By H. Herman, M. E. Fine

Kinetics of reversion and reformation of GP I were studied resistometrically in Al-1.7 at. pct Cu. The reversion process is over in roughly 1/2 minute at 205 "C irrespective of the amount of primary aging. After reversion the occurrence of an incubation time before reaging begins has been substantiated. The reaging kinetics is drastically accelerated by plastic deformation to the specimen. An incubation time is observed only if the specimen is aged before reversion. The incubation time and the effect of plastic deformation indicate that nucleation of GP I is heterogeneous. Simple clusters of copper atoms apparently do not act as nuclei for GP I. AFTER quenching aluminum-rich copper from the solid solution range, Guinier-Preston zones of the first kind, GP I, form very rapidly at room temperature. The rate, largely controlled by the concentration of vacancies, is initially most rapid1 (that is, at the time of the first measurement: 1/2 min) and decreases with time. The nucleation is thought to be athermal. If after aging for several days the GP I is dissolved by reversion at 205°C, according to measurement of Young's modulus an incubation period is observed before GP I begins to form on subsequent aging.2 Yet if the reversion is carried out immediately after quenching, both resistivity3 and modulus changes2 show no incubation effect. The zones which form after reversion have the same structure as those which form after the quench.4 Because of entropy considerations and also the short diffusion time, the solid solution after reversion, 2 min at 205°C, is probably more highly clustered than at the original solution treating temperature, 520" to 550°C. It appears most reasonable to associate with nucleation the incubation time observed on reaging after reversion. A simple cluster of copper atoms, many of which are presumed to be present after reversion, is then not a sufficient nucleus for GP I; a GP I nucleus must contain something in addition to a cluster of copper atoms. The purpose of the present note is to give some additional experimental information concerning the incubation time and rates of reaging after reversion. The existence of the incubation time has been verified by measurement of another property, the electrical resistivity. Acceleration of reaging after reversion by plastic deformation has also been investigated. In acl.dition, the kinetics of the reversion process itself was studied. EXPERIMENTAL Electrical resistance was measured by the poten-tiometric four probe method. The 1.7 at. pct Cu alloy was furnished by the Aluminum Co. of America in the form of 1/2 in. rod. The major impurities reported by Alcoa were Fe (0.002 wt pct), Si (0.003 wt pct), and Mg (0.001 wt pct). Specimens for measuremenl of resistance were prepared by rolling to 0.010 in., cutting 2 by 0.2 in. pieces, rolling the middle pclrtions of these to 0.005 in., and splitting the 0.010 in. sections up to the reduced central section to form current and potential leads. Aluminum extension wires insulated with ceramic tubes were spot welded to the leads. The specimen was supported by the lead wires. The whole specimen assembly was annealed at 500" C in an air furnace for more than 12 hr and then aged at room temperature. This was done to assure quick and complete resolution during subsequent solution treatments. These were carried out in Houghton's "430 Temper Salt" at 520'C for 1 hr. Unless otherwise specified, quenching was accomplished by quickly transferring the specimen from a salt pot to 25°C water. Aging was carried out in a 3 liter dewar of distilled water, rotated and stirred. The temperature was controlled to +0.01°C with a thermomercurial regulator in conjunction with a transistorized relay

Jan 1, 1962

By Milton E. Wadsworth, R. Ted Wimber

Cobalt sulfate solutions containing ammonium acetate and chloroplatinic acid were reduced by hydrogen in a pyrex-glass lined autoclave in the temperature range of 170o to 232°C and hydrogen partial pressure range of 115 to 830 psia. The reduction rate was directly proportional to the hydrogen partial pressure and surface area of the pyrex glass and was independent of the quantity of chloroplatinic acid added initially. Experiments involving the variation of the relative concentration of ammonium acetate indicated that the reducible cobalt complex was probably the diacetate complex of cobalt, Co(AC)4H20, or a new mononcetate complex Co Ac, which was in solubility equilibrium with a pink precipitate of CO(AC)-4HzO. THE reaction in which a metal is dissolved by an acid to produce gaseous hydrogen and a salt solution was discovered early in the history of chemistry. In 1859 Beketoff found experimentally that this reaction could be reversed; i.e., a salt solution could be reduced by gaseous hydrogen to produce a metal and an acid. A review of work done on this phenomenon since that time may be found elsewhere., The hydrogen reduction of a cobalt salt solution is facilitated by complexing the cobalt ion. An ammonia complex of cobalt has been reduced commercially in the recovery of cobalt metal. A new reducible complex of cobalt was discovered5 when it was found that a co-baltous sulfate solution containing ammonium acetate could be reduced by hydrogen at temperatures in the region of 200°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature below its normal boiling point, a violet color became apparent, indicating complex formation. The nature of this complex was investigated5 by the addition of NH4Ac to a CoSO4 solution maintained at 85o. During the first additions of NH, Ac, the pH of the solution remained fairly constant at about 5.85. However, as the ratio of NH,Ac to CoSO, approached two, the pH rose and then leveled off at about 6.05. The absorption spectra of a Co(Ac), solution and a CoSO,, NH Ac solution were obtained at 85°C and were compared and found to be the same. These findings suggested that the diacetate complex of cobalt, Co(Ac),.4H20, was formed at 85°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature above about 165o, a finely divided pink precipitate appeared. The X-ray diffraction pattern of this precipitate indicated that it was Co(Ac), - 4H,O. In addition, it was discovered that when chloroplatinic acid, H,PtCl;, was added initially to the cobalt sulfate-ammonium acetate solution, a faster reduction was obtained. The roles of the solution complex, pink precipitate and chloroplatinic acid in the reduction process were then investigated. APPARATUS The experimental work was carried out in a two-liter stainless-steel autoclave. Adetailed description of the autoclave and the auxiliary equipment used in maintaining constant temperature and pressure may be found elsewhere.= Because the stainless steel was corroded, and also because it acted as a hydrogena-tion catalyst, an all-glass liner was fabricated such that the solution came only into contact with flame-polished pyrex glass. EXPERIMENTAL PROCEDURE The solutions used in the experimental work were prepared by dissolving reagent grade chemicals in distilled water. Although variation of the brand of ammonium acetate appeared to have no effect on the experimental results, CoSO, 7H O from the J. T. Baker Chemical Co. of Phillipsburg, N. J.,was found to give faster reductions than that prepared by Allied Chemical and Dye Corp., N. Y. The former was used throughout the course of the experimental work and was weighed up at the outset of each experiment. The ammonium acetate was dissolved to form a 6M stock solution, which was stored under refrigeration. A 10 pct solution of chloroplatinic acid (J. T. Baker Chemical Co.) was diluted to a 1.15 x 1Q2 M stock solution, which was standardized by precipitation of K,PtCl, as outlined by Scott. The appropriate volume of the chloroplatinic acid, H,PtCl,, solution was pipetted into the clean, dry glass liner. The cobalt sulfate-ammonium acetate solution, which had previously been saturated with

Jan 1, 1962

By Larry Kaufman

A useful method for estimating the entropy of NaCl type compounds has been developed by combining the Debye theory of specific heat with the Lindemann formula. This method pemnits calculation of the entropy from a knowledge of the atomic weight, atomic volume, and melting point of the compound. Comparison of the calculated and observed entropies of 35 NaCl type compounds over a wide temperature range yields good agreement thus establishing the usefulness of the method. Application of the method to other crystal types is also discussed. KUBASCHEWSKI~ has suggested a useful method of estimating the enthalpy of formation of inter-metallic compounds from a knowledge of the crystal structure, lattice parameter, and heats of sublimation of the component elements. This method is quite valuable in predicting the tendency for compound formation in a given system and is of particular value in considering systems for which no experimental data are available. In order to supplement the enthalpy calculation afforded by Kubschewski's method, it would be of value to be able to estimate the entropy of compounds so that the entropy and free energy of formation could be evaluated. Although a considerable body of such data determined by calorimetric and equilibration techniques exists at present, the difficulty of making such measurements (particularly at high temperatures) and the ever increasing number of new compounds which are of interest make the desirability of such a computational method clear. This paper deals with a method for calculating the entropy of a compound from a knowledge of the atomic weight, atomic volume, and melting point. Since these data are generally easier to determine and therefore more readily available than thermo-dynamic data, they should provide an additional tool in estimating the stability and reactivity of compounds at high temperatures. I) THE ENTROPY OF PURE METALS As a first approximation, the specific heat of a pure metal can be represented by a sum of terms where C,($/tI is the vibrational specific heat calculated on the basis of the Debye theory, lo4 TC, (0/T) is an approximation to the Cp - C, correction. T is the electronic specific heat, and Cp (p) is the magnetic specific heat. Although the Debye theory does not provide a complete description of the vibrational specific heat, i.e., the Debye temperature 0 is not a constant, it does provide a good approximation when used properly. Blackman6'7 has written several reviews on this subject discussing the different values of 0 determined by various methods (specific heat, X-rays, elastic constants, electrical resistivity, and so forth), as well as the observed temperature dependence of 0 with T. In the present case the 0 in Eq. [I] naturally refers to the specific heat 0. The variation of Debye 0 (as determined from specific heat measurements) with temperature is observed to exhibit its most radical behavior at very low temperatures. At higher temperatures the 8 values are observed to become more nearly constant. Blackman6'7 has presented the variation of 0 with temperature for several metals. His tabulation is reproduced in Table I. Reference to Table I shows that above a certain temperature level, 0 remains fairly constant. The value of 0 which is most useful in computing the specific heat, and hence the entropy, is the value of 0 in the range 0/6 « T « 0. In 1910, Lindemann' suggested a relation for estimating Debye 0 values. According to this formula, where V is the atomic volume, T is the melting point in 'K, M is the atomic weight, and CL is a constant. Mott and Jones9 present this formula and state that there is at present no satisfactory theoretical explanation, but that it does have an empirical basis. By using the valuesof 0 in Table I along with known1' values of M, T, and the molar volume VM, where the Lindemann constant can be evaluated. This

Jan 1, 1962

By Per Kofstad, Hallstein Kjöllesdal

The oxidation behavior of niobium (columbium) has been studied in the temperature range 500° to 1200°C and at oxygen pressures of 760,100, 10, 1, and 0.1 mm of Hg. The work comprises kinetic studies of the oxidation as well as structural investigations of the oxidized specimens by means of X-ray diffraction, electron diffraclion, electron microscopy, and metal1ographic techniques. The oxidation reaction has a highly irregular temperature dependence and is unusually sensitive to changes in the oxygen pressure. The complex oxidation behavior is suggested to be due to formation of different Nb2O5 modifications in different temperature regions. During oxidation oxygen is also dissolved in the metal. Formation of oxide whiskers take place on the oxide surface at temperatures above approximately 800°C. VARIOUS aspects of the oxidation of niobium have been studied.l-12 The investigations show that niobium has a complex oxidation behavior, and the oxidation

Jan 1, 1962

By Gerald W. Elger

This report compares the quality of zirconium metal prepared by batch reduction of zirconium tetrachloride by (1) sodium, (2) magnesium, and (3) mixtures of sodium and magnesium. Criteria for quality are based on chemical analyses and hardness testing of zirconium arc-melted from sponge. The best quality zirconium with respect to low oxygen content and hardness numbers was prepared by reaction of zirconium tetrachloride with a mixture of sodium and magnesium. It was found that this reaction could be successfully carried out by two methods: (1) addition of sodium and magnesium before the initial reaction and (2) periodic injection of sodium during reaction of zirconium tetrachloride with magnesium. The largest quantity of metal was found to be recovered from experiments in which a mixture of sodium and magnesium was used. Magnesium appeared to be a better reductant than sodium because magnesium-reduced zirconium contained less oxygen and exhibited lower hardness numbers than sodium-reduced metal.

Jan 1, 1962

By A. T. Aldred

HIS note reports the existence of several new scandium intermetallic compounds of the A2B and AB stoichiometries where the A element is scandium and the B element is from group VIII or IB of the periodic table. Alloys were arc melted from high-purity materials using 2-g charges. Typical lot analyses for the materials used are given in Table I. Chemical analyses were not made on the alloys as there was little or no weight loss on melting. After annealing the specimens for 14 days at 600°C and water quenching, metallographic and X-ray techniques were used to determine the occurrence of the various phases. Table II lists the relevant data for the A2B phases. The Ti2Ni structure,2 has ninety-six atoms in a face-centered cubic cell, whilst the Al2Cu structure is body-centered tetragonal.3 The occurrence and stability of the various A2B type phases in transition metal alloy systems has recently been considered by Nevitt.4 The Ti2 Ni-type phases occur over a relatively narrow range of radius ratios from 1.14-1.26 with A partners mainly from the titanium group and B partners predominantly from the cobalt group. This suggests that both a favorable relative size of the atoms and a favorable electron concentration are necessary conditions for the existence of this structure type. A12Cu-type phases involving Ti group elements as A partners are formed with B partners from the cobalt and nickel groups, predominantly the latter, and have a higher radius ratio (1.27-1.29) than the Ti2Ni-type phases. The occurrence of both Sc2Pd and Sc2Co can be rationalized in terms of these considerations but SczNi is anomalous because of its high radius ratio. The radius ratios are calculated from the Goldschmidt CN12 radii and it might be postulated that the scandium atom is reduced in size in the compound. Unfortunately the apparent atomic size of scandium in the compound cannot be calculated from a knowledge of the structure and lattice dimensions. The crystal structure of the Sc2Au compound could not be identified from the powder diffraction pattern, but it is interesting to note that it is isostructural with a series of A2Au phases where A is a rare earth element.5 Pertinent information concerning the AB phases found in this investigation is given in Table 111. All the phases have the ordered bcc CsCl structure. The occurrence and stability of CsC1-type phases have recently been discussed by Dwight,7 who concludes that the relative sizes of the atoms do not appear to be a controlling factor (the radius ratios of all the known phases vary between 0.985 and 1.439) but that the occurrence of the phase is predominantly dependent on the relative positions of the A and B partners in the periodic table. As a measure of the stability of a given CsCl phase it has been customary to define a lattice contraction on alloying, DAB — dAB, where DAB is the AB interatomic spacing as calculated from the Goldschmidt CN8 radii and dAB is the AB interatomic distance in the compound (= v3/2 ao). Values of the parameter DscB -dScB for the compounds found in this investigation are given in column 5 of Table III and are plotted in Fig. 1. If the lattice contraction does in fact reflect the stability of a phase then Fig. 1 shows two very interesting trends when the position of the B partner in the periodic table is considered. Firstly, within any given group the stability increases in order on going from the first to third long period. Secondly, within any given period the stability increases in order as the B partner is taken from the copper, nickel, and cobalt groups. In the case of the second long period, the lattice contraction reaches a maximum at ScRh and then decreases to ScRu. The same trend could

Jan 1, 1962

By C. S. Boland

The Copper Range Company's mining properties are located in the Upper Penisula of Michigan. (Fig.). Early work indicated the presence of copper ore in a bedded deposit, confined to the base of the Upper Keweenawan Nonesuch shale, and exploitation of this deposit on a portion of the Company's property was undertaken by White Pine Copper Company. Diamond drilling of the White Pine orebody indicated that a major fault pattern terminated the values to the South-west. Further drilling Southwest of the fault zone proved a downward displacement of the ore bearing horizon some 1,500 feet and a lateral displacement of approximately 4,000 feet; and in this area an ore deposit was outlined in a large asymmetrical syncline locally plunging to the South-west. (Figs. 2 and 3)

Jan 1, 1962

By John C. Sawyer

A brief review is given to show that catastrophic oxidation of stainless steel in the presence of lead oxide is similar in many respects to catastrophic oxidation as caused by MoO3 and V2O5, Experimental data are presented to show that lead oxide accelerates the normal oxidation process of stainless steel by chemically altering the normally protective oxide film formed on the base metal. Data are given to show that similar reactions occur during oxidation of stainless steel in the presence of MOO3,and V2O5. THE mechanism by which pure metals oxidize at high temperatures has been the subject of intensive research for many years and much has been accomplished towards understanding the processes involved. The mechanisms by which alloys oxidize have also been investigated, but due partly to the fewer number of investigations and partly to the complexity of the oxide systems present, available knowledge is not as extensive as with pure metals. When oxidation processes are further complicated by atmospheres contaminated with sulfide, halide, or oxide vapors, the knowledge of fundamentals becomes meager or altogether lacking. Thus, it is not surprising to find that the catastrophic oxidation of stainless steels in metal oxide vapors of MOO, and V2O5 is not a well understood phenomenon despite the fact that a number of investigations have been undertaken. The literature in dealing with the subject of catastrophic oxidation is primarily concerned with the effects of MOO3 and V2O5, but does mention that other metal oxide vapors, one of which is lead oxide, appear to promote a similar type of accelerated oxidation. While this latter effect is virtually unknown, the deleterious effect of lead oxide is of considerable commercial importance, as it is believed to be one of the fundamental reasons for exhaust-valve failure in gasoline engines. For this reason studies have been in progress for many years attempting to better understand the mechanism involved. Modern exhaust-valve alloys"2containing 20 to 25 pct Cr plus nickel and/or manganese are in effect high-grade austenitic stainless steels exhibiting ex- cellent oxidation resistance in air at exhaust valve operating temperatures of 1100° to 1700°F; yet these same alloys are prone to corrode during engine service because of the conditions attending their operation. These conditions are such that the valves become coated with deposits of complex lead compounds mainly derived from gasoline additives of tetraethyllead, ethylene dibromide, and ethylene dichloride. Literature searches3-7 and discussions with various investigators show that considerable difference of opinion exists as to the nature of the lead-bearing deposits found on the surface of exhaust valves and the atmospheres to which they are subjected; yet, all seem to generally agree that corrosion, a gradual transformation of alloy to nonmetallic products of corrosion, is a consequence of the presence of lead compounds. This majority opinion seems to be substantiated by laboratory engine tests which show that corrosion does not occur to any appreciable extent when lead-free fuels are used. The first observations of catastrophic oxidation reported in the literature were probably made by pfeil,8 but it was Leslie and Fontana9 who undertook the first detailed study of the phenomenon. Their work was chiefly centered on the acceleration of oxidation which took place when stainless steels containing more than 3 pct Mo were heated in air with restricted circulation. These investigators reported that the presence of other oxides near the surface would further accelerate the rapid oxidation which occurred. While they recognized that the effect was attributable to the presence of molybdenum, it was Rathenau and Meijering" who emphasized the fact that the presence of molybdenum in the alloy was incidental to the presence of MOO3 vapor in the atmosphere surrounding the specimens. Evans,11 as well as Cunningham and Brasunas 12 studied similar

Jan 1, 1962

By William J. Campbell

Evaluation by the Bureau of Mines of published expansion values for magnesium oxide shows significant variation in values, which may be attributed to sample variables, experimental errors, or systematic differences between measuring techniques. To eliminate the sample variable in measuring expansion, thermal expansion characteristics of a high-purity polycrystalline magnesium oxide were determined by 21 cooperating laboratories using one or more of the following techniques; X-ray camera, X-ray diffractometer, dilatometer, interferometer, and telemicroscope. All expansion values were corrected by the author to a single reference temperature of 25° C. Linear expansion was expressed as a power series in the form of the following equation. Expansion (percent) = [[ A + B (?t) + C (?t)2] ?t 104] The constants, A, B, and C, were determined by least square techniques for X-ray camera, X-ray diffractometer, and dilatometer data separately, and for combined data of all five techniques. Expansion values are tabulated from 26° C. to 1,400° C. in 2° C. intervals using constants derived from X-ray camera data. Below approximately 500° C., expansion values obtained by dilatometric and interferometric methods are significantly lower than those by X-ray methods; above 500° C., this bias decreases rapidly. Comparison of results within methods showed the least variance for X-ray camera results; dilatometer and X-ray diffractometer results have about the same variance. The average deviations, in percent, between observed and calculated expansion values among methods were approximately 10 percent from 100°C. to 300°C., 5 percent from 300°C. to 500°C., and 2 percent from 500°C. to 1,400°C. Maximum deviations were approximately twice as large in most instances.

Jan 1, 1962

By E. J. Yoder, N. B. Aughenbaugh, R. B. Johnson

Mineral aggregates experience degradation during field and laboratory compaction. Reduction in the aggregate size is accomplished by abrasion of the particle edges and fracturing of individual pieces which have become overstressed. Little is known of the factors that govern the amount of breakdown experienced for a given situation. A field study was made of the factors affecting aggregate breakdown under compaction using three carbonate aggregates of different physical properties. The preliminary results indicate that rock type, compactive effort, gradation, and thickness of compactive layer are factors which exert the greatest influence. Mineral aggregates experience a mechanical breakdown of some of the aggregate pieces into smaller fragments during any compaction process, whether in the field or laboratory. This phenomenon occurs as abrasion of the sharp edges during movement and reorientation of the particles in densifying and/or as granulation and fracturing of those pieces which have become overstressed. Two types of aggregate breakdown occur in the field. These may be classed in a general category of aggregate degradation.* One occurs during the con- * Aggregate degradation has been defined in many different ways. For this paper it is considered as any breakdown of larger particles into smaller ones, whether mechanical or chemical. struction period and is related to the densification of the aggregate body from a loose state to a relatively dense mass by heavy compaction equipment. This type is almost entirely a mechanical action. The other occurs after the construction period when the roadway has been put into use. This in-service breakdown is; a different phenomenon from the breakdown during construction in the sense that it combines mechanical with chemical changes. Time becomes an important consideration that may cause subordinate factors in construction degradation to develop into principal ones for in-service breakdown. Breakdown of aggregates in service has been extensively studied by investigators from the northwestern

Jan 1, 1962

By R. J. Wasilewski

The resistivity of single crystal and of polycrystalline metal has been determined between 77° and 1500°K. At comparable purity, the resistivity of the poly crystalline metal differs from that calculated from the axial resistivity values. The observed anisotropy is briefly discussed. A zone refined titanium rod was obtained from F. J. Darnell.1 The hardness of this material varied between 52 and 64 Bhn, indicative of its high purity. Single-crystal specimens were cut out from a few large grains, elongated predominantly along <1120>. Resistance measurements were taken with specimens immersed in liquid nitrogen, solid CO,, and acetone, and at ice point, and then recorded continuously between room temperature and 1200" to 1250°C, throughout at least one full heating and cooling cycle at a rate of l° to 3°C per min. Four probe measurements were taken using spot-welded Pt wire 0.003 in. in diam as potential terminals, and the electromotive force drop was determined poten-tiometrically. A standard resistance, in series with the specimen, served to determine the dc current (generally about 80 ma) in the circuit. In order to eliminate spurious thermal electromotive forces, the circuit polarity was automatically reversed at 5-min intervals, and the mean of the two adjacent readings taken as the true electromotive force value. The discrepancy between the readings at reversed polarities was generally of the order of a few µ v, as all the spot-welded joints were contained within a volume of some 5 mm cube. The relative resistance (R T/R 273o) variation with temperature is tabulated below, and shown in Fig. 1, as measured during the first heating run. The discontinuous drop in resistance, corresponding to the a — ß transformation, started for both initial orientations at 1170°K; i.e., some 15°K above the accepted value of 882°C (1155°K). Judging by the temperature ranse of transformation—some 30°K for the single crystal and 20°K for the polycrystal-line specimen—this difference is believed caused by the solution of the oxygen present initially on the surface of the specimens. The general trend of the resistance vs temperature shown in Fi,;. 1 is in qualitative agreement with that previously reported for polycrystalline titanium metal. 2,3 Significant anisotropy is, however, indicated by the crossing over of the curves for <1120> and <0001> orientations at 273°, 650°, and 1000°K. This difference is most startlingly shown in Fig. 2, where instantaneous temperature coefficients (l/R273 x dR /dT) are plotted for both the first heat-

Jan 1, 1962

By David J. Mack, Chin Bea Kim

The decomposition of the Ni-Zn eutectoid at 56 wt pct Zn was studied by isothermal transformation. Its progress was followed by metallographic, hardness, and X-ray diffraction methods. Three transformation products were found: lamellar pearlite at high temperatures; an intermediate temperature structure; and martensite at the lower temperaCures. No transition structu,ves were found. THE decomposition of the Ni-Zn eutectoid at 56 wt pct Zn was stuadied as part of a long-range program of study on the eutectoid transformation in alloy systems which do not have one or more components which exhibit allotropy. Available information on the Ni-Zn eutectoid transformation is limited to that presented in connection with the determination of the phase dilagram. No systematic studies of the eutectoid were found in the literature, alkhough the microstructures of the Ni-Zn eutectoid were reported by Tamuru.3 X-ray diffraction data exist for the ß, ß1, y , and y1 phases.&apos; EXPERIMENTAL PROCEDURE The eutectoid alloy was prepared from "A" nickel shot and Bunker Hill super-purity zinc (99.998 pct).

Jan 1, 1962

By Oliver C. Fursman

These investigations were conducted to determine conditions for recovery of nickel and copper from Funter Bay, Alaska, sulfide ore and recovery of nickel from nickel-silicate ore, Nickel Mountain, Riddle, Oreg. Samples of Funter Bay cupriferous and nickeliferous pyrrhotite ore, were treated by beneficiation, roasting, electric smelting of roasted are for matte production, chlorination, leaching, and sulfatizing roasting with subsequent leaching. Funter Bay and Nickel Mountain ores were smelted together to produce matte. Total sulfide flotation, followed by magnetic separation of the tailings to recover entrained nickel-bearing pyrrhotite, resulted in the highest nickel recovery in beneficiation tests on Funter Bay are. Overall beneficiation resulted in recovery of 98.5 percent of the copper and 95.4 percent of the nickel in the concentrate that contained 3.5 percent copper and 1.7 percent nickel.

Jan 1, 1962

By A. M. Gaudin

In the first place, let me thank you for inviting me to appear before you today to speak to you on "Mineral Industry Problems - Present and Future". It is a distinguished honor for me to have this opportunity, and I am highly appreciative of this distinction. The beautiful surroundings of Gatlinburg and the pleasantness of a summer occasion are a wonderful tonic for all of us, yet they should not blind us to the seriousness of our Industry&apos;s problems No doubt, because of my past appearances before members of the Society of Mining Engineers, at which I discussed wholly scientific topics, or research in the Applied Sciences, you may be expecting me to revert to these subjects. But I intend to venture in a field that is new to me, yet old to all of us, the field of Economics.

Jan 1, 1962

By Charles Wurms, Robert Steinitz

DURING an investigation to determine the compatibility of several metals with tungsten, the degree of reaction between tungsten and lead was determined. A literature survey showed considerable disagreement between the results of various earlier investigators. Information presented by M. Hansen1 states that, according to S. Inouye,2 tungsten has very poor resistance against attack by molten lead, even at the low temperature near the melting point of lead. A phase diagram in the same reference indicates a solubility of 30 wt pct W in molten lead at 1300°C. Contrary evidence was shown by Parkman and shepard3 in their investigation of materials for use in heat transfer systems containing liquid lead alloys; they performed experiments at 980°C for times up to 50 hr without noticing any appreciable attack on the tungsten. Tungsten sheet was immersed in molten lead contained in Vycor tubes evacuated to at least 10-4 mm Hg. R. Bernard4 and R. I. Jaffee5 also indicate that no reaction occurs between molten lead and tungsten. However, no experimental data were included in these reports. In order to settle the question of the solubility of tungsten in molten lead, tungsten powder with an average Fisher subsieve particle size of 6µ was pressed in a double-acting die at 6 tsi to small compacts. They were then sintered in an atmosphere of hydrogen for 2 hr at 1700°C, resulting in a sintered density of 64 pct of theoretical with final dimensions of 0.260 in. in height and 0.245 in. in diameter. For all tests, the tungsten pellets were immersed in molten lead. Table I is a summary of the experimental procedures showing atmospheres, temperatures, and times. The first experiments were performed at 650°C; at this temperature, the liquid lead should wet the porous tungsten better than at its melting point, and penetrate into the pores. The lead was heated in a graphite crucible with a graphite cover. No protective atmosphere was used, as it was expected that the formation of CO would be sufficient to prevent oxidation. This, however, proved to be wrong, and all tungsten samples showed a slight oxide film after treatment. The tungsten samples were immersed in the molten lead for times of 5 min, 10 min, 1/2 hr, 1 hr, and 2 hr. After this time, the melt was poured into a form and the

Jan 1, 1962

By Robert D. Pehlke, Arden L. Bement

A mass transfer coefficient for the removal of hydrogen from liquid aluminum by inert flush degassing has been determined experimentally at 700°C. A mathematical model has been derived, assuming transport control, which adequately describes the experimental data. The removal of hydrogen is shown to increase with decreasing bubble size, and with increasing flow of flushing gas. The presence of hydrogen in liquid metals in amounts which exceed the solid solubility at one atmosphere hydrogen pressure is highly undesirable, causing unsound ingots or castings, or resulting in difficulties during further fabrication. The removal of hydrogen from liquid metals can be accomplished by several methods, the principal two being vacuum treating and inert flush degassing. The design of a process involving either of these techniques is based on the mass transfer coefficient for hydrogen between the liquid metal and a hydrogen-dilute gas phase. In an effort to extend our knowledge in this area, an investigation of the rate of removal of hydrogen from liquid metals by inert gas flushing was undertaken. In view of the difficulties encountered with gas porosity in the casting of aluminum and aluminum alloys, and because of certain experimental advantages, liquid aluminum was selected for the study. PREVIOUS INVESTIGATIONS The removal of gases from liquid metals, particularly steel, has received considerable attention in recent years, The first definitive work of a theoretical nature was presented by Geller1 who considered the case where equilibrium exists between purging gases and metal bath during flushing, and also deviations from this ideal case. Hulme2 has surveyed a number of experimental studies and discussed some of the practical limitations of removing dissolved gases from molten metals. More recently a number of studies have been reported on degassing of steel melts by flushing with an inert gas.3&apos;4 Considerable work has also been reported on aqueous and organic liquid-gas systems, and an excellent summary prepared by Hovis.5 The treatment of liquid aluminum by a flushing gas to remove dissolved hydrogen has been known for several decades.6 A number of gases have been used for this purpose, including nitrogen, argon, and chlorine, or mixtures of these gases. Tikkanen and Erkko7 have studied the relative density changes of aluminum castings poured from melts degassed with chlorine, nitrogen, and mixtures of the two gases. Their

Jan 1, 1962

By C. L. Ray, R. E. Baarson, H. B. Treweek

As an example of nonmetallic mineral flotation, the separation of several pegmatite minerals will be discussed in considerable detail, from both the laboratory-testing and plant-operation standpoints. The pegmatites have been chosen to illustrate the practicality of the selective separations of the minerals in a complex nonmetallic ore and, in so doing, to set forth a summation of the flotation art and technology which is applicable in part to the beneficiation of several less complex nonmetallic ores. In addition, a brief summary of descriptions of other nonnietallic mineral flowsheets and separations is included. Some of the industrial minerals now being concentrated by froth flotation methods commercially, or in the laboratory, are listed in Table 1. GENERAL CONSIDERATIONS There are two classes of chemicals that are normally utilized as collectors in froth flotation separations of nonmetallic minerals. These are defined as anionic and cationic and are typified by the fatty acids and amines, respectively. The fatty acids are selective to those minerals that have a high concentration of positive surface charges, such as the various calcium minerals typified by calcite, phosphate rock, and fluorspar. The amines are selective to those minerals with a high concentration of negative surface charges, such as silica sand and silicates. It should be noted, however, that by using various inorganic chemicals, a new or synthetic surface can be placed on specific minerals which produces different characteristics, thereby reversing the flotation reagent required for separation. The polar end of the collector attaches to the mineral surface either by chemical or physical adsorption; the nonpolar unreactive end is oriented away from the mineral surface. The result is a hydrophobic coating at the mineral surface which causes attachment to air bubbles. It is this surface condition that permits the floating of minerals which normally sink in water. In order to utilize these fatty acids and amine derivatives, several conditions .must be fulfilled. Before there can be a selective flotation process,

Jan 1, 1962

By Monte J. Pool, Rudolph Speiser, George R. St. Pierre, William T. Ebihara

Standard free energies of formation of WO,, W O W20058 and WO3from oxygen and the lower oxide or tungsten have been determined in the tempel-ature range of 700° to 1220°C. A tentative W-O phase diagmm is presented based on the evidence that the oxide phases, "W18O49" and "W20058", are unstable at l~atm total pressure, below 585° and 485°C:, respectively. A HE need for a complete quantitative treatment of the phase equilibria of the W-O system has been establishedby metallurgists during the past few years. In an attempt to improve the endurance of tungsten exposed to oxidizing atmospheres at high temperatures, many research groups have studied the kinetics of tungsten oxidation. The reverse process, the reduction of the tungsten oxides to metal, has also been investigated to some extent. Regardless of the particular interest, metal to oxide or oxide to metal, a knowledge of the phase equilibria of the W-O system is required to properly interpret all of the kinetic observations. It should be possible to state the stable phases of the W-O system at any given values of the chemical potential of oxygen and the temperature.

Jan 1, 1962

By E. C. Perkins

As part of a program for developing methods of using domestic titanium deposits, the Bureau of Mines investigated methods for chlorinating titanium slags prepared from titaniferous minerals by electrosmelting. Titaniferous slags were made from ilmenites in the following deposits: Valley County, Idaho; Trail Ridge, Fla.; Aiken, S. C.; and Maclntyre, N. Y.; titaniferous magnetite from Iron Mountain, Wyo., were also evaluated. The tests were made in two chlorinators, a 4-inch and a 36-inch unit. Preliminary testing was done in a 40-millimeter bench-type unit. Chlorine gas was contacted with a loose mixture of titaniferous slag and carbon at a high temperature to form titanium tetrachloride. The moving-bed system used in this work involved a downward movement of feed countercurrent to the chlorine flow, and residues continuously removed from the bottom of the reactor. The performance characteristics of these slags depended on their composition, which varied widely according to the geographic source of the ore. The results showed that all but two of the slags could be chlorinated as effectively as rutile, converting 70 to 80 percent of the titanium to the tetra-, chloride. The two slags that proved difficult were made from New York ilmenite and Wyoming titaniferous magnetite. These slags contained enough magnesium to cause clinkering, which necessitated that the bed be prematurely withdrawn before more than 70 percent of it could react. The iron content of the slags did not interfere with operating the chlorinators. The data from the 4-inch and the 36-inch units were in agreement on the relative amenability of the slags to chlorination.

Jan 1, 1962

By C. W. Dwiggins

This report describes the development, theory, and application of techniques and instruments for quantitatively determining nickel, vanadium, and iron in oils, using direct, X-ray emission spectrographic methods (5, 6).3 The methods developed apply to petroleum and other oils as well as some specific fractions of oils. The quantities of nickel, vanadium, and iron in various petroleums are of practical and theoretical interest. Even traces of nickel and vanadium may poison cracking catalysts, and X-ray methods have been used for determining nickel in such catalysts (7). At least parts of the nickel and vanadium occur as metal-porphyrin complexes, a fact which may have considerable bearing on knowledge of the origin of petroleum.

Jan 1, 1962