By J. N. Ong

The oxidation of tantalum is assumed to occur by four simultaneous first-order chain reactions; solution of oxygen in the metal, nucleation and growth of a suboxide phase at the metal surface and two phase boundary processes which give rise to two different modifications of Ta2O5. A rate equation is then formulated which accounts for all principal details of oxidation behavior, unifies and correlatss the results of the principal investigations, and expresses the rate as a function of pressure, temperature, and time. For purposes of practical application, the expressions: may be used below and above 700T respectively to determine the regression rate of tantalum in cm per hr, where T is to be expressed in "K and P in atmospheres pressure of oxygm. The equations will reproduce within a factor of two all reported experimental rates in the temperature range 475" to 1400°C and pressure range 0.000026 to 40.8 atm 0. 1 HE oxidation kinetics of tantalum have been investigated thoroughly in the temperature range 50" to 1400 and pressure range 1.32 x l0-' to 40.8 atm pressure of 0,and as a result, the principal features of the oxidation of tantalum are known and have been described in considerable detail. The exposition of the characteristics of the behavior of tantalum in oxygen has been largely descriptive, with considerable attention being devoted to elucidating the structure, composition, and morphology of the resulting oxide products. The weight change vs time results have usually been reported graphically. With the exception of the linear rate below 700 C and the process of diffusion of interstitial oxygen into the metal,6'9 no effort has been made to characterize the reaction rates in functional form. It is the purpose of this paper to demonstrate that when the fundamental principles of chemical kinetics are rigorously followed, the results of the principal investigations will be correlated and unified and the oxidation rale may be expressed as an analytic function of pressure, temperature, and time. In addition to accounting for the temperature and pressure dependency of the oxidation rate, the following minor features will be accounted for as a result of the basic analysis: the initial period of nonline-arity in rate at low temperatures, which decreases with increasing temperature;3'5'7 the rate vs temperature cusps obtained at constant pressure"5 the concentration gradient of oxygen interstitially dissolved in the metal.5'7 The analysis will also be consistent with the overall chemistry of reaction and with all visual, microscopic, and X-ray observations. DEVELOPMENT OF RATE EQUATION As a fundamental basis for the treatment of metal-oxygen reaction kinetics, it will be regarded that the rate of reaction is determined by the concentration and not the activity or chemical potential. It is further assumed that all metal-oxygen reactions are first order complex chain reactions" whose rate is dependent on the concentration of an intermediate species which is a complex function of the oxygen concentration, or oxygen pressure, only. The basic rate equation is therefore: is the weight of oxygen consumed by the reaction, A is that portion of the area of the metal over which the reaction is occurring (cm2), t the time (sec), kf the rate constant for forward reaction, C the intermediate species concentration and f '([Oz]) and f (Po,) are complex functions of oxygen concentration and Oxygen pressure respectively. Reverse reactions may usually be neglected in metal-oxygen systems since a large negative free energy generally accompanies these reactions. Eq. [I] takes different forms when the rate of reaction is controlled by diffusion into or through a phase or at a phase boundary. For diffusion into the metal phase, the rate is given by1' Di is the diffusion coefficient of species diffusing into the metal phase (cm2/sec), and Q is the corre-

Jan 1, 1962

By R. B. G. Yeo

Pronounced isothermal martensite formation at room temperature was measured dilatometrically in a steel containing 0.01 pct C, 24.9 pct Ni, 0.26 pctAl, 2.58 pct Ti and 0.25 pct Cb. It is shown that martensite will form isothermally if stabilization of the austenite-martensite transformation is eliminated by removal of carbon. The decarburization of two iron-nickel alloys allows isothermal transformation to martensite to occur at temperatures above their athermal Ms temperatures. In an Fe-22.4 pct Ni alloy, at the 0.008 pct C level, the Ms temperature during air cooling is 85°F higher than that during- water quenching-. At the 0.15 pct C level this difference is reduced to only 5°F. The introduction of carbon causes stabilization during air cooling which lowers the Ms temperature virtually to the same level as determined during mate?. quenching. Thus in the 0.15 pct C alloy, the Ms temperature is almost independent of cooling rate. It is suggested that rival theories of martensite formation should be reexamined in alloys of sufficiently low carbon and nitrogen content to eliminate the complication of stabilization. The Ms temperature of a steel containing 0.01 pct C, 24.9 pct Ni, 0.26 pct Al, 1.58 pct Ti and 0.15 pct Cb, solution treated at 1500°F and air cooled as 1/8-in. diam specimens, was found to be 57 °F. 1 However, when held for several hours at room temperature the steel hardened slightly and became appreciably ferromagnetic. Isothermal transformation to martensite was first revealed by Kurdjumov and Maksimova2 in an iron-base alloy containing 0.6 pct C, 6.0 pct Mn and 2 pct Cu. Most of the other studies of isothermal martensite have also been confined to highly alloyed steels which transform at subzero temperatures; for instance, DasGupta and Lement, 3 Cech and Hollomon, 4 Machlin and Cohen,5 Shih, Averbach, and Cohen.6 Averbach and cohen7 noted a rapidly decaying volume increase at room temperature in a steel containing 1 pct C, 1.5 pct Cr and 0.2 pct V. cina8 and Marshall, Perry, and Harpster9 have described the isothermal transformation to martensite at room and subzero temperature in stainless steels. Kurdjumov10 has recently reviewed the subject, noting that the isothermal formation of martensite can be observed only in the temperature range somewhat below Ms or below -50°C. The isothermal formation of martensite may be characterized as follows: 1) It occurs in steels of widely different compositions, the main prerequisite being a low transformation temperature. 2) The transformation occurs by the formation of new plates and not by the growth of old ones. 3) The isothermal transformation is suppresed by stabilization during slow cooling or holding at temperatures near room temperature. However, the factors governing this mode of transformation are still not fully understood. The formation of martensite isothermally suggests an activated process. The early theories of martensite formation did, in fact, utilize classical nucleation concepts. Kurdjumov 11 first proposed the presence of thermally activated nuclei of different sizes and compositions which would grow if they reached critical size during cooling. This treatment was enlarged and developed quantitatively by Fisher, Holloman, and Turnbull12,13 and was later reviewed by the latter two authors.14 Fisher15 associates Ms with a nucleation rate of one per cc per sec. At slightly higher temperatures the nucleation rate is so low that isothermal formation of martensite is not observed in reasonable times. At slightly lower temperatures the nucleation rate is so high that it could not be suppressed by rapid cooling. By judicious use of parameters Fisher 16 was able to obtain good agreement between classical nucleation theory and the incubation times of martensite formation.4 However the application of these principles to martensite formation in iron-nickel alloys15 predicts that an alloy containing about 30 pct (31 at. pet) Ni would not transform. The presence of an Ms temperature at -223° C in an alloy containing 34.1 pct (33 at. pct) Ni led Kaufman and cohen17 to reject the hypothesis of homogeneous nucleation in favor of the reaction path theory originally proposed by Cohen, Machlin and Paranjpe.18 This theory conveniently explains the formation of martensite athermally but becomes labored when dealing with isothermal formation. Kaufman and cohen19 did explain the isothermal activation of embryos by assuming it to be a result of the expansion of their boundary dislocation loops but this treatment predicts an upper temperature limit of isothermal martensite formation.

Jan 1, 1962

By D. J. Stoops

The object of the research described in this paper was to investigate the effect of metallurgical and surface treatments on the corrosion behavior of arc-melted reactor-grade zirconium in cupric or ferric chloride solutions. An apparatus was constructed and specimens of various metallurgical conditions and surface treatments were tested for 6 days at 35° C., with aeration. Some correlations were observed between corrosion rate and the metal's condition and treatment, Specifically, the unattacked or least attacked specimens were those that had been etched as a final treatment before testing. The most severely attacked specimens were those that had been vacuum-annealed as a final treatment before testing. The moderately attacked specimens were those neither vacuum-annealed nor etched, but having a final surface treatment which left a cold-worked surface. Attack by cupric and ferric chloride was by pit- ting with no preference for grain boundaries, The corrosion scale was cow posed predominately of very fine zirconim particles, Particles from the FeC1,-corroded specimens were more pyrophoric than those from CuCl2-corroded specimens, and appeared to have a higher surface area to volume ratio. Comparison of results to those of previous investigators showed that at certain salt concentrations the more pure, reactor-grade zirconium was quite resistant to attack while the less pure, graphite-melted zirconium was severely attacked.

Jan 1, 1962

By T. R. Cass, M. R. Achter

A technique for measuring the creep and rupture strength of nickel specimens bonded by sintered oxide layers has been developed for the investigation of the role of grain-boundary oxide in the oxidation strengthening of nickel during creep at 817 °C. Prom the inverse dependence of the rate of bonding on the thickness of the starting oxide, it is suggested that the rate of diffusion of Ni++ through NiO is the controlling process at the start of sintering. Cornparisons of the creep and rupture strength and of the microstructure of sintered couples with conventionul creep specimens suggest rupture in nickel is prevented by load-bearikzg, ikltergranular layers of oxide. A number of recent investigations have shown that at high temperature and low stress the creep-rupture strength of nickel and nickel-base alloys may be much greater in air than in an inert gas or vacuum.'-7 For example, at 817°C and 2500 psi, nickep failed in vacuum in 48 hr but not in air after 4000 hr, and a Ni-Cr-A1 alloy5 at 1038°C and 3000 psi failed in vacuum in 4 hr but not in air after 731 hr. Fig. 1 is a typical creep curve in air for materials experiencing this pronounced environmental strengthening. A common feature of these curves is the entry into a third stage of accelerating creep, concurrent with the for-

Jan 1, 1962

By M. Kaufman, A. E. Palty

The phase structure and aging characteristics of two nickel-base alloys, Inconel 718 and 702, were investigated. Wrought and cast Inconel 718 showed ArisCb as the major hardening phase, as well as ture was positively identified. Inconel 702 had Ni3Al as the major hardening phase, as well as Cr7C3-of the phase amounts with temperature was determined. 1 HE value of phase structure and aging rate information in the utilization of alloys has been well established. As part of a continuing program, the results obtained on two nickel-base alloys, hconel 718 and Inconel 702, are presented here. Inconel 718 is a relatively new alloy considered for application in both sheet and cast form. Its novelty lies in the use of high columbium tantalum levels in a Ni-Cr-Fe base. No previous work on this type of alloy has been reported in the literature. Inconel 702 is being used now as an oxidation-resistant sheet alloy. Occasional fabrication problems spurred work on its basic structural behavior. The composition of 702 is essentially nichrome plus aluminum and titanium for strengthening and added oxidation resistance. This puts it in the basic class of other nickel-base alloys which have already been studied. The two alloys will be treated separately. INCONEL 718 Phase Study Methods. The phases present after the various conditions investigated were determined by X-ray diffraction analysis of two different elec-trolytically extracted residues and microscopic examination. The extraction methods, using 10 pct HC1 in alcohol and 10 pct H3PO, in water and the X-ray technique have been described previously.' The effect of temperature on the phase behavior was studied on sheet material using the following heat treatments: 2250°F, 2 hr, ice brine quench 1300 100 hr, water quench 2250°F, 2 hr, ice brine quench 1400°, 100 hr, water quench 2250°F, 2 hr, ice brine quench 1500°F, 100 hr, water quench 2250o 2 hr, ice brine quench 1700°F, 48 hr, water quench 2250°F, 2 hr, ice brine quench 1850°, 24 hr, water quench 2250°, 2 hr, ice brine quench 2000°F, 6 hr, water quench The high solution temperature was an attempt to dissolve as many phases as possible without causing melting. Aging exposures were made longer than normal heat treating times in order to approach equilibrium conditions more closely. Cast material was examined only in the as-cast condition and with the normal heat treatment (1700°F, 1 hr, air cool 1325oF, 16 hr,air cool). Materials. The full phase study was performed on sheet specimens approximately 1/2 in. by 2 in. by 1/16 in. The cast pieces were cut from the gating system of a vacuum-cast test piece. An all weld-metal specimen was made by running many weld beads on the sheet using filler made from the sheared edges of the sheet. All external contamination was removed by belt-sanding followed by an electro-polishing treatment. The typical composition of wrought Inco 718 is as follows: The alloy is air-melted. Cast hco 718 may have higher molybdenum. Due to the expectation of finding a Ni-Cb phase (Ni, Cb) for which no X-ray diffraction pattern was available in the ASTM Index, a special 5 Ib heat to the stoichiometric composition of this intermetallic

Jan 1, 1962

By A. H. Daane, B. J. Beaudry

The Sc-Ti system was studied by thermal, metal-lographic, and X-ray methods. Scandium was found to transform at 1334 °C from a (hexagonal) to ß which was concluded to be bee since a continuous series of solid solutions is formed between ß scandium and ß titanium at elevated temperatures. There is a minimum in the solidus at 51 wt pet Ti and 1300°C, a monotectoid at 1050°C and 49 wt pet Ti, and a eutectoid at 875°C and 91.5 wt pet Ti. The maximum solubility of titanium in a scandium is 13.5 wt pet at the monotectoid temperature, while the maximum solubility of scandium in a titanium is 6.5 wt pet at 875°C. SCANDIUM, a member of Group 111 A of the periodic table, and now called a rare-earth metal,' has become of interest recently due to its low density (2.99 g per cc) and relatively high melting point (1539°C).Spedding,' et al. have described a method of preparation of pure scandium metal and have made a study of its basic properties. Since scandium is approximately 10 to 12 pet smaller in at. diam than the other rare earths while its electronegativity and valence are the same, a knowledge of its alloying behavior in contrast to these elements should be very helpful to fundamental alloy theory. Since scandium is quite scarce and difficult to prepare in pure form, its use as a structural material by itself seems quite unlikely. However, its use in special cases as an alloying addi- tive to other low-density materials is a possible application; the Sc-Ti system was chosen for this reason and for others of fundamental interest. Scandium was suspected of having a high temperature bee form as do some of the other rare-earth metals.3'4 Since titanium has a high-temperature bee form, a continuous series of solid solutions at elevated temperatures between ß scandium and ß titanium would prove the existence and structure of the high-temperature form of scandium. The existence of a continuous series of hexagonal solid solutions at room temperature was predicted by Burkhanov and Savitskiy,5 but Hias shown to be incorrect in early X-ray studies. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar titanium and distilled scandium prepared by the method described by Spedding,2 et al. The major impurities are listed in Table I in PPm. Alloy Preparation. All the alloys examined were initially formed in a nonconsumable electrode are-melting furnace under an atmosphere of purified helium or argon. A curve based on the observed weight loss of 0.6 pet* when titanium was melted

Jan 1, 1962

By John Fitzpatrick

In this Bureau of Mines investigation a device was developed that permits the determination of the modulus of elasticity of the stress-relief cores obtained in the process of making in situ stress measurements. This determination is made by hydraulically loading the external surface of the stress-relief cores and by measuring the corresponding borehole deformation. The theoretical relationship between the borehole deformation, the applied pressure, and the modulus of elasticity is presented. Also, experimental results obtained from measurements on a simulated stress-relief core made of aluminum and on a limestone stress-relief core are given. Because of the symmetrical loading obtained with this device, the isotropy of the core material can be evaluated. With this device it is also possible to study the effect of eccentricity, that is, the effect within cores in which the inner hole is not coincident with the long axis of the specimen.

Jan 1, 1962

By H. R. Babitzke

The purpose of this investigation was to evaluate the potential of columbium-hafnium alloys as structural materials for use at elevated temperatures. The work described in this report was conducted to determine the properties of columbium-hafnium alloys and to select the more promising ones for further improvement. Properties determined in this report were machinability, hardness, workability, tensile strength, and oxidation resistance. Ten ingots, ranging from 100 percent columbium to 70 atomic-percent hafnium, were prepared and subjected to tests. The test results showed that the alloys with 33 and 50 atomic-percent hafnium were superior in workability, strength, and oxidation resistance. For the alloy series tested, the strength and hardness values increased with the increasing hafnium content. Maximum values were reached with 50 atomic-percent hafnium. The oxidation resistance was poorest at the 1 atomic-percent hafnium level but improved with increasing hafnium content through 70 atomic-percent. Eight of the ten ingots were fabricable at room temperature. The two remaining ingots, those with 5 and 10 atomic-percent hafnium, required hot-working.

Jan 1, 1962

By Harold Margalin, Elmars Ence

M. H. Mueller, M. V. Nevitt, and H. W. Knott (Argonne National Laboratory)—We have reported1 the crystal structure of Ti2CU as body centered tetragonal with a. = 2.944A and co = 10.786A, six atoms per unit cell, and space groupl4/mmm(MoSi2 type). This cell is larger but definitely related to the unit cell reported by the authors. It permits definite positions for the titanium and copper atoms in the cell located as follows: 2 Cu (a) 0 0 0; 1/2 1/2 1/2 4 Ti (e) 0 0 z; 1/2 1/2 1/2 + z; 0 0z; 1/2 1/2 1/2- z where z = 0.341 The face centered tetragonal cell reported by the authors can be transformed to a small body centered tetragonal cell with flo (small bet) = ao(fct)v2 Both unit cells have the same CO. Neither the face centered tetragonal cell with four atoms per unit cell nor the small body centered tetragonal cell with its two atoms per unit cell lend themselves conveniently to an orderly arrangment of the 2 to 1 ratio of titanium to copper atoms. When the co of this small body centered cell is tripled, however, a large body centered tetragonal cell results with six atoms per unit cell as described above. We had also noted that the X-ray patterns of Ti2Cu indicated that the structure could be approximately described by the face centered tetragonal cell as reported by the authors; how- ever, there was evidence for a few additional very weak lines whose positions indicated a larger unit cell. Since the X-ray scattering amplitudes of titanium and copper are nearly equal, it is evident that it is difficult to distinguish their positions especially from X-ray powder patterns. It was therefore decided to look at a powder pattern obtained by neutron diffraction since the scattering amplitudes of the two elements are considerably different in magnitude and opposite in sign. The sample used for neutron diffraction was selected from a group of three alloys prepared by arc melting using crystal bar titanium of 99.92 pet nominal purity and 99.999 pet pure Cu. The alloys designated as A, B, and C had the following respective compositions: Ti-32.8 at. pet Cu, Ti-33.3 at. pet Cu, and Ti-33.8 at. pet Cu. On the basis of the melting losses incurred, it was established that the actual concentration of either component in any of the alloys probably did not deviate from the intended value by as much as 0.1 at. pet. The alloys were annealed for 5 days at 700°C in evacuated Vycor capsules and quenched in tap water. The metallographic structures of these alloys are shown in Fig. 1. None of the alloys contained sufficient second phase to permit its positive identification. Since alloy B contained the least amount of second phase and since its composition placed it closest to the ideal stoichiometry, it was chosen for the neutron diffraction study. The oxygen content of alloy B was found by chemical analysis to be 0.06 at. pet. This particular intermetallic compound is especially suitable for investigation with neutron diffraction since if the titanium and copper atoms have a random statistical distribution, a near null-matrix would result in which there would be practically no coherent scattering of neutrons, and hence no Bragg diffraction peaks. Such a condition could come

Jan 1, 1962

By Morris Cohen

STAFF: Editor, Gerhard Derge Acting Editor, Paul G. Shewmon Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Production Editor, Otto T. Johnson THE METALLURGICAL SOCIETY: Karl L. Fetters, President; J.S. Smart, Jr., Past-President; R. C. Cole, Vice President; R. L. Hennebach, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: W. O. Phil-brook, Chairman; H. L. Bishop, R. C. Cole, J. N. Hobstetter, W. A. Krivsky, E. R. Morgan, F. C. Langenberg, R. E. Lund, Paul Queneau, L. L. Seigle, R. L. Smith, and T. V. Wainwright. Review and selection of manuscripts is under the supervision of the following Publicotions Committes: Extractive Metallurgy Division: R. E. Lund, Chairman; M. E. Wadsworth, Vice Chairman; D. H. Baker, Jr., G. M. Bell, R. E. Grace, W. A. Krivsky, R. A. Lewis, Charles O'Neill, A. W. Schlechten, R. E. Shinkoskey, and W. W. Stephens. Iran and Steel Division: T. V. Wainright, Choirman; H. L. Bishop, R. E. Boni, T. E. Dancy, D. W. Murphy, Johannes M. Uys, J. B. Wogstoff, and R. G. Ward. Institute of Metals Division: J. N. Hobstetter, Chairman; P. A. Beck, J. J. Becker, G. F. Bolling, J. 0. Brittain, J. B. Clark, R. S. Davis, A. E. Dwight, R. W. Fountain, L. R. Girifolco, J. C. Gurland, H. S. Kalish, E. L. Harmon, J. J. Heger, A. A. Hendrickson, L. Himmel, J. P. Hirth, H. H. Johnson, Jr., R. R. Nosh, T. N. Rhodin, R. H. Richman, H. C. Rogers, W. Rostoker, C. Sherby, C. W. Spencer, L. Slifkin, J. K. Stanley, R. Steinitz, H. C. Stumpf, and R. Swalin. Published bimonthly by the Americon Institute of Mining, Metallurgicol, and Petroleum Engineers, Inc., 345 East 47th Street, New York 17, N. Y. Telephone PLaza 2-6800. Subscription $30 peryear for non-AIME members in United States and North, South, and Centrol America; $32, foreign; $30per$7.50 for AlME members. Single copies, $6.00, single copies foreign, $6.50. The AlME is not responsible for any stotement made or opinion expressed in its publications ... Copyright 1962 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York . . . Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . . Second class postage paid at New York, N. Y., and Ann Arbor, Mich. Volume 224, Number 4.

Jan 1, 1962

By H. O. Seigel

Induced Polarization includes many types of dipolar charge distributions set up by the passage of current through consolidated or unconsolidated rocks. Among its causes are concentration polarization and electrokinetic effects in all rocks and the phenomenon of Overvoltage in rocks containing electronic conductors such as metallic sulphides and graphite. In normal rocks the polarization effects may be usually con-fined within relatively narrow limits and any large departures may be at-tributable to the presence of electronic conductors. In practice, Induced Polarization is measured in one of two ways. In the first a steady current of some seconds duration is passed and abruptly interrupted and the slowly decaying transient voltages existing in the ~round are measured after interruption. This is known as the "pulse", "transient", or Direct Cur-rent Induced Polarization (D.C.I.P.).The second method entails a comparison of apparent resistivities using sinusoidal alternating current of two or more frequencies, generally within the range of 1/10 to 10 c.p.s. Induced Polarization extends the

Jan 1, 1962

By L. G. Marshall

This report is one of a series published by the Federal Bureau of Mines, describing mining methods and performance at individual mining operations throughout the United States. The objective of these papers is to promote development and conservation of our mineral resources by disseminating reliable technological information on mining methods, practices, and performance. Limestone deposits in Iowa are extensive and reserves are large. Most of the past production came from the eastern third of the state, although over half of the counties in the state have produced, or are now producing limestone. The stone is used as aggregate, road metal, agricultural lime, riprap, fluxing stone, railroad ballast, and in the manufacture of cement and lime.

Jan 1, 1962

By R. Maddin, A. Lawley

Single crystal Mo-Re alloys (99.99+ purity), grown by electron bombardment floating zone heating, were deformed in tension at temperatures from -196° to +200°C. At -196oC, Mo-6 pet Re and Mo-20 pct Re alloys deform by slip on systems of the type (101) [1ll]. Above-78oC, the operative slip system is of the type (112) [111], (101) [1ll], or (211) [1ll], depending upon orientation. Mo-39 pct Re alloys deform by twinning and slip at all test temperatures with a (112) [111] type twinning system. Critical resolved shear stress for slip and twinning is calculated as a function of composition and temperature, and the mechanical properties compared with those of less Pure polycrystalline alloys. HEXAGONAL close-packed rhenium, c/a = 1.615, is highly soluble in molybdenum. The bee molybdenum-rich solid solution extends to approximately 42 at. pet Re* at 2500°C,' Fig. 1. Recent work on polycrystalline alloys has shown conclusively that the addition of rhenium to molybdenum improves both the fabricability and the low-temperature ductility.2"5 Similar behavior is observed for W-Re and Cr-Re alloys.5 Initially, Geach and Hughes2 found that the Mo-30 pct Re alloy could be cold rolled to approximately 90 pct reduction before the onset of cracking. The remarkable effect of the rhenium was later confirmed by Jaffee et al. 3-5 with an optimum condition of maximum strength combined with maximum ductility at the Mo-35 pet composition. At higher rhenium contents, the ductility was severely impaired due apparently to the presence of brittle tetragonal s phase, Fig. 1. In the Mo-35 pet Re alloy, at least 110 ppm (parts per million) oxygen could be tolerated before cold workability was reduced. By comparison, the corresponding tolerance figure in unalloyed molybdenum is ~ 10 ppm. The effect of rhenium was considered in terms of: 1) a reduction in oxygen solubility in the lattice; 2) a redistribution of intergranular oxide from grain boundary films to isolated spheres; and 3) the promotion of twinning as a further mode of plastic deformation. Paradoxically, twinning is often associated with brittle fracture in iron and the silicon irons.6'7 Work to date has been restricted to are-melted and powder metallurgy polycrystalline material of ~ 99.9 pet purity. The present investigation was initiated for the purpose of determining the mode and crystallography of plastic deformation of a series of bee Mo-Re alloy single crystals over a wide temperature range from -196o to +200°C. Using high-purity zone-melted material (~ 99.99 + pet purity), the specific role of rhenium in the molybdenum lattice may be understood more fully since effects due to grain boundaries and oxide redistribution will be absent. At the same time, the study provides a comparison of single and polycrystalline deformation behavior. EXPERIMENTAL TECHNIQUES A) Preparation and Purity of Single Crystals. Alloys in the form of either are-cast and swaged or sintered and ground bar, 0.120 in. diam, were obtained from the Chase Brass and Copper Co. Alloy single crystals ~ 8-in. long were grown from the

Jan 1, 1962

By E. W. Lucht

THE term "high pressure", as used in industry today, is applied rather loosely. Generally, it refers to pressures that are higher than those encountered in most industrial processes although no definite limits are normally stated. For the purpose of this talk I should like to set rather arbitrary limits to the term "high pressure", and in ab-solute figures this would be the range from 1000 psi to perhaps 40,000 or 50,000 p.s.i. The scope of high pressure technology is very broad, and it would take more time than we have avail-able here today to cover fully even one aspect of the field. Therefore, I should like to discuss just some of the techniques used and problems en-countered in high pressure operations. Research work into the high pressure region dates back about 150 years, but it was not until 1910 that the first commercial application of high pressure technology was made in the production of ammonia.

Jan 1, 1962

By B. W. Veal, B. S. Chandrasekhar

THE Laue method of orienting single crystals requires the use of tables of angles between crystal-lographic planes, and between zone axes. Such tables have been published for cubic crystals, and some rhombohedra12 and hexagonal3 crystals. A table of angles between planes in ß-tin has also been published;4 these angles refer to only low-index planes, and are not particularly helpful in the actual indexing of spots on a Laue photograph. Furthermore, it is often useful to know the angles between zones which share a common low-index plane. We have calculated such tables of angles for ß-tin and indium, both between planes in principal zones, and between zones passing through principal planes. The results are given in Tables I and 11. The standard formulas were used, with c/a = 0.54554 for 0-tin, and 1.07586 for indium.

Jan 1, 1962

By G. R. St. Pierre, A. J. Wilhelem

In connection with the reduction of hematite or magnetite to metallic iron, it appeared desirable to study the rate of reduction of each oxide to the next lower oxide under conditions which excluded all other condensed phases. For this purpose, pellets of Fe,O,, Fe,O,, and oFeOo were prepared. A gas train for the preparation of Ar-Hz-H20 mixtures was employed to establish a continuous flow of a controlled atmosphere over a pellet suspended on a balance. In this manner the following individual reduction steps could be studied: For example, pellets of hematite were reduced solely to magnetite by adjusting the gas atmosphere such that it was oxidizing to wustite. In other words, the reaction was complete when the hematite pellet had been totally converted to magnetite. The pellets were prepared from Baker Chemical ferric oxide. The ferric oxide powder was moistened and handrolled. Air sintering at 950°C produced Fe,0, pellets with a density of 3.65 g per cm3. The pellets ranged in size from 0.6 to 1.2 cm diam. The magnetite and

Jan 1, 1962

By J. Philibert, A. G. Guy

Diffusion in the presence of deformation was studied by the method of vacuum dezincification of copper-rich and silver-rich solid solutions containing 7 to 30 pct Zn. The specimens were designed to permit the study of diffusion in separate portions of a given specimen characterized by strain rates ranging from essentially zero to approximately 10 sec-. No effect of deformation on diffusion was observed. BEGINNING with the work of Buffington and Cohen: interest in the question of the effect of stress or strain on diffusion has largely been concentrated on the enhancement of diffusion in specimens subjected to Continuous plastic deformation. The present research is a contribution to this limited area. However, as a preliminary to focusing attention on this special topic, it will be desirable to make a broad survey of the larger question, especially since there has been considerable foreign work in areas outside those of current interest in the United States. Since most of the topics referred to in the following section are both complex and imperfectly understood at present, it has been expedient in most instances to offer only a guide to the general nature of the work rather than a critical evaluation. PREVIOUS WORK The effect of elastic stress on diffusion has received considerable attention, especially with regard to the thermodynamic driving force for diffusion. The thermodynamic treatments have been based on the work of Gibb, Voigt, Planck, and Leontovich.' Konobeevskii and Selisski6 made a first attempt at treating the problem in 1933, and Gorskii7 a few years later gave a solution applicable to single crystals as well as to polycrystalline specimens. In 1943 Konobeevski8 published treatments that have been the basis of much Russian work up to the present. For example, Aleksandrov and Lyubov used his work in explaining the velocity of lateral growth of pearlite. Early work in the United States was that of Mooradian and Norton, which showed that lattice distortion tends to be relieved before it can significantly affect the diffusion process. Druyvesteyn and Berghoutl1 observed a slight effect of elastic strain on self-diffusion in copper, while de Kazinczy12 found that both elastic and plastic deformation increased the rate of diffusion of hydrogen in steel. On the other hand, Grimes58 observed no effect of either elastic or plastic straining on the diffusion of hydrogen in nickel. High-frequency alternating stresses have been reported by various investigator s13-l5 to increase the rate of diffusion. A special form of elastic stressing is the imposition of hydrostatic pressure, a condition that is amenable to Conventional thermodvnamic analysis. Most of the experimental results in this area are consistent in showing a slight decrease in diffusion rates at high pressures.16-l8 Although Geguzinl reported a pronounced effect of relatively small pressures, Barnes and Mazey20 failed to Corroborate this finding, while Guy and Spinelli21 advanced an explanation of the phenomenon observed by Geguzin. It has been recognized that the thermodynamic treatment of diffusion phenomena in an arbitrarily stressed body is complicated by the fact that the desired state of quasi-equilibrium of the shear stresses cannot be maintained during a general diffusion process. However, attempts have been made by Meix-ner22-24 and Fasto to treat certain restricted cases, such as relaxation. FastovZ7 has also incorporated the general stress tensor into the thermodynamics of irreversible processes. The lattice strain that accompanies the formation of a solid solution has been the subject of much study,28-s0 and indirectly it has entered into many recent theories of diffusion. However, some Russian investigators31'32 have taken other views of this matter and have predicted large effects on diffusion rates because of concentration stresses.o In completing this brief resume of previous work involving elastic strains and before proceeding to a consideration of the effect of continuous plastic deformation, it should be pointed out that deformation of various additional types may also influence diffusion. The effect of cold-working on subsequent diffusion has been studied directly by AndreevaS and by Schumann and Erdmann-Jesnitzer, while indirect evidence has been obtained by Miller and Guarnieri and by Vitman.38 Thermal stresses may also influence diffusion, contributions to this subject having been made by Fastovs7 and by Aleksandrov and Lyubv. The work of Johnson and Martin,o Dienes and Damask,3Band DamaskS considered the question of radiation-enhanced diffusion. In considering previous work on the subject of plastic deformation and diffusion, attention will be directed to those studies concerned primarily with diffusion rather than with its relation to Creep, e.g., the work of Dorn, or to the acceleration of diffusion -controlled reactions. Observations of the effect of

Jan 1, 1962

By William R. Wayment

The objective of this investigation was to obtain data on friction-head losses of sand slurries during their transport in pipelines. The data ultimately will be used in designing hydraulic transport systems. Information that was incidental to the primary objective was gathered on degradation, changed percolation characteristics, and critical velocities of the slurries~ Tests were made in a closed-circuit pilot plant, with one type of tailing, through horizontal 2-, 3-, and 4-inch-pipe test sections at various pulp densities and flow velocities. Tests were made in a closed-circuit pilot plant, with one type of tailing, through horizontal 2-, 3-, and 4-inch-pipe test sections at various pulp densities and flow velocities. Approximately 2,000 tests were run in the pilot plant. The ranges of flow velocities used in the experiment were 2.8 to 19 f.p.s. in the 2-inch line, 4 to 14.5 f.p.s. in the 3-inch line, and 4 to 11 f.p.s. in the 4-inch line. Velocities were varied in increments of 0.5 f.p.s. through the entire velocity range in each pipe size. Densities were varied in 3-percent increments from 40 to 70 percent solids by weight except for one series of tests in the 2-inch line; in this series, densities were varied in 5-percent increments from 5 to 65 percent solids by weight.

Jan 1, 1962

By Dogan E. Gücer

In the following note, with the help of a new parameter of strain hardening, the attention is drawn to the close relationship between the relative performances of steels under plastic range cycling and their strain hardening characteristics. If a cantilever beam of rectangular cross section is tested with the arrangement shown in Fig. 1 in reversed bending between constant deflection limits at the lever head, the longitudinal strain-deflection hysteresis shown in Fig. 2 is obtained. There is no lateral strain due to constraint at the rectangular test section.' If the absolute value of strain undergone between a maximum state of tension and maximum state of compression is called A, it will be seen that A decreases with cycling rapidly due to the strain hardening in the test section and the ensuing change in the bent beam profile. It will also be seen that A reaches an approximately stable value around 10th cycle. If we call the first cycle strain range, A,, and that of 10th cycle, A,,, then is an index of the strain hardening capacity at a particular deflection level. A plot of n vs ? is reproduced in Fig. 3 for two ASTM steels: A-302 and A-201. A-302 is a low alloy structural steel, A-201 a low-carbon steel. The specimens were first normalized at 1650°F for 75 min then grooved with a milling cutter; and the notches were ground to 50G finish. The final operation before testing was a stress relief at 1150°F for 75 min. The behavior of the two steels changes around ?1 = 0.8 pct or A,, = A, -n = 0.7. If these curves are compared with the endurance life curves given in Fig. 4, it will be seen that the relative performance of the two steels also change around A,, =. 0.70 pct. The steel with lower strain hardening capacity (7) at a certain strain level shows a longer endurance life, irrespective of their strength levels. Since the exponent governs strain hardening at lower strain levels than the Modulus, the relative values of both parameters also coincide with the change in n values and the relative performances of the two steels at different strain levels. These two observations indicate to the close relationship be-

Jan 1, 1962

By P. Chollet, A Constant

THE RESULTS of a previous investigation ( 1) on the work-softening of some heat-treated steels have led to the conclusion that the occurrence and intensity of the phenomenon is possibly governed by the work-hardening capacity of the material, and the relative amount of retained austenite. The first assumption is compatible with Polakowski's theory (2) that the absence of work-softening, in steels quenched and tempered at relatively low temperatures, may be attributed to the high rate of work-hardening which compensates for, and even out-weighs, the loss of internal energy associated with the simultaneous rearrangement of the original system of internal stresses. Indeed, Polakowski first considered the work-softening as a manifestation of a partial release (by cold-working) of the latent strain energy stored in

Jan 1, 1962