By M. V. Lowry

This paper outlines the economic considerations that led to the recent installation of a thickener at St. Joseph LeadCo.'s Balmat, N.Y. mill. To incorporate storage of concentrates, they decided upon a single, unusually deep tank to be used for both storage and thickening. The abnormally high rake lift required was achieved by the novel feature of having the entire drive platform raise and lower. Initial operating problems are described along with the satisfactory solutions. Total costs for concentrate handling before and after installation of the storage thickeners are compared. In Northern New York State, the St. Joseph Lead Co. conducts a 2100 tpd zinc mining and milling operation at its Balmat Plant. Conventional crushing, grinding, and flotation is used to produce a zinc concentrate. For 32 years, from 1930 through 1962, the plant operated with the concentrates going directly from flotation to the filtering, drying, and loading facilities. All of the concentrate handling equipment, therefore, had to operate 24 hrs per day. It also had to accommodate wide fluctuations in tonnage, due to variations in the grade of ore. Many problems were thereby encountered in filtering and drying, but it was never concluded that the cost could be justified for installing a conventional, large diameter thickener. Finally, in 1963, they installed an unconventional thickener that is unusual in several respects. The tank depth is 16 ft instead of the normal 8 ft. The rakes are raised and lowered by having the main drive gear located on a movable platform. Automatic controls are programmed to raise the drive platform and rakes during one shift of storage. During the next two shifts of withdrawal, the controls are programmed to lower the drive platform and rakes. After three years of operating this unique storage-thickener, the conclusion is that a correct choice was made from several alternative schemes for storing concentrates. The various considerations involved in the final selection will here be analyzed, and the design features and installation details will be de- scribed. Operating problems and modifications made to the equipment will next be considered, and finally the effects upon filtering, drying, and loading will be reported. SELECTION CONSIDERATIONS Even without a thickener, concentrate handling had become reasonably efficient at the Balmat Mill by the year 1962. A tonnage that varied between 6 and 25 tph was being handled fairly satisfactorily. The filter cake moisture of 8%% seemed quite respectable, except that two large filters were usually in service. Three filters often had to be operated in order to prevent excessive filter overflow with consequent loss of values. This situation occurred when zinc concentrates from flotation exceeded 20 tph and when filter cloth blinding developed. Over the years, numerous small improvements had been effected, such as: selection of a filter cloth with better flow characteristics; addition of flocculant to the filter feed; and, in 1953, the smallest of three drum filters was replaced by a five disc, 8' 10" diam filter with a bottom agitator and snap blow. As another example of fairly efficient operation, the oil-fired dryer was doing a seemingly satisfactory job of further reducing the moisture content to an average of 3%. However, there were often considerable dust losses when the tonnage suddenly dropped off to 6 tph. At high tonnage rates, the resulting high moistures of 4% and 5% caused difficulties due to concentrates sticking and freezing in chutes leading to the box car loaders. (Drying of concentrates is justified because of the high freight rate for the long shipping distance to the company owned smelter at Josephtown, Pa. near Pittsburgh.) It was long realized that installation of a thickener would permit the subsequent steps of concentrate handling to proceed more smoothly and would alleviate the problems existing in the filtering, drying, and loading operations. It was also realized that even a slightly lower filter cake moisture could mean considerable savings in fuel oil. However, all these factors were never quite sufficient to warrant the expense of a thickener until three more considerations were added to the picture. First, the advent of flocculants meant that a thickener of relatively small area could now be considered. Secondly, a complete renovation of the zinc flotation circuit was made between 1957 and 1961. The

Jan 1, 1967

By H. I. Aaronson, H. A. Domian, G. M. Pound

The thernodyna,nics of I the Proeutectoid ferrite re-action ha1.e been investigated on the bases of three diifevent descviptions of the statistical thernzodynamics of interstitzal solid solutions. Especially at low ternperatures, substantial dijeretzces are found in the valltes of the extrapolated y/y + a and cr/a + y equilibriurn curls, and in the To- co7nposilion metastable eqliilibriunz curl-es thus co,npited. Although neither actiztity nor phase-diagram date are able to distingrish udeqiutely among the various descviptions, the statustics of Lacher, Fouller, and Guggenheinz provide the ?nost conplete epresentation az3ailable of the single carbon-ctrbon interaction energy (w) nzodel of an intevstitiril solid solution, and the relationships deduced frojrl then2 are accordingly pre.ferred. The findings tlzut w in austenite 'aries significu?ztly uith tenpevntrue and that phase-diagawr data arc not accurately con?palible usith eqcrctions deduced on the basis of actility infoation indicate, hou'e13er, that a wzore cornplex nlodel of the uustenite , und pvobably of the .feyrite, solirl solutions will have to forn the basis of f4tuve statistical t1.eat1nents. Some suggestions for such a ruodel arc advanced. Althoug11 w represents a vepltlsio energy in austozite, it was found to corvcsporzd in ferrite to a binding energy, in qualitatit.e accord zc,itlz the internal-friclion results of Keefer and wert. ThE transformation of austenite to proeutectoid fer-rite is becoming recognized as an exceptionally useful vehicle for quantitative studies of the kinetics of phase transformations.'" Reasons for this popularity include well-characterized microstructures which develop on a convenient scale with acceptable kinetics within a considerable temperature-composition region, the absence of great sensitivity to common impurities, and, especially. the availability of a unique wealth of the ancillary information indispensable for the quantitative interpretation of kinetic measurements, including phase diagram,3 crystallographies diffusivity,5 inter-facial energy,=17 elastiit," specific vlume, ''' and ativity'-' data. Development of considerable amounts of additional thermodynamic information from activity data is of particular importance with respect to kinetic studies, since much of this information is needed in temperature-composition regions not directly accessible to presently available techniques for the measurement of equilibrium properties. A generally useful approach to the thermodynamics of solid solutions, which is of especial value in this situation, is based upon the formulation of the free energy of such solutions as a function of temperature and composition. The free energy of solid solutions has been resolved into many components. Particularly in the case of interstitial solutions, with which we shall be concerned in the present study, however, only the positional entropy component has been intensively studied. The other components are conventionally taken into account by fitting equations for the activity of the interstitial species or the temperature-composition path of phase boundaries, derived principally from positional entropy considerations, to experimental information on these quantities through adjustment of one or more constants in the equations. A number of studies of the thermodynamics of interstitial solid solutions have been made primarily on this basis,'"25 but only Kaufman, Radcliffe, and cohenZ2 (hereafter KRC) and ener''% ave applied the results of such studies to develop relationships for the thermodynamic quantities of interest in the austenite —- proeutectoid ferrite transformation. KRC made use of a model developed by cheil'' (on the basis of a previous study by ohansson'), and subsequently rede-rived correctly by Speiser and retnak,' in which a carbon atom is considered to inhibit occupancy of a certain number of its nearest-neighboring interstitial sites. schei120 determined the number of sites in austenite thus excluded by matching calculated and experimentally measured curves for the variation of carbon activity with the mole fraction of carbon. zener17 used a different approach. He assumed that the positional entropy of carbon is ideal both in austenite and in ferrite (i.e., no excluded interstitial sites), and included all other contributions of carbon in a temperature-independent "free-energy change" accompanying the transfer of 1 mole of carbon between the two phases. This quantity was determined by "pinning" an equation derived for the boundaries of the a + y region to experimental data on the compositions of these boundaries at a single temperature. In the present investigation, three different approaches to the thermodynamics of the proeutectoid ferrite reaction are examined comparatively: I) the method of Zener; 2) the model employed by KRC and predecessors; and 3) the more detailed statistical thermodynamic treatment of the same model developed by acher and Fowler and uenheim, ' in which the problem of overlapping regions of influence of individual interstitial atoms is resolved. In order to make these comparisons, it is necessary to undertake an extension of one aspect of Zener's method; since the Lacher- Fowler -Guggenheim (LFG) treatment has not been previously used in the present context, the necessary thermodynamic "superstructure" for this treatment will be developed in parallel

Jan 1, 1967

By R. E. Mussler, F. E. Block, T. T. Campbell

An exploratovy study was made to deternzine the feasibility of preparing beryllium by the metallother-. mic reduction of beryllium oxide. The procedure involved heating a relatively nonvolatile metal reductant in contact with beryllium oxide in a vacuum. Beryllium vapors formed in the reaction were condensed as a coherent deposit on a heated surface. Reductants tested included tanthanun, yttrium, thorium, Th-Mg, and Zr- Ti alloys, and the hydrides of lanthaniir~z, yttriunz, and zirconiur?7,. Test ten7pevatures ranged from 1350'to 175O' C, and reaction times ranged frot 30 to 100 lzr. In most cases metal recoveries were lola, although yields close to 90 pct of theoretical were obtained with latzthanum, yttrium, and zirconium reductants. In most cases metal deposits were contanzinated by beryllides, /ls/cally of the Beln M or Bel3 M type. BERYLLIUM has a variety of unique properties including light weight (sp gr 1.85), low thermal neutron absorption cross section, high scattering cross section, excellent dimensional stability, high strength to weight ratio, high melting point (1285"C), high specific heat, and high thermal conductivity. Interest in beryllium as a structural material in aerospace and nuclear-reactor applications is based on these properties. In general, the potential of beryllium has been only partially realized, largely because of the brittleness of poly crystalline forms of beryllium, difficulties associated in its fabrication, and joining problems encountered in its use in structural applications. Several excellent books and monographs are available to those interested in the occurrence, extractive metallurgy, and utilization of beryllium.1"* Although an extensive amount of research on beryllium has been in progress during the past 10 years, much of the work has been concerned either with the so-called "ductility problem" or with the development of methods of fabrication and evaluation of properties of various commercial or purified grades of metal. A recent survey of the literature indicates that only limited efforts are presently being directed toward developing new methods for reducing beryllium compounds to metal. Two major commercial methods now used to produce beryllium are the magnesium reduction of beryllium fluoride and e lec trow inn ing of beryllium from fused sodium chloride-beryllium chloride salt baths. Only a limited amount of work has been done on the direct reduction of beryllium oxide. Major factors which complicate this method are the great stability of beryllium oxide and the reactive nature of beryllium metal. The stability of the oxide necessitates extremely high reduction temperatures and vacuum operation to liberate beryllium metal vapor and cause reactions of the following type to proceed: XBeO(s) +YM(s)-MYOX(s) + XBe(& As early as 1939, roll' used this reaction for the direct reduction of beryllia by zirconium and titanium, and later in 1952 ~a~el~ studied the reduction of beryl-

Jan 1, 1967

By P. G. Winchell, R. J. Russell

The distribution of displacements of originally plane surfaces by an invariant-plane strain has been analyzed statistically. The displacement ratio (the magnitude of the displacement of a point originally a unit distance from the invariant plane) can be determined from an analysis either of tilts of random surfaces or of displacements of random scratches scribed on a randowz surface. In either case the mean of the tangent of the observed displacement angle is related to the displacement ratio, and the number of observations used in determining the mean is related to the confidence limits placed on the estimate of the displacement ratio. In estimating the effect of applied stress on a phase transformation whose displacement effects can be approximated as an invariant-plane strain,* the dis- placement ratio of the invariant-plane strain is of primary importance. Two procedures for determining such displacement ratios are considered here. In the tilt method the measured quantity is taken to be the angle through which a random polish plane is rotated by the invariant-plane strain. In the scratch method the measured quantity is taken to be the angle between the original direction of a random scratch in a random polish plane and the projection of its final direction in the polish plane. In order to obtain precise results from either of the methods, it is necessary to measure the relative volume change associated with the strain in a separate experiment. TILT METHOD A locally homogeneous invariant-plane strain, P, with displacement ratio, S, may be written&apos; where ; and < are unit vectors indicating the displacement direction and invariant-plane normal, respectively, as pictured in Fig. 1. Eq. [I] describes a uniaxial strain if the direction of displacement is parallel to the invariant-plane normal and a pure shear strain if the displacement direction is perpendicular to the invariant-plane normal. The original orientation of the random polish plane relative to the invariant plane and to the displacement direction is shown in Fig. 2. The angle 03 between < and u is related to the relative volume change, ?V/V, and to the displacement ratio by As a result of the invariant-plane strain, the polish plane is rotated about its intersection with the invariant plane by the angle y, which is always taken to be positive. The tangent of this angle in terms of the above parameters is

Jan 1, 1967

By J. J. Shields

The Bureau of Mines observed two different types of longwall mining; the advancing longwall method and the retreating longwall method at seven bituminous coal mines located in five of the coal producing states. In two mines using the advancing face method, the coal faces were abandoned because of roof failures and poor production. In the other five mines using the retreating method, roof control was good as was production. The success of longwall mining depends on good roof control and good production. The use of self-advancing hydraulic roof supports, such as Westfalia, Dowty, and Wanheim props along with Westfalia coal planers and the Anderton and Eickhoff shearer-loaders have been a factor in recent successes.

Jan 1, 1967

By P. K. Leung, S. R. Allada, P. M. Dranchuk, D. Quon

The alternating direction explicit procedure (ADEP) makes use of the boundary conditions to reduce multi-dimensional problems to a series of one-dimensional problems. The method, previously applied to reservoirs containing only an under-saturated oil, has now been extended to cover the case of natural gas reservoirs. l his involves solving a non-linear partial differential equation, application of the procedure is straightforward and no calcuIational problems were encountered. INTRODUCTION There has been a growing interest in formulating mathematical models of petroleum and natural gas reservoirs — models which permit the engineer to examine and evaluate the physical and economic consequences of various alternative production policies. The tremendous reduction in the cost of solving such models in recent years has made possible their use as an almost routine management tool. This reduction is the result not only of improved computer hardware but also of the development of more efficient mathematical techniques. The present paper is concerned with the application of a recently proposed numerical method (ADEP) to two-dimensional gas reservoirs. STATEMENT OF THE PROBLEM Given a two-dimensional Region R, bounded by a closed Curve C (Fig. 1) such that the behavior on Curve C is known, the differential mass balance for each fluid phase in R, neglecting gravitational effects and assuming Darcy&apos;s law for fluid transport, can be written as:

Jan 1, 1967

By R. C. Ku, A. J. McEvily, T. L. Johnston

The microplastic response of a series ofas-quenched Fe-Ni-C martensites has been measured at 77°K. At strains less than JO&apos;3 the flow stress is governed primarily by the transformation-induced dislocation structure of the martensite. Only at strains in excess of 10-3 is the influence of carbon manifested in the flow stress. At these macroscopic strains, typically 10-2, the solid-solution hardening is proportional to (wt pct C)1/3, and, in an alloy containing 0.39 wt pct C, amounts to 50 pct of the flow stress. THE technological significance of high-strength ferrous martensite has stimulated many investigations of its structure and properties. Although our knowledge of the characteristics of martensite has increased immensely, especially with the advent of high-resolution techniques, an understanding of the basic strengthening mechanism still remains elusive. The purpose of the present paper is to consider certain aspects of micro-plastic behavior of Fe-Ni-C martensite which we feel can help to resolve this important problem. Such alloys are particularly suitable for experimental investigation because their compositions can be adjusted to reduce the M, to a temperature low enough essentially to eliminate the diffusion of carbon in the freshly formed martensite.1 The mechanical properties in this condition are of interest inasmuch as they reflect a state that is free of the important but complicating influence of precipitation processes. In this virgin martensite the carbon is distributed as it was inherited from the parent austenite; i.e., it is present interstitially, and gives rise to tetragonality through strain-induced ordering.&apos; In order to determine the source of strength of such alloys, Winchell and Cohen1 investigated the low-temperature macroscopic stress-strain behavior of a series of virgin martensites of increasing carbon content but of common M, temperature (-35°C). They found that the flow stress increased rapidly with carbon content up to 0.4 wt pct; beyond this point the flow stress increased at a much slower rate. It was concluded that martensite is inherently strong. To account quantitatively for the strength of virgin or as- quenched martensite in terms of the role of carbon, Winchell and cohen3 suggested that the carbon atoms, trapped in their original positions by the diffusionless martensite transformation, interfere with dislocation motion according to a model akin to that of Mott and Nabarro. 4 In this treatment, individual carbon atoms are considered to constitute centers of elastic strain and thereby generate an average stress resisting the motion of dislocations throughout the lattice. The additional stress necessary to move dislocations, over and above that necessary for motion in a carbon-free martensite, is given by where L is an effective length of dislocation capable of motion. L was assumed to be limited to the spacing between the twins that are an essential structural element of Fe-Ni-C martensites. They assumtd the spacing to be invariant and of the order of 100A. However, recent work5 has shown that L is variable and can be in excess of 1000Å, so that the assignment of an appropriate value of L is not straightforward. In contrast to the above conclusion that there is an intrinsically high resistance to plastic flow, it has been suggested by Polakowski6 that freshly quenched martensite is in fact "soft" in the sense that dislocations are initially free to move upon application of stress. The high indentation hardness and macroscopic yield stress of ferrous martensites are then a consequence of rapid strain hardening that depends upon carbon in solution. Consistent with this point of view are the results of Beau lieu and Dubé who measured the rate of recovery of internal friction as a function of aging (tempering) temperature in a freshly quenched steel containing 0.90 wt pct C, 0.37 wt pct Mn, 0.1 wt pct Cr, and 0.07 wt pct Ni. The kinetics were clearly consistent with the idea that many dislocations are unpinned in the as-quenched state and that during aging they become progressively pinned by carbon at a rate controlled by carbon diffusion in the body-centered martensite lattice. In order to provide a basis upon which to distinguish between the "hard" and "soft" interpretations indicated above, we have made studies of the initial stages of plastic deformation in Fe-Ni-C martensites similar to those&apos;used by Winchell and Cohen. It will be shown that the results support the contention that dislocation segments in as-quenched material are indeed

Jan 1, 1967

By d&apos, Kathleen J. Amico

This summary appears in Minerals Yearbook volumes I and III, which cover mineral production in the United States, its island possessions, the Canal Zone, and the Commonwealth of Puerto Rico, as well as the principal minerals imported into and exported from the United States. The several commodity and area chapters contain further details on production. A summary table comparing world and U.S. mineral production also is included. Mineral production may be measured at any of several stages of extraction and processing. The stage of measurement used in the chapter is normally what is termed "mine output." It usually refers to minerals in the form in which they are first extracted from the ground, but customarily includes for some minerals the product of auxiliary processing operations at or near mines.

Jan 1, 1967

By Thomas C. Wilder

The activities of both components and the partial and integral molar thermodynamic properties of mixing for the liquid Al-Ge system at 1200°K and for the gertnanium-rich Al-Ge liquidus have been determined from data for eighteen alloys of compositions in the range 0.0593 < 0.880 using the reuersible gal-vanic. cell in the temperature interval 9320 to 1258°K. The liqui-dus compositions above 93 2 °K loere also ve determined by observing the discontinuities in the C us T plots for the high-melting alloys. This system shows moderate negative deviation from ideality throughout, the values for y° being 0.212 and 0.189 for aluminum and germanium, respectively, at 1200°K. Pavtial molar Properties of aluminum on the germanium-rich solidus and at infinite dilution in Ge(s) oboue 932°K were estimated from the foregozng measurements and the equlibrium data of previous investzgators. RECENT compilations of data1" have shown an increasing demand for knowledge of the thermodynamic properties of mixing of metallic alloy systems. In the case of binary-liquid systems where one of the components is a semiconductor this information is useful because, primarily, properties of the second (dopant) component on the liquidus, solidus, and at infinite dilution may be determined more accurately than from calculations based on the phase diagram. In this investigation a reversible galvanic cell was used to determine the chemical potential of aluminum in the two-phase region, liquid + [Ge], on the germanium-rich side of the A1-Ge system in the temperature range 932" to 1193°K. In addition, similar measurements for homogeneous liquid A1-Ge alloys for the entire composition range were obtained for the temperature interval 932" to 1258°K. The cell used was: The experimental technique and the treatment of the data were essentially the same as described earlier394 and are elaborated upon only briefly here. Each cell consisted of a liquid aluminum anode and three A1-Ge alloy cathodes of different composition which were held in Morganite alumina crucibles. The alloys were made up from aluminum and germanium weighed to the nearest 0.1 mg to a total weight of 5 to 10 g. Aluminum was a gift of Aluminum Co. of America and had a purity of 99.995+ pct. Germanium of transistor grade was a gift of Bell Telephone Laboratories. The four electrodes were contained in a larger alumina crucible which also held the prepurified fused chloride electrolyte. Contact to the electrodes was made by tantalum wire leads sheathed in alumina. The tantalum leads were centered in the electrodes by suitable positioning of an alumina radiation shield which fitted on the top of the - alulnina crucible. Two chrome l-alumel thermocouples, sheathed in quartz wells, completed the internal cell arrangement. The entire assembly was enclosed in an alumina tube, fitted with a water-cooled copper head so the system could be evacuated and then flushed with purified argon. *

Jan 1, 1967

By E. H. Rennhack

When cast hypoeutectic Zn-Ti alloys are rolled, the TiZn15 compound particles arising from eutectic decomposition form a network of fibers promoting improved creep resistance.&apos; The effect is magnified with increasing titanium content and extends to hy-pereutectic concentrations. Strip produced from the latter-type alloys, however, also contains large, primary crystals of the compound that tend to initiate cracking during subsequent fabrication operations. In a study of the influence of various casting modifications on the size and distribution of these crystals, the phase relationships existing between the eutectic and the TiZnIs intermetallic compound in the Zn-Ti system were of major interest. Although several in- vestigators1 4 have explored the equilibria within this compositional range, their results show considerable lack of agreement. Consequently, with the exception of the solvus boundary, the constitution of this system containing up to approximately 1.0 wt pct Ti was . The findings are reported in the present note.

Jan 1, 1967

By S. Shapiro, G. Krauss

RECENT investigations1 3 of the products of marten-sitic transformation in Fe-Ni and Fe-Ni-C alloys have made use of light microscopy to describe mar-tensitic fine structure. The application of conventional metallographic techniques to this problem was possible because of the similarity of distributions of parallel striations developed by etching polished surfaces to distributions of transformation twins which are positively identified in thin films by transmission electron microscopy. The surface striations frequently are not well-defined, and could also be due to, for example, rows of etch pits which are not resolved by the light microscope. This note describes the etching effects revealed by examination of surface replicas of mar-tensite in the electron microscope. The application of a replica technique both extends the observations of fine structure made with the light microscope and allows the results of conventional metallography to be used with more confidence. Samples of an Fe-33 wt pct Ni alloy were used for this study because of the detailed knowledge of the fine structure of martensite which has been developed&apos;-4 for alloys of about this composition. Samples transformed to martensite at -120°C, and transformed samples heated to 340°C to effect a small amount of reversal of martensite to austenite, were examined. Surfaces were first prepared for replication by elec-tropolishing in a chromium oxide-acetic acid electrolyte at a current density of 0.1 amp per sq cm and a temperature of 15°C or a perchloric acid-acetic acid electrolyte at a current density of approximately 2 amps per sq cm and a temperature of 15°C. The polished surfaces were then etched for 4 to 7 sec by immersion in a solution of equal parts HC1, HNO,, and H20. Application of the etchant for this period of time produced discrete attack of certain features without loss of resolution due to overlapping of areas most susceptible to etching. The etched surfaces were replicated by 1) preshadowing with Pt-Pd alloy at an angle of 20 to 30 deg, 2) depositing a thin carbon film, and 3) stripping the film and shadowing material by immersion in a 5 pct nital solution. Two types of etching effects were observed by examination of the surface replicas in the electron microscope: l) continuous striations centered at the bottom of long grooves or the tops of pyramidal elevations on the sample surface, and 2) high densities of fine etch pits. Examples of both types of features are shown in Figs. 1 to 4. The striations are in each case continuous and have the same characteristic configurations as do transformation twins in martensite. Fig. 1 shows that the density of grooves decreases toward the edge of a martensite plate and Fig. 2 shows a region where the striations are of varying length. Similar examples of transformation twin arrangements determined by transmission electron microscopy of thinned foils of martensite have been shown in the literature,&apos;~ and, based on these similarities, the striations and their associated grooves or mounds are considered to be evidence for the presence of transformation twins. The transf~rmation twins in martensite are on the order of l00 A thick, much too fine for resolution by the light microscope. It appears that orientation-dependent etching of the matrix martensite about the twins results in grooves or surface elevations which

Jan 1, 1967

By T. Estelle Gardner

The Bureau of Mines made enthalpy measurements on sodium bromide and sodium iodide in the temperature range 400° to 1,200° K using an ice calorimeter. Equations representing enthalpy as a function of temperature were derived from the data by the method of least squares. These equations were used to calculate smooth values of heat capacity, enthalpy, and entropy at 50° K intervals from the ice point to 1,200° K. The melting point determined for sodium bromide was 1,020° K; the melting point of sodium iodide was 934° K. The heats of fusion of sodium bromide and sodium iodide were calculated to be 6,270 and 5,680 cal/mole, respectively.

Jan 1, 1967

A method is proposed for the analysis of tin in cassiterite ores. Tin is volatilised by heating with ammonium iodide. The tin iodide so formed is extracted with hydrochloric acid and the concentration is measured by atomic absorption spectroscopy using an air-hydrogen flame.It is considered that a more efficient extraction of tin and faster reproducible results are obtained than by any other known method.

Jan 1, 1967

By Donald W. Mitchell

The fire hazard of neoprene, polyvinyl chloride, and rubber conveyor belts was studied at the Federal Bureau of Mines Experimental Coal Mine. The effects of intensity of ignition source, velocity of the ventilating air, and type of belt were investigated at three levels in small-scale gallery experiments. Studies were made in the mine on the effects on ignition and flame propagation of belt-entry dimensions, belt widths, and belt configuration. Methods for extinguishing belt fires were also investigated under simulated mining conditions, and during these trials coal dust and grease were placed on the belt. The research showed that conveyor belts will burn. Neoprene, polyvinyl chloride, and rubber belts, with and without carcass, ignited and propagated flame. The highest rate of flame propagation was obtained on rubber belt. The fire hazard increased with increase in intensity of ignition source and air velocity. Flame propagated only when air was forced through the test zone; propagation was not obtained when forced ventilation was not used, as would exist in a neutral entry in a mine. Automatic water sprays and high-expansion foam effectively arrested flame propagation; direct application of water and bicarbonate dusts was ineffective.

Jan 1, 1967

By Stephen C. Brown

The major developments of the world&apos;s Mineral economy in 1955 were the continued rise in production and consumption of practically all major minerals. the sharp increase in output of the fertilizer minerals in response to demands for greater food output, the cutback, in new investment for steel capacity in Europe and Japan, Europe&apos;s continuing decline as a producer of primary minerals, and the emergence of nuclear power as an economically competitive factor in the energy economies of the United States and Western Europe. In resource development, discovery of new natural gas deposits in the North Sea and the continued development of Australia&apos;s bauxite and iron ore resources, making this country a major source for these commodities, were significant.

Jan 1, 1967

By Harold J. Bennett

This report deals with the processing and marketing of iron and steal scrap in the intermountain States of Arizona, Colorado, New Mexico, Utah, and Wyoming and the northwestern Plains States of Nebraska, North Dakota, and South Dakota. The quantity and quality of iron and steel scrap consumed in both the steel mills and iron foundries in these States in 1964 were decided by (1) the type of facilities used to produce an end product; (2) the availability of a dependable source of iron and steel scrap at competitive prices; and (3) the, ratio of the cost of iron in iron ore to iron in scrap. In recent years the quantity of scrap used per ton of steel ingot produced has decreased. The major individual. consumers of iron and steel scrap were the steel mills in Arizona, Colorado, and Utah, foundries in Utah and Arizona, and copper leaching, operations in Arizona, New Mexico, and Utah. About 2 million tons of iron and steel scrap was used by the iron and steel industry in 1964. Although there has been a decline in the amount of scrap used per ton of steel ingot produced because of changes in steelmaking methods, there has been a slight increase in the overall quantity of scrap used because of the increase in ingot production. It is estimated that the scrap consumption in the steel industry will increase by 19 percent by 1980. In addition to the scrap consumed by the steel industry, 273,000 tons of ferrous scrap were used by copper-leaching operations. Thirty-one percent of the ferrous scrap used by the steel industry in 1964 was purchased from dealers and other sources. The CF&I Steel Corp. (formerly The Colorado Fuel and Iron Corp.) at Pueblo, Colo., complemented its blast- and open-hearth-furnace operations with basic-oxygen converters in 1962. The basic-oxygen and open-hearth furnaces were charged with 30 and 90 percent scrap, respectively. Future use of the open-hearths would probably be used to supplement ingot production requirements. Because it was more economical to use less scrap and a high molten-metal charge, the United States Steel Corp. at Geneva, Utah, which uses the open-hearth process to make steel, charges the furnaces with 25 to 35 percent scrap. The Allison Steel Manufacturing Co. at Tempe, Ariz., uses a 100 percent scrap charge in its electric furnace. Although it was estimated that there were 327,000 tons of various grades of motor vehicle scrap generated in 1963, no estimates were made concerning the total quantity and grade of scrap available in the area. Most of the scrap used in the steelmaking industry originated within the area. It was advantageous to sell scrap generated in eastern Nebraska, North Dakota, and South Dakota to markets in the Midwest because of freight costs.

Jan 1, 1967

By M. L. Rudee, R. A. Huggins

Samples of iron containing nitrogen or carbon have been given treatments similar to those used in cold-work peak (CWP) measurements and examined by transmission electron microscopy. It was observed that the unusual and nonreproducible behavior of the carbon CWP can be explained by a strong tendency for carbon to form grain boundary precipitates at temperatures below those used for CWP measurements. These precipitates dissolved at the temperatures used in the CWP measurements. There was no evidence for nitrogen precipitation at grain boundaries. There was no indication of precipitation along dislocations in either carburized or nitrided samples given treatments similar to those of CWP measurements. Although it is possible that subelectron-microscopic clustering had occurred, this observation supports the theories of the CWP that are based on continuous atmospheres rather than on individual precipitates. In an earlier paper,&apos; the present authors developed a new distribution function to predict the occupation of sites for interstitial impurity atoms around a dislocation. When this distribution was applied to the case of carbon and nitrogen in iron, it predicted that, if the temperature dependence of the concentration of solute atoms in the matrix was controlled by the presence of equilibrium carbide or nitride precipitates, the tendency for nitrogen to segregate to dislocations would be greater than that for carbon even though their binding energies to dislocations are identical. The cold-work internal-friction peak (CWP) is considered by most authors to be produced by the interaction of interstitial impurities with dislocations. Many investigators have studied the CWP in iron containing carbon and nitrogen and have observed a significant difference between its behavior in the two cases. In this paper a series of experiments will be reported that were initiated to determine whether the application of the new distribution function would explain the observed differences between the carbon and nitrogen CWP. Although it was found that the distribution function, pev se, did not explain the differences, the differences became clear, and some insight into the mechanism of the CWP was realized. Before reporting the present experiments, the literature pertaining to the differences between the carbon and nitrogen CWP in iron and the various mechanisms proposed for the CWP will be reviewed. LITERATURE REVIEW Snoek2 first observed the CWP in iron specimens containing nitrogen, but also reported a weak and unreliable peak in carburized samples. Later, Ke3 established that the CWP height was proportional to the degree of deformation. The presence of nitrogen alone would produce a peak of the same size as found in a sample containing both nitrogen and carbon, and KG concluded that the CWP was caused by nitrogen. In a discussion of G&apos;s paper it was reported that Dijkstra had investigated the CWP in samples that contained only carbon. He found it to be much smaller than the nitrogen peak and "unstable". KG et al.4 charged specimens of iron with both carbon and nitrogen. They observed that the carbon CWP was much smaller than that observed in nitrided samples, but that aging at 300°C caused the carbon peak to increase. A similar treatment produced no change in a nitrogen peak. Annealing at higher temperatures caused the height of the CWP in both the nitrogen and carbon samples to decrease. This behavior was also observed by Kamber et al. 5 who found that the activation energy for the annealing of the CWP was identical with the activation energy for the self-diffusion of iron. They concluded that the annihilation of dislocations by climb caused the reduction in the CWP height. Kamber et al. studied the "unstable" carbon peak in detail. They measured both the Snoek and CWP during various aging treatments. In carburized samples, aging at 100°C caused the Snoek peak to disappear, although the CWP peak remained small. However, a subsequent treatment for 5 hr at 240°C caused the CWP to reach a maximum. They proposed that an additional location for the carbon, other than whatever site produced the CWP, is present. In nitrided samples the CWP was completely developed as soon as a measurement was made; additional sites are not present. No explanation of either the additional site or the difference in the behavior of carbon and nitrogen was offered. petarra5 performed a systematic study of the effect of composition on the CWP. Using three kinds of "pure" iron, he showed that there was a residual CWP when the carbon and nitrogen concentrations had been reduced to less than that detectable by Snoek-peak measurements. He observed the same general annealing behavior and composition dependence as previous investigators, with the following exceptions. On first measuring the carbon CWP, it was found to be identical with the residual peak, and essentially independent of the carbon content. If the CWP was measured a second time in the same sample, it increased in size, but was still only about one-fourth the size of a CWP in a sample of the same iron nitrided to the same composition. On the other hand, a series of annealing experiments showed that the nitrogen CWP was not al-

Jan 1, 1967

By G. A. Gross

"The Soviet Union has enormous reserves of iron ore in many different kinds of deposits that are widely distributed in this vast land area. The present iron ore industry is based mainly on deposits in Precambrian cherty iron-formation at Krivoy Rog, Kursk and Murmansk. Extensive reserves of both naturally enriched hematite ore and magnetite iron-formation in these areas alone could sup-ply all the domestic ore required for several hundred years.Many contact metasomatic magnetite deposits discovery in recent years in the eastern Ural Mountain belt and east of the Kusnetsov basin in Siberia are being developed, with ore reserves measured in billions of tons. Oolitic limonite-chamosite-siderite ores of Cretaceous and younger age at Kerch on the Black Sea and around the east and southern perimeter of the West Siberian basin constitute some of the largest concentrations of iron in the world. These sedimentary ores are low grade, of poor quality and difficult to beneficiate. Banded jasper magnetite and hematite iron-formation in volcanic rocks of Devonian age in Kazakhstan and along the Mongolian border are of special geoloica1 significance.Iron deposits in the Krivoy Rog and Kursk areas were examined and a large number of geologists discussed their work on deposits in many other parts of the Soviet Union during the writer's seven-week study tour of mines and research institutes in Moscow, Leningrad, Novosibirsk in Siberia and Kiev in the Ukraine. The descriptive geology of iron deposits of useable ore and of marginal material has been well documented in the course of systematic work and a large number of scientists are studying fundamental problems on the origin and treatment of iron ore."

Jan 1, 1967

By H. J. Morel-Seytoux

The influence of patten, geometry on assisted oil recovery for a particular dispIacement mechanism is the object of investigation in this paper. The displacement is assumed to be of unit mobility ratio and piston-like. Fluids are assumed incompressible and gravity and capillary effects are neglected. With these assumptions it is possible to calculate by analytical methods the quantities of interest to the reservoir engineer for a great variety of patterns. Specifically, this paper presents (1) very brieily, the methods and mathematical derivations required to obtain the results of engineering concern, and (2) typical results in the dorm of graphs or formulae that can be used readily without prior study of the methods. Results of this work provide checks for solutions obtained from programmed numerical techniques. They also reveal the effect of pattern geometry and, even though the assumptions of piston- like displacement and of unit mobility ratio are restrictive, they can nevertheless be used for rather crude but quick, cheap estimates. ,These estimates can be refined to account for non-unit mobility ratio and two-phase flow by correlating analytical results in the case M = 1 and the numerical results for non-piston, non-unit mobility ratio displacements. In an earlier paper1 it was also shown that from the knowledge of closed form solutions for unit mobility ratio, quantities called "scale factors" could be readily calculated, increasing considerably the flexibility of the numerical techniques. Many new closed farm solutions are given in this paper. INTRODUCTION BACKGROUND Pattern geometry is a major factor in making water-fIood recovery predictions. For this reason many numerical schemes have been devised to predict oil recovery in either regular patterns or arbitrary configurations. The numerical solutions, based on the method of finite difference approximation, are subject to errors often difficult to evaluate. An estimate of the error is possible by comparison with exact solutions. To provide a variety of checks on numerical solutions, a thorough study of the unit mobility ratio displacement process was undertaken. To calculate quantities of interest to the reservoir engineer (oil recovery, sweep efficiency, etc.), it is necessary to first know the pressure distribution in the pattern. Then analytical procedures are used to calculate, in order of increasing difficulty: injectivity, breakthrough areal sweep efficiency, normalized oil recovery and water-oil ratio as a function of normalized PV injected.

Jan 1, 1967

By William E. Mead

Although this paper has been entitled "Design of Embankments for Tailings Ponds and Waste Dumps," a better title might have been "Site Selection and Design Planning for Tailings Ponds and Waste Dumps," The procedures normally followed in performing the engineering calculations based upon the measured soil properties will not be detailed. Instead, we shall look at the subject in broader perspective which considers the environmental factors and the fundamental design principles. Disposal of waste materials left from the extraction and processing of mineral deposits has become, in recent years, an important engineering consideration for mine and mill operators. Land occupancy and land values almost everywhere are increasing at a rapid rate. So is the size of mine and mill waste dumps, thanks to our advancing technology in mineral beneficiation. Mining companies are being pressured to "clean up" their operations, both literally and in a safety hazard sense. Once, long ago, the miner could use any convenient location to get rid of his mine waste and mill tailings without being concerned over possible infringement on the rights and well-being of the public. Today, however, he must pay close attention to these matters if he wishes to avoid liability suits and the unfavorable reaction of civic groups as well as local and regional government. Most operators keenly sense their increased responsibility, not only because they are legally vulnerable, but because they realize the necessity for sharing space harmoniously with the rest of society.

Jan 1, 1967