Aerial photography is a recognized and integral part of the search for petroleum and for the metallic ores, but its application lags seriously; in the search for the industrial minerals This is, in all probability, a result of the relatively stringent economics of the various industrial mineral industries. The oil and mining companies (particularly the oil companies) can afford generous exploration budgets and thus can experiment with unorthodox approaches such as photogeology. The industrial mineral industry is more restricted, and up to now has relied on less sophisticated methods of exploration. The industrial minerals have been generally defined as those materials extracted from the earth that are neither metals, metallic ores, fuels, nor ground water. Any group chat must be defined in such a negative manner, by citing the things that they do not include, must in themselves be extremely diverse in character. This is truly the case for the industrial minerals; the full list of industrial minerals is incredibly long and tends to increase year by year.

Jan 1, 1964

By A. H. Duane, A. E. Miller

The high-temperature allotropy of some heavy rare-earth metals and their alloying behavior with magnesium in the 0 to 50 at. pct Mg region was studied by thermal, microscopic, and X-ray methods. Examination of a hcc phase retained upon quenching alloys of different magnesium content confirmed the existence of a bcc high-temperature allotrope in pure gadolinium, terbium, dysprosium, holmium, erbium, thulium, and lutetium. The lattice constants of the pure metals were determined from a Vegard's Law extrapolation and .found to be 4.05, 4.02, 3.98, 3.96, 3.94, 3.92, and 3.90 + 0.02 A, respectively. In all of the systems studied, the high-temperature bcc phase decomposed eutec-toidally, when slowly cooled, into a hexagonal rare earth-Mg solid solution and a simple-cubic peritec-tic AB-type compound. In 1956, Spedding et al.' observed high-temperature resistivity anomalies in the light rare-earth metals and made several unsuccessful attempts to retain the high-temperature form of these materials at room temperature by quenching the pure metals from temperatures near their melting points. High-temperature X-ray techniques were used by Spedding et a1.' in 1959, to investigate the high-temperature allotropy of the rare-earth metals. This study showed that lanthanum, cerium, praseodymium, neodymium, ytterbium, and possibly gadolinium are bcc at temperatures near their melting points. Discontinuous changes in resistivity at elevated temperatures were also observed for pure gadolinium, terbium, dysprosium, holmium, and lutetium, thus indicating the possible existence of a high-temperature crystalline transformation in these metals. However, due to experimental difficulties encountered in the high-temperature X-ray analysis of these metals, their allotropic form was not identified. Spedding et a~.~ in 1960 observed that yttrium displayed a continuous solid solubility with lanthanum at elevated temperatures, thus showing the high-temperature structure of yttrium to be the same as that of lanthanum, i.e., bcc. Similarly, the high-temperature alloying behavior of gadolinium with yttrium showed gadolinium to be bcc at elevated temperatures. The bcc nature of the high-temperature form of yttrium was again recognized in 1960 by Eash and carlson4 in their study of the alloying behavior of yttrium with thorium. Gibson and Carlson, in a similar study of the alloying behavior of yttrium with magnesium, found that by quenching Y-Mg alloys from within the 0-solid solution region, Fig. l, they were able to retain the allotropic form of yttrium. It was the present authors' intention to use this method to show the existence of a bcc high-temperature form of the heavy rare-earth metals gadolinium, terbium, dysprosium, holmium, erbium, thulium, and lutetium. Simultaneous with the present work, Beaudry and Daane' have shown the bcc nature of the high-temperature form of scandium. EXPERIMENTAL PROCEDURES Materials. The rare-earth metals used in this study were prepared by the calcium reduction of the fluoride and were further purified by vacuum distillation. The magnesium was obtained from the New England Lime Co. and was also purified by distillation prior to its use in the preparation of the rare earth-Mg alloys. The results of chemical and spec-

Jan 1, 1964

By J. H. Swislzer

TWO-LIQUID miscibility gaps have been found to exist in both the CaO-SiO, system above 1705 and the Cr,03 system above 2200"c. Glasser and 0sborn3 studied the extension of these miscibility gaps into the Ca0-Si0,-Crz03 ternary system and reported that the two-liquid region is not present at temperatures below the monotectic temperature of 1705°C in the CaO-SiO, system. The present authors, in connection with other work on surface-tension measurements and foam stabilities in the same ternary system,4 observed that the miscibility gap exists at temperatures as low as 1600°C. A brief experimental study was devoted to deter- mining tie-line positions in the two-phase region. The technique used was to obtain a separation of phases at 1600°C, then to quench-in the high-temperature phases and obtain a chemical analysis of each phase. It was necessary to take special precautions in obtaining a phase separation because of a tendency toward emulsification of the two liquids. The procedure followed is described in the schematic drawing in Fig. 1. A small platinum crucible containing several pinholes on its sides was placed inside a larger platinum crucible. An excess of Crz03 was placed in the outer crucible, together with a prefused binary CaO-Si02 mixture, and the Cr203 was allowed to diffuse through the pinholes and saturate the same binary CaO-SiOl mixture in the smaller crucible. After equilibration at 1600°C, the inner crucible contained only the lighter liquid (liquid A) saturated with Cr203. The outer crucible contained layers of both liquids. Experimental data were obtained by analyzing the entire contents of the inner crucible and only the bottom layer of the larger crucible (liquid B). The upper layer of the outer crucible was not suitable for chemical-analysis purposes because dispersions of the second phase sometimes were found in the samples. The technique is described in more detail in Ref. 4. The same method was used by Grieveson and urkdoan' to study a miscibility gap in sulfate-ferrite melts, where the liquids were difficult to separate because of similarities in density. In addition to the phase-separation experiments, a few others were conducted to obtain information

Jan 1, 1964

By D. T. Peters, J. C. Bisseliches, J. W. Spretnak

The pain boundary relaxation phenomenon in high-purity copper, 0FHC copper, and a precipitation-hardenable alloy o-fCu-2 uit pct Co has been studied by internal ,friction and elastic aftereffect techniques. The data were analyzed by assuming the broad distribution of relaxation times observed obeys a lognormal distribution law which enables calculation of the relaxation strength. Grain size had no effect on relaxation strength, although the peak width increased with increasing grain size and decreasing temperature. A double grain boundary peak was produced in high-purity copper by annealing to produce secondary recrystallization. The activation energy measured for 99.999 pct Cu is 37.5 * 3 kcal per mol and 46.5 kcal per mole for OFHC copper. A small peak in the Cu-Co alloy at about 220°C at 1 cps was deduced to be the grain boundary peak. Its height increased and its activation energy decreased with increasing aging time. Except for erratic peak positions the observations were consistent with the theory of pain boundary sliding. BEFORE the mechanism of the grain boundary internal friction peak in metals can be satisfactorily explained, the detailed characteristics of the relaxation process must be documented. Of interest are the effect of grain size on relaxation strength, the high-temperature background, and peak width and position. The effect on the grain boundary peak of a precipitate at grain boundaries and of the change in distribution of the particles with aging time must also be explained by any existing or forthcoming theory. The model which has received the most attention was proposed by KG' and zener2 and proposes that the anelastic strain results from sliding of adjacent crystals at grain boundaries. The sliding is limited by the interlocking of grain corners. It follows, according to this model, that the relaxation strength is independent of and the relaxation time is proportional to the grain size. The proportionality between grain size, D, and relaxation time, t, has been confirmed by K&' and Bisseliches . In this case, the internal-friction peaks of various specimens can be superimposed by plotting Q-' as a function of the parameter vD exp H/RT where v is the frequency and H the activation energy. However, the data of Starr et 01.' and Leak6 fit better to a parameter containing D to an exponent near two. A meaningful relationship is not always deducible from the shift of peak temperature with grain size. KG7 demonstrated that a twofold variation in grain size obtained by varying the amount of cold work followed by identical recrystallization anneals will cause a peak shift that is too large to be accounted for even by an exponent of two. Since the decreased grain boundary area existing with a larger grain size is exactly compensated for by an increased sliding distance, the relaxation strength should not decrease with increasing grain size. The height of the internal-friction peak has generally been observed to be rather insensitive to grain size as long as the average grain diameter does not approach the specimen diameter. Exceptions have been reported by Koster, Bangert, and Lang8 for copper, and by Leak6 for iron. The observations for copper could well have been confused by the presence df 0.3 pct0. The possibility that the peaks may simply be increasing in width with increasing grain size and that the relaxation strength, which is proportional to the area under the peak, may remain constant was not examined. his point has been checked in this investigation using high-purity copper. Atomic mechanisms to account for damping by sliding at grain boundaries have been proposed by KG7 and Mott. KG predicts the activation energy to be identical to that for self-diffusion. Mott's "island" model suggests the activation energy is nL where n is the number of atoms in an island and L is the latent heat of fusion per atom. Other authors have felt that a value equal to the activa-

Jan 1, 1964

By E. T. Turkdogan, P. Grieveson

Experimental results are presented for the rate of solution of nitrogen in a iron in the temperature range 750° to 873°C and in 6 iron in the temperature range 1410° to 1470°C. It is shown that the rate controlling process is diffusion of nitrogen into the iron. The diffusiting of nitrogen in a and 6 iron is derived from the results, and the temperature dependence of the diffusivity is represented by the equation D = 7.8 x e- 18,900/RT sq cm per sec. The solubility of nitrogen in a and 6 iron, in equilibrium with 1 atm pressure of nitrogen, has been measured. Using these results and other available data, it is found that the variation of the logarithm of nitrogen solubility with the reciprocal of absolute temperature is nonlinear. In an Appendix, some results of Darken and Smith are presented for the rate of solution of nitrogen in iron using ammonia + hyidrogen mixtures. These data also support the view that diffudsion of nitrogen in iron is the rate-controlling process when ammonia + hydrogen mixtures are used. A considerable effort has been made to obtain data on the solubility1-5 and diffusivity of nitrogen in a iron6-l2 because an understanding of the effect of nitrogen on the properties of steel must be based on an accurate knowledge of the properties of nitrogen in pure iron. However, no information is available concerning the kinetics of solution of nitrogen in a and 6 iron. Recently the authors13 have investigated the rate-controlling mechanism operating in the kinetics of solution of nitrogen in y iron. This study was directed to determine the rate-controlling processes for similar reactions with a and 6 iron as well as to establish values for the solubility of nitrogen in equilibrium with nitrogen gas in a and a iron. EXPERIMENTAL The procedure used in experiments to determine the rate of solution in cylindrical iron rods was the same as that described in a previous communication.13 Ferrovac E grade iron used in all experiments contained the following impurities in weight percent: C, 0.005; Mn, 0.001; P, 0.002; S, 0.006; Si, 0.006; Ni, 0.025; Cr, 0.002; V, 0.004; W, 0.02; Mo, 0.01; Cu, 0.001; Co, 0.01; 0, 0.007. After cleaning the surface, the iron rods were treated in an atmosphere of purified hydrogen for 17 hr before the reacting gas was introduced for known experimental times. After quenching, the samples were sectioned radially and analyzed for nitrogen. In addition to experiments using rods, iron foils were used in the measurements of solution rates of nitrogen in a iron. The foils of two different thicknesses were prepared by cold rolling Ferrovac E grade iron cylindrical rod to 0.051 and 0.152 cm. Foil samples were used in a rectangular form 5 cm long and 1.25 cm wide. The specimens were thoroughly cleaned of surface oxide with fine emery cloth and degreased with carbon tetrachloride immediately before entry into the furnace. The experimental procedure was the same as that used in the study with rods. At the completion of an experiment, the foil samples of the nitrogenized iron were analyzed for nitrogen after discarding 0.3 cm from the perimeter of the specimen. Iron foils were nitrogenized and denitrogenized in the a and 6 range with a gas mixture of 95 pct N and 5 pct H for times varying from 5 min to 2 hr. Results obtained for the average composition of nitrogen in iron for these experiments are presented in Fig. 1. Prior to the denitrogenization experiments, the samples were saturated with nitrogen at 1000°C and 0.67 atm N, giving a uniform nitrogen concentration of 0.0204 pct. According to the known a-y phase boundary in the Fe-N system,14 this composition lies within the ferrite region at temperatures 750" to 850°C. Use of this initial nitrogen content insured that reaction occurred between the gas and a single solid phase, a iron. Examples of the results for the mean concentrations of nitrogen in cylindrical iron rods, 0.356 cm radius for both the a and 6 ranges are given in Fig. 2. Typical examples of the results obtained for the radial distributions of nitrogen in rods are presented in Fig. 3. It appears that the results for radial distributions can be extrapolated to constant surface compositions which agree with the equi-

Jan 1, 1964

By James E. Hill

TECHNOLOGY is best nurtured by a sympathetic climate that is a composite of many factors. Necessity is a highly motivating factor as illustrated by the abnormal surge of technologic development curing wartime. Other factors include appropriate timing, economic pressures, available personnel, and in some instances, legislative action. Problems of recent concern to mining technology have been the quality and quantity of available technical personnel and the possibilities of restrictive legislation. The quality and quantity of technically trained personnel may be inadequate to meet the rapidly increasing complexity of modern technology coupled with the growing demand for qualified personnel. The question of appropriate training was a subject for debate.2 The curriculum and methods of teaching have changed. Questions have been raised on the relationship of scientist and engineer, interdisciplinary versus specialized curriculum, undergraduate versus graduate training, and the place of the smaller schools versus the large university-research complexes that have developed at some universities. Various aspects of the subject of engineering education for the mining industry were discussed at the meeting on Mining and Mineral Engineering Manpower at the Michigan College of Mining and Technology, November 18-19, 1963. Meanwhile, the trend toward interdisciplinary training gathers momentum as illustrated by the establishment of the School of Engineering Science at Johns Hopkins, the Schools of Engineering and Applied Science at Columbia, Princeton, and Yale, the Division of Engineering and Applied Physics at Harvard and, more recently, the School of Engineering Science at Florida State University which cuts across the conventional areas of civil, mechanical, electrical, and chemical engineering.

Jan 1, 1964

By E. P. Cadwell

"Throughout the years Cyanamid has been a supplier of cyanide and a supplier of information to the mining industry. In general, the knowledge of mineralogy is greatly overlooked. Mineral deposits in the Western hemisphere have been exceedingly rich in the past but now they are becoming poorer. In other words, we will have to use our talents to the utmost to extract the precious metals and base metals from these ores. Modifications of some of the mineralogical equipment displayed here belong in the mill.Cyanidation of copper has been one of the main projects in our labs in recent years. De-rimming or de-filming of copper in order to upgrade copper concentrate was the main aspect investigated. A study was made as to how wide spread was the filming of secondary copper on pyrite, and to what extent it affected the copper industry. It was very wide.Often there is no conception as to what the minerals are. One open pit copper producer with a chalcopyrite ore was producing a copper concentrate with a 5% copper value whereas chalcopyrite contains 35% copper. They used primary and secondary grinding and a regrinding section. The ore contained about 8 parts chalcopyrite to one part of other copper minerals. In tests, a 3 1/ 2% copper rougher concentrate, cleaned without regrinding but conditioned with cyanide for a low contact time of 30 seconds produced a 30% copper concentrate with 90% recovery by removal of the film. It was of utmost importance that some quantitative mineralogical analysis be made before flow sheet changes were made. Every man should be trained to do his own microscopic examination in order to get quick answers. The fundamental thing in all mineral dressing is to first of all know the minerals and the mineral associations."

Jan 1, 1964

By R. T. DeHoff

A general method for determining the geometric properties of structures composed of particles which are all the same shape and size is presented. The application of the method requires a knowledge of' the qualitative shape of the particles in the structure, ad a maximum of three simple counting measurenzents, which are made on a representative plane section taken through the structure. It is also shown that the number of different kinds of measurements necessary JOY the complete description of the structure can be decreased if some independent information about individual particles is available. The geometric properties that can be determined quantitatiz~ely from counting measurements for susch structures are size, shape, number, surface area, vlolume, ad such extensive properties as volume Mction and surface area per unit volume. THE simplest kinds of measurements that may be made on a metallographic section are counting measurements. There are three such simple counting measurements, which are determined by sampling the microstructure with a point, a line, and an area. The first of these, the point count, is probably the most familiar among metallographers. The second count, the number of intersections a test line makes with particle outline, is somewhat more recent in its origin and application. The third counting measurement, the number of particle sections observed in unit area of the plane of polish, has long been used in the estimation of grain sizes. The real utility of these three counting measurements lies in the fact that they are rigorously and unambiguously related to certain extensive geometric properties of the three-dimensional structure of which the metallographic section is a sample. These relationships will be reviewed briefly below. Of somewhat secondary importance to the fundamental relationships is the observation that, if some simplifying assumptions about the geometry of the three-dimensional structure are introduced, manipulation of the counting measurements gives a more complete description of the structure. Specifically, in addition to the extensive properties which these measurements rigorously estimate, the number of particles, their size, and their shape may be determined. The purpose of the present paper is to explore the consequences of introducing the assumption of constant size and shape. A later paper will deal with the estimation of geometric properties of structures which may be characterized by a two-parameter size distribution. It should be mentioned that the introduction of this simplest of assumptions, while clearly not generally justified in metallurgical structures, is not without precedent. For example, many estimates of the number of particles per unit volume of structure, based upon a single counting measurement, are scattered throughout the literature.13 Virtually all of these developments assume a constant particle shape, e.g., spherical or polyhydral, and constant size. That such an assumption is necessary is evident from the fact that, for more general structures, more than a single parameter is required to describe the three-dimensional structure, so that the determination of a single parameter on a section would be insufficient to specify the structure. Similar developments for the estimation of particle size from a single counting measurement, e.g., routine grain-size determinations, make the same very limiting assumption,435 but have nonetheless proven of practical value. The present paper embodies a generalized approach to the development of relationships among the two-dimensional counting measurements and the three-dimensional geometry of the structure, subject to the assumption of constant particle size and shape. It is the hope of the author that by presenting the relationships and the assumptions involved in dealing with this approximation, in a single, unified treatment, the reader may be impressed with the usefulness of the counting measurements, may be guided in their application to the estimation of details of the geometry in specific structures in which he may be interested, and may be moved to apply the results, with understanding, to new structural problems. Several authors6, 7 have demonstrated independently that it is possible to obtain unbiased estimates

Jan 1, 1964

This paper states how alloy and welding advances have made possible the rapid development of the use of aluminum in the construction of equipment for earth moving and off -highway rock hauling. The main details are given regarding the construction and field testing carried out on an aluminum prototype body. The test results of strain gauge readings are analysed, and a description is given of how these have been applied in subsequent designs. The increase in the number of aluminum units put into the various types of service in Canada, as well as the problems encountered, is described, and the experience gained from five years of field service is discussed in some detail. An assessment is also made of the durability of the e units. The economics of using aluminum, together with the current development position, are reviewed, and predictions are made for considerable future increases in the use of aluminum units in open-pit and off-highway operations.

Jan 1, 1964

By Robert A. Rapp, Jan E. Verfurth

From the measurement of internal-oxidation band widths in Ag-In and Cu-A1 alloys, products for the solubility No and the diffusivity Do of oxygen in silver and apparent NODo products in copper have been obtained over a range of temperature. The NODO products for silver are in agreement with the product of the individually determined No and Do values of Eichenauer and Müller. Although interstitial diffusion of oxygen in silver is expected, the temperature-independent factor Do of the diffusion coefficient does not agree well with the theory of Wert and Zener. For Cu-A1 alloys internal oxidation does not follow the expression derived for ideal kinetics, since the apparent NODo product calculated from internal-oxidation measurements is a function of the alloy content in the specimen. Thus, unequivocal values for No or DO or even the product NODO in copper are not available from the literature. RELIABLE values for the saturation solubility NO and diffusivity DO of oxygen in fcc metals are lacking and difficult to determine, partially because internal-friction measurements are not applicable. Permeability experiments and Sieverts7-type adsorption -desorption methods3 have met with difficulty; however, Eichenauer and Müller4 have recently reported on the solubility and diffusivity of oxygen in silver as determined by the latter technique . Rhines, Johnson, and Anderson,5 and independently Meijering and Druyvesteyn,' introduced the possibility of deriving values for the product NODO in a metal from measurements of the widths of internal-oxidation zones (subscales) formed during the internal oxidation of alloys. In addition to these authors, several other investigators7-9 have made such measurements in various silver and copper alloys at various temperatures, mostly using me- chanically polished specimen surfaces. The purpose of this investigation was to determine over a range of temperature the calculated products NODO in silver and copper from systematic measurements of the widths of internally oxidized zones in Ag-In and Cu-A1 alloys, using specimens with electro-etched surfaces. Consider the internal oxidation of a dilute solid-solution alloy in which the base metal is not oxidized. If diffusion of oxygen is the rate-controlling step, then the depth 5 of the internal-oxidation zone is given by where y is a dimensionless parameter and t the oxidation time. Based on the solution of the diffusion equation, wagnerl0 has shown that under certain conditions several mathematical simplifications may be used in the evaluation of y, so that Eq. [I] may be expressed for the case that y « 1, and y(Do/DB) 1, where N(so)the is the equilibrium solubility (mole fraction) of oxygen in the solvent metal for the given oxidizing atmosphere, is the mole fraction of the solute metal in the bulk alloy, 4 is the diffusivity of the solute in the base metal, and v is the ratio of oxygen atoms to solute atoms in the precipitated oxide BO,. Rearranging Eq. [2] Maak' has derived an expression analogous to Eq. [3] for the case that an external-oxide scale, in addition to an internal-oxidation zone, is formed. For this combined external and internal oxidation for the case that 5/2 where 5 is the distance of the internal-oxidation front from the original external s.urface, and X is the distance of the external oxide/metal interface from the original external interface. The function F is defined by the expression

Jan 1, 1964

By M. Semchyshen, A. P. Coldren, W. G. Scholz

A survey of the Fe-Mo-B system was made to determine the extent to which boron might affect the microstructure and strength properties of iron-rich Fe-Mo alloys. Seventeen vacuum-induc tion melted ingots were prepared with approximate mo-lybednum contents 01 2, 4, 9, and 19 wt pct and approximate boron contents of 5, 14,50, and 630 ppm by weight. Phases extracted from annealed specimens and identified by X-ray diffraction analysis included E Fe3MO2, Mo2FeB2, and an oxide hazling a diffraction pattern practically identical to that of MnFez04. Three types of alloy strengthening were observed: a) Fe-2 pct Mo-B alloys were hardenable by a bainitic-type transformtion of austenite to ferrile; b) Fe-4 pct Mo-B alloys were hardened by the solid-solution mechanism; and C) Fe-9 pct Mo-B and Fe-19 pct Mo-B alloys were hardened by precipitation of the E Fe3Moz phase. Boron was observed to have a very strong hardening effect in the Fe-2 pct Mo alloys and a mild strengthening effect on the 1200°F properties of the Fe-4 pct Mo alloys. In the Fe-9 pct Mo alloys there was no consistent effect of boron on strength at either room temperature or 1200° F. The Fe-19 pct Mo alloys were so brittle that meaningful tensile or creep-rupture data could not he obtained. No dispersion hardening from borides was recognized in any of the alloys. THE high-temperature properties of iron-rich Fe-Mo alloys were studied by Reiter and Hibbard.' They found that the strength of the alloys increased markedly as the molybdenum content was raised from 0 to 15.9 pct by weight. The authors explained the various degrees of strengthening in terms of a) solid-solution strengthening, b) strengthening from a martensitic-type transformation, and C) precipitation strengthening. The objective of the present investigation was to conduct a survey of the iron-rich portion of the Fe-Mo-B system to determine whether the beneficial effects of molybdenum on the strength of iron can be enhanced by the presence of boron. It was thought that perhaps fine dispersions of molybdenum- rich borides would be found which could improve the high-temperature strength of ferritic alloys beyond the strengths attainable by molybdenum additions alone. Also, it was considered worthwhile to study the effects of boron in alloys which are essentially free of carbon. Most, if not all, of our present knowledge about boron in high-temperature alloys pertains to alloys containing carbon and carbides. EXPERIMENTAL PROCEDURES Alloy Preparation. Seventeen 8-lb ingots were prepared from electrolytic Plastiron, unalloyed molybdenum chips, and boron powder by a vacuum-induction melting procedure employing hydrogen as the main deoxidizer. The alloys were melted in alumina crucibles using 35-lb melts, with each melt being split four ways to achieve varying boron contents within four Fe-Mo base compositions. The results of chemical analyses conducted on chips machined from the chilled ends of the ingots are presented in Table I. The boron analyses were performed by a spectrographic method utilizing primary standards prepared from boric acid. They indicated that in ingots to which no boron was

Jan 1, 1964

By B. J. Dalton

The Helium Research Center, Helium Activity, Bureau of Mines, is presently engaged in a critical examination of all of the PVT data on helium that appear in the literature. The long-range objective is the development of a single equation of state for helium that will allow all of the thermodynamic properties to be calculated and will reproduce all of the data within the accuracy with which the data arc known. A preliminary objective is to obtain the best val¬ues of the second virial coefficients and to develop an equation that will reproduce the best values as a function of temperature. The method of treatment consists in expressing the PV product of a gas, for a given isotherm, in terms of a power series in either the pressure or the density and evaluating the constants by least squares solution. Associated with these functions whose coefficients have been evaluated by least squares, the following errors, or deviations, are of interest; the standard error of a single measurement; the standard error in each coefficient; and the standard error of the resulting function.

Jan 1, 1964

By H. C. Fiedler

The development of cube-on-edge secondary re crystallization texture in Si-Fe strip depends upon the ability of inclusions, such as manganese sulfide, to restrain nomal grain gvowth. The ability of inclusions to perform this function is shown to depend upon their size and distribution. The desired uniform dispersion of many small inclusions is obtained by controlling the cooling rate from above the solution tempmature of the inclusions or, alternatively, by drastic 'quenching from above the solution temperature followed by heat treating at a lower temperature. The development of the cube-on-edge secondary recrystallization texture in Si-Fe strip depends upon both establishing the proper primary recrystallization texture and having inclusions to restrain normal grain growth. It has been suggested that the first requirement is met with a texture which, though weak, is near (110)[001]. A mechanism for secondary recrystallization originally proposed by ielsen' is consistent with the presence of this primary texture. It is visualized that a secondary grain appears where two adjacent grains happen to be sufficiently similar in orientation to be capable of behaving as a single large grain. This pair of grains will grow at the expense of its smaller neighbors as a consequence of its having lower grain boundary free energy. Other explanations of the origin of the secondary recrystallization texture have been offered,' and it can be concluded that the mechanism is not fully understood. Nevertheless, it is apparent that operationally the necessary primary recrystallization texture is obtained simply by interposing an anneal during the cold reduction to final gage. The role of inclusions in the development of the secondary recrystallization texture has been demonstrated by May and Turnbull4 in a comparison of a high-purity heat and a heat containing manganese sulfide. They showed that the driving force for secondary recrystallization is inversely proportional to the diameter of the matrix grains and that the function of the inclusions is to maintain a small matrix grain size. Other inclusions, such as various sul- fides,')' silicon nitride,8 and vanadium nitride,' titanium carbide,'' and vanadium carbide," have been shown to be effective in promoting secondary recrystallization to the cube-on-edge texture. There is also evidence that silica inclusions in Si-Fe strip made by powder-metallurgy techniques perform this function.' This report is concerned with the second of the two requirements for secondary recrystallization, namely the importance of the metallurgical control of the size and therefore number of inclusions. While the concepts involved are simple, they are fundamental to the making of this material. EXPERIMENTAL PROCEDURE A heat containing 3.27 pct Si, 0.026 pct S, 0.06 pct Mn, and 0.004 pct C was made in an air induction furnace from electrolytic iron, 98 pct ferro-silicon, electrolytic manganese, and iron sulfide. The heat was divided between graphite and baked-sand molds with a cavity 2-5/8 by 5 in. and with walls 2-3/4 in. thick. Slabs, 1 in. thick and 2-5/8 by 5 in., were cut from the ingots and hot-rolled either in the as-cast condition or after one of the heat treatments described later. After pickling, the 80- to 100-mil-thick hot-rolled band was, unless otherwise noted, heat-treated for 5 min at 900°C before being cold-rolled to 25 mils. After a heat treatment of 1 to 3 min at 860°C, the strip was cold-rolled to 12 mils, the final thickness. The percent cube-on-edge texture was determined by dividing the maximum torque as averaged from four samples by the maximum torque of a 3-1/4 pct Si-Fe single crystal having the (110) plane in the plane of the sample. The torque measurements were made in a field of 1000 oe on 1-in.-diam disks. RESULTS AND DISCUSSION The importance of the thermal history of the ingot is evident in Fig. 1 from the appearance of strips heat-treated in a temperature gradient. The sample

Jan 1, 1964

By J. O. Brittain, E. P. Lautenschlager, F. Felberbauer

This investigation was undertaken to evaluate the effect of a dispersed phase in a iron upon the strain hardening and the stress dependency of dislocation velocity as inferred from the strain-rate sensitivitv. Experiments were made in a-iron specimens with controlled amounts of carbon and/or A12O3. They were tested at various temperatures between 195' and 373 'K under a variety of conditions oj-concentration, strain rate, and quench aging. The resulting yield strength, flow strength, and strain hardening increased with addition of Al2O3. The parameter m, measured from changes in strain rate, was xsed to describe the stress dependency of the dislocation velocity. m was found to increase with additions of A12O3, increasing carbon in solution, and with increasing temperature. When applied to a recent model for yielding based upon dislocation multiplication and velocity characteristics, the values of m alone did not successfully predict yielding for the materials of this investigalion, but had to be adjusted with a consideration of the number of unlocked dislocations nucleated heterogeneously at discontinuities or inclusions. The change of yield strength with Al2O3 Interpar-ticle spacing appeared to obey a theory of Orowan. EVER since the concept of dislocations has been introduced to explain plastic deformation in crystalline materials, the origin of dislocations and the source of the number of dislocations required to account for plastic deformation have been persistent questions. Ruling out the possibility of homogeneous nucleation,' Gilman2 drew attention to the various cases of heterogeneous nucleation as the source of dislocations, whereas Frank and Read3 introduced the Frank-Read source. However, Gil-man found that the Frank-Read sources did not play a dominant role in the deformation of LiF crystals, but that small precipitates are often, if not always, associated with the nucleation of dislocations. In LiF crystals, however, most of the dislocations arose through the multiplication of moving dislocations in a mechanism described by Koehler4 and Orowan,5 Thus, relatively few precipitates could account for a large number of dislocations. A similar observation of dislocation nucleation at inclusions of precipitates was made by Stein and LOW' on Si-Fe crystals. Their crystals contained

Jan 1, 1964

By K. R. Janowski, H. Conrad

As part of a program to establish the effect of crystal imperfections on laser output, a detailed study was made of the dislocation structure of ruby crystals obtained from varioius sources. Using KHSO4 as an etchant, a detailed mapping of the dislocation structure on the (0001) and the (1150) planes was carried out. A less extensive study was made of the rhombohedral planes. The average dislocation density on the basal plane was 1.5 to 3 x 106 cm&apos;2 and on the (1120) planes -5 x 10&apos; cm-2. Howe7!er, considerable variation existed between areas on a given plane. The subboundaries in the basal plane tended to lie along [1100] type directions while those on the (1120) plane tended to lie: a) parallel to the basal plane, b) along truces of the (1101) plane, and c) along normals to the traces of the (0001) planes. The orientations suggest that mang of the dislocations lie on the (0001), (1701), and (1150) planes A Laue back-rellection nnalysis Of c-axis wander in one crystal revealed a gradual increase in misorientation from me end of the crystal to the other, with a maximum variation of 1°35&apos;. Slight etching of a mechanically polished crystal revealed mumerous polishing scratches, suggesting the existence of a plastic flow layer. It is recognized that chromium concentration, lineage, and other crystalline imperfections play a role in the efficiency of ruby lasers.&apos; Consequently, it is desirable to establish in detail the imperfection structure of ruby crystals to be used as lasers. Some exploratory work along this line had already been done by Barnes&apos; and Dils and Martin.&apos;" How- referred to as the morphological system, as described by Kronberg.4 The Miller indices given in the present paper will be based on this morphological system. In this system, the three common growth planes are the (0001), the {1120}, and the {1101}.5 Since these planes are of high stability, it is expected that they are most suitable for study by the etch-pit technique. In the present investigation, a detailed mapping of the dislocation structure was carried out for the (0001) and the (1130) planes. A less extensive study was made of the etch-pit structure on rhombohedra1 planes. An analysis of dislocations in sapphire (the ruby host) was first made by kronberg,4 who postulated that slip on the (0001) plane occurred by motion of dislocations with Burgers vector 1/3 <1150> and that these dislocations might dissociate into quarter partials. An etch-pit technique using boiling phosphoric acid was developed by Scheuplein and Gibbs6, 7 for identifying dislocations intersecting the (0001) planes and the planes near (2021) in sapphire. Al-ford and Stephens8 were able to reveal dislocations on the (0001) and {1120} planes in sapphire and ruby by etching in fused potassium bisulfate (KHS04) at 675°C. The termini of basal dislocations [(000l), <1120>] were revealed by Palmour and Kriegel9 on {1120} and {1010} by thermally etching sapphire. Bond and Harvey10 were able to decorate dislocations in sapphire by adding 1 pet by weight of ZrO2 to the Al2O3 powder used in the growth of the crystals by the Verneuil technique and then heating the grown crystals for 4 hr at 1500°C. They found, using optical transmission microscopy, that many dislocations had straight segments which were parallel to one of the six [1120] directions in the basal plane. Single dislocation lines curved smoothly from one alignment to the other, turning through angles of 60 to 120 deg. Also observed were isolated hexagonal loops, approximately 10 µ in diameter, the sides of which lay along the same directions as did the longer dislocations. MATERIAL AND ETCHING PROCEDURE The ruby specimens used in this study (all containing approximately 0.04 pet Cr) had been obtained from four different sources: Linde Co., Meller Co., Valpey Crystal Corp., and those grown at Aerospace Corp.* For the initial phase of this study, several specimens were cut from the slab shown schematically in Fig. 1 which had previously been cut from a disk boule obtained from the Linde

Jan 1, 1964

By J. Leja, A. Pomianowski

This paper deals with equimolar solutions of xanthate and alkyl trimethyl ammonium bromide adsorption on copper, nickel and sphalerite powders. After an exposition of the experimental methods used and the results obtained, a thorough discussion leads to the conclusion that some molecular association between xanthates and CnTAB&apos;s does take place in the bulk of the solution as well as at the air/liquid interface. A spectrophotometric study of xanthate solutions alone and their mixtures with equimolar amounts of alkyl trimethyl ammonium bromide (CnTAB) has established the additivity of ultraviolet spectra (190 to 400 mµ) for potassium ethyl xanthate (KEtX) and C12TAB. No obvious effect of C12TAB addition on the decomposition rate of KEtX was observed, the half life of which was established as 29±3 days at 22°C and pH ~ 6. In mixed solutions of longer xanthate homologues (e.g. hexyl and nonyl) and equimolar CnTAB, colloidal precipitates are gradually formed which contain primarily the corresponding xanthate molecules. The kinetics of collector abstraction by copper, nickel and sphalerite powders were studied in 10-5 to 10"3 M solutions of KEtX alone and in equimolar mixtures of KEtX and CI2TAB. Presence of C12TAB caused a two to three fold increase in the amounts of xanthate (equivalent to many monolayers) abstracted by copper and nickel powders (and in their rates of abstraction) but had no effect on the abstraction of xanthate by unactivated sphalerite (equivalent to less than a monolayer). The adsorption of C12TAB itself from the mixed solutions was very low, at most one monolayer only, and was not influenced by the nature of the solid powder used. A change in the rates of abstraction, observed with copper powder, was interpreted as a completion of a multilayer coating (completely enveloping the grains of powder) following which the rate of reaction between solution and substrate becomes controlled by diffusion through this coating. Work of Buckenham and Schulmanl on molecular associations between different collectors has shown unusual synergistic effects in flotation of individual minerals using mixtures of xanthates and alkyl trimethyl ammonium bromides. The objectives of the present work were: 1) to determine whether these molecular associations between the two types of collectors (indicated by strong surface tension lowering in Buckenham and Schulman&apos;s work) take place at the air/liquid interface only or in the bulk of solution as well 2) to establish whether different solids adsorb any species from the mixture of these amphipatic molecules preferentially or as molecular complexes 3) to establish whether there are any differences in the kinetics of adsorption. Metallic copper and sphalerite powder were chosen as adsorbents since they represent two extremes since copper readily adsorbs multilayers of xanthate (and is easily floated with ethyl xanthate) while unactivated sphalerite does not appreciably adsorb xanthate but is known to be readily floated by the amine type collectors. Metallic nickel was included because the infrared spectroscopic work2 on xanthate

Jan 1, 1964

By C. H. Ma, J. S. Makris

This paper describes a modified X-ray diffraction microscope wzethod based on the general principles of Berg-Bawett&apos;s Method, Lang&apos;s Method, and Woosters1 Technique. This new method may be used for stationary or oscillatory photomacrographs, with both reflection and transmission techniques. In the stationary technique, a small point-source of a divergent X-ray beam of white radiation is used; in the oscillatory technique, a monochromatic divergent beam is employed. The chief advantages of the method described herein are that only approximate alignment of the Bragg angle -of-interest is needed during exposure, and that a large portion of a crystal-specimen surface can he irradiated. In recent years, the study of dislocations through X-ray diffraction microscope techniques has received considerable attention as concerns the per,fection of single crystals. Very promising results have appeared in the literature.&apos;-&apos; These techniques are very useful when the dislocation density of a crystal is near 105 per sq cm or lower. The principle of X-ray diffraction microscopy is based on the differential effect of X-ray primary extinction between the distorted parts and the perfect parts of a crystal. When an X-ray beam impinges on a set of planes of a crystal at the correct Bragg angle, diffraction of X-rays will occur with a 90-deg phase shift of the diffracted beam. This once-diffracted beam still forms the correct Bragg angle with the planes ahead of it, if the planes are not distorted. Thus, part of the strength of the once-diffracted beam is rediffracted and the beam continues to travel in the direction of the primary X-ray beam. This twice-diffracted beam not only takes away part of the strength of the once-diffracted beam, but also causes destructive interference with the primary beam because it now is exactly 180 deg out of phase with the primary beam. As the primary beam goes farther and farther into the crystal, its intensity is continuously weakened. Asa result, the ultimate X-ray diffraction power of a set of undistorted planes is largely extinguished. This phenomenon is called primary extinction.1,2&apos;4 If the set of planes ahead of it is distorted, the once-diffracted beam will have less chance to be rediffracted, because it could not meet the exactly correct Bragg angle for rediffraction. If a part of the beam does rediffract, this twice-diffracted beam is not exactly 180 deg out of phase with the primary beam, and thus it causes less destructive interference. As a result, the registered X-ray diffraction power of the distorted part of a crystal appears stronger than that of the perfect part. Thus, point-by-point contrast of a diffraction image is theoretically possible from a crystal containing dislocations. Two most popular X-ray diffraction microscope techniques today are Berg-Barrett&apos;s Method and Lang&apos;s Method. Both of these techniques require a

Jan 1, 1964

By I. R. Kramer

The apparent activation energy, U, JOY plastic deformation of aluminium, copper, and gold single crystals and polycrystalline aluminum was found to he dependent upon surface condition. At low strains, the value for U for aluminum single crystals was 4200 cal per mole ; however, this value decreased to 920 cal per mole when the specimens were polished during the test at a rate of 50 X 10-5 win-1 The activated volume also was found to increase with the rate of metal removal. That the surface plays an important role in plastic-deformation processes has been adequately demonstrated.1-4 Of particular interest at this time are the observations4 that the creep rate of single crystals of fee metals is increased markedly when specimens are polished during the deformation process. These observations were interpreted in terms of a dislocation debris layer at the surface regions of the crystal. This layer, which appears to be a region containing a high concentration of dislocations or segments of dislocations, not only will impede the egress of dislocations on the primary slip system, but will also provide a barrier against which dislocations may pile up. By this means, a stress which opposes the motion of dislocations will be generated. It is considered that this stress must be taken into account in any theory which describes the plastic-deformation process. Although a detailed dislocation model cannot be given at this time, it may be stated that the stresses opposing the motion of dislocations arise from the dislocations in the debris layer, Ts, and ti due to the resistance to motion imposed by internal obstacles such as Lomer-Cottrell barriers, subgrain and grain boundaries, forest dislocations, and so forth, as well as the resistance due to the presence of jogs on dislocations and the interaction of the stress fields of dislocations, and so forth. In essence, we have added an additional term, ts, to the usual form of the equation T = Ta- Tb, where Tb is the back stress due to the various types of obstacles which impede the motion of dislocation. Accordingly, the net stress, t, acting on a dislocation may be written as where Ta is the applied shear stress. For deformation which occurs by a thermally activated process5,8 ?=Ae-u/kT = A e(u,-VT)/kT [2] and U = Uo- Vt PI where U = activation energy for plastic flow, y = shear strain rate, Uo = activated energy for plastic deformation in the absence of stress and depends upon the particular deformation process, V = activated volume, k = Boltzmann constant, T = temperature, OK, and A = frequency factor. From Eqs. [I] and [3], U = Uo- V(Ta - Ti - TS) [4] and it is seen that if Ts decreases, the activation energy, U, must decrease if V remains constant. However, as will be shown, V is a function of the surface conditions. In their work on aluminum, Lytton and coworkers7 reported that at low strains the activation energy was 3400 cal per mole and at high strains it was 28,000 cal per mole. The lower value was interpreted in terms of the energy necessary to overcome the Peierls force, while the higher value was associated with the energy necessary for dislocations to move by a cross-slip process. It will be shown that the lower activation energy is associated with the surface debris layer rather than with the Peierls force. EXPERIMENTAL PROCEDURE Single crystals having a nominal cross section of 1/8 in. and a 3-in. gage length were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The initial purity of the metals was 99.997, 99.999, and 99.999 pet for aluminum, copper, and gold, respectively. The orientation of the specimens is given in Fig. 1. The measurement of the activation energy as a

Jan 1, 1964

By A. U. Seybolt, F. J. Norton

A standard technique for heat treating small metallurgical samples where no appreciable contamination from the atmosphere can be tolerated is that of sealing small samples in evacuated fused-silica tubes. Since vitreous silica is relatively impervious to diffusion of gases, even at temperatures approaching the devitrification range, around 1100°C, this simple procedure has been very widely adopted as a standard technique in metallurgical research. Many workers have recognized that, with metals of fairly high reactivity, insulation from direct contact with the SiOz envelope is desirable in order to avoid displacement reactions of the type M + SOz-- MOz + Si(in M). It is not so generally known, however, that the &apos;rate of permeation of oxygen from the air through the SiOz enclosure at tem-

Jan 1, 1964

By John L. Burnett

Manufacture of lightweight concrete aggregate from common shale is one of the most rapidly growing industries in the field of nonmetallic or industrial minerals. Although expanded shale" has been in use since it was developed by Stephen J. Hayde in 1917, it was not until after World War II that it became a substantial competitor with other aggregates. There are some 70 plants now producing this aggregate in the United States, approximately half of them in states west of the Mississippi River. Expanding plants throughout the U. S. are grouped around major urban centers such as Los Angeles, New York, Chicago, and Denver. Concrete made with expanded shale aggregate combines the desirable features of low weight with relatively high strength, making it especially useful in concrete block, in structural concrete for multi-story buildings and in a variety of specialized concrete products such as prestressed panels and beams, and storage tanks. As the cost of construction continues to rise, lightweight concrete will probably be used in increasing quantities because of its low cost relative to the more traditional construction materials such as wood, brick and steel

Jan 1, 1964