Search Documents

By F. R. Cattoir

The Federal Bureau of Mines refined chromium from an aqueous electrolytic process in molten sodium chloride-chromium chloride electrolytes. Oxygen and nitrogen contents were reduced by a factor of 10 to 40, but most other impurities were little changed. The product usually contained a little more iron than the feed. Since iron was entering the bath from the iron pot and the graphite liner at a nearly constant rate, contamination of the chromium deposits by it was more serious at low currents and deposition rates. A few runs in an iron cell with a nickel liner yielded chromium containing one half as much iron as the feed, but up to 1.5 pct. nickel. In all cases the anode feed lay in the bottom of the container, which itself was used as the anode connection. With a 12-in. cell, variations in applied voltage from 0.05 to 1.5, in current from less than 10 to over 100 a., and in initial cathode current densities from less than 100 to over 2,000 a./sq.ft. had little or no effect upon the analysis of the metal produced) except for iron content. Changes in bath analysis from 3 to 11 pct. chromium were also without effect. These changes did bring about large differences in the physical forms of the crystals obtained. The thick heavy crystals produced at low voltage and current contained voids which made them difficult to leach free of chlorides. Easiest to leach were the thin leaf-like crystals obtained at around 1 v.

Jan 1, 1960

By Victor Erickson

ECONOMIC recovery, which began in 1958, carried through into 1959 but was somewhat retarded by the 116-day steel strike beginning in July 1959. Recovery and economic growth increased production and consumption of mineral fuels 3 percent above 1958. The increase was accomplished despite a drop of 26 percent in coal exports. Prices remained constant during the year so that the value of production and consumption also increased 3 percent over 1958. Stocks in the hands of producers at yearend were little changed from the supply at the beginning of the year. Employment in the field of mineral fuels decreased 6.4 percent from 1958. Average hourly earnings were up 7 percent, and average hours worked were up 5 percent, with the result that weekly earnings gained 11.8 percent. Internal freight rates were relatively constant, but ocean tanker rates declined both in 1958 and 1959 from the high rates charged during the Suez crisis. The index of major input expenses decreased for anthracite, held constant for bituminous coal, and increased for petroleum. The index of labor cost per dollar of product and per ton of product declined again in 1959 to a new low in anthracite and bituminous-coal mining industries.

Jan 1, 1960

By R. F. Rolsten

VAN Arkel 1 prepared ductile tantalum by the thermal decompoiition of tantalum pentachloride on a resistively heated wire (2000° C) in an evacuated bulb maintained at 100°C. Burgers and Basart2'3 observed the formation of a mixture of tantalum carbide and free metal when a carbon deposition base was used. campbel14 suggested the thermal decomposition of the iodide if a lower decomposition tem- perature was desired. To date, the details for preparing high-purity iodide tantalum have not been disclosed. EXPERIMENTAL The tantalum to be purified was symmetrically placed around the clear quartz deposition surface centrally located within a 64 mm cylindrical Vycor bulb. The deposition vessel usually employed5 was modified6 by incorporating a reentrant fin,mer in place of the customary metal filament in the head

Jan 1, 1960

By C. C. Clark, J. S. Iwanski

The purpose of this investigation was to study mi-crostructural changes that take place in a commercial nickel-chromium-iron alloy, such as Incoloy "901," over long periods of time at temperatures up to 13 50°F and to correlate such changes with creep-rupture properties. of the alloy. In the course of the investigation, some microstructural changes were observed which correspond to microstructural alterations found in previous studies of Inconel "X." Microstructural phases have been identified in both alloys with the aid of electron and X-ray diffraction and an electron probe microanalyzer. The materials used in this investigation were from commercial heats of the following chemical composition: Pct Cr Pct Ni Pct Mo Pct Fe Pct Cb Incoloy "901" 12.51 43.67 5.72 Bal. -Inconel "X" 14.61 73.44 - 6.61 1.02 Pct A1 Pct Ti Pct Mn Pct Si Pct C Incoloy "901" 0.10 2.46 0.46 0.24 0.05 Inconel "X" 0.70 2.43 0.51 0.36 0.04 Long-term creep-rupture tests were conducted on Incoloy "901" at temperatures of 1000°, 1200°1 and 1350°F. A summary of these results is shown in Table I along with the results of a long-term creep-rupture test conducted on Inconel "X" at 1500°F. The heat treatments given the specimens are also shown in Table I. When the creep-rupture results on Incoloy "901" are compared with shorter-tertn data, there is no evidence of any undue deterioration of the creep-rupture strength with time, nor is the elongation decreased more than would be expected from the influence of time alone. INCOLOY "901" PHASE IDENTIFICATION Microscopic examination of the Incoloy "901" specimens reveals a dark etching grain boundary constituent in the specimen which was under test for about 11,500 hr at 1000°F. This grain boundary constituent was seen to increase in size as the test temperature was increased to 1200" and 1350°F, Figs. 1, 2, and 3. Simultaneously, an acicular structure of definite crystallographic orientation appears within the grains of the 1350°F specimen, Fig. 3. Under examination with the electron microscope, a fine precipitate is observed in the 1200 °F specimen. Fig. 4. It becomes considerably larger in the 2850-hr 1350°F specimen, Fig. 5. In a few areas the precipitated particles have been replaced by, or transformed to, small needles or platelets. After 7380 hr at 1350°F, Figs. 3 and 6, the needles are much larger and have replaced nearly all of the fine precipitate. X-ray diffraction studies detected the presence of hexagonal Laves phase and hexagonal n phase (Ni,Ti) in the 1350°F specimens, Table 11. Only the Laves phase was detected by X-ray diffraction in the 1200°F specimen and none was detected in the 1000°F specimen. In this latter specimen, however, the small quantity of precipitate in the grain boundaries (presumed to be Laves phase) precludes its detection by X-ray diffraction. Composition of the hexagonal Laves phase is not yet known, although its diffraction

Jan 1, 1960

By E. A. Cisney

The formula for calculating the crystallographic angles of a tetragonal lattice is: C°S =where $ is the angle between planes (HKL) and (hkl). The angles in Table I have been calculated for indium

Jan 1, 1960

By R. J. Leary

A small electronic digital computer employing punched cards has been used to facilitate the solution of a variety of problems in Bureau of Mines pyrometallurgical research. In this work the computer has been found to be economical for solving both simple problems that occur repeatedly and those involving complex or iterative calculations. Each of these classes of problems and their respective solutions are described. These small computers can be used effectively by researchers when they work in consultation with a computer specialist. Close team work produces the required solutions in less time, and, oftentimes, in a more useful form. Participation in programming by researchers develops in them a skill for evaluating the suitability of problems for electronic computing.

Jan 1, 1960

Yallourn brown coal and its characteristics have been the subject of innumerable papers and discussions. The Lurgi process adopted for the production of Towns gas by the gasification of brown coal has been described frequently in literature.The application of the Lurgi process for the gasification of Yallourn briquettes has naturally lead to some unexpected problems. Rather than attempt to review the whole field of experience gained in the first two years of operation of the gasification plant at Morwell, this paper attempts to describe two problems encountered, peculiar to the fuel used, and the steps taken in overcoming them.THE PROCESS AND PLANTTo clarify the conditions surrounding the problems, it is necessary to briefly describe the gasification and cooling processes and plant.Brown coal briquettes are gasified in a pressure generator, using a mixture of steam and oxygen as a gasifying medium. Crude gas produced in the generator is washed and cooled in the waste heat boiler and coolers. Figure 1 shows an arrangement of the generator and coolers. The gasifying medium enters the generator through a hollow shaft in the base. This shaft drives the grate, which has three purposes: (a) to distribute the gasifying medium into the fuel bed; (b) to extract the ash from the fuel bed; (c) to support the fuel bed.Briquettes enter the top of the generator through the coal lock chamber and the fuel bed is maintained at a reasonably...

Jan 1, 1960

By W. W. Vaughn, R. H. Barnett, E. E. Wilson

Soon after the search for uranium ores on the Colorado Plateau began in earnest, thousands of feet of drill core ranging from 1 1/8 to 2 1/8 in. diam became available for study. Although significant advances had been made in the technique of quantitative gamma-ray borehole logging, instrumentation was in the development stage, and complete reliance could not be placed on gamma-ray logs alone to interpret quantitatively the meaning of radioactivity in a drillhole. A method that would be faster than chemical analysis and still give reproducible and reliable results for various drill core sizes was desirable to provide additional information on the enormous footage of drill core being accumulated. A solid phosphor scintillation drill core scanner was designed and constructed. Basically the instrument was developed to measure radiation from a drill core which would not be clearly recorded by a gamma-ray logger using a Geiger tube as the sensitive element. Such data would be beneficial in constructing isorad maps to delineate ore-bearing zones. A calibration in the range 0.01 to 0.1 pct eU.,O, was provided; above 0.1 pct eU3O8 gamma-ray logs were available and were being used to calculate grade and tonnage of ore reserves. The core scanner, however, has been used to estimate equivalent uranium content of ore-grade materials containing as much as 2.2 pct eU3O8 with an accuracy of ± 10 pct, the sample being in the form of a BX drill core. Actually, an apparent calibration of eU3O8 vs counts per unit time is a straight line with a slope that is a function of the sensitive element and the geometry of the counting assembly. A true calibration that will show the expected departure from a straight line is due principally to the random nature of the pulse from a radiation source and the nonlinearity of the electron circuitry. Design and Construction: Three methods of detecting radioactivity were considered and applied in developing the core scanner now in use: 1) the Geiger tube, 2) liquid scintillation phosphors, and 3) solid scintillation phosphors. The desired sensitivity and long-term drift characteristics needed for this operation could be attained only by using solid scintillation phosphors. All three methods are discussed. Before scintillation counters were common, nine beta-gamma sensitive Geiger tubes 7/8 in. diam by 12 in. long were used, arranged to surround the drill core with tube axes parallel to the axis of the core. This arrangement of Geiger tubes was en- closed in a lead shield 1 in. thick, and provision was made to slide a 6-ft length of drill core manually into the counting chamber, one foot at a time. A count for each segment was taken with a scaler while the core remained stationary. The equivalent uranium content of the different sections of drill core could then be estimated with the aid of a calibration curve of counts per unit time vs percent equivalent uranium (eU). In rare cases the effects of the radioactivity concentrated in small areas within the core introduced errors in the readings made with the Geiger tube arrangement owing to the geometry of the measurement. The variability of counting rate due to a localized concentration of radioactivity in a spot in the wall of a drill core is illustrated in Fig. 1. This effect and the inherent low efficiency of the Geiger tube were considered major disadvantages of this counting arrangement. When liquid scintillation phosphors became available the core scanner in Fig. 2 was constructed to make a more accurate measurement of the equivalent uranium content of a sample. This instrument contains about 4 liters of liquid phosphor in a stainless steel coaxial cylinder 1 ft long, with inner and outer walls 0.060 in. and 0.125 in. thick, respectively. Four end-window type photomulti-plier tube with cathodes of 2 in. diam, immersed in the solution at right angles to the axis of the core, were used to observe light flashes in the phosphor. The liquid phosphor offered equal sensitivity to radiation originating at any point in the enclosure and represented geometrically the optimum in design. However, providing a semi-permanent leak-proof seal between the glass envelope of the phototube and the metal walls of the container proved to be a serious problem in constructing the equipment. The most effective seals were especially machined O-rings from sections of large tygon tubing. The tygon took a permanent set owing to cold flow characteristics and in most cases sealed completely. The light absorption characteristics of the liquid phosphor changed gradually with time, and after one month the counting rate had decreased to half the original value. The most sensitive liquid phosphor tested proved to be a solution containing 4 g of 2.5-diphenyloxazole and 0.01 g of 2-(1-naphthy1)-5-phenyloxazole per liter of toluene. With fresh solution in the chamber and with all photomultiplier tubes operating in parallel, the counting rate contributed by any one of the four photomultiplier tubes was about 85 pct of the counting rate from a single tube operated individually. From these observations it was concluded that owing to coincident loss and light attenuation within the liquid phosphor, the apparent sensitivity could not have been materially increased by additional phototubes. However, this approach to core

Jan 1, 1960

By J. W. Eckerd

The crushing of chestnut-size (1-5/8 by 13/16 inch) Pennsylvania anthracite in four commercial crushers (impact) jaw) hammer-mill) and gyratory types) was studied by the Bureau of Mines to determine which could produce the largest proportions of buckwheat Nos. 1 and 2 sizes (9/16 by 3/16 inch). Single pass dry and wet crushing techniques and the effect of stage crushing were evaluated. Calculations were made to show the effect of closed-circuit reduction on production rates and yield of the various sizes. The data show that the gyratory crushers produced the greatest percentage of the desired sizes. A ring-type hammer mill produced the greatest tonnage of buckwheat No.1 and rice (14.9 tons per hr.) during dry grinding tests) but the yield of these sizes was only about 55 percent) as compared with 62 to 70 percent for the gyratory crushers. The impact and jaw crushers produced the smallest amount of buckwheat and rice and the largest quantity of oversize material.

Jan 1, 1960

By Joseph A. DeCarlo

This publication presents a tabulation of oven-and beehive-coke plants in the United States as well as pertinent statistical data on the number, capacity, kind, and condition of the ovens. Coke is an essential raw material in pig-iron production and the coal-chemical materials produced during the coking process are used to manufacture fertilizers, paints, plastics, synthetic rubber, explosives, detergents, nylon, pharmaceuticals; dyes, and many other products necessary to the high standard of living in this country. In table 1 the oven-coke plants in the United States on December 31, 1959, are listed. This shows the name and address of the company, location of the plant, classification or type of ownership, number and type of ovens, annual coke capacity, and the coal-chemical materials produced. The "furnace" plants I are those owned by iron and steel companies and most of them are integrated with blast furnaces to facilitate transportation of raw materials for steel making. Furnace plants represented 87 percent of the total coking capacity and their average annual capacity was 1. 3 million tons. The "merchant" plants are those associated with chemical companies, gas utilities, as well as those that produce metallurgical, industrial, and residential-heating grades of coke and coal-chemical materials for sale on the open market. These coke plants are smaller than furnace plants and in 1959 their average coke capacity was only 520 thousand tons annually. On December 3l, 1959, there were 54 furnace and 20 merchant oven-coke plants in existence in the United States.

Jan 1, 1960

By S. C. Sun

Most previous work on sedimentation of coal 1 and mineral 2-3 suspensions has been conducted in graduated 1-liter glass cylinders of 6-cm diam. With this type of large container it is often difficult to see through the suspension and tedious to perform a large number of tests. Furthermore, the heavy glass walls and the graduation lines of glass cylinders cause internal and stray reflections, respectively. To obviate these difficulties, an Atlab Emulsion Viewer from Arthur H. Thomas Co. was adopted as an alternative apparatus. Equipment: The viewer," shown in Fig. 1, consists of: 1) a stainless steel frame rack holding 21 flat-bottom Nessler tubes or an ungraduated replica 1.64 cm ID and 1.80 cm OD, 2) a movable masked 150-w lumaline lamp behind the tubes, and 3) a scaled glass panel with 100 vertical divisions in front of the tubes. The tubes are snugly held by springs in slots formed by spacer bars, which also serve as shields to eliminate stray light. The lumaline lamp is mounted behind a slit in a movable housing so that it can be positioned behind the suspension to be examined. The lowest or 100-divi-sion line on the front glass plate is leveled with the upper side of the bottom of all tubes. The scaled portion of each tube, roughly 19 cm high and 40 ml in volume, is used to study coal and mineral suspensions. Procedure: The following procedure was used in many tests. A 1.6-gm sample of dry coal was mixed with 16 ml of distilled water in an ordinary test tube and allowed to stand for three days, with occasional shaking to insure thorough wetting of all particles. The slurry was transferred to a Nessler tube and diluted to 32 ml. The pH regulator and flocculating reagent were added, and the slurry was diluted to reach the uppermost or zero-division line. The tube was immediately stoppered and inverted downward and up again ten times during a period of 35 to 40 sec. The lumaline lamp was turned on during the inversion period. After inversion the tube was quickly returned to the viewer rack. The time elapsed for each 10-division drop of the demarcation line between solid and liquid was recorded by stopwatch until the 80-division line was reached in the zone of compression. Additional readings were taken at 15, 30, and 60 min after settling began. The clarity of the supernatent liquid was observed also. As the settling rate became considerably slower at the 75-division line, it was convenient at this time to start the next test in a separate Nessler tube. This was continued until the suspensions in any number of the 21 tubes were tested. An attempt was made to correlate the experimental results between the Nessler tube and a 1-liter glass cylinder. Table I shows that coal particles settle much faster in the cylinder than in the tube, which has a large wall effect.' The correction factor for the tube impedance is 1.662 2 0.145 at the 40-division line in the hindered settling zone, and 1.614 & 0.139 at the 75-division line in the compression zone. This rough correlation was established by dividing the pulp height of each container into 100 divisions and comparing the settling rates of the two containers at the same divisions. Tests were also performed to determine the accuracy of the viewer. The results, not presented, showed that error was within 10 pct.

Jan 1, 1960

By R. V. Lundquist

Lime-soda sinters, made and processed for recovering alumina and soda, consisted of several types of compound structures differing from the ideal dicalcium silicate and sodium aluminate. Many or these compound structures were causes for low alumina recovery and contributed to the relation or leach slurries. Presence or free lime, whether in the sinter or released by hydrolysis of sinter compounds, contributed to relation of leach slurries. Free lime tends to establish the initial viscosity assumed by a leach slurry. Previous investigations by the Bureau of Mines (1, 4)4/ and by other laboratories (5) have demonstrated the technical applicability of the lime-soda sinter process to the recovery of alumina from aluminum silicate materials. The basic concept of the process is sintering aluminum silicate materials with limestone and soda ash for the production of dicalcium silicate and sodium aluminate and then extracting the sodium aluminate by leaching the sinter in causticized liquors. Alumina is precipitated from the pregnant liquors by carbonating with carbon dioxide. Reaction in the sintering operation may be represented by the following simplified equation: A1203?SiO + 2CaCO3 + Na2C03 = 2Ca0?SiO + Na20?Al203 + 3C02

Jan 1, 1960

By J. A. Jaekel, W. C. Aitkenhead

Uranium deposits in the Spokane Indian Reservation, as well as those around Mt. Spokane, are essentially low grade, much of the ore containing less than 0.2 pct U3O8. The Mining Experiment Station of the Division of Industrial Research, State College of Washington, has been engaged in intensive research on the amenability of these low grade ores to froth flotation. The results: successful flotation of autinite, chief mineral constituent. At the outset of this work the goal was a concentrate of 1 pct U3O8 with a 90 pct recovery from ores containing less than 0.2 pct U3O8. Most of the work has been done on argillite ore from the Midnight mine on the Spokane Indian Reservation. The goal has not been attained using this ore, but samples of the granite ore from Mt. Spokane yielded successful results. For example, a concentrate containing 11.2 pcl U3O8 was produced from a Mt. Spokane high grade ore containing 1.27 pct U3O8 with a recovery of 97.8 pct. Another Mt. Spokane ore yielded a concentrate of 5.0 pct U3O8 from an ore containing 0.13 pct U3O8. with a recovery of 85 pct. This same ore gave a recovery of 93.5 pct when the grade of concentrate was reduced to 2.0 pct. It has been concluded that a successful method for floating autunite has been developed and that the mediocre results from the Midnight argillite ore are probably caused by the presence of some other uranium mineral or minerals less amenable to these reagents. The experimenters tested a third type of Washington ore, found on the Northwest Uranium Mines Inc. property on the Spokane Indian Reservation. This is a conglomerate of pebbles and small boulders of partially decomposed granite and is shot through with autunite. Its characteristics lie between those of the Midnight ore and the granite ore from the Spokane district. It responds better than the ore from Midnight but not as well as that from Mt. Spokane. As the fatty acids are the only type of collectors showing promise, investigation has been concerned with these acids and the optimum conditions for their use. The first method for treating the argillite ore from the Spokane Indian Reservation made use of Cyanamid's R-708 as a collector, a tall oil product described as a substitute for oleic acid. Although the investigators proved that R-708 is a collector for autunite when mixtures of autunite and silica sand are used, results on the ore were mediocre. Tests of other fatty acids revealed that the solid fatty acids of the saturated series are collectors for autunite and that their collecting power increases with the length of the carbon chain. The even carbon members of the whole series were tested from the 10 carbon acid (capric) to the 22 carbon acid (be-henic). The least expensive collector, stearic acid (18 carbon), proved to be a good one, so this was used in most of the tests. In first attempts with stearic acid, the collector was dissolved in various hydrocarbons and the solutions were added to the flotation cell. Cyclohexane, gasoline, fuel oil, kerosene, and other solvents were tried. Small amounts of high grade concentrates could be brought up, but recoveries were low. Finally emulsions of stearic acid were tried. It was discovered that stearic acid alone has little collecting power except when conditioning is carried out at high temperature. When hydrocarbon solvents were also present, it proved to be an excellent collector. An example of one emulsion that proved satisfactory for some ores is given as follows: 1 part stearic acid by weight, 1 part sodium oleate by weight, 1.2 parts kerosene by weight, 100 parts water. In some successful tests part of the stearic acid was replaced by oleic acid. The emulsions were made by agitating the stearic acid and sodium oleate together with hot water, then adding the kerosene and agitating while cooling. In the five tests reported in Table 1, 650 g of ore were ground with 650 cc water in a laboratory rod mill. The pulp was filtered to eliminate excess water and the ground ore transferred to a stainless steel beaker for conditioning at high pulp density. In most of the tests sodium hydroxide was added to the conditioner during agitation, then the collector emulsion, and finally the sodium silicate. The amount of alkali was adjusted to give a pH of 8.5 to 9.0 in the flotation cell. After conditioning the pulp was transferred to a laboratory flotation cell and the test completed in a normal manner. It is interesting to note that a deposit of high grade concentrate forms on the conditioning agitator and in the conditioning vessel, and at times on the agitator of the flotation cell itself. A few grams of concentrate running as high as 4 pct U3O8 were recovered from the conditioner when Midnight ore containing less than 0.2 pct U3O8 was treated. In the examples given in Table I this conditioner concentrate is calculated as part of the total concentrate. The authors have not yet fully explored the possi-

Jan 1, 1960

By T. A. Sullivan

Research undertaken by the Bureau of Mines in 1938 has resulted in the development of titanium from a laboratory curiosity to a commercial metal. Along with processes for producing the metal, it was necessary for the Bureau to develop methods for analyzing the metal, raw materials, and intermediate products. Some of the methods developed have been published.3 4 5/ General Services Administration (GSA) was responsible for purchasing titanium metal under Defense Production Act contracts with commercial producers. GSA designated the Federal Bureau of Mines to analyze this metal and establish its compliance with Government specifications. A substantial quantity of tin was found in some of the samples analyzed, and in July 1957 tin was added to the list of impurity elements to be determined. The specifications limited the amount of tin in titanium sponge to a maximum of 0.10 percent. A program was immediately initiated to investigate methods and techniques for determining tin in the range of 0 to 1.0 percent. A method accurate at the 0.10 percent level was necessary, as this level was the critical range for acceptance or rejection of the metal.

Jan 1, 1960

By J. W. H. Clare

An equilibrium isotherm at 550°C is given for ternary alloys rich in aluminum containing 0 to 15 wt pct Cr and 0 to 20 wt pct Mn. Phases encountered are: aluminum solid solution; stable temary compound G; and MnAl8,. In addition, a limited number of alloys were annealed at 450°C to check for differences from the 550°C isotherm. These experiments limited the composition of the G phase at 550°C and further experiments established that the G Dhase is not stable above 590 ± 1 °C. RAYNOR and Little1 established several equilibrium isotherms using aluminum-rich alloys containing up to 5 pct of the elements chromium and manganese. These isotherms showed that, in addition to an a solid solution and the two binary intermediate compounds 8 and MnAl6, a stable ternary compound ex-isted in the system. This phase was called the G phase because of its ghostly appearance in micro-sections. Little, Raynor, and Hume-Rothery2 found a similar phase in binary aluminum-manganese alloys and, as a result of their experiments, concluded that the G phase was a metastable phase existing in the aluminum-manganese system. This phase was stabilized by the addition of chromium. The constitutional work of Raynor and Little,' although showing the existence of the G phase in the aluminum-chromium-manganese system, did not establish precisely the composition limits of the phase or the temperature above which the phase became unstable and disappeared from the system. The work described in this paper was undertaken to provide this information. An examination of the previous work' showed that an isotherm at 550°C would provide the required data regarding composition in the shortest possible time, as the (a + G) phase field narrows considerably at higher temperatures. The same work showed that the G phase ceased to exist between 580° and 595°C. A more precise estimate of the transformation temperature would therefore be obtained by annealing selected alloys at successively higher temperatures beginning at 580°C. EXPERIMENTAL PROCEDURE 1) Materials Used—The experimental alloys were prepared from four master alloys containing 15.00 w pct Cr, 15.28 wt pct Cr, 19.80 wt pct Mn, and 19.38 wt pct Mn which were made from super-purity aluminum, electrolytic chromium, and electrolytic manganese. The aluminum was of 99.996 pct purity, the principal impurities being copper, iron, and silicon. The chromium and manganese were 99.9 pct pure, the principal impurities being antimony, calcium, and magnesium. 2) Preparation of the Experimental Alloys—The alloys were prepared in 20-g quantities by melting together the requisite amounts of master alloy and aluminum in an alumina-lined crucible and, after thorough stirring with an alumina rod, cast into a cold copper mold to give ingots 1/4 in. in diam and 3 in. in length.

Jan 1, 1960

By J. W. MacDonald

Two coal mine shafts recently completed in Franklin County, Ill., afford experience and accomplishment to warrant review, These shafts provide access to a tract with a potential recovery of one hundred million tons. This work provided the initial sinking by other than a contractor's organization since 1918. Four additional shafts required during the interim were sunk under contract arrangement with others. Supervisory contact and inspection afforded experience to govern planning and conduct of the recent work.

Jan 1, 1960

By S. R. B. Cooke, H. S. Choi, I. Iwasaki

Oleic acid is the chief ingredient of fatty acids used as collectors in nonsulfide flotation. With a few notable exceptions, the various quantities of saturated and other unsaturated acids comprising the remainder are usually unspecified. There have been occasional investigations to determine the collecting ability of these other acids and their effect on collection with oleic acid, but much remains to be done in this field. Hukki and Vartiainen, on the basis of tests using palmitic, oleic, and linoleic acids and an impure linolenic acid, concluded: "The collecting power of fatty acids used in flotation increases with increasing unsaturation of the hydrocarbon chain." ' Their work was concerned mainly with the response of ilmenite to the foregoing collectors, although tests were also made with magnetite, pyrite, hematite, and rutile. Cooke and Nummela, employing an almost identical technical procedure to evaluate flotation of hematite, magnetite, and goethite with various fatty acids, including oleic, linoleic, and linolenic acids of the highest purity obtainable, found: "The effectiveness of 18-carbon unsaturated fatty acids, as collectors for hematite, decreases with increase in the number of non-conjugated double bonds." 2 Vn the foregoing investigations, collector efficacy was measured on the basis of reagent addition in moles per liter. Sources of fatty acids which may be used as collectors are legion, but provided the oleic acid content is high enough, cost is normally the determining factor. Usually this restricts severely the purity of the collector in terms of its oleic acid content. Within the past year or so users of crude oleic acid have become somewhat more discriminating, apparently realizing that some of the organic acid impurities may exert deleterious effects upon certain separations. Marine fish oils have been used as collecting agents, particularly in the earlier days of froth flotation. Currently their use is restricted in this field to relatively minor applications, although they are cheap sources of fatty acids. In an effort to increase the range of uses for fish oils, the U. S. Fish and Wildlife Service has awarded contracts to study these materials as sources of new products suitable for commercial development. Funds for these investigations were provided by the Saltonstall-Ken-nedy Act of 1954. One such contract was awarded to the University of Minnesota School of Mines and Metallurgy for the purpose of investigating the use of fish oil fatty acids and their derivatives in ore flotation. Besides the esters of various saturated aliphatic acids and of palmitoleic and oleic acids, fish oil also contains esters of monoethenoid and polyethenoid acids with 20, 22, and 2 carbon atoms. The basic purpose of the investigation was to determine whether the longer-chained unsaturated acids possess collective properties superior to those of the C,, monoethenoid oleic acid, the C16 monoethenoid palmitoleic acid, or the saturated C,, stearic acid and its shorter chain homologues; whether highly unsaturated acids have merit as collectors; whether rela-

Jan 1, 1960

By E. Morrice

The metallurgical laboratory data developed in this study indicate an improved electrowinning process for producing higher purity cerium ingot. A typical sample of the Reno electrocerium contains 99.9 weight-percent cerium and the following impurities: Total other rare-earth elements, less than 0.04 percent; iron not detected; silicon and aluminum, less than 0.02 percent each; calcium plus magnesium, less than 0.01 percent; carbon, 0.01 percent; oxygen, 0.002 percent; hydrogen, 0.0003 percent; and nitrogen, 0.0015 percent.

Jan 1, 1960

By James L. McGregor

St. Joseph Lead Company has been paying incentive bonuses for well over 40 years. In 1958 almost half of St. Joe's 1,860 employees in Southeast Missouri received some form of incentive bonus in addition to their guaranteed wages. There are very few payroll jobs in St. Joe s Southeast Missouri organization that lend themselves to a reasonably good measurement of production or quality, or both, where an incentive bonus is not paid. The term "Incentive Bonus" is used to differentiate betwen bonuses that are based on quantity or quality of work, and those that are merely additional pay of a standard amount per hour or day because of an employee being temporarily assigned to some unusual task, An employee temporarily assigned to a job where the working conditions make the job performance unusually difficult or where a special skill is used is often given a bonus of some standard amount per hour or shift in addition to his usual rate. This is merely a convenient way of paying something extra without disturbing the normal rate structure. Actually, it is differential pay similar to that almost universally paid for evening and night shift work. Bonuses of that type are not being considered in this paper. The basic reason or theory for paying incentive bonuses 9s to get improved production at lower cost, Unfortunately, it is often difficult, if not impossible, to find a yardstick by which it can be definitely proved that a particular bonus plan is accomplishing its purpose, It becomes, then, a matter of judgment on the part of management personnel as to the value of the bonus plan. The fact that St. Joe Lead Company has continued to pay bonuses for over 40 yews and has increased the number of bonus schedules used attests to a definite belief that they are beneficial to the company's successful operations.

Jan 1, 1960

By A. Soundraraj, S. Singh, R. C. Deshpande

THE detonation of a high-explosive charge having a metal-lined conical cavity (shaped charge) results in a fast-moving jet and a slow-moving slug.1-4 Clark and Bruckner reported the metallographic studies of a cast-iron slug. The present note describes the metallographic studies of a copper slug and discusses the principle of flow involved. The shaped charge consisted of a 5-cm diam cylinder of cast high explosive (60-40 RDX-TNT mixture) having a 45 deg and 0.16-cm thick copper cone. The copper (99.5 pct purity) had a grain size of 0.06 to 0.08 mm diam and a hardness of 65 to 75 Hv. These were fired into a deep container of water and the slugs were recovered undamaged. The longitudinal and transverse sections of the slug were polished, etched, and examined for mi-crostructural changes. Macroexamination revealed a radial grain flow inwards towards the center and a downward component of flow towards the base of the slug. Fig. 1 shows schematically the micro-structural changes observed on the longitudinal section of the slug. The region D near the apex and also along the outer surface of the slug was characterized by the presence of heavily deformed and twinned grains. Some of the grains were having bent or crossed twins, Fig. 2. The grain size in this region was of the same order as that of the

Jan 1, 1960