Search Documents

By M. M. Fine

Chalcocite flotation concentrates (26-34 percent Cu and 6-7 percent S) were roasted in air to determine sulfur elimination as a function of temperature, airflow rate, and residence time. Fluosolids roasting was evaluated batchwise and continuously in a 4-inch fluid-bed reactor. Kiln roasting tests were carried out in a 4-inch ID by 6-inch-long rotary drum. Pelletizing the very fine concentrates prior to roasting was essential to minimize dust losses and accretions. Concentrate pellets, sized minus 10 plus 20 mesh and bonded with 2 percent bentonite, were excellent feed for fluosol¬ids roasting and limited dust losses to 10 percent or less. One-fourth-inch pellets were best suited to kiln roasting. Both techniques were capable of producing copper calcines analyzing well under 1 percent residual sulfur when operated at 900° C with average retention times of 3 to 4 hours. Calcined pellets were strong, porous, and readily reducible.

Jan 1, 1970

Jan 1, 1970

By Sadao Maruyama

INTRODUCTION Since the big discovery of Kuroko deposits in Kosaka mine, Akita Pref., northeastern Japan in 1959, major Japanese mining companies have been engaged in extensive exploration for the deposits expending large amounts of money. Above all their exploration activities have been particularly fruitful in discovering new deposits in northern Akita Pref. It is estimated that the total ore reserves newly found in the area are at least 50 million tons. Kuroko deposits are the most important ore source of copper, lead and zinc in Japan and have been mined since last century in the said area. Kuroko (black ore) is fine, compact aggregates with sphalerite , glena and barite as principal constituents and chalco- pyrite, pyrite and tetrahedrite as subsequent constituents. The name Kuroko comes from its appearance. It is not rare that total grade of copper, lead and zinc reaches 20 - 30% and the gold and silver content is also fairly good. Accordingly the unit value of the ore is much higher than the ore from other types of deposits. Besides the Kuroko ore, the Kuroko deposits consists of Ohko (yellow ore, massive cupriferous pyritic ore), Keikoh (silicious ore, cupriferous network ore) and gypsum ore. This type of deposit is considered to be not only an important source of base metal but also a source of gypsum and barite. Although the importance of this type of deposit had been commonly recognized, sub-surface nature of the occurrence hampered exploration work. In recent years the improved exploration techniques and increased knowledge of the Kuroko deposits have met with remarkable success in the location of new deposits. This outburst of exploration and dis-

Jan 1, 1970

By Manuel Gomez

The purpose of this study was to evaluate the feasibility of using statistical response surface regression analysis to predict the sulfur and ash distributions and the washability characteristics of coal along a seam in advance of mining. Prediction equations were developed with experimental data from channel, bench, and core samples from the Pittsburgh coal seam in Greene County, Pa. It was not possible, with the available experimental data, to construct mathematical models to predict ash and sulfur concentrations between sample points. In the authors' opinion, however, the good agreement between experimentally determined and predicted values at given sample points demonstrates the usefulness of the method. More input data, such as geologic information, seam characteristics (rock-to-coal ratio), petrographic analysis, and chemical data, would perhaps make it possible to predict sulfur and ash concentrations and washability characteristics between sample points.

Jan 1, 1970

By Morris Cohen, Robert C. Ruhl

The phases in Fe-C alloys over a wide composition range have been studied after splal quenching from the liquid state. Binary alloys containing 0 to 5.1 wt pel C as /cell as a large number of ternary Fe-C-Si alloys with 2.5 to 5.0 wt pct C and 0.3 to 5.1 wt pct Si were attlong those sludied. Olher Fe-C-X alloys, zcilh X being Co, Cr, ,Wn, Ni, and Ru , were also inrestigated after splat quenching. At high carbon contents, a new hcp phase (designaled 6 phase, but different from e carbide) is retained upon splat quenching. The .fraction of this phase varies up lo 97 pcl for a Fe-4.K-1.9% alloy. The composition of the E phase ranges from about 3.8 10 4.8 wt pet C, and the corresponding laltice parameters increase linearly ulith carbon content, while the c/a ratio remains essentially conslc~nl. The E phrtse appears to he a solulion of carbon in E iron, the latler being nornially found only at high pressures. It is deduced that the unit cell of the E phase corresponds to the formula Fe12C3, and llzal il is relaled to tlie ordered slruclures 0.f 6 iron carbide and c iron nilride. The E phase is compared and contrasted to the olher known carbides and nitrides of iron and nickel. An exlrapolaTion of the atomic volume 1,s carhon conlent of /he E pllase lzcts giz.en a neu7 estitnale jor /he alomic volume of E iron, 11.30 cu A, a1 atmospheric pressure and temperature. Other alomic volume relalionships lead to /he co~zpositioti Fe2.iC tor E iron carbide, /he unit cell fortr~ula being -Fe2rClo The E phase undergoes a lulo-slage decomposition upon healing, .forrning firsl rnarlensile plus E carhide, a/ler 1 hr at 140" lo 200°C, slid then ferr ite Plus cementile, after 1 lir a1 330" to 460°C. A1 carbo,l contents between 1.5 and 3.0 LC/ pcl, (he predo.wirzar/t plzase alley quenching is fcc austenite. The retained carbon content of this phase increases with itlcreasing silicon in certain concentration ranges, reaching a maximum of 2.37 wt pct C itz a Fe-2.6C-4.OSi alloy. This is the highest carbon conten1 reLaitled in austenite to date. These high-carbon aus-tenites can be partially tm?zsforttled lo tnartensile hy severe deformation in the temperature range of — 190 to -50°C. TECHNIQUES for splat quenching from the liquid state have been utilized in numerous recent investigations to produce metastable phases in a variety of alloy systems. Among the several ways of splat quenching, the shock-tube method appears to yield the highest cooling rates1-3, 7, 8 and was adopted here. Estimated cooling rates attained in the present experiments ranged from 10' to 10 80Cper sec.' As a part of a research program on interstitial al- loy phases, the Fe-C system was selected for splat-quenching studies. It was hoped that splat quenching would allow high metastable supersaturations of carbon to be retained in solution. Also of considerable interest were the conditions governing the occurrence of the various intermediate phases upon solidification. The alloys investigated included both binary Fe-C compositions as well as six ternary Fe-C-X alloy systems. The known phases in the Fe-C system are summarized in Table I.* Only the ferrite and graphite are ent investigation.14 and is described in detail herein Table II summarizes corresponding data on Fe-N phases, which are also of interest here because of their similarity to the Fe-C phases. EXPERIMENTAL PROCEDURES Alloys were prepared by melting the elements. 99.9 pct purity, in an inert gas nonconsumable electrode arc furnace. The buttons. weighing about 5 g. were remelted twice. were then fragmented. and their interior surfaces were examined for uniformity: if any doubt existed. they were remelted again. Chemical analyses were performed on all the alloys. the accuracy being about k0.05 wt pct. At high temperatures, carbon-containing alloys react with alumina crucibles as follows: If the atmosphere in the splat-quenching furnace does not contain sufficient carbon monoxide the alloy can be depleted of carbon and contaminated with aluminum. Calculations and experimental observations showed that 50 to 100 torr CO partial pressure effectively blocked the above reaction in all the alloys investigated. The splat-quenching equipment in Figs. 1 and 2 provides for evacuation and back-filling with CO-Ar mixtures. The furnace is capable of operation up to 1650°C. and the gettering action of the graphite heating element reduces the oxygen partial pressure in the furnace atmosphere to below 10-5 torr, thus preventing oxidation of the specimens.

Jan 1, 1970

By Willaim A. Berg

Vegetative stabilization can help meet the esthetic objections and pollution problems posed by mine wastes. However, mine wastes are often unfavorable growth media and special treatments and techniques are needed for plant establishment and continued growth. The establishment of vegetation on mine wastes was the subject of many papers presented at the International Symposium on Ecology and Revegetation of Drastically Disturbed Areas held at Pennsylvania State University on August 3-16, 1969. This paper is a summary of those papers presented at the symposium that dealt with the nutritional and physical aspects of plant establishment on a variety of mine wastes. The synopsis presented is a combination of excerpts from the abstracts, notes on the oral presentations, and rough drafts of some of the papers. The papers will eventually be published in the symposium proceedings.

Jan 1, 1970

By C. J. Chindgren

A refractory-lined, garage-type automobile incinerator with a natural gas afterburner for air pollution control was cooperatively constructed and tested by the Bureau of Mines and the Wasatch Metal & Salvage Co. in Salt Lake City, Utah. The incinerator is capable of relatively smokeless burning of 32 to 60 cars per day, dependent on the degree to which the cars are stripped prior to incineration. Preliminary burning campaigns indicate the cost of incineration to be approximately $2.75 per car.

Jan 1, 1970

By Paul G. Mahoney

The original Radum aggregate plant, built by Henry Kaiser in 1931, is the oldest of the nearly 200 individual operations established by the Kaiser companies. Since that time it has been producing aggregate products primarily for the San Francisco Bay Area. Currently, and for many years, this plant has been listed as the Nation's No. One aggregate producer. Early this year a new $10,000,000 facility went on line replacing the old plant. Construction of the facilities was performed under the direction of Kaiser Engineers construction management teams. The existing plant continued to operate without interruption during the entire construction period.

Jan 1, 1970

Average annual growth in consumption of primary energy in Australia over the past ten years has been 5.5% compared to a world average of 4.1%. Over the next ten years growth rate is expected to increase to 6% per annum due largely to the rapid development in the mineral processing industry. By the end of the 1970's natural gas is expected to supply more than 9% of Australia's, primary energy market. Coal will supply 40% and petroleum products 47%. Nuclear energy will make its appearance but-will only make a small contribution in the period. Australia has adequate reserves of natural gas and coal to supply its needs in the 1970's and beyond. However the newly developed reserves of crude, while supplying 60-70% of requirements-in the initial years; will need regular and sizable additions if they are to .keep pace with the expanding consumption. For Australia to become self sufficient in the period 1970-1990 it is estimated *that new discoveries-will need to approximate. ten times the volume of recoverable reserves found in Australia to date. .

Jan 1, 1970

By P. Dosmond

In ore mining technology, the loading and hauling operations are undoubtedly the area where the most spectacular progress has been made during the last twenty years. In the iron ore mines of Eastern France production of 62 million tons for 1962 and 19863 constitute a worthwhile experience worldwide. These deposits which are located in Lorraine are of sedimentary origin and they contain many mineralized horizons with workable seams varying in depth from 330 to 830 ft.

Jan 1, 1970

By L. B. Pankratz

Enthalpies above 298° K were determined for AgCl to 1,400° K and for AgBr to 1,200° K by copper-block calorimetry. Before melting, both compounds showed an anomalous increase in enthalpy, an effect associated with lattice defect formation. Melting points and heats of fusion were determined to be AgCl, 730° K and 2,945 cal/mole; AgBr, 700° K and 2,030 cal/mole. The heat capacity of both melted substances decreased with increasing temperature over the entire liquid ranges investigated. Enthalpies above 298° K were tabulated at even temperatures along with derived entropy increments and heat capacity values. The results were combined with the known heats of formation and entropies at 29.8.15° K to obtain values of the heats and free energies of formation over the range 298.15° to 1,400° K for AgC1 and 298.15° to 1,200° K for AgBr.

Jan 1, 1970

By M. Metzger, J. C. Bilello

Microyielding in 99.999 pct Cu occuwed in two distinct parabolic microstages and was substantially indeoendent of grain size at the relatiz~ely large grain sizes stzcdied. The strain recouered on unloading was a significant fraction of the forward strain and was initially higher in a copper-coated single crystal than in poly crystals. Results were interpreted in terms of cooperative yielding and short-range dislocation motion activated otter a range of stresses, and a formalism was given for the first microstage. It was suggested that models involving long-range dislocation motion are more appropriate for impure or alloyed fcc metals. THERE are still many unanswered questions concerning the degree and origin of the grain size dependence of plastic properties. In the microstrain region, a theory of the stress-strain curve proposed by Brown and Lukens,' based on an exhaustion hardening model in which the grain boundaries limit the amount of slip per source, accounted for the variation with grain size of microyielding in iron, zinc, and copper.' This theory assumes N dislocation sources per unit volume whose activation stress varies only with grain orientation. Dislocations pile-up against grain boundaries until the back stress deactivates the source, which leads to a relationship between the axial stress and the strain in the microstrain region given by: where G is the shear modulus, D the grain diameter, a the flow stress, and a, is the stress required to activate a source in the most favorably oriented grain.3 If this or other grain-boundary pile-up models are correct, then the reverse strain on unloading would be much larger for a polycrystalline specimen than for a single crystal. Also, the microplasticity would become insensitive to grain size if this could be made larger than the mean dislocation glide path for a single crystal in the microregion. These questions are examined in the present work on polycrys-talline copper and a single crystal coated to provide a synthetic polycrystal. EXPERIMENTAL PROCEDURE Tensile specimens 3 mm sq were prepared from 99.999 pct Cu after a sequence of rolling and vacuum annealing treatments similar to those recommended by Cook and Richards4-6 to minimize preferred orientation. Grain size variation from 0.05 to 0.38 mm was obtained by a final anneal at temperatures from 310" to 700°C. Dislocation etching7 revealed pits on those few grains within 3 deg of (111). For all grain sizes dislocation densities could be estimated as -107 cm per cu cm with no prominent subboundaries. The single crystals, of the same cross section, were grown by the Bridgman technique with axes 8 deg from [Oll] and one face 2 deg from (111). An anneal at 1050°C produced dislocation densities of 2 x 106 cm per cu cm and subboundaries -1 mm apart in these single crystals. A Pb-Sn-Ag creep resistant solder was used to mount the specimens, with a 19 mm effective gage length, into aligned sleeve grips fitted to receive the strain gages. All specimens were chemically polished and rinsed8 to remove surface films just prior to testing. The synthetic polycrystal was made by electroplating a single crystal with 1 µ of polycrystalline copper from a cyanide bath. Mechanical testing was carried out on an Instron machine using two matched LVDT tranducers to measure specimen displacement, the temperature and the measuring circuit being sufficiently stable to yield a strain sensitivity of 5 x 107. At the crosshead speeds employed, plastic strain rates were, above strains of 10¯4, about 10¯5 per sec for polycrystalline specimens and 10-4 per sec for the single crystals. Plastic strain rates were an order of magnitude lower at strains near l0- '. A few checks at strain rates tenfold higher were made for reassurance that the initial yielding of polycrystalline copper was not strongly strain-rate dependent. Test procedures followed the general framework outlined by Roberts and Brown.9,10 An alignment preload of 8 g per sq mm for polycrystals, and 2 to 4 g per sq mm for single crystals, was used for all tests. These gave no detectable permanent strain within the sensitivity of the present experiments; although at these stress levels, small permanent strains are detectable in copper with methods of higher sensitivity.11 12 stress and strain data are reported in terms of axial components. RESULTS General. The initial yielding is shown in the stress vs strain data of Fig. 1. For polycrystals, cycle lc, the loading line bent over gradually without a well-defined proportional limit, and almost all of the plastic prestrain appeared as permanent strain at the end of the cycle. The unloading curve was accurately linear over most of its length with a distinct break indicating the onset of a significant nonelastic reverse strain at the stress o u, indicated by the arrows. The yielding in subsequent cycles, Id and le, had the same general character. The single crystal behavior, shown to a different scale at the right of Fig. 1, was different in that initially the nonlinear reverse strain was unexpectedly much greater than for polycrystals. It should be noted that these soft crystals had a small elastic

Jan 1, 1970

By H. V. Fairbanks

This report covers a study of three different methods for drying ultrafine coals by sound waves. Ultrafine material is classified as coal which passes through a 100-mesh sieve. During the investigations, it was found that the addition of acoustic radiation to the drying of ultrafine coal is effective in increasing the rate of drying; the effect of acoustic radiation to improve drying decreases with an increase in the temperature of the system; the drying rate increased 10-40% when acoustic radiation was introduced into a rotary kiln but was dependent upon the environmental conditions; the application of vertical vibrations to multi-tiered drying screens increased the rate of moisture removal ten times over that obtained in the rotary kiln; the formation of coal balls in any of the drier systems retards the rate of drying; the higher the initial moisture content of the coal the greater the amount of coal balls formed.

Jan 1, 1970

Jan 1, 1970

By John V. Beall

If there is one thing that makes a fellow feel like the years are catching up with him, it is to go through a second cycle in which the adequacy of mineral resources is being "viewed with alarm." The first time we experienced such a flap was in 1951. At that time, the United Nations convened a meeting at Lake Success to study ways and means of averting a crisis in minerals. Presently there is some sentiment being expressed about the mineral scarcities that will occur in the decades ahead, in view of world population trends and increasing per capita consumption of metals. To be greatly concerned about the adequacy of metal supplies is to be highly pessimistic about the capabilities of technology. As in the past, shortages will be of temporary duration for as far ahead as the most ambitious prognosticators are projecting. The study of mineral economics is a fascinating and surprising subject. The law of supply and demand is but a starting point. The iron ore market for the steel industry is an example which comes to mind because of our receipt this week of the United Nations report "Survey of World Iron Ore Resources."

Jan 1, 1970

By C. J. Lewis

Considerable amounts of the world's known reserves of elemental sulfur are found near the surface in areas of volcanic activity both active and inactive. Because such deposits cannot in general-be mined by the well-known Frasch process, and because other methods of recovery have not proven to be economically competitive except in isolated instances, at present these reserves remain relatively undeveloped. However, projections of world sulfur demand indicate that new sources of marketable sulfur will be needed in future years 2/, 19/. For this reason, recovery of elemental sulfur from these near-surface deposits is of continuing interest. Solvent extraction as an approach to recovery of elemental sulfur from open pit-mined ores of these non-Frasch deposits has received considerable attention particularly at the research and development level 3 /, 7/, l l /, 16/, 21/,23/, 29/ This method has been and continues to be attractive because it presents the potential of high sulfur recovery and purity of product coupled with a relatively simple process flowsheet in which low energy requirements and reasonable operating costs are thought to be possible. However, the physical and chemical characteristics of the native-sulfur ores, of elemental sulfur, and of the known solvents, have presented difficulties in the development of solvent extraction processes. Up to the present time, viable processes have not been realized within the framework of sulfur marketing conditions.

Jan 1, 1970

By L. C. Noakes

Despite a long history of mining. Australia had no Commonwealth organization dealing specifically with the mineral industry until 1946, when the Australian Bureau of Mineral Resources, Geology and Geophysics was established. Once formed, this new organization quickly expanded to include a Mineral Economics Section, which was established in 1947. Australia's slowness to develop a Federal bureau for the mineral industry can best be explained in the light of her political history. From a group of British crown colonies, Australia evolved into six sovereign states which had no unified federal government until they formed the present Commonwealth in 1901.

Jan 1, 1970

By Robert W. Gordon

The art of excavating tunnels with continuous, full-face boring machines began almost 90 years ago, in the early 1880's. At this time, Colonel Beaumont designed and manufactured a seven-foot diameter tunneler for boring under the English Channel, Despite the absence of modern materials and manufacturing techniques, Beaumont's tunneler, powered by compressed air piped in from the surface, was quite successful. During its short, but impressive existence, this machine set a record of advancing in chalk 50 feet per day for 53 days - which is impressive even by today's standards. Despite the apparent success of this early tunneler, almost 80 years passed before any further significant development was accomplished in this field. Demands from the construction and mining industry and society itself have motivated the development of the modern tunneling machine. Our rapidly growing civilization needs faster, less expensive and safer means of excavating tunnels. Space age technology and materials have played a major role in making hardrock tunneling machines possible.

Jan 1, 1970

By Richard A. Queeney, Lance G. Peterson

ESTIMATES of the stacking fault free energy of copper reported in the literature show an extensive divergence of results. Based on measurements of dislocation node radii, Thornton et al.7 find the lower limit of stacking fault energy to be 60 ergs per sq cm: Jossang and coworkers4 estimate the same value should be less than 40 ergs per sq cm. Assuming stacking fault free energy to be twice the coherent twin boundary free energy, Valenzuela8 reports 72 ergs per cm, while Inman and Khan2 cite a value of 24 ergs per sq cm. which can no doubt be accounted for by almost complete absence of interstitials in solution. However, the minute concentration was sufficient to permit observable recovery of dislocation damping. Assuming a dislocation density of 1010 CM -2 and an average loop length of 0.5 , a concentration of interstitials as low as 0.01 at. ppm is sufficient to reduce dislocation damping by more than a factor of ten. The concentration of interstitial solute atoms in Ferrovac E-0.15 pct Ti was thus estimated at 0.01 at. ppm < (C + N) < 2 at. ppm. The absence at elevated temperature of strengthening due to interstitials, Fig. 1, was therefore anticipated in the titanium alloy. The temperature dependence of the flow stress below 300°K was unaffected by addition of either titanium&apos; or zirconium.&apos; Observed, however, was an initial difference in the absolute value of the flow stress below 320oK, Fig. 1. Grain size may account for the difference; the grain diameter of Ferrovac E was 30 to 45 µ and that of Ferrovac E-0.15 pct Ti 65 to 90 µ. Although second phase particles in the form of titanium carbides and nitrides precipitated in the Ferrovac E-0.15 pct Ti alloy, the spacing was too large to produce any strengthening effect. The mechanical properties measured, therefore, were inherent to the bcc lattice. 1W. C. Leslie and R. J. Sober: Trans. ASm, 1967, vol. 60, pp. 99-111. 2 H. Conrad: Journal of Metals, 1964, vol. 16, pp. 582-88. 3 A. S. Keh and W. C. Leslie: Materials Science Research. H. H. Stadelmaier and W.W.Austin, eds., vol. 1.pp. 208.50, Plenum Press, New York, 1963. 4A. S. Keh, Y. Nakada, and W. C. Leslie: Dislocation Dymmics, Rosenfield, Hahn, Bement, Jr., and Jaffe, eds., pp. 381-406, McCraw-Hill Book Co., New York, 1968. &apos;W. J. Bratina, J. T. McCrath, and H. E. Rosinger: Can. Met. Quart., in press. 6 W. J. Bratina, J. T. McGrath, and D. Mills: Suppl. Trans. Japan Inst. Metals. 1968, vol. 9, pp. 436-43. &apos;H. E. Rosinger and C. B. Craig: Can. Met. Quart., In press. %. Mills. J. T. McGrath. and W. J. Bratina: ScriptaMet,, 1968, vol. 2, pp. 311-13. The purpose of this note is to present the results of a direct measurement of the stacking fault free energy in copper. The present method avoids both the question of interaction forces of nodal dislocations and the assumption that the coherent twin boundary free energy is one-half that of a stacking fault. Fig. 1 shows a transmission electron micrograph of a stacking fault intersecting a high angle grain boundary in copper: Fig. 2 is a schematic representation of the intersecting interfaces. To produce the specimen, pure copper was rolled to 0.002 in. thickness and annealed for several hours at 875°C. These foils were strained in tension to l04 µ in. per in., and rean-nealed to 8 min. Recrystallization and/or grain growth were not observed during the second anneal, indicating that intersections such as Fig. 1 are equilibrium configurations. Many such stacking faults were observed, but few were noted as intersecting grain boundaries in well-illuminated areas. The intersection of Fig. 1 was well away from the specimen edge. Since similar defects have not been observed in fully recrystal-lized and annealed copper, it is felt that this defect is due to the tensile straining. Electron transmission

Jan 1, 1970

By R. W. Carpenter, J. C. Ogle

It is possible, by using pack-rolling instead of conventional rolling, to reduce a number of metals to thicknesses of 2µm or less. Such thinfoils are generally made at room temperature without intermediate annealing. In addition, pack-rolled foils fail by developing pinholes at thicknesses near 2µm instead of developing the shear cracks usually observed in cold-rolled ductile metals. This paper presents the results of a general investigation of the deformation substructure and texture developed in copper and iron pack -rolled from 130 to about 2µm thickness. Electron microscopy showed that in both metals a fine (0.2 to 0.5?µ m) deformation subgrain structure formed during pack-rolling; in neither case was this substructure grossly different from substructures formed during conventional rolling. The deformation texture formed in pack-rolled iron was quite similar to usual bcc textures; however, in the case of copper, the cube texture was stable during pack-rolling and the normal copper deformation texture was unstable. It is shown analytically that the constraining pack induced a large hydrostatic pressure in the foils during pack-rolling. The pinhole failure mechanism is attributed to the presence of the large hydrostatic pressure during pack-rolling; this strongly suppressed the growth of shear cracks. The stability of the cube texture in copper is also probably due to the unusuul stress distribution developed during pack-rolling. EXPERIMENTS at several laboratories have shown that very thin foils of the common structural metals and many of the rare earths can be made by "pack-rolling". 1-3 The technique was originally developed to make specimens for nuclear scattering experiments and foils for X-ray filters. It is also useful for making experimental laminar metallic composite bodies and foils thin enough for direct examination by ultra-high voltage electron microscopy without the need for special thinning techniques. Pack-rolling in the present context means a three-layer pack, with the material to be rolled into foil comprising the center layer. The outer two layers, which constrain the foil during reduction, are ordinarily austenitic stainless steel. Typically, a 130 µm (0.005 in.) metal strip can be reduced to a final thickness of 2 µm or less by this process. This is accomplished at room temperature, without intermediate annealing. It has been observed that foils produced by this process do not exhibit at any stage of their reduction the severe work-hardening found in strip rolled by conventional cold-rolling methods. Neither is the failure characteristic the same."&apos; Conventionally cold-rolled ductile metal strip fails by developing shear cracks on planes whose normals nearly bisect the angle between the rolling direction and normal to the rolling plane; these are planes of maximum shear stress. In pack-rolling this mechanism has not been observed; failure occurs by the formation of pinholes on the foil surface (penetrating the foil). If pack-rolling is continued the hole density increases. These differences in behavior imply the existence of appreciably different substructure in pack-rolled foils compared to substructure in conventionally rolled material, or perhaps that the geometry of pack-rolling has an effect on the foil behavior. This paper describes an investigation of deformation substructure and texture in some specimens of pack-rolled copper and iron, and some considerations of the stress distribution in the foils during rolling that result from the geometry of pack-rolling. EXPERIMENTAL DETAILS Three different materials were used for pack-rolling in the present work: soft copper sheet (99.8 pct Cu, 0.03 pct 0, electrolytic tough pitch) and two types of iron, Ferrovac E* and Armco iron. Each was "Crucible Stccl Co. initially in the form of 130 µm annealed strip with grain size ranges of approximately 10 to 40 µm. The initial texture of the copper (determined as noted below) was the normally observed cube type (001)[100]; there was evidence of a small amount of material in the cube-twin orientation reported by Beck and Hu.4 The initial texture of the Ferrovac E was similar to that reported for recrystallized iron by Kurdjumov and sachs,5 who list the principal orientations as {111}<112>, {001}<110> 15degfrom RD and a weak component {112}(110) 15 deg from RD. The starting texture of the Armco iron was not determined. Pack-Rolling Procedure. A four-high mill was used for all specimens. The work roll and backing roll diameters were 1.625 and 5.25 in., respectively. The peripheral roll speed of the work rolls was about 2.5 in. per sec. All foils were initially reduced from 130 to 100 µm by conventional straight rolling and then inserted into a pack, without any intermediate annealing, for further reduction. The pack consisted of an 0.033 in. (838 µm) thick 3 by 6 in. polished sheet of austenitic stainless steel, folded to make a 3 by 3 in. jacket. After folding, the jacket was given a small reduction to close the fold tightly before insertion of the foil. During pack-rolling a constant change in roll spacing was made every third pass. The roll-spacing change corresponded to a 5 pct reduction in thickness for a new pack. This approached a 10 pct reduction when the pack had decreased to about half its original thickness. At this point the deformed pack was discarded and a new one

Jan 1, 1970