By H. W. Mead, C. E. Birchenall

SELF-DIFFUSION of cobalt has been investigated by Ruder and Birchenall,1, 2 Nix and Jaumot,3 and Gruzin.4 The results for a given tem- perature differ by a factor of about six in the extreme cases with no really close agreement between any two sets of data. The first two groups of investigators employed the decrease of surface activity method. Since Ruder and Birchenall have shown that the values obtained from this method are sensitive to the surface preparation, it seemed desirable to perform a few check experiments by a method not open to this objection.

Jan 1, 1956

By G. P. Conard, R. C. Hall, J. F. Libsch

The 50 pct Fe-50 pct Co alloy undergoes a transformation from disorder to an ordered structure of the CsCl type reportedly in the vicinity of 732OC. During this process, the coercive force goes through a maximum, apparently as a result of strains associated with the coherent nucleation and growth reaction. This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction, which is associated with annealing to a high degree of order with the continuous application of a magnetic field. The increase in ratio can be explained on the basis of a decrease in 90' domain boundaries and, perhaps, by an increase in anisotropy resulting from lattice distortion. THE 50 pct Fe-50 pct Co alloy undergoes a disorder-order transformation which has been reported to occur in the vicinity of 732°C1,2 The ordered structure is the CsCl type.' This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction as a result of heat treatment in a magnetic field, sometimes called a response to magnetic anneal.'-' The purpose of this investigation was to study the course of the ordering reaction, the nature of the response to .heat treatment in a magnetic field, and the relation, if any, between ordering and the response. Procedure The method of approach in this investigation was to produce an initial structure as completely disordered as possible and then gradually to order the alloy by isothermal anneals at various temperatures under different conditions of the applied magnetic field. Magnetic, magnetostriction, and X-ray analyses were of primary importance in determining the property and structural changes resulting from the isothermal anneals. Rings of the 50 pct Fe-50 pct Co alloy were prepared from the elemental powders by a powder metallurgy technique, further details of which may be found in ref. 7. The initial structure was produced by annealing the specimens for ½ hr at 1000°C, cooling to and holding for ½ hr at 900°C (in the a range above the ordering temperature), and water quenching. Isothermal anneals were performed at 600°, 675°, 720°, and 740°C. For example, rings were heated to 600°C, held for a predetermined period of time, and cooled by natural cooling at a rate slightly slower than an air cool (average of 20" to 25°C per min). The tests (magnetic, etc.) were made after each heat treatment. All high temperature treatments were performed in a purified hydrogen atmosphere. The treatments at the various temperatures were carried out under one or more conditions of an applied field including 1—no field, 2—field of 20 oersteds applied on cooling only, and 3—field of 20 oersteds applied continuously during heating, holding, and cooling. Magnetic measurements were made using the standard Rowland ring technique8 with a maximum field strength of 100 oersteds. The magnetization curve, induction at 100 oersteds (B.), residual induction (Bt), and coercive force (Hc) were determined. All magnetic analysis data were based on an average of the results from three rings. A strain gage technique9 as used for the measurement of magnetostriction. The X-ray determination of the relative amount of ordered phase present was made on the ring specimen used for magnetic measurement. This was done by the back-reflection method using a rotating specimen (because of the large grain size) with unfiltered CoKa radiation and a 7 hr exposure time. Intensity measurements of the ordered line (300) were made by comparing visually the films so obtained with standard films prepared by exposing for different lengths of time a specimen given a long time anneal (high degree of order). Results In all instances the saturation induction (induction at 100 oersteds) was found to increase slightly with annealing time. This effect was small and appears to be the increase in saturation induction to be expected on ordering.10-13 The residual induction behavior was markedly influenced by the field condition during annealing, Figs. 1, 2. For the condition of no applied field, the ratio of residual to saturation induction remained essentially constant for short annealing times but showed a significant increase at longer times. With increasing annealing temperature, less time was required to produce this increase in the ratio. In the case of the 600°C anneals, the increase did not occur until approximately 20 hr, Fig. I, while on annealing at 740°C the increase was immediate, Fig. 2. Slight decreases in the ratio may be observed at 100 hr for specimens treated at 720°C and at 1 hr for those treated at 740°C. Specimens annealed in a field of 20 oersteds showed a residual to saturation induction ratio consistently higher than that for the specimens annealed without the field. The first anneal with the field (¼ hr) caused an abrupt increase in the ratio at all temperatures; thereafter, the increase in the ratio was generally similar for specimens annealed

Jan 1, 1956

By Leendert de Witte, Fred J. Radd

In many areas caring failures can be directly related to electrical currents observed in the casings. It is the thesis of this paper that the observed casing currents are mainly due to electrochemical potentials of the type in evidence on spontaneous potential curves of electrical logs. The general nature of these potentials are discussed and an equivalent circuit is given for current and potential distributions around open holes. The casing forms a short circuit to these potentials and tends to average the effects of local cells. The case of casing corrosion opposite the Dakota water sands in the salt-mud area of Kansas is discussed anil used us a qualitative, illustration of the relation between SP's and casing currents. A method of quantitative derivation of casing current distribution frorn electric log SP curves, using linear transform theory, is described and results are compared with a measured current profile. The effects of hydrogen over-potentials at the cathodic portions of the pipe are considered and some laboratory data are given in support of conclusions regarding the over-1.01tuge.s. INTRODUCTION To date an appreciable amount of work has been done on the measurement of oil well casing currents and on the correlation of the anodic portions of the current profiles with corrosive casing failures. Speculations on the origin of the casing currents have, however, remained rather vague; and although almost every plausible cause has been mentioned, there is to the writers' knowledge no clear-cut expose' on the details of the causes of the corrosive currents in the literature. A study of current surveys and casing failures in the N.W. Burnett field, Ellis County. Kan.. indicated the probability that concentration cell emf's between the Wellington salt section and the relatively fresh waters in the Dakota sands were a major cause of the corrosion currents. A more general concept evolved upon analysis of the severe corrosive conditions in the Pleistocene sands in the Ventura Avenue and San Miguelito fields in California. In this area no major variations in the salt content of the formation waters occur and yet large casing currents are observed. An explanation is found in the fact that the local spontaneous potentials which are set up due to concentration contrast between the drilling fluid and the connate water are short circuited when casing is set. The very conductive path through the casing increases the magnitude of the currents and has the tendency to average local sources over fairly large intervals. Current will flow between the sections that are predominently shaly and the sections that are mostly sandy. At the places where the current leaves the pipe, corrosive attack will occur. This same phenomenon will be present wherever unprotected pipe is set through sections that show large SP kicks on the electric logs over reasonably thick interval~. GENERAL- NATURE OF THE SPONTANEOUS POTENTIALS When a sequence of sedimentary rocks is penetrated by a drill hole filled with a mud which has a different salt concentration from that in the formation waters, various types of electrochemical potentials are established between the formations and different parts of the mud column. Opposite clean sand sections. a simple liquid-liquid junction potential will be observed; while opposite argillaccous formations, a membrane potential, often referred to as shale potential, will be established. The first quantitative analysis of these emf's in terms of liquid junction and membrane potentials is due to Wyllie.1

Jan 1, 1956

By J. J. Gilman

Examination showed that characteristic cleavage step patterns are observed on the cleavage surfaces of undeformed, slipped, bent, twinned, compressed, and indented zinc crystals; and the effect of temperature is discussed. Dimples were seen to produce cleavage steps in a treelike pattern in otherwise undeformed crystals. The steps seem to originate when cracks intersect screw dislocations. IT has been known for a long time that the path of fracture in polycrystals may be discontinuous (see Jaffe, Reed, and Mannl for review). Recently, Kies, Sullivan, and Irwin2 have proposed, and given evidence, that crack propagation is discontinuous within individual crystals as well. Other evidence has been given by Low.' When discontinuous cracks within a crystal join together to make a macrocrack, the lamellae between each set of two cracks are torn somewhere, forming small cliffs. These cliffs appear as lines when the cleavage surface is observed microscopically.4,5 The lines have been called vein, tree, and riverlike markings by various authors, and they have sometimes been mistaken for fissures. The descriptive term cleavage steps is used in this paper. Cleavage steps vary in height over a wide range of values, from molecular dimensionsG to lor. and larger. Kies, Sullivan, and Irwin,2 as well as George,' have shown that the gross cleavage step patterns for plastics, polycrystalline metals, and for mono-crystals are sometimes similar. Thus, they depend mostly on the mechanical variables that prevail during cleavage and are relatively insensitive to the structure of the material. For example, parabolic markings2,7,8 sometimes result when cracks open up ahead of, and not coplanar with, the main crack front. If the advance crack has the same velocity as the main crack, their intersection line is a parabola, otherwise it is a hyperbola or an ellipse. The patterns are strongly affected by differences in crack velocities. This results in chevron patterns which point to the place of origin of the main crack. It is the purpose of this paper to demonstrate the existence of a mechanism of cleavage step formation which is a continuous rather than a discontinuous process. Also, certain characteristic step patterns are described, and the strong effect of temperature is shown. The specimens were zinc monocrystals (grown from 99.999+ pct pure metal). These were cleaved at room temperature and at — 196°C. Results and Discussion Cleavage step patterns are highly variable from point to point on a given specimen, as well as from one specimen to another. Although the patterns shown in the photographs are typical, they have been selected for graphic illustration. Figs. la and lb compare undeformed crystals that were cleaved at —196 °C and room temperature, respectively. Cleavage at room temperature (Fig. lb) resulted in a higher density of high steps (dark black lines) and enhanced the visibility of the fine background markings. Deformation by simple slip caused no marked change in the step patterns until the glide strain reached about 1.0. But, as Fig. lc shows, the density of high cleavage steps was greatly increased by large glide strains. Corrugations lying perpendicular to the slip direction may also be seen in Fig. lc. These are caused by deformation bands. The cleavage resistance of the crystal of Fig. lc was very high compared to undeformed crystals (estimated by the force on a needle required for cleavage). Striking and varied cleavage step patterns were observed on bent crystals. Two characteristic patterns that were observed on crystals bent at 25°C, and cleaved by reverse bending at —196°C, are shown in Figs. 2a and 2b. The first, Fig. 2a, consists of V-shaped lines similar to the parabolas of other materials2,7 Fig. 2b shows a pattern that is the equivalent of Fig. la, consisting of faint background lines with a few higher step markings. Cleavage of bent crystals at room temperature resulted in Figs. 2c and 2d. Now, the cleavage step lines show a strong tendency to follow one of two perpendicular paths. In Fig. 2c (bent once), many of the cleavage step components that lie parallel to the bend axis are assembled into irregular lines. In Fig. 2d (bent twice), the cleavage steps again tend to consist of two perpendicular components, but neither of the components is assembled into lines. Also, the step density is higher.

Jan 1, 1956

By T. C. Atchison

This report describes a mobile laboratory designed and constructed by the Bureau of Mines in 1950 to meet the needs of an experimental blasting research program. The laboratory has facilities for making; film recordings of 16 simultaneous transient electrical signals over a broad range of amplitude, frequency, and duration. The signals are recorded with specially designed oscilloscopes and high-speed drum cameras. Each of the 16 channels records on a separate strip of 35-millimeter film by using interchangeable input units, transducers having different sensitivities and output impedances can be accommodated. The laboratory can be used to record both steady-state and transient phenomena originating as electrical voltages or capable of being converted to electrical voltages by appropriate transducers. Thus, the laboratory can, be used in studying various types of vibration problems or high-speed phenomena, such as ground and building vibrations, machinery vibrations, airborne vibrations, electrical-circuit switching phenomena, millisecond timing, and seismic phenomena occurring when rock is broken by explosives.

Jan 1, 1956

By J. M. McDowell

A study has been made to deter~r~irre how the behavior of a water drivee reservoir changes as a function of the permeability of the formation and as a function of the size of the aquifer. The effect of pressure maintenance programs on the rote of nat11rn1 water influx is also studied, (IS well as the influence on the influx of the position of water injection we1ls with reference to the oil-water contact. The results are determined by the use of an electrical reservoir analyzer and are plotted as families of curves of pressure, natural water influx, and water injection vs time or cumulalive production. Two size aquifers are studided. One is limited with a 36-inile radius, and the, other approximates an infinite reservoir. The field remains the same in all respects for the completed. study except that the permeability is changed to agree with that assumed for the aquifer. 1 N TR ODUCTI ON this study was undertaken in -dcr to determine how the pres- sure decline and water influx of a water drive field would change as a function of the rate of fluid withdrawals, as a function of the permeability of the formation, and as a function of the size of the aquifer. The effect of pressure maintenance programs on the rate of natural water influx was also studied as was the position of water injection wells with reference to the oil-water contact. The information has been determined by the use of an electrical reservoir analyzer1, sometimes referred to as a Carter type analyzer. This instrument is an analog type computer which can be set up to represent a water-drive oil field. It can reproduce the past performance of the field in terms of analogous electrical quantities when the proper circuit analog of resistors and condensers has been determined, also, it can determine the future behavior for any method of production which may be selected, or permit the comparison among several different methods. Although most applications of the reservoir analyzer"" have been to thc study of specific field performance, it is intended to use the analyzer here to help understand how various reservoir characteristics effect the final performance of the field and to sec under what conditions water injection will be of benefit and to what extent. Within the oil industry the performance of water-drive reservoirs was first described analytically by LV. Hurst' and M. Muskat2 for certain types of boundary conditions. The solutions of the equations developed involved products of exponential functions and Bessel functions. Later publications by Hurst4 and van Ever-clingen" and the hooks of Muskat6 gave further information on reservoirs with other boundary conditions. They also presented rather extensive curves and tables to help evaluate the analytical expressions involved. A rccent series of publications by Chatas. bascd on the work of Hurst and van Everdingen, gives quite complete charts and tables of data to evaluate the pressure decline or water influx in infinite or limited radial reservoirs. and in linear reservoirs. The curves in all of these publications are given in dimensionless form

Jan 1, 1956

By Harris J. W

Mr. Gillie and Mr. Harris have given us a wealth of information and food for thought on the vital subject of information and food fo rthought on the vital subject of reducing costs and mention considerable saving in some of the larger items. There are a number of points on which I would like further information, but I will confine my remarks to a relatively small saving which is of particular interest in view of another paper to be presented this afternoon.Mention is made of a 50 per cent reduction in the amount of zinc used in the precipitation of gold slime from the pregnant solution. Would Mr. Harris enlarge on the methods by which they obtained this reduction; and could he give an actual figure of zinc consumption either by ton of ore treated or per ounce of bullion recovered.AuthorsWe consider the reduction of zinc is due to improved clarification of the pregnant solutions. The sand clarifiers used prior to the installation of the 50 ft. -thickener were not satisfactory due mainly to the blending of the hessian and matting under the sand. Under these conditions the leaf clarifiers were fed with overflow solution from the clarifiers and were overloaded in consequence. The addition of Calgon has also been beneficial.The present consumption of zinc per ton of solution treated is 088 lb. per ton.A. L. "Keats (No,rth Broken Hill Limited)In the operation of milling equipment there is a progressive increase in maintenance expenditure during the life of a machine, so that when comparing the cost of operating old equipment with the cost of operating new equip...

Jan 1, 1956

By R. S. Shoemaker, D. L. Harris

PST investigations into the possibility of concentrating the low-grade iron ores of the Gogebic Range in Wisconsin have been hampered by the complex association of the constituent minerals. In part the problem arises from the fact that the iron occurs essentially as two minerals, hematite and goethite, having nearly the same chemical composition but exhibiting different physical properties. Individual grains of these minerals are usually so small that the ore must be ground to a size finer than 325 mesh if substantial liberation of the minerals is to be secured. Appraisal of beneficiation tests on this iron ore requires, therefore, some method of determining quantitatively the contents of constituent minerals in the various products of the beneficiation. Because of the chemical similarity of the two iron minerals, chemical analyses do not provide a means of differentiation. Although the minerals are different physically, they are both opaque and friable, and as the ore must be ground to a very fine size for liberation to be secured, quantitative microscopic methods of analysis are extremely difficult at best. In an effort to overcome these analytical problems, a quantitative X-ray diffraction analysis method has been developed at the University of Wisconsin for the research program on iron ore beneficiation. The X-ray diffraction analysis of chemical compounds of crystalline form has proved of inestimable value for structure studies and rapid qualitative analytical purposes in a number of fields.' In some cases X-ray diffraction analysis has been found suitable for quantitative determinations. H. P. Klug2 found that quantitative procedures for quartz powders when mixed with calcium fluoride were reproducible within ±1.0 pct. Talvenheimo and White3 reported quantitative analyses of clay minerals to be accurate within 10 pct and also detected 1 pct of bentonite in 99 pct illite. In other investigations,'" powders of quartz and mica have been analyzed quantitatively with accuracies from 1 to 5 pct. A powder of tungsten carbide was analyzed similarly by Redmond7 and Rooksby8 reported the determination of small amounts (0.11 pct) of calcium oxide in magnesium oxide. In the most generally practiced use of X-ray diffraction, traces of the diffracted beam are recorded as lines on a film much as lines of elements are recorded on an optical spectrograph film. As with the spectrograph, the darkness of the lines denotes the amount of the constituent in the sample. If the film is replaced by a Geiger tube assembly and a graphic recorder or a scaling unit, the intensity of the diffracted beam can be registered as a peak on a chart or energy impulses per unit of time on the scaler. Several methods of quantitative measurement have been investigated and reported in literature. Klug2 used manual operation of the goniometer and a counting technique to determine the difference in counting rates at the diffracted angle and for the background. In another case3 the area under the recorded diffracted peak was the basis for the determination. In other instances the height of the recorded diffraction peak above background, measured while the goniometer was moving, has been the basis for the measurement. The sizes of particles most suitable for diffraction techniques are reported in the literature as follows: for tungsten carbide a maximum of 40 microns7 and for quartz a maximum of 5 microns.' Very fine sizes of crystals are known to cause a broadening of the diffused beams; hence some workers have set a lower limit of 0.1 micron for quantitative results. Guinier10 has indicated that broadening of the diffracted X-ray beam is not appreciable for crystallites larger than 0.02 to 0.03

Jan 1, 1956

Jan 1, 1956

By R. Silverman, H. Blumenthal

It was found that despite the similarity of chemical analyses of different titanium carbides used as base materials for cermets, the physical properties, especially transverse-rupture strengths, of test bars were different. Hence this metallographic study attempts to link physical properties to micro-structures. It is shown that microstructure, grain shape, and grain growth are functions of three interrelated factors: 1—powder production procedure, 2—surface conditioning of the particles, and 3—impurities either contained in the original powder or acquired during ball milling. An explanation is offered for the "coring effect," long observed, but heretofore of unknown origin. The explanation is based on assumption of an oxide film and on chemical analyses which substantiate these findings. TITANIUM carbide has become in recent years a material of great interest in the high temperature field. Consequently, many manufacturers in the United States and Europe are producing titanium carbide for cermet applications as well as for additions to the well known tungsten carbide tools. All present commercial processes of titanium carbide production utilize the chemical reaction of titanium dioxide and carbon to form as nearly as possible stoichiometric Tic. This reaction is carried out in three ways: 1—in a menstruum of molten metal,' 2—in the solid state, either in a protective atmosphere2 or in vacuum;" or 3—in an are-melting operation. In spite of the fact that the pure carbides obtained in these operations are almost identical chemically, the physical properties vary considerably when they are combined with a binder (Ni, Co) to form cermets. This fact led the authors to examine metal-lographically nickel-bonded titanium carbide in order to find the possible reasons for this behavior. Materials and Methods Five different titanium carbides were used in this investigation. They are identified in Table I. The first four materials were used in the as-received condition. Material E, received in lumps, was crushed to —100 mesh and carried through a flotation process in order to bring its graphite content in line with the other products. A Galagher flotation cell was used with pine oil as frothing agent. The chemical analyses of the investigated materials are given in Table 11. The binder used was carbonyl nickel of 9 to 14 microns particle size, supplied by A. D. Mackay. The materials were ball milled at a ball to charge ratio of 6:1 using procedures described under "Experiments and Results." All particle sizes mentioned are averages determined with a Fisher Sub-sieve Sizer. Test bars (lx0.40x0.16 in.) were prepared by 1—hot pressing to 85 to 95 pct of theoretical density at pressures between 1 and 1½ tsi and temperatures from 1600" to 1800°C, 2-—-cold presssing after 3 pct camphor had been added, or 3—wet pressing, both 2 and 3 at pressures between 5 and 10 tsi. All pressed bars were sintered in a vacuum of 105 to 10-6 mm Hg for 2 hr at 1350 °C. Transverse-rupture strengths were determined by breaking on a Baldwin Universal Testing Machine over a 9/16 in. span. Densities were measured by water displacement. The preparation of the specimens for micrographs was done according to Silverman and Doshna Luscz." All magnifications are at X1000. A sodium picrate electrolytic etch was used. Experiments and Results The influence of ball-milling procedure, ball-milling medium, pressing procedure, and sintering procedure on the microstructure of 80/20 — TiC/Ni were investigated. Ball Milling of Materials A, B, and C in a Steel Mill: Figs. 1 and 2 show microstructures of hot-pressed and vacuum-sintered test bars of materials A and B after the respective materials had been ball milled to 2.1 microns particle size in a steel mill and mixed with 20 pct Ni binder. Material A (Fig. 1) shows considerable grain growth. Also evident is a tendency of the carbide grains to coalesce. The density is 98 pct and the low transverse-rupture strength of 111,000 psi is probably caused by many large grains and an unfavorable packing factor. Almost all grains show a slight indication of "coring." Material B (Fig. 2), although showing grain growth, still has many small particles and a better distribution of binder and carbide due to the relative absence of the coalescing tendency. "Coring" can be observed in almost all grains. The high transverse-rupture strength of 179,000 psi and the density of 100 pct are believed to be due to the many small grains completely surrounded by the binder phase. There is also a preference to form spherical grains with material A, while most grains of material B preserve their angular shapes. Material C, of which no picture is given, stays between A and B in every respect. Rounding of some grains can be observed as well as coring, but the latter to a lesser degree than with material B. Its densification is good and the transverse-rupture strength obtained is 142,000 psi. Ball Milling of Materials A, B, C, and E in a WC Mill: When the Tic powders were ball milled to 2 microns particle size in a we mill, then ball-mill mixed with 20 pct Ni binder, hot pressed, and vacuum

Jan 1, 1956

By J. E. Papin

MORENCI ores contain as an average about 0.015 pct molybdenite, MoS2. Incidental to the concentrating operations applied for the recovery of copper minerals, approximately two-thirds of the molybdenite is floated and appears in the final copper concentrate. The economic importance of molybdenum and the success achieved in its recovery in milling operations elsewhere encouraged research directed toward its recovery in marketable form. Several procedures are utilized to effect separation of molybdenite from copper and iron sulphides, but only two have wide application. In the better known of these two methods the molybdenite in the copper concentrate is depressed in a flotation operation using soluble starch as the depressant. The tailing from this treatment thus becomes a low-grade molybdenite concentrate which after thickening, filtering, and low temperature roasting is repulped with water and subjected to additional flotation steps for recovery of the molybdenite. A thio-phos-phate collecting agent is employed in flotation of the copper minerals. Presumably the stability and lasting effects of that collector type necessitated the practice of depressing molybdenite followed by subsequent roasting to insure elimination of copper and iron sulphides from final molybdenite concentrate. The second important method of recovery is applied at various southwestern plants. In those plants xanthates are in use as copper collecting agents. It has been found that xanthates are relatively unstable and their collecting power for sulphides is destroyed by very simple procedures. The method generally applied is to subject the xanthate-acti-vated concentrate, in the form of a pulp, to prolonged heating using steam as the heating medium. A concentrate thus treated may then be subjected to a flotation operation for recovery of the molybdenite, using mineral oil collecting agents, and the copper and iron sulphides will be depressed. Neither of the above processes was applicable to Morenci concentrates. Morenci uses a thio-phos-phate collecting agent in its flotation operation. However, it was established that soluble starch was not a depressant for Morenci molybdenite; therefore the first step in that process was not applicable. AS would be expected the copper and iron sulphides in Morenci concentrates could not be depressed by the heating methods used on xanthate activated concentrates. Low-temperature roasting did eliminate the effects of the thio-phosphate but had to be rejected as uneconomic in as much as the tonnage of concentrates involved was too great. Preliminary research having established the above facts, it became obvious that new methods would have to be developed for the recovery of molybdenite from Morenci concentrates. A broad laboratory investigation was initiated along two general lines, both directed toward depression of copper and iron sulphides. One approach was through the use of water-soluble oxidizing agents with the objective of destroying the thio-phosphate in the concentrate and thus eliminating its collector effect. The other approach involved the use of soluble sulphides, which have long been recognized as sulphide depressants. These efforts resulted in laboratory processes which showed promise. Research was then extended to a pilot plant having a daily capacity of several tons of concentrate. This operation soon demonstrated that soluble sulphide—basically sodium polysulphide—when applied to a pulp made slightly acid with sulphuric acid, proved to be the most effective sulphide depressant. The rate of concentrate treatment in this plant and the low molybdenite content of the concentrate prevented carrying the process to a conclusion, namely, production of molybdenite concentrate of marketable grade. Laboratory treatment of pilot plant concentrate indicated that a marketable product could be made from it, given a tonnage suited to available cleaner flotation machine capacity. Accordingly, the molybdenite plant was enlarged to permit treatment of the total copper concentrate from the extension plant, maximum of approximately 800 tons per day. In the enlarged plant a major difficulty was encountered. No criteria could be established as a basis for control of the process. In the early stages of flotation, because of the small amount of molybdenite involved, there was no visual evidence of the relative floatability of molybdenite with respect to

Jan 1, 1956

By D. W. Blaylock

I. The Lower Kittaning bed is the most important bed in Clarion County from the standpoint of present production, but the Clarion bed has the largest recoverable reserve. 2. Known measured and indicated reserves in all beds, based on a minim thickness of 14 inches and 1,800 short tons per acre-foot of coal in place, are estimated at 1,210 million short tons as of January 1, 1952. Of this total, 790 million short tons is in beds 28 inches and mare thick. Areas in some beds were omitted from the estimate because available data relative to the bed characteristics are too wager for ding an estimate that conforms with the definitions of measured and indicated coal adopted for this study. Should future drilling or development prove reserves in these areas, they should be added to the total estimated reserves.

Jan 1, 1956

By R. E. Carter, C. Wagner, F. D. Richardson

By means of inert markers of radio-platinum, it has been shown that cobalt metal oxidizes by out-ward diffusion of cobalt atoms through the oxide. Oxidation rates have been measured at various temperatures and oxygen pressures and have been found to agree with the rates calculated from the Wagner equation and the authors' values for the diffusion coefficient of cobalt in the oxide. The distribution of radio-cobalt in growing oxide loyers has been accurately measured and found to be different from that predicted from the Wagner oxidation theory. Attempts have been made to measure the change of lattice parameter of the oxide with composition. SEVERAL investigators have shown that cobalt metal oxidizes according to the parabolic law,1-3 but no detailed study has been made of the oxidation mechanism. Cobaltous oxide has a metal-deficient lattice, but the defect concentration which is dependent on the oxygen pressure is only approximately known.' From the similarities in the structures of "CoO" and "FeO" and the rate laws governing the oxidation of cobalt and iron, Gulbransen- as suggested that cobalt, like iron," oxidizes by diffusion of cobaltous ions through the oxide layer. To substantiate this hypothesis, he has attempted to measure the oxidation rate of cobalt as a function of the oxygen pressure but has been able to report only that the rate depends on a "small" power of the pressure. On the other hand, Preece," Valensi,' and Arkharov' all have suggested from indirect evidence that oxygen diffuses through the COO to the metal-oxide interface. The present authors, in a previous paper,' have shown that the rate of diffusion of cobalt in cobaltous oxide is dependent on the oxygen pressure. In that investigation, they also found that cobaltous oxide disks made by complete oxidation of cobalt metal were porous at their centers (Fig. 5L, ref. 4). Both these facts strongly suggest that oxidation of the metal proceeds via outward diffusion of cations. In order to establish the mechanism unequivocally, oxidation experiments were made with inert radioactive platinum markers, and the dependence of oxidation rate on oxygen pressure was measured. In addition, an attempt was made to determine the form of the cation vacancy gradient, which the marker experiment showed must exist across a growing oxide layer. This was done by depositing radioactive Co on the surface of a cobalt disk and then measuring the tracer distribution across the oxide layer produced by partial oxidation of the metal. Finally, an X-ray examination was made in an attempt to find the expected change of lattice parameter of COO with oxygen pressure. Experimental The apparatus and materials used were substantially the same as those previously described by the authors.4 Marker Studies: The use of inert markers to follow oxidation reactions was first attempted by Pfeil" in 1929, and radioactive markers have recently been used by Davies et al.' In the investigation reported here, the markers were applied as an (NH4)2PtCI6 slurry in several thin streaks across both faces of four disks of cobalt metal 1 mm thick and 14 mm in diameter. The disks were then oxidized almost to completion at 1200°C in pure oxygen. After oxidation, they were mounted and sectioned and auto-radiographs were taken to locate the markers. Oxidation Rate: The oxidation rate of cobalt was measured at 1148°C at oxygen pressures ranging from 0.0055 to 1.0 atm and at 1000°, 1148", and 1350°C under 1 atm of oxygen. The rate was deter-

Jan 1, 1956

By J. O. Edstrom, G. Bitsianes

Parabolic rate constants were determined for the formation of wiistite by the solid state reaction between magnetite and iron. The reaction was diffusion controlled and inert marker studies indicated that the mass transport through the wiistite layer was accomplished by means of iron migration. Relationships between rate constants and self-diffusivities are discussed. The transport capacity for iron through dense wustite layers was found to be sufficient to carry on reduction, even in gaseous reduction processes. REDUCTION of iron oxides has been the subject of many investigations. Most of the work, however, has been done on rather crude material and there have been difficulties in correlating the data on a quantitative basis. The reverse process of the oxidation of iron has been studied more thoroughly and usually by starting from the pure metal. As a result, the mechanisms of oxidation are now fairly well known.It has generally been found that the oxidation of metals follows the so-called parabolic 1aw;Q hat is, when the oxides are formed as dense layers, their thicknesses are proportional to the square root of the reaction time. This parabolic law follows directly from Fick's first law of diffusion The flux, J, is defined as the quantity of diffusing substance passing per unit time through unit area of a plane at right angles to the direction of diffusion. This flux is proportional to the concentration gradient of the diffusing substance, and the factor D, known as the diffusion coefficient, is introduced as the proportionality factor with dimensions of (length)'/time. If the flux is measured as the increase of thickness of the oxide layer (Ax) per unit time (t) and the assumption is made that the concentrations of the reactants at the phase boundaries of the layer are independent of time, Eq. 1 reduces to Integration of this expression yields the parabolic function ax = k . t. [31 The product of the diffusion coefficient and the concentration difference across the oxide layer is included in the constant k. When iron is exposed to a highly oxidizing atmosphere, the oxide phases are formed normally in a topochemical fashion, i.e., the interfaces between the phases maintain parallel positions to the original surface of the specimen. Above 570°C, the phases are orientated usually in the order of iron, wiistite, magnetite, and hematite, a condition in conformance with the requirements of the Fe-0 system. Below 570°C, the wiistite phase is unstable and has not been found as a normal constituent in the oxidation products of iron. There is a strong probability that continuous layers of the solid oxides are formed as the specific volumes of the phases increase in direct order from iron to hematite.' , ' Regarding mass transport through dense solid oxide layers, Wagner' has postulated that diffusion in oxides generally may be interpreted as migration processes of ions and electrons. There must be normally a concentration gradient across the growing oxide layer for diffusion to occur. This condition requires that there be deviations from the ideal stoi-chiometric composition of the oxide and accordingly deviations from the strict order of an ideal lattice. Such "lattice defects" include interstitial ions, cation and anion vacancies, quasi-free electrons, and electron holes and are decisive for all migration processes.' Cations, anions, and electrons all may have some mobility in the oxides but the movement of one of the particles generally far exceeds that of the others. Previous work', 1,2,7 has shown that during the oxidation of iron the migration through the wiistite layer, and probably also the magnetite layer, is confined to the movement of iron ions. Migration through hematite, however, has been found to take place by oxide ion movement. These behaviors are in direct agreement with the type of vacancies present in the respective oxides. Reduction of Iron Oxides The gaseous reduction of iron oxides, like the oxidation of iron, takes place in a topochemical fashion at distinct interfaces between the appearing phases."-'" Porosities might be expected in these reaction products, since their specific volumes are less than that of the starting material. Frank and van Der Merwe" have shown, however, that it is theoretically possible for nonporous layers to form if the degree of misfit in specific volume is less than about 15 pct. These aspects on porosity formation

Jan 1, 1956

By P. Breidt, E. S. Greiner

THIS note reports a determination of the melting point of germanium, and the liquidus of the Ge-Ga alloys; lattice constants of the a phase are given. The alloys were prepared by melting germanium (>20 ohm-cm resistivity) and gallium (99.6 pct) in evacuated silica tubes. The materials (50 to 70 g) were heated at 1000°C, held in the liquid state for about ¾ hr, and then cooled rapidly in the tubes. Points on the liquidus were obtained by thermal analysis which consisted of obtaining time-temperature data during heating and cooling the materials in high purity graphite crucibles and a helium at- mosphere. Temperatures were determined with a Pt—Pt-Rh thermocouple protected by a silica sheath. The couple was calibrated against a National Bureau of Standards calibrated couple and also against the freezing points of copper, silver, aluminum, and the 28.1 wt pct Cu, 71.9 wt pct Ag alloy eutectic. The samples for X-ray analysis were prepared by heating small pieces of the ingots in evacuated glass or quartz tubes at temperatures between 600" and 900°C for periods ranging from 2 hr to 22 days, periods deemed sufficient for equilibrium to be attained, followed by quenching in water. The heat-treated samples were ground to powder for X-ray analysis. The lattice constants of the germanium-rich phase (a) were determined with a baok-reflection focusing camera. The X-ray reflections (331 and 422 Cr Ka, 422 and 333 Cr KB) were corrected

Jan 1, 1956

By C. T. Baroch

This report summarizes cost data accumulated during 15 months of sustained operation of the Bureau of Mines Boulder City (Nev.) titanium plant, which had a capacity of about 1,350 pounds of titanium sponge per day. The plant was constructed during the 1952 fiscal year with funds supplied by the Ordnance Corps, Department of the Army. Its original purpose was to engage in process development work as a continuing phase of the Bureau of Mines policy to seek improvements in producing titanium metal. In early 1953 the Defense Materials Procurement Agency contracted with the Bureau of Mines for producing approximately one-half million pounds of usable ductile titanium sponge. Production began in May 1953, ended in September 1954, and yielded 492,503 pounds of acceptable metal. Operating costs covering this period of operation, with suggested depreciation and administrative costs, are given, as well as outlines of building and equipment capital costs. In addition, miscellaneous economic considerations are discussed, including labor and operating-time schedules.

Jan 1, 1956

By W. S. Hyler, W. L. Bruckart

The powder metallurgy and arc-cast types of wrought molybdenum stock were studied in rotating beam fatigue. Endurance ratios of unnotched specimens after 5x10 cycles were found to be 0.74 and 0.81, respectively. Fatigue notch factors (K,) of 1.36 and 2.05, respectively, were obtained on V-notched specimens having a theoretical stress-concentration factor Kt = 3.1. MOLYBDENUM and its alloys are rapidly gaining importance as engineering materials of construction for high temperature applications. AS a wrought material, molybdenum and its alloys are outstanding above 1800°F. It is necessary, however, with molybdenum to provide elevated temperature oxidation protection. This is currently being studied by a number of investigators. Thus far, there have been no published data on the fatigue behavior of molybdenum either at room temperature or at elevated temperature. The knowledge of fatigue behavior, particularly notched fatigue behavior, becomes increasingly important as the engineering importance of a material increases, especially from the design standpoint. The work described here was directed toward determination of the notched and unnotched rotating beam fatigue characteristics of molybdenum at room temperature. Also, it was desired to learn whether any difference exists between wrought molybdenum of the powder metallurgy and the are-cast types. Fabrication History of Bar Stock For this work, bar stock was procured from Climax Molybdenum Co. (are-cast type) and from Westing-house Electric Corp. (powder metallurgy type). The processing histories of these materials are listed in Table I. The first lot of are-cast molybdenum was deoxidized by aluminum additions. The second lot was deoxidized by carbon." Both lots of the powder Microstructure A microscopic examination of these materials, as received, revealed the powder metallurgy molybdenum to be free of inclusions and to be finely fibered. On the other hand, the are-cast C molybdenum possessed numerous carbide inclusions, and the arc-cast A appeared to have coarse grained fibers. These are shown in Fig. 1. Owing to the large apparent difference in fineness of fiber between the are-cast A and the powder product and are-cast C, a check was made of the recrystallized grain sizes to determine whether these differences persisted. A series of recrystallization anneals revealed mixed grain sizes in both the are-cast A and the powder product. Variations in grain diameter of as much as 50 times were found after full recrystallization at 1200°C for 30 min. There was no distinction between the two. Arc-cast C was not checked. Room Temperature Mechanical Properties Prior to subjecting the materials to fatigue tests, room temperature mechanical properties were determined. These data, together with the tensil: strength of the notched bars, data,togetherare listed in Table tensil: There were no significant differences in the tensile strengths of the two types of molybdenum. However, the powder metallurgy material was generally more ductile and yielded at a somewhat lower stress than the arc-cast material. Tensile strengths of the notched specimens indicated a slightly greater notch strengthening effect in the are-cast C than in the powder product, lot 2. Room Temperature Fatigue Properties Sample Preparation: Specimens were prepared for use in R. R. Moore rotating beam fatigue machines. These specimens had a continuous radius test section with a minimum diameter of 0.260 in. The specimens were prepared by grinding to shape and polishing to produce a smooth unworked surface. Polishing consisted of rotating a disk in the continuous radius section on which were attached, successively, emery belts of 240, 400, and 600 grit. The specimens were slowly rotated during the operation. The belt speed was high, and rotation was such that polishing scratches were longitudinal. Unnotched Fatigue Properties: Unnotched fatigue data were obtained from a number of specimens of each of the four lots of molybdenum. The results of the tests are presented in Fig. 2. From this figure,

Jan 1, 1956

By A. H. Roberson, L. H. Banning

DURING the past few years, a considerable tonnage of ilmenite has been produced as a byproduct of a monazite dredging operation and stockpiled near Boise, Idaho. This ilmenite has not been marketed because of the long distance from ilmenite-consuming areas and its comparatively low TiO2 content. Production of monazite from the alluvial sand deposits of Idaho is a mar- ginal venture when it is the only marketable product, and it will be necessary to establish a byproduct market before the operation becomes economically stable. Early in 1954, the Bureau of Mines Northwest Electrodevelopment Laboratory at Albany, Ore., conducted a series of tests which demonstrated that arc furnace smelting could be utilized to produce commercial quality pig iron and a high titanium content slag from these ilmenites. Additional studies showed that the slag chlorinated readily to produce a satisfactory yield of TiCl4. The investigation was carried out by two research teams. The Ferrous Metals Branch, with adequate

Jan 1, 1956

By John W. King

Uranium ore was first discovered in the Edgemont district of the southern Black Hills in the summer of 1951. The discovery was not made known for some time, but after the news leaked out prospecting became intense, and several hundred claims were staked in the spring of 1952. The Hot Springs Sub Office of the Atomic Energy Commission was established at that time and airborne radiometric surveys were commenced by the Government and by private companies. During the succeeding summer another important discovery was made by private airborne surveys in the northern Black Hills, and the area favorable for uranium ore was expanded many times. Between that summer of 1952 and the present, many individuals and groups have explored, developed, and exploited their claims until now uranium ore is produced in significant quantities and substantial reserves have been developed. The Black Hills portion of the geologic map of the U. S. issued by the U. S. Geological Survey is shown in Fig. 1. Sedimentary formations are exposed as a series of cuestas and hogbacks in a roughly annular pattern with the older sediments resting on the pre-Cambrian core, which is exposed in the eastern and southern portions of the dome.

Jan 1, 1956

By E. J. Haug, M. M. Fine

FOR several years work has been carried on by the U.S. Bureau of Mines at Rolla, Mo., to develop improved methods of concentrating the oxidized ores of lead and zinc. Various samples have been investigated, and results on some have been published 1,2 lished.l, 2 Details of the progress to date are given in a mineral dressing study now being conducted for an extensive oxidized lead-bearing tract in southeast Missouri, property of St. Joseph Lead Co. These oxidized ores present problems typical of many encountered in modern mineral dressing research in that recovery of very fine particles is of

Jan 1, 1956