Search Documents

By V. A. Nieberlein

This paper presents the results of research undertaken to recover titanium and columbium by low-temperature chlorination of low-grade columbium-bearing ilmenite concentrates, and to simultaneously remove chlorinated impurities from the volatile chlorides without resort to distillation. Coke-reduced ilmenite was chlorinated at 400° to 500° C., and the resulting TiC14 was free of most impurities before condensation. A heated purification column was used wherein various packing materials reacted chemically or physically with the impurities which passed through them in the vapor phase. A nearly water-white TiC14 product was obtained directly. The principal impurities in the titanium tetrachloride were: 0.02 percent Fe, 0.01 percent V, 0.05 percent A1, 0.04 percent Si, and 0.07 percent Cb. This is a less pure product than commercial TiC14. Most of the columbium was recovered as crude CbC15, requiring further refining.

Jan 1, 1960

By Charles T. Baroch

RESEARCH strengthened the position of cesium as the preferred material (commonly but erroneously called "fuel") for ionic propulsion engines. Its use as an element of the plasma thermocouple for generating electricity also seemed more likely. Domestic Production.-No domestic ore of cesium and rubidium was produced. San Antonio Chemicals, Inc., San Antonio, Tex., and Maywood Chemical Works, Maywood, N.J., continued to produce cesium and rubidium compounds including carbonate, chromate, hydroxide, nitrate, sulfate, and all four halides. Rocky Mountain Research, Inc., Denver, Colo., began producing various cesium and rubidium salts. American Potash & Chemical Corp., Los Angeles, Calif., offered cesium and rubidium for sale.

Jan 1, 1960

By N. P. Titkov

This paper presents the results of laboratory and pilot plant investigations for the development of efficient methods of beneficiating hematite ores from the Krivoi Rog, Kursk Magnetic Anomoly, Olenogorsk, and other localities. The tests included gravity, magnetic (in a high intensity field), flota¬tion, and magnetizing roasting methods. It was possible to develop efficient beneficiation methods depending on the mineral composition of the ore and degree of dissemination of ore and gangue minerals. The paper shows the relationship between the iron silicate and quartz content of the ore and the technologic indices of the various beneficiation methods. Some of the conclusions based on these investigations and the technical and economic computations related to the cost of one ton of pig iron produced from concentrates obtained by the various beneficiation methods are: 1. If the hematite ore is not disseminated uniformly, it is expedient to use a combined gravity and flotation process. Ore particles up to 50 am. in size are beneficiated by gravity (heavy suspension, jigging, and others) and yield a lump concentrate. The middlings from this process are recrushed and floated; 2. Finely disseminated hematite ores, containing small quantities (less than 5 percent) of iron silicates, are most effectively beneficiated by flotation. Anionic (sulphate soap, tall oil emulsion with various foam depressors) as well as cationic collectors may be used. Depending on the mineral and chemical composition of the ore, it is possible to obtain concentrates containing up to 65 percent iron with an extraction up to 94 percent; 3. Finely disseminated, mixed hematite-magnetite ores may be beneficiated by flotation or a magnetic separation-flotation process; 4. Finely disseminated hematite ores, containing large quantities of iron silicates and earthy hematite ores are most efficiently beneficiated by the magnetizing roasting method. This method will yield concentrates containing up to 68 percent iron with extractions up to 90 percent. Although beneficiation by the magnetizing roasting process is costly, it will nonetheless, when employed on this type of ore, yield the least expensive pig iron.

Jan 1, 1960

By G. L. Coleman, D. S. Hutton, W. C. Leslie

The occurrence of twins in a iron, generated during cooling through the ?-a transformation, is well established,1-8 but this phenomenon has been nearly ignored during the past 20 years. It is the purpose of this note to call attention to the prevalence of such twins and to illustrate their appearance. The work of paxton7 and Kelly8 has demonstrated beyond reasonable doubt that for Neumann bands (mechanical twins) in a iron the twinning plane is (112) and the twinning direction <III>. The agreement with McKeehan&apos;s earlier work4 on transformation twins indicates that both types of twins in ferrite follow the same twinning law. There is little doubt of this conclusion, but it could be strengthened by a microbeam X-ray determination of the orientation relationship between a single ferrite grain and a transformation twin within that grain, as in the technique used by Kelly8 on Neumann bands. RESULTS AND DISCUSSION Transformation twins, identified by their appearance on a polished and etched section, were found in

Jan 1, 1960

By Henry P. Chandler

Tripoli is the general name for a number of fine-grained, lightweight, friable, minutely porous, forms of decomposed siliceous rock, probably derived from siliceous limestones or calcareous cherts. Tripoli is often confused, both in the trade and technical literature, with tripolite, a diatomaceous earth (diatomite), found in Tripoli, North Africa. A material found near Seneca, Mo., resembling tripolite was incorrectly termed "tripoli." This name has persisted and now has a definite physical and trade meaning. However, tripoli contains no diatoms, is of an entirely different origin, and has chemical and physical properties different from those of tripolite. There are two distinct types of tripoli in the United States; that from the Missouri-Oklahoma field and that from the Southern Illinois field. Commercially the term "tripoli" is applied to the material from the Missouri-Oklahoma field, while the material from the Southern Illinois area is often referred to as "amorphous" or "soft" silica. Material similar to the Missouri-Oklahoma tripoli, but finer grained, occurs in northwestern Arkansas. In its Minerals Yearbook the Federal Bureau of Mines groups statistically under "natural silica abrasives," tripoli from these producing areas and rottenstone from Pennsylvania. The justification for this grouping is the similarity of use. Composition and Physical Properties Commercial tripoli contains 97 to 99 pet SiO2. The remainder is mostly alumina, iron, lime, soda, and potash, some of which may impart desirable physical properties to the material. Variations in the chemical composition of tripoli are not as important as its physical characteristics. The color of tripoli varies from white to cream, brown, rose, and red, the variations from white being the result of iron deposited from percolating surface waters. The commercial varieties of tripoli mined in the Missouri-Oklahoma area are designated as cream and rose. Other physical properties of the tripoli from this area are: Free quartz, less than 0.5 pct; oil absorption, 50.71 to 53.14 pct; water absorption of the crude tripoli, about 38 pct, and of prepared material, about 52 pct; fracture, uneven to conchoidal; specific gravity, 2.15 to 2.62; weight per cubic foot crude, 35 lb, ground, 55 lb; fusion point, 3,225° to 3,300°F; and refractive index, 1.54. Tripoli occupies about 1 cu yd to the short ton in place and about 1.5 cu yd when broken. Packed for shipment, the powdered material occupies about 33 cu ft to the ton. Its value and usefulness depend primarily on a low content of crystalline silica, size of the natural particles, absorption, and color. Some beds in the Missouri-Oklahoma area are of sufficiently compact material that large, fairly strong blocks may be removed. These find a market as filter blocks and have been used for building material. In the Southern Illinois field the color of the material is the important physical property; pure white is preferred. The rottenstone mined in Pennsylvania is of higher density and lower in silica content than the various types of tripoli. Its composition approximates 60 pct silica, 18 pct alumina, 9 pct iron oxide, 8 pct alkalies, with small amounts of lime and magnesia. The material apparently is a ferruginous and siliceous shale, having properties rendering it suitable as an abrasive or as a filter for paint, rubber, and plastics.

Jan 1, 1960

By Alla D. Mah

THERMODYNAMIC data for manganese and its inorganic compounds have not been critically surveyed since the work of Maier (31) 3 in 1934. At that time data were lacking or inadequate for many of the important metallurgical compounds. Experimental work, conducted during the intervening years, has supplied so many new thermodynamic values that it is again desirable to examine the available data and compile them into a single publication for handy reference. This paper consists of three main sections. The first summarizes the basic metallurgical thermodynamic data for manganese and its compounds, including heat capacities, entropies, heat contents, temperatures and heats of phase changes, vapor pressures, and heats and free energies of formation. All data available to May 1959 have been considered. The second section contains heats, free energies, equilibrium pressures, and equilibrium constants of reactions of manganese compounds, with special emphasis on metallurgical reactions. The third section supplies basic thermodynamic data for other elements and compounds encountered in metallurgical reactions of manganese, thus making it possible for the reader to conduct thermodynamic calculations without recourse to other literature.

Jan 1, 1960

By Walter W. Fowkes

Leonardite is a coallike substance, similar in structure and composition to lignitic coal and believed to be derived from lignitic coal by the process of natural oxidation. Leonardite is little known outside lignite-producing areas and has been developed commercially only to a minor extent. The higher oxygen content and less compact structure of leonardite, compared with lignite, make it undesirable as a fuel but indicate that it has potential as a source of chemicals and for other nonfuel uses. It is a convenient source of humic acids. The United States has a large natural reserve of leonardite; furthermore, it can be produced in the laboratory under controlled conditions. The significant elemental difference between leonardite and lignite is the oxygen content (leonardite, 28-29 percent; lignite, 19-20 percent). The higher oxygen content of leonardite is due entirely to a Larger number of carboxylic acid groups. This fact explains the 17-Cold increase in alkali solubility of leonardite. Spectral studies indicate that the material is mixed salts of humic acids.

Jan 1, 1960

By Rollien R. Wells

THERE are two recognized methods of recording the state of the metallurgical art. One involves delineation of individual advances reported in the literature. This approach is used effectively in the excellent annual reviews published by some of the leading technical journals and in the technology sections of the individual commodity chapters in this volume. In an effort to more clearly indicate the current trend of metallurgical research and development, the authors of this chapter chose the method of discussing generally selected items of interest brought to their attention during 1959. Since technology cannot be confined by dates on a calendar, most of the items mentioned have been in the process of development for several years. No attempt was made to identify the sources of information used here. Material was drawn from many sources : Nonconfidential correspondence and conversations with authorities of the metallurgical fraternity, papers delivered at technical meetings, and articles noted in the technical press, including particularly Engineering and Mining Journal, Metal Progress, Journal of Metals, Mining Engineering, Industrial and Engineering Chemistry, Chemical Engineering, Chemical and Engineering News, Chemical Week, Materials in Design Engineering, Review of Metal Literature, the Canadian Mining and Metallurgical Bulletin, the Mining Journal (British), and the Journal of the Institute of Metals (British).

Jan 1, 1960

By C. A. Frenzel

Extensive spectroscopic data are needed in making reliable vibrational assignments for use in calculating thermodynamic functions of polyatomic molecules. The fundamental vibrations of organic molecules may be observed at any wavelength from 2.5 to 200 microns (micron = µ = 10-4 centimeters), but most often in the region from 3µ to 50µ. Raman spectra generally cover the range in which fundamental vibrations occur, but equally important infrared spectra usually are not measured at wavelengths longer than 25µ. This limitation results because most infrared spectra are determined for analytical purposes, which seldom require information outside the region 2µ to 25µ. Measurements of infrared spectra in the range 15µ to 35µ recently were begun by the Bureau of Mines to obtain data needed in making vibrational assignments. This report presents the spectra of the following thirteen compounds: Tetrahydrofuran, 1-methylpyrrole, piperidine, 2-methylpyridine, 3-miuthylpyridine, 2-propanethiol, cyclopentanethiol, 2-methyl-2-butanethiol, 3,3-dimethyl-2-thiabutane, cyclohexanethiol, cyclopentyl-l-thiaethane, 2,4-dimethyl-3-thiapentane, and hexamethyldisiloxane.

Jan 1, 1960

By R. M. N. Pelloux

This study of aluminum-copper alloys had two aims: 1) To determine the effect of the amount and distribution of a second phase, CuAl2, on the creep-rupture strength, ductility, and fracture characteristics of the alloys. The work of Gemmell and grant&apos; on single-phase aluminum-copper alloys provided a basis for the present study. 2) To attempt to provide a relation between the microstructure and strength of two-phase alloys deformed at comparatively high temperatures (greater than 0.45 T,). The creep behavior of the two-phase magnesium alloys Mg;Ce and Mg-A1, has been treated by Roberts. 9 In work reported by Sully and Hardy4 and by Underwood, Marsh, and Manning~ on A1-Cu two-phase alloys, and also in a portion of the work of Gemmell and grant,&apos; aging took place during the creep tests. &apos;In the present work, overaged aluminum-copper alloys were subjected to creep deformation at two temperatures, 500 and 700OF. The overaging treatments to produce the precipitate dispersions were performed prior to the test, at temperatures which were the same as the ultimate respective test temperatures. Hence, the present study is concerned with the creep behavior of stable (in contrast to "underaged") two-phase A1-Cu alloys, i.e., alloys in which no depletion of the solid-solution matrix occurred during: creep. MATERIALS AND PROCEDURE A 2 and a 3 pct Cu alloy, supplied by Alcoa, were studied; Table I shows the compositions. The grain size of the specimens, 0.9 to 1.0 mm, was achieved by annealing the machined test bars for 2 hr at 1000°F, followed by furnace-cooling to 900°F, and homogenizing for 4 hr. Both compositions are in the single-phase condition at 900°F. Two types of overaged dispersions, termed "over-aged I" and "overaged 11" were prepared after the grain size and the homogenization anneals. The overaged I alloys were prepared by quenching to room temperature after homogenization, aging at either 500&apos; or 700°F for 72 hr, and air-cooling to room temperature. The overaged I1 alloys were prepared by furnace-cooling after homogenization, to either 500&apos; or 700°F, and holding at the necessary temperature for 72 hr. The times for furnace-cooling from 900°F to 700° and 500°F were, respectively, about 2 and 3.5 hr. The structures of the A1-2 pct Cu alloys are shown in Fig. 1 (overaged I) and in Fig. 2 (overaged 11). A comparison of Figs. 1 and 2 shows that in the overaged I alloys the precipitate particles along the grain boundaries are much more closely spaced and the grain boundaries are straighter than they are in the overaged I1 alloys. Further, the particle size and spacing in the grains are smaller than in the overaged I1 alloys. Microstructures of the A1-3 pct Cu alloys have not been shown; the structures of these alloys differed from those of the A1-2 pct Cu alloys only in that the distribution density of the particles was greater. The creep specimens had a gage section 1 in. long with a diameter of 0.155 to 0.195 in. Before testing, specimens were electropolished in a solution of 100 cc glacial acetic acid, and 30 cc of 60 pct perchloric acid, at 40&apos; to 50°F, at 24 v. The specimens were kept refrigerated prior to testing to avoid precipitation at room temperature. Constant stress creep tests were conducted; the load was applied 75 min after heating of the specimens to test temperature had begun. EXPERIMENTAL RESULTS Creep-Rupture—Fig. 3 shows the log stress-log rupture life plotfor the overaged alloys studied, and also for the underaged A1-2 pct Cu alloy.&apos; At 700°F, the stress-rupture life relationship is nearly independent of both the amount of precipitate (i.e., composition) and of the type of overaging treatment (i.e., precipitate dispersion). At 500°F it is apparent that the increase in rupture life that was ex-

Jan 1, 1960

By R. J. Block, G. H. Kehl

IN order to investigate the possibility of a spontaneous low-temperature transformation, resistivity measurements were made on a sample of eutectoid beryllium- copper. A cast specimen of 5.965 pct Be, 94.035 pct Cu was homogenized at 650°C for 22 hr, furnace cooled to 550°C, and held for 2 hr to allow the 0 - a ß-a+? reaction to proceed. In an attempt to refine the ß grain size, the specimen was then reheated to 620°C, held

Jan 1, 1960

By E. L. Litchfield

This report of work by the Federal Bureau of Mines has two primary objectives: A survey of the present status and usefulness of the minimum ignition-energy concept, and the presentation of recent data that are believed to bear on the safety problem associated with the ignition of combustible gases by electric discharges. The minimum ignition-energy concept has widespread applicability, especially to safety. The primary obstacle in making theoretical calculations of the requisite ignition energy is the lack of data on chemical kinetics and flame hydrodynamics. The new data on electrical ignition are representative of the great increase in knowledge that can be achieved by proper utilization of geometrical and electrical characteristics associated with the ignition source. CONCEPT OF MINIMUM IGNITION ENERGY The basic concept of a minimum ignition energy (the minimum amount of energy required to cause ignition) follows quite naturally from general physical principles and from the stability (lack of chemical reaction) of the gaseous mixture under the initial conditions. It also follows that if, as a first condition, lossless, instantaneous, and spatially localized energy can be injected and, as a second condition, the relaxation time for conversion of this type of energy to the type required for the reaction is short compared to some characteristic time scale of the ignition phenomenon, the energy requirements will be essentially independent of the type of energy source. Even if condition one cannot be fulfilled, it is sometimes possible to estimate the energy content of the gas required for ignition, and under these circumstances, condition one is fulfilled in effect. There are several instances where results can be interpreted for circumstances that effectively satisfy conditions one and two; these will be discussed later.

Jan 1, 1960

By T. E. Gray

This report describes preparation characteristics of the significant coalbeds in Marion County, W. Va., as determined by the Bureau of Mines. It is one in a series telling what coals are suitable for producing metallurgical coke, either as mined or after beneficiation. Over 9.4 million tons of coal was produced in Marion County, W. Va., in 1958, of which almost 6 million tons was cleaned mechanically in nine cleaning plants. All of the coal mechanically cleaned came from the Pittsburgh bed. The Bureau of Mines estimated that 1,578 million tons of recoverable coal remained in the county in beds 28 inches or more thick as of January 1, 1955.

Jan 1, 1960

By D. Geiselman, A. G. Guy

Single cvystals were grown from high-purity magnesium containing known amounts of nitvogen in the range 0.0008 to 0.0048 wt pet. Crystals of known ovientation were tested in tension in an Instron ma chine to determine the yield strength and to obsevue wheather a yield point occurred. Slowly cooled crystals or those given a solution heat treatment did not show a yield point. However, crystals that were aged following a solution treatment showed a yield point for all of the nitrogen contents studied. It was concluded that nitrogen caused the yield point by the Cottrell mechanism. NITROGEN has been shown to produce sharp yield points in single crystals of cadmium, zinc,2&apos;3 ß-brass,4 and iron,5,6 as well as in polycrystalline iron7 and molybdenum.8,9 Since magnesium has a structure similar to zinc and cadmium, it seemed reasonable that magnesium should also exhibit a sharp yield point provided it contained sufficient nitrogen. Bobalek and Shrader10 reported a total nitrogen content of 0.002 to 0.0065 wt pct in com- mercial magnesium alloys, an amount well in excess of that required by theory. However. magnesium differs from cadmium and zinc in that it forms a stable nitride, Mg3N2, which has a standard free energy of formation of -95,480 cal per mole at 25" c." If rather than being in solid solution, the nitrogen were predominantly combined as the nitride, it could not act to produce a yield point. This type of behavior is the basis for the elimination of strain aging and a yield point in steel by the addition of strong nitride formers such as titanium,12 columbium,13 aluminum,14 vanadium,15 and boron.16,17 Thus, there appeared to be factors both favorable and unfavorable to the production by nitrogen of a sharp yield point in magnesium, and the purpose of this investigation was to determine the actual behavior of magnesium crystals containing known amounts of nitrogen.

Jan 1, 1960

By Jack D. Ramsdell

The objective of this investigation was to make a preliminary evaluation of titanium-vanadium-zirconium, alloys using room-temperature tensile properties as criteria for selecting promising alloys for future critical studies. Arc-melted titanium-vanadium-zirconium alloys ranging in composition from 5 to 20 a/o (atomic-percent) vanadium and 5 to 30 a/o zirconium, were investigated to evaluate hardness, hot workability, and room-temperature tensile properties. Metallographic examination coupled with hardness measurements were used to follow structural changes and aging response. Room-temperature tensile properties were criteria for evaluating mechanical and engineering properties of the alloys.

Jan 1, 1960

By J. D. Ramsdell

To obtain information on the effects of cobalt on microstructure and tensile properties of titanium-vanadium-cobalt alloys, the composition ranges of 4 to 16 percent vanadium with 1 to 4 percent cobalt have been studied. The beta phase was not completely retained with vanadium additions up to 16 weight-percent or in the same alloys containing up to 4 percent cobalt.

Jan 1, 1960

By H. Hu

Observations were made on the recrystallization of a 70 pct cdd-rolled silicon-iron crystal with an initial orientation of (113) [332]. Its polygonization and recrystallization characteristics were studied. Results indicated that re crystallization tendency of the deformed crystal is much weakened by the polygonization of the matrix. Complete recrystallization in such specimens is achieved by the growth of recrystallized grains of sufficient size and of the right orientations in relation to the matrix. Evidence was also furnished which suggests that the difference in the re-crystallization tendency is a result of the difference in the severity of lattice bending rather than the difference in orientation of the deformation texture. DUNN and Koh1,2 have made an extensive study on the rolling and annealing textures in silicon-iron crystals. Their results indicated that the recrystallization tendency can be widely different in crystals with different orientations. A particularly interesting example of their results was a crystal with an initial orientation of (113) [332], which developed a deformation texture of (001) [110] after 70 pct cold-rolling. Recrystallization in this crystal took long time anneals at high temperatures. Other crystals having different orientations recrystallized very rapidly. Wiener and corcoran3 have observed the retention of the (100) [011] deformation texture in a low-temperature annealed specimen of a commercial silicon-iron alloy, corresponding to areas of light-etching low-angle boundaries in the annealed struc-

Jan 1, 1960

By J. D. Kalasky

Continuous mining has revolutionized the coal industry but intensified the problems of earlier mechanization. From the installation of the first miner, it was recognized that face ventilation would be one of these problems. To establish an efficient work cycle for the equipment being used, conventional mechanized mining provides four or more development faces. Continuous mining, relying on a single machine, requires only one face, although more than one can be driven alternately by the same machine. In gaseous areas mined by the older methods, the intermittent rate of exposure allows time for the face to bleed off or be cleared, and the width obtained with conventional units makes it possible to hang a brattice line almost to the face. Continuous mining increases the ventilation hazards; there is no margin of time, and very limited space. For all practical purposes, continuous miners available today can be grouped into two major types, rippers and borers. The two can be further classified, respectively, as flexible and rigid. Both types have been in operation in U. S. coal mines for the past five to ten years in a number of seams, under various conditions ranging from slightly gaseous to very gaseous. Common methods of face ventilation utilizing jute or plastic brattice material for line curtains, stoppings, and checks have so far met with success. Air volumes to operating sections are greater than for conventional mining, and specific instructions have been given to section crews stressing the precautions needed in dealing with a steady rate of gas emission and the importance of maintaining reasonably air-tight brattice to direct a good steady flow toward the face at all times. Operators of continuous miners, as well as the foreman on each section, are equipped with an approved safety lamp for gas testing. When the miner is in steady operation, tests for gas at the face are made at 15 to 30-min intervals, depending on the

Jan 1, 1960

By N. J. Grant, H. Brunner

This paber is concerned with the determination of equations relating elongation to the amount of shear taking place both along grain boundaries and in slip planes of poly crystalline aggregates during creep. Certain discrepancies with previously used equations are pointed out. Grain boundaries were observed to become serrated during creep, but it is shown that this does not necessarily prevent further grain boundary sliding. Direct obser-vations of subgrain boundary ingration lead to the conclusion that this migration facilitates sliding along serrated grain boundaries. It is bointed out that the state of stress at triple boints is still unknown. MOST of the mechanisms of deformation contributing to elongation are shear processes, such as slip, kinking, grain boundary sliding, and twinning. For quantitative investigations of individual deformation mechanism it is necessary to know the equation which permits the calculation of speci-tnen elongation from measured amounts of shear. This calculated elongation must then be compared with the observed total elongation. The authors&apos; special interest concerned grain boundary sliding during creep. Although this subject has already been investigated quantitatively by McLean,&apos; Rachinger,&apos; and Fazan, Sherby, and Dorn, calculations indicated that none of the equations used thus far to relate shear with elongation were sufficiently well founded. A basic study of this relationship was thus made and the results of this study (which do not entirely agree with those previously used) are presented. Most of the ideas set forth apply not only to grain boundary sliding but to other mechanisms of shear as well. THE SPEAR-ELONGATION RELATIONSHIP Basic Models—The relationship between shear and elongation is trivial in the simplest case of shear, which is shown in Fig. l(a). The vector A; designates the displacement across the shear interface, and Au, and Aut are its components parallel and normal to the tensile direction, respectively. It is evident that the specimen elongation due to shear is equal to the longitudinal component of the shear vector, and it should be noted that the normal component does not contribute to the elongation of the specimen (there are, of course, two normal components in a three-dimensional model). The model shown in Fig. l(b) may be applied to mechanical twinning and to subgrain boundary tnigration. In this case the width (h) of an already existing shear band increases by the migration of an interface, but the shear angle y (angle of mis-orientation in the case of a subgrain boundary) remains constant. The geometrical relationships indicated in Fig. l(b) permit this case to be reduced to the one shown in Fig. l(a). For the resulting elongation A6 we find: where AV/V = fraction of the volume of the specimen swept by migrating interfaces , and 1 = length of specimen. Thus, assuming for example that the angle of mis-orientation is 1 deg, and that P = 45 deg, we find that the specimen elongates 0.87 pct of its length if the entire volume of the specimen is swept once by such a subgrain boundary. An example of deformation by migration of subgrain boundaries is shown in Fig. 2. The specimen shown was repolished after 9.8 pct creep strain and the test then continued for another \ pct. Since the shear vector has, in general, a component normal to the surface, subgrain boundary migration results in the formation of an inclined band delineating the region swept by the subgrain boundary. These inclined bands become clearly visible when observed with oblique illumina-

Jan 1, 1960

By R. F. Rolsten

The preparation of pure metals by the thermal decomposition of volatile halides was developed byde boer&apos; and van Arkel.2 This has proved to be a useful technique for the refining of columbium,the mechanical and physical properties of which are seriously altered by such interstitial contaminants as oxygen, nitrogen, hydrogen, and carbon. The conventional deposition surface of a resis-tively heated metal filament was replaced, Fig. I, with an indirectly heated clear quartz surface. The impure columbium (feed) was contained in the annular space between the Vycor deposition bulb and the perforated molybdenum retaining cylinder. The head assembly was attached to the deposition bulb by fusing the Vycor at "A". This unit was then connected to a vacuum system composed of a three-turn glass coil to eliminate fracture due to vibration or expansion, a McLeod gage, a cold trap, a two-stage mercury diffusion pump, and a mechanical pump. The entire system was cold outgassed, and the 10 to 20 g of iodine in the auxiliary bulb (reservoir) was held in dry ice to prevent excessive loss of iodine. The columbium was hot outgassed at 800" to 825oC with the pressure maintained at l0-5 to 10-6 mm Hg for 48 hr and cooled under vacuum to 200° to 240oC. Iodine was sublimed from the reservoir and collected in the deposition bulb. The feed material temperature was adjusted to give the desired iodide vapor pressure and the finger temperature of 1000" C was independently attained and measured with a platinum-platinum 10 pct Rh thermocouple located in the center of the nichrome wire helical heating element, "F." The system was attended until temperature equilibrium was established, whence it operated without attention. This is a definite ad- vantage over the conventional "hot-wire" technique which required either constant attention or automatic control. In operation, the iodine vapor originally introduced into the vessel reacted with the crude metal to form a columbium iodide. This iodide vapor diffused to the hot deposition surface where it thermally decomposed, depositing columbium and releasing iodine. This liberated iodine then diffused back to the crude columbium where iodide was formed again. Thus, by repetition of this process, the iodine carried pure columbium from the crude material to the filament, where it deposited. The success of the "iodide" process in producing ductile metals depends on preventing the transfer of oxygen, nitrogen, hydrogen, and carbon from the feed material to the deposit. In many cases relatively minor quantities of these interstitial contaminants impair the ductility of metals. The material produced by the iodide process has such exceptional ductility that it is frequently and mistakenly assumed that iodide metal is always of very high purity. This assumption is not necessarily true since a number of metallic impurities can also be transferred. In the present investigation, the temperature of the feed material was adjusted to iodinate selectively and the deposition temperature adjusted to decompose the iodides selectively. By this technique, some metals present in the feed material were prevented from codepositing with the columbium. It is quite important to have the feed material symmetrically located around the deposition surface in order to obtain a uniform deposit at the maximum rate. For example, Runnalls and pidgeon3 observed that, when the base of a titanium filament was about 1 cm from the feed material, deposition was rapid on that section close to the feed, but that the rate decreased with distance from the feed so that a

Jan 1, 1960