or hydrochloric acid, a petroleum light oil having a viscosity of 5.73 centipoises at 77 °F was added and conditioned for 2 min. Finally, pine oil was introduced and the froth was collected for exactly 3 min. The weight ratio of petroleum light oil to pine oil was kept constant at 1.5 to 1. Tap water was used for all flotation tests. Contact angles were measured with a captive bubble machine. For each coal sample, three specimens were mounted in transoptic mounts and polished with levigated alumina, first on a sheet glass, then on a cloth-covered metal polishing wheel. The polished specimen was first washed with distilled water and wiped thoroughly on a cleaned linen pad, then transferred into the pyrex cell of the captive bubble machine and conditioned for 6 min., and finally measured for contact angles at three or more points. Except where otherwise stated, the induction time for each measurement was 1 min. The contact angle representing each material was obtained by averaging the measurements of three specimens. The linen pad was first washed with warm distilled water, then boiled 30 min in a 2N sodium hydroxide solution, and finally washed with distilled water until no trace of sodium hydroxide could be detected in the decanted solution. The cleaned linen pad was stored under distilled water. Immediately before using, the pad was rewashed and transferred into a clean pyrex petri dish partly filled with distilled water. The glassware and rubber gloves used were cleaned by soaking in sulphuric acid-potassium dichromate cleaning solution, followed by rinsing with distilled water. The polished specimens were handled only by glass forceps. The ultimate and proximate analyses were made in accordance with the ASTM standard procedures for coal and coke. The extractable bitumen-A was determined by weighing 1 g of —100 mesh sample and placing it in a desiccated and weighed ASTM aluminum-extraction thimble. The thimble was placed in condenser hooks and inserted into an extraction flask containing 100 cu cm of benzene. The flask was heated and the benzene vapor was condensed by water coils. At the end of 24 hr of percolation, the thimble was removed, desiccated, and weighed. Loss in weight of sample was taken as bitumen-A and calculated to dry and ash-free basis.

Jan 1, 1955

By Murray Greyson

A number of tests were made with various methanation catalysts in fixed-bed, conventional fluidized-bed, and multiple-feed, fluidized-bed equipment to develop catalysts and processes for methanation of synthesis gas. The results show: 1. Methanation reactions may be carried out in 1-inch, bench-scale equipment at high synthesis-gas throughputs with good temperature control of the reactions if a multiple-feed type of fluidized-bed design is used. 2. Nickel is superior to iron as a catalyst for the methanation of synthesis gas, unless the process is considered in terms of a combined operation that produces both gaseous and liquid products. 3. Techniques of catalyst preparation determine, to a large extent, the process life of nickel catalysts, and these techniques must be thoroughly investigated before any conclusions can be reached. 4. Enough data are available to indicate that the sulfur concentrations in synthesis gas that is used for methanation are extremely critical, and maximum process limits should be carefully evaluated.

Jan 1, 1955

By F. M. Stewart, F. H. Callaway, R. E. Gladfelter

In this paper oil initially in place is calculated by the various methods commonly used for analysis of water drive fields using data available as time progresses. Rate and pressure are predicted by means of the same methods using data available at the end of two years&apos; history. These predictions are then compared with subsequent performance permitting an evaluation of the methods, which are Modified Schilthuis, Simplified Hurst, van Everdingen et al (1952), and the Electric Analyzer. INTRODUCTION Several variations of the material balance equation, differing in the term used to evaluate water influx, are in common use for estimating oil in place, predicting rate and volume of water influx, and forecasting producing rates and reservoir pressure in water drive reservoirs. The electric analyzer with an electrical network set up to simulate the oil reservoir and aquifer and their contained fluids may be used for the same purpose. Examples of the application of one or another of these methods have appeared in the literature. The accuracy and reliability of the material balance for calculating oil in place have been covered.&apos; However, there have been few articles in which more than one method has been applied to an actual field allowing a comparison. It is felt that a field example, simple in nature, where the Modified Schilthuis, Simplified Hurst, van Everdingen et al (1952), and the Electric Analyzer have been applied would be of benefit in providing an evaluation of these methods as to their comparative usefulness and reliability in calculating initial oil in place and predicting performance. The Torchlight Tensleep reservoir is a small field in a large aquifer. The reservoir oil is greatly under-saturated, having a bubble point of only 55 psi and 2 cu ft/bbl of gas in solution. Changes in the reservoir volume factor in the range of pressures encountered are small, meaning little error in converting production to reservoir conditions. The pressure has declined from 1,618 psi initially to 137 psi during the first four and one-half years. Water production has been negligible. For Torchlight, the material balance equation as discussed later is considerably simplified by the omission of terms having to do with free gas. Thus with simpler equations, less variables to consider, the large pressure drop, the absence of a gas phase, and rapid pressure-rate adjustments, which mean an unusual amount of history in a short time, the reservoir appears suitable for comparing the methods listed above. GENERAL INFORMATION ON THE FIELD The Torchlight field is located on the eastern side of the Big Horn Basin, Big Horn County, Wyo., approximately 3 miles east of the town of Basin. The Tensleep reservoir was discovered in September, 1947. It lies at a depth of about 3,000 ft and produces oil of 35" API gravity. A total of five wells have been completed in the Tensleep, but only four are now producing. The reservoir is well defined in areal extent in that a total of 13 wells have penetrated the Ten-

Jan 1, 1955

By C. Wagner

When an alloy solidifies and the composition of the solid differs from the composition of the liquid, atoms of the alloying elements rejected at the solid-liquid interface have to diffuse toward the bulk liquid. Diffusion may be supported by convection. Theoretical calculations have been made for a liquid without convection, for a liquid involving natural convection, and for solidification of a liquid alloy at the surface of a rotating disk as an example of forced convection. WHEN an alloy solidifies, the equilibrium composition of the originating solid phase differs in general from the composition of the liquid phase. Thus, segregation may take place, i.e., the composition of the solid phase formed at different times differs from the bulk composition. The degree of segregation depends on several factors such as the partition ratio of the alloying elements between the liquid and the solid phase, the rate of solidification, and convection. To clarify, a theoretical analysis has been worked out. The following presuppositions are made: 1—Calculations are confined to the solidification of binary alloys in which the concentration of component A (solvent) is much greater than that of component B (solute). 2—The equilibrium concentration of the alloying element B is assumed to be lower in the solid phase than in the coexisting liquid phase. 3—At the solid-liquid interface, partition equilibrium is assumed. 4—The dependence of the partition ratio of the solute between the liquid and the solid phase on concentration and temperature is disregarded since only small concentrations of the solute are considered. 5—The concentration of the alloying element B in the solid phase is supposed to be lower than the saturation concentration for the formation of a second solid phase. 6—diffusion in the solid phase is disregarded, since diffusion rates in the solid state are comparatively low. When the partition ratio of the solute between the liquid and the solid phase is greater than unity, a part of the solute is rejected at the solid-liquid inter- face and has to diffuse toward the bulk liquid. Thus there is necessarily a concentration difference in the liquid between the solid-liquid interface and the bulk liquid as has been pointed out by Hayes and Chipman,&apos; Rutter and Chalmers,&apos; Tiller, Jackson, Rutter, and Chalmers, and others (see Fig. 1). In view of the concentration gradient in the liquid phase, the ratio of the concentration of the solute in the solid phase to that in the bulk liquid differs from the equilibrium ratio, although at the solid-liquid interface, partition equilibrium is assumed. Under certain limiting conditions, the solid may even have virtually the composition of the bulk liquid as is shown below. General Equations Let u be the linear crystallization velocity in cm per sec, D the diffusion coefficient of component B in the liquid phase in cm2 sec-&apos;, c&apos;,, and c", the concentrations of component B in the liquid and the solid phase, respectively, in mol per cm", and s the distance from the solid-liquid interface toward the bulk liquid at a given time t. The partition ratio is assumed to be equal to a partition constant K. Thus. The difference in the specific volume between the liquid and the solid phase may be disregarded. In view of the discontinuity of the concentration of the solute at the interface according to Eq. 1, u(c&apos;, — c",), , , = tic&apos;, (S = 0)(1 — K) gram-atoms B per unit area per unit time are rejected at the interface and have to diffuse toward the bulk liquid. From Fick&apos;s first law it follows that uc&apos;,,(s = 0) (1 ~K) == - D(dc&apos;,,/?>s). _-„. [2] The concentration profile in the liquid near the interface depends on the interplay of diffusion and convection as is discussed in the following sections. A schematic concentration profile is shown in Fig. 1. The "effective thickness of the diffusion boundary

Jan 1, 1955