By H. C. van Elst

Ultrahigh-speedphotographic and electronic meth-ods were applied to an investigation of details of brittle-fracture propagation in steel. The brittle fractures studied were obtained in steel plate with the aid of a Robertson apparatus. It was found that a brittle fracture proceeds by discrete steps ranging from 30 mm near the stop temperature to less than 2 mm at lower temperatures. The halting FROM prior metallographic observations of brittle fracture in steel' it could be concluded that the distribution of mechanical twins along a brittle fracture was similar to the distribution of mechanical twins induced by explosive deformation. It was therefore assumed that a running brittle fracture created stress waves, cf. Refs. 2-7. An emission of stress waves by a brittle fracture, however, seems only conceivable if the fracture propagates by discrete steps. For this reason a study of the details of times between successive steps drop in this tem-perature region from 20 usec to about 1 psec. The stepwise propagation mechanism is accompanied by an intermittent emission of stress waves of the order of 100 to 200 kg per sq mm. These stress waves seen1 to play an important role in the mechanism of brittle fracture as will be discussed. brittle-fracture propagation was undertaken to investigate the possible determination of the fracture steps and the emitted stress waves associated with the assumed mechanism. The more practical object of this work is the development of a test method for the determination of the ductile-brittle transition in small specimens. This has special advantages for the study of irradiation damage in steel. In this test method, which will be published in a following paper, the stress waves emitted by an actual brittle fracture are reproduced with explosive or electrical means and are then transmitted through small specimens at various temperatures. In the present paper only the results of the brittle-fracture study will be reported.

Jan 1, 1964

By B. J. Dalton

The Helium Research Center, Helium Activity, Bureau of Mines, is presently engaged in a critical examination of all of the PVT data on helium that appear in the literature. The long-range objective is the development of a single equation of state for helium that will allow all of the thermodynamic properties to be calculated and will reproduce all of the data within the accuracy with which the data are known. A preliminary objective is to obtain the best values of the second virial coefficients and to develop an equation that will reproduce the best values as a function of temperature. The method of treatment consists in expressing the PV product of a gas, for a given isotherm, in terms of a power series in either the pressure or the density and evaluating the constants by least squares solution. Associated with these functions whose coefficients have been evaluated by least squares, the following errors, or deviations, are of interest; the standard error of a single measurement; the standard error in each coefficient; and the standard error of the resulting function.

Jan 1, 1964

By L. C. Raymond

Good afternoon. I have entitled my talk "Investment for Progress," implying thereby a spark of friendly competition by private enterprise with such government-inspired foreign aid and investment programs as the Alliance for Progress. While the subject of foreign investment is hardly a new one, the perpetual flux of the political and economic surface of this earth we inhabit makes it forever timely and forever interesting. Especially do tremendous opportunities for international investment constantly present themselves to the mineral industry, and just as often must the industry approach these opportunities with a great deal of investigation and caution. This is not to say that the mineral industry--no less than any other industry--should be unenthusiastic about the foreign scene, but like everyone who proposes to put his money where his hope is, it should consider all the factors and weigh the possible disappointments as well as the rewards.

Jan 1, 1964

By O. M. Wicken

Magnesite has the unique combination of properties that make it useful in a wide variety of metallurgical applications. The use of refractory magnesite has been increasing throughout the world, but the source of the "ore" differs. The United States has increased production of synthetic magnesites while the rest of the world is exploiting its resources, using natural magnesites. The history and methods of manufacturing synthetic magnesite are discussed as well as the practices for beneficiating natural magnesite. The properties, costs, and uses of the two types of magnesite are discussed and compared.

Jan 1, 1964

The addition of a thallous salt to the cyanide leach of a calcined pyritic concentrate causes a marked increase in the"rate of extraction of gold. This probably is due to the activation of passive gold by.th,e. thallous ions'.''Lea'd, bismuth, and mercury salts, which should produce ' a, similai effect, fail to do so. It is postulated that'this latter result, together with'the reprecipitation of silver at low cyanide levels, is due to the presence of soluble sulphide. The use of thallous salts to reduce leaching time is discussed briefly.

Jan 1, 1964

By S. Weissmann, P. R. Swann, D. F. Wriedt

The sizes and density of precipitates in an intemally oxidized 0.19 wt pct Al-Ag single crystal have been determined by low-angle X-ray scattering and by transmission electron microscopy . The correlation in particle sizes measured by the two techniques is reasonably good. For an oxidizing temperature of 800°C the particles were found to INTERNAL oxidation of dilute alloys of aluminum in silver produces an oxide which has an excess of oxygen compared to Al2O3.' It is believed that the excess oxygen is an indication of the small sizes of the oxide particles. Depending upon the particular model chosen for the oxide structure, the size of the o-A1 particles can be calculated as a function of the oxygen-to-aluminum ratio. These calculations pre- have diameters in the range 30 to 140A, with a mean size of about 50.4 as observed by electron microscopy. At lower oxidizing temperatures, less than 600°C, no clearly resolved particles are formed, and it is suspected that if A1-0 clusters exist they must be exceedingly small, i.e., 10A or less in diameter. dicto that the particles would vary in size from 15 to 100A. This range of sizes is amenable to detection by both small-angle X-ray scattering and transmission electron microscopy. This paper compares the cluster sizes in such internally oxidized A1-Ag alloys determined by transmission electron microscopy and small-angle X-ray scattering. SPECIMEN PREPARATION Single crystals were prepared from 99.9999 pct Ag, obtained from Cominco Products, and 99.99 pct Al, obtained from Aluminum Co. of America. All melting operations were carried out in graphite molds under flowing purified hydrogen in a horizontal zone refiner. The silver was first degassed,

Jan 1, 1964

By J. A. Faucher

The mining industry has undergone significant technological advances in metallurgical process methods in recent years. The 1000 tpd concentrator of St. Lawrence Colum-bium Metals Corp. portrays the continuing effort made by the industry to achieve economical concentration of new and difficult ores. During the active search for sources of uranium in the early fifties, radioactive minerals were found in the Oka district near Montreal. The compatatively small quantities of uranium which were found occurred in association with widespread columbium (niobium) mineralization which included perovskite, a calcium titanate containing roughly 40% Cb2O5; niocalite, a silicate containing some 20% Cb2O5; and pyrochlore, a calcium niobate containing 45 -70% Cb2O5 as well as fluorine and some water. An idealized formula for one type of pyrochlore is: A typical chemical analysis of pyrochlore is shown in Table I. An important feature of this analysis is the lack of tin, lead, sulphur and P2O5 which conforms with the requirements of most consumers. In general the cerium content varies with sodium content and any increase in Ta2O5 lowers the Cb2O5 content of the concentrate. However, Ta2O5 rarely exceeds 0.5%. The carbonatite host rock of the columbium mineralization has the average mineral composition shown in Table 11. In Table 11, the term "diopside" is used to cover all silicates except mica which is shown separately because of the problems involved with its separation during the concentration process. In some ore zones, small quantities of rare earth minerals, such as monazite are present.

Jan 1, 1964

By Irving B. Cadoff, Alvin A. Machonis

The resistivity, Hall coefficient, Seebeck coefficient, and thermal conductivity were measured as a function of temperature for cation-rich alloy single crystals covering the composition range across the PbTe-SnTe system. Alloying of PbTe with up to 20 pct SnTe was found to have little effect on the energy gap. Above 20 pct SnTe the alloys were "p" type but below this range the sign could be varied by heat treatment. The lattice thermal resistivity of the compounds SnTe and PbTe is raised by alloying one with the other. Z values in the order the interesting values obtained. THE PbTe-SnTe system has several interesting features. For one, PbTe is a useful thermoelectric material and the possibility of improving its figure of merit by alloying with SnTe, an isomorphous compound, has been suggested since these pseudo-binary solid solutions generally have a more favorable ratio of electrical conductivity to thermal conductivity than either of the components.' Other interesting features relate to the conductivity mechanism, band structure, and stoichiometry of the compounds and their alloys. PbTe is a semiconductor with an energy gap of about 0.29 ev2 at room temperature whose conductivity sign and magnitude can be varied from "n" to "p" by controlling the proportion of lead and tellurium with respect to the stoichiometric ratio.3 Excess lead results in "n"-type conduction. SnTe is found to exist only as a "p"-type material of relatively high conductivity. This behavior is attributed to stoichiometric deviation by Brebrick4 but Sagar and Miller proposed that the behavior of SnTe must be due in part to the presence of an overlapped band. An investigation of alloys of this system, therefore, might give additional information which would permit one to evaluate which of the two proposals is the more appropriate one. Abrikosov et al.' studied the room-temperature electrical properties of these alloys and reported data for Seebeck coefficient and resistivity on poly-crystalline alloys. The present work is a more exhaustive survey of the PbTe-SnTe system. Re- sistivity, Hall coefficient, Seebeck coefficient, and thermal conductivity were measured over a wide temperature range for single crystals at 10-pct intervals of lead/tin ratio across the pseudobinary system. The relative concentration of tellurium was controlled so as to obtain metal-ion excesses in all cases. SAMPLE PREPARATION The crystals were prepared by melting elemental lead, tin, and tellurium in weighed proportions in evacuated Vycor capsules. The lead and tellurium were high-purity grades obtained from American Smelting & Refining Co. The tin was supplied by Comico. The proper calculated proportions of lead, tin, and tellurium were weighed and charged into prepared Vycor capsules prior to evacuation. The capsules were prepared from 15-mm Vycor tubing. A sharp point was worked on one end of the tube. A pyrolytic graphite coating was deposited on the Vycor walls by heating the tip to 800°C in an atmosphere of acetone-saturated argon. An additional coating of graphite was deposited on the pyrolytic coating from an Aquadag suspension. Above the coated tip the tube was reduced in diameter to form a constrictive neck. To avoid scratching the graphite coatings the charge was placed in the tube above the constriction. After a low-temperature bake, the evacuated capsule was sealed. On subsequent heating the charge melted down into the lower portion of the capsule. The crystals were grown by lowering the capsule through a Bridgman-Stockbarger furnace. The lowering rate was 1 in. per 8 hr. The upper portion of the furnace was set for 950°C and the lower portion for 800°C. In general the yield of single crystals was about 25 pct. The mixed compositions were, as expected, the most difficult to grow. The finished crystals were sectioned into 5/8-in. slices. The tip, end, and middle slices from each crystal were analyzed by X-ray fluorescence to determine the lead-to-tin ratio. The resulting values were used to plot a composition vs distance plot for each crystal. Slices were selected from each crystal, with the aid of the composition plots, to cover the complete range of compositions at 10-pct intervals. In general, the slices selected were taken from the seed end of the crystal where the longitudinal segregation (as determined from the X-ray fluorescence analysis) was a minimum. Laue single-crystal analysis and metallographic analysis was used to verify if a slice was single or polycrystal. Any grain boundaries were clearly visible in the as-cut and polished condition. In ad-

Jan 1, 1964

By Warren E. Morrison

INCREASED production and utilization of minerals fuels and power accompanied the overall expansion in U.S. economic activity during 1963, which saw continued advances toward higher production, employment, and purchasing power. During 1963, record levels of wages, profits, and consumption were attained, while costs and prices maintained the stability exhibited throughout most of the recovery period. Expanding industrial production, the average index of which went from 118.3 in 1962 to 124.3 in 1963, narrowed the gap of unused manufacturing capacity to an estimated 5 percent. Gross national product (GNP), another major indicator of economic activity, reached a record level of $583.9 million (current dollars) during the year, this being $27.7 billion, or 4.9 percent above 1962. These achievements were somewhat marred by unemployment, which remained at 5.5 percent of the labor force in 1963, and the continued deficit in the U.S. balance of payments. Against this general background, total national consumption of energy resources for the year was equivalent to 49,816 trillion British thermal units (Btu), an increase of 4.2 percent over 1962. This represented a somewhat lower rate of growth than for GNP during the year.

Jan 1, 1964

By Mrs. V. J. DeCarlo, G. P. Salvo, H. W. Schadler, L. M. Osika

The lattice parameter of the inlerrnetallic compound Nb3Sn has been measured as a function of temperature from 80° to 1290°K. The results are compared with published data on the thermal ex- ThE recent interest in the intermetallic compound, Nb3Sn, as an engineering material for the production of superconducting devices has necessitated that certain engineering data be obtained. Because of the difficulty encountered in producing bulk pansion of niobium and indicate that the compound when made by diffusion of tin into niobium at 1000°C, would be subjected to a tensile strain of about 0.1 pct when cooled to room temperature. material which is single phase, the coefficient of thermal expansion has not been measured by dilata-tional methods. Therefore the lattice parameters of fine-grained samples of Nb3Sn produced on the surface of a niobium sheet by heating in molten tin at 950°C have been obtained as a function of temperature. The results are compared with published data on niobium2 and Nb3Sn3 and with lattice-parameter measurements made on small single crystals of Nb3Sn.

Jan 1, 1964

Jan 1, 1964

By A. A. Brant

In this presentation, concepts of the formation and evolution of the universe, the earth, and the cyclic civilizations of man are broadly outlined. The 5 billion or more years of the universe and the 4% billion years of the earth are contrasted to the 5000 years of modern society and the 100 years of objective scientific breakthrough. THE UNIVERSE Let us start back as far as possible, to the beginnings of this universe, some 5 billion or more years ago. This is a time interval that can be crudely underestimated by the moon-earth tidal friction effects that have increased the length of the day by about 1/1000 second per century — from a 5 to 7 hour day to its present 24 — and have moved the moon away at 5 inches per year to its present 240,000 miles. The oldest stony meteorites from interplanetary space give an age dating of some 4.6 billion years, approximating the time of formation of our earth. Further, certain stars pulsate, the period of pulsation being related to their absolute brightness. Measuring apparent brightness and comparing, gives the distance away. Thus Hubble and Shapley of Harvard, from 1925 on, were able to show that the universe reached as far as our telescopes could scan. The Doppler shift of the hydrogen red lines could only mean that the nebulae, or galaxies, were moving away away at velocities increasing with their distances, by 180 km/sec velocity increase for every million light year's distance. In short, the universe is expanding like an exploded bomb. Comparing the velocity increase per million light year's distance again indicates a zero time of some 5 billion years' Thus it appears that this universe had a finite beginning. Physical measurements and present theories permit some picture of our universe's birth. We know since Einstein that many forms of energy are equivalent, e.g., mass, and electromagnetic radiation, aspects of which are heat and light. Now with expansion, radiation density or equivalent mass decreases as a length factor to the 4th power, while mass as matter decreases at a length factor cubed. The temperature in outer space is now perhaps 100° absolute and the radiation mass equivalent is but 1/1000 the rarefied interstellar gas densities. Decompressing the universe to a starting point, however, raises temperature more rapidly than mass density, and results in a high radiation mass energy fraction, which since it is proportional to temperature to the 4th power suggests a zero point temperature of several billion degrees, brighter than any sun. "Let there be light and there was light," according to Genesis 1-3. Now what further initial conditions must there be to explain the relative abundance of the elements in the universe, which by spectral analyses of the earth's crust, stony meteorites, and the sun and stars is surprisingly uniform throughout. Some 55% of all cosmic matter is hydrogen, some 44% is helium and only 1% is made up of all the heavier elements in much the same proportions as on earth. These latter decrease logarithmically in abundance up to atomic weight 100, then level out. This consistent abundance distribution of elements in the universe may be generally explained by taking at Time Zero a hot neutron gas of density about 10-3 grams per cc, at a temperature of several billion degrees Centigrade, with a high radiation energy fraction. Generally neutrons break down into positrons and electrons within about ten minutes, but at the initial high temperature and radiation pressure would recom-bine. However, with rapid expansion and decrease of temperature and pressure, the neutron disintegration would run uncompensated and aggregation would result from neutrons and protons uniting in different degrees of complexity. The total calculated element aggregation time would be about one hour while the temperature still remained above one billion degrees. The element abundances formed would depend on density of the nuclear gas, simplicity of the atom formed, and the neutron capture cross section. Thus a higher density

Jan 1, 1964

By William A. Beck

This report describes the loading and transportation practices employed at the zinc-lead mines of The Eagle-Picher Co., Jo Daviess County, Ill., and Lafayette County, Wis. The report also gives a brief history of the Illinois-Wisconsin zinc-lead district and the operations of the company in the area. The diesel-powered, rubber-tired loading and haulage equipment is described and illustrated from the operational point of view only, and an analysis is made of the materials-handling system without going into health and safety factors. The costs per ton of the various components of mechanical loading, underground haulage, underground crushing, and hoisting for fiscal year 1960 are tabulated.

Jan 1, 1964

By Horace Pops

ThE shape of the primary solid-solubility limits in copper-rich Cu-Si-Zn alloys has been discussed recently1 in terms of the atomic size effects and the electron concentration, e/a. Although these limits are parallel to lines of constant e/a near the Cu-Zn binary system, they deviate and become sharply restricted near the Cu-Si binary system. Hence, it appears that the primary solid solutions with higher silicon contents are restricted by the presence of the intermediate phases, [, X, and p, which follow them in the ternary system. owever, a similar restriction in solid solubility might also result from an interaction in the copper matrix between silicon and zinc. Evidence for such possible interactions has been observed, for example, in the Al-Mg-Si systion.A where a contraction of lattice spacings in the ternary solid solution appears to correspond to an electrochemical interaction between the two solute elements, magnesium and silicon. The observed contraction is associated with restricted solid solubility. It was also shown1 that the extent of the primary solid solubility did not follow the trends predicted by the lattice-distortion oncept." This again suggested that the solubility limits are strongly affected by the stability of the intermediate phases, I, 1, and X . In order to test the above hypotheses, lattice-parameter measurements of the fcc @-phase alloys were determined within the ternary system at a constant electron concentration (e/a = 1.30) and also at a constant zinc content. Alloys of predetermined composition were prepared from high-purity metals and melted and cast under reduced pressures of helium in quartz capsules. Since the weight losses were very slight and did not exceed one part in 2000, the nominal compositions listed in Table I were accepted without chemical analyses. The ingots were homogenized

Jan 1, 1964

By Avnulf Muan, P. V. Riboud

The effect of Cr2O3 on melting relations of iron oxide at oxygen pressures slightly above those prevailing in contact with metallic iron has been determined. Liquidus and solidus temperatures of wüstite are raised by the addition of Cr2O3, from 1385°C for pure iron oxide to 1420°C at the peri-ledie point where wüstite, iron chromite, liquid, and gas coexist in equilibrium under the atmospheric conditions used in the present investigation (CO2/H2 = 1). It has been shown in a previous investigation1 that the liquidus and solidus temperatures of iron oxide are drastically increased by the addition of Cr2O3 under the relatively oxidizing conditions prevailing in air. This is to be expected in view of the easy substitution of cr3+ for Fe3+ in crystalline oxide structures which are stable at high oxygen pressures, as demonstrated for instance by the completeness of the solid solution series Fe2O3-Cr2O3 at high temperatures (>1000°C). The stable phase of iron oxide at oxygen pressures approximating those prevailing when metallic iron is present is wüstite. This phase, although commonly represented by the simplified formula FeO for sake of convenience, in reality has a defect structure in which a part of the iron ions are present as Fe3+. It is to be expected that at least a limited amount of cr3 ions will substitute for Fe in this structure when Cr2O3 is added to wüstite. Depending on the ease of this substitution in comparison with that of cr3 substitution for Fe in iron oxide-Cr2O3 liquids under the same atmos- pheric conditions, the liquidus and solidus temperatures of wüstite may increase or decrease upon addition of Cr2O3. The methods of establishing these melting relations and the results obtained are presented in the following. I) EXPERIMENTAL METHOD 1) General Procedure. The quenching technique was used in this study. Oxide mixtures were heated at chosen constant temperatures in an atmosphere consisting of equal parts of CO2 and H2 until equilibrium was established among gas and condensed phases. The samples were then quenched in mercury to room temperature, and the phases present were determined by microscopic and X-ray investigation. 2) Preparation of the Mixtures. Starting mixtures were prepared by weighing and thoroughly mixing Fe2O3 and Cr2O3, or wüstite and Cr2O3. The Fe2O3 and Cr2O3 used were "Baker Analyzed" reagent grades, whereas wüstite of composition was synthesized by reducing Fe203 at 1325°C in an atmosphere consisting of equal parts of CG andHz. In order to avoid contact with crucibles, the equilibration runs were made with small pellets suspended from thin (-0.004-in.) platinum wires. Mixtures made from FOs and Cr203 were readily pelletized at a pressure of 500 atm in a 9.5-mm die, whereas mixtures made from wüstite and Cr203 when treated identically were too weak for handling. In order to obtain a stronger product, these pellets were sintered by heating for 2 min at -1200°C in the same atmosphere as was subsequently used for the equilibration runs (CG/H2 = 1:1). During the sintering, these pellets were wrapped in thin (0.0004-in.) platinum foil, which was stripped off before the equilibration runs. In order to reduce the time needed for equilibrium to be attained, preliminary equilibration of relatively large pellets of each mixture was carried out at -1200°C for 4 to 12 hr. Smaller pellets

Jan 1, 1964

By S. J. Hruska, G. M. Pound

The critical supersaturations for appreciable nucleation rate of cadmium crystals on copper and glass substrates at 186°Kwere measured as a junction of thermal-beam energy over a range of source temperatures between 616" and 839OK. There was no effect of source temperature on critical super saturation. This implies that the adsmbate prior to nucleation is in thermal equilibrium with the substrate. THE deposition of metallic vapors on solid substrates has been found to exhibit a critical behavior in that the rate of formation of deposit increases markedly when the intensity of the vapor source is increased slightly.* Evidence of the ability of sub- where Je is the flux which would arrive if the substrate were equilibrated with bulk condensate at the adsorbate temperature. The following work was undertaken to test this hypothesis. A) Energy Exchange Between Metallic Vapor and Substrates. When a freely translating atom collides with a stationary solid body its energy and momentum undergo changes which determine whether the atom is reflected or adsorbed. An atom is considered to be reflected if it returns to a freely translating state after remaining under the influence of the body for only a time comparable to the period of oscillation of atoms on the surface. An atom which remains for a longer time is said to be in an adsorbed state. The parameter which describes the energy transfer occurring at the interface is the thermal-accommodation coefficient which may be defined in terms of energy as Ei = average energy of impingent atoms, Eeq = average energy of an emergent atom which has equilibrated with the substrate, and Eem = average energy of an emergent atom. If a temperature is assigned to each of these energies, we have at as defined by Knudsen.2 Since this allows no distinction between reflected and evaporated atoms, a more specific definition is introduced for the present purposes, namely 71 = probability that an impingent atom is transferred to an adsorbed state, aj = thermal-accommodation coefficient for reflected atoms, and aTc = thermal-accommodation coefficient for adsorbed atoms. During a time t,, the mean stay time, prior to evaporation the adsorbed atom (adatom) will interact with the substrate and this will have the net effect of transferring the adatom towards a state of

Jan 1, 1964

By Kenneth B. Higbie

METALLURGICAL ACTIVITY in 1963 was again dominated by the insatiate demands of research and development conducted in conjunction with the nation's defense and aerospace programs. An increasing effort was noticeable throughout the year, however, to apply to the commercial field many of the processes and techniques that have been developed by government-sponsored research. Particularly effective has been the Industrial Applications Program of the National Aeronautic and Space Agency through which many of the technological advancements made during the course of NASA research and development have been published and released to the public. POWDER TECHNOLOGY Powder metallurgy techniques for fabricating metals, not long ago declared outmoded because of improved casting and shaping methods, have since made an astonishing comeback. Traditionally mechanical pressing of powder shapes has been employed when melting and casting was difficult or impossible, when phase relationships needed to be sidestepped, or when machining costs could be avoided. Hence, it has long been used for producing relatively small special shapes of high-melting metals and alloys. Small iron parts produced with a punch and die have been common for many years, but powder metallurgy techniques are now applicable to a wide range of materials and items. Hard-to-handle materials including refractory metals and their alloys are now rolled, forged, or extruded from billets made by sintering isostatically compacted powders. The major element of the powder metallurgy industry still comprises iron shapes, however, and two-thirds of the annual 100,000 tons of powder metallurgy products are made of iron. The largest single user of powder-forming techniques is the automobile industry which currently consumes 14,000 to 16,000 tons of iron powder per year. A typical 1963 model auto contained more than 100 pressed powder parts (e.g., transmission gears, timing gears, sprockets, ball joint suspensions) totaling 5 to 7 pounds per car. Some of these powders are used in self-lubricating parts of porous copper and copper alloys containing as much as 20 volume-percent lubricating oil. The expanded use of powder techniques, coupled with

Jan 1, 1964

By N. A. Warner

Dense cylindrical specimens of artificial hematite were reduced in hydrogen over a range 0-f total pressures between 0.1 and 1.0 atm and temperatures between 650" and 950°C. Hydrogen reduction at a total pressure of 1.0 atm in the presence of a chemically inert diluent and reduction in hydrogen/water mixtures were also studied Znter.face movement during reduction was followed using metallographic techniques. Substantiu1 partial-pressure gradients are shown to exist in both the gas film and the reduced iron layer. The results are consistent with a mixed-control mechanism involving an interaction of gaseous-difusion effects with a first-order reversible chemical reaction at the iron/wüstite interface. Over the hydrogen-pressure range of 0.1 to 1.0 atm, the rate is not directly proportional to the hydrogen pressure in the bulk gas stream. Nitrogen dilution of the reducing gas masks the true effect of hydrogen partial pressure by influencing the effective molecular dif-fusivity and gives an apparent first-order relationship. The transport of hydrogen and water vapor across the iron layer is consistent with molecular gaseous diffusion rather than a Knudsen diffusion mechanism. ALTHOUGH the literature on the reduction of iron oxides is very extensive, it is only comparatively recently that a definite quantitative model for the reduction of hematite has been proposed. This development has been largely due to the work of McKewan. An extensive literature review of previous work has recently been compiled by Themelis and Gauvin. Exclusive control by gaseous diffusion in the reduction of hematite has been recently advocated by Kawasaki and coworkers.' Although the results of the latter workers are of considerable practical significance, the extreme porosity (approximately 30 pct) of their specimens precludes their application to a kinetic evaluation of the reduction of dense polycrystalline hematite. The salient features of the kinetic model used by McKewan for the gaseous reduction of dense hematite at temperatures in excess of 560°C (when FeO is stable) are: 1) The reduction is a topochemical reaction taking place through 'the series FeO/FesO4/FeO/ Fe; 2) The gas-solid type of reaction takes place only at the FeO/Fe interface and the internal reduction: FeO proceeds by solid state diffusion; 3) The iron layer formed is quite porous and offers negligible impedance to gaseous diffusion; 4) The rate-controlling step in the reduction is a chemical process occurring at the Fe/FeO interface. In view of the relatively fast reaction rates involved when hematite is reduced in a stream of hydrogen, it seemed possible that the simplifying assumptions of negligible diffusional resistance in both the bulk gas phase and the reduced iron layer could introduce serious errors in the interpretation of experimental reduction data. The present work was initiated to elucidate the effect of gaseous diffusion on the reduction rate and to determine its possible influence in the formulation of the reaction mechanism at the metal/oxide interface. EXPERIMENTAL Procedure and Apparatus. Dense cylindrical compacts of artificial hematite were prepared by sintering pressed compacts of reagent-grade ferric oxide, containing 99.6 pct FezO, in air at 1200°C for 80 hr. The resulting compacts had a final porosity of less than 2 pct and a height and diameter of approximately 1 cm. Variations in sintering atmosphere from air to pure oxygen, in sintering time from 20 to 80 hr, and temperature from 1150" to 1250°C had no effect on the subsequent reduction behavior. The reduction of the samples took place in a vertical tube furnace in which was placed a 1-in. transparent silica tube. The 24-in. heated length

Jan 1, 1964

The system of keeping geological plans and sections for the Geco Mine at Manitouwadge, Ontario, is described. Special methods employed to save draughting time with-out sacrificing accuracy, such as the extensive use of black line prints, are discussed. The uses made of the plans and sections by the mine planning engineers in their designs of stopes, and by the blast-hole engineer in ~is preparation of blast-hole layouts, are noted. An unusual scheme for portraying the distribution of .copper, zinc and silver values within the ore zone is de-scribed. The method of estimating the grade of ore to be "blasted in each ring of blast holes is outlined, as is the method of estimating the annual ore reserves. The design of an effective but simple transparent geo-logical and mine development model, used as a display for -visitors, is discussed. A large-scale model used for the study of problems in geological structure is also de-scribed.

Jan 1, 1964

THE metal iron has physical arid chemical properties which are some- what different from those of steels, but a knowledge of the pure metal is a useful starting point in studying the behavior of steels. Solid iron exists in two different crystalline forms, called alpha (a) and gamma (?) iron the former being the ordinary form at room temperature. When heated above the "A2 point," 769 C (1416 F), the metal becomes nonmagnetic, and at the "A3 point," 911 C (1672 F), it undergoes a change in crystalline form to become gamma iron. 111 the range 769 to 911 C, it is sometimes called beta (ß) iron to distinguish it from the magnetic alpha, but the two are identical in crystal structure. When gamma iron is further heated to 1392 C (2538 F), it changes into delta (d) iron, which is identical with beta or nonmagnetic alpha iron. Pure iron melts (in an inert atmosphere) at 1536 C (2797 F); the melting point is generally lowered by alloys or impurities. PHYSICAL AND THERMAL PROPERTIES OF IRON Many of the properties of iron undergo abrupt changes at the transition temperatures.1 For example, in heating through the A3 point, a sudden shrinkage in volume occurs. Similarly, melting is attended by sharp physical changes such as an increase in volume. Table 16-1 contains a summary of the measured physical properties of pure iron at several temperatures. Usually the properties change smoothly with the range of stability of a given form, but this is not always true. For ex- ample, the specific heat reaches a sharp maximum at the A2 point al- though no transformation occurs. (See Fig. 14-1.) Solvent Powers of Liquid Iron. Liquid iron is capable of dissolving most of the other metals and many nonmetallic elements as well. Of the metals that are liquid at the melting point of iron, only lead, silver, and bismuth refuse to dissolve to an appreciable extent. Table 16-2 contains a list of the common elements classified with respect to their solubility in liquid iron. Those which are very soluble or practically insoluble require no further discussion, but several of the nonmetals that are gases and exhibit limited solubility are of considerable importance to us and merit more detailed consideration.

Jan 1, 1964