By Larsen. Edward P.

The principle of "bed blending" in the agglomeration of materials is about 56 years old, but de- spite all education via technical papers, operating reports and results from functioning installations, the concepts of blending are still somewhat vague. Confusion exists between "mixing", "blending," and the basic role of each. The terms "blending" and mixing" are often used interchangeably, yet they describe two different processes. As properly understood and applied, a blend is a combination of different varieties of material which produces a desired quality, or the mingling of different elements to form a harmonious whole. In other words, blending is a process of combining granular materials by mechanical means, wherein the final product, or a portion thereof, must contain an exact proportional amount of every one of the several different materials which contributed to the mass and wherein all particles are so thoroughly intermingled with each other as to have lost their individual identities and become a part of the whole so that when a portion of the blend is taken at any time it will be substantially identical, chemically and physically, to any other portion taken throughout.

Jan 1, 1962

By John D. Bardill

Data from extensive tests was obtained on friction-head losses of various sand slurries, composed of materials of different specific gravities and under varying transport conditions, to provide useful information for designing hydraulic transport systems. The tests were run in a pilot plant through 2-, 3-, and 4-inch lines with slurries composed of relatively pure barite and limestone solids. Available grinding and classification equipment did not permit attaining a comparable size distribution in the two materials tested, thus preventing direct correlation of friction-head loss values to physical properties or mineral composition. A total of 495 measurements were made of limestone slurries in the 2-, 3-, and 4-inch pipe test sections at flow velocities from 6 to 14 feet per second and pulp densities from 40 to 70 percent solids. A total of 640 measurements of barite slurries were made in the 3-and 4-inch pipe test sections at flow velocities between 7 and 14 f.p.s. and pulp densities ranging from 40 to 80 percent solids.

Jan 1, 1962

By S. Y. Ogawa

The effects of sulfur (up to 0.1 pet) on the deformation and fracture characteristics of iron, in cast form, were studied at strain rates up to 100 pct pcr sec and at temperatures of 1600o to -3300 oF. The effects of oxygen and manganese additions on the behavior of Fe-S alloys were studied under comparable test conditions. Brittle fracture characteristics, evident at all strain rates, resulted from the presence of the liquid iron sulfide phase at grain boundaries. Ductility could be restored in three ways: solution of the sulfide in solid y iron at higher temperatures, spheroid-zzation of the liquid sulfide, and increase. in the melting point ot the sulfide. THE literature shows that most previous studies of deformation and fracture at hot working temperatures have been based on measurements of energy absorption, reduction of height in forging upset tests, torsion tests of bar or wire samples, and so forth,' but that relatively few tension tests have been used at high temperatures and strain rates. The present work was initiated to study the ef- fects of temperature, strain rate, composition, and structure on the deformation and fracture characteristics of iron, utilizing cast specimens tested in tension. As in a previous study,' strain rates up to 100 pct per sec were chosen for the temperature range 1600° to 2400° to provide data which might be useful in the interpretation of the deformation and fracture behavior of steels under hot working conditions. The previous work was with Fe-P solid solution al10ys;2 this work is concerned with Fe-S alloys, and with the effects of oxygen and manganese additions. MATERIALS AND PROCEDURE Cast tes! specimens were employed throughout, since most of the difficulty during hot working occurs in the initial breakdown of the ingot. Alloy Systems. Ten 25 lb. heats containing sulphur were prepared. Of these, three had manganese additions, and two had oxygen additions. The sulfur content varied from 0.023 to 0.10 pct. Manganese contents were intended to be ten to twenty times the sulfur content of the particular alloy. Oxygen, being more difficult to control in small melts, was varied by the amount of solid deoxidizer added, but poor control of the oxygen content was experienced in most instances. Table I shows the chemical analyses of the heats. Melting and Casting. Electrolytic-iron chips were melted by high frequency induction in a prefired, clay-graphite crucible lined with rammed magnesite.

Jan 1, 1962

Jan 1, 1962

By V. F. Swanson

As part of the Bureau of Mines titanium resources examination program, samples of altered rock (saprolite) and unaltered rock from the Roseland anorthosite near Roseland, Nelson County, Va., were tested for amenability to beneficiation by flotation. A flotation technique was developed to produce bulk concentrates of ilmenite, rutile, sphene, and leucoxene. It was necessary to first float apatite using oleic acid as the collector, in an alkaline pulp with dextrine as a titanium mineral depressant. The titanium minerals could then be floated from the apatite tailing, using fluosilicic acid to depress the remaining apatite, morin to depress ferromagnesian minerals (when present), and oleic acid as the collector. A bulk titanium mineral concentrate, analyzing 66.0 percent Ti02 and 0.08 percent P205, was obtained from a sample of the unaltered rock which contained 5.45 percent TiO2 and 2.81 percent P205. Overall recovery in the concentrate was 47.1 percent of the total TiO2 in the ore. About 55 to 65 percent of the saprolite sample was clay and was removed by attrition scrubbing and decantation. The apatite prefloat procedure was applied to the saprolite sands; subsequent titanium mine: 1 flotation recovered 72.2 percent of the Ti02 in a bulk concentrate containing 65.1 percent TiO2 and 0.20 percent P205.

Jan 1, 1962

By I. C. Edwards, D. C. Smith

THE milling plant of Bicroft Uranium Mines Limited at Ban-croft, Ontario, was one of the first in Canada to employ ion excl1ange for the selecti1•e recovery of uranium from acid leach liquors. The ion ex-change circuit started operating early in November, 1956, and by June 1 I959, had handled more than two million tons of pregnant solution containing I,830,000 pounds of U3Os. Each column had been saturated and eluted about 430 times. The ion exchange columns are the conventional fixed bed type. Uranium is eluted from the resin with a sodium chloride-sulphuric acid solution and is precipitated continuous-ly with magnesia. After filtering and drying, the precipitate, or "yellow cake," is packaged in drums for shipment to the refinery.

Jan 1, 1962

By S. A. Ronlov

The importance of recognizing vibration problems during the plant design stage is emphasized in this paper. Often an experienced designer can recommend what type of support to use and how to tune the structure. However, obtaining sufficient information is a serious problem dealing with vibration. Vibration is a well known phenomena which, simply and generally, can be defined as a periodic motion. It is experienced in nature as caused by eerth- quake, wind, or ocean waves, and must be dealt with in the design of structure or ships. It must be realized that wherever there are moving or rotating elements, it is possible that unbalanced forces may induce vibration in the elements themselves, in adjacent parts, or in the supporting structure. Under certain circumstances, vibration will destroy machines or structures quickly and totally. The most widely known case is the total collapse of the Tacoma bridge when subjected to a wind of only 42 mph. Failures due to vibration of machines and/or their supports may occur in industrial plants where heavy equipment employed in the process must be supported and several machines are combined in close proximity. In the Metallurgical and Chemical Div. of The

Jan 1, 1962

By R. A. Sullivan

I T IS one of the unwritten policies at Preston Mines that we examine closely any method or tool that will help us in our constant battle against rising costs. It is our personal conviction that most work methods can be improved. Therefore even though the job went well yesterday, it does not necessarily follow that it should be done by the same method today. With the arrival of the natural gas pipe line in the Porcupine area it was obvious that we would have to take a good look at the possibilities of using this source of fuel for plant heating. • Steam presently generated at Preston is for heating purposes only, no process steam being required. Prior to the fall of 1960, the heating plant consisted of two low pressure, coal-fired, fire-tube boilers, operating at an approximate pressure of 14 pounds per square inch. These boilers were underfed by stokers and could be operated either singly or together. ~o. 1 unit was a horizontal return tubular boiler, registered at 100 h.p. No. 2 unit was a fire-box boiler, registered at 75 h.p.

Jan 1, 1962

By Charles White Merrill, James W. Pennington

No metallurgical process developed in the 20th century compares with froth flotation in its effect on the mineral industry. Processes like gravity - concentration, amalgamation, and pyrometallurgical reduction are of ancient origin; others like cyanidation and electrolytic reduction were well established by 1900. Such metallurgical processes as heavy-media separation, ion-exchange, and solvent extraction belong to this century, but their influence is small compared with froth flotation. Data collected by the U. S. Bureau of Mines* in a canvass of 202 froth flotation plants reveal that, in 1960, 198- million tons of material was treated to recover 20-million tons of concentrates which contained approximately $1 billion in recoverable products. SIGNIFICANCE OF FLOTATION Froth flotation as described in this chapter refers to a wet process for separating properly ground mineral particles into two or more products. It involves the separation of mineral particles from each other in a liquid pulp by means of air bubbles. Finely crushed ore is agitated in water with the addition of air or other gases. Various chemicals and oils are added to cause the selected mineral particles to attach themselves to the air or gas bubbles. These bubbles, carrying the mineral particles, rise to the surface where they are removed in a froth, while the other particles remain suspended in the pulp. The earliest flotation divided the raw material into two products: a bulk concentrate that was removed as a froth and a tailing that remained in the flotation machine. The froth usually contained the valuable constituents. The successful application of such a process depended on the recovery of a single concentrate from which one or more valuable constituents could be recovered by a chemical or smelting process. With the advance of the art, however, the principle of selective flotation, by which two or more relatively pure products could be recovered from complex raw materials, was evolved. Other chapters in this volume describe the developments during the last 50

Jan 1, 1962

By Paul A. Beck, M. N. Parthasarathi

The vecrystallization texture. formed by selective growth of random nuclei in an 80 pct volled 99.997 pct A1 crystal of initial orientation mear (123) (41.21 was found to consist of components related to the single-component rolling texture by 40 deg. rota-tiows around [111]axes. The relative-volume fractiovz of the various recrystallization-texture componezts may be accouzted for 012 the basis of the Lou) mobility of twist boundaries, if it is assumed that the mobility of the tilt boundaries also varies with their orientation. Similar results with a, aluminum-alloy cystal of the (110) [112] orientation, containing iron, silicon, and zinc, show that these solute contents do not impair the effectivezess of the oriented growth mechanism of re cry s-tallization- texture formation. In a previous investigation1,2 it was found that a sharp recrystallization texture is formed as a result of the oriented growth of random artificial nuclei in an aluminum crystal rolled to 80 pct RA, on the (110) plane in the [ 112] direction. Four recrystallization-texture components were found to occur, with orientations corresponding to 40-deg rotations around [111 1 axes of the deformation texture. Reorientations of this type were already found in earlier work,3,4 where the presence of random nuclei could be reasonably assumed, but was not rigorously documented. The same orientation relationship was found also by Lucke and Liebmann, who actually measured the orientation dependence of boundary-migration rates in the recrystallization of A1 crystals slightly deformed in tension.5,6 The occurrence in the recrystallization texture of only four of the eight crystallographically equivalent orientations of the type referred to above remained unexplained,1,2 although it was clearly not a result of the absence of suitable nuclei. Recently Burgers7 suggested that this effect may be due to the aniso-tropy of boundary mobility observed2'6; it was found that the recrystallized grains of the 40-deg [111]-rotated type grow much faster in directions perpendicular to the [ 111] they have in common with the matrix than parallel to this direction, i.e., the tilt boundaries have much higher mobility than the twist boundaries. The four orientations corresponding to

Jan 1, 1962

By J. E. Pavlick, A. G. Guy

The total creep of tin alloys containing antimony in solid solution was observed to decrease with increase in antimony content. However, near the solubility limit an anomalous maximum in deformation was. found, in agreement with similiar observations by Bochvar. IT has long been recognized that alloys may deform more rapidly under stress if there is a tendency for a phase change or other structural change to occur simultaneously. However, the phenomena involved are complex and in some instances the opposite effect, strengthening, may result.' This area of research has not attracted much interest in the western world, and although Russian investigators have studied it for the past 15 years their work has not received due attention here. Recently diametrically opposing views on one aspect of this problem have been espoused by two Russian investigators, Kornilov and Bochvar. The question is this: in certain binary alloys tested in creep at the temperature where the solute is at the limit of solid solubility, does the incipient formation of the second phase strengthen or weaken the alloy? Korni-lov's arguments in favor of strengthening were presented at the 1954 Symposium at the National Physical Laboratory, =Creep and Fracture of Metals at High Temperatures.The most recent statement of Boch-var's theory of weakening is in Oding's new book on creep and rupture.3 Although Bochvar agrees that strengthening occurs in some alloy systems, he argues that in certain alloys an anomalous weakening is observed. However, the extensive work of Korni-lov's group on creep properties of alloy systems has not revealed any anomaly of this type, but instead has tended to refute Bochvar's theory. This clear-cut controversy offered a good opportunity for a simple experiment to resolve the problem. The experiment and its results supporting Bochvar are the subject of this paper. However, it will be helpful first to sketch the present status of the larger question of the effect of a phase change or other structural change on plastic deformation. PREVIOUS WORK One of the first researches in this area was by Pfei1,37 who investigated the creep resistance of an 80 Ni-20 Cr alloy containing varying amounts of titanium. He found that the resistance to creep increased rapidly as the solid solubility limit in the alloy at 775'c was approached and slightly exceeded. With further addition of titanium the creep resistance decreased, presumably because of precipitation effects. Bochvar's first work in this field was a study in 1945 of "superplasticity" in zinc alloys containing 15 to 25 pct Al.4 He found that alloys quenched from about 400 had anomalously low hardness when tested below this temperature. The following year, in a paper on the dependence of mechanical properties on the composition and structure of alloys,5 he extended some observations of Kurnakov to predict that at high temperatures of testing the hardness values for solid-solution alloys might be lower than those for the component metals. He also pointed out the influence of changes in solidus temperature in affecting curves of hardness vs composition, and he

Jan 1, 1962

By H. D. Mellom

The direction of the optic or "C" axis of a uniaxial metal crystal can be found with the metallurgical polarizing microscope by examining two planes of section on the crystal. Complete orientation of the crystal can be determined if a twin crystal is common to both surfaces of section. Examination of Uniaxial Metals in Polarized Light-Rotation of a uniaxial crystal surface, properly prepared,' shows four extinction positions 90 deg apart, provided that the surface is not close to a basal section. One of these two extinction directions corresponds with the projection of the optic axis on the surface of section. This direction can be found if the 'sign of the rotationr2 for the metal is known. To find the direction of the optic axis, the crystal is rotated on the stage 45 deg from an extinction position. With a crystal of negative sign, to produce extinction the analyser must be rotated towards the optic axial direction and vice versa. All sections, other than basal, of a uniaxial crystal have the same sign of rotation and, since there is no change in sign with wave length, white light can be used for these measurements. U the sign of the rotation is not known the presumed direction of the optic axis can be determined assuming a positive sign. A third section cut normal to the presumed optic axis will show basal extinction if the assumption is correct. It is convenient to use the edge between the two planes of section as a fiducial direction common to both surfaces. The optic axis can be related to this direction. If the above measurements are repeated on the other plane of section and the angle between the two section planes measured, stereographic projection can be used to determine the orientation of the crystal optic axis. Determination of Complete Orientation—The complete orientation of a uniaxial crystal can be determined provided that a twin crystal is common to both surfaces of section, and the twin law is known. The orientation of the twin crystal optic axis can be determined in the same way as for the main crystal

Jan 1, 1962

By Franklin J. Hill, Theodore D. Tiemann

Sized fractions of Wisconsin Gogebic taconite were reduced with hydrogen over the temperature range from 600° to 1000°C. In general, the degree and rate of reduction increase with temperature. Particle size has no observable effect except in the smaller fractions at 900°C and above, where reduction is impeded, possibly due to the siliceous nature of the ore. Gaseous diffusion appears to be significant as a rate controlling factor at certain stages. THE depletion of high grade iron ore reserves in the United States has established the need to utilize all available iron ore deposits, both in long range planning and from the viewpoint of national emergency. This has led to extensive research and development in this field. The beneficiation of Wisconsin Gogebic taconite ore has been previously studied by investigators at the University of Wiscconsin, 1 the United States Bureau of Mines,, Battelle Memorial Institute, 3 and others. Methods investigated have included concentration by flotation processes, magnetic and gravity separation, magnetic roasting and various combinations of them. The foregoing studies have been concerned with the production of an enriched ore suitable for blast furnace use. If the ore could first be reduced to metallic iron and then beneficiated, the product could be used directly in the open hearth or electric steel-making furnace. The by-passing of the blast furnace should enhance the economic feasibility of the beneficiating process. The work reported here,4 was undertaken to establish data on the hydrogen reduction of Wisconsin taconite that would eventually lead to the development of an economic direct reduction process for this and perhaps other low grade siliceous ores. The volume of work on direct reduction can be judged by the fact that 240 direct reduction processes were patented in the United States alone up to 1951, 5 and numerous additional processes have since been developed. Some of the factors contributing to direct reduction development are: 1) The increasing capital cost of the blast furnace and its accessory equipment. 2) The decreasing availability of high grade domestic ore. 3) The high cost of steel scrap for use in the open hearth and electric furnaces. In general, direct reduction processes can be divided into two types; those using a solid reductant (coal, peat, lignite) usually carried out in a kiln, and those using a gaseous reductant (H2, CO) in a shaft furnace or a fluidized bed retort. As there is no low cost coal readily available in northern Wisconsin but natural gas could be quite easily obtained, it is believed a gaseous reductant process would offer the greater feasibility for use on Wisconsin taconite. It is hoped that this preliminary work will beof interest to other investigators in this increasingly important field. TACONITE ORE The ore used in the investigation was obtained originally from the U. S. Bureau of Mines, and consisted of a representative composite made up from trench samples of the Norrie, Pabst, Plymouth, Pence, and Yale members of the Wisconsin Gogebic range iron formation. Chemically, the ore contains approximately 52 pct SiO, and 30 pct Fe. X-ray diffraction and other studies indicate the principal minerals to be quartz (SiO2), hematite (Fe2O3), and goethite (Fe2O3. H2O). Minor amounts of iron containing silicates, siderite (FecO3), and magnetite (FeO-Fe2O3) are present. The iron minerals and quartz are so finely disseminated that the ore requires grinding to less than 200 mesh (74 µ) for essential liberation.l,2 The iron content of each of the several size fractions studied is shown in Table I. EXPERIMENTAL METHOD The method used throughout the investigation was based on that developed by the U. S. Bureau of Mines in Minneaopolis6,7 in which the course of reduction is followed by the loss in weight of the ore sample. More specifically, a 100-g sample of the size frac-

Jan 1, 1962

By H. W. Meyer, H. N. Lander, F. D. Delve

A method of calculating the changes in blast-furnace performance brought about by burden and/or blast modifications is presented. Essentially the method consists of three simultaneous equutions derived from materials and heat balances. These equations can be used not only to evaluate quantitatively the effect of changes in process operating variables on furnace performance, but also to provide a useful means of evaluating changes in process variables which cannot be measured directly. It has been customary for a number of years to use simple heat and materials balances as a basis for assessing blast-furnace practice. A good example of the method used to set up these balances is that proposed by Joseph and Neustatter.1 This approach to process assessment has limited utility, however, in that it cannot be used to predict the furnace coke rate or production under new operating conditions. Using an approach based on multiple correlation of blast-furnace variables, R V. Flint2 has developed an equation which may be used to predict the change in coke rate that will result from some changes in operating conditions with a reasonable degree of accuracy. Although this equation has useful applications in production planning, it cannot be used to study the relationships between the operating variables and the fundamental thermochemi-cal characteristics of the process. In attempting to analyze the blast-furnace process quantitatively, the idea of dividing the furnace into zones3 may at first appear attractive. In our present state of knowledge, however, it is not possible to define with any accuracy the physical limits of such zones in relationship to their temperatures or to the reactions which may occur in them. Although its application is restricted, the zonal approach to blast-furnace analysis is useful in some instances. For example, the change in the calculated flame temperature in the "combustion zone" caused by injecting steam constitutes information which is helpful in understanding why the addition of steam to the blast is best accompanied by an increase in blast temperature. The zonal approach cannot, at the present time, be used to establish the relationships between process variables and process performance if the whole process rather than part of it is to be considered. One of the earliest approaches to the problem of relating blast-furnace operating variables to pro- duction and coke rate was that developed by Marshall.4 Essentially Marshall's work showed that it was possible to estimate the performance of a furnace by solving three simultaneous equations which consisted of rudimentary carbon and heat balances plus a further equation relating the production, wind rate, and the carbon burned at the tuyeres. Although these equations did not include all of the chemical and thermal variables of the process, their derivation and application seems to be the earliest attempt which achieved any success in relating prior furnace operating data to the calculation of furnace performance under different blast conditions. Work carried out in Germany has been directed mainly towards prediction of coke rates using material and thermal balances rather than statistical methods. wesemann5 used prior furnace operating data as part of the basis for predicting the change in coke rate accompanying a change in burden composition. This author employed a method of successive approximations to estimate the secondary changes in slag volume and stone rate brought about by the change in coke rate. The most recent analysis, which seems to have been developed concurrently with the thermochemical model presented in this paper, has been described by Georgen.6 This author has succeeded in improving on Wesemann's approach by expressing the total changes in the slag volume and stone rate in terms of the change in coke rate itself. This is accomplished in a manner similar to that used in the thermochemical model described in this paper. Although Georgen makes use of a calculated furnace heat loss, he does not relate the heat loss per unit of hot metal to the production rate as is done in the present work. Georgen's approach may be used to calculate the changes in materials requirements accompanying changes in furnace operation; it cannot be used to assess the resulting changes in production. The fact that blast-furnace behavior can be interpreted by consideration of the heat requirements of the process was demonstrated by Dancy, Sadler, and Lander.7 In the analysis of blast-furnace operation with oxygen and steam injection these authors showed that it was possible to account for the changes in production and coke rate

Jan 1, 1962

By Hsun Hu

The formation of annealing textures in high-purity silver, from the various rolling textures obtanled in the course of texture transition, was studied. It was found that from a brass-type rolling texture the recrystallization texture is mainly (120) [211] type, which is quite different from the recrystallization texture of brass. From a predominantly copper-type rolling texture, the reclystallization texture is mainly (100) [001]. The recrystallization texture of silver- varies also with the degree of purity. In each case, however, the reorientation can be expressed as [Ill] rotations of 30° to 40°, which is consistent with the oriented growth theory of the formation of annealing textures. ThE recrystallization textures of rolled silver were studied long ago by Glocker and co-workers (1924-27) and were reported to be (113) [iil] upon annealing at low temperatures.1 Since that time, no further study of the recrystallization textures of silver, particularly with the modern techniques of quantitative texture determinations, has been reported in the literature. In a previous study2y3 it was found that the rolling texture of high-purity silver (99.999 +pct pure) is changed gradually from the common silver- or brass-type to the copper-type by raising the temperature of rolling from 0" to 200°C. The formation of annealing textures from the various rolling textures in the same material is, therefore, of considerable interest. The present paper constitutes the results of such a study. MATERIAL AND METHOD Specimens were taken from the same strips of high-purity silver* that were used previously for

Jan 1, 1962

By J. R. Lucas, H. E. Rutherford

The primary objective of this research was to evaluate the feasibility of ultrasonic testing for the purpose of analyzing the structure and properties of rock material. A secondary objective of this study was to determine experimentally the elastic wnstants of various rock specimens with the use of ultrasonic equipment. Elastic constants can definitely be determined quickly and accurately by ultrasonic investigation. With proper equipment there are indications that ultrasonic waves could be utilized in the detection of flaws, such as fractures and planes of weakness, measurement of thickness, and the study of structure of rock material. Ultrasonic principles have been applied in many industries for the purpose of determining the structural characteristics of various materials. The principal applications of interest here are detecting flaws, measuring thicknesses, and determining elastic constants. The main advantage of ultrasonic analysis is that it is nondestructive. It also has extreme sensitivity, high penetrability, good accuracy, rapid response, and the necessity to have access to only one side of the specimen. These various applications and advantages lead one to think that ultrasonic principles might be applied to rock material in situ for purposes of analyzing its structural characteristics. Therefore, the primary objective of this research was to evaluate the feasibility of ultrasonic testing for the purpose of analyzing the structure and properties of rock material. A secondary objective of this research was to determine experimentally the elastic constants of various rock specimens with the use of ultrasonic equipment. The term ultrasonics is given to that branch of acoustics dealing with periodic sounds whose fre- quencies are above the audible range or above approximately 15,.000 to 20,000 cps. The first practical production of this high frequency sound was made possible after World War I due to developments of electronically controlled sound wave sources. At the present, the maximum practically attainable ultrasonic frequency is approximately 1000 megacycles per sec. Sound waves of sufficiently high frequency can be made to travel in a beam with little spreading. Therefore, such a beam can explore a material and detect nonhomogeneities in it by reflection. This is the principle of the ultrasonic reflectoscope invented by F. A. Firestone' in 1942. An ultrasonic beam, on pulse-penetratink a solid material medium, produces an echo when it strikes a flaw which has different acoustical properties than the surrounding medium. This echo can be detected by the same transducer which sends out the original pulse. This principle is the basis of the important industrial techniques of nondestructive ultrasonic testing of metals and other solid material. Later developments in the field of ultrasonic testing of solid material have been mostly improvements in equipment and instrumentation. To date, most of the industrial applications of ultrasonic analysis of solid bodies have been in the aircraft, electrical, and nuclear energy fields on the nondestructive testing of metal. The one solid material similar somewhat to rock material, upon which some work has been done to apply ultrasonic testing techniques to study structural integrity, is concrete. Jones and Gatfield3 briefly summarize this work on concrete. Their basic conclusion was that the strength of concrete was a function of the change of the longitudinal sound wave velocity in the concrete. Only recently has any extensive study been made to apply ultrasonic testing techniques to rock material. Lutsch studied rock material by an ultrasonic pulse method to determine the extent and degree of fracture of rock faces. Lutsch states that the number of observed reflections is a measure of the degree of fracture and that only ultrasonic waves are able to detect fractured zones subjected to high pressure. Suzuki, Sasaki, and Siohara5 studied the characteristics of the sonic wave in rock for propagation over a wide range of wave lengths. They indicated that, in rock, the propagation constant and attenuation of the

Jan 1, 1962

By Pierre R. Hines

The first progress in American ore dressing practice was made in the mills of the Mother Lode in Calif., the Comstock Lode in Nev., and Gilpin County in Colo., during the years 1861 to 1870, when the ancient wooden stamp battery, with square wooden stems, was converted into the 'California' stamp made of wrought and cast iron, with round stems which rotated. Eli Whitney Blake invented the jaw crusher in 1858 for stone crushing, and it was soon used for crushing ore. F. W. Gates' gyratory crusher followed twenty years later. S. R. Krom, Thomas A. Edison, and others improved the Cornish rolls by increasing their size and spring pressures; the Symons Brothers made horizontal and vertical disc crushers; W. Ball and E. T. Leavitt designed powerful steam stamps for Lake Superior native copper ores; and jigs were mechanized. William B. Frue, a mill superintendent in the Lake Superior copper district, invented the vanner in 1874. Arthur F. Wilfley built his riffled concentrating table in 1895, just after Dr. Robert H. Richards commenced his Ore Dressing. The Wilfley table so changed concentrator flow sheets that Dr. Richards was compelled to revise his text, and its publication was delayed until 1903. The value of sizing or classifying before concentration was recognized. Dr. Richards had persuaded the Anaconda Copper Mining Co. to install round tables with special surfaces to catch the 'extremely fine free mineral.'l Gravity concentration had achieved almost every refinement for recovering or separating minerals by the difference in their specific gravities. However, one serious problem remained unsolved, i.e., how to retrieve the enormous loss of the extremely fine mineral in the slime portion of the ore. Slime, then, as now, was not a precise term due to the variation in the mineral composition of the ores and the different requirements in crushing, grinding, sizing, and classifying. At that time, slime was considered to be fine sand and colloidal material passing 100 mesh.2 Most sulfide ore minerals are more friable than their associated gangue minerals, so that crushing and grinding increased the proportion of the extremely fine ore minerals in the slime. Sparkling specks of galena, chalcopyrite, argentite, or ruby silvers, according to the ore, floating away on the tailing stream from vanners and slime tables, were familiar sights in the old gravity concentrators. Gravity concentration practice was aimed at recovering the ore minerals at the coarsest possible size because the recovery was higher and unnecessary

Jan 1, 1962

By J. M. Dahl, R. J. Warrick, O. K. Riegger, H. Van Vlack

A liquid which is rich in oxygen (and silicon) develops at steel rolling temperatures in resulfurized and plain-carbon steels. This liquid fluxes solid manganese sulfide. The composition of the liquid and the resulting microstructures vary with the manganese/silicon/oxygen ratios in the steel. The observations and conclusions zuhich are presented are used 1) to suggest a mechanism for MnS deformation in resulfurized steels, and 2) to rationulize hot-shortness anomalies between plain-carbon and resulfurized steels. 1 HIS is a summary of the dependence of sulfide inclusion microstructures upon steel composition, and an interpretation of the behavior of sulfide inclusions at steel-rolling temperatures. Sulfide inclusions are known to have several metallurgical effects upon steel. Their effects upon hot-shortness are best appreciated. Although hot-shortness is well known, it is questionable whether its mechanism is fully understood because there are several anomalies in our interpretation. For example, why should not high sulfur contents produce extensive hot-shortness in free-machining steels ? A second metallurgical consequence of sulfide inclusions appears because sulfide inclusions improve machinability. Furthermore, globular inclu- sions are to be desired over elongated inclusions. To date, we know that lower silicon contents (< 0.010 pct) favor the globular sulfides, but we do not know why this interrelationship between silicon content and inclusion shape exists. Finally, the evidence is strong that the surface quality of a hot-rolled steel is particularly sensitive to the sulfur content. SUMMARY OF PREVIOUS WORK The role of sulfur in hot-shortness was first suggested during the past century. It is uncertain who was the first to conclude that sulfur was less deleterious in the presence of manganese, and that manganese altered the sulfide phase from a liquid FeS to a solid MnS at steel-rolling temperatures. However, Urban and chipman&apos; emphasized that liquid FeS may accumulate as an interdendritic film during solidification. More recently, Keh and Van lack&apos; showed that the intergranular liquid does not completely surround the metal grains at all rolling temperatures. Rather, a small finite dihedral angle exists when geometric equilibration is attained at

Jan 1, 1962

By A. J. Jacobs, G. Katz

MANY of the studies of intermetallic compounds containing uranium were performed during the early 1940&apos;s under the aegis of the Manhattan Project. Subsequently, much of this work was declassified and published after 1949. In some instances this early work, completed with relatively impure materials, represents the only source of X-ray diffraction powder data available in the literature. In the case of the intermetallic compound U,Fe some discrepancies in the powder pattern exist in the literature. Since this compound has been prepared in this laboratory, it is believed that the publication of the indexed powder pattern would help clarify the conflict in the literature. In studies of the U-Fe system, Gordon and Kauf-mannl and Grogan and Clews2 independently reported the intermetallic compound U,Fe in 1950. The crystal structure was described by Baenziger, Rundle, Snow, and Wilson3 in 1950. It is isostructural with U,Mn, U,Ni, and U,Co and crystallizes in a body-centered tetragonal lattice. The lattice constants determined by Baenziger et al. are: giving an X-ray density = 17.7 g cm-3 for 4 mol per unit cell. The compound used in this study was prepared by melting a stoichiometric mixture of the constituent metals in an argon-arc furnace using a nonconsum-mable tungsten electrode. Before the argon of 99.98 pct purity was introduced into the furnace, it was passed through CaC1, to remove water vapor and afterwards through a stainless steel tube containing calcium turnings heated at 600°C for the removal of nitrogen and oxygen. The purity of the uranium used was better than 99.9 pct and that of the iron was 99.97 pct. Before and during melting a zirconium getter was used to further purify the argon atmos-

Jan 1, 1962

By A. L. Mular

lnput energy-size modulus relation at small reduc-tion ratios is expressed by Et = (M, -Mt) k;. In some cases 13 is close to Schuhmann&apos;s distribution modulus a in value. Experimental results in conjunc-tion with the equation demonstrate the fact that energy input which produced fracture is not expended on unbroken starting material inside the mill at any time. Recently, schuhmann1 derived the Charles equation2 using the postulate that complex com-minution operations can be considered as a summa- tion of many comminution events. The fragments resulting from each event are assumed to follow the Gaudin-Schuhmamn distribution. In his derivation, Schuhmann implies that the size distribution of the total mass of a material is determined by the fraction of that mass actually subjected to comminution. Consider a feed to contain a volume, Vo, of uni- formly sized homogeneous material. After t seconds of grinding, let the volume of broken material be Vo - Vt where Vt is the volume of starting material not yet broken. The size distribution of the broken material is given by: where V is the cumulative volume less than size X, and k, is the size modulus of the broken material at time t. The distribution for the total volume at this

Jan 1, 1962