By G. P. Contractor

Medium and low carbon steels, modified with uranium, were studied in order to evaluate the influence of uranium on forge ability, mechanical 11roperties, response to heat treatment and microstructure. Uranium contents ranged up to 0.70 per cent. The medium carbon steels are hot short if the uranium content exceeds about 0.35 per cent. More uranium can be tolerated in low carbon steels. The hot shortness is caused by the formation of intergranular phase UFe2. Critical transformation temperatures, Jominy hardenability, and resistance to tempering are not significantly affected by the 11resence of uranium. Similarly, uranium has little or no effect on the tensile properties of carbon steels. The addition of uranium has a favourable effect 11n the stress-rupture characteristics and some beneficial effect on fatigue properties. However, more results are required for verification. In the steels investigated, it seems that most of the uranium carbide combines to form complex inclusions of U (0, C, N) or (C, N), rich in oxygen or nitrogen or both.

Jan 1, 1963

By S. E. Bronisz, Dana L. Douglass

a Uranium was deformed by cold rolling, and the effects of this plustic deformation on the microstruc-ture of the metal were observed by the technique of transmission elecbon microscopy. The recrystalli-zation of selected cold-wmked samples was also studied by this method. The samples were prepared for examination by electrolytic thinning in a standard metallographic electrolyte which has not been previously reported as being used in producing thin foils of uranium. The microstructural changes observed in the a uranium were generally similar to those seen by optical microscopy. The changes in the microstructure of a uranium following cold work and recrystallization treatments have been the subjects of several studies employing optical and X-ray techniques.12-19 These studies indicated that twinning was the redominant mode of deformation at room temperature20 and that the regions of high energy associated with the deformation twins were preferred sites for the initiation of recrystallization.15,18, Recently several workers have prepared thin foils of uranium suitable for examination by transmission electron microscopy.'-lo The foils thus prepared have been used to study fission fragment damage; a particular dislocation reaction,' and gas precipitation." At this laboratory the microstructural changes occurring during the cold working and recrystallizing of a uranium samples have been studied by using transmission electron-microscopy techniques. The foils used in this work were electrolytically thinned in a polishing bath not reported previously in the literature as being used for this purpose. EXPERIMENTAL PROCEDURE The uranium used in this investigation was depleted a uranium sheet 4 mils thick. The results of a spectrochemical analysis of this material are shown in Table I. The as-received uranium was cut into strips, 1 in. wide by 5 in. long, and annealed in vacuo at 600°C for 2-1/2 hr. The resulting microstructure consisted of relatively uniform, equiaxed grains having diameters of 10 to 50 p. Cold Working. The cold-worked samples were prepared by rolling several of the annealed uranium strips to various thicknesses. The strips were reduced 3.5 ± 0.5, 6.0 ± 0.6, 10.0 ± 0.5, 19.5 ± 1.0, and 28.5 ± 2.0 pct in thickness. It was not possible to achieve these reductions with a single pass through the rolling mill, so the strips were turned end for end during the rolling procedure. The cold-rolled strips were stored in dry ice until samples from them could be thinned and examined (within 24 hr after rolling). Annealing. The samples used in studying the re-crystallization behavior of a uranium were obtained by annealing sections of the strips which had been reduced 10.0 and 28.5 pct. These samples were sealed in evacuated Pyrex capsules and were annealed in a tube furnace at temperatures from 200" to 600°C and for times from 1/2 to 2 hr, see Table l. Thinning: The samples from the rolling and heat treatments were prepared for examination in the electron microscope by electropolishing in a bath composed of 25 g chromic acid, 133 ml glacial acetic acid, and 25 ml water. This electrolyte has been used and recommended for preparing specimens for optical metallography It was necessary to mask the edges of the sample with a stop-off paint in order to prevent preferential attack in these areas. The paint used was made by dissolving polystyrene in benzene. The electrolytic cell consisted of a cylindrical stainless-steel cathode placed in a beaker containing the electrolyte, with the sample as the anode positioned at the cell axis. The temperature of the electrolyte was held below 15°C by cooling with liquid

Jan 1, 1963

By Leon D. Keller

Hydraulic concentration of minerals has been practiced for a good many years. Until recently, however, the practice has been limited to a multiplicity of small pockets and relatively low tonnages and flows. The adaptation of the SiphonSizer to the concentration and classification of magnetite has changed this concept. Some fifty commercial units are currently in operation on magnetite, varying in size from 16 ft diameter circular unit to a 25 ft by 100 ft rectangular unit. Additional units up to 38 ft diameter are under construction. Depending upon the application in the flowsheet, upgrading-varies from 0.75% to 14% Fe in a single stage. To those not familiar with taconite processing, the importance of the struggle to economically remove as much silica as possible may not be fully appreciated. These figures pertaining only to transportation may be thought-provoking. If a 10,000,000 ton per year plant could reduce the silica content of their concentrate by 17, a savings in boat freight alone would amount to 100,000 tons at $2.00 per ton annually.

Jan 1, 1963

By H. H. Kellogg, T. R. Ingraham

Three anhydrous zinc sulfates have been identified. They are: ZnSO,(a), stable below 1007°K; ZnS04(/3), stable above 1007OK; and ZnO.ZZnSO,. The decomposition pressure of each sulfate has been measured and the following relations calculated from the results: The measured data have been combined with the known themzodynamic properties of ZnS, ZnO, Zn, SO,, and SO, to yield univariant and bivariant phase diagrams for the system Zn-S-0. The application of these diagrams to problems of roasting zinc concentrates is discussed. PRESENT knowledge of the equilibrium chemistry of the system Zn-S:O, so essential to scientific control of zinc-blende roasting, is deficient in several respects. A basic sulfate of zinc has been reported by many investigators, but its composition is in doubt and its thermodynamic properties have not been measured. Our scanty knowledge of the properties of the normal sulfate at roasting temperatures is based on old and inexact studies. A crystal transformation in the normal sulfate, involving a sizable heat effect, has been noted by several investigators but has never been quantified. The studies reported herein were designed to fill these gaps in knowledge and to make possible a reasonably complete thermodynamic description of the system Zn-S-0 at roasting temperatures. The results make possible a far more exact understanding of zinc roasting chemistry than was hitherto possible. EXPERIMENTAL The principal experimental technique employed was the measurement of the total gas pressure developed from decomposition of either ZnSO, or ZnO2ZnS0, in a closed system. The apparatus employed was essentially the same as that described by Warner and lngrahaml and Flengas and tngraham.' The unusual feature is a flexible Pyrex bellows used to separate the reaction gas mixture (S03, SOz, and 02) from the mercury in the manometer and thus prevent corrosion of the mercury by SO3. The bellows operates without evidence of hysteresis and, barring accidents, may be used for several months. The response of the bellows varies from manometer to manometer, but is generally of the order of 0.6-cm displacement for a l-cm change in pressure. The response for all manometers has been linear over the range 0 to 1 atm. To prevent condensation and polymerization of sulfur trioxide, the bellows-manometer was maintained at 100.0" * 0.5" by a circulating bath of silicone oil. The connecting tubing between the manometer and the furnace was maintained at 100.0" * 0.2"* also, with a stirred air bath. The open end of the manometer was connected with a chamber which was maintained at a known pressure. The pressure could be varied so that readings of the height of the mercury column, measured with a cathetometer, could be made with both rising and falling mercury column. By using the average of the readings, any error due to sticking of the mercury column was minimized. The sample was placed in a 2-in.-long platinum boat formed into the shape of a half-cylinder. The sample was prepared as a fine powder and pressed against the inner wall of the platinum boat. A silica thermocouple well, covered with a platinum sleeve, was placed lengthwise along the center of the boat. The temperature of the sample was read on a calibrated Pt-10 pct Rh theirnocouple. The temperature profile of the furnace was constant within ± 0.2 C over the length of furnace occupied by the sample. The horizontal furnace used to contain the sample and the quartz reaction tube was electrically heated, with the control thermocouple placed 1/4 in. from the windings. A Brown Pyro-O-Vane temperature controller with a 3-sec response time was used to maintain the furnace temperature. Before beginning a run, the apparatus, including the bellows manometer, was thoroughly washed in sib with acid and distilled water to remove any

Jan 1, 1963

By R. G. Ward

The temperature gradient in the subhearth metal or "salamandern of the iron bhst furnace results in the establishment of gradients in the concentrations of silicon, manganese, carbon, and sulfur. The temperature and compositional variations observed in three blast furnaces are analyzed according to irreversible thermodynamics and the systems appear to be close to the steady state condition. Apparent heats of transport, Q, for silicon, manganese, carbon, and sulfur are found to be respectively -17.5, -5, -2.1, and+22k cal per g mol. In conclusion the significance of thermal diffusion in extraction metallurgy is briefly discussed. INCREASING interest has been shown in recent years in the application of irreversible thermodynamics to metallurgical problems. In particular studies have been made of the transport of matter in thermal gradients1-' and under chemical gradients imposed by a binary solvent However, no detailed example in extraction metallurgy has been reported although gradients are the essence of many extractive processes. The case of the distribution of elements in molten blast furnace iron under a thermal gradient is discussed here. DATA In blast furnace operation the hearth bottom is often extensively destroyed by molten metal, and the metal may penetrate perhaps 10 ft into the furnace foundations forming a "bear" or "salamander". Several hundred tons of molten metal may thus exist beneath the level of the conventional tap hole and remain relatively undisturbed for several years under a thermal gradient. This system is subject to little convective stirring because the temperature decreases from top to bottom, and mechanical stirring due to movements in the stack and to tapping operations is unlikely to penetrate far into the metal. The system may thus be regarded as static

Jan 1, 1963

By Rollien R. Wells

A REPORT of technological advancements restricted to a specific 12-month period is impractical. Inherent in the nature and development of technology is the element of time; rarely can a new process or product be attributed to a particular year. An overall picture of general trends and pattern changes, however, is indicative of technological growth. This paper presents selected observations and discussions of current metallurgical research and practices in an attempt to develop' such a picture. Of the estimated $16.5 billion spent for research and development in the United States in 1962, at least 80 percent was earmarked for the aircraft, electronics, chemical, and machinery industries. Much of the effort was of the end-use variety and was oriented closely to the national defense and aerospace programs. Only a small fraction of the total research money was directed to studies of the utilization and improvement of metals. Even if the investigations in allied fields such as solid state physics are included, the total research expenditure for metal and mineral materials barely reached $500 million. An additional $200 million was spent by industry and government for development of minerals recovery and processing methods.

Jan 1, 1963

By Charles L. Guettel

The temperature coefficients of electrical resistance of 31 alloys in the nickel-rich corner of the Ni-Cr-Fe system were determined. The results indicate that a range of binary Ni-Cr alloys has lower temperature coefficients than a specific region of Ni-Cr-Fe alloys which has been reported and quoted by others as providing the lowest coefficients in the ternary system. DESIRABLE properties of resistivity and temperature coefficients of resistance have been the basis for the successful commercial application of various Ni-Cr and Ni-Cr-Fe alloys. In particular, low or negligible temperature coefficients of resistance are necessary for wire used in precision wire wound resistors and potentiometers involved in closely controlled electrical and electronic circuitry. Alloys most successfully applied to this purpose basically have not been ternary Ni-Cr-Fe alloys but rather heat-treated Ni-Cr alloys in the region of approximately 73 to 79 pct Ni and 20 pct Cr with significant additions of other elements such as aluminum, silicon, iron, copper, manganese, and cobalt. While the addition elements play a vital role in the nature and control of the temperature-resistance curve of any one of these alloys, the inherent relatively low temperature coefficient of the binary Ni-Cr base composition itself in the approximate region of 80 pct Ni and 20 pct Cr contributes fundamentally to the eventual negligible temperature coefficient obtained with the applied alloys. W. A. Dean 1 has reported mean temperature coefficients (20' to 100oC) of as-cast samples for the Ni-Cr-Fe system, the nickel corner of which is given in Fig. 1. Dean had to use as-cast samples because alloys from a considerable region of the system were unworkable. Dean refers to the work of Hunter and sebast2 who used annealed wire samples to show that, for chromium contents of 10 to 25 pct, the temperature coefficient increases as the iron content is increased at the expense of nickel. Although the data of Hunter and Sebast were limited in the nickel-rich areas to eight samples of 60 to 91 pct Ni with only four samples containing iron, the possibility that no Ni-Cr-Fe alloy has a lower temperature coefficient than certain binary Ni-Cr alloys should have been given serious consideration. However, Dean's work has been referred to by J. S. Marsh,3 who, quoting Dean, states that for the temperature coefficients "the smallest values-about 0.0001 per oC (100 ppm)—were found for alloys containing about 55 pct Ni and 20 pct Cr" (balance iron). A region such as that reported by Dean would be significant to those trying to develop alloys for the applications described. Therefore, a series of three-pound laboratory open-air induction melts of Ni-Cr and Ni-Cr-Fe alloys were melted, conventionally processed to 0.005 in. diam wire, and continuously strand annealed at 1900° F. The basic Ni-Cr compositions, with balances essentially iron other than usual minor impurities, and the corresponding temperature coefficients of resistance and resistivities are given in Table I. The resistivities are approximate and are not to be considered as a basis for relating them to their position of composition in the ternary system. The wire diameters were determined with a micrometer, and not by weight and density measurements which would be required for accurate resistivity values. However,

Jan 1, 1963

From time to time the Bureau of Mines has interpreted and applied certain provisions of the Federal Coal Mine Safety Act and Federal Mine Safety Codes, primarily for the guidance of Federal Coal Mine Inspectors. Although interpretations of the Act have appeared in the Federal Register, the Code interpretations and practical applications have not been published. In response to many requests from representatives of the coal-mining industry, the Bureau is publishing this information to promote better understanding of those provisions that may be misinterpreted or misapplied. INTERPRETATIONS AND APPLICATIONS Two Federal Mine Safety Codes are discussed in this report, namely the Federal Mine Safety Code for Bituminous-Coal and Lignite Mines of the United States, Part 1, and the Federal Mine Safety Code, Anthracite Mines of the United States, Part 1. In this circular the word Codes refers to both directives; Code* refers to the code for bituminous-coal and lignite mines; Code? refers to the one for anthracite mines. Act* refers only to bituminous-coal and lignite mines.

Jan 1, 1963

By Moskovits E. E

Spodumene was recovered from pegmatite by flotation in laboratory and pilot-plant tests using an anionic collector emulsion. A similar process applied to beryl pegmatite gave encouraging results.INTRODUCTIONOver the past two decades lithium and beryllium have aroused increasing interest in the metallurgical world. Both these light metals have potential uses in nuclear shielding and cooling and in lightweight alloys, and there is a growing demand for lithium chemicals for ceramics, air conditioning and lubricants. The use, technology and history of lithium has been surveyed by Schreck (1961).For many years, the only commercial production of lithium and beryllium was from pegmatite deposits amenable to hand cobbing. The most important minerals of these ores are spodumene and beryl, which are respectively lithium aluminium silicate and beryllium aluminium silicate. Norman and Gieseke (1940) investigated the treatment of lithium ores by froth flotation. The process of flotation of the pegmatite constituents away from the spodumene was applied commercially in 1951, and the operation has been described by Goter, Rainey and Hudspeth (1953). Subsequently, the flotation of the spodumene from the pegmatite was studied by Munson and Clark (1955) and Browning and McVay (1961), and this method has superceded the reverse flotation process commercially. Muskett, Tasker and Hobson (1962), in applying the method of Browning and McVay in pilot-scale tests, reported difficulty because of activation of quartz and felspar by iron salts introduced during milling of the ore.The flotation of beryl, reported by Ashton and Weir...

Jan 1, 1963

By Laurence Pellier

Electron microscopical studies were made of the effect of sensitization at 1200oF on a Type-.104 stainless steel with high carbon and low nitrogen and oxygen contents, after solution annealing and after cold working. The loci of the carbide precipitates in the early stages of sensitization were followed in dry stripped plastic replicas. Some observations were made by direct electron transmission on thinned films. Intragranular dislocations showed a high degree of stability through the annealing necessary to produce sensitization. I HE present work was undertaken to determine the effect of sensitization, at 1200°F, for 1/2 hr, on the electron microstructure of a Type-304 stainless steel with high carbon, and low nitrogen and oxygen contents, after solution annealing and after cold working. Many electron microscopical studies of sensitization of 18-8 stainless steels have already been made. Most of them utilized extraction replicas, from which the morphology and composition of the precipitated carbides could be established.'-" ry stripped replicas were seldom used for such studies, although it was demonstrated that they are applicable, in general, to EurveYs of the general microstructure of many alloys' and, in particular, to the observation of precipitated carbides in austenitic stainless steels.3

Jan 1, 1963

By H. W. Knott, M. H. Mueller

The crystal structures of Ti2Cu, Ti2Ni, Ti4Ni2O, and Ti4Cu20 have been determined using powder specimens examined by X-ray and neutron diffraction. Lattice constants have been determined for all four phases using X-ray powder diffraction films. Atom positional parameters of all four phases have been determined from observed neutron intensities. X-ray diffraction calculated intensity data have been presented also for the phase Ti2Cu to point out the particular suitability of neutron diffraction in this case. Interatomic distances have been determined using the positional parameters obtained from neutron diffraction. ALTHOUGH some investigations of the crystal structures have been made of these four compounds previously,'-13 it was the purpose of the present investigation to expand the previous work in order to locate the various atoms, determine their coordinates, and to confirm or to correct some of the previous work. It was convenient to group these four compounds together since they are related chemicallv and/or structurally. The compound Ti2Cu is tetragonil; and Ti2Ni, Ti4Ni2O, and Ti4CU2O are all large fees of the same space group. Ti2Cu has been previously reported as a fee phase by Laves and Wallbaum;1 and Rostoker2 which was possibly the oxide phase, Ti4Cu20. Joukainen, Grant, and Floe;3 and Trzebiatowski, Berak, and Ramotow-ski4 have also reported a phase of this composition. karlsson5 has reported a small fct phase of the composition Ti3Cu which may be the presently discussed Ti2Cu phase. More recently Ence and Margolin6 have reported a small fct phase for Ti2Cu and the present authors7 together with Nevitt8 have briefly reported it to be a bet related to the fct with a co three times the length of the co of the fct and have also reported that this phase has a very limited composition. Further refinements will be reported which have varied some of the parameters of this bct structure slightly. Ti2Ni has been reported as a fee phase by Laves and wallbaum;1 Duwez and taylor;9 Rostoker;2 Poole and Hume-Rothery;10 and Yurko, Barton, and parr.11 In a later paper Yurko, Barton, and parr12 have given the complete structure of this phase based on an X-ray diffraction study which was independently confirmed with neutron diffraction by Mueller and knott.7 Additional crystal structure information will be given. Ti4Ti2O, Ti4Cu2O, and a number of other compounds including Ti4Fe2O have been reported as fcc phases by Rostoker,2 and more recently Nevitt13 has confirmed the Ti4Ti2O phase. Rostoker,2 however has reported diffraction lines for Ti4Fe2O which do not have all odd or all even indices. These lines, therefore, cannot be observed if this compound has a fee structure. This same error has crept into the diffraction results reported for TiNi2O and Ti4Cu20 in the ASTM powder data which has been credited from Rostoker's data. Complete crystal structures of these two phases will be presented. Although all four of these structures have large unit cells and hence do not lend themselves for completely resolved neutron powder patterns, a sufficient number of individual reflections was observed for solving the structure. They also serve as good examples of some of the advantages to be gained by using both neutron and X-ray diffraction techniques. EXPERIMENTAL PROCEDURE All of the alloys were prepared by arc melting. The starting metals had the following purity: Cu 99.999 pct, Ni 99.83 pct, and Ti 99.92 pct. Oxygen was introduced into the two oxide phases as chemically pure TiO2, with the remainder of the titanium coming from the above mentioned metal. All of the sample buttons were annealed in evacuated Vycor tubes, the two binary phases for 5 days at 700°C and the two oxide phases for 3 days at 900°C. Oxygen analyses were performed on all four phases by two independent laboratories with the following amounts of oxygen present in atomic percent; Ti2Cu-0.06, Ti2Ni-1.03, Ti4Ni2O-13.95, and Ti4Cu20-13.87. The stoichiometric amount for the oxide phases is 14.29 at. pct. Since all of the samples were very brittle they were easily reduced to a powder for diffraction measurements. The lattice constants given in Table I were determined for the four compounds from X-ray diffraction patterns of powder samples exposed to filtered copper radiation using a 114.59 mm diam Debye-Scherrer type camera using the Straumanis loading. None of the patterns showed a detectable amount of a second phase. The lattice constants were obtained from an IBM 704 computer program employing a least squares treatment with systematic correction terms as previously reported.14

Jan 1, 1963

By Roy L. Wilfong

The linear expansion of high-purity oxides of yttrium, cerium, samarium, europium, and dysprosium was determined by the interferometric method for the temperature range 25° to 1,000° C. Single-crystal magnesium oxide and single-crystal aluminum oxide were used as reference materials. The bulk density and crystal form of the nonreference materials also were determined. The coefficients of linear expansion in the range 25° to 1,000° C were found to be 8.10 x 10-6 for yttria, 12.10 x 10-6 for ceria, 10.81 x 10'6 for samaria (monoclinic), 10.35 x 10-6 for europia (monoclinic), and 8.13 x 10-6 for dysprosia, each given in centimeters per centimeter per degree Centigrade. A detailed investigation of the interferometric technique for measuring thermal expansion in this temperature range was made. The interferometer was found to be a precise tool but only when adequate precautions were taken. These precautions are described.

Jan 1, 1963

By D. Bienstock

To develop a rugged catalyst capable of withstanding hydraulic attrition resulting from the oil-circulation process for synthesizing liquid fuels, use of an iron catalyst containing an active coating surrounding an inert solid core of metal was investigated. This massive-iron catalyst in the form of steel shot and lathe turnings was activated by partial oxidation with steam at 600° C, impregnated with alkali, and reduced with hydrogen at 450° 6. The massive-iron catalysts were resistant to oxidation and spalling, and a 6-month catalyst life was attained. Higher operating temperatures could be employed than with fused iron oxide catalysts, resulting in greater gasoline yields. Because the lathe turnings pack with void volumes of 70 to 90 percent, it has become possible to employ a fixed bed without the danger of cementation that occurs with fused iron oxides.

Jan 1, 1963

By T. P. Chen, F. W. Bowdish

Studies made with a captive bubble apparatus on the sulfidization and collection by amyl xanthate of true chrysocolla specimens have defined the ranges of pH value and sulfide concentration which permit contact between the bubble and the mineral surface. Titanium compounds were the most effective of the materials found to activate the sulfidization of chrysocolla. With titanium activation, the contact angles and the ranges of pH value and sulfide wncentration giving bubble contact were all increased. Chrysocolla ores were concentrated by flotation. Chrysocolla ores occur at many localities in grade and quantity sufficient to make mining and millin feasible, but no satisfactory method of concentratio has been found. Although chrysocolla may be leached with acid, only those ores without acid-consuming gangue may be leached economically. Because of its potential importance, a study of the conditions nece sary for flotation of chrysocolla has been carried ou The literature contains a few references to flotation of chrysocolla. Two methods were developed by the U. S. Bureau of Mines.1,2 The first consisted of a fatty acid soap and a high xanthate as collectors of chrysocolla from a synthetic ore, while the second involved the use of hydrogen sulfide and xanthate. Ludt and DeWitt3 demonstrated the difference in adsorptive powers of chrysocolla and quartz for bas triphenyl methane dyes and suggested the use of butyl, hexyl or octyl-substituted malachite green as collector. Jackel4 emphasized the effects of combin tions of reagents such as Aerofloat 31, pine oil, and Reagents 404 and 425 with sodium sulfide and zinc hydrosulfite as conditioning agents. Although he reported recoveries of 89% from a synthetic ore and 98% from a natural ore containing azurite, malachite, chalcopyrite and chrysocolla, careful application of Jackel's method to chrysocolla from Tyrone, N.M., failed to give a high recovery. MATERIALS AND TECHNIQUE Samples from Inspiration, Ariz., and Tyrone and Magdalena, N. M., were used for experimentation and verified as true chrysocolla by leaching tests, specific gravity tests and X-ray diffraction. Chrysocolla does not dissolve at pH 4, although malachite and azurite do. Chrysocolla is about half as dense as the copper carbonates. X-ray diffraction analyses by the powder camera method confirmed the samples as true chrysocolla. A captive bubble apparatus, which cast an enlarged image of the air bubble and the mineral surface upon a screen, was used to check on the character of the surfaces. The specimens were prepared by grinding a flat surface on a glass plate using fine abrasive; then they were washed and kept in distilled water until they were to be treated with reagents. Before each reagent treatment, the specimen was carefully checked for cleanliness in the captive bubble apparatus. It was assumed that the surface was clean if, after fine grinding and washing of the specimen, the bubble would not stick. Specimens were handled with glass forceps, and precautions were taken to avoid contamination of the mineral surfaces. Contact angle measurements were carefully made several times on each treated specimen to obtain reliable average values. EFFECT OF pH VALUE AND SODIUM SULFIDE CONCENTRATION In each experiment, a specimen with a freshly ground surface was immersed for 10 min in a solution of sodium sulfide, washed and immersed for 15 min in a solution containing 30 mg per 1 of potassium amyl xanthate. The specimen was then washed again in distilled water and tested for contact angle in the captive bubble apparatus while submerged in distilled water. In this series of experiments, the pH of the sulfidizing solution was varied from 3 to 7, and the concentration of sodium sulfide, containing 60% Na2S, was varied from 50 to 650 mg per 1. Many combinations of pH value and sulfide concentration resulted in no contact between the bubble and the surface, but over a limited range of conditions, contact angles varying from 24ºto 52ºwere obtained. The data in Fig. 1 show sulfidization conditions that lead to bubble contact and those that do not. The region of contact is surprisingly small, which may indicate why flotation of chrysocolla involving sulfidization has proven so difficult in practice. Several features of the system are illustrated in Fig. 1. In the region between pH values of 4 and 6 with sodium sulfide concentrations below about 350

Jan 1, 1963

By James J. Scott

Three dimensional photoelastic techniques have been developed which provide information on the state of stress at any point in a model investigated. This investigation utilizes these techniques to determine the stress distributions in the pillars and the roof of a room and pillar mine model. Castolite plastic was used for the construction of the model in which a stress pattern was developed by the stress freezing process. Analysis of the stress pattern was accomplished by use of data obtained by observing points in slices from the model with a polariscope and solving data obtained by' the shear-difference method. Slices through the centerline, edge of pillar and centerline of span were investigated. Results of this work provide information on the overall stress distribution on points of stress concentration in compression, shear and tension, show relative magnitude of stress throughout the model and indicate directions of the most important stress values. A generalized roof bolt pattern is developed for room and pillar mines based on the stress distribution. A digital computer was used in the reduction of data and proved to be extremely useful for investigation of this type.

Jan 1, 1963

By C. J. Thompson

Two sulfur compounds--the 2,2,5-trimethyl- and the 2,2,5,5-tetramethyl derivatives of thiacyclopentane--were identified in Wilmington, Calif., crude oil, using microdesulfurization and gas-liquid chromtography techniques.

Jan 1, 1963

By Kung-Lee Wang

FOLLOWING the rapid recovery of previous years, the U.S. economy continued the upward trend and moved forward moderately and sporadically during the first half of 1962. There was a slow-down in the recovery rate, which was especially notable in the third quarter. The economy recovered in the fourth quarter, and by the end of 1962 the gross national product amounted to $555 billion, a new high, 7 percent above that of 1961. Production, employment, personal income, and corporate profits all achieved new peaks, but unemployment continued high and the prospects for improvement remained poor. The economy again failed to us~ its full potential; 1962 was a good year, but not good enough. During 1962, all industrial production climbed from the low in January to a high in late summer which lasted through the fall, and declined slightly at yearend. Mining production followed this pattern closely and most sectors were approaching record highs. Most minerals gained in value and volume of production. The steel-associated minerals group was the only exception, and it sustained a small net loss. The nonfuel minerals industry opened the year at a high level, maintained this high level until late summer, with the peak in May, and drifted downward toward the end of the year. The gains recorded by nonferrous metal mining partly offset the loss of ferrous metal mining, resulting in a small gain for metal mining as a whole. The upsurge of construction material minerals output was primarily responsible for the substantial increase in production of nonmetals other

Jan 1, 1963

By L. Adler

The author recently proposed a technique for handling the effect of planes of weakness on failure in geologic material.1 The technique employed an "extended" Mohr's rupture envelope, on which was superimposed a generalized three dimensional stress representation. Subsequently, the method was applied to so-called two-dimensional stress states" which were in reality degenerate three-dimensional ones. Since a two-dimensional stress solution usually refers to a plane stress condition, the terminology was confusing. The distinction between a plane stress state and a degenerate three-dimensional one is shown in Fig. 1. The solution of problems involving a generalized three-dimensional stress state is greatly aided by continual reference to the basic principle that no stress components can act on a plane, oriented as is the weakness plane, which lies outside of the weakness plane's rupture enVelope.2 This is shown in Fig. 2; and if it is also remembered that the radii of the Mohr's Circles give the orientation of such a plane, solutions are easier to follow, and perform. Sample Problem 1: Site Location (generalized three-dimensional case).' Given: 1) Both rupture envelope for the solid and plane of weakness. 2) Existing principal stresses and orientations in space (?12, ?13) obtained from a stress analysis of the proposed structure. Find: Permissible orientations of the weakness plane in order to select a suitable site.

Jan 1, 1963

By W. T. Abel

Laboratory tests were conducted with a closed, recycling system to evaluate the effectiveness of solid-in-gas suspensions as heat transport mediums. Micronized graphite in helium or nitrogen was circulated by a centrifugal compressor to determine the feasibility of the method and heat transfer capabilities of the mediums. Suspensions were circulated without plugging or eroding the compressor or piping. At low flowrates and light (0.1 to 0.2 volume-percent) graphite loadings, slightly less power was required to transport a given amount of heat with suspensions than with helium alone. Graphite deposition on the heat exchange surfaces of the cooler decreased the heat transfer effectiveness at higher solids concentration. Efforts to eliminate deposition are described.

Jan 1, 1963

By G. R. Kotler, W. A. Tiller, W. C. Johnston

Experiments carried out on 100 g samples of molten tin and Sn-Pb alloys showed that the magnitude of the field strength, H, does not effect the supercooling, aTn, at which the initial nucleus of solid forms. However, the nuwlber of nuclei forming per cc, n, is found to increase greatly with H for fixed ATN and to increase with ATN for fixed H. The value of n increases greatly with the presence of solute and is found to he indefiendent of the cooling rate of the simples. Further, the most effective time for stirring to enhance n is immediately following the initiation of recalescence. The effect of inducing nucleation with the aid of a mechanical impact both in the presence and absence of stirring has also been studied. All proposed mechanisms for the enhancement of n by physical means seem to be inadequate in accounting for these results. IN any real nucleation experiment there are two effects influencing the results that would not be predieted from classical homogeneous nucleation theory. These may be separated into chemical and mechanical effects. The chemical effects are twofold. 1) Nucleation catalysts are present which enhance the nucleation frequency of new grains over that predicted by classical homogeneous nucleation theory.' 2) Solute will restrain the growth of nuclei so that many others may form.2,3 The mechanical effects are also two-fold. 1) Vibration (sonic or ultrasonic) of the freezing liquid enhances the nucleation frequency of new grains over that given by the chemical effects alone.4-6 2) Macroscopic fluid-flow effects produce the same effect as l).'7' It is also possible to influence the nucleation experiment by certain physical effects such as the application of electric and magnetic fields.9 From classical homogeneous nucleation theory one would predict the following relationship between the nucleation rate, N1 (number of nuclei formed per unit volume per unit time), and bath supercooling, AT, for an isothermal experiment.

Jan 1, 1963