By J. B. Cohen, B. W. Howlett, M. B. Bever

The partial molar heats of solution at infinite dilution in tin of aluminum at 300° and 350°C and of gallium, indium, and thallium at 240°, 300°, and 350°C have been measured by tin solution calori-metry. Aluminum, gallium, and thallium are endo-thermic on solution; indium is exothermic. Any temperature dependence of the heats of solution lies within the experimental scatter. Over the dilute ranges investigated, only aluminum has a measurable change in its heat of solution with composition. HEATS of solution of one element in another reflect the interaction between them. The investigation of partial molar heats of solution in dilute alloys is of particular interest as the properties of the solvent are altered to only a limited extent by the presence of the solute and also as the interaction between solute atoms is small. When the heats of solution of a related series of elements in a solvent are known, a systematic comparison may be made. In the investigation reported here, the partial molar heats of solution of the Group III elements aluminum, gallium, indium, and thallium in dilute solution in tin were measured. This work follows an investigation of the heats of solution in tin of the Group IB elements.' EXPERIMENTAL PROCEDURES Materials. Samples of gallium, indium, and thallium were obtained from Johnson, Mathey and Co., Ltd. Indium and thallium were supplied as wire, 1.6 mm in diam; gallium was in the form of irregular pieces. The supplier reported the following minimum purities: gallium—99.95 pct; indium—99.99 pct; thallium—99.99 pct. The aluminum, obtained from Alcoa Research Laboratories, was reported to be 99.995 pct pure. The tin was supplied by Baker and Co., Inc.; the reported analysis indicated a tin content of at least 99.96 pct with lead as principal impurity. Calorimeter. this description will cover only the essential features of the calorimeter with special attention to modifications made since an earlier description was published.' A Dewar flask containing the tin bath was held in a constant-temperature bath of a near-eutectic mixture of lithium, sodium, and potassium nitrates. This bath, which was stirred vigorously, was heated by a primary resistance winding in the container wall and by a secondary winding immersed in the salt. The voltage supplied to both windings was stabilized. The temperature of the salt bath was controlled by means of a platinum resistance thermometer in one arm of a Wheatstone bridge. The light from a mirror galvanometer in the bridge circuit fell on a photocell which controlled the current in a saturable reactor in series with the secondary winding. In this manner, the temperature of the salt bath was controlled to ±0.003°C and that of the tin bath to at least ±0.002°C. Each of these temperatures was measured by two iron-constantan thermocouples in series, coiled in a helix to minimize heat loss and immersed in the salt and tin baths in protective sheaths. The temperature of the laboratory was kept constant to ± 1°C during a run. Specimens were dropped into the tin bath from an addition arm held at O°C which was part of the cal-orimetric system. The system was evacuated to about 0.02 1 to minimize oxidation and to reduce transfer of heat. The bath was stirred by a glass stirrer introduced through a double Wilson seal. The samples were scraped clean before weighing, which was carried out as rapidly as possible. Each sample was immediately placed in the evacuated addition arm to minimize contamination. These precautions were especially necessary with aluminum. After the runs with gallium and thallium at all temperatures and with indium at 240° and 350°C (Series I) were completed and before the runs with indium at 300°C and aluminum at 300° and 350°C (Series 11) were begun the following changes were made. The shape of the Dewar flask was changed so as to result in a lower surface to volume ratio of the bath and at the same time the amount of tin was reduced from 500 to 400 g. The paddle type stirrer was replaced by a helical screw and the rate of stirring was increased to about 150 to 200 rpm.

Jan 1, 1962

By Charles Zahn

Direct mass spectrometric determination of alcohols in the presence of hydrocarbons has not been possible because of the similarity of hydrocarbon and alcohol mass spectra. Experiments have demonstrated that by converting the alcohols to their trimethylsilyl derivatives, characteristic mass spectra are obtained free of interference from hydrocarbon ion fragmentation. Hexa- methyldisilazane is the reagent selected for the conversion, An improved method of preparing the reagent is given, Mass spectrometric determination of alcohols as trimethylsilyl ethers now is not only possible without prior separation from other materials, but the range of the room-temperature mass spectrometer is also extended to include the C10 alcohol region. Water does not interfere because it is converted to hexamethyldisiloxane, which has its own distinctive mass spectral peak, Experience indicates that other compounds such as glycols, amines, and phenols probably could also be determined by mass spectrometry of their trimethylsilyl ethers. Studies on the similar detemination of phenols in coal oils have been started, When mass spectrometry is not available, gas-liquid chromatography of alcohols before and after their conversion to the trimethylsilyl derivatives probably could be performed. The preparation and properties of the trimethylsilyl derivatives of 23 alcohols, 2 glycols, 3 amines, and 1 mercaptan are detailed. INRODUCTION During investigations by the Bureau of Mines at the Pittsburgh Coal Research Center relative to the development of Fischer-Tropsch processes, complications were encountered in the mass spectrometric analysis of alcohols in hydrocarbon oils. The fragmentation peaks of the alcohols and the hydrocarbons were so similar that an accurate analysis was not possible, Since involved separation techniques are necessary to isolate alcohols from hydro-carbons for separate determinations, efforts were turned to the search for a

Jan 1, 1962

By W. A. Wood, H. M. Bendler

Cylindrical fatigue specimens of OFHC* copper were subjected to alternating torsion while under axial tension. The superimposed tension strongly influenced the fatigue life of the specimens as well as causing characteristic changes in the structure of the fissures that form and develop throughout the life of the specimen. A further effect of the superimposed tension is a continuous extension of the specimen throughout its life in a manner formally similar to creep at elevated temperatures. RECENTLY, studies of the structural changes leading to fracture of metals by fatigue have been made by a technique which reveals, in section, the lattice distortion arising from slip movements inside the metal and the disturbances built up by these slip movements at the metal surface.1'2 According to this approach, fatigue develops as follows: a) fine slip movements concentrate in bands, producing little strain-hardening and thus permitting abnormal totals of plastic strain before fracture and, therefore, abnormal amounts of lattice distortion along each slip band; b) both forward and backward slip movements occur in each band which, according to their distribution across the band, may build up surface disturbances that include sharp notches; c) these notches early in the life of a specimen penetrate the distorted slip zones and transform them into deep, fine fissures; d) the fissures on continued cycling locally saturate the metal and cause local collapse in the form of a microcrack. Thus, the significant consequence of fatigue or cyclic

Jan 1, 1962

By Paul A. Beck, M. N. Parthasarathi

By determining the (220) pole figure for OFHC copper rolled to 96 pct R. .A., the occurrence of four texture components of the type (135) [211] was confirmed. It was found that the total volume fraction of material close to the four symmetrical orientations of this type is larger than the volume fraction of the other components put together. THE rolling texture of copper was described by early investigators1'" as a mixture of components of the (110)[l12] and (112) [11l] types. Other studies, still using the qualitative photographic method of texture determination arrived, instead, at orientations of the type (135) [533] or (135) [211] for copper3'4 and at the closely related "Z-texture" for a fee nickel-iron alloy.5 The prevalence of this type of orientation, near (123) [412], in the rolling texture of aluminum and of copper was later confirmed by means of quantitative diffractometer methods.' However, in a recent paper7 Jones and Fell stated that the (110) [112] and (112) [111] double texture was in better agreement with the measurements of Young's modulus for cold-rolled copper.' These authors also expressed their belief that the "roll texture" can be determined by means of two photographic quasi-fiber texture patterns taken with sheet specimens rotated around the rolling direction and the transverse direction, respectively. Jones and Fell found7 that the results obtained from such patterns for cold-rolled nickel did not agree with any of the orientations mentioned above, but they suggested that the observed diffraction spots may have been brought about by the overlapping of reflections due to the (110) [112] and (112) [11l] double texture components. Jones and Fell concluded that the (123) 14121 type orientation is inconsistent with their patterns. They also stated, without offering any supporting evidence, that this orientation is inconsistent with the (220) pole figure. "Ideal orientations" are often used for a very rough description of the principal orientations encountered in a texture, It is, however, well to remember the fact that, no matter how "accurate", these ideal orientations are only schematic representatives of a continuous distribution9, which often (as in the case of rolled copper) includes extensive orientation spreads. The attempt by Jones and Fell7 to use elastic modulus data in deciding between various ideal orientations in the rolling texture of copper neglects this fact. The inadequacy of two-dimensional "axis density figures" in describing orientation distributions in sheet textures was previously discussed.9 It was also pointed out9 that there is no reliable evidence to prove that orientation distributions derived by the "quasi-fiber method" from rotated sheet specimens are fully equivalent to the corresponding information obtainable from quantitative pole figures. The view that a sheet texture could be adequately determined by means of two photographic quasi-fiber texture patterns is obviously erroneous9. The question as to the consistency with the (220) pole figure of ideal orientations derived from the (111) and (200) pole figures is, on the other hand, certainly very relevant. Since no quantitative (220) pole figure for cold-rolled copper appears to be available in the literature, the following work was undertaken. EXPERIMENTAL METHOD An extruded rod of OFHC copper, 1 in. in diam, was given alternate rolling (30 to 35 pct R.A.) and

Jan 1, 1962

By C. Richards Honeycutt, Frederick C. Langenberg, Guenter Pestel

Solidification in a moving electromagnetic field was successful in altering the as-cast grain structure of steel ingots. The equipment is described and exerimental results are presented for several different alloys. Conditions for optimum grain refinement are described and an empirical design constant presented. The effect of the grain refinement on hot workability is briefly discussed. T HE grain structure of a steel ingot teemed into a metal mold can be defined by macroscopic examination in semiquantitative terms. For example, the relative volume of obviously differing structures can be estimated with the classic definitions of chill, columnar, and equiaxed zones. Experimental evidence has proven that the grain structure of an ingot is affected by changes in such factors as teeming temperature, rate of teeming, degree of turbulence, size of ingot, mold characteristics (including preheat temperature, design and coating), and composition of the metal (especially as it affects the range of solidification). Significant advances have been made in fundamental solidification studies; but the principles which have been developed are difficult to apply tothe complex and changing phenomena that occur simultaneously during ingot solidification. In particular, many attempts have been made to refine the as-cast structure of ingots, with special emphasis on the columnar grains. The formation of large columnar grains is generally considered harmful to the further fabrication of an ingot. It may also result in undesired ani-sotropic properties. However, columnar grains are not undesirable in all grades, or product applications, and caution must be exercised to determine in which grades and applications columnar grains are not desired in the ingot. Although the literature on the refinement of as-cast ingot grain structures is too vast in general to review here, it is noteworthy that such methods are additions of artificial nuclei, mold vibration, mechanical stirring or ultrasonic agitation of the molten metal, and controlled cooling and reheating during solidification have been tried with varying degrees of success. However, it is doubtful that any method of refining the as-cast ingot grain structure has been completely successful on a commercial basis. The purpose of

Jan 1, 1962

By E. N. Silverman

Mixtures of' MnS, ZFeO-SiO,, ZMnO.SiO, FeO, and MnO were prepared synthetically and used to study the planes ZFeO. Si0,-ZMnO.SiO,-MnS, FeO-MnO-MnS, and Fe0-MnO.Si0,-MnS in the quaternary system. Because the oxides and silicates studied flux MnS, inclusions in this system are partly liquid during rolling. Also, oxygen can modify subsurface inclusions through the reaction MnS + FeO—FeS + MnO during the soaking of ingots and the reheating of blooms and billets. NONMETALLIC inclusions in steel have long been a subject of study and conjecture because the properties of many steels are known to be affected by the the kind and amount of inclusions present. In free-machining steels, the type of inclusion present has a direct bearing on their machinability; in other steels, cleanliness is important and metallurgists direct their efforts at reducing the amount of non-metallic inclusions. Thus, the accumulation of knowledge about the formation and behavior of inclusions during all stages of steelmaking and processing should aid in improving the quality of steels and decreasing the production costs resulting from rejections. Previous studies of inclusions have contributed greatly to our understanding. The investigators have generally examined inclusions in finished steel. Boulger, Moorehead, and Garvey1 found that in Bessemer steels, low silicon contents results in globular sulfide inclusions with attendant high machin- ability ratings. Van vlack2 also found that low silicon contents favor inclusion morphology that contributes to high machinability ratings. Boquist and Stoll* found that silicon content affected sulfide inclusions and machinability of blooms, billets and bars more than did the finishing temperature in the range between 1775° and 2075°F. Carney and Rudolphy3 studied the distribution of sulfur, manganese, silicon, and carbon in a commercial ingot of resulfur-ized steel and found that silicon was concentrated near the bottom. This helped to explain why bottom cuts had poorer machinability. Klinger and Koch4 developed techniques for extracting inclusions from steel, and the technique devised by Gurry, Chris-takos, and stricker5 for extracting carbides can also be adapted to the study of inclusions. A different approach to the study of inclusions in steel consists of synthesizing the constituents that form inclusions and determining the phase eauilibria in the system that contains the constituents. The resulting phase diagrams can then be used to determine the effect of the various constituents upon each other. In this way, it becomes possible to under-

Jan 1, 1962

By C. L. Meyers, J. L. Lytton, T. E. Tietz

The recovery of tensile flow stress of 99.995-pct Al and Al-1 pct Mg alloy was investigated using a fractional recovery parameter. Tensile strainirg was conducted at room temperature, and recovery treatments were made in the range from 80° to 200°C. Equal values of fractional flow stress recovery were found to result in equivalent structural states. Identical recovery treatments were found to produce constant values of fractional flow stress re covery, independent of prestrain. The activation energy for recovery of the 99.995-pct A1 between 80" and 200°C was found to be 23,000 +2000 cal per mole, and the activation energy for the Al-1 pct Mg alloy was 27,500 cal per mole. 1 HE degree of recovery of a cold-worked metal may be studied by measuring the changes which take place in any of a number of properties. Some of the properties which have been used by past investigators include X-ray diffraction phenomena, electrical resistivity, hardness, creep strength, elastic limit, and flow stress. Despite the apparent preponderance of such studies, little is known concerning the effect of recovery on the strength of metals except as deduced from changes in various types of hardness measurements. Furthermore, little information is avail- able concerning the effects which specific solute atoms have on the recovery process. Limited studies have indicated that in some cases solid-solution additions greatly decrease the rate of recovery,' whereas in at least the case of magnesium additions to alluminum an increase in the rate has been reported.2 The purpose of this investigation was to determine the effect of a 1 pct Mg addition on the recovery of high-purity aluminum. Because of the particular interest in the effect of solute additions on the recovery behavior as related to mechanical properties, the degree of recovery was evaluated in terms of tensile flow stress. For the purposes of this study, a recovery process shall be defined as any process, short of recrystallization, whereby the properties, of work-hardened metals tend toward their values ill the unstrained state. EXPERIMENTAL PROCEDURE Test Materials. The materials used in this study were a 99.995-3 A1 and an Al-1 pct Mg alloy made from high-purity base metal. The high-purity aluminum contained the following wt pct impurities: 0.001 pct Cu, 0.002 pct Fe, 0.001 pct Si, and 0.0004 pct Mg. The Pil-1 pct Mg alloy contained 0.001 pct Cu, 0.002 pct Fe, 0.003 pct Si, and 0.99 pct Mg. Both materials were obtained in the form of as-rolled 0.125-in.-thick sheets, from the Alcoa Research Laboratories, New Kensington, Penn. Tensile specimens were cut from these sheets with the longitudinal axis in the rolling direction. Both materials were recrystallized in a molten salt bath; the high-purity aluminum at 450° C for 20 min and

Jan 1, 1962

By E. T. Turkdogan, L. S. Darken

Calcium ferrite melts were equilibrated with sulfur and oxygen-bearing gases at temperatures within the range 1290°C to 1620°C. The results show that at oxygen partial pressures below 10-4 atm the sulfide-reaction occurs and at higher oxygen pressures the sulfur dissolves in the melt principally as sulfate ion. It is also observed that when the product increases, sulfate ions are converted to pyrosulfate ions and the results permit the evaluation of the pyrosulfate/sulfate ratio. It is shown that the ratio y CaSO,/rCaO increases with decreasing concentration of calcium oxide in calcium ferrite, silicate and aluminate melts. Indications are that oxy-acids, e.g. silica, alumina and ferric oxide, increase yCaS0,. A few experiments were carried out within the sul-tide range and the results are in accord with those obtained by other investigators on aluminate and silicate melts. BECAUSE of the industrial importance and theoretical interest, many investigators have studied the reactions between molten oxides, silicates or alumi-nates, and gases containing oxygen and sulfur. The early work reviewed by Schenckl and studies made by Bardenheuer and Geller2 indicates that solution of gaseous sulfur in an oxide melt resulted in the replacement of the oxide ions by the sulfide ions. Measurements made by Grant and Chipman3 on the equilibrium partition of sulfur between molten iron and complex silicate melts also demonstrated that, for a given temperature and silicate composition, the distribution of sulfur between slag and metal increased with decreasing oxygen content of the metal. Fincham and Richardson4 studied the effects of temperature and partial pressures of sulfur and oxygen on the solubility of sulfur in simple silicate and alumino-silicate melts. They observed that at oxygen partial pressures below about 10-5 atm sulfur in the gas dissolved in the melt as sulfide ions, replacing an equal number of oxide ions of the melt. At oxygen partial pressures higher than 10-3 atm, sulfur entered the melt as sulfate ions. Similar studies were made by St. Pierre and Chipman5 using calcium ferrite and calcium silico-ferrite melts. The experimental data presented in this paper were obtained in this Laboratory about 10 years ago; this is the first formal presentation although a preliminary report was given previously.6 In each of these experiments, a pure synthetic CaO-Fe2O3 melt in a platinum crucible was equilibrated with a gas mixture (SO2-O2, SO,-air, SO2-CO, or SO2-CO2-CO) at a temperature ranging from 1296°to 1620°C. The experimental technique was essentially the same as that reported by Darken and Gurry,7 the main difference being that the atmosphere in the reaction chamber contained sulfur dioxide together with oxygen, or carbon dioxide-carbon monoxide

Jan 1, 1962

By O. N. Carlson, S. A. Bradford

Discontinuous yielding in tensile tests was observed in V-O alloys in the temperature ranges of 150° to 175°C and also 350° to 400°C. The magnitude and intensity of the serrations were found to vary considerably with oxygen content. Maxima were observed in tensile and yield strengths and in the strain-hardening coefficient at the higher temperature only. The strain rate sensitivity was observed to be negative between 150° and 400°C. THIS investigation was undertaken to study the effect of oxygen on the tensile properties of iodide vanadium in the temperature range of 25o to 450°C. Brown1 observed an increase in strength between room temperature and 400°C in vanadium metal, and found that oxygen and nitrogen had a rather pronounced effect on the strength and ductility. A maximum in the tensile strength was observed by Rostoker et al.2 near 300oC and by Pugh3 around 450°C for calcium-reduced vanadium. Pugh also found a maximum in the yield strength and in the strain-hardening exponent, and minima in the elongation and strain rate sensitivity at the same temperature. Eustice and Carlson4 reported the appearance of serrations in the stress-strain curves between 140° and 180°C in iodide vanadium containing 600 ppm O. These anomalies in the mechanical properties indicate that strain aging occurs in vanadium, but the impurity or impurities responsible for the above-mentioned effects have not been identified. The phenomenon of strain aging is usually characterized by the return of the yield point after interruption of a strength test. In the temperature range where strain aging occurs, the yield and tensile strengths attain maximum values, elongation and strain rate sensitivity exhibit minima, and discontinuous yielding is generally observed in the stress-strain curve. Cottrell5, 6 has postulated that strain aging is due to the migration of solute atoms to dislocation sites to produce locking after the dislocations have broken free from their impurity atmospheres during the initial yielding. At the strain-aging temperature the process is a dynamic one in which the solute impurity atoms diffuse to the vicinity of the moving disloca- tion producing "locking" which gives rise to maxima in the tensile strength and serrations in the elongation curves. Cottrel17 has noted that discontinuous yielding in iron occurs when the diffusion coefficient of nitrogen, D, and the strain rate, i, are related by D = 10-9 €. EXPERTMENTAL PROCEDURE The vanadium metal employed in this study was prepared by the iodide refining process as described by Carlson and owen.8 A representative analysis of the vanadium used in this investigation was: 150 ppm O, <5 ppm N, <1 ppm H, 150 ppm C, 150 ppm Fe, 70 ppm Cr, <50 ppm Si, 30ppm Cu, 20 ppm Ni, <20 ppm Ca, <20 ppm Mg and <20 ppm Ti. Alloys containing from 200 to 1800 ppm O, all of which lie in the solid solution range of the V-O system, were prepared by arc melting vanadium together with portions of a high-oxygen master alloy. The master alloy was prepared by tamping pure V2O5 into holes drilled in a vanadium ingot and arc melting this five or six times in an inert gas atmosphere, inverting the button between each melting step. The oxygen content of the master alloy was then determined by vacuum fusion analysis. Vanadium containing less than 150 ppm O was prepared in the following manner. A bar of iodide vanadium was deoxidized by sealing it in a tantalum crucible with a few grams of high-purity calcium. This was held at 1100°C for 4 days to allow time for the oxygen to diffuse to the surface and to react with the calcium vapors. The calcium oxide product was later dissolved from the surface of the bar with dilute acetic acid. In this way vanadium containing from 20 to 50 ppm O was prepared. Sample Preparation. The are-melted ingots were cold swaged into 3/16-in. diam rods and these were machined into cylindrical tensile specimens with a reduced section of 1.00-in. length and 0.120-in. diam. The test specimens were annealed for 4 hr at 900°C in a dynamic vacuum of mm of Hg to remove hydrogen from the metal. This recrystal-lization treatment produced a uniformly fine-grained structure with a mean grain size of approximately 0.06-mm diam. The oxygen contents reported in this paper were determined by a vacuum fusion analysis of the tensile specimens after testing. Analyses for other interstitial or metallic impurities showed no significant changes from that of the original material. Tension Tests. Tension tests were performed on a screw-driven tensile machine at a constant cross-head speed of 0.01 in. per min. Tests at elevated temperatures were carried out by heating the

Jan 1, 1962

By Harold L. Riley

This Bureau of Mines paper describes the methods and practices used at the Peck quarry of the Crab Orchard Stone Co., Inc., one of the leading producers of dimension stone in the Crossville, Tenn., area. The product is marketed under the registered trademark "Crab Orchard Stone". Another large producer of stone from the Crossville district sells its product under the registered trademark of "Tenn-Quartz". Both companies, and a number of other companies and individuals who quarry and process dimension stone from the same general geological formation, are members of the Quartzite Producers Association of Tennessee. The salable product is shipped throughout the country for use as architectural building stone. In 1959, 653,008 cubic feet of stone was produced in the Crossville area and was sold for $1,414,405. Terms and descriptions used in this report are those of the quarry and building trades. The offices, pitching sheds, wire saws, railroad siding, and storage areas of the Crab Orchard Stone Co., Inc., are on a side road 0.3 mile north from a point 2.2 miles east of Crossville, Tenn., on U.S. Highway 70. The quarry is on this same side road 2.0 miles south of Highway 70. Crossville is 62 miles west of Knoxville and 65 miles northeast of Chattanooga, Tenn.

Jan 1, 1962

By B. Fitch

This paper deals with the behavior of sedimenting suspensions. More particularly, it treats, in as organized a manner as possible, the body of knowledge, theoretical or empirical, by which one predicts the behavior of miscellaneous swarms of particles in suspension. Such knowledge is necessary for precise and economical design of equipment. While the behavior of a single spherical particle settling through an infinite sea of quiescent fluid is well understood, practical sedimentation processes are almost always concerned with particles of assorted sizes, densities, and shapes, in such concentration that there is profound particle interaction. Such swarms of particles are observed to settle in any of four markedly different manners. Which one they follow is governed by particle interaction. It is determined largely by the dilution of the suspension, and the relative tendency of the particles to cohere. TYPES OF SEDIMENTATION The relationship between the different modes of sedimentation is shown paragenetically in Fig. 1. The left side of the diagram represents particles having little tendency to cohere; the right side represents particles for which interparticle cohesion is large compared to the settling force. The vertical axis represents dilution. As seen in the diagram, sedimentation is divided into three broad fields or regimes. At high dilutions there exists a regime here named &apos;clarification.&apos; Particles in clarification may settle either individually, or by collecting into separated floccules. Thus there are two different possible modes of settling in the clarification regime. It is characteristic c~f this regime that there will be no clear line of demarcation between settling suspension and a supernatant. Faster particles settle out ahead of slower ones. In batch tests there develops a gradation of both particle sizes and pulp density due to progressive depletion of the largest particles from any given pulp level.

Jan 1, 1962

By Robin O. Williams

The textures which are produced by simple shear in poly crystalline samples of copper, brass, aluminum, iron, and zirconium have been determined. For the fcc materials, there are two major textures, both of which are oriented for slip on the usual slip systems. It is shown that each grain will, in general, give rise to both orientations through the production of deformation bands. This is considered a clear demonstration that such bands aye produced by the heterogeneous deformation which takes place instead of the five-slip-system model considered by Taylor. The results on iron and zirconium are more limited but would appear to exhibit certain additional complexities. It is suspected, however, that the general consideration of deformation bands may apply here also. One finds some correlation between the textures produced by this single shear and the conventional textures although it would appear- that additional data and analysis are requived to produce a strong correlation. It is somewhat remarkable that of all the texture investigations only a very few have been concerned with the action of simple shear on polycrystalline aggregates. Of these limited investigations, all used torsional strains and only in Backofen&apos;s&apos; and Backofen and Hundy&apos;s "ork was sampling carried out so as to derive a texture in terms of the shear direction. Some rather remarkable conclusions re- sulted from Backofens&apos;1,2work: 1) the rate of texture formation in copper is high, being almost complete at a shear strain of unity; 2) the texture does not change if the sample is sheared back, although the surface grains return to their original shape; and 3) the texture is complex in that it has four components, three of which have [110] as a shear direction. These conclusions were based on both qualitative and quantitative data. Shear deformation is intermediate in complexity between simple shear of single crystals and the usual deformation of polycrystals; hence, one might expect to learn considerable from the extension of this work. CONVENTION Deformation in simple shear has the lowest possible symmetr3, less than the other simple modes of deformation (rolling, drawing, and compression); hence, one cannot necessarily expect the textures to have the same degree of symmetry. The geometry of the process is represented by Fig. 1 along with its sltereographic projection. One has the shear plane, the shear direction, the mirror plane normal to the shear plane and containing the shear direction, and a neutral plane normal to both the shear plane and mirror plane. These planes divide the projection into four quadrants. These quadrants are not, however, identical, since all directions within the upper left and lower right are being shortened by the shear process, and the other directions are being lengthened. The first kind are called compression quadrants and the direction of greatest contraction rate, at 45 deg, is labeled with a minus sign; the corresponding direction of greatest extension rate

Jan 1, 1962

By D. G. Oss, S. E. Erickson

An automatic control method for the ferrosilicon heavy media process maintains media density within 0.01 specific gravity points. Continued demands for higher grade, competitive products from the Mesabi Range have resulted in experimental work such as that detailed for one concentrator. Various methods, step by step procedures and instruments used at an iron ore beneficiation plant in the development of an automatic control system are described. Work continues and it is hoped that further applications of control instrumentation can be made in the next operating season. The need for instrumentation and automatic control of the various parameters in the heavy media process of iron ore beneficiation has been apparent for some time. Continued demands for higher grade, competitive products from the Mesabi Range have made it necessary to increase the efficiency of the process in every possible way. In a typical heavy media flow scheme for iron ore beneficiation (Fig. 1) a sized, prepared feed (generally about —1% in. to +% in.) is fed to a heavy media separatory vessel, along with a ferrosilicon slurry. A separation of the feed is made on the basis of specific gravity. Low density particles overflow a tailings discharge weir, while high density ore particles sink to the bottom of the high density pool and are moved away to the concentrate discharge chute. Both products are passed over drainage screens and then are cleaned thoroughly of attached ferrosilicon on wash screens. Float material is generally stockpiled, while the sink product is shipped as a final concentrate. Undersize from the drain screens is returned directly to the circulating media sump. Wash screen undersize is cleaned of contaminating ore particles and slimes by passing through magnetic separators. Provision is also made for splitting a portion of the tailings drain undersize into the cleaning circuit if necessary for control of depth of tailings overflow, or for additional cleaning as required. Cleaned ferrosilicon is stored in a densifier and returned to the Circulating media sump as make-up material. Dilution water is also added to this sump to maintain a desired specific gravity of the circulating media. As in any process, operational intelligence is secured only by keeping records of the process variables. Generally apeaking, plant operators have neither the inclination nor the time to keep complete and detailed records of these variables over the course of their shift. Before instrumentation was added to aid the operator, specific gravity was measured by weighing a given volume of pulp at intervals of from 30 to 60 min. Scale readings were made at the beginning and end of each shift. No records were kept of operating conditions, such as rpm of the separatory ves-sel, media level in the machine, tons per hour of the products, and so forth. These items were recorded only when spot checks were made by the metallurgical staff. CONTlNlJOUS DENSITY RECORDING The first process instrument used, other than the usual ammeter on the drive motor of the separatory vessel, was a nuclear density gauge and its associated circular chart recorder. These instruments were used to indicate and record specific gravity of the circulating media. This was a tremendous aid to the operator in that tie was able to observe and correct the specific gravity at any time. There was also added incentive to make frequent corrections because of the permanent record made by the recorder of the densities. The addition of the nuclear density gauge was influential in securing optimum quality and recovery of the heavy media product. Manual control was improved, and it became possible for a good operator to main control within f.05 specific gravity units. This compares with an unknown quantity, estimated at f0.15 gravity units, when manual measurement and control was used. An example of the improvement in manual control over the course of one season&apos;s operations is shown in Fig. 2. Chart A is typical of the records made shortly after the gauge was installed. Needless to say, it was difficult for operators and foremen alike

Jan 1, 1962

By R. J. Sherman, M. R. Achter

IT has often been reported that coatings may strengthen single crystals and polycrystalline specimens of coarse grain size. This note reports the effect of a surface layer of fine grains on the creep-rupture properties of coarse grained nickel 99.8 pct pure. Sheet specimens were machined from cold-rolled material, finished by surface grinding and annealed at 1230°C in vacuum for 4 hr. Half of them were re-ground on faces and sides and annealed at 925"C for 1 1/4 hr. The double grind-anneal treatment produced a structure consisting of a surface layer of fine grains of 0.02 mm diam on a coarse-grained substrate of grains of 0.40 mm diam. Comparison with specimens which received only the single grind showed that the second grind-anneal did not alter the structure of the substrate. Several modifications were made in specimen design to eliminate erratic rupture behavior outside of the gage length. In the final design the gage section, oriented parallel to the rolling direction, was 1.00 in. long, 0.4 in. wide, and 0.0625 in. thick. End tabs were pinned in place. Although other configurations (welded end tabs, transverse orientation, and wider gage section) showed similar effects of a layer of fine grains, because of the erratic rupture behavior, only the data from the final design are reported here. Creep tests were performed at 650°C in air and in a vacuum of 10~5 mm Hg. Creep rates were measured from the movements of the lever arm. Since the broken sheet specimens could not be fitted together, elongations at fracture measured by means of gage marks, do not include the necked portions adjacent to the fracture. Results of the creep tests with and without the fine grained surface are given in Table I. An explanation for the lower strength in air than in vacuum has been proposed previously in terms of the reduction of crack propagation energy by gas adsorption.l In both environments the fine-grained layer produced a small decrease in minimum creep rate and, except for the shortest test in air, a substantial increase in rupture life. The elongation values at rupture, as they are measured here, do not demonstrate an appreciable effect of the grain structure but do show much smaller ductilities in air than in vacuum. Greater elongations maybe associated with the finegrained layer, however, especially in vacuum, in creep curves such as those in Fig. 1. Duplicate tests were not run to determine the re-producibility of the data. It is felt, however, that, in view of the consistent behavior, the prolongation of rupture life may be attributed to the effect of the fine-grained surface. In the data not reported be-

Jan 1, 1962

By H. D. Kline

This paper is one of a series being prepared by the Bureau of Mines on methods, practices, and costs in various mining districts in the United States. The paper describes mining and ore recovery methods common to the Batesville manganese district, Independence County, Ark., and gives the costs of producing merchantable ore by three operators whose methods were more or less typical of those of many other local manganese producers. The operating costs reported were those of Leonard Baxter at mines on Brooks Hill for the calendar year 1958 and Arkansas Mining and Exploration Corp. at Section 16 mine and the Searcy group of mines and Miller-McGee Corp. at the Diener mine during the first 6 months of 1959. Manganese are was mined in the district as early as 1849 and almost continuously thereafter until August 1959, when termination of the Government&apos;s domestic manganese purchase program resulted in complete cessation of mining activity. During those years, production came from more than 189 mines and properties, of which only a few produced as much as 30,000 tons of merchantable ore.

Jan 1, 1962

By L. F. Mondolfo

An investigation of the relationship between properties of the elements and type of binary diagram formed was conducted. It was found that, for each type of equilibrium diagram, the factors for the size, valence, electronegativity, period, melting point, entropies of fusion, and sublimation calculated for each pair of elements cover a range of values. However, these factors show sufficient relationship to the equilibrium diagram so that the correlation of several of them can be used to predict the type of diagram formed, or at least limit the choice to only a few types. ThE goal of the metallurgist concerned with alloy development has always been to find a method that predicts the properties that can be obtained when a certain metal is added to another one. In most cases a qualitative predictiton of properties can be made if the equilibrium diagram is known. However, this means that for new metals the alloy development has to start with the experimental determination of the equilibrium diagrams. Because this determination is at least as complicated and time-consuming as the determination of the properties themselves, most alloy development has taken place by trial and error, and the study of the equilibrium diagrams has followed rather than preceded the creation of new alloys. Alloy structures and properties depend on the interaction between electrons and a complete knowledge of these interactions would permit prediction of structure and properties of alloys. Unfortunately direct measurement of these interactions is extremely difficult and somewhat doubtful and only properties that depend on them can be measured easily and with certainty. Study of the relationship between properties of the elements and equilibrium diagrams is not new. Besides the well known Hume-Rothery rule of the necessity of an atomic diameter fit within 15 pct for extensive miscibility in the solid, and the wide knowledge of the effect of such factors as size, electronegativity, electron-atom ratio on solid state features,"&apos; work relating to liquid state and liquid-solid reactions can be found in the literature. Of particular interest is the work by Axon,3 who investigated the effect of size and melting point on a selected number of eutectic and monotectic dia-

Jan 1, 1962

By R. E. Steiner, A. F. Weinberg, R. J. Van Thyne

Uranium solubility in molten bismuth was determined in the temperature range 350" to 600°C, varying from 0.09 wt pct to near 2 wl pct, respectively. Zirconium and magnesium, simulated fission products, and sodium were found to increase or decrease uranium solubility in bismuth in the temperature range 370° to 420°C, depending upon the addition or temperature. Data were obtained by both chemical analysis of samples obtained by filtration from saturated melts and by measurement of the variation of electrical resistance with temperature. IN a study for the United States Atomic Energy Commission, a Liquid Metal Fuel Reactor Experiment (LMFRE) was proposed in which a solution of uranium dissolved in molten bismuth served as both the fuel solution and the primary coolant. It was proven necessary to add other elements to this solution for certain desirable properties: 1) zirconium acts to prevent reaction of the fuel solution with the graphite core (which would result in the formation of uranium carbide) and also to inhibit mass transfer of iron and chromium from the walls of the reactor tubing to cold spots resulting in blockage; and 2) magnesium acts as a deoxidant and prevents loss of uranium. In addition to these intentional additives, other elements entering the solution are: 1) fission products which are a by-productof reactor operation, 2) sodium (the secondary coolant) through possible small leaks in the heat exchange system, and 3) iron and chromium from the container walls. Each of these elements may affect the solubility of uranium in the fuel solution. Since the concept of this reactor is based upon a liquid solution, the relatively low solubility of uranium in bismuth will dictate the minimum temperature at which the reactor heat exchanger can be operated. The solubility of uranium in liquid bismuth and the effect of some additives on this solubility have pre- viously been investigated1-&apos; (more recent results6" became avaliable after initiation of this investigation). However, some discrepancies between the various results have been noted, and also the cumulative effect of the several additions or impurities was not known. This investigation was commenced to obtain definitive results. MATERIALS Analyses of the materials used are presented in Table I. Although ostensibly of extreme purity (99.999 wt pct), the bismuth was found to contain a significant amount of impurities, probably oxides. Except for determination of the binary system, Bi-U, prior to use all bismuth was hydrogen-refined and

Jan 1, 1962

By G. K. Manning, E. R. Stein, E. E. Underwood

Columbium, carbon. and nickel additions were made to iron-base alloys with 20 pct CY. The effects on microstructure, precipitation-hardening characteristics, and High-temperature properties were investigated by means of metallographic, hot-hardness, and magnetic measurements. An austenitic alloy consistilzg of Fe-20Cr-14Ni-0.8C-2.5Cb had higher hot-lzaciness at 1700°F than the other alloys investigated. Its favorable standing is attributed to an enhanced interaction of Cb and Cr4C particles dispersed within a stable austenitic matrix. FOR the past 20 years, cobalt- and nickel-base alloys have been used for the more stringent high-temperature applications because of their excellent creep resistance. Although their performance is quite satisfactory, other base materials must be considered for large tonnage, low-cost applications such as for the automotive gas turbine. Iron-base alloys are also used extensively, but at somewhat lower temperatures, primarily because of the instability of particles or because precipitation occurs at relatively low temperatures. Since unusual stability has been reported for Fe-Cb and Cb-C compounds.1-3 it was hoped that effective amounts of these compounds could be taken into solution at temperatures just below the melting range, then precipitated upon reheating. Actually, strengthening was found to occur by both precipitation hardening in some alloys and by phase transformations in others. Among the alloys investigated, that with the best high-temperature properties owes its strengthening to a combination of carbide particle interaction and a relatively stable austenitic matrix. EXPERIMENTAL PROCEDURES Small preliminary melts of about 100 g were made in a vertical Glotube furnace, using alundum crucibles and an argon atmosphere. Alloys weighing 35 lb were melted in a basic-lined induction furnace, also under argon. The compositions of the alloys are given in Table I. The nickel-free alloys were usually ferritic, while those containing nickel were generally austenitic. Depending upon the particular heat treatments, or the combination of alloying elements, two-phase alloys of ferrite and austenite could be obtained. In the following text, however, the nickel-free or nickel-bearing alloys are referred to simply as either ferritic or austenitic alloys respectively. The small ingots were swaged at 2000°F, in steps, to rods of approximately 3/16-in. diam. The large ingots were forged at 2100°F to 1-in. sq bars. No difficulties were encountered in swaging or forging any of the alloys to as much as 90 pct reduction in area. For heat treating at temperatures above 2000°F, specimens were sealed in quartz tubes under a partial pressure of helium. No special precautions were found to be necessary at lower temperatures. Intermetallic compounds in the preliminary alloys were identified by means of X-ray diffraction measurements. Correlation of these results with micro-structural characteristics (such as color, shape, size, and location) of the compounds aided in their identification. Magnetic susceptibilities were also obtained at room temperature with a Magne Gage instrument after the various heat treatments. To

Jan 1, 1962

By H. I. Aaronson

Isothermally formed plates of proeutectoid a, lengthen at approximately the rates predicted by the Zener-Hillert equation, indicating that their lengthening kinetics are controlled by the volume diffusion of chromium in the ß matrix. Solution annealing treatments in the vicinity of the transus introduce a second mode of transformation, in which the lengthening rate is at least 1.8 x 104 faster than predicted by this equation. Little or no volume diffusion appears to accompany the latter transformation. The Presence of oxygen is evidently a Prerequisite for the occurrence of this reaction. X HE effects of thermal history prior to the initiation of transformations which proceed by nucleation and diffusional growth are currently evoking considerable interest. The rate of nucleation (but not the rates of growth) of pearlitel and of bainite,2 and the over-all rates of aging reactions in Al-cu3 and Al-si4 alloys have been shown to be appreciably dependent upon thermal history in the solid-solution region"&apos; or in the two-phase region prior to the onset of pre~ipitation.3,4 In none of these reactions, however, was the transformation mechanism changed by variations in the temperature-time path used to reach the reaction temperature. Preliminary experiments reported by M. K. McQuillan5,8 and a systematic investigation by Farrar and Margolin7 have disclosed that the transformation behavior of hypoeutectoid Ti-Cr alloys is considerably more sensitive to thermal history. Qualitative evidence strongly suggests that not only the rate of nucleation but also the rate of growth and even the mechanism of the ß — a reaction can undergo remarkable changes when a solution annealing treatment in the vicinity of the ß/a +ß, or transus temperature, is interposed between a high-temperature solution anneal (conventionallq at 1000°C) and the isothermal reaction treatment. The present investigation was undertaken in an attempt to ascertain the nature and origin of these effects. Study of the changes in the kinetics and morphology of the ß - a, reaction produced by varialtions in thermal history was the primary means employed for this purpose. EXPERIMENTAL PROCEDURE The compositions of the alloys used in this in~esti~ation are given in Table I. These alloys were homogenized for 5 days at 1050° C in evacuated (2 x 10 -5 mm of Hg), zirconium-gettered fused quartz capsules. The capsules themselves were enclosed in a porcelain chamber evacuated with a mechanical pump during the homogenization anneals. Upon completion of homogenization, the alloys were cooled to room temperature and then reheated to 550°C for 3 1/2 days in order to transform the alloys to a finely divided mixture of a and TiCr2, and thus provide an approximately constant initial mi-crostructure. Individual specimens were sealed in evacuated and internally gettered Vycor capsules and heat treated as previously described.8,9 EXPERIMENTAL RESULTS Ti-10.64 Pet Cr. This investigation was largely performed on the 0.64 pet Cr alloy. The "base"

Jan 1, 1962

By E. P. Abrahamson

The effect of transition element binary solid solution additions upon the recrystallization temperature of titanium has been investigated. All additions, except columbium and tungsten, raised the recrystallization temperature. A correlation is obtained between the logarithm of the absolute rate of change of recrystallization temperature with atomic percent solute and the number of uuter d shell electrons attributed to the free atom of the solute element in its ground state. The work of Abrahamson, et aL.1-6 on dilute binary solid solution alloys indicated a correlation between the free atom ground state electron configuration of the solute and both the brittle-ductile transition and recrystallization temperature. It is shown in these studies that the number of outer s and d electrons in the solute are of prime importance in determining the absolute rate of change of recrystallization or transition temperature with composition. Furthermore, the limit of initial linearity (in the curve of recrystallization temperature vs at. pct solute) has been shown to be a function of the number of d shell electrons in the solute for dilute iron- and vanadium-base alloys. To date no complete systematic recrystallization study of dilute binary titanium base alloys has been made. This study together with that of zirconium base alloys 6 will provide the data for the comparison of the effect of the same solutes upon two solvents with the same number of outer d shell electrons.

Jan 1, 1962