By A Palynchuk

The development of welded pipe has paralleled the general industrial development and, in particular, that of the petroleum industry. The petroleum industry's need for high-grade, economical pipeline material to make many 'of its projects feasible has been a significant factor in the development of light-wall, high-grade welded pipe. The modern welding processes, such as high-frequency, electric resistance, flash, submerged arc, etc., have some basically different characteristics. The modern high-frequency weld mill is a complex of specialized equipment that is integrated into a production unit. Each component in the unit performs a specific function in the production process. Quality control must be built into the process on an operating basis and, to maintain the quality required for pipeline standards, must be more than a policing operation. The further development of the welded pipe industry will be determined by changing and increasing demands. The technical and economic views and requirements that will influence the development have to be resolved.

Jan 1, 1964

By Bruce Chalmers, D. C. Larson

Aluminum crystals with longitudinal-axis orientations of (111) . (110), and (100) were deforined in tension and annealed. The conditions of deformation were controlled so that the re crystallization nuclei originated in either the heavily deformed regions at saw cuts {artificial nucleation) or in the lightly deformed matrix (spontaneous nucleation). The artificial-nucleatioln experiments showed that in lightly deformed (110) and (100) crystals low-angle twist boundaries are most mobile, while in (111> crystals and heavily deformed (110) and (100) crystals high-angle tilt boundaries with near (111) rotations are favored. The spontaneous-nucleation experiments showed the existence of preferred orientations in the (111) crystals. The nonrandomness of the grain orientations is quantitatively determined through a comparison with the results which would he obtained from a randowl set of grain ovientations. PREVIOUS recrystallization studies have been performed on single crystals deformed in tension.1 7 The crystals used in these studies usually had random tensile-axis orientations and the extent of deformation was not a primary consideration. The present study concerns the recrystallization of single crystals with tensile-axis orientations of (Ill), (110), and (100). The emphasis of this work is on the influence of the tensile-axis orientation and the degree of deformation on both the nucleation and growth processes. The multiple-slip orientations were chosen because secondary slip or slip intersection promotes nucleation.1,5,8 These crystals recrystallize at lower strains than the crystals which are oriented for single slip. Also, the greatest variation in deformation behavior is exhibited by the multiple-slip orientations. The stress-strain curves for crystals with tensile-axis orientations of (111) are higher than the stress-strain curves for poly-crystals, and the stress-strain curves for crystals with tensile-axis orientations of (100) are lower (at large strains) than the stress-strain curves for the crystals which deform initially in single slip.g The recrystallization nuclei originated in either 1) the homogeneously* deformed matrix of the crys- tals or 2) the heavily and inhomogeneously deformed regions at saw cuts. The nuclei will be referred to hereafter as spontaneous and artificial nuclei, respectively. The two terms do not imply a difference in the nature of the nuclei; they imply simply a difference in the mode of introduction of the nuclei. During spontaneous nucleation very few (always less than ten) grains nucleate, while during artificial nucleation large numbers of grains nucleate. Only a fraction of the artificially nucleated grains penetrate very far into the deformed matrix during annealing. The grains that penetrate the farthest into the deformed matrix will be referred to as the dominant grains. EXPERIMENTAL PROCEDURE The thirty-five crystals used in this investigation were grown from the melt in milled graphite boats at a rate of 1.6 cm per hr. The crystals had dimensions of approximately 6 by 12 by 80 or 6 by 6 by 80 mm and the aluminum was of 99.992 pet purity. The as-grown crystals were annealed at 610°C for 24 hr and furnace-cooled. They were then heavily etched and electropolished in a solution of five parts methanol to one part perchloric acid. The crystal orientations were obtained by back-reflection Laue photographs and were accurate to ±2 deg. The tensile-axis orientations were (loo), (110), and (111). Two of the side faces of the (111) crystals were (110) lanes. The (110) crystals had both {100) and {110) side faces and the (100) crystals had (100) side faces. The crystals were deformed at a strain rate of 0.003 per min. Shear stress and shear strain were obtained by multiplying and dividing the tensile stress and strain, respectively, by the Schmid factor, m. For the (111) crystals m = 0.272 and for the (110) and the (100) crystals m = 0.408. The Schmid factor is effectively constant during deformation for all orientations. The deformed crystals were sawed into 1-in.-long specimens while the crystals were totally enclosed in a graphite boat. The sawing was performed very carefully in order to limit the plastic deformation to the sawed regions. The specimens were electropolished in the solution mentioned above to remove the sawed-end deformation as well as controlled amounts of surface material. A special stainless-steel grip was used to hold the specimens during the electropolishing treatment. The gripping faces were flat, with no teeth, to prevent the introduction of extraneous de-

Jan 1, 1964

By Rupert Spivey

Kennecott Copper's Chino mine is one of the oldest copper mines in the United States, having been operated by the Spaniards as early as 1800. At that time haulage methods were indeed primitive. Indians brought the ore up on "chicken ladders" in leather buckets. It was then melted into crude bars and hauled to Chihuahua by mule train. There are still remnants of the old trails near the present pit where the mule hooves cut grooves in solid rock. The mines were worked as underground operations off' and on until open-pit mining was started in 1910 by John Sully and Daniel C. Jackling. Since that time many haulage methods have been used: mule carts, steam and electric trains and finally large haulage trucks, now believed to be the best method for this mine. The general shape of the pit is oval with dimensions of 1% miles by 1% miles. Working benches are 50 ft high, with the bottom bench at 5750 ft and the top at 6450 ft above sea level.

Jan 1, 1964

By L. C. Brown, J. S. Kirkaldy

Measurements have been made of carbon diffuswn in the five ternary austenites Fe-C-Si, Fe-C-Ni, Fe-C-Co, Fe-C-Mn, and Fe-C-Cr in which the carbon (component 1) diffuses through interstitial sites and the ternary addition (component 2) diffuses substitutionally. Values of the diffusion-coefficient ratio, D12/D11 were determined for each system with finite couples using the transient equilibrium method. The effect of temperature and of concentrations of both the carbon and substitutional component upon D12/D was examined and was found to agree with the theoretical predictions. It is concluded that within an experimental uncertainty of 10 to 15 pct, it is possible to calculate the ratio D12/D11 from purely thermody-namic data. Difficulties of measuring the other off-diagonal coefficient, 4,, are discussed. Any quantitative attack on the fundamentals of the hardenability problem in steel must begin with the multicomponent diffusion formalism and with the accumulation of data pertaining thereto. In a recent paper Kirkaldy and purdy 1 employed the formalism derived from irreversible thermodynamics to treat the problem of diffusion in ternary austenites. In the latter solutions, carbon diffuses through interstitial sites and the substitutional component diffuses through the lattice. Examples were given of diffusion in the systems Fe-Mn-C and Fe-Si-C. In the present paper, we present new results on and discuss their agreement with the thermody-namic theory. Since the theory has been slightly modified from the original presentation of Kirkaldy and Purdy, their results on Fe-Si-C and Fe-Mn-C have been recalculated and are presented here for completeness. The flux of the interstitial component with respect to a fixed lattice framework can be written as a linear expansion in the independent concentration gradients, where X1 and X2 are the independent thermody-namic forces in the lattice fixed frame of reference. These forces can be obtained from the general statement for forces in a volume fixed frame2 if the partial molar volume of carbon atoms is set equal to zero and that of the substitutional component 2 is set equal to unity, viz where the are the chemical potentials and the N's are mole fractions. Introducing into [3] and [4] the function If, as suggested by statistical arguments, the off-diagonal interaction L12 is sufficiently small, [6] reduces to i.e., the coefficient ratio becomes purely thermo-dynamic. The activity of components 1 and 2 in a dilute ternary system (standard state at infinite dilution) may be represented by the expansion3

Jan 1, 1964

By W J. Riva

This paper reviews the circumstances that led to the development and construction of a commercial-scale vertical shaft carbonizer at Conmore, Alberta. This form coking process may be regarded as having potential application in other areas. Coal pelletizing offers a promising method of decreasing coal agglomeration costs under certain circumstances. Pellets can be rolled easily from -35-mesh coal, provided that a minimum of -200-mesh coal is present. Bentonite was found to be the best binder and was most effective when added in amounts of about 2 per cent. The water content of the coal pellets was observed to vary from 18 to 23 per cent. As a by-product of this investigation, it seems possible that fine coal could be converted into stoker feed by this process. A short investigation of the effect of heating rate on the carbonization of pellets was conducted. The low maximum heating rates in certain temperature ranges, necessary to avoid crack formation in the pellets as reported by other

Jan 1, 1964

By O. N. Carlson, E. D. Gibson, D. W. Bare

SEVERAL investigators have recently contributed to a clarification of the controversy concerning the allotropy of chromium. Ross and Hume-Rothery1 and Vasyutinskii et a1.2 have reported high-temperature X-ray data on unalloyed chromium from which they have concluded that no allotropic transformation occurs in this metal. Bechtoldt and vacher3 in their investigation of the Cr-Ni alloy system found no evidence for a transformation in chromium and Smart and Haynes4 in critically analyzing the data presented to date concerning this system could find no evidence for a eutectoid reaction in this system. Wyder and Hoch5 in research concurrent with our

Jan 1, 1964

By M. J. Pool, C. E. Lundin

THE relative partial molar enthalpies of aluminum, gallium, and indium in liquid tin have been measured at 750°K by liquid-metal solution calorimetry. The measured heat effects and the calculated relative partial molar heats of solutions at infinite dilution are listed in Table I along with the relative heat contents of the solutes calculated from the data of Kelley. All of the values are referred to 750°K even though the calorimeter temperature fluctuated by +1°K during the entire series of experiments. The effect of this small temperature variation on the experimental values should be less than the experimental error. The limits of error given in Table I represent the standard deviations of all values from the mean. In no case was the experimental deviation greater than the listed error limits. The reported error estimates only apply to the estimated precision of experimental values and not to their accuracy. Systematic errors could be present in the calorimeter which would affect the absolute values given. Moreover the heat-content data used could also be in error and this would affect the end results. The relative enthalpies used were listed in Table I so that future corrections could be made if necessary. The relative partial molar heats of solutions of aluminum in liquid tin and dilute A1-Sn liquid solutions are large and positive. The value at infinite dilution is given in Table I. In the dilute-solution region investigated the relative partial molar heat of solution was a linear function of composition. A least-squares analysis of the data gave the following expression at 750°K: Atf^ = 6195 - 12,160 A:A1(cal/g-atom) where XA1 is the mole fraction of aluminum in the alloy. This can be compared with the data of Cohen, Howlett, and ever' who obtained the expression: 1SM = 6075 - 10,750 XM at 573°K Apparently both the partial molar heat of solution at infinite dilution and the concentration dependence increase with increasing temperature. This same

Jan 1, 1964

By Murray Udy

La Corporación Venezolana de Guayana ( CVG) decidió renovar su noveno horno eléctrico de reducción a través de un nuevo proceso para la fabricación del fierro Strategic-Ud. En este sentido, el presente artículo señala la la instalación de este nuevo proceso de producción de hierro en la planta siderúrgica del Orinoco. La implantación del Strategic-Udy se inició en 1963 y es una combinación de operaciones unitarias conocidas con una técnica operativa mejorada, a fin de ofrecer mejor control sobre los procesos químicos e incrementar la eficiencia de la técnica antigua. Asimismo este nuevo proceso, elimina las limitaciones de tamaño y calidad del material impuestas en los procesos existentes para la fabricación del fierro.

Jan 1, 1964

By James J. Scott

Longwall mining has not received a great deal of attention in the United States; however, this system offers many advantages over the conventional room-and-pillar methods now being used. In order to conserve the coal resources of this country, the U. S. Bureau of Mines has investi¬gated the feasibility of adapting European longwall mining methods to American coal seams. Their studies showed longwall mining to be well suited to thinner seams and, greater depths; and, in addition, permitted almost 100 percent recovery of the coal. Most, experiments with this method resulted in higher overall production-costs than were commonly obtained with highly mechanized room-and-pillar techniques This high cost-was largely due to the excessive amount of labor required to maintain adequate roof support with conventional longwall mining techniques. With the substitution of hydraulic-powered, self-advancing roof support systems for conventional supports, this excessive labor cost has been decreased, and longwall mining costs are now competitive with those of modern room-and-pillar mining.

Jan 1, 1964

By D. H. Polonis, M. B. Kasen

AN unusual thermal etching phenomenon has been observed on the surface of a Cu-Si alloy. The observations were made during studies of vacancy condensation pit formation which were reported in previous papers.1,2 Figs. 1 and 2 are photomicrographs of the surface of a Cu-4.8 pct Si alloy after heating in vacuo (3 x X mm Hg) to 525°C and subsequently holding at that temperature for 16 hr in an impure (air-contaminated) argon atmosphere. Under these conditions preferential removal of silicon from the matrix by oxidation results in a surface which is entirely a phase overlying an a plus y structure. The light areas of Fig. 1 are regions in which very little thermal etching has occurred, while the majority of the surface has experienced severe etching. Similar regions in Fig. 2 are seen as plateaus above contours produced by net transfer of material from the specimen surface. Twin boundaries are also visible in Fig. 2. The difference in matrix mi-crostructure between Figs. l and 2 reflects the par- ticular orientation of low-index planes with respect to the surface of observation. Thermal etching contours of this type have been studied in detail by Hondros and Moore Both of the photomicrographs show that one or more dark spots are located approximately at the center of every protected area; where two spots are in close proximity, the protected areas have merged. The microstructures indicate that the anomalous resistance to thermal etching is related to the presence of these spots. Williams and Hayfield have shown that local regions of unusually high oxidation resistance can be caused by a surface monolayer of atoms with a work function higher than that of the base material. The result is an inhibition of the rate of electron removal from the base material and a decrease in the oxidation rate. The source of the protected layer may be either surface diffusion from contaminants on the specimen surface or pipe diffusion of solute atoms followed by migration across the surface. In the latter case the driving force is a difference in chemical potential resulting in a Gibbs adsorption phenomenon. In the present case, chemical polishing of the specimen surface precluded contaminants of a strictly surface nature. Consequently, diffusion of impurity atoms from within the lattice appears to be the most tenable explanation of the observed phenomena. The authors propose that the structures of Figs. 1 and 2 reflect the diffusion of impurity atoms along extended dislocations within the individual a phase grains prior to surface oxidation. The central spots within the protected regions are seen as sites of dislocation emergence which have become locally decorated with oxide in the manner discussed in Ref. 1. Williams and Hayfield observed protected regions adjacent to the grain boundaries of iron-contaminated copper which they attributed to the segregation of iron to the grain boundaries coupled with high dif-fusivity along the complex dislocation array at such boundaries. No evidence of such grain boundary protection was observed in the Cu-Si alloy; this

Jan 1, 1964

By John Chipman, Wayne L. Worrell

Using recent thermodynamic data for the carbides and oxides of tantalum, columbium, and vanadium, the stable solid phases aboue 1300°K and at 1 atm CO(g) pressure in each M-C-O system have been determined. Pourbaix-Ellingham diagrams have been constructed and are used to estimate the minimum temperatures necessary to obtain these metals by carbothermic reduction under reduced pressures. TANTALUM, columbium, and vanadium react with carbon to form the M,C and MC carbide phases. The M,C carbides have narrow homogeneity ranges, but the MC phases possess considerable ranges of homogeneity.' The free energies of formation of the MC carbides were recently measured, and those of MC and M2Ccarbides have been estimated., (The notations MC and MC denote, respectively, the carbide compositions at the carbon-rich and at the metal-rich boundaries of the homogeneous MC phase.) In this paper, these carbide data are combined with thermodynamic data for the oxides to predict the stable phases in the Ta-C-O, Cb-C-O, and V-C-O systems at specified temperatures and oxygen pressures. M-C-O PHASE DIAGRAMS The solid phases in equilibrium above 1300°K for each M-C-0 system are shown in Figs. 1, 2, and 3. Above 1300°K, the vapor would consist entirely of carbon monoxide; and these phase diagrams were obtained by specifying the vapor pressure of CO(g) to be 1 atm. The temperature at which any two solid phases become unstable is specified along the two-phase equilibrium lines in each diagram. To simplify the diagrams, all solid phases in the Ta-C-O and Cb-C-O systems are represented as stoichiometric compounds. However, the homogeneity ranges of VO and VC are indicated, because they form a complete series of solid solutions.3 It also should be noted that the homogeneity range of

Jan 1, 1964

By F J. Pearce

The Steel Company of Canada, utilizing the S-L process, has produced partially and highly reduced pellets for use in the blast furnace. Experimental blast furnace tests, using reduced pellet burdens, have been carried out. The changes in production rate, fuel rate and general performance of both the S-L and the blast furnace processes are indicated. Introduction T HE ore burdens for a blast furnace may be improved in two ways: chemically, by concentrating the ore to a high degree of purity; and physically, by agglomerating or closely sizing the ore particles. Today, many b1ast furnaces are charged with closely sized agglomerates, some of which contain upwards of 66 per cent iron. The further improvement of these burdens by chemical concentration may, in many instances, be uneconomic due to the large losses of iron that occur during processing. Assuming that it would be possible to reject all of the gangue minerals, the maximum level of concentration of iron in the hematitic ores would be only about 70 per cent.

Jan 1, 1964

To enable AN-FO .tòo' be used on an equal .weight basis wish Nitro Gl reerin.e expl3oòsives r smaller diameter bore holes became necessary With consequent modifications to drill steel and burden on holes, De't'onation of AN-FO "in small diameter holes proved successful' both with 'and without primer charges but some altorat-ions were required to. adopt Anolodeòr.s to the smaller -holes, Important factors in training all operators In the new charging method were the retention of imp-,cved, fragmentat'ion, avoidance of excel ive ove:break and keeping wall rock dilution 'to an absoluato mi. iArurle ò The ò successful storage of Ammonium 14t-rate in c"!ime.tic conditions 'with daily'.-' temperature fluctuationc above and below the critical' 90¦F, has. been "achieved,

Jan 1, 1964

By B. Trafton, H. L. Hartman

An earlier paper1 introduced a rapid solution for mine ventilation network problems, employing the digital computer. In this paper, refinements and additions to the computer program which expand its scope of application and a solution to a ventilation network having a coal-mine configuration are presented. The revised program-written in FORTRAN for the IBM 7074 computer in Penn State's Computation Center-is applicable to any mine ventilation network employing natural splitting and having its fan located externally. It accomplishes the following: 1) Distributes an assumed total quantity of air flow among all airways of the network, performing iterations until an acceptable level of error is attained and the flow in each airway is known. 2) Computes the pressure drop (head loss) in all airways and the overall network and mine head losses. 3) Determines the operating point for the mine and a given fan, adjusting all air flows and head losses to the actual values. The basis of analysis used is the Hardy Cross method of successive approximation for solution of any fluid network, explained in detail in the earlier article. In brief, corrections to assumed air flows are computed for all the loops of a network; following distribution to the airways of each loop, the process is repeated until acceptable accuracy is attained. When a hand or desk-calculator solution is used, there is advantage to close approximation of the actual flows in the original assumption of air-flow distribution in the network. Since publication of the previous paper, in which assumption of initial quantities was also necessary in the computer solution, the program has been modified to make the first distribution itself, assigning the total quantity to one specified path in a split and then proceeding to correct the flows. The number of iterations required for a high-accuracy solution is little affected, at least in networks of few loops, 10 to 15 being sufficient to reduce the error to 1 pct or less. The principal limitation of the original program was that it contained no provision for handling a fan. Further, it did not determine the overall head loss in the network and was not designed for multiple parallel openings, such as occur in coal mines. The revised program was written to overcome these disadvantages and also to print out the adjusted flows for all airways, corrected for the system operating point. At the present time, the program can handle only an external fan. The procedure employed in solving a ventilation network is now as follows: 1) Input data consisting of airway characteristics and loop designation along with assumed direction of flow, for each branch of the network and any trunk airways, are fed into the computer. 2) Employing the resistance relationship, where R is resistance, K is friction factor, P is perimeter, L is length, A is area, and n is number of airways (where multiple intakes and returns are employed); values are computed for all airways. 3) An arbitrary, continuous route of flow through the circuit—from beginning to end—is selected and the path identified by airway numbers and read in. 4) Based on a total assumed quantity of flow Q (usually 100,000 cfm.) the computer employs the procedure described in the previous article in distributing quantities of flow among all the airways until a satisfactory level of accuracy has been attained (in the current program, the machine is turned off when the cumulative corrective error in cfm, is reduced to five times the number of airways). 5) Airway head losses H are calculated by the relation H = R Q2 and cumulated along the original designated flow route to find the overall head loss for the network. Trunk airways are then included to obtain the mine head.

Jan 1, 1964

ALTHOUGH the open-hearth charge contributes CO, C02, H2, A and water vapor to the combustion gases and absorbs oxygen from them, in the main the thermal effects in the melting charge and molten bath can be considered independently of those in fuel combustion; the latter then is regarded simply as the source of the net heat required to finish a heat of steel. First of all, it should be remembered that a large percentage of the heat supplied to the bath is furnished by oxidation of the various elements in the charge itself. If this charge consisted of 80 to 100 per cent of hot metal and the oxidation were accomplished by blowing in air or oxygen, as in the bessemer converter, the net heat absorption would be negative; that is, the bath would contribute part of the heat required to keep the melting chamber hot, in addition to that contained in the finished steel and slag. In actual open-hearth practices, probably the nearest approach to this is in the duplex furnace, charged with bessemer-blown metal and some hot metal, where very little heat is required to complete the refining and nearly all the heat energy from fuel combustion is used to keep the roof and walls of the melting chamber up to around 2900 to 3000 F (1600 to 1650 C), so that the bath will not cool off during the refining. The other extreme is with all-cold charges containing around 80 per cent steel scrap and 20 per cent cast iron or cold pig iron, in which case a very large proportion of the heat in the bath at tap is supplied from the fuel combustion. THERMAL EFFECTS IN MELTING In a typical heat, the fuel furnishes about four million British thermal units per ton of steel produced. The heat required, for the metallurgical processes is not easily defined in useful manner but it ranges downward from about one million Btu, depending not only on the charge but on the manner of calculation. In, any event, this requirement appears. small in comparison with the

Jan 1, 1964

By J. J. Sense

This paper deals with the Asarco method for the determination of equipment availability. It is apparent that no single availability equation will provide all of the information necessary for the complete record of equipment availability. In the Asarco system, three separate availability records are carried on major equipment. The first is mechanical availability, the second is operational availability, and the third is a historical record of equipment use. The derivation of the three items and the definitions of the time elements used in the various availability equations are presented and discussed. The Mission unit of American Smelting and Refining Co. is located in Pima County, Ariz., approximately twenty miles southwest of Tucson. The unit consists of an open pit copper mine and concentrator. The concentrate is shipped by rail to company smelters at Hayden, Ariz., or El Paso, Tex. Mine stripping began at Mission in the fall of 1959, and construction of the 15,000 tpd concentrator was started in the spring of 1960. The first ore was treated in midsummer of 1961 and full ore production was reached in August 1961. At that time over 46 million tons of material had been moved from the pit. Current production (ore and waste) averages over 100,000 tpd. Total production to date (ore and waste) is over 120 million tons. Major equipment currently in operation at the Mission pit is as follows: 3 P & H 1800 Electric Shovels - 9 cu yd dippers 1 P & H 1900 Electric Shovel - 9 cu yd dipper 2 B.E. 190-B Electric Shovels - 9 cu yd dippers 35 Euclid LLD Trucks - 60-ton capacity 6 KW-Dart 55-T Trucks - 55-ton capacity 1 KW-Dart D-2550 Truck - 65-ton capacity 1 LeTourneau Westinghouse 65 Haulpak - 65-ton capacity 3 Euclid S-18 Scrapers - 274011 capacity 4 Caterpillar D-8 Dozers 4 LeTourneau Westinghouse Tournadozers 1 Michigan 280 Dozer 2 Caterpillar Model 12 Motor Graders

Jan 1, 1964

By G. W. Leney

Iron ores occur in such a wide variety of forms that nearly every kind of prospecting, geological knowledge, and geophysical technique has some application in the search for them. The type of orebody that is considered desirable depends on political and economic considerations, on transportation and markets, on the characteristics of the orebody, on the metallurgy of the ore, and on its comparison with other available ores. In North America, materials that can be efficiently processed into high grade concentrates and pellets are now the object of most exploration work. These are usually shallow, relatively unoxidized, metamorphosed iron formations that are particularly suitable for geophysical methods of exploration. Magnetic surveys are used for the direct discovery of new orebodies, for mapping stratigraphy and structure, and at times to locate oxidized zones in magnetic iron formation. Gravity mapping provides supplementary information, indicates gross tonnages, is useful in regional studies, and can discover non-magnetic orebodies. Electrical methods have not been fully exploited but self-potential, resistivity, applied potential, electromagnetic and perhaps induced polarization surveys all have restricted but highly useful applications. The use of all geophysical techniques promises to increase as the number of exposed easily discoverable orebodies decreases. A high consumption of steel, and consequently of iron ore is the chief characteristic of an industrial society and this consumption has been increasing at an average rate of about 35% every ten years for the past century. To supply this demand, iron ores and iron bearing materials in a wide variety of forms have been exploited on every inhabited continent and in nearly every country. Nearly every kind of prospecting, geological knowledge and geophysical technique has some application in the search for them. The type of orebody that is con-

Jan 1, 1964

By Jacques Friedel

Jan 1, 1964

By Charles A. Stickels, Edward E. Hucke

The dihedral angle, formed by the intersection of three interfaces, is often determined by measuring a sample of apparent angles of intersection seen on a random plane of polish, then comparing the exerimental distribution of angles to the distribution calculated by Harker and Parker. Statistical tests show that the latter distribution does not satisfactorily describe the population from which samples are drawn. It is concluded that the major reason for this discrepancy is the presence of a range of dihedral angles in all specimens. When reasonable care is used experimentally, random measuring error is unimportant. It is shown that measurements made on dispersed second-phase inclusions are subject to a systematic error depending on inclusion size, which can be minimized by using adequate magnification. A dihedral angle, calculated from a sample of observed angles as though a unique dihedral angle were present, is termed an "effective dihedral angle". Experience has shown that "effective dihedral angles'' are reproducible quantities, useful for characterizing samples. Methods of determining an "effective dihedral angle", establishing its reliability, and making comparisons between samples are discussed. THE authors have recently reported measurements of the dihedral angle formed by liquid-lead inclusions lying in nickel grain boundaries.' Di- hedral angles were measured by the statistical method first employed by Harker and parker2 and used subsequently by many other workers.3"8 Since a relatively high degree of accuracy was necessary in the authors' experiments, the reliability of this method of dihedral-angle measurement was examined. Briefly, this method of measuring dihedral angles is usually performed as follows. A multiphase alloy is prepared, equilibrated under conditions which allow sufficient interface mobility to establish equilibrium, quenched to room temperature, then prepared for metallographic examination. A large number of observed angles, formed by the traces of grain boundaries and/or interphase boundaries on the plane of polish, are measured at high magnification. If all orientations of interfaces in the specimen are equally probable, Harker and parker2 showed that the population of observed angles is described by a distribution function containing a single parameter, the dihedral angle, 8. certain properties of the population, e.g., the mode or median, have been calculated from this distribution function in terms of the dihedral angle.3, 9 Thus, if the mode or median of a sample is identified with the corresponding property of the population, a unique value for the dihedral angle is determined. One defect in this procedure lies in identifying the properties of a sample of observed angles with the properties of the population from which they are drawn. If one were to proceed in a more rigorous fashion, it would be necessary to find a function of sample properties which is an estimator of the dihedral angle. Then by determining the distribution function for the estimator one could set limits on the value of the dihedral angle. The most apparent obstacle to this straightforward approach is the complexity of the distribution function assumed to describe the population. In analytical form, the distribution function may be written:2, 10

Jan 1, 1964

By Erle I. Shobert

In the comparison and consideration of synthetic and natural materials, graphites represent a situation in which natural graphites amount to less than 10% of the total carbon and graphite production by weight, and less than 5% in dollar volume, There are few applications where it could not be re- placed by synthetic graphite. On the contrary, synthetic graphite materials can be engineered to cover an extremely wide range of applications. These include electrographite brushes for rotating machinery, pyrolytic graphite, graphite-impervious pipe, nuclear moderators, high purity spectrographic graphite, power tube anodes, graphite rotary shaft seals, and rocket nozzles. The special qualities of natural graphite and its limitations are delineated and the almost unlimited possibilities in artificial graphite materials are discussed.

Jan 1, 1964