By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,' indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1', following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By R. W. Borio, T. S. Spicer

Inflammability and crossing point apparatus were used to study the influence of increasing amounts oi such inerts as ash, fly-ash, pyrite, limestone and Portland cement with several pulverized bituminous coals. The results indicate that it requires large proportions of inerts to substantially suppress the ease of ignition. The ignition phase of the combustion of solid fuels has been under study periodically since 1900. With the advent of pulverized coal firing some 60 years ago, a technique now dominating the coal utilization field, the ignitibility characteristics have become increasingly important. Much of the early work was directed toward the prevention of coal dust explosions and improved mine safety rather than combustion. Many factors affecting ignitibility have been studied and numerous methods devised in an effort to measure the ignition temperature and these have been reviewed by other authors. A recent survey was made by Finney and Spicerl in 1959, so a discussion of previous work will be omitted. Despite these efforts, the initial stage of combustion, termed ignitibility, is still a little understood phenomenon. In fact, no ASTM method has been adopted for the calibration of this illusive property. However, a D-5 Subcommittee XVI on Ignitibility of Coal and Coke of ASTM (now inactive) defined ignitibility:' "The ignitibility of a fuel is that char-

Jan 1, 1963

By J. Laganiere

A considerable part of the sulphuric acid requirements of the Aluminum Company of Canada's Arvida smelter comes from the burning of 180-200 tons per day of zinc '"'sulphide concentrates in a 22-ft.-diam-eter fluidized bed roaster. The plant and its operation were fully de-scribed in a publication that appeared about ten year ago (1). A simplified flowsheet of the roasting and gas-cleaning sections of the plant is given in Figure 1. The wet zinc sulphide concentrates are un-loaded into a pug mixer, by means of a Pay loader, and mixed with water in a mixing tank to make a slurry of 80 per cent solids. The slurry is transferred to a .feed tank and then introduced into the roaster at a point four feet above the constriction plate, which is the height of the settled bed of zinc calcines. The roasting temperature is con-

Jan 1, 1963

By M. R. Louthan

The susceptibility of titanium to stress orientation of hydride precipitates was investigated. It was determined that, when hydride precipitation occurred in titanium under an applied tensile stress of 30,000 psi, the hydrides precipitated on the titanium habit plane oriented most nearly perpendicular to the stress axis. Stress orientation of the hydride platelets occurred because the precipitation of the lower density hydride phase perpendicular to the stress axis caused expansion of the matrix in a direction that tended to relieve the applied stress. The Ti-H system has received considerable study in recent years, mainly because of concern over the effects of hydrogen on the mechanical properties of titanium. The amount of hydrogen present in commercial titanium is now quite low and should have no appreciable effect on its mechanical properties; however, many titanium applications require ex- posure to hydrogenous atmospheres under conditions in which hydrogen pickup is likely. In such cases continued exposures may cause the hydrogen content to increase to the extent that titanium hydride does precipitate as a second phase. The hydride phase has been shown 1,2 to have an adverse effect on the mechanical properties, particularly the impact properties, causing reductions in strength and ductility. BACKGROUND The behavior of titanium is often quite similar to that of zirconium and zirconium-base alloys, and the technology developed on one metal can often be applied to the other. Marshall and Louthan3,4 have shown that Zircaloy is susceptible to stress orientation* of zirconium hydride platelets, and that the platelet orientation has a pronounced effect on the mechanical properties of Zircaloy. They showed that when zirconium hydride precipitated in Zircaloy under an applied stress the hydride platelets tended to be aligned parallel to a compressive stress and perpendicular to a tensile stress. They also showed

Jan 1, 1963

By J. C. Borland, J. H. Rogerson

Jan 1, 1963

By James H. Gary

Data regarding the composition and physical properties of Florida land-pebble phosphate-waste slime are presented, and the feasibility of dewatering and beneficiating the slime by several different methods is discussed. Chemical analyses, electron micrographs, and X-ray diffraction data showed that principal constituents of the slime included quartz, attapulgite, and flaorapatite. Viscosity of the slime changed with pH; thixotropic, Newtonian, and rheopectic states were observed as the pH increased. Use of various flocculating agents was not effective in improving thickening properties of the slime. Dewatering tests using pressure filtration showed that temperature influenced the filtration rate more than pressure; the filtration rate at 165° C was tenfold that at room temperature. Selective flotation of the slime, using two different processes, gave promising results. About 25 pct of the phosphate was recovered in a concentrate assaying 31 pct P205, Other tests demonstrated that the slime could be successfully fractionated at 20-microns using a hydrocyclone. In hydrometallurgical tests about 80 pct of the phosphorus and alumina were chemically extracted from the slime using sulfuric acid. Limited bacteriological studies made of the slime showed that several types of microorganisms were present and grew in the material despite the presence of fluorine-bearing minerals.

Jan 1, 1963

By M. E. Wadsworth, I. B. Cutler, R. W. Bartlett

The oxidation kinetics of ZrC was studied between 450" and 580°C in oxygen pressures from 6.5 x 10-to 1 atm using a ther mogravimetric apparatus and sized powder samples. Two parallel rate controlling processes were observed. A surface reaction occurring at the ZrC-ZrO2 phase boundary accounted for most of the oxidation and had an activation enthalpy of 46 kcal per mole. The other process, believed to be diffusion of oxygen into the ZrC lattice partially replacing carbon, had an activation enthalpy of 53 kcal per mole. The enthalpy for chemisorption of O2 on ZrC was determined to be —13 kcal per mole. Water vapor in the presence of oxygen accelerated the surface reaction rate. THERE has been little reporting of formal rate studies or attempts to ascertain the mechanism of oxidation of carbides. MacDonald and Ransley1 studied the oxidation of titanium carbide which has the same structure as zirconium carbide, fcc. They observed an initial increase in rate with increasing temperature followed by a rapid decrease through a rate minimum and a subsequent second increase at higher temperatures. The discontinuity in the rate rise was attributed to a phase change in the oxide which changed the rate determining step from the surface reaction at the carbide-oxide interface to diffusion through the oxide layer. Samsonov and Golybera 2 studied titanium carbide and reported that during the initial period of oxidation a dense film of Tic-TiO was formed followed by the formation of less adhering layers of higher oxides. The purpose of this investigation was to study the kinetics of oxidation of zirconium carbide and to attempt to gain some knowledge of the mechanism by which oxidation occurs. EXPERIMENTAL PROCEDURE Measurement of the weight gain associated with the oxidation of ZrC was used to determine oxidation rates. The principal experimental parameters were surface area, temperature, and oxygen pressure. Although moderately sized crystals of ZrC can be grown by the Van Arkel method, the only commercially available ZrC is a powder. In using powders, the surface area must be controlled either by fabricating the powder into a sintered pellet with a measurable surface area, relatively fixed during oxidation, or by using sized unconsolidated powder and applying appropriate geometric considerations to the shape of the grains to correct for their diminishing surface areas as they oxidize. Both techniques involve some difficulties. pellets of binder-free zirconium carbide can be made by hot pressing, but it is difficult to obtain densities greater than 90 pct of

Jan 1, 1963

By Bruce E. Kester

The concurrent observation of the phenomena of alkali-aggregate reaction and development of efficient dust collection systems on rotary kilns made mandatory the process modifications to produce low alkali cements. Such low alkali cements as were available prior to these recent changes were either the rare result of low alkali raw materials, the loss of alkalies with dust loss from the kiln stack, or in some instances by the use of CaC12 in the kiln feed to increase volitalization of the alkalies and their subsequent loss or discard with the normal dust emission from the kiln. The relative slowly soluble nature of natural occurring alkali minerals in cement raw materials as compared to the very soluble nature of the alkali salts as present in cement kiln reaction products, either in clinker or in dust emission led to the development of the water leaching system. Two distinctly different problems of leaching are created by the two major systems of portland cement production, the wet and dry processes. The wet process is characterized by moderate dust loads and concentration of soluble forms of alkali in the dust. Further the return of the leached dust slurry does not materially change the characteristics of kiln feed on reintroduction and subsequently does not materially influence kiln operation. The dry process differs in high levels of dust emission and the presence in the collected dust of large amounts of unreacted kiln feed with its sparingly soluble alkali minerals. In the dry process reintroduction of leached dust slurry changes the dry process to what may be classed as a damp process. This change results in some decrease in kiln capacity and creates conditions of operation which are uncommon to either the wet or dry process.

Jan 1, 1963

By John C. Machisak

THIS INFORMATION CIRCULAR contains injury and employment data for all stone quarries in the United States for the Calendar year 1960. This publication contains statistical data on injuries and employment pertinent to the stone quarries and related operations, such as the manufacture of cement and lime, rock dressing etc., but excludes statistics for clay and sand and gravel operations. Data for these commodities may be found in other Bureau publications. Reports received from the operators are voluntary responses to the Bureau's request for information; therefore, the figures may not be complete for the industry. However, since these data contribute greatly to the promotion of safety, every effort has been made to make them representative of the industry.

Jan 1, 1963

By S. J. Rothman, L. T. Lloyd

S. J. Rothman and L. T. Lloyd (Argonne National Laboratory)— Hagel's paperz0 discusses the question of the mechanism for self-diffusion in bcc transition metals. Recent work21"23 has led us to agree with him in reabandoning the ring mechanism in favor of a defect mechanism, most likely vacancies. On the other hand, we think that Hagel's attempt to group together all self-diffusion in bcc transition metals is wrong. We prefer the scheme of Peart, Graham, and omlin," who separate them into two groups. One group contains the anomalously behaved metals P titanium,', y uranium, and perhaps zirconim.' The other group contains a iron," this alloy was held at 1800°C for 2 hr before quenching, its structure was all a. B. C. Giessen, I. Rump, and N. J. Grant (Authors' reply)—We very much appreciate the discussion by Deardorff and Kato regarding the a to /3 transformation temperature of hafnium. In the W-Hf program, as well as in a current study of the system Cr-Hf, standard precautions were exercised against contamination, including vacua of less than 10"5 mm Hg and a weight control check of all specimens to insure an impurity rise of less than 100 ppm. Following receipt of the above discussion, a revision was made in the annealing process. Arc-cast specimens were etched with a 10 pct HF-90 pct HNO solution until 1 mm of surface, including a possible oxide film, was removed. Annealing was done in a hafnium container which provided a long diffusion path for gaseous contaminants. Finally, the heat treating time was shortened. Structural changes were noted to occur quite slowly. A 99.5 at. pct Hf alloy showed 70 pct /3 after 30 min at 1700°C and was 100 pct /3 after 10 min at 1715°C. After 24 hr at 1740C, the alloy was found to be 10 pct/3. This change is due to contamination; it was estimated that it corresponds to an increase of 60°C in the transformation temperature over a 24 hr period. The corresponding change in 30 rnin would be slight. Using the same hafnium as in the above publication, and three new alloys at 98, 99, and 99.5 at. pct Hf, the transformation temperature was indicated to be 1715" 15°C. Since this hafnium contained 4.4 at. pct Zr, a correction of 40 5C, based on an assumed approximately linear transformation temperature curve, must be made for pure hafnium. This yields a value of 1755 20°C in good agreement with Deardorff and Kato's value. Because the slope of the boundary is small, this permits a good extrapolation, and we regard the W-Hf alloys as well suited to check the Hf transformation temperature. niobirn,'' and molybdenum,22 whose activation energies correlate with the melting temperature and whose Do values follow Zener's predictions.28 We have no quarrel with Hagel's placing chromium into the second group; we disagree with his interpreting our data to make uranium fit into that group. Hagel considers that the measurements of self-diffusion in uranium below about 950°C represent combined volume and grain boundary diffusion. This contention is based on the curvature of the penetration plot for our 891°C run,4 which also has a nearly straight line plot of log c vs x. Hagel has extrapolated these characteristics to our 803.5C run and fitted his Arrhenius plot for self-diffusion in y uranium to our four highest temperature points only. We think this is wrong for the following reasons.

Jan 1, 1963

By C. M. Mason

Bureau of Mines studies were made on the sensitivity of several ammonium nitrate-fuel oil (AN-FO) mixtures to bullet impact. The experimental work was done with one military rifle and two high-velocity sporting rifles with a variety of ammunition. For the three rifles used, the order of efficiency in initiating detonation in AN-FO mixtures was 220 Swift >300 Weatherby Magnum >30-&apos;06. The velocity of the bullet was found to be a decisive factor in the initiation. The sensitivity of various materials studied increased as follows: Clay-coated prills with 4 percent oil <fresh surfactant-coated prills with 4 or 6 percent oil <surfactant-coated prills with 4 or 6 percent oil and aged 270 days <crushed prills with 6 percent oil <very low-density, surfactant-coated prills (micronized), with 4 percent oil.

Jan 1, 1963

By John C. Sawyer

The mechanism of catastrophic oxidation of chromium and 446 stainless steel is examined. Data are presented to show that accelerated oxidation of these two materials, as caused by lead oxide, can occur in the absence of a liquid layer contrary to presently accepted theory. An alternate theory is proposed in which the rate of accelerated oxidation is a function of the rate at which lead oxide destroys the protective oxide formed on the base metal. An example of the application of the theory is given for the catastrophic oxidation of chromium in the presence of lead oxide. WHEN stainless iron-, nickel-, or cobalt-base alloys are heated in air to moderate temperatures in the presence of certain metallic oxides, oxidation will proceed at an accelerated rate. This phenomenon, often called "catastrophic oxidation", is most pronounced for the stainless steels. With these alloys the condition is so severe that large masses of oxide will form on the surface of the alloy in 1 hr or less at temperatures of 1200o to 1700oF. While a number of oxides are known to cause this effect, PbO, V2O5, and Moo3 are the most familiar, having been the subject of one or more investigations which have appeared in the literature.1-7 In presenting the results of these investigations, many of the authors have offered possible explanations to account for the more rapid rate of oxidation observed; however, the liquid layer theory as proposed by Rathenau and Meijering 2 has been the most commonly accepted mechanism. The liquid layer theory proposes that a low-melting oxide layer is formed on the surface of the alloy as the result of the interaction of the alloy oxide and the contaminating oxide. When the temperature of oxidation is above the melting point of the oxide on the surface, a liquid layer will form and oxidation will proceed at an accelerated rate. At temperatures below the melting point of the surface oxide, oxidation will proceed more slowly in the normal manner. It is argued that the rates of diffusion of oxygen and metal ions through the liquid layer are extremely rapid thereby accounting for the high rate of oxidation. Various experimental data have been presented to show that the temperature at which accelerated oxidation first becomes apparent coincides with the melting point of the eutectic oxide which would be present on the surface. Some exceptions have been observed, e.g., silver will oxidize in the presence of Moo3 at temperatures below the lowest melting eutectic; on the other hand, stainless steel will not be catastrophically oxidized at 1500oF in a molten bath of PbO and SiO2. In reviewing the various theories which have been used to explain catastrophic oxidation, Kubaschewski and Hopkins 8 favor the liquid layer theory, but note that, ".. .as experimental observations are not altogether in agreement with this theory (liquid layer theory), one should consider it a necessary but not a sufficient condition." In contemplating the liquid layer theory, it appears that sufficient evidence has not been presented to establish the theory beyond question. As a means of further clarification, a program of research was undertaken to determine in greater detail the mechanism of accelerated oxidation as caused by lead oxide. The first part of the program deals with a comparison of the oxidation of both AISI 446 stainless steel and chromium metal in the presence of lead oxide, vs the oxidation of these two materials in air alone. These comparisons are made at a number of different temperatures, most of which are below the melting point of the surface oxides. The second part of the program is concerned with a presentation of an alternate theory of accelerated oxidation exemplified by the system Cr-PbO-Air. PROCEDURE AND RESULTS Several experimental methods are commonly used to follow the progress of oxidation. One of these, the weight-gain method, was chosen for this work. This procedure requires that a specimen of the alloy be weighed, oxidized for a given period of time at an elevated temperature, and reweighed—the difference between the two weights being noted. The weight gain of the specimen represents the amount of oxygen acquired from the atmosphere to transform a portion of the specimen to oxide. In those cases where there is a tendency for the specimen or oxide to volatilize at the testing temperature, additional data must be collected so that a correction factor can be determined. This factor must be applied to the weight change in order to ascertain the actual amount of oxidation which has taken place. The specimens used for this work were 1 1/2 in.

Jan 1, 1963

By W. S. Owen, A. R. Rosenfield

The measured changes in the yield stress of a poly crystalline Ta-O alloy after strain aging at 100°C have been separated into two components; the change inflow stress and the change in dislocation locking parameter. These two components vary independently indicating that at least two separate recovery processes take place during strain-aging. Variations in the locking parameter can be accounted for by segregation of oxygen atoms to dislocations, but variations inflow stress cannot be explained by current theories. STRAIN-AGING in Fe-C and Fe-N alloys has been studied extensively.&apos; The kinetics of the removal of the interstitial solute from solution appear to agree with the predictions of the cottrell-bilby2 model or a variation of it proposed by harper.3 Solute segregates to the dislocations under the influence of the elastic strain field of the dislocation and the rate of depletion of the solute can be measured by following the change in electrical resistivity4 or internal friction.5 On reloading a prestrained specimen, plastic flow starts at Fig. 1, but after aging the reloaded specimen yields discontinuously at a higher stress The aging index reflects the extent to which the yield has returned. Until recently it was usual to assume that ? is a result solely of the pinning of dislocations by the segregated solute atoms, that is, that op and oj coincide and the strain hardening curves AB and CD are continuous. Thomas

Jan 1, 1963

By F. B. Petermann

Two-stage electric smelting tests, using small submerged arc furnaces, were made on high-iron manganiferous materials from the Pioche District, Nev., and the Cuyuna Range, Minn. The object was to reduce sufficient iron in the first stage to give a slag with a favorable Mn to Fe ratio for smelting to ferromanganese in the second stage. The nodulized flotation concentrate from the Pioche District contained 29.2 percent Mn and had a Mn to Fe ratio of 2.3:l. When smelted with coke and silica or alumina as flux, more than 90 percent of the manganese was recovered in slags with Mn to Fe ratios of 10: :24:1. The Pioche slag was smelted to ferromanganese using coke and lime- stone or dolomite as flux. The ferromanganese was high in silicon but other- wise met specifications. Recovery of manganese to ferromanganese in this step was 73 to 78 percent. Overall recovery of manganese was about 70 percent. The sintered flotation concentrate from the Cuyuna Range material contained 12.9 percent Mn and had a Mn to Fe ratio of 0.3:1. When smelted with limestone as flux, about 83 percent of the manganese was recovered in a slag with a Mn to Fe ratio of about 6:1. The Cuyuna slag was smelted to ferromanganese with coke and limestone for flux. Recovery in this step was 61 percent of the manganese in a high silicon ferromanganese. Overall recovery of manganese was about 50 percent.

Jan 1, 1963

By A. R. Taylor

The Bureau of Mines has determined the heat capacity and enthalpy values for beryllium sulfate (BeS04) throughout the temperature ranges of 10° to 300° K in an adiabatic calorimeter, and 350° to 860° K in a Bunsen-type ice calorimter, The heat-capacity data were extrapolated to 0° K, and smooth values of heat capacity, entropy, enthalpy function, and free-energy function were reported at 10-degree intervals between 0° and 300° K. The method of least squares was used to fit the enthalpy data with an algebraic equation. The equation also was used to calculate values of heat capacity, entropy, enthalpy function, and free-energy function at 50-degree intervals between 300° and 900° K.

Jan 1, 1963

By César Alvarado Olivares

El presente trabajo describe la solución planteada al problema de renovar el equipo de celdas de flotación que por el tiempo de uso (19 años) y por su tipo de diseño, ya no ofrecfa el rendimiento que hoy en día se puede conseguir en esta clase de tratamiento. La solución consiste en

Jan 1, 1963

By E. J. Rapperport, E. D. Levine

The boundaries of the (a +ß) field in the Al-Li system were determined between 150°and 550°C utilizing quantitative metallography and lattice-parameter measurements. The solubility of lithium in aluminum decreases from 12.0at. pct Li at 550°C to 5.5 at. pct Li at 150°C. P Al-Li is saturated with aluminum at 45.8 at. pct Li and has this boundary value constant over the temperature range 150°to 550°C. THE solid solubility of lithium in aluminum has been determined by several investigators, 1-6 but, as shown in Fig. 1, there is little agreement among the various determinations. The earliest investiga-tions&apos;-&apos; are suspect because of the use of impure materials. Although high-purity materials were employed in more recent work,4&apos;5 the experimental techniques may have led to contamination of the specimens. Probably the best work has been that of Costas and Marshall,6 who obtained close agreement between results obtained by two independent phase-boundary techniques: electrical resistivity and mi-crohardness. No detailed studies of the solubility of aluminum in the bcc ß phase, Al-Li, have been reported. Cursory investigations1,2,6 have indicated only that the (a+ß) -p boundary lies between 40 and 50 at. pct Li and is relatively independent of temperature. The present work was undertaken in order to provide an independent check on Costas and Marshall&apos;s determination of the solubility of lithium in aluminum, to extend knowledge of this solubility limit to temperatures below 225°C, and to make an accurate determination of the solubility of aluminum in Al-Li. EXPEFUMENTAL Alloy Preparation. In view of the difficulties encountered in previous investigations of the A1-Li system, close attention was paid to the use of methods of alloy preparation and treatment that would minimize contamination. Aluminum sheet (99.99 + pct Al) was vacuum-induction melted in a beryllia crucible to remove hydrogen. Lithium (99.9 pct Li) was charged with pre-melted aluminum into a beryllia crucible, in a helium-filled drybox. The crucible was sealed in a Vycor tube and transferred from the drybox to an induction furnace. Melting of alloys was performed by induction heating in a helium atmosphere. Solidification was accomplished by means of a suction apparatus, shown in Fig. 2, in which the alloy was forced by changes of pressure into a 3/16-in. inside diam closed-end beryllia tube. This technique produced rapid solidification of a small portion of the melt, resulting in alloys with a high degree of homogeneity. Typical lithium distributions are presented in Table I. Transverse sections 1/8 in. long were cut from the alloy rods, and each section was split in half longitudinally. One half of each section was analyzed for lithium, and the opposing halves were employed for phase-boundary determinations. Lithium contents were determined by flame photometry with an accuracy of 1 pct of the amount of lithium present. Thermal Treatments. Homogenization and equilibration heat treatments were performed in electrical-resistance furnaces with temperatures controlled to ± 2OC. Calibrated chromel-alumel thermocouples were employed to measure temperature. Homogenization was performed in helium-filled l?yrex tubes for 1 hr at 565°C. The encapsulated specimens were then transferred directly to furnaces maintained at lower temperatures for equilibration. Equilibration times were 2 hr at 550°C, 8 hr at 450°C, 27 hr at 350°c, 90 hr at 250°c, and 285 hr at 150"~. These times were chosen on the basis of conditions employed by previous investigators. Alloys were quenched from the equilibration temperatures by breaking the capsules into a silicone oil bath. By performing all possible operations either in sealed capsules or in a helium-filled drybox, the specimens were given minimum exposure to the atmosphere. Quantitative Metallography. Metallography of Al-Li alloys is difficult because of the atmospheric reactivity of the ß phase. It was found possible, however, to prepare surfaces of good metallographic quality by preventing contact with moisture during preparation. Grinding through 4/0 paper was performed in the drybox. The specimens were then transferred under kerosene to the polishing wheel. Three polishing stages were employed: 25-p alundum with kerosene lubricant on billiard cloth, 1-µ diamond paste on Microcloth, and 1/4-p diamond paste on Microcloth. Between stages the samples were cleaned by rinsing in trichloroethylene and buffing

Jan 1, 1963

By George Simkovich

It was hypothesized that solid-state point defects should alter the flotation properties of solids. Tests conducted on pure AgCl and AgCl doped with CdC12 show that atomic point defects exhibit an important role in the floatability of AgC1. Tests conducted on PbS doped with Ag2s or Bi2S3, also show that the defect structures resulting from these dope additions, i.e., a combination of electronic and atomic point defects, contribute significantly to the flotation of PbS. IT has been established that flotation occurs only when a finite contact angle exists between a solid and a gaseous bubble.&apos; This angle, measured through the liquid phase, is expressed by the equation where the are inter facial free energies and the subscripts S, G, and L represent solid, gas, and liquid phases, respectively. As is seen in Eq. [I] three interface free energies, sG, sl, and GL, enter into the contact angle equation. Therefore, any variation in these energies which sufficiently varies the contact angle will, in turn, vary flotation processes. Changes made in any of the phases concerned, i.e., gas, liquid, or solid phase, are reflected through the changes occurring in two of the surface energy terms. Thus, a change in the liquid composition would be noted in sL and GL, and it is this phase, the liquid, which is most frequently altered in flotation studies., Changes in the solid phase must be reflected through the changes occurring in the sG and sL terms. In particular, it is hypothesized that changes in the surface concentrations of point defects in the solid-phase will alter the sG and sL terms which, in turn, will be reflected by flotation results. As an illustration of this hypothesis one may consider the defect structure and the flotation of AgC1. The bulk defect structure of AgCl is essentially one involving equal number of cation vacancies and interstitial cations.3 Upon adding CdC1, to AgC1, a greater number of silver ion vacancies are created in the bulk of the crystal.4 On the surface of the crystal the smaller binding forces and the free space accomodations may also allow for the creation of "surface interstitial anions", which will be designated as ad-anions. Thus, the point defect structure of the surface of AgCl doped with CdCl, will consist of cation vacancies and/or adanions. If the molecular forces responsible for the surface energies, ?SG and ?sL, are significantly altered by the presence of these surface point defects, then differences in flotation results will be noted as the concentration of these defects is varied. The defects present in AgCl are predominantly atomic in nature. In the case of PbS both electronic and atomic defects are present.5 This compound conducts electrically by either electrons or electron holes depending upon whether excess lead or excess sulfur is present. Upon disolving BiS3 in stoichio-metric PbS, one increases the concentration of cation vacancies and the number of electron carriers in the bulk of the crystal.5" At the surface, the possibility of ad-anions must also be considered. Conversely, upon dissolving AgS in stoichiometric PbS one increases the concentration of interstitial cations and the number of electronhole carriers in the bulk of the crystal.5,6&apos; At the surface the interstitial cations will be designated as ad-cations. Thus, the point defect structure of the surface of a PbS crystal doped with Bi2S3 will consist of a number of cation vacancies and/or ad-anions and an excess of electrons. Conversely the point defects on the surface of a PbS crystal doped with Ag2S will consist of a number of ad-cations and an excess of electron holes. Again, as in the case of AgC1, should the molecular forces responsible for the magnitude of the interface free energies, ?sG and ?sL, be significantly altered by the presence of these surface defects then significant differences in flotation results will be noted as the concentration of these defects is varied. EXPERIMENTAL To test this hypothesis flotation tests were conducted on pure and doped AgCl and on PbS doped with either Bi2S3 or Ag2S. Preparation of the AgCl samples was performed as follows: AgCl and weighed amounts of CdC1, were melted in a porcelain crucible. The melt was then forced through a capillary tube and the particles emitted solidified in air as they fell about 1.5 meters. Spherical particles, -0.50 + 0.25 mm, were separated from the remaining solidified material

Jan 1, 1963

By Leonard F. Heising

At the Groveland mine iron ore is mined by open-pit methods and concentrated by means of spirals and flotation. A brief history of the mine and its early development is given. The ore deposit is described, with emphasis on those physical characteristics that affect the choice of mining and milling methods. Development and mining, which include breaking ground, loading, transportation, engineering, and operating control, are explained, and the milling method is described Mining and milling costs are given in percent of total cost.

Jan 1, 1963

By C. O. Hawk

As an exploratory effort to produce useful products from coal by a new path, the Bureau has made a few experiments on the fast heating of finely ground coal particles by irradiation with a flash of high intensity light. The flash was produced by an electrical discharge at high voltage through a xenon-filled tube. The flashes lasted from 2 to 3 milliseconds. The reaction took place in small sample tubes, ½ inch-dimeter by 4 inches long, and with small amounts of coal (total amount charged 0.1 gram, probable effective amount not more than 20 milligrams). Average particle size of the coal, estimated on a numerical basis, was 20 microns. Temperatures reached were evidently quite high, because all products obtained in quantity were characteristic of high temperature pyrolysis. Apparently, conversion of the coal was extensive where isolated particles received the full benefit of a flash. It seems particularly significant that acetylene was present in appreciable amounts--comprising almost 3 percent of the total gaseous product in one case. This is good evidence of a short heating period to very high temperature (well above 1,000° C) followed by rapid quenching. Although the results are interesting, they do not suggest any immediate practical application.

Jan 1, 1963