Search Documents

By R. H. Hiltz, N. J. Grant

Solid-solution titanium-cerium alloys, cold-rolled to 0.010 in. thickness, and annealed, were internally oxidized to produce a fine dispersion of CeO2 in the titanium matrix. The oxidized alloys were cut into sheet stress-rupture specimens and tested for rupture life at 426°C, 538°C, and 648°C. There was noted an improvement in strength over that of pure titanium, the internally-oxidized alloys showing curves with a much flatter slope on the log stress—log rupture life plot, characteristic of the stable metal-metal oxide class of alloy. DURING the past 3 to 4-year period, considerable interest has been aroused by the potential offered by alloys based on the ultra fine dispersion of a hard insoluble phase in pure metals or solid-solution alloys for use at high temperatures. The impetus to the development and study of such alloys was provided by Irmann.1,2 through the success of the SAP alloy (pure aluminum containing about 12-14 volume pct of A12O3). Subsequent studies have thrown light on the true potential of this class of alloys in the remarkable stability of the structure after long-time exposure at high stresses and high temperatures.a-5 While success has been demonstrated in the special case of the A1-Al2O3 alloys, and more recently

Jan 1, 1959

By J. O. Betterton, W. K. Noyce

I~JTI HE work on the indium-zirconium system is part A of a larger investigation of zirconium-phase diagrams with solute elements, silver, cadmium, indium, tin, and antimony, which is intended to provide information about the metallic valency of zirconium. The system is an ideal example since the sizes of indium and zirconium atoms are nearly the same, and the solute and the solvent occur in the same row of the periodic table. The only solute from Group III B which had previously been added to zirconium was aluminum' and it was of interest to determine whether indium would dissolve appreciably in alpha zirconium and stabilize this phase in the same manner. Experimental Procedure The experimental methods used in the indium-zirconium work are similar to those described earlier for the silver-zirconium system.' Reactor Grade 1 iodide zirconium of 99.95 pct purity* and indium of 99.99 pct purity were arc cast, and then annealed in silica capsules with protective foils of zirconium and molybdenum. Annealing temperatures and times varied from 1 day at 1300°C to 43 days at 550°C. The compositions of the alloys were detcrmined by an individual chemical analysis of the actual metallographic specimens after two or more sides were examined to insure the absence of solute segregation. Calibrated thermocouples were used throughout, and the uncertainty in the temperatures reported, owing to calibration error, furnace control, and measurement of the small temperature gradients near the capsules, is believed to be well within ±2°C. Typical impurities in the alloys were found by a neutron-activation analysis of four different alloys. The results are given in Table I where the ranges of values will be seen to compare favorably with the usual values for iodide zirconium. With respect to oxygen, nitrogen, and carbon the absence of any unusual amount of these elements compared to iodide zirconium was indicated by the alloy hardness values, since hardness is increased sharply by the presence of these elements. The value for 0 pct In, obtained from the alloys by extrapolation, is 58 2 7 VPN which is in the low part3 f the normal range of hardness found in iodide zirconium. Results of the Experiments The zirconium-rich portion of the indium-zirconium phase diagram from the annealing experiments is shown in Fig. 1. Indium was found to

Jan 1, 1959

By C. Feng, C. Elbaum

AN investigation of the fracture plane of titanium, containing 0.5 wt pct to 1 wt pct 0, was recently carried out by fracturing large-grain specimens in a tensile jig at room and liquid air temperature. The experiments were carried out on strip specimens 3 to 5 mm wide, 2 mm thick and about 100 mm long. The specimens consisted of several grains, each occupying the entire cross section of the strip and extending over a length varying from 5 to 20 mm. These specimens were prepared by a method described elsewhere.' The identification of the fracture plane was possible in twelve of approximately thirty crystals investigated. In some cases severe local distortion took place near the fracture and prevented identification of the fracture plane. On, at least, three occasions the fracture propagated in a helicoidal

Jan 1, 1959

By E. Buehler

THE floating zone refining technique'-4 has provided a new experimental approach to the purification of many reactive materials especially those with high melting points. The method avoids the use of a crucible and at the same time it provides a favorable environment at the freezing interface for the growth of single crystals. The physical properties of refractory metals such as molybdenum and tungsten have long been of interest from a fundamental point of view and because of their widespread use in vacuum electronics. Single crystals are often desirable for study. Prior to the introduction of zone melting, single crystals of these metals were usually grown in the solid state at temperatures slightly below the melting point by strain annealing3 or by the application of a moving temperature gradient. Such techniques were mostly successful on wires, ribbons, or rods having small cross-sectional areas. Recently, larger samples of tungsten, molydbenum, tantalum, columbium, and rhenium were melted by a floating zone process which employed electron bombardment heating.10 Single crystals were obtained in many instances

Jan 1, 1959

By D. J. Mack, J. A. Mullendore

MUCH work has been reported in the literature on the separation of individual phases in steels, particularly carbides, for the purpose of structural and chemical analysis. The methods usually involve separation of the particles from the matrix by chemical or electrochemical methods. Another .group of alloys ideally suited for selective removal of one phase is the commercial aluminum bronzes. Al-

Jan 1, 1959

By J. W. Downey, A. E. Dwight, R. A. Conner

THE MgCu2 type Laves phase has been observed in the thorium-osmium and thorium-iridium systems. Two alloys corresponding to ThOs2 and ThIr, were prepared by arc melting a 5-g charge in a water-cooled copper. crucible. Both alloys were very brittle. X-ray diffraction patterns were obtained using filtered Cu and Co radiation with a Straumanis-type DeBye-Scherrer camera. The a,, values as shown in Table I were obtained by a Nelson-Riley extrapolation. The structure belongs to space group Oh7-Fd3m. Relative intensities for each of these compounds were calculated on the assumption that 8 thorium atoms occupy (a) positions and 16 osmium or irid-ium atoms occupy (d) positions. The calculated intensities are the product of the Lorentz-polarization factor, the multiplicity factor and F', the structure factor, neglecting the absorption and temperature

Jan 1, 1959

By J. Gurland

A method of measuring the degree of contact between grains of 1 phase in multiphase alloys is derived. It is shown that the number and the areas of contacts between grains can be determined by metallographic analysis. Relations between the area of contact, the dihedral angle, and the mean free path of spherical grains are developed. It is often desirable to interpret the mechanical behavior of alloys in terms of structural features observed under the microscope. A quantitative description of microstructures of multi-phase alloys requires consideration of geometrical and topological factors such as the amount, size, and shape of grains and the continuity of the constituent phases. The number and dimensions of grains may be metallographically determined by applying the methods described by Smith and Guttman1 and by Fullman2 in their papers on the measurement of particle size and internal boundaries in opaque bodies. The present work intends to show that the same methods can be used to evaluate some of the parameters of phase continuity; namely, contiguity, number of contacts, and areas of contact of grains of 1 phase. Application of these concepts may be found in such problems as the calculation of electrical conductivity of 2-phase alloys, or the evaluation of the length of fracture path through grains of a brittle phase more or less dispersed in a matrix. I. DEFINITION The following definitions and derivations are based on 2-phase alloys, of which the units of the microstructure are grains. Contiguity is defined as the average fraction of surface area shared by 1 grain of a phase with all neighboring grains of the same phase. In a 2-phase alloy of constituents A and B, the contiguity of phase B is given by: where Cb is the contiguity of phase B aBß is the average area of contact between a grain of phase B and adjacent grains of phase B, aAB is the average area of contact between a grain of phase B and adjacent grains of phase A. The contiguity is a measure of the average degree of contact between grains of phase B in the 2-phase mixture. The ratio varies from 0 to 1 as the distribution of phase B changes from a completely dispersed to a fully agglomerated structure. Smith and Guttman1 have shown that the relative areas of 2 kinds of interfaces in a volume are directly proportional to the number of interfaces of each type intersected by a random line. The lines can be drawn on metallographically prepared surfaces as long as these are random sections through the sample. The contiguity ratio of phase B then becomes: Cb = 2NBB/NAB + 2N BB [2] where: NBB is the number of interfaces between grains of phase B intersected per unit length of random line. Nab is the number of interfaces between grains of phase B and grains of phase A intersected per unit length of random line. The factor 2 arises in Eq. [2] because each interface B-B is associated with 2 grains of B-phase, whereas the interface A-B involves only 1 grain of B-phase. The calculations of contiguity do not require any assumption as to volume fraction, particle size, or particle shape. Fullman2 gives an expression for the determination of the mean free path between particles. The mean free path PB between grains of phase A, i.e., through grains or agglomerates of phase B, may be found from the relationship: PB =2fB/NAB [3] where fB is the volume fraction of phase B. The calculation of the mean free path is independent of grain shape and grain size distribution. The calculation of the number of contacts and of contact area requires assumptions of grain shape, grain size, and contact shape. In the case of uni-

Jan 1, 1959

By T. F. Archbold, R. E. Grace

The use of interference colors is the simplest experimental way to determine the approximate film thicknesses of oxides formed on liquid metals. A large amount of data under various conditions can be obtained easily and quickly. The oxidation of liquid lead has been studied by several investigators,1-5 but all of these studies have been on thick oxide scales. The purpose of- this work was to investigate the range 0 to 2000A film thickness. By using electron diffraction, Jenkins concluded that the surface of the film on molten lead is yellow orthorhombic PbO with the (110) planes parallel to the surface. This was confirmed by Shimaoka and Yamai7 who also used electron diffraction from the melting point of lead to 730°C. The rate of oxidation of pure liquid lead in air was measured in the temperature range 453" to 643°C by observing the rate of formation of interference colors on static lead baths. Approximately 170 g of lead (99.999 pct) was placed in a refractory dish having a working surface of 13.8 sq cm. This crucible was placed in a deep-well resistance furnace open to the atmosphere. The times at which the various interference colors appeared, after wiping the molten metal surface clean, were determined at 453", 533°, 600°, and 643°C. Elapsed times were determined with a stopwatch and all colors were estimated by eye. Bath temperatures

Jan 1, 1959

By E. S. Bartlett, D. N. Williams

QUANTITATIVE values for the oxidation rate of unalloyed molybdenum in air at temperatures above the melting point (1460°F) of the characteristic oxide are contained in the literature as a result of previous investigations. Lustman' reported values corresponding to 0.36 in. penetration per day (IPD) at 1500 and 1600°F in still air, noting essentially no variation in rate with temperature. Jones, Spretnak, and Speiser' reported values corresponding to 0.14 and 0.13 IPD at 1500 and 1800°F, respectively, in still air, attributing the decreased oxidation rate at higher temperatures to a lesser accumulation of the corrosive molten oxide on the surface at the higher temperature as a result of increased volatilization rate. Harwood3 ecently summarized work in the field, presenting generalized data corresponding to 0.48 to 0.96 IPD at 1800°F and 0.55 to 0.83 IPD at 1700°F in slowly flowing air. In a recent program at Battelle, it became desirable to know more about the characteristic oxidation behavior of molybdenum under varying conditions of temperature and atmosphere. Using oxidation-test apparatus designed for dynamic, continuous recording of weight change during testing,' values for the oxidation rate of molybdenum were obtained at temperatures from 1400 to 2150°F. In addition the effect of air flow on the oxidation rate was studied briefly at temperatures of 1600, 1800, and 2000°F. Exhaust of the contaminated atmosphere from the oxidation chamber was effected by an impeller pump attached to a 3/16-in.-diam opening in the oxidation chamber. The volumetric exhaust rate (cubic feet per hour) was normally maintained slightly in excess of the input rate to avoid condensation of MOO,,' on the sample suspension rod. The entering atmosphere was preheated prior to admission to the oxidation chamber by a 1 1/2-in.-diam cup packed with shredded asbestos. The experimental data are presented in Table I. Comparing conditions 2 and 3 (taking into account the temperature difference) and conditions 8 and 9. shows that in the absence of forced exhaust an atmosphere of moving air results in greater oxidation rate than a stagnant atmosphere. The use of forced exhaust, as shown by comparing conditions 3 and 4 and conditions 14 and 15: resulted in an even greater increase in oxidation rate. By virtue of the size of the atmosphere input and exhaust openings, it was calculated that the exhaust velocity was about 60 times that of the input velocity for essentially equal volumetric flow rates. Because of the proximity (about 3/4 in.) of the exhaust port to the specimen, it is logical to assume that cleansing of the atmosphere immediately surrounding the specimen was accomplished much more efficiently by the exhaust flow than by the input flow at a constant-volumetric flow rate. Also, it can be seen by comparing conditions 4 through 7 and conditions 11 through 13 that increasing the rate of atmosphere flow (by increasing input velocity with a proportional increase in exhaust velocity) above some optimum value has little, if any, further effect on the oxidation rate. These results suggest that there is a maximum oxidation rate for molydenum at a given temperature which is obtained when conditions are maintained such that the partial pressure of MOO3 in the atmosphere surrounding the specimen is at a low value. By controlling the partial pressure of MOO, surrounding the sample, it is possible to control the rate of volatilization of MOO:, from the surface. This, in turn, affects the rate of oxidation, since the thickness of the MOO3 layer determines the amount of oxygen which will be able to reach the reaction surface.' When the liquid oxide layer is less than some critical thickness, i.e., when the volatilization rate is high, enough oxygen is transported to the active surface to permit oxidation to proceed at the maximum rate allowed by the kinetics of the oxidation reaction. However, if the volatilization of MOO,, is suppressed, the thickness of the layer of MOO3 on the surface increases, and the diffusion of oxygen through the oxide layer becomes the rate-controlling step in the oxidation process. The lack of agreement between the present results and those of previous investigators is presumed to be due to differences in removal of the oxidation product (Moo,) from the immediate vicinity of the sample. By comparing conditions 1, 5, 10, 12 and 14, it is seen that when forced exhaust was used the oxidation rate of molybdenum increased with increasing temperature. A rapid increase was observed between 1400 and 1600°F, attributable to the effects

Jan 1, 1959

By G. A. Alers, J. H. Bechtold, R. W. Armstrong

The plastic flow of .molybdenum was studied in compression at temperatures below the ductile-to-brittle transition in tension. It was found that molybdenum is ductile in compression at all temperatures down to —196°C. The yield strength continues to increase with decreased test temperature below the tensile ductile-to-brittle transition temperature range. Difficulty was encountered in correlating the experimental data obtained with existing theories of plastic flow. THE body-centered-cubic metals as a group show a rapid and very large increase in yield strength with decreasing test temperature.' It is of fundamental importance to the understanding of the mechanism of plastic flow that this general characteristic be examined carefully. Unfortunately, brittle fracture in low-temperature tensile tests prohibits the measurement of flow properties at very low temperatures. By using compression tests, fracture can be suppressed and the plastic flow of the bcc metals can be studied far below their tensile ductile-to-brittle transition temperatures. Molybdenum was chosen for this experiment and plastic-flow data were obtained down to —196°C.

Jan 1, 1959

By A. H. Daane, J. J. Hanak, F. H. Spedding

IN the study of the rare earths at the authors' laboratory, methods have been devised for preparing pure rare earths and many of their properties'- have been determined. Very little information is found in the literature on the properties of europium metal, which is the scarcest of the naturally occurring rare earths. Since we have recently prepared europium in appreciable quantities, we are in a position to describe the method of preparation and some of the properties of this metal. Metallic europium was first prepared by Klemm and Bommera who heated a mixture of potassium and EuC1, in vacuo, and obtained a mixture of europium metal and KC1. Trombe4 electrolyzed a molten salt bath containing NaC1, KC1 and EuC1, and collected the europium in a molten cadmium electrode as a cadmium alloy. The cadmium was subsequently removed by distillation but the properties of the residue indicate that pure europium was not obtained. McCoy attempted to prepare europium by distilling mercury from europium amalgam, but the stability of the Eu-Hg intermetallic compounds prevented a complete separation of the two elements. The preparation of very pure europium was suggested by previous work in this laboratory1,4 in which ytterbium and samarium were prepared by heating the respective sesquioxides with lanthanum metal turnings to 1450°C in vacuo and distilling ytterbium and samarium from the mixtures. Subsequently, small test experiments showed that europium also could be prepared by this method. A more detailed version of this method was used in the work described in this paper. Klemm and Bommer3 found by X-ray analysis that the metal had a body-centered cubic (bcc) structure with a lattice constant a, = 4.582 ± 0.00A (converted from kX units), with a bulk density of 5.30 g per cu cm. They found europium to be weakly ferromagnetic. Spedding, et al,7 found a,, to be 4.606 ± 0.001A. Barrett' showed that the bcc structure persists throughout the temperature range 5 to 3000K with a, at 5, 78, and 300°K being 4.551 ± 0.003, 4.551 ± 0.004 and 4.577 ± 0.001A, respectively. Trombe1 described europium as being iron gray, malleable, about as hard as neodymium and not attacked by cold water. He estimated the melting point to be between 1100 and 1200°C. Previous work in this laboratory indicated that the pure metal corrodes rapidly in air and reacts with cold

Jan 1, 1959

By P. G. Shewmon

THIS paper is concerned with the redistribution of a second phase when a 2-phase solid alloy is annealed in a temperature gradient. An examplewhich is discussed in detail is the redistribution of carbides in a low-carbon steel annealed in a temperature gradient below the A, temperature. As a result of such a treatment, the carbides at the cooler side disappear, while those at the hotter side grow in size. In a 2-phase zirconium-hydrogen alloy, the amount of hydride will tend to be increased at the cold end and decreased at the hot end. That such an effect can occur in solid metals is not generally appreciated. However, with the trend toward higher operating temperatures in several fields, this phenomenon will become more important in the future. Actually, such effects should be rather common in the core of nuclear power reactors where the op- erating temperatures are high and temperature gradients are an order of magnitude higher than in previous high-temperature applications of alloys. The purpose of this paper is to point out the existence of such an effect, to discuss the manner in which one predicts whether a redistribution of the second phase will occur in a given system, whether the second phase will go to the hot or cold face, and how rapidly the redistribution will occur. One aspect of this problem has been discussed by pfam and Wernick2who considered the migration of a small liquid region through a solid. In their case, the diffusivity in the liquid is much larger than in the solid and they have interpreted their results successfully by using Fick's first law as the flux equation in the liquid, and taking the concentration gradient from the phase diagram. For all the cases they have studied, this type of analysis predicts that the liquid region migrates from the cold end to the hot end, and this is what was found ex-

Jan 1, 1959

By C. F. Lucks, W. D. Wood, H. W. Deem

Electrical ad thermal-conductivity measurements have been made on titanium and 6 titanium alloys. The following expression was derived for calculating thermal conductivity from electrical conductivity: K = 0.626 s T x 10-8 + 0.00497 where K = thermal conductivity, cal sec-1 cm-2 cm0C-1 s = electrical conductivity, ohm-]cm-1 T = temperature, deg Kelvin This expression gives calculated thermal conductivities that are not in error by more than 10 pct from the experimental values for A-55 titanium and the 6 alloys measured; namely, A-110AT, C-110M, C-130AM, Ti-6A1-4V, Ti-140A, and Ti-155A, which are representative of the presently available commercial a and a-ß titanium alloys. THERMAL conduction in a gas, liquid, or amorphous solid is accomplished by energy diffusion from molecule to molecule, a relatively slow process. For this reason, such materials have a low thermal conductivity. When a material is crystalline, there is in addition a heat transfer by a vibratory motion of the crystal lattice. It is the contribution of this lattice conduction that makes a crystal a much better conductor than a gas, liquid, or amorphous solid. Lattice conduction, however, does not account for the relatively enormous thermal conductivity of a metal. This is explained by the freedom of movement of valence electrons. These valence electrons drift in a metal in a direction toward a drop in electrical potential and, to a lesser degree, in the direction of a temperature drop in the metal. Since both the electrical and thermal conductivities of a metal depend upon the presence of free electrons, there should be some relatively simple relation between the two. Wiedemann and Franz in 1653 first discovered an approximate empirical relation between the electrical and thermal conductivities of metals at the same temperature. This ratio varies appreciably with temperature, and Lorenz later showed that by adding a temperature factor to the Wiedemann-Franz ratio the value of K/(s T) is constant, where K is the thermal conductivity, a the electrical conductivity, and T the absolute temperature. This Lorenz constant shows a greater variation for alloys than it does for pure metals, the ratio increasing slightly as the proportion of alloying elements increases. It has been found that a closer correlation between electrical conductivity and thermal conductivity can be obtained by means of an equation of the form K - A s T + B [1] where A and B are constants. In this equation the term AsT is the contribution of electronic conduction and B is the contribution of lattice conduction to the total thermal conductivity. EXPERIMENTAL MEASUREMENTS Electrical-resistivity and thermal-conductivity measurements on titanium and 6 titanium alloys serve as the basis for determining an equation of the K = AsT + B type for titanium alloys. Specimens—Table I shows nominal compositions of the 7 metals on which electrical and thermal conductivities were measured. The electrical and thermal-conductivity specimens for each alloy were taken from stock of the same heat and usually from adjacent sections of the same bar. All of the metals measured were in a mill-annealed condition. Methods—Electrical-resistivity measurements

Jan 1, 1959

By J. D. Lubahn

Prior tests by Dorn, where the strain rate in a tensile test was suddenly changed, have shown a small, but definite rate-history effect to exist. If this effect is neglected in the calculation of creep behavior from tensile results, an error should occur. This paper shows that this error is smaller than experimental scattering, and may be neglected. DORN1 has found a small but definite rate-history effect in the aluminum alloy 250 at liquid-nitrogen temperature using tensile tests with an abrupt rate change. Such an effect is to be expected from pre-viously known2-6 temperature-history effects, together with general experience that effects produced by changing the strain rate a large amount are simi-

Jan 1, 1959

By J. R. Mihalisin

THE application of electron-microscopic techniques to the study of high-temperature alloys has met with considerable success.' This is due, in part, to the submicroscopic nature of the phases present in this type of alloy making high resolution methods necessary. Among the newer electron-microscopic techniques, the extraction replica technique' has proven to be of great value. This method allows phases to be examined in situ in the microstructure and permits their identification by means of electron diffracticn. This technique eliminates the main disadvantage in using electrolytic extraction of residues as a means of phase identification; that is, the uncertainty of relating constituents identified in the residue to what is observed microscopically. In the course of work relating microstructure to physical properties in high-temperature alloys, it was found that the formation of grain-boundary carbide phases and intragranular precipitation of an age-hardening phase greatly influence strength and ductility at high temperature. In particular, it was found that the formation of a unique type of precipitate in Nimonic "80" (a nickel-chromium-aluminum-titanium type superalloy), termed cellular or discontinuous precipitate, at grain boundaries generally results in poor ductility at high temperature. However, this mode of precipitation can be avoided by proper heat-treatment. It was assumed that this precipitate was either a carbide or age-hardening type of phase. Using various etching procedures with the extraction-replica technique, it was found to be possible to extract the carbide and age-hardening phases preferentially in this type of alloy. Previous work has shown that the age-hardening phase can be extracted from superalloys merely by

Jan 1, 1959

By J. O. Betterton, D. S. Easton

A detailed investigation was made of the phase diagram of silver-zirconium, particularly in the region 0 to 36 at. pct Ag. The system was found to be characterized by two intermediate phases Zr2Ag and ZrAg and a eutectoid reaction in which the -zirconium solid solution decomposes into a-zirconium and Zr2Ag. It was found that impurities in the range 0.05 pct from the iodide-type zirconium were sufficient to introduce deviations from binary behavior, and that with partial removal of these impurities an increase in the a-phase solid solubility limit from 0.1 to 1.1 at. pct Ag was observed. The phase diagram of the silver-zirconium system is of interest as an example of alloying a transition metal from the left side of the Periodic Table with a Group IB element. Silver would normally act as a univalent metal, its filled 4d-shell remaining undisturbed during the alloying. However, there is a possibility that some of the 4d electrons might transfer to the zirconium. An insight into such a question can occasionally be obtained by comparison of phase diagrams. The silver-zirconium system forms part of a more complete review of various solutes in zirconium in which these valency effects were studied.' Earlier work on the silver-zirconium system was done by Raub and Enge1,2 who investigated the silver-rich alloys. After the start of the present experhents, work on this system was reported by Kemper3 and by Karlsson4 which for the most part agrees with the phase diagram presented here. EXPERIMENTAL PROCEDURE The alloys were prepared by arc casting on a water-cooled, copper hearth with a tungsten electrode and in a pure argon atmosphere. Uniform solute composition was attained by multiple melting on alternate sides of the same ingot. Progressive improvements in the vacuum conditions inside the apparatus during the course of the experiments reduced the Vickers hardness increase of the pure zirconium control ingot from 10 to 20 points, observed initially, to negligible amounts at the end of the experiments. Such hardness changes in zirconium are a well known indication of purity. For example, -01 wt pct additions of oxygen, nitrogen, and carbon increase hardness by 6, 10, and 3 VPN respectively. '9' Further verification that the final casting technique did not add a significant quantity of impurities was obtained when pure zirconium was arc cast and then isothermally annealed in the vicinity of the allotropic transition. The transition was always observed to take place over the same temperature range as in the original crystal bar. The alloy ingots were annealed in sealed silica capsules for times and temperatures which varied between 1 day at 1300°C and 60 days at 700°C. The best method found to prevent the reaction of the zirconium with the silica was foil wrapping of molybdenum or tantalum. With this method, samples of pure zirconium were found to be unchanged in hardness after annealing for 3 days at 1200°C. In most of the experiments the protection of these foils was supplemented by an additional layer of zirconium foil inside the molybdenum or tantalum foil. The alloys, foil, and the capsule were outgassed at pressures in the range 10 to l0-7mm Hg in the temperature range 800" to 1100°C before each anneal in order to remove hydrogen and other impurities, and to provide a suitable container for the high purity, inert atmosphere, which is essential in the annealing of zirconium. The temperature measurements were made with Pt/Pt + 10 pct Rh thermocouples calibrated frequently during the experiments against the melting points of zinc, aluminum, silver, gold, and palladium. For the longer anneals the sum of various temperature errors was generally well within ± 2°C. For short-time anneals and during thermal analysis the overall temperature error is considered to be within ± 0.5°C. The compositions of the alloys from the quenching experiments were determined by chemical analysis at Johnson Matthey and Company, Ltd., under the direction of Mr. F. M. Lever. The actual metallo-graphic samples were individually analyzed in every case, and prior to the analyses two or more sides of each specimen were examined to insure that the specimen was not segregated. The sum of the solute and solvent analyses was in each case within the range 99.9 to 100.1 pct. In the course of the experiments, minor impurities in the range 0 to 500 ppm were found to have significant effects on the zirconium-rich portion of the phase diagram. Similar effects had been encountered previously in other zirconium phase-

Jan 1, 1959

By A. G. Metcalfe, Koeneman

A study of the structure of chemically deposited nickel by Goldenstein, Rostoker, Scpssberger, and Gutzeit has been reported recently. In this work it was shown that the nickel deposit produced by the catalytic nickel-reduction process was an amorphous solid. Crystallization occurred at elevated temperatures when the original powder pattern which showed only a diffuse ring with a d-spacing of 2.01A became sharp, revealing nickel and nickel-phosphide lines. The phosphide was indexed provision%lly on a tetragonal lattice of parameters a = 9.01A and c = 4.42A, which is in reasonable agreement with the structure of Ni3P proposed by No-wotny and Henglein.3 The transformation from the amorphous to the solid state occurs abruptly (e.g., after 7 min holding at 400°C) with the evolution of considerably more than 1000 cal per gm-mole. A more detailed analysis of these effects requires a knowledge of the solubility of phosphorus in nickel. Konstanti-now3 mapped out the phase diagram in 1908 but did not determine the solid solubility. The eutectic was placed at 11 pct P and 880°C. The purity of typical catalytic nickel deposits is very high.' Spectrographic analysis for heavier elements showed only trace amounts of aluminum, calcium, iron, magnesium, lead, and silicon. The term "strace" is a qualitative definition for less than 0.1 pct and probably less than 0.01 pct. Analysis for the interstitial elements yielded 0.04 pct C, 0.0023 pct 0, 0.0005 pct N, and 0.0016 pct H. Some of this material with 7.5 pct P was used in the present work. EXPERIMENTAL METHODS Alloys were prepared from carbonyl-nickel shot and a master composition containing 7.5 pct P. Cold-crucible, nonconsumable-arc melting was used.

Jan 1, 1959

By E. A. Peretti

BEFORE embarking on a detailed investigation of the system indium-antimony-bismuth, experiments were carried out to determine the existence of quasi-binary sections. The bordering binary systems are known1 and show the occurrence of three intermetallic binary species corresponding closely to InSb, InBi and In2Bi. Attention was focused on the low-indium end of the ternary diagram where the possible quasi-binary sections, excluding ternary compound formation, would involve the pairs: InSb-Bi, InBi-Sb and InSb-InBi. The latter pair revealed itself as a true quasi-binary, so it was investigated fully by thermal analysis, x-ray and microscopic examinations. All compositions were made by proper combination of three elements involved. The indium had a guaranteed purity of 99.97 pet; the antimony contained 99.99 pet Sb, and the bismuth had a purity of 99.99 pet. Alloys were made by melting together antimony, bismuth and indium in evacuated, sealed pyrex-glass tubes at a temperature of 600°C with vigorous agitation. The melts, weighing about 80 grams, were allowed to freeze in the sealed tubes and finally were transferred to glass tubes for the taking of cooling and heating curves. A protective atmosphere of helium was used, and the melts were stirred mechanically while cooling at rates of from 0.5 to 3°C per min. Temperatures were measured with a calibrated chromel-alumel thermocouple and were recorded graphically on a Minneapolis-Honeywell extended-range recorder working in conjunction with a Leeds and Northrup type K-2 potentiometer. Conventional polishing techniques gave satisfactory results in preparing specimens for microscopic examination. Etching was carried out with Vilella's reagent or aqueous mixtures of chromic oxide with either nitric acid or sulfuric acid plus dichromate. Conclusions deduced from the thermal analysis and microscopic examinations were confirmed by X-ray photograms using Co-K alpha radiation. The phase diagram is shown in Fig. 1. The liqui-dus consists of an uninterrupted line running from the freezing point of InSb (525°C) to a eutectic point experimentally indistinguishable from the freezing point of InBi (110°C). X-ray patterns of the InSb show a slight expansion of the lattice with the addition of InBi, and microscopic work indicated the solid solubility of InBi in InSb to be less than 0.5 pet at room temperature. Acknowledgment We wish to thank the Indium Corporation of America for the loan of the indium used in this investigation. References 1 E. A. Peretti and S. C. Carapella, Jr.: Trans. ASM., 1949, vol. 41, P. 947. T. S. Liu and E. A. Peretti: Trans. ASM, 1952, vol. 44, p. 539. Metals Reference Book, vol. 1, 2nd ed., AIME, p. 345.

Jan 1, 1959

By W. Rostoker, R. F. Domagala, R. P. Elliott

The phase equilibria of the Hg-Th system over the composition range 0-100 pct Th and temperatures up to 1000°C have been studied for a small-volume, closed system. The solubility of Th in liquid Hg is about 5 pct at 300°C and decreases sharply with decreasing temperature. Two intermediate phases occur, Hg3 Th and HgTh. The structures of these are hexagonal (nonideally close-packed) and face-centered cubic, respectively. The HgTh phase decomposes eutectoidally at 400°-500°C. The solubility of Hg in solid thorium seems to be negligible. AFULL-phase diagram for this system would have to be defined on temperature-composition-pressure co-ordinates. This paper describes the pseudo phase diagram of a closed system, that is, where the alloy enclosed in a small volume equilibrates with a vapor pressure of mercury dictated by composition and temperature. Because of the experimental difficulties in studying a system of this nature, many of the phase relations can only be sketched. Alloy Preparation Alloys over the full range of composition were made from triple distilled mercury and one of two grades of thorium. For the bulk of the work, a calcium-reduced metal in sintered pellet form of reported 99+ pct total thorium content was used. Arc-melted specimens of this thorium gave a hardness of 135 VPN. The microstructure showed small primary dendrites of ThO2. A number of alloy compositions were made with a high-purity, iodide-decomposition thorium metal. The are-melted hardness of a button of this material was 35 VPN. Although the microstructure of the arc-melted specimens showed no dendrites of ThO2, there was definite evidence of an unidentified phase enveloping the grain bound-aries. There were no distinguishable differences between the constitution of alloys made with the two grades of thorium metal. Under normal conditions thorium is not wetted by liquid mercury. The film of ThO2 on all thorium metal cannot be penetrated by either liquid or vaporous mercury. It was therefore necessary to comminute thorium in the presence of mercury under such conditions that oxide films could not reform on the newly exposed metal surfaces. This was accomplished by the use of a high-speed, carbide-tipped rotary cutter incorporated in a chamber purged with argon and connected at the bottom to a demountable Vycor bulb containing a weighed amount of mercury. This experimental device is fully described in a separate paper.1 Alloy compositions were calculated by weighing the empty bulb, the bulb containing the mercury, and the bulb containing the mercury and the thorium chips. Many alloys were analyzed chemically for thorium and/or mercury after subsequent homogenization; the agreement between analyzed and calculated compositions was invariably very close. Bulbs containing the requisite amounts of mercury and fine thorium chips were clamped off, removed to a sealing unit, evacuated and sealed. Amalgamation under these conditions proceeded rapidly even at room temperature. To insure homogeneity, the specimens were annealed to 300-400°C. Alloys containing less than 30 pct Th remained pasty after all treatments, indicating an equilibrium condition of liquid plus solid. Alloys with more than 30 pct Th were transformed into a dark powdery product. These latter specimens were annealed for times of up to 1 week to complete interdiffusion. Many of the alloy compositions are pyrophoric. On exposure to air they oxidize with considerable evolution of heat to a mixture of ThO2 and free mercury. It was mandatory that alloy specimens be handled in a "dry box" purged thoroughly with argon. All X-ray diffraction specimens were powdered, screened, and sealed in capillary tubes within the dry box. Experimental Procedures Thermal analysis experiments, useful only in the mercury-rich region of the system, were conducted with the alloys in their original containers. A reentrant thermocouple well formed an integral part of the bulb. These bulbs were heated in a silicone oil bath and cooled in a dry ice-acetone mixture. The rates of heating and cooling were slowed by immersing the specimen bulb in a larger tube containing silicone oil. This provided a suitable thermal lag. In all tests, pure mercury was run as a basic standard. While the invariant reaction at about the melting point of mercury was detected by thermal analysis, the heat effect at the liquidus was not sufficient to produce an inflection in the cooling curve. It was necessary to determine the liquidus temperatures at the mercury-rich end of the system by "breaks" in electrical reslstivity versus temperature curves for individual alloys. The apparatus for this purpose consisted of a pyrex tube about 2 in. diam and 12 in

Jan 1, 1959

By L. C. Weiner

For zinc single crystals, xo = 3o, a surface coating raises both the cleavage and yield strengths over a large temperature range. The "brittle temperature," associated with slip after completion of twinning, does not coincide with the point of intersection of the flow and cleavage curves, which is associated with twinning. A surface film has no effect on the brittle temperature, while it lowers the intersection temperature some 20°. For crystals, yn = 83o, a coating decreases the cleavage strength, making it temperature independent, as well as increases the brittle temperature or its equivalent, the intersection temperature, 20°. These observations are described on the basis of a dislocation-pile-up-at-a-barrier model for brittle fracture; in crystals x,, = 3o the number and distribution of twins play a vital role. IN a recent investigation on the effects of solid environments on the brittle fracture of zinc single crystals,' it was demonstrated that the presence of a surface film changes the cleavage strength of these crystals, either increasing or decreasing it, depending on the crystal orientation. An increase in cleavage strength of some 43 per cent was found for coated crystals oriented x, — 3o K = 28",* while a decrease of 48 per cent was observed with crystals X" = y» — 83". Moreover, these effects were found

Jan 1, 1959