By J. A. Snyder, W. L. Finlay

G. Edmunds—Solid solubility is considered to be of either the interstitial or the substitutional type. Is it possible, in a binary alloy as the simplest case, that some of the solute atoms are present in the normal lattice sites (substitutionally or filling lattice vacancies) while simultaneously others are in interstitial positionss One might even ask whether a distribution of the two types may be the normal situation. H. M. Meyer—Metastable states of interstitial atoms occupying vacant lattice sites possibly occur as well as of substitutional atoms squeezed in between regular matrix positions. However (as we know since Hume-Rothery), the solute atoms choose between the two kinds of solutions; consequently, every solute will be unequivocally either substitutional or interstitial in the equilibrium state of the solid solution. M. Balicki—In view of the fact that the authors apparently correlate the analysis of the alloys at the ingot stage with the properties exhibited at the testing stage, I would like to ask whether this is a fully justifiable procedure. In other words, how good are their determinations of solute concentration for correlating them with the mechanical properties. The answer to this question may explain some of the divergencies. Assuming good enough homogenization of the samples and exact determination of mechanical properties the position of the plotted experimental points will depend solely upon the accuracy of composition determination. If this is not accurate, say due to loss or pickup of elements during processing from the ingot to the testing stage, or due to a systematic error in the method employed for obtaining solute concentration data, the points will deviate from their true position and may align themselves along a different curve than the one expected. H. V. Kinsey—We have been studying the creep-rupture properties of titanium-base alloys at 1000°F. In the course of this work, anomalies in behavior of the alloys that would suggest that the material under test was becoming stronger as the test progressed have been observed. If this was so, the most likely explanation that we could think of was that the test bars were absorbing oxygen and nitrogen from the air during the test and were thereby becoming strengthened. In an attempt to determine the strengthening effect of absorbed oxygen and nitrogen the following experiment was conducted. A length of cold-rolled titanium was supplied by the E. I. du Pont Co. Two test bars, having a 1/4 in. diam gauge length, were prepared from this material. One bar was tested in the as-received condition. The second bar was heated in air at 1550°F for 100 hr and subsequently air cooled prior to testing. A testing temperature of 1000°F was employed. The results of these tests are tabulated in table 11. In the author's opinion, is it reasonable to assume that the bar that was exposed to air at 1550°F for 100 hr was stronger because it absorbed oxygen and nitrogen from the air during this heat treatment? W. L. Finlay (authors' reply)—Direct experimental evidence for or against Mr. Edmunds' interesting suggestion will probably never be available. It seems possible, however, that mixed interstitial-substitutional solid solution might well occur with interstitial elements. The less likely possibility of interstitial solution of a normally substitutional element like copper in aluminum was recently discussed at length by the

Jan 1, 1951

By C. S. Smith, E. W. Palmer

IN 1934, when Gregg and Daniloffl wrote their excellent monograph on the alloys of iron and copper, the most recent literature on the constitution of the alloys indicated a narrow single-liquid area for 20" above the liquidus with a closed liquid mis-cibility gap above this. Since that time, however, a number of investigators have confirmed the much earlier studies of Mushet2 and Stead3 who, among others in the nineteenth century, had described the true state of affairs. Liquid copper and iron are completely miscible in the absence of carbon, but small amounts of carbon cause liquid segregation. In 1934, one of the writers' mentioned evidence for the absence of liquid separation in carbon-free alloys at temperatures up to 1700°C. Two years later, Mad-docks and Claussen5 unequivocally established the absence of liquid segregation and published a revised diagram, reproduced in fig. 1. They also studied the limits of the two-liquid area in ternary alloys of iron, copper, and carbon as a function of carbon and iron content. In the same year Simpson and Bannister" and Schumacher and Souden7 described in some detail the properties of alloys containing 50 to 75 pct Cu. More recently Hodges et al.16 have developed the copper-rich alloys for use as high-strength conductors. In 1937, Iwase, Okamoto, and Ameniya8 published data on the miscibility gap in ternary alloys of iron, copper, and carbon that supported the conclusions of Maddocks and Claussen, and definitely located the two-liquid area at temperatures of 1450" and 1540°C. They also reported that additions of 1 pct Al, Ni, Pb, Sn, or Zn caused no segregation in 50 pct Cu alloys at 1540°C. The use of copper in amounts approximating 1 pct has found industrial employment to an increasing degree in both wrought and cast steels, for such steels are capable of being precipitation-hardened following normalizing, and have high yield strengths. This is summarized by Gregg and Daniloff,1 Sallitt,9 and Lorig and Adams,10 while Alexander" gives additional information on the heat treatment of copper-steel castings. Lippert12 has described Digby's two-phase steels containing copper and chromium. The work described in the present paper was done in the years 1932 to 1934, at which time much of the information was new. The excellent work subsequently done in other laboratories but more promptly published makes the present paper in part only a confirmation of what is now well known. There has not, however, been published any unified study of

Jan 1, 1951

By E. F. Bailey, W. J. Harris

THE temperature of the ferrite to austenite re-action is established frequently by continuous heating experiments. However, equilibrium studies of this reaction have demonstrated that austenite may form at temperatures considerably below those at which the reaction is first observed during continuous heating. Because of this discrepancy, tempering is sometimes performed above the true critical temperature and in these cases austenite forms during tempering. The lowest temperature at which austenite forms and the kinetics of the reaction have been studied by Bain,' Bleakney and Gros-venor,2 and Dube and Cunningham. This austenite can affect the properties either as austenite per se, if it is retained at room temperature, or as a decomposition product if it transforms. The effect of austenite formation during tempering on low temperature impact properties of an 8 1/2 pct nickel steel was reported by Brophy and Miller4 in work published after the present investigation was initiated. They concluded that the improvement in low-temperature notch toughness which followed tempering at certain temperatures could be attributed to the austenite formed during tempering. Kramer et al.5 found anomalous hardness increases and embrittlement after tempering of a low-carbon manganese-nickel steel. They concluded that austenite formed during tempering, and that the decomposition products were responsible for the increase in hardness and the embrittlement. Quan-titative correlations of the microconstituents and mechanical properties were not made by these investigators. The present study was undertaken in order to establish the kinetics of formation of austenite at various temperatures, the characteristics of the decomposition of this austenite, and the relationship between mechanical properties and the phases present. Experimental Procedure A low-carbon manganese-nickel steel was selected because of the sluggishness of its austenite decom-position reactions. The composition of this steel in percent was: C, 0.10; Mn, 3.52; Ni, 2.34; Mo, 0.52; Cr, 0.17; Si, 0.19; V, 0.15; P, 0.019; and S, 0.020. Samples were prepared by forging sections from a large ingot to 3/4 in. bars. Formation and decomposition of austenite were investigated by dilatometric techniques which were checked by X-ray measurements. Dilatometer specimens were hollow cylinders 1 in. long, 1/2 in. diam, with a 1/8 in. central hole. All specimens were aus-tenitized for 1 hr at 1650°F and quenched in water prior to insertion in the dilatometer. Oxidation was prevented by using an inert atmosphere of purified nitrogen. Dilation was measured with a dial gauge which could be read by interpolation to 0.00005 in. Temperature was maintained within ± 3°F by a Brown Electronik Controller. Chromel-alumel thermocouple leads were welded to opposite ends of the specimen with the specimen serving as the hot junction. As a check on temperature uniformity comparison was made of the specimen temperature as measured with the chromel-alumel leads and the temperature of the center of the specimen as measured with a calibrated platinum—platinum-rhodium thermocouple embedded in asbestos in the central hole of the specimen. During heating a 5°F temperature difference was noted below 1000°F, but none above, while in cooling, a 5°F difference was observed from 1300" to 735°F, but none below. Heating rates of 35°F per min and cooling rates of 60°F per min were employed for all dilatometric studies. For transformation studies below room temperature, the dilatometer was allowed to cool to 150°F and then was quenched into liquid nitrogen.

Jan 1, 1951

By L. H. Harrison

In coal mines equipped with electrically driven mechanical mining equipment, the problem of protection for electrical circuits and machinery important, because the hazards of fires and explosions resulting from electrical failures is greater than in most other industries. There is need for better methods and improved protective devices for this service. Studies and tests designed to determine possible value of the short-circuiting contactor as an electrical device for coal mine service were investigated. Preliminary made to determine the operating characteristics of the device, after which tests were made under actual service in three coal mines. Ordinarily, electrical protection in coal mines is divided into three classes, as follows: 1. Overload protection that is intended to protect against damage from overheating and excessive mechanical strain due to overloading. 2. Short-circuit protection that provides a means of de-energizing the equipment instantly when an accidental short circuit occurs in the equipment or on the power system. Short cm protection tends to damage from fires and, explosions resulting in the dissipation of large amounts of electrical energy in a short circuit. 3. Ground fault protection that, in its various forms, is intended, to maintain the frames of electrical equipment at or near the same potential surfaces in contact with the earth for the purpose of safe-guarding human life.

Jan 1, 1951

By E. J. Burrough

Coal Reserves The Crowsnest Pass coal fields form part of a greater area which comprises the Inner Foothills belt of the Alberta coal fields and the southeastern coal fields of British Columbia. The most valuable and most extensive reserves of the bituminous coals of Canada are concentrated in this?area, of which the Crowsnest Pass fields form an important part. The extent of these coal reserves together with those of the rest of Canada were recently studied by the Geological Survey of Canada for the Royal Commission on Coal of 1946 (1). Quotin from the report, it is of interest to note that, prior to this work, the most widely known, and in fact the only Canadian-wide estimates of, coal reserves of Canada available to the Commission were those prepared by Dr. Dowling in 1913 (2). At that time it was estimated that Canada's reserves of coal were over twelve hundred billion tons. The more recent estimates of mineable coal for the whole of Canada are of the order of 10 per cent of that figure and are reported. as 99 billion tons, which is further reduced to 40 billion tons on the basis of the estimation of recoverable coal. This considerable divergence in estimated reserves is explained in part by the big difference in the bases of measurements. For example, in the original report, seams of one foot occurring at a depth of 4,000 feet were included in the estimates.

Jan 1, 1951

By H. Rush Spedden, Arvid Thunaes

R. R. Knobler and F. E. Albertson—Following the testwork done by Thunaes and Spedden, a Sullivan deck plant was built for the Colquiri mill. This plant started to operate in April 1945 and continues in successful operation. Since May 1950 the Colquiri mill has operated with a completely revamped flowsheet at a rate of 1000 tons per day. The old Sullivan deck section was retained with this new flowsheet. The "slime plant" in Colquiri consists of one 12-cell Denver No. 18-Sp. Sub-A flotation machine, one 16-ft and one 12-ft hydroseparator, six five-deck Sullivan-frames and six shaking tables for cleaning up the Sullivan deck concentrates, as well as 12 Deister plus three Plat-O tables on which the fine sands, which are not treated on the S-decks, are concentrated. Only —325-mesh fines are treated on the Sullivan decks. The combined hydroseparator overflows are fed to the S-decks. From 1946 to 1949, i.e. with the "old" flowsheet and an average mill feed of 800 tons per day an average of 45 tons per day was treated on four Sullivan rougher frames. The two additional frames were used as cleaners. At times, up to 90 and 120 tons of slimes were treated successfully on this Sullivan deck installation. The average operating data for the S-deck section in Colquiri for the year 1949 were as follows: The tests reported in this paper indicated a tin recovery of 42 pct. The actual plant results for 1949 show a 54 pct tin recovery from the Sullivan decks. The total average quantity of tin produced from the S-deck section in 1949 was 15 tons of tin per month. This corresponds to 3 pct of the total mill recovery. The difference between the 6 pct overall recovery-increase expected after the tests in 1943 and the actual plant results given for 1949 is explained as follows. According to the tests, a total of 170 tons was expected to be routed to the Sullivan decks, but because of certain changes in the flowsheet and mill amplifications,

Jan 1, 1951

By O. C. Ralston, F. Fraas

VIRTUALLY all commercial use of electrostatic separation has employed separators depending on differences of conductance of the broken, solid mixtures treated by them. The two main types of conductance separators have been: (1) Those in which the separating field is as near a static field between two charged electrodes as it is possible to maintain in the face of the usual leakage that takes place between electrodes with some 5 to 50 kv tension between them and spacing of 1/2 to 3 in.; (2) those in which a convective discharge of corona or spray type, but not a spark discharge, takes place between the carrier electrode and a charged electrode facing it, which is of very restricted area, such as a row of needle points or a small diameter wire parallel to the face of the carrier electrode. The present paper deals with this latter type. The principle is usable in separators where the carrier electrode, usually grounded, has the shape of a roller, a conveyor belt, a vibrating table, a sloping chute, or a nearly vertical plate. The innovation studied by us has been the use of the convective field for charging material on the carrier electrode and succeeded by a field between the carrier electrode and an electrode made of a true dielectric which cannot take on a charge by conduction but is charged by being in the radius of the corona discharge. The acquired charge is of the same sign as that of the corona but is not dischargable by contact with a good conductor. However, high-tension charge tends to leak off because of the ionization of the ambient air. The field between this electrode and the carrier electrode is as near static as it is possible to obtain. There are some differences in behavior of this electrode and that of the gas tube electrode used by Sutton, as will be discussed below. Both electrodes cause increased adhesion of nonconductive particles to the carrier roll. The particles are pinned there because they are convectively charged on their outer surfaces facing the corona electrode. The electrodes also cause increased rate of release of conductive particles tending to be pinned by corona charging but conveying the charge to the grounded carrier roll almost as rapidly as it is received by the particles. The sign of the potential on the corona-emitting electrode makes little difference in the separation. An electrode usually emits negative corona somewhat more easily than it emits positive corona, as electrons are then the fundamental particles emitted. With a positive electrode the flow of electrons involved in positive corona discharge is onto the electrode from the ambient gas. Theory In the separator illustrated in fig. 1, the nonioniz-ing electrode is a rotating, nonconductive dielectric cylinder designated as B. The ions emitted by the corona electrode, or wire F, charge both the particles on the carrier electrode, or roll A, and the surface of the dielectric electrode B. Whereas the space between roll A and wire F contains ions, the space between electrode B and roll A is a pure static field free of ions. The dielectric electrode has been described by Bullock.1 However, the corona electrode, which Bullock uses for the purpose of charging only the dielectric electrode, is adapted here to also charge the particles on the carrier roll. In operation the ionic field from the corona electrode is balanced with the static field from the dielectric electrode. The ionic field charges the particle so that it adheres to the roll. The static field intensifies the discharge of the corona charge by interfacial conduction and permits the release of the particle. The ionic and static fields therefore have opposing effects.2 The values of both fields are adjusted so that the poor conductor will adhere and the good conductor will be released.

Jan 1, 1951

THE solid nonmetallic inclusions present to some extent in all commercial steels have been variously designated. In early references they were usually called slag inclusions, and this terminology is still retained to some extent. On the premise that all nonmetallic matter produced in a metallurgical process is slag, this can be justified. We have come to think of slag, how- ever, in a more restricted sense, and calling these particles slag inclusions is further objectionable because it fosters the erroneous concept that they are actually incorporated portions of furnace slag. Rarely is this true. The term sonims (coined from solid nonmetallic impurities) was proposed many years ago but never came into common use. In general, the term non- metallic inclusions seems to be satisfactory and adequate. NATURE AND CONSTITUTION OF NONMETALLIC INCLUSIONS From the standpoint of origin, inclusions fall naturally into two classes: (1) those occurring as a result of reactions taking place in the body of molten or solidifying metal and (2) those resulting from mechanical incorporation of refractories or other materials with which molten steel comes in contact. The former are by far the more numerous and have been called indigenous, natural, or native inclusions. The latter are by their very nature sporadic in occurrence and have been called exogenous, accidental, adventitious, or foreign inclusions. They are often referred to as the "slag-stringer" type, though here also the material is not likely to be furnace slag. Substances Found in Inclusions. Nonmetallic inclusions are composed principally of oxides and sulfides but carbides and nitrides sometimes play an important role. In the case of indigenous inclusions the reactions by which these particles are precipitated from molten or solidifying steel may be caused by: (1) oxidation such as may occur during refining or during tapping and teeming, (2) deoxidation by added alloys, (3) change

Jan 1, 1951

By D. C. Hilty, W. Crafts

The solubility of oxygen in iron containing aluminum has been determined at 1550°, 1600°, and 1650°C and found to be much higher than predicted from theoretical considerations, possibly due to equilibria with an iron-aluminum spinel phase rather than pure AI,O.. The presence of manganese greatly increased the deoxidizing power of aluminum. DEOXIDATION and inclusion formation in steel have proved to be elusive phenomena that are difficult to control in spite of much effort to understand and evaluate the reactions. Study of the problem indicated that more accurate data on the solubility of oxygen in iron containing deoxidizers were essential to further progress, and an empirical determination of oxygen solubilities has been initiated at the Union Carbide and Carbon Research Laboratories, Inc. The investigation has included the effects of aluminum, silicon, manganese, and combinations of these elements at 1550°, 1600°, and 1650°C. The equipment and experimental procedure as well as the results of a study of the effects of aluminum are described below. In general, it was found that the solubility of oxygen in iron containing aluminum is much higher than predicted, possibly because of the formation of complex nonmetallic phases, and that manganese greatly increases the deoxidizing power of aluminum. The generally accepted deoxidation curves for 1600°C are summarized in fig. 1, from "Basic Open Hearth Steelmaking"'. These curves are assumed to represent the solubility of oxygen in the presence of deoxidizers and should indicate the limits of mis-cibility gaps in the phase diagrams of the systems that control the formation and character of non-metallic inclusions as described by Benedicks and Lofquist'. They were derived mainly by application of the methods of thermodynamics to the available experimental observations, and by calculations based on the thermal constants of the pure substances when experimental data were lacking. Among the more notable researches contributing to the development of knowledge of oxygen solubilities are those of Korber and Oelsen8, 4, C. H. Herty, Jr. and associates5,6, Krings and Schackmann7, Went-rup and Hieber8 Schenck and Briiggeman9, Vacher and Hamilton'" and Chipman and co-authors 1,11,12,13 Practically, the deoxidation curves are of limited value in predicting oxygen content and rationalizing deoxidation practices. The reasons for this inadequacy appear to be error from inaccurate data, oversimplifying assumptions, interacting effects of combined deoxidizers, and possibly unknown extra-equilibrium and side reactions. Although inclusion formation is a very complex reaction it must be re-

Jan 1, 1951

OFFICIAL Washington is gravely concerned over the adverse military situation caused by the all-out intervention of the Chinese Communists in Korea. What the policies of the United Nations and the United States will be in the new crisis is unknown. However, Stuart Symington, chairman of the NSRB, set the general pattern for mobilization in the near future when he said that this country would move from a "light gray to a dark gray mobilization." The implications of accelerated mobilization for the mining industry are particularly apparent with respect to the manpower situation. Revised policies recently initiated for the recall of reservists may be abrogated, in which case key personnel in the mining industry may face calls to active duty with insufficient consideration given to their indispensability to national defense in their present positions.

Jan 1, 1951

Copper entering a lead ,smelter in concentrate or from other sources is recoVered as matte and speiss which contain appreciable quantities of lead. The matte and speiss are usually sold to copper smelters to recover the copper content and also any gold and silver in these products, but the value of the lead is largely lost. Some copper plants pay for portion of the lead content, but regarded as a means of recovering lead it is more costly and less efficient than if the lead were recovered at the lead smelter.Because of the value of this lead loss, the metallurgy of copper recovery has assumed greater importance in recent years owing to the rise on the price of lead.Two processes are in use today to produce matte and speiss, namely the iron matte process and the soda matte process developed by the American Smelting and Refining Co. 1 in D.S.A. The latter process is characterised by a higher copper to lead ratio than the older iron matting process.The following analyses are typical of matte and speiss produced at Broken Hill Associated Smelters, by both processes, although the soda matte process is still in a developmental stage and experience indicates that matte and speiss of lower lead tenor can be produced under favourable conditions.

Jan 1, 1951

OF the many categories into which scientific knowledge has been arbitrarily divided, the one that has proved most applicable in our attempts to gain an insight into the details of steelmaking processes is physical chemistry. To the young metallurgist who has only recently survived a college course in this subject, the application of its principles to reactions in liquid steel should not be difficult. The many excellent textbooks of physical chemistry1 provide ample material on the principles of this subject for the student of steelmaking processes; yet with- out exception those texts draw the greater part of their illustrative material from room-temperature data. It is the purpose of this chapter to provide a concise review of the principles of physical chemistry that have proved useful in studies of steelmaking and at the same time to present some of the data that are essential to the application of physical chemistry to reactions at high temperatures. Certain parts of physical chemistry require rather formidable mathematics for their complete development but in the main those applications in which we are here interested can be ex- pressed in fairly simple terms. Many of the equations are logarithmic, and we shall use the symbols In X and log X to represent respectively the natural and the common logarithm of X. The two are related by In X = 2.303 log X. Logarithms may be read from a good slide rule with sufficient accuracy for our purposes. In a few spots a knowledge of the calculus will be, helpfu1. MATTER Innumerable forms of matter may be recognized, and these may be converted by chemical processes into others, as ore, coke, and air are converted into iron, slag, and gas. Whenever such a change occurs there is a corresponding change in

Jan 1, 1951

Jan 1, 1951

New Products Equipment

Jan 1, 1951

By C. G. Dunn, F. W. Daniels, M. J. Bolton

IN recent papers on interface energies in metals¹,² the concept of an equilibrium of forces has been used in the measurement of interfacial tensions. Mathematically the equilibrium of three forces is given by the relations: where the 2's are the interfacial tensions (interface energies per unit area of interface) of three phases or grains meeting at angles 21 22 and 23 (212 relates to the 1-2 boundary formed by grains 1 and 2;223 to the 2-3 boundary, etc.). If these relationships are valid, one can calculate relative values of the interface energies from measured boundary angles on specimens which have been brought to equilibrium. Since Eq 1 may be derived through a mathematical process of minimizing the grain boundary energy under the restriction that the ?'s be independent of boundary orientation: the concepts of surface tensions and equilibrium of forces are not particularly essential. To deal with the general case involving dependence of boundary energy on boundary orientation, it becomes desirable to drop certain concepts formerly held (namely that energy per unit area is identical with force per unit length or surface tension) and to use the energy concept alone. It is appropriate, therefore, to use E in place of ? in deriving and using the more general equations that express the anisotropic nature of the grain boundary energy. Herring3# ' recently has derived the required general equations using the principle of minimization of energy. Specifying the boundary orientations in terms of angles (4) measured with reference to crystal axes within the grains, Herring's equations take the form E23 + E21 cos?8 + E12 cos?2 — sin ?12 + sin?2-?E12/?12 =O [2] where the partial derivatives are measured in the direction of counterclockwise rotation of the boundaries. Eq 2 implies that an infinitesimal displacement of the triple point along the 2-3 boundary produces no change in the boundary energy. Similar equations apply for infinitesimal displacements along each of the other two boundaries. From such equations Herring obtains the following general relationship (1 + E1 E2) sin?8 + (E2 — E1) cos?3 ________ E38______________ = (1+ E2 E8) sin ?1+ (E3— E2) cos ?1 __________^5____________[3] (1 + E sin ?2, + (E1 — E8,) COS ?2 1 E28 where E1 = 1/E23- E25 and PC and c8 have similar expressions. It is apparent that Eq 3 reduces to Eq 1 when the c's vanish. Eq 3 also reduces to Eq 1 when the E'S are all equal. Shockley and Read' have pointed out one limitation to these equations. When E plotted versus 4 appears as an energy cusp, as their theory requires, for example, for the energy near a twin boundary position, then Eq 3 (and therefore Eq 1 also) no longer applies if one boundary is in the minimum energy position. One of the equations of form Eq 2, however, applies if the infinitesimal displacement is along the boundary associated with the energy cusp. From the foregoing treatment it will be apparent that equilibrium angles alone are not sufficient in general for calculating relative interface energies.

Jan 1, 1951

By M. G. Driessen, H. E. Criner

THE cyclone thickener has two important applications in wet washing plants: (1) water clarification, and (2) fine coal recovery. The thickener consists of a conical chamber into which the fluid is injected through a tangential nozzle at the periphery of the large end. The solids of the slurry are concentrated and removed from the apex of the cone while the "thinner" portion is discharged from a central tube in a flat head at the large end, fig. 1. The advantages of the cyclone thickener are that large volumes of slurry may be treated with small space requirements and that the underflow concentration may be controlled easily and readily to meet varying feed conditions. Control of Washery Water Solids Concentration: The first requirement, in the process of controlling solids concentration, is that the solids be removed from the body of circulating water at the rate at which they are introduced. If this condition is satisfied the concentration will remain at a fixed value and will not increase to uncontrollable levels. The second requirement is that the solids concentration

Jan 1, 1951

By J. J. Casey, R. S. Busk, D. L. Leman

The mechanical properties and the phase-temperature relationships of magnesium-lithium-aluminum, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys are presented. It is shown that the strengths of some of these alloys can be tripled by heat treating and aging but that the high strength is accompanied by brittleness and lack of stability. MAGNESIUM-LITHIUM alloys are interesting because the hexagonal structure of magnesium can be changed into the more ductile and workable body-centered cubic structure by the addition of only 10 pct lithium.1 After Loonam2 determined that the ductility of the magnesium-lithium alloys is destroyed by even trace quantities of sodium, it was possible to prepare ductile alioys and study their mechanical properties. Jackson3 and coworkers have ably described their results with both the binary and polynary magnesium-lithium alloys. The present paper is a report of the mechanical properties of wrought magnesium-lithium-aluminurn, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys. Experimental Procedure The alloys were made by melting 7 lb of magnesium in a steel crucible under a molten flux of 75 pct LiCl + 25 pct LiF3 previously dried at 1600°F. The metal was heated to 1300°F for alloying aluminum and zinc and then cooled to 1250°F for adding lithium (sodium content: 0.01 to 0.04 pct). After the lithium had been alloyed, dry LiF powder was sprinkled on the melt to thicken the excess flux. After a 15 min holding period, the flux was skimmed off. Paraffin vapors were used to protect the metal as it was poured into 3 in. diam by 11 in. long magnesium molds. Billets were extruded into 3/8-in. diam rod and 1/16 x 3/4-in. strip; sheet was prepared from 1/8x 7/8-in. extruded strip, first by hot rolling and then by cold rolling 2 pct per pass. Hot rollability, or the temperature range through which the alloys could be rolled, was determined by rolling the strip two passes at 30 pct reduction per pass. Cold rollability, or the percentage of cold reduction to cause detrimental cracking, was determined on 0.064-in. hot-rolled sheet. Standard ASTM procedures were followed to obtain the mechanical properties, using 0.2 pct offset for the yield strengths. The level of properties produced with commercial magnesium alloys using the procedure described is given in a previous publication." Results Magnesium - Lithium - Aluminum System: The good workability of magnesium-lithium alloys is illustrated by the data in table I, which shows approximately how the extrusion pressure decreases as the amount of cubic phase increases. Binary magnesium-lithium alloys are soft and weak, but aluminum raises their strengths con-

Jan 1, 1951

By J. E. Hawley

Abstract Spectrographic methods for the analysis of minor constituents such as platinum-group metals, gold, silver, and silica in palladium and platinum refinery sponge are described. These involve the conversion of the sponge metals to the black form by reduction with high purity aluminum filings in either acid or alkaline media. Standards of known composition are prepared in the same manner from either refinery or spectrographically standardized sponge metals. Samples of the black metals are mounted in pellet form and a multisource spark discharge used for excitation. The range of concentrations of impurities studied are those common to refinery samples. Excellent reproducibility of intensity ratios using major constituents as internal standards, is demonstrated and two methods have noted by which the accuracy of the procedures are shown to be of the order of 3 per cent, on the basis of synthetic preparations. Introduction During the past two years an investigation has been carried out in the Spectrographic Laboratory, Queen's University, to determine the suitability of modern spectrographic techniques for the precise analysis of the platinum-group metals palladium, platinum, rhodium, iridium, and ruthenium in the form of refinery sponge analyzing about 99 per cent of the major constituent.

Jan 1, 1951

By F. P. Bobrowski, G. B. Spencer, Alton B. Cook

In estimating production gas/oil ratios and oil recoveries from reservoirs containing highly volatile oils it is highly important to include condensate that may be recovered from the gas produced from the reservoir. The volume of the hydrocarbon liquid condensed from the production of the solution gas that has been liberated. in some reservoirs may equal or even exceed the volume of recoverable stock-tank oil as estimated by present methods. The usual procedure1, 2, 3 in estimating future reservoir performance includes use of relative permeability data of the reservoir rock to gas and oil and includes material-balance calculations utilizing data on the volume of the reservoir fluids, oil and gas production and reservoir pressure decline, and data on the physical properties of the initial reservoir fluids. The inaccuracy in the procedure results from the false assumption that all of the free or liberated gas that enters the well bore of reservoirs containing highly volatile oils remains in the gaseous phase as it is produced. This paper presents a method for estimating future reservoir performance and oil recoveries based on special labora. tory analyses of reservoir-oil samples and recognition of the additional volume of hydrocarbon liquid that will be recovered at various stages of depletion from a solution.gas.drive reservoir. The method also includes calculations of the volume and composition of the hydrocarbon liquids that can be recovered by processing the produced gas in a natural-gasoline plant. The development of the method resulted from a study of laboratory analyses of reservoir samples and of field data obtained from two reservoirs containing oil of the highly velatile type. Relatively high pressures and temperatures prevail in oil reservoirs discovered at the greater depths of present-day drilling. The contained fluids may have high saturation -Dressures and large volumes of gas in solution. The oils and gases under these conditions may be almost identical in compositions and densities.4,5 Also, engineers have noted that, for a number of oil reservoirs and especially the deeper reservoirs, the API gravity of the stock-tank oil increaees as the production gas/oil ratios increase. They attributed this increase in API gravity of the stock-tank oil to the formation of condensate as the liberated gas in the reservoir is being produced. SOURCE OF DATA FOR CALCULATIONS Subsurface oil samples and well-test data were obtained from the E. Constantin-Lambert Well No. 1 in the Elk City Field, Okla., to demonstrate the need for and a method of calculating future reservoir performance when consideration is given to the recoverable hydrocarbon liquid from the production of solution gas that has been or will be liberated in a reservoir. The Lambert well is located in C, SW 1/4, SW 1/4, Set- 18, T-l0-N, R-20-W, Washita County, Okla. At the time of completion it was on the east edge of the development and Was producing from conglomerate through 30 perforations in the 5 1/2-in. casing at a depth of 9,859 to 9,864 ft. The well Was completed on July 9, 1949, and subsurface oil samples were obtained July 29 and August 1, 1949. Production gas/oil ratio data were obtained during the operation in series of two Separators at high and low-pressures of 314 and 44 psia, respectively, and at an average temperature of approximately 60°F. The flowing bottom-hole pressure at the time of sampling was 3,934 psis. The static bottom-hole pressure was not obtained at the time of sampling, as the well could not be shut in long enough for testing because gas produced from the well was used for fuel at an offset drilling well. However, the initial reservoir pressure was calculated to be 4,364 psia from knowledge of pressure gradients in other wells in the field and the depth of the casing perforations in the Lambert NO. 1 well.

Jan 1, 1951

OPEN-HEARTH refractories are not merely an accessory to the furnace. They are the furnace, to all intents and purposes. The steel work of the main structure is merely an open frame which helps to support the refractories; and the regenerators, a necessary part of the furnace system, consist almost entirely of refractories. Not only do refractories constitute the essential part of the furnace, but they also carry the liquid steel all the way 'to the point where it begins to solidify. On leaving the furnace the liquid passes through a refractory runner into a refractory-lined ladle, then through a refractory nozzle closed by a refractory stopper on the end of a rod protected by refractory sleeve bricks. The liquid is sometimes sent through an additional refractory- lined tundish, a supplementary ladle, or a refractory runner for bottom pouring, until it finally enters the iron mold in which it solidifies. Even in the mold, refractory materials are sometimes used to provide a nonconducting "hot top." This series, from runner and ladle to hot top, inclusive, is often referred to collectively as the "pouring-pit refractories." REFRACTORY RAW MATERIALS The raw materials available are best classified into basic and acid types. The principal basic raw materials are magnesite, dolomite, and chrome ore. The principal acid materials are silica in various natural forms, and fireclay. Magnesite. Austria was the principal source of magnesite (MgC03) until recent years, when the Province of Quebec, in Canada, and the states of Nevada and Washington became important sources for the American steel industry. More recently these natural sources have been supplemented by the so-called "sea-water magnesite"-which is the name somewhat incorrectly given to magnesium hydroxide obtained as one of the products

Jan 1, 1951