By J. R. Cahoon, W. V. Youdelis

In a previous communication by one of us,1 a theory of inverse segregation was presented by which the maximum segregation and segregation distribution throughout a unidirectionally solidified, binary-alloy ingot could be calculated. The theory, which is based on the mechanism of volume contraction and interdendritic flow, quantitatively accounts for the observed maximum segregation in the A1 (rich)-CU' and Al-Zn2 alloy systems, and for the segregation distribution along the ingot lengths for the A1-Cu system.''4 One of the drawbacks to a more extensive use of the segregation equations is their complexity, particularly for the calculation of the segregation distribution throughout the length of the ingot, involving long tedious numerical calculations to obtain the segregation. Computer pro- grams, written in Fortran II for use on an IBM 1620 computer, have been developed by the authors (and are available from them), providing quick and accurate methods for the determination of the theoretical maximum segregation in any binary-alloy system, and also for the segregation distribution in any unidirectionally solidified binary-alloy ingot. The segregation distribution is controlled by the lengths of the various solidification zones'74 which are in turn controlled by the cooling rate, and are determined from temperature-distribution curves obtained during solidification. The theoretical segregation distributions shown in Fig. 1 illustrate the effect of the zone lengths on the distribution Curve 1, indicative of a slowly cooled ingot, represents an ingot having long solidification zones, while Curve 2, indicative of a rapidly cooled ingot, represents an ingot having relatively short zones. Although these distributions are calculated for an A1-10 pct Cu ingot, the shape of the distribution would be similar for any binary-alloy ingot. These curves show clearly why early workers obtained results which indicated that the maximum (chill-face) segregation approached zero at very fast cooling rates.3 Actually, the maximum segregation is independent of cooling rate,' but even at short distances from the chill face the amount of segregation drops considerably, particularly in a rapidly cooled ingot, making it very difficult to establish the amount of segregation occurring at the chill-face. The authors would like to thank Dr. J. A. Goldak for his assistance in the preparation of the programs. The financial assistance of the Steel Co. of Canada and of the National Research Council of Canada in the form of Scholarships to one of us (J. R. Cahoon) is gratefully acknowledged.

Jan 1, 1964

By R. A. Vandermeer, C. J. McHargue

The (001) fiber-texture component, found in aluminum rods extruded at subzero temperatures, consists of particles of various sizes having extremely irregular shapes dispersed in a nonuniform way throughout a matrix of the (111) orientation. Apparently the (001) texture component is not a result of recrystallization but rather is due to the presence of reimanents of the original grains which fragmented from the main body of material as it reoriented towards the (111) orientation during the extrusion process. Both X-ray line-broadening measurements and electron-microscopic observatwns indicate that, after extrusion, regions having (001) orientations are in a state of relatively less strain and distortion than (111) regions, suggesting that the former have undergone less plastic deformation. A (001) fiber-texture component is also found after complete recrystallization of extruded specimens. Approximately one third of the recrys-stallized volume has this orientation. The (001) fragments, formed during the extrusion process, act as nuclei for recrystallization; i.e., the pain boundaries separating these fragments from the matrix are capable of migrating during annealing. Electron-transmission microscopic observations and X-ray line-broadening measurements indicate that (001) regions recover at a much more rapid rate than (111) regions at annealing temperatures up to 187°C. DURING the extrusion of a rod or the drawing of a wire the individual grains comprising the piece tend to reorient towards a preferred orientation (texture) which is of the fiber type where a particular crys-tallographic direction, (uvw), in each crystallite tends to be aligned parallel to the longitudinal axis

Jan 1, 1964

By B. S. Graves

Deep well disposal of selected industrial wastes has been proved feasible and acceptable in the New Orleans area by several industries including Shell Oil Company's Norco Refinery and Chemical Plant where three of the six successful disposal wells in this area are operating. Well design and procedures for restoration of capacity are based, in most cases, on the principles of brine injection developed by oil producers in South Louisiana. Geological formations in the Gulf Coast area are suited to this type of injection because receiving strata are porous, isolated from sources of potable water and their water is compatible with the liquid wastes to be injected. This method of disposal is a simple, complete and economical solution to the problems presented by certain hard to treat wastes.

Jan 1, 1964

By E. H. Hall

"Perhaps .I should start this talk on Arsine poisoning, by giving a brief background and history of the Bralorne Mill.The present Bralorne company started milling operations in 1932, with amalgamation and flotation, and operated continuously until 19 61 . In 19 59, it was decided to change over to cyanidation, and to use double filtration rather than counter current. The cyanide portion of this new plant was completed and went on stream in August 1961 utilizing the grinding circuit of the old flotation plant. The new grinding circuit was completed and started operating December 15, 1961.The grinding circuit consists of a 7 1 x 101 Hardinge Rod Mill, and a 7 1 x 101 Hardinge Ball Mill. In series with the rod mill is a 16"" x 24"" Denver Duplex Jig, and two of these jigs are also in parallel with the ball mill. The rod mill product is classified by a Kreb cyclone, the oversize going to the ball mill. The ball mill is in closed circuit with this same cyclone. The jig products are amalgamated daily, and the amalgam barrel tails are returned to the ball mill for regrind. Arsenious oxide (As203) is one of the reagents used in amalgamation. Approximately 39 ozs. per day is used.The cyanide circuit consists of a 481 x 121 thickener, three 24' x 24' agitators, two 141 x 161 drum filters and a Merrill Crowe precipitation unit.The Krebcone overflow is thickened to 60 - 62% solids. Hydrated lime, along with a settling agent is added to the thickener. Some of the overflow water from the thickener is returned for use in the jigs. The balance of this overflow water goes to waste. To the thickened pulp entering No. 1 agitator, barren solution is added, along with sodium cyanide and hydrated lime. Cyanide strength is held at 0. 9 - 1. 0 lbs/ ton solution and lime at 0. 8 lbs/ ton solution. The lime content usually drops to 0. 5 lbs/ ton in No. 3 agitator. The two drum filters are in series and are washed with barren solution. The discharge of No. 3 agitator is fed to No. 1 filter and the discharge of No. 1 filter is repulped in barren solution and feeds No. 2 filter. No. 2 filter discharges to tails, The filtrate is clarified, deaerated and the gold precipitated. One hundred to two hundred tons of barren solution are bled to waste each day. The ore contains 1 % Arsenopyrite and 1. 5% Pyrite."

Jan 1, 1964

By J. E. Steiner, J. M. Hodge, M. A. Orehoski

Ingots of four steels (1045, 1080, Ni-Mo-V, and Ni-Cr-Mo-V) were cast at pressures varying from about 1 to 760 mm of mercury, so as to obtain a range of hydrogen contents in each steel. The susceptibility of these steels to flaking was evaluated by cooling hot-rolled blooms at a range of cooling rates, varying from water quenching to slag cooling, and studying the occurrence of flaking as a function of cooling rate. The steels exhibited differences in susceptibility to flaking, and a tlzreshold value for hydrogen content for each steel was found, below which the susceptibility was very low and above which the susceptibility increased markedly with increasing hydrogen content. Mechanical property evaluations, metallogvaplzic exantinations, and X-my diffraction determinations o,t retained austenite were made on samples from the blooms. A mechanism of flaking which is consistent with the observed behaviors, the effects of hvdrogen content, and the differences in susceptibility among the steels investigated is postulated, based on the results of mechanical property evaluations and metallographic and X-ray diffraction studies. ThE important role of hydrogen as a factor in the occurrence of "flakes" or "hair-line cracks" in steel has now been established by many investigations. These have included investigations by steel producers and forging manufacturers, to whom the prevention of flaking is a very real and serious problem, and many research studies aimed primarily at establishing the mechanism of this behavior Several investigators3 have reported that steels cast at reduced pressures (absolute pressures of about 1 mm) not only are low in hydrogen content but are essentially insensitive to the formation of flakes. These investigations have shown that a general relationship exists between hydrogen content and susceptibility to flaking. The difficulty of obtaining suitable samples of steels of a given composition with the desired range of hydrogen contents, particularly in the relatively large sections in which flaking most commonly occurs, has been the principal obstacle to quantitative evaluations of these relationships. Steels with intermediate hydrogen contents between 1 ppm, and the 4ppm or higher of air-cast steels are generally not available in commercially produced steels. Laboratory procedures, in which the hydrogen is introduced into solid steel samples by heating in a hydrogen atmosphere under pressure, generally involve a limitation in the size of the sample which can be treated, and thus are not representative of the behaviors in large sections. The availability of a facility at the South Chicago Works of U.S. Steel, in which several ingots could be cast from a single heat of steel at total air pressures ranging from 0.25 to 760 mm of Hg, has made it possible to overcome this obstacle and to obtain ingots of a given steel covering the intermediate range of hydrogen contents desired. These ingots, furthermore, are of a size suitable for the production of product with section sizes large enough to be representative of the products in which flaking most commonly occurs in commercial production. In these experiments, this facility was used to study the relationships between hydrogen content and the susceptibility to flaking of four steels, two plain carbon steels at 0.45 and 0.80 pct C and two low-carbon alloy steels representing a medium and a rather high hardenability level. These flaking studies were supplemented by evaluations of mechanical properties and by metallographic studies on samples from the blooms, in order to obtain pertinent information on the factors other than hydrogen content which influence the susceptibilities of these steels to flaking. Based on the results of these tests, a mechanism for the initiation and propagation of the flaking cracks, which is consistent with the observed behaviors, is postulated. MATERIALS AND EXPERIMENTAL WORK Steelmaking and Conversion. To provide material for the investigation, five 29- by 35-in., hot-topped, big-end-up ingots were cast from each of four 80-ton, basic electric-furnace heats of four different steels (a 1045 steel, a 1080 steel, a Ni-Mo-V steel, and a Ni-Cr-Mo-V steel). A double-slag practice was used on all steels and the two plain carbon steels were Si-A1 deoxidized with an addition of 2 lb of A1 per ton, while the Ni-Mo-V and Ni-Cr-Mo-V steels were deoxidized only with silicon and

Jan 1, 1964

By Charles R. Boardman

Recent underground nuclear tests in tuff, alluvium, salt, and granite have yielded data essential to the evaluation of mining applications of contained nuclear detonations. The data indicate that for these media the cavity radius is predictable within ±20% without regard to the properties of the rock in the immediate shot environment. Properties of the chimney of broken rock resulting from collapse of the cavity, on the other hand, are found to be related to the properties of the rock and its preshot structural weaknesses. Seismic effects and radioactivity distribution are sufficiently documented to serve as a basis for predicting the safety conditions associated with detonations for a variety of yields.

Jan 1, 1964

By B. Tani, K. Anderson, I. Johnson, R. Schablaske

INVESTIGATION of the various rare earth-cadmium binary systems discloses the existence of a compound corresponding to the composition MCd6 in all systems save the La-Cd system. Lattice constants for all of the MCde compounds, except LaCd6 which apparently does not form, and PmCd6 whose synthesis was not attempted, are also recorded herein. Iandelli and Ferro 1 report the existence of the compound CeCd6. No additional information, structural details, and so forth are given. Elliott and Lemons2,3' have measured the vapor pressure of cadmium over CeCd6 and have calculated the activity of cadmium in solid CeCd6. These authors find that CeCd6 exists over a composition range from 5.967 to 6.098 (Cd:Ce ratio) at 584oC, and from 5.971 to 6.118 at 639°C. The following is an excerpt from the paper by Elliott and Lemons: 2 "Recently Mr. F. H. Ellinger of this laboratory has indexed an X-ray diffraction powder pattern of CeCd6.00 which we had prepared by gas phase reaction. The compound has a primitive cubic unit cell with a = 15.783 + 0.001A Based on the volume of the cubes surrounding an elemental cerium or an elemental cadmium atom, Mr. Ellinger finds room for 24.10 CeCd6 formula units in the CeCd6 unit cell; similar calculations based on CeCd2 and CeCd11 yield 24.18 formula units per unit cell. The presence of 24 CeCd6 units per unit cell seems probable with an X-ray density of 8.255 grams per cubic centimeter. The most one can say about in-terstitial~ is that there appears to be room in the crystal even at room temperature." Measurements of the solubility of the rare earths in liquid cadmium4 led to the discovery of GdCd6,

Jan 1, 1964

Cominco began investigations about ten years ago relative to noise abatement in underground operations. As a result of intensive research, this study has advanced so that the practice now has wide application. Automotive mufflers are used on vane-type blasthole diamond drills. Exhaust hoses are attached to longhole percussion drills. Hand-held drills, such as airlegs and stopers, are equipped with mufflers which are either part of the drill, as received from the manufacturer, or are light rubber de-vices developed, fabricated and installed by Cominco. Ear defenders are in general use. The paper reviews details of practices employed, and assesses the success achieved. Noise is generally associated with some of the basic equipment used in mining. About ten years ago, in order to improve on this situation. The Consolidated Mining and Smelting Company of Canada Limited began investigations relative to noise abatement in its underground operations. As a result of intensive research, this study has advanced to the point

Jan 1, 1964

By Jei Y. Choi, P. G. Shewmon

The surfrrce-diffusion coefficients (DJ for Aulg8 on (100) and (111) surfaces of copper have been determined between 1050" and 780°C using a new avuzlysis imd experimental procedure. The results are: D, has also been determined fm cua4 at 870°C, and the values found are 4.5 times larger than those measured by the grain boundary grooving technique for the same surface orientations. This difference is felt to result from the approximate nature of the mathematical solution used in the present work. Attempts to measure D, for silver on copper and silver surfaces indicated a means of matter transport different from surface diffision was dominant in moving tracer from the source out over the surface. Cnlculations and experiment both indicate that this is the flow of silver through the vapor phase which completely masks the much smaller flow due to surface diffusion. The previous self-difhsion studies of D, for silver and copper are discussed in terms of our own analysis and found to yield values of D, factors of lo5 or more greater than those found by the grain boundary grooving tech -nique. UNTIL about 5 years ago it was widely believed that the activation energy for surface diffusion, AH, , was less than that for grain boundary diffusion, AHb,, which in turn was less than that for diffusion through the lattice, AHz.' This was concluded from various evidence that D,> Db>Dl, and one tracer study of D, for silver on silver from which AH, was inferred.2 In 1959 Mullins and Shewmon demonstrated that D, could be determined from the kinetics of the growth of grain-boundary grooves.3 Using this procedure, Gjostein measured D, on copper between 800" and 1050°C and found that the activation energy was roughly equal to AHl .4 Subsequent work on copper,5" silver,',' and goldg between the melting temperature T, and 0.87 T, confirmed that AH, as determined using the grain boundary grooving or scratch-relaxation technique was equal to or greater than AHz. During the same period, Drew and Pye again determined AH, for silver on silver using a tracer techniquelo and a mathematical solution similar to that of Nicker son and arker.' Though the values of D, Drew and Pye measured at any given temperature were about 200 times smaller than those reported by Nickerson and Parker, they again found a low activation energy of about 10 kcal, or about one fifth that found at the higher temperatures with the mass transport technique. A distinguishing characteristic of these two previous tracer studies is that they have worked at low temperatures (-1/2 T,) where they felt volume diffusion was negligible and then analyzed these data as if all tracer atoms leaving the source flowed out into and remained in a homogeneous high-diffusivity surface layer of undefined thickness. This is totally different from the model used in the mass-transport studies or the studies of grain boundary diffusion, which assume the high-diffusivity surface layer to be only a few angstroms thick. If this latter model is applied to the earlier tracer studies, it is shown that the tracer has really pe!etrated into the lattice a mean distance of 1000A. Thus the tracer distribution observed after an anneal is thought to be due to the combined effects of surface and volume diffusion. Independent of the relative validity of the two models, it seems evident to us that any comparison of the values of D, as determined in these two ways is meaningless and misleading, since the values of D, and AH, obtained in these two ways would be totally different for the same physical distributions of tracer. Once the fundamental difference in the approaches of the two techniques is established, we are faced with the question of which model better approximates physical reality. Here all the evidence seems to be on the side of the ''thin surface layer" analysis. In fact, the authors of Refs. 2 and 9 do not argue for the "thick-layer model" we have described; they simply invoke it through the equation they use to calculate D, . The primary evidence for the thin-film approach is: a) grain boundary grooves and scratches widen in proportion to tU4 and Mullins' rigorous analysis shows that this is only valid for a surface layer which is quite thin relative to the width of the groove;11 b) all accepted or seriously discussed models of solid-vapor interfaces and high-angle grain boundaries assume that the disturbed region of the interface is at most a few a0 thick. With the above in mind, it was desirable to determine D, using a radioactive tracer and a "thin-

Jan 1, 1964

By H. L. Lovell

The growing production of fly ash with the many attendant problems of economics, disposal and potential uses suggests an urgent need to consider those properties which are basic in its beneficiation. Fly ash is extremely variable and heterogeneous in all respects except its fine size. Because of its production in huge quantities, it becomes significant as a potential raw material. Detailed data are presented describing particle size and shape, density distribution and magnetic characteristics. The major components include combustible residuals, magnetite and silicates. These data are discussed in terms of beneficiation processes and uses, The results of air classification to produce a uniformly fine-sized low combustible product are encouraging. It is proposed that major increases in the future use of fly ash, must involve some form of beneficiation. Both the coal producing industries and the consuming utilities would benefit from increased utilization.

Jan 1, 1964

By J. F. Breedis

The morphology and crystallography of marten -site formed during quenclzing were examined by transmission electron microscopy in alloys whose compositions lie between Fe-19 wt pct Cr-11 wt pet Ni and Fe-33 wt pet Ni. Depending upon composition, four types of transformation products were observed in this portion of the Fe-Cr-Ni system. Three of these products are denoted as lath, plate, and surface martensite. The hcp structure found in association with martensite it? certain higlz-clzromium stairzless steels does not influence the transformation crystallogyaphy and cannot he Considered to act as a transitional structure in the transformation from austenite to martensite. DISTINCT changes in the characteristics of mar-tensitic transformations are produced by the partial replacement of nickel by chromium in austenitic iron alloys. Large, discrete martensite plates form in Fe-30 pct Ni, while aggregates of small crystals form in sheets parallel with (111)A austenite planes in stainless steels containing in the vicinity of 18 pct Cr and 8 pct Ni. These transformation structures are termed plate and lath martensite, respectively. In addition, an hcp structure (E) has been observed in certain high-chromium stainless steels in association with martensite. It has been suggested that the E structure acts as an intermediate step in the nucleation of martensitel-' and influences the morphology and crystallography of the final transformation product. However, this structure may be the consequence of the deformation of austenite arising from the shape distortion accompanying the transformation to bcc martensite.' An hcp stacking of atoms is produced in an fcc lattice by the introduction of an intrinsic stacking fault on alternate (111)A planes. At present, the arguments behind each explanation for the E structure are based on circumstantial evidence. This investigation seeks to determine the importance of the hcp structure to the martensitic transformation, and to examine the crystallography and morphology of the structures produced in bulk samples by quenching in alloys whose compositions lie between Fe-19 wt pct Cr-11 wt pct Ni and Fe-33 wt pct Ni. These aspects of the martensitic transformations occurring in these alloys have been studied by electron metallography and selected-area diffraction of foils examined in transmission in the electron microscope. EXPERIMENTAL METHODS The alloys have been prepared from thoroughly mixed powders of pure iron (99.6+ pct, 0.06 max pct C, 0.15 max pct N), chromium (99.9+ pct), and nickel (99.9+ pct). After sintering in an Ar-H2 atmosphere, the mixtures were melted by induction heating in recrystallized alumina boats under purified argon. The ingots were cold-rolled to 0.4-mm sheets (100 pct reduction in thickness) after the removal of at least 1.5 mm from their surfaces by grinding. Three-millimeter discs were punched from the cold-rolled sheet and annealed at 1150°C for approximately 24 hr in evacuated quartz capsules. The average grain size was 40 µ Thin foils for examination in transmission in the electron microscope were prepared from discs quenched to liquid-nitrogen temperature. A depression was first jet-machined into the center of a disc and a thin area (less than approximately 3000A in thickness) was produced at the base of the depression by electropolishing. Electron-microscope studies utilized the RCA EMU-3 and the Philips EM-100B microscopes operating at 100 kv. X-ray examination of the polycrystalline alloys was performed either in a diffractometer or in a

Jan 1, 1964

By P. Beardmore, A. H. Holtzman, M. B. Bever

Specimens of the alloy CU3AU in the ordered and disordered states were subjected to explosive loading at shock pressures in the range from 160 to 475 kbars. The resulting changes in the resistivity, stored energy, microhardness, and microstructure were determined. By comparing the effects of explosive loading on ordered and disordered specimens a separation of structura1 and configurational changes has been made. In the pressure range from 290 to 370 kbars, representing a small increment of strain, the degree of long-range order in the ordered alloy decreased sharply. This change is attributed to the generation of shear stresses in excess of the theoretical shear strength of the alloy. Disordered CU3AU under explosive loading behaves in a manner considered to be characteristic of fee solid-solution alloys generally. The response of metals to high-velocity deformation and, in particular, to explosive loading has attracted much interest in recent years.' In general, metals are substantially strengthened by the passage of shock waves although the permanent strains are small. Explosive loading induces this strengthening by causing the metal to undergo rapidly a transient strain in a narrow region, first in the shock front and then in the rarefaction wave, which releases the pressure. The transient strain is given by e = 4/3 In V/Vo, where Vo and v are the specific volumes in the uncompressed and compressed states.2 The process produces many defects, which account for the strengthening. For the investigation reported here, an ordered alloy was chosen because it was expected to give sensitive indications of the near-neighbor effects produced by shock waves. The ordered alloy CU3AU was of special interest because of past work on the effects of conventional deformation on this alloy.314 The disordered alloy was included as a standard for comparison and as an alloy typical of a solid solution containing short-range order. The effects of explosive loading were followed by measurements of the resistivity, stored energy, and microhardness, and by metallographic examination. EXPERIMENTAL PROCEDURES Preparation of Specimens. Part of an ingot of the alloy Cu3Au prepared previously4 was cold-rolled with several intermediate anneals in vacuum to a final thickness of 0.042 in. Specimens of dimensions 2.0 by 1.0 by 0.042 in. were machined from this strip. After a recrystallization treatment of 1 hr at 565oC, half of the specimens were disordered by heating in evacuated Pyrex capsules for 1 hr at 460°C and quenching into water. Although they contained short-range order, they will be referred to as 'disordered" to indicate the absence of long-range order. The rest of the specimens were cooled slowly from 380°C to induce long-range order. The grain size of the ordered and disordered specimens was 0.012 mm. Explosive Loading. This was carried out at the Eastern Laboratory, Explosives Department, E. I. du Pont de Nemours & Co., by a driver-plate procedure described elsewhere.2 Two ordered specimens were stacked alongside two disordered speci-

Jan 1, 1964

By R. S. Kinasevich, D. D. Crabtree, D. W. Fuerstenau, T. P. Meloy, A. L. Mular

This paper presents details of the concept that size reduction in comminution machines takes place by three mechanisms; namely impact, abrasion, and chipping grinding. Experimental evidence is presented to show that each of these comminution mechanisms produces particles of a characteristic size distribution. The actual product from a comminution device has been postulated to be the result of a composite of these three types of mechanisms. Composite curves are demonstrated for a material following the Gaudin-Schuhmann, Gaudin-Meloy, and Rosin-Rammler size distributions. About forty years ago, Gaudin1 showed that grinding may be considered a combination of impact and attrition. Since that time, major efforts have been devoted to studies, both experimental and theoretical, of impact and compression fracture, while attrition has been almost wholly neglected, at least quantitatively. A significant attempt to distinguish between attrition and impact grinding is the work of Tanaka2 in Japan. By means of an instrumented abrasion grinder and a drop weight device, he determined coefficients relating the increase in surface area of various materials to the energy expended by the two methods of comminution. He showed that physical properties of a material determine its response to attrition and impact grinding. By extending his ideas to ball milling, he concluded that to a large extent the basic comminution process in a ball mill is due to the impact of falling media. Because Tanaka used a mass of particles in his drop weight device, however, he did not obtain pure impact size reduction. The purpose of this paper is to define basic mechanisms of size reduction, to verify that each has a characteristic and meaningful distribution curve, and to show how a combination of these mechanisms results in a size distribution very like that produced by grinding mills. DEFINITION OF COMMINUTION MECHANISMS The product from a grinding device will be considered to be the sum of the contributions resulting from the action of three basic mechanisms of size reduction which operate in a ball and rod mill. These are impact grinding and two forms of attrition, namely abrasion grinding and chipping grinding. Each is defined below. Impact Grinding: If a straight line is obtained when the cumulative weight fraction finer than a given size is plotted on log-log paper as a function of that size, the slope of the line is defined as the distribution modulus. A number of investigators 3,4,5 have shown that impact fracture of single specimens of different composition and shape results in a distribution of daughter particles that exhibit a distribution modulus of unity. This has also been true for materials broken in slow compression. Moreover, under slow compression or impact fracture conditions, theoretical distribution equations6*' which approximate the Gaudin-Schuhmann distribution when the distribution modulus is close to unity agree reasonably well with the experimentally obtained products. If one now considers a comminution process where many impact or compression fracture events are taking place, then any rational summation of the individual events yields, in the finer size range, a Gaudin-Schuhmann distribution whose distribution modulus is also unity. If the size distribution of the product from a mill has a distribution modulus of unity, it is implied that particles are fractured in a manner which results in a comminution event having a distribution like that obtained for the breakage of single specimens. These impact events would occur when a particle is smashed between balls or between a ball and the mill liner. Attrition, on the other hand, is that form of grinding which cannot be called impact grinding, and comprises both abrasion and chipping grinding. Abrasion Grinding: Abrasion is a form of surface wear resulting when particles rub against each other or against balls or the mill liner of a tumbling mill, somewhat like a piece of wood being rubbed over a piece of sandpaper. The surface wears at a more or

Jan 1, 1964

By J. W. Spretnak, G. W. King

THE crystallography and morphology of 0-Al,Fe precipitates in an A1 + 0.5 wt pct Fe alloy have been studied by transmission electron microscopy. The alloy was cast in cylindrical ingots, 15 cm in diameter and 60 cm in length, and cooled slowly. The measured composition was 0.527 wt pct Fe, 0.001 wt pct Mg, and 0.003 wt pct Cu. Spectrographic analysis revealed no additional trace impurities. Thin slices were cut from the ingot and reduced by more than 95 pct by rolling to a thickness of 0.1 mm with no intermediate annealing treatments. These thin sheets were then vacuum-annealed for 1 hr at 612°C and air-cooled in their capsules. Thin foils for examination in the electron microscope were prepared by electropolishing. The precipitate is found in the form of oval platelets on the (110) planes of the matrix. The major axes of the platelets are parallel to the (110) directions of the matrix, and vary in length from 1/2 to 2 p. The thickness is about 1/10 p. Examples of platelets, both in the plane of the foil and normal to the foil, are shown in Figs. l(a) and l(b), respectively. lack' found that ?-A13Fe (more correctly All13Fe4) belongs to the monoclinic system. Using Black's structural data and simultaneous electron-diffraction patterns from the matrix and precipitates, the habit planes and directions were determined to be: (00l)? || (110)Al [100]? || [001]Al The orthogonal crystallographic axes of the precipitates are accurately in the habit plane, while the measured coincidences of the directions are only within 10 deg. The major axis of the platelet is parallel to [010] in the 0. This orientation corresponds to the direction of nearest registry of the lattices.

Jan 1, 1964

By C. A. Hollingsworth

The Deep Leg Flotation Cell was developed to solve a problem which confronted the Smith-Douglass Company on moving from one mining area to another. Poor recovery and, to some extent, inferior concentrate grade were encountered in the silica flota¬tion circuit. This was believed due to the softness of the phosphate which caused it to form slime. In view of the urgency of the matter, the problem was attacked from two angles. The first involved the development of a flotation cell which would not create slime and the second, a new or improved reagent for floating silica from phosphate rock which would be less sensitive to slime than reagents currently in use.

Jan 1, 1964

By Evan Adams

The Ireland Mine is located some seven miles South of Moundsville West Virginia, along the bank of the Ohio River. We are mining the Pittsburgh #8 seam. This seam is approximately 60" in thickness, and is immediately overlain by some 10 feet of a conglommerate material. The roof is difficult to control, due to the fact that it frequently is composed of substances not hard enough to be held together with 6-foot roof bolts. In many cases, we must use 10-foot roof bolts, in order to get bolt anchorage in the limestone above the conglommerate. Due to the elasticity of the limestone and its tendency to bend rather than to break, we have been unable to maintain a pillar line. Thus, we have found it necessary to mine by the room and pillar system. Belt haulage is used on room entries to automatic loading stations, thence into 15-ton mine cars, controlled at the loading point by car spotters. The maximum belt length is 2,000 feet. Rail haulage to the slope-bottom dump is by 27- and 50-ton locomotives. The mine produces coal two shifts per day, with 7 production crews on each shift. Mine and machinery maintenance is performed on the Midnight shift. We handle an average of 660 tons per machine shift.

Jan 1, 1964

By D. A. Kraai, S. Floreen

The effect of 1 to 50 ppm S on the ductility of nickel at 800° to 1400°F was studied. Results at each temperature showed a decrease in the reduction of area from approximately 95 to 5 pet over the sulfur range studied. Ductility varied with grain size, but only to a minor extent relative to the sulfiw effect. The effects of sulfur were completely offset by the addition of small amounts of magnesium. The results indicate that the "hot-short" loss in ductility is not an inherent property of nickel. Some possible mechanisms which cause the loss in ductility are described. MANY metals or alloys that normally possess high ductility exhibit a ductility loss at intermediate temperatures. This loss in ductility is often called "hot-shortness". Numerous examples of this phenomenon have been reported in the literature. Much of this work has been reviewed by McLean1 and by Rhines and Wray.2 To date there is no fully satisfactory explanation of the cause of this intermediate-temperature hot-shortness. It is generally recognized that impurities, and particularly impurities that form low-melting phases, can cause embrittlement. Examples of hot-shortness have been reported, however, where there were no obvious impurities present which would lower the ductility. Thus there has been some basis for believing that hot-shortness is an inherent property, and that even the purest metal would display a hot-short loss in ductility. This latter hypothesis was recently put forward by Rhines and wray2 based on studies of nickel and nickel alloys. In the discussion of this paper, however, Guard noted that high-purity nickel showed no hot-shortness.3 Thus there is reason to doubt whether pure nickel, or by inference any other pure metal, will inherently exhibit hot-shortness. The present work was initiated to determine the extent to which hot ductility was sensitive to very small amounts of an impurity element. If it could be demonstrated that hot-shortness could be induced by only minor amounts of an impurity, then it might be argued that hot-shortness in general is an impurity effect, and not a fundamental property of pure metals. The particular impurity studied was sulfur in nickel. The deleterious effects of sulfur are well- known. It is also well-known, and will be shown below, that additions of magnesium will render sulfur innocuous. When no such refining agents are added, however, the Ni-S system is a very useful one for studying the influence of small amounts of impurities. EXPERIMENTAL PROCEDURE Two heats containing -24 ppm S were vacuum-melted and small amounts of magnesium were then added under an argon atmosphere. These alloys were used to show the effectiveness of the normal magnesium treatment in overcoming the influence of sulfur. A second series of alloys with a sulfur range of 1 to 50 ppm was then prepared by vacuum melting nickel in alumina crucibles. No elements, such as magnesium, which tend to combine with sulfur were added. The higher sulfur contents were attained by adding nickel sulfide. Lower sulfur contents were prepared using a method in which the melt was oxidized under vacuum to produce the reaction S + 2O = SO2 These heats were subsequently deoxidized with carbon. Ten- to twenty-pound ingots were cast of all of the alloys studied. The compositions are given in Table I. The ingots were forged and hot-rolled to 3/4-in. bar. They were then annealed at either 2000" or 1600°F to produce different grain sizes. One-quarter-in.-diam tensile specimens were machined from the bars. These were tested at 800°, 1000o, 1200°, and 1400°F. The specimens were held at temperature approximately 45 min before testing. The strain rates were 0.005 min-1 to yielding, and 0.05 min-' after yielding. No extensometers or gage marks were placed on the specimens because the higher sulfur heats tended to fracture at the knife-edge indentations or gage marks. The properties measured were ultimate tensile strength and reduction of area. The analytical technique for determining sulfur at low levels was that developed by Burke and Davis.4 They reported a standard deviation of 1 ppm at an average sulfur level of 4 ppm in NBS standards. A standard deviation of 3 ppm is probably more realistic for the alloys used in this investigation considering the possibility of some segregation in the ingots. RESULTS A summary of the tensile results is given in Table I. As shown in the table, both heats to which

Jan 1, 1964

This paper outlines the position and capabilities of Western Canada's bituminous coal industry, and indicates the increasing importance of Japan as an export market. The use of coal in Japan is reviewed, especially as regards future trends, and an appraisal is made of Canadian coal in comparison with domestic Japanese coal and imports from other countries. The importance of maintaining a solid nucleous within the Canadian bituminous coal industry is emphasized. I N RECENT years, Japan has emerged as a valuable market for Canadian exports. The first major product exported in volume to Japan was wheat, which has become very successfully established in Japanese markets. Following this, iron ore gradually found a market in Japan, with exports usually based on long-term contracts. This iron ore was produced entirely in British Columbia In 1958, the Western Canadian bituminous coal industry -jointly with the Dominion Coal Board -sent an official mission to Japan to investigate the

Jan 1, 1964

By C. C. Herrick

The vapor pressure of indium has been measured by the torque-effusion technique, as a function of temperature between 1102o and 1422oK. For liquid indium, the vapor pressure (in atmospheres) can be represented by the equation -R In P = 5.782 x104/T - 25.29from 1000o to 1422oK. Extrapolation yields a calculated normal boiling point of 2329°K and a heat of vaporization at 298 oK of 58.09 kcal per mole by the third-law method and of 58.39 kcal per mole by the second-law method. Calculations indicate that the free-energy functions of Hultgren are to be preferred to those of Guruich. BECAUSE of the potential uses of liquid metals, it is important that convenient experimental methods be developed which will lead to a sufficient body of thermodynamic data so that reasonable estimates of properties of liquid metals can be made. Indium is particularly well-suited to investigation, since it remains liquid over a long temperature interval, it alloys readily, suitable containers for it are easily procured, and relatively few investigations of its thermodynamic properties in the region above 1000°K have been made. PREVIOUS RESEARCH The first determination of the vapor pressure of indium was made by Anderson,' using the Knudsen method and silica-lines stainless-steel cells. Kohlmeyer and spandau2 determined the normal boiling point, and a mass-spectroscopic investigation has been made by Lyubimov and Lyubitov.3 (Unfortunately, only an equation representing the data of the latter investigators has been available to us.) Hultgren et al.4 and Gurvich5 have published discordant tables of the free-energy functions for indium. EXPERIMENTAL METHOD The torsion-effusion principle has been described amply in the literature.8,7 With this method, one observes the angular deflection induced by effusion of vapor from a multihole effusion cell which is suspended from a filament producing a small rotational restoring force. The pressure within the effusion cell can be computed from the relation ziaifiai where k is the torsion constant of the filament, 6 is the observed angular deflection, and ai, fi, and qi are the area, force factor, and moment arm of the ith effusion orifice. The force factor f is analogous to the Clausing factor,' and corrects for the reduction in effusive force attributable to the finite geometry of the effusion orifice. Schultz and Searcy' have tabulated the force factors for various tube geometries. EXPERIMENTAL APPARATUS The physical arrangement employed in this study is shown in Fig. 1. The furnace elements are six Globar heat rods with 15-in. hot zones. Temperature is maintained to * 1°K by a Beck mechanism driving two 26-amp Powerstats in parallel. A Pt (Pt, Rh 10 pct) thermocouple serves as the sensing element. Four inner tubes act as vibration isolators; the air pressure required for maximum isolation was determined empirically, and is maintained by a solenoid valve. The tungsten fiber, 9 by 0.002 in., is joined to an 0.008-in. tungsten wire or graphite rod via a machined lightweight chuck.

Jan 1, 1964

OF the many categories into which scientific knowledge has been arbitrarily 'divided, the one that has proved most. applicable in our attempts to gain an insight into the details of steelmaking processes is physical chemistry. To the young metallurgist who has only recently survived a college course in this subject, the application of its principles to reactions in liquid steel should not be difficult. The many excellent textbooks of physical chemistry provide ample material on the principles of this subject for the student of steelmaking processes. It is the purpose of this chapter to provide a concise review of the principles of physical chemistry that have proved useful in studies of steelmaking and at the same time to present some of the data that are essential to the application of physical chemistry to reactions at high temperatures. Certain parts of physical chemistry require rather formidable mathematics for their complete development, but in the main those applications in which we are here interested can be expressed in fairly simple terms. Many of the equations are logarithmic, and we shall use the symbols In X and log X to represent, respectively the natural and the common logarithm of X. The two are related-by In X = 2.303 log X. Logarithms may, be read from a good slide rule with sufficient accuracy for our purposes. In a few spots a knowledge of the calculus will be helpful. MATTER Innumerable forms of matter may, be recognized, and these may be converted by chemical processes into others, as ore, coke, and air are converted into iron, slag, and gas.. Whenever such a change occurs there is a corresponding change in the amount of energy associated with the matter. The process may require an input of energy, as in the electrolytic production of aluminum, or it may result in an output of energy, as in the combustion of fuel. The basic laws of the conservation of matter and of energy tell us that we cannot change the total amount of matter or the total amour t of energy.. When the fuel pile is used up, we realize that it has simply been converted into other forms of matter; .i.e., ash

Jan 1, 1964