By D. E. Fogelson

In a factorial experiment, blasting caps were detonated in three sizes of shotholes in mortar with three types of stemming--dry sand, wet sand, and hydrostone. Free-surface displacement pulses were recorded with a capacitive-displacement gage at a distance of 15 inches. The effects of decoupling and the type of stemming on the amplitude and the duration of the displacement pulse were determined. Both the amplitude and the duration of the displacement pulse were significantly decreased by increasing the decoupling, but they were little affected by the type of stemming.

Jan 1, 1965

By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The microhardness of single crystals of tungsten disilicide has been investigated by the Knoop method. The average random room-temperature hardness of the WSi, matrix was 1350 kg per sq mm. Hardness crnisotropy was noted with respect to plane and indenter orientation as determined by single-crq.stal X-rny studies. Annealing at 1600" and 1800°C decreased the average hardness to 1310 and 1230 kg per sq tnm, respectively, and produced a second phase identified by X-ray diffraction and electron-microprobe analysis to be wSio.7. Ball-impact experiwzents produced rosettes at 850°C. Optical and electron microscopy showed evidence of slip and cross slip and twinning produced by microhardness indentations. Prismatic (100), [001] slip was found and cor~elated with hardness data. THE present study was undertaken to investigate the hardness anisotropy of as-grown and annealed single crystals of tungsten disilicide. The existence of the silicide WSiz in the W-Si system has been well-established and its structure thoroughly investigated zachariasen2 found WSi, to have a tetragonal C type of structure, similar to that of MoSi, with lattice parameters a = 3.212A, Kieffer et al. studied the W-Si system and measured the density and microhardness (at a 100-g load) of both polycrystalline WSi, and WSi,.,. The values found were 9.25 g per cu cm and 1090 kg per sq mm for WSi,, and 12.21 per cu cm and 770 kg per sq mm for WSi0.7, respectively. According to Samsonov et a1.5 the microhardness of polycrystalline WSi2 is 1430 kg per sq mm (at a 120-g load). EXPERIMENTAL The WSi, single-crystal boules investigated in this paper were grown by a Verneuil-type process using an electric arc by the Linde Division of the Union Carbide Corp.6 The largest specimens were 8 mm in diameter by 16 mm long. The crystals had an average density of 9.01 g per cu cm with a tungsten • silicon content of 99.9 wt pct. The major impurities were: 87 ppm O, 41 ppm N. 54 pprn C, 500 ppm Zr, 50 ppm Na, and 50 ppm Mn. The crystals were silicon-poor, the average silicon content being 22.20 pct (stoichiometric value is 23.40 pct), and tungsten-rich, the average tungsten content being 77.70 pct (stoichiometric value is 76.60 pct). As-received single crystals were ground and analyzed by powder X-ray diffraction technique using Cu Ka radiation. Laue and layer line rotation patterns were obtained on cleaved sections of WSi, single crystals. Electron-microprobe traverses of representative crystals were done using a Phillips-AMR electron microanalyzer. Carbon replicas were used to prepare electron micrographs. This work was done with a JEM-6A electron microscope. Prior to the metallographic examination, the specimens were mounted in Lucite and then polished for short times on polishing wheels using 9-, 3-, and 1-p diamond-grade pastes. Finally they were fine-polished with Linde A powder for 24 hr on a Syntron vibratory polisher. The samples were etched with 4H 2 O:1HF:2HNO3, which is a medium fast-acting etchant. The combination 1HF:2HNO3:5 lactic acid is also a satisfactory etchant. Annealing runs for selected specimens were made at 1600" and 1800°C for 3 hr at 1.0 to 3.0 x 10-5 mm Hg. A Brew tantalum resistance furnace with WSi2 powder for setters was used. The WSi2 powder was the same as that used for the crystal growth. Temperatures were measured with a calibrated W, W-26 pct Re thermocouple and a microoptical pyrometer. Powder X-ray diffraction, emission spectrographic, and electron-microprobe analyses were done after the annealing runs. For microhardness measurements a Tukon Microhardness Tester Type FB with a Knoop indenter was used. Although measurements were taken at loads ranging from 25 to 1000 g, the 100-g load was chosen as the standard load. All measurements were taken at room temperature. Only indentations of cracking classes 1 and 2 were considered.' DISCUSSION OF RESULTS Powder X-ray diffraction analysis showed the as-received crystals to be single-phase WSi2. Laue and layer line rotation patterns obtained on cleaved sections of WSi2 single crystals proved them to be tetragonal WS 2 2 The results also indicated that the c axis of the crystal was oriented parallel to the boule or growth axis. Electron-microprobe traverses across the matrix of the as-grown crystals showed them to be homogeneous WSi,. Optical and electron microscopy of etched crystals, however, revealed that they contained minute amounts of the "golden" and the "blue" second phases as opposed to the "white" or WSi2 phase. These two second phases were concentrated in inclusion and etch-pit

Jan 1, 1965

Laboratory flotation tests on sized fractions of a certain number of selected minerals with homologous fatty acid derivatives (i.e. sodium salts and amine acetates) confirm that the higher homologues are more efficient collectors than the lower. Tests were carried out on sized material and finer size fractions floated at lower collector concentrations.It is suggested that selective flotation is best achieved with the reagent which most readily floats the most friable mineral in the ore, and that grade of product will be improved with the lowest usable homologue.INTRODUCTIONFlotation of non-sulphide minerals with fatty acids as collectors is usually less selective than the flotation of sulphide minerals with xanthate collectors. It is common to use the gradation in collecting power of homologous series of xanthates, as well as the more specific effects of activators and depressants, to achieve the separation of sulphides.The original aim of the work was to ascertain whether sodium salts of fatty acids (anionic) and fatty amine aceta:tes (cationic) could be selected from a homologous series to achieve better selectivity in separation of nonsulphide minerals by flotation. Subsequently the importance of friability of minerals in selective flotation was observed and the aim was expanded to develop a more practical approach to the testing of ore.MATERIALS USEDMineralsA series of massive mineral specimens, as pure as could be obtained, was procured. The specimens were cleaned by removing extraneous material, and then crushed and dry...

Jan 1, 1965

By Craig R. Barrett, Jack L. Lytton, Oleg D. Sherby

The types of substructures developed during high-temperature creep of (110)[001]-oriented polycrys-talline Fe-3.1 pct Si were examined by electroetching of dislocation sites. Edge dislocations were observed to accumulate adjacent to grain boundaries and poly-gonize perpendicular to their glide planes to form a "Pile-up" of nearly parallel tilt boundaries. The dislocation density developed within the grains during steady-state creep was found to increase with increasing stress. The formation of periodically spaced groups of edge dislocations along grain boundaries was observed, and it was proposed that these formed to relive bending stresses at grain boundary shear .faults. Grain boundary serrations developed at these faults, and it was suggested that this was a result of localized grain boundary migration at the polygonized groups. THE authors have conducted a series of high-temperature creep tests on (110)[001]-oriented poly-crystalline Fe-3.1 pct Si sheet. The creep specimens were examined at various stages of creep by means of electrolytic etching of dislocation sites using the chrome-acetic acid solution developed by Morris.' Hibbard and Dunn2 have demonstrated that the etch pits produced with this technique correspond to single dislocations. It is the purpose of this paper to present and discuss the dislocation substructures which were formed during high-temperature creep at constant stress. EXPERIMENTAL PROCEDURES The polycrystalline Fe-3.1 pct Si sheet employed in this study contained a (110)[001] texture. This texture was quite strong, and the elastic properties of the sheet closely approached those of a single crystal of iron.3,4 A typical analysis in weight percent for this material is 3.1 Si, 0.1 Mn, 0.003 C,

Jan 1, 1965

By Ralph H. Whaite

The Bureau of Mines program for microfilming maps of abandoned mines in the Pennsylvania anthracite region is described. A catalog of the maps that have been microfilmed in the Eastern Middle anthracite field--the first area to be covered in the program--is presented. Additional catalogs will be published as significant mining areas are completed.

Jan 1, 1965

By R. J. Quigg, G. S. Doble

Commercial stress -relieved TD Nickel bar was shown to retain room- and elevated-temperature tensile strength after exposure up to 2501°F. Cold swaging increased both room -temperature and 2000°F tensile strength. After annealing at 2500°F the strengthening due to swaging was retained at 2000°F hilt eliminated at room temperature. Annealing produced changes in hardness and X-ray half peak width indicating the presence of recovery processes as 1071° as 1000°F but no recrystallization of swaged material was noted at any temperature. In contrast to swaging, rolling induced a recrystal-lized structure after annealing. The tensile strength of this recrystallized structure was comparable to the cold-worked condition. High-temperature tensile properties of as -received bar were highly anisotropic with the transverse tensile strength being one fifth the longitudinal value. The aniso-/ropy is affected by working direction and may he partially reversed by changing the direction of metal flow. The divergence in tensile strength, beginning above 550°F or- approximate one third the absolute melting point, is strain-rate dependent. T D Nickel is a commercial dispersion-hardened alloy containing 2 vol pct thoria. The dispersion, consisting of spherical particles 0.030 to 0.050 in diameter with an interparticle spacing of less than 1 is reported to maintain stable properties up to 2400°F.1 This stability of second phase results in maintenance of elevated-temperature strength at higher temperatures and longer times than normal nickel-base superalloys.2 The purpose of this paper is to describe the effect of various mechanical working operations on the strength and microstructural stability of TD Nickel bar. MATERIAL AND PROCEDURES All material used in this study was commercial TD Nickel bar. This material is produced by a chemical process which results in a nickel powder containing a dispersion of thoria particles. The powder is then pressed, sintered, extruded, and subsequently worked to bar stock. Three starting materials from three separate lots were used: as-extruded bar. 1-in.-diam stress-relieved bar, and 1/2-in.-diam stress-relieved bar. Since TD Nickel bar stock is cold-worked without a recrystalliza-tion anneal, the accumulated deformation or degree of cold work in these materials increases as the bar diameter decreases. Some of the 1/2-in.-diam bar was swaged to 1/4 in. diameter at room temperature in order to produce an as-worked condition for comparison with the stress-relieved stock. Tensile testing was performed on an Instron Tensile Tester at a constant crosshead speed of 0.020 in. per min. The 0.2 pct offset yield strength was measured from the load-crosshead movement plot. Specimen gage dimensions were 0.080 in. in diameter by 0.40 in. in length, producing a strain rate of approximately 0.050 min-1. Specimens were tested in air and heated within a resistance-wound furnace controlled to ±5°F. A 15-min soak at temperature was employed before testing. Samples were heat-treated in air and specimens machined after exposure with sufficient material removed to eliminate any surface contamination. X-ray line breadth was determined from a diffractometer scan of a transverse face of a bar using copper K, radiation. Metallographic preparation utilized standard mechanical polishing with Carapella's etch. Specimens for electron microscopy were electropolished in a 1:7 sulfuric/methaol solution and chromium-shadowed collodion replicas prepared. RESULTS AND DISCUSSION I) Effect of Elevated-Temperature Exposure on the properties of TD Nickel. The effect of various elevated-temperature exposures on the room-temperature tensile strength of TD Nickel is shown in Table I. In the unexposed condition the tensile strength, reduction in area, and hardness all increase with increasing accumulated deformation while the elongation decreases. After exposure at 2500°F the strength of all three materials decreases to about 65,000 psi and the elongations increase slightly. The apparent increase in strength of the 1-in. bar after a 2000°F treatment is probably experimental scatter. These results indicate that the room-temperature strengthening due to additional deformation is annealed out upon elevated-temperature exposure. In contrast to the room-temperature data, the 2000°F tensile strengths increase in order of increasing deformation even after exposure. Although some loss of strength occurs after exposure, much of the effect of working is still maintained at 2000°F. The room-temperature hardness after various

Jan 1, 1965

By J. D. Grace

[Screening by centrifugal force is an unique, subject, for with the exception of only one vibrating screen presently on the market, all vibrating screens depend upon, gravity to pass material through a sizing mesh or screen cloth. This one screen that sizes by centrifugal force and utilizes gravity only to convey materiel along the screen, is the SYMONS V-Screen. This screen was designed by Loren Symons, a member of the family that has contributed so much to the metallic and non-metallic mineral processing industries. Among Symons' other outstanding contribution to these industries are the original Cone Crusher which revolutionized reduction crushing practice, the first high-speed horizontal vibrating screen, the original Rod Deck Screen, and one of the earliest vibrating Bar Grizzlies.]

Jan 1, 1965

By A F. Kravic

Carbonyl nickel powders of irregular particle shape and low a11parent density are used extensively in the production of porous nickel electrodes for nickel-cadmium storage batteries and hydrogen-oxygen fuel cells employing alkaline electrolytes. Such porous nickel matrices are at-tractive for these intended applications as they are relatively inexpensive, are corrosion resistant, have good electrical conductivity, can be welded to form electrical contacts, have a long life (as demonstrated in alkaline storage batteries), and are rugged and vibration and shock resistant. This paper describes a feasibility study concerning the production of porous multi-layer nickel electrodes by the pressing and sintering of stacked layers of green-powder rolled nickel sheet. Background H AUSNER (1) conveniently listed nine different powder compaction processes used for forming metal powders into useful shapes. These are shown in Table I. There are additional powder metallurgy processes; however, most of these are combinations of two or more processes listed in the Table. A study of the literature revealed that every powder compacting process, with the exception of isostatic pressing and explosive forming, has been evaluated or is being used for the manufacture of porous metal electrodes.

Jan 1, 1965

By A. S. Koster, G. D. Rieck

X-ray experiments were carried out to show the occurrence of cylindrical texture in drawn tungsten wire. Only a small amount of (110) (110) cylindrical texture could he found in wires of intermediate thickness, i.e., of about 1.5 mm diameter. DRAWN wires of tungsten and other bcc metals like iron and molybdenum show a well-established (110) fiber texture. Now it might be conceivable that in drawing radial stresses remove the randomness of the crystallites around the [110} axis, thus giving a fiber texture of higher symmetry. In the resulting so-called cylindrical textures a specified plane normal coincides with the radius of the wire. Several authors discuss the occurrence of cylindrical textures in bcc metals. ~ieck' found no cylindrical texture in drawn tungsten wires of 165 n diameter. Leber~ states that in tungsten wires of 3 mm diameter a cylindrical {100)(110) texture is developed, which is gradually converted to a normal fiber texture by subsequent drawing. He also reported a definite cylindrical texture at the surface of iron wires. Peck and Thomas3 observed a nonuniform mode of deformation of the grains in transverse sections of heavily drawn tungsten and iron wires. According to Bhandary and cullity4 a swaged iron wire has neither a perfect (110) fiber texture nor a perfect {100}(110) cylindrical texture. It is clear that the concept of cylindrical texture in bcc metals still lacks a firm experimental basis. Leber's eviden~e,~ which seems to be the strongest, rests upon qualitative interpretation of photographs. The appearance of the 110 and 200 lines on the photograph of 3-mm wire, however, can be very well attributed5 to a normal ( 110) fiber texture superimposed on random background; our Fig. 1, giving a Debye-Scherrer diagram of etched tungsten wire of 180 p, is free of cylindrical texture according to all authors, but is quite similar to Leber's diagram. It was therefore decided to use a different method of X-ray texture determination on tungsten wires of diameters where cylindrical textures may be expected.

Jan 1, 1965

By G. T. Horne, P. J. Wray, S. Kinoshita

CONSIDERABLE evidence exists for a strengthening mechanism operative at intermediate temperatures in bee metals containing interstitial solute atoms. The strengthening is indicated by a maximum in the ultimate tensile strength1 as well as the fatigue

Jan 1, 1965

By John W. Sweeney

Shales and clays from Illinois were sampled, tested, and evaluated to determine feasibility of producing lightweight aggregate by rotary-kiln methods. Sampling procedures and the 1 ,,,y of the Pennsylvanian shale units are discussed. Chemical, X-ray spectrographic and X-ray petrographic analyses were run on the samples to determine if a correlation existed between chemical mineralogic composition and expansion. Preliminary expansion testing was conducted in a muffle furnace. Rotary-kiln tests were conducted in a 16- inch by 14-foot rotary kiln. The weight of the aggregate ranged from 27 to 59 pounds per cubic foot. Concrete cubes employing the aggregate were tested to determine the qualities of the concrete. Compressive strength of the concrete using the 7-bag of cement cement per cubic yard mix, after autoclave curing for 6 hours, ranged from 2,950 to 6,750 psi. No correlation was found between the chemical, X-ray spectrographic, and X-ray and petrographic analyses and expansion, Sixteen samples made suitable lightweight aggregates in the laboratory rotary kiln. The expansion temperature range of eight of the samples was extremely narrow, and difficulties would probably be encountered in processing these materials commercially.

Jan 1, 1965

By John R. Riede

Most modern crushing and grinding facilities are automated to some degree. Some, of course, have a very minimum of automatic control whereas others utilize very complex control equipment. However, with very few exceptions, the re has not been a new basic control philosophy applied in this field in the past seven years. The philosophy has been broadened in scope and applied to larger plants, some of them with data logging and so- called computer control, but almost always the same tried and proven basic control philosophy is the basis for the control system. New types of control devices to better implement the automatic control have been developed and are continuing to be developed. These devices and their application will be explained and the advantages and disadvantages of each will be discussed. Automatic lubrication of plant equipment is most essential, but this paper will not cover these systems. The use of data logging and computer analysis of the data obtained is fairly recent and it is hoped that by careful analysis of this information that new and better basic control philosophy will be forthcoming. This paper will describe the basic philosophy applied in its simplest form to several types of crushing and grinding equipment, and it will describe how it is being expanded to more complex systems. Some of the economics with regard to first cost, return on investment and maintenance will be covered.

Jan 1, 1965

By James R. Boyle

The mining methods and practices used at the Young zinc mine, American Zinc Co. of Tennessee, have resulted in a low-cost, high-yield operation. Zinc ore (sphalerite) occurs in limestone-dolomite beds of the Kingsport Formation and is mined by modified room and pillar method. Utilizing trackless mining equipment which incorporates a high degree of flexibility, this operation has had a steady increase in productivity.

Jan 1, 1965

By George L. Gates

The Bureau of Mines developed a rapid instrumental method of analyzing oil well scales containing primarily barium sulfate. After removal of oil and water by carbon disulfide) the scale was dissolved in strong hydrochloric acid. The cations, barium, calcium, strontium, magnesium, and iron, were determined with the flame photometer using the method of additions. Sulfate was deter-mined colorimetrically after separation by selective adsorption on an alumina column. Phosphate was determined colorimetrically and carbonate titrimetrically. The method was reasonably accurate, although iron and magnesium were found to have mutual interference.

Jan 1, 1965

By Charles E. Whieldon

Data on the oil fields in Mahoning Columbiana, Carroll, Jefferson, and Harrison Counties, Ohio, were collected from scattered sources and com- piled to make the information readily available to operators who may be interested in conducting secondary-recovery operations in the area. General geology, oil production, oil-productive acreage, core data, reservoir calculations by townships, and miscellaneous data and reference material are presented.

Jan 1, 1965

By W. E. Howlett, R. L. Slobod

Jan 1, 1965

By R. F. Hehemann, R. H. Goodenow

Thermal arrest, hot-stage microscopy, and transtnission electron microscopy techniques have been employed to study the transformations in low-carbon iron and Fe-9 pct Ni alloys. In continuous cooling experiments, each alloy transforms at an essentially constant temperature for cooling rates below the critical rate required for martensite formation. However, high-tenzperature transformation in pure iron takes place by a different mechanism than that in the 9 pct Ni alloys. Pure iron exhibits an equi-a a structure with a low and random dislocation density while the 9 pct Ni alloy exhibits a cell or lathlike substructure analogous to that of low-carbon martensite. This same substructure characterizes upper bainite in higher-carbon inaterials. UNTIL relatively recently, diffusionless transformations have been considered to take place by the same mechanism and have been termed mar-tensitic transformations.l-3 The most characteristic feature2 of this mode of transformation is the shape change produced by a shear deformation and growth of the product phase frequently occurs at an extremely high velocity approaching that of an elastic wave.4'5 A different mechanism of diffusionless transformation was recognized first in Cu-Ga and other copper-base alloys.6,7 From the absence of surface tilting in these alloys, it has been concluded that transformation is not accomplished by the cooperative shear displacements that occur in mar-tensitic reactions. Transformation presumably takes place by the rapid movement of an incoherent interface which is capable of propagating across parent grain boundaries. Although the transformation is diffusionless in the macroscopic sense, advancement of these interfaces is accomplished by an atom by atom rearrangement. Transformations of this type therefore require thermal activation and are generally operative only at high temperature. Although requiring short-range diffusion at the interface, propagation still occurs so rapidly that the reaction cannot be suppressed with normal cooling rates.7 The resulting microstructures exhibit large, irregular-shaped regions of the product phase, which are essentially free of crystallographic features. Consequently, these reactions have been termed massive transformations. Transformation by the massive mechanism has been reported to occur in ferrous systems involving pure iron and binary alloys of iron with nickel, chromium, and silicon by Gilbert and owen.' The Fe-Ni system is of special interest in that the massive transformation was observed in alloys with less than 15 pct Ni while alloys having more than about 28 pct Ni transformed by the conventional mar-tensitic mechanism. By employing cooling rates substantially higher than those used by Gilbert and Owen, Swanson and Parr have been able to suppress the massive transformation in alloys with 0 to 10 pct Ni9 and produce martensite as revealed by surface relief. The massive transformation in the alloys having less than 15 pct Ni was identified by the lack of surface relief and an irregular rather than clearly acicular microstructure.' Speich and Swann, using thin-foil electron microscopy, identified three distinctly different structures10 in quenched binary Fe-Ni alloys. From 0 to 4 pct Ni the structure consisted of blocky grains of a with a low and random dislocation density. Alloys with 4 to 25 pct Ni exhibited a cell structure with a high dislocation density; and at greater than 25 pct Ni the structure consisted of internally twinned plates. The structural change at approximately 4 pct Ni suggests that alloys with low nickel content transform by a different mechanism than those with intermediate nickel contents and the transition from the cellular to the internally twinned structures at approximately 25 pct Ni is analogous to the transition from needles to internally twinned plates that occurs over a narrow range of carbon contents in Fe-C martensites.11,12 Conventional bainitic and martensitic modes of austenite decomposition operate in ternary Fe-C-Ni alloys having less than 10 pct Ni. This investigation was conducted in order to explore the conditions under which the massive, bainitic, and martensitic transformations occur and the relationships between these modes of decomposition.

Jan 1, 1965

By D. E. Peacock, B. Harris

The mechanical behavior of a niobium (columbium)TUNG alloy containing 20 wt pet Ta. 15 wt pet W, and 5 wt pct Mo has been studied in the temperature range 77° to 423°K. All specitrzens tested, apart from those into which oxygen was introduced deliberately, were fully recrystallized at 1500°C, had an average grain diameter of approximately 0.03 mm, and a combined carbon, ox-vgen. nitrogen, and hydrogen content of not not more than 250 ppm The meckatnical behavior of this alloy was found to be similar in seine respects to that of unalloyed bcc transilion metals. Both yield and flow stresses were sensililae to changes in deformation rate and both increased rapidly as the temperature was lowered below 150°C. A detailed examination revealed, however, that most of the temperature dependencc of the yield stress could be accounted for by the temperature dependence of the elaslic, modulus, whish is not true of the unualloyed metals. In lension at moderate strain rates, the trunsition fvom ducfile to hvittle behavior occurred just belour room teunperature bur incveasing the oxygen content from 190 to 200 pptn raised the transition temperature to about 4000K. TUNGSTEN and molybdenum have been found to be very effective high-temperature solid-solution strengtheners of niobium, but the amounts of these elements that can be added are limited if the alloy is to retain useful room-temperature ductility. It has been shown, however, that partial replacement of niobium with tantalum lowers the ductile-to-brittle transition temperature of such alloys and allows larger additions of molybdenum and tungsten to be made. Some of the high-temperature properties of niobium alloys containing these elements have been reported by Bartlett et al.,' and the work presented here describes the low-temperature behavior of one of these, a solid-solution alloy containing, by weight, 20 pct Ta, 15 pct W, and 5 pct Mo. The elastic modulus, the temperature and strain-rate dependence of the yield and ultimate tensile stresses, and strain-hardening effects are discussed and compared with those of unalloyed niobium. EXPERIMENTAL MATERIAL AND PROCEDURE The material used in this investigation was produced from a 6-in.-diameter, double arc-melted ingot. This was can-extruded at about 1150°C to a 3-in.-diameter billet, and after annealing for 1 hr at 1345°C the billet was heated to 1315OC and part rolled and part forged to 0.5-in.-thick plate. The resulting material exhibited a cold-worked structure

Jan 1, 1965

By R. W. Stahl

Gas accumulation and dust suspension are the major safety hazards in coal stockpiling and reclaiming operations. This report presents a schedule of safety precautions and plant design features devised by the Bureau of Mines to reduce danger from these and other sources.

Jan 1, 1965

By T. S. Plaskett

A striated structure perpendicular to the growth axis was observed by the copper-decoration tech-nique in dislocation-free, .float-zoned silicon crystals. The striations, which were spaced about 100 p apart, fitted the relationship d = f/u , where d is the spacing, f is the growth rate, and u is the crystal rotation rate. Each stria was resolved into an UNDOPED silicon crystals pulled from quartz crucibles by the Czochralski technique usually exhibit a striated structure perpendicular to the growth axis.'-' This structure has been attributed to oxygen segregation, with the oxygen being introduced from the quartz crucible. If the crucible is rotated, the level of oxygen contamination has been reported as high as 10° atoms per cu cm.10 These striations are similar to solute striations commonly observed in doped Czochralski-grown crystals. The periodic nature of the striations is caused by a periodic variation in the growth rate",12 which is attributed mainly to thermal gradients in the melt.13 A finer striated structure14 attributed to constitutional supercooling is sometimes observed between the coarse striae. The oxygen striations have been observed by infrared transmission techniques,' by the copper-decoration technique,' by X-ray diffraction microscopy,6-8 and by 9 p absorption measurements3 on crystals pulled from the melt both with and without dislocations. In this investigation float-zoned dislocation-free crystals were examined by the copper-decoration technique. The level of oxygen for float-zone material is less than 1016 atoms per cu cm the lower limit of detection by 9 p absorption measurement. EXPERIMENTAL TECHNIQUE The crystals were grown by the float-zone process with the rf heating coil outside of the quartz envelope containing the silicon. All float zoning was done under an atmosphere of purified helium. The Dash technique15 was used to grow the crystal dislocation-free. This involves growing the crystal initially with a diameter between 2 and 3 mm and at array of starlike precipitates of copper. The strucLure was not .found at the surface tor a depth of about 1.5 mm, or in a region of similar width ahead of a dislocation network. The structure is postulated to consist of vacancy clusterings or dislocation loops. very rapid rates, about 20 mm per min, for a distance of about 3 cm. The diameter of the crystal is then increased to the diameter of the source of silicon, which in this case was about 19 mm. Because of the arrangement of the apparatus, the zone was passed downward rather than upward, contrary to the standard float-zoning practice. Also, the source was rotated rather than the seed. ziegler17 has made dislocation-free crystals by a similar technique but has passed the zone upwards. The starting material was zone-refined and had a p-type resistivity of 150 ohm-cm. The major impurity was boron; the total impurity excluding the boron was reported by the supplier (Dow-Corning) to be typically less than 2 x 1013 atoms per cu cm. The crystals were examined by the Dash copper-decoration technique18'19—a method in which about 10" atoms per cu cm of copper are diffused at a temperature between 900" and 1000°C into silicon which is then quenched to room temperature. On quenching, the copper precipitates on crystalline defects which are then visible when viewed by transmission infrared microscopy. The photomicrographs shown were taken either of the infrared image tube screen or directly on infrared film. All sections prior to decorating were chemically polished and, for some sections, given a sirtlZ0 dislocation etch-pit examination. After decorating, the samples were mechanically polished. RESULTS A photomicrograph, taken in transmission of a decorated cross section, is shown in Fig. 1. The portion of the section shown is near the surface of the crystal. The entire cross section showed no dislocation etch pits after being given a Sirtl etch treatment. It is seen that the copper precipitated randomly. Each precipitate, as has been reported by others, was found to have a starlike structure.

Jan 1, 1965