By Riki Kobayashi, Donald L. Katz

The dew point of natural gas which has been in equilibrium with gas hydrates has been reported to be lower than that obtained for natural gas in equilibrium with water1,? Hammerschmidt' reports a lowering of the dew point of 13 F for a natural gas in equilibrium with hydrate at 380 F and 525 psi. Records and Seely2 likewise show that the dew point of gas leaving hydrate separators' is as much as 150 F below the separator temperature. This paper presents the reasons for the observed differences between the equilibrium temperatures and the dew point temperatures. Descriptions of the dew point determination by the Bureau of Mines and ASTM tester3 indicate that the dew point is taken as the temperature at which liquid water droplets first begin to appear on the cooled mirror surface even though the temperatures involved are below that required for the formation of gas hydrates or ice. PRESSURE-TEMPERATURE DIAGRAM FOR METHANE-WATEK SYSTEM Fig. 1 presents a schematic pressure-temperature diagram for the methane-water system" for some constant pressure between the critical pressures of pure methane and pure water i.e., pressures frequently encountered in pipeline operations. The possible equilibrium relations are shown by the heavy solid lines. Curve AE represents the saturated water content or dew point of gas in equilibrium with a water-rich liquid solution while curve EF represents the dew point of gas in equilibrium with hydrates. In addition the dotted line DE labelled "metastable dew point" is introduced to explain the apparent discrepancy betwceen the dew point determination and gas-hydrate equilibria. Thermodynamics place certain restrictions on the location of line DE6, namely, that (1) the concentration of water along the line DE be greater than the concentration of water along EF or that the metastable line split the angle formed by the intersection of line GE and EF

Jan 1, 1956

By C. C. Harris

The 3-parameter equation* was introduced1 as having the necessary form and flexibility for describing the major features of size distribution curves. Also, Eq. 1 was shown to contain most of the widely used 2-parameter equations as special cases. Special methods are necessary in order to determine the parameters of 3-parameter equations by graphical means. The procedure given previously required double graphical interpolation followed by regraphing the interpolated data. The theoretical basis of the method was a difference equation eliminating y. Several other methods for obtaining the parameters have been under development and one method appears to overcome the disadvantages of the earlier method and satisfies several procedural requirements. The points in favor of the new method as compared to the earlier method are as follows: 1. Estimation of the quality of fit is direct, and is in fact an essential part of the procedure. 2. The data is plotted directly without the necessity of interpolation from a graph. 3. The method makes use of Rosin-Rammler2 paper which because of expanded scaling in the coarse sizes leads to improved accuracy1 as compared with the log-log plot for the Gates3-Gaudin4-Schubann5 representation. 4. There is a gain over the earlier method in overall accuracy and in simplicity.

Jan 1, 1970

By R. E. Bish

IN an effort to distinguish experimentally between the radically different limits of two-liquid im-miscibility reported for the Cu-Pb system by Borne-inann and Wagenmann and by Briesemeister (see Fig. I), it was found that the high temperature homogeneous liquid containing between 41 and 93 pct Pb could not be frozen without separation into two liquids with the fastest cooling technique that could be devised. Thus, the two-phase state could not be distinguished with certainty from the one-phase state by the examination of quenched samples. To overcome this obstacle the following method for detecting the presence of an interface between two immiscible conducting liquids at temperature was developed. Measurements made by the new method substantiate the Briesemeister diagram in its general form. The method consists essentially in the measure-

Jan 1, 1953

By P. R. Sperry

A METHOD was recently devised to indicate two or more successive stages of the migration of grain boundaries in aluminum, and to record the direction of the migration. This technique was used for the study of the various types of boundary migration occurring in high purity aluminum.' The method employs alternate annealing and electrolytic etching treatments, repeated as many times as desired. All successive sets of grain boun- dary positions revealed by the various etches appear superimposed on each other. The last etch is designed to leave an oxide film on the surface which is optically anisotropic. The orientation of the oxide film at each point is determined by the orientation of the underlying aluminum grain. When viewed with polarized light using crossed nicols and a Biot-Klein quartz plate, grains with differing orientations appear in different colors, as described by Hone and Pearson.' The last boundary positions are revealed by these color differences. The first step of the process is to obtain a desired starting grain size by annealing, for example, if high

Jan 1, 1951

By A. A. Burr, D. Caplan

IN carrying out experiments in metal-gas systems, it is often difficult to estimate how long a reaction period must be allowed for equilibration. This is especially true in systems for which the diffusion coefficient is not known. In an investigation of the Cr-O system, the necessary information was obtained in the way described subsequently. Two pieces of chromium sheet of different thicknesses were packed in mixed powders of chromium and Cr2O3 and sealed into an evacuated metal capsule by welding. Austenitic stainless steel proved suitable as a capsule material up to 1350°C and molybdenum at higher temperatures. The capsule then was heated at a specific temperature for a time sufficient to saturate with oxygen the thinner but not the thicker specimen. The time is readily estimated from a preliminary experiment if a sufficient thickness differential is chosen. Under these experimental conditions, the metal sheet is exposed to a partial pressure of oxygen equal to that of the dissociation pressure of the oxide and hence can become saturated with oxygen without developing any second phase. After cooling, both samples were analyzed for oxygen by the vacuum fusion technique. Assuming that the surface of the specimens is kept saturated with oxygen throughout the experiment, the diffusivity can be calculated by application of the appropriate solution to Fick's second law. This is most conveniently accomplished by use of a plot of mean fractional saturation (Cm-Co) / (Cs-Co) vs (Dt) ½/L as given by Darken,' where t is time, L the half-thickness of the sheet, and D the diffusion coefficient. Cm, the mean concentration at time t, is given by the oxygen percentage in the thicker specimen; Cs, the constant surface concentration, is the oxygen percentage in the thinner specimen; Co is the oxygen content of the original chromium sheet. (Cm-Co) / (Cs-Co) is calculated and the corresponding (Dt) ½/L is read from the graph and D thereby calculated. By performing the experiment at two temperatures and plotting log D vs 1/T, the D for any temperature is established. (The activation energy for diffusion may be obtained from the slope of the line.) Once D is known as a function of temperature, it is a simple matter to estimate the correct reaction time for experiments with single specimens at other temperatures by equating (Dt) ½/L to its value for effective saturation. Darken' points out that this is approximately unity. The solubility of oxygen in chromium, as determined from the thin samples at each temperature, proved to be approximately 0.03 pct at 1350°C and less at lower temperatures. Due to low solubility and to the known difficulties of the vacuum fusion method in this low range, the values obtained for D (5x10-0 sq cm per sec at 1350°C) are estimated to be correct only within an order of magnitude. Nevertheless, the method has proved useful in estimating reaction times. Its usefulness will be greater in metal-gas systems where the solubility is appreciable. A second function of the method is to permit the determination of diffusion coefficients in systems for which the conventional techniques are experimentally difficult or impossible.

Jan 1, 1956

By I. Sheinhartz, H. M. McCullough

DURING the course of a lubrication study in relation to the compacting of metal powders, it became desirable to measure the thickness of sprayed graphite coatings on steel dies for hot pressing. The thickness of these lubricant coatings ranged between 0.0001 and 0.002 in. In their particular case, the authors were interested in a method for measuring the lubricant thickness on tapered die inserts having curved surfaces. The lubricant was sprayed on the inserts at an elevated temperature and it was desirable to measure the thickness as soon as possible after application. Various standard types of commercial equipment were tried. Most of the available devices operated on either a mechanical or magnetic principle. The mechanical devices, such as micrometers, dial indi-

Jan 1, 1956

By L. G. Schulz

THE possibility of using reflected X-rays to produce images of crystals was explored by Barrettl who developed simple experimental procedures for X-ray microscopy and who showed by numerous examples the great range of information that could be made available. In his method characteris radiation is used to produce an image of a limited area of the sample on fine-grained film, this image subsequently being enlarged approximately X100. A somewhat different method will be described here;' white radiation from a fine-focus X-ray tube-"' is used to produce an image of a relatively large area of a single-crystal surface. part of the sample; therefore, white radiation is needed. The resolution in the image formed on the photographic film will depend on the size of the focal spot of the X-ray tube. If the sample is made

Jan 1, 1955

By L. D. Jaffe

IT is now well established that quenched and tempered titanium alloys have much better ductility when the quenching is from a two phase a-B structure, rather than from an all B structure. The corresponding microstructural differences, however, have not been shown in previous publications. Accordingly, specimens were cut from a % in. rod of commercial RC-130A, containing 7.9 pct Mn and 0.12 pct C, which had been previously hot rolled, heated 1 hr at 1100°F, and air cooled. (The same heat has been studied by others." 7 Samples about 1/4 in. cube were heated in helium 1/2 hr at 1450' or 1700°F, quenched in brine, tempered in helium 1 hr at various temperatures up to 1250°F, and quenched in brine. They were then sectioned and metallo-graphically examined, using an etchant of HF-HNO, in glycerine. As quenched from 1700°F, the microstructure observed was clear /3. (Probably also present was U, as the hardness was 400 Vhn, but w is not yet reliably revealed by any metallographic technique.) When the /3 quenched alloy was tempered at a high temperature, a precipitated as a grain boundary film

Jan 1, 1957

By R. D. Reiswig, D. J. Mack

THE use of pyrophoric alloys in ignition devices dates back more than fifty years to a German patent granted to Carl Auer von Welsbach in 1903.' This patent named a composition essentially the same as that used in most present-day cigarette lighter "flints:" 70 pct mischmetal, 30 pct Fe, referred to here as "Auer alloy." Among the few current exceptions to this composition are those "flints" based on titanium or zirconium. The rare-earth metals of which mischmetal is composed are so similar chemically and physically remarkable similarity in their alloying behaviors would be expected. Comparison of the binary phase diagrams2 of these elements with nonrare-earth metals shows that this is true to a striking degree, so much so, in fact, that it appears that a mixture of these elements may be treated as a single component of alloys without fear of serious error. In considering alloys containing mischmetal, therefore, the mixture of rare-earth elements will be referred to merely as "cerium," the predominant element in mischmetal. In polishing cerium alloys for metallographic examination, it was soon discovered that aqueous polishing media were highly corrosive. Free cerium in the alloys acts similarly to calcium (though not quite so rapidly) in evolving bubbles of hydrogen at the metal-water interface; thus, special metallographic techniques are required. The simplest polishing technique found to be satisfactory consisted of slow hand grinding on dry emery papers through

Jan 1, 1956

By P. Dayal, L. S. Darken

THE migration of carbon in austenite under the influence of an electric current has been observed qualitatively several times.14 Lebedev and Guterman5 recently have reported quantitative measurements; their method consisted of welding a low-carbon to a high-carbon wire, passing current, and later estimating the carbon distribution metal-lographically. We believe the method reported in this paper is superior in principle since electrolytic migration and ordinary diffusion are not necessarily coupled as in the weld method; also for the first time the extent of migration is determined by combustion analysis for carbon. A uniform tubular specimen (S.A.E. 1045 or 1095) was mounted as illustrated in the figures. the whole assembly being in an atmosphere of purified nitrogen. Direct current (129 to 226 amp at 0.65 to 1.0 v) served as source both of heat and of potential gradient for carbon migration. The duration of experiment was 7.5 to 12 hr, during which time the temperature was controlled (±10°C) manually. The experimental conditions are indicated in the first five columns of table I. With this experimental arrangement, the temperature initially has a maximum value at the central plane. Also, in this vicinity (by virtue of the symmetry), the carbon entering any volume element is equal in quantity to that leaving; the loss or accumulation of carbon occurs near the electrodes since the carbon moves uniformly near the center and is "frozen" at the cold ends. Hence, providing the time of experiment is not sufficiently long to seriously influence the conditions at the central plane, carbon crosses this plane only under the influence of the electrical potential gradient and not under the influence of temperature or concentration gradient. The amount of carbon which has crossed this plane was determined by combustion analysis of the two halves of the specimen. The results of these analyses are shown in the sixth and seventh columns of table I. It will be noted that substantial amounts of carbon migrated from the anode portion to the cathode portion (except at 920°C, which temperature was too low to exhibit the effect in the allotted time). In spite of precau-tions taken, considerable decarburization occurred as may be seen by comparing cols. 8 and 5. In three cases (indicated by asterisks in table I) the specimen was ground on one side, polished, and examined metallographically before analysis. One specimen was normalized and re-examined. Micrographs of selected areas in specimens 4 and 6 are shown in figs. 1 and 2, respectively. Evidence of carbon migration from the anode toward the cathode is quite apparent. Fig. 2 shows abundant graphite as well as cementite in a region near the cathode. The temperature of this zone is estimated at about 800°C. In fig. 1, particularly in the micrograph on the extreme right (the right side of which is of unaltered carbon content), there is evidence of slight depletion of carbon in the immediate vicinity of the cathode as contrasted to the general increase in carbon of the cathode half of the specimen. Although this may be attributed in part to decarbur-ization, it is believed that it is occasioned also by thermal diffusion—migration (of carbon) from a cool to a hot zone4—a phenomenon superimposed upon the electrical migration. Evidence of carbon migration was visible particu-larly during the course of the high-temperature,

Jan 1, 1951

By R. C. Troxell, S. C. Sun

EFFORTS to obtain definite quantitative data when employing the currently used bubble pick-up method1,2 as a pre-flotation investigation tool led to the adoption of the magnifying mirror method and the microscopic method modifications. Quantitative data obtained by these two methods were converted into bubble pick-up indices and bubble pick-up coefficients. Rough correlations were established between the calculated indices and the results of contact angle testing as well as actual flotation under the same conditions. The basic steps of the magnifying mirror method are as follows: 1—mixing 200 ml distilled water, sized and cleaned mineral particles of approximately 0.5 g, pH regulator, and flotation reagents in a glass beaker; 2—swirling the mineral particles to the center of the beaker to leave a clear circumference; 3—pressing an air bubble against the mineral particles for about 1 sec, and then moving the mineralized air bubble to the clear part of the beaker; and 4—dropping all the attached mineral particles of the air bubble by tapping the bubble holder, and counting the number of the dropped particles by looking at the magnified image in the mirror positioned beneath the beaker. This method is impractical for mineral particles which are transparent in water or finer than 200 mesh. The microscopic method is essentially similar to the above described magnifying mirror method, with the exception that the mineralized air bubble was drawn up into the bubble holder and subsequently discharged onto an externally placed watch glass, where the number of pick-up particles was counted with the aid of a microscope or hand lens. Drying was necessary when the discharged liquid interfered with the counting. The results of the bubble pick-up tests can be simply expressed in the form of the actual count. However, this can be misleading because the number of pick-up particles varies not only with the size of bubble but also with the size of particles. This short-coming is largely remedied by the use of the bubble pick-up index. as calculated from the following equation: PI = (pn/p) 100 [1] in which PI and pn are respectively the pick-up index and the number of pick-up particles under any test conditions, and p is the maximum number of pick-up particles of the same mineral under optimum flotation conditions, with the same size holder and particle. The bubble pick-up coefficient is a term coined to denote the difference between the bubble pick-up index of mineral particles in a liquid and that of the same mineral-liquid mixture plus a chemical reagent at the same pH value. For example, the difference between the pick-up index of a naturally floatable bituminous coal in a solution of water and kerosene and that of the same coal in water alone is a bubble pick-up coefficient. Compared with the contact angle method, the quantitative bubble pick-up method is inferior in accuracy but superior in sensitivity. Other advantages of the bubble pick-up method are that the apparatus can be easily assembled, the mineral sample is conventionally prepared, and the test procedure is relatively simple. References S. R. B. Cooke: The Flotation of Quartz Using Calcium Ion As Activator, Trans. AIME (1949) 184, p. 306. 'G. A. Last and M. A. Cook: Theory of Collector-Depressant Equilibrium at Mineral Surfaces. Paper presented at St. Louis Meeting, AIME (February, 1951).

Jan 1, 1954

By K. E. Beu

THE integrated intensity X-ray method of meas-uring retained austenite concentrations in hardened plain carbon or low alloy steels as proposed by Averbach and Cohen1,2 has the advantages of being a highly sensitive and precise quantitative method. The various phases of this method have been studied and several modifications have been developed which aid not only in reducing the time required per determination, but which also increase the possible accuracy of the method. A fundamental step in the original calculation procedure is to plot V.A(?) curves for austenite and martensite and to obtain VM/VA ratios from these curves.' In taking this ratio the absorption factor A (8) drops out since it is constant for a. given diffraction angle 8. The reason for eliminating A(?) in this manner is because it is apparently assumed

Jan 1, 1953

By G. Vaux, M. L. Fuller

AN apparatus and procedure for the determination by X-ray reflection of preferred orientation of crystals in rolled metal with the Geiger counter X-ray spectrometer was described by Schulz.' This is an excellent procedure and we have used it continually for several years. In our use of the procedure, two modifications have been made and used during most of this period. One of these provides for automatic scanning and recording of the reflections, and the other makes possible the application of the procedure to coarse-grained specimens and permits measurement of almost all orientations without resort to the transmission technique. The automatic scanning and recording are accomplished by a motor drive of the inner ring of the Schulz apparatus (see R, in Fig. 2 of his paper and R2 in Fig. 1 of this note) in synchronism with the chart recorder of the North American Philips 90" X-ray spectrometer. A rate of 10" per min is used. A scan of 180" is obtained corresponding to poles on the stereographic projection whose locus is a great circle. The modification for coarse-grained material is accomplished by allowing a larger area of the specimen to contribute to the X-ray diffraction. In the Schulz apparatus the incident X-ray beam is confined by a slit system to rays in the plane of the spectrometer. Schulz demonstrated that this restriction of the X-ray beam permits a survey of the X-ray reflections without correction up to about 80" on either side of that specimen position in which the specimen is perpendicular to the plane of the spectrometer. This is the angle + of rotation of the inner ring R2. One of these slits is horizontal and extends across the X-ray source side of the specimen. In the modification this slit is removed, thus permitting greater divergence in the X-ray beam and the irradiation of a larger area of the specimen surface. Fig. 1 shows the apparatus with the motor drive and with the slit removed. Discontinuities in the recorded X-ray intensity plot due to the few participating crystals in coarse-grained metal are much lessened. The increased divergence does not cause reflections from other crystal planes to enter the Geiger counter slit. An important advantage of the original Schulz scheme is thus lost and a system for correction is required. To do this, a compact of atomized copper powder was prepared and tested by the original Schulz method for the absence of preferred orientation. The horizontal slit was then removed and a curve recorded showing the variation of intensity with angle +. In our arrangement the intensity was uniform within the range + equals ±30°. Beyond this the intensity fell off rapidly reaching zero at ±90°. The curve thus produced is then used to correct measurements made on preferred orientation specimens. In practice this is accomplished by constructing from this calibration curve a family of curves which, as a transparency, can be superimposed on the recorder chart to read corrected intensity directly. Not only does this method permit the handling of coarse-grained material but it also makes possible the plotting of intensities almost to the circumference of the stereographic pole figure projection. Thus, nearly the entire pole figure can be plotted without the necessity of using the transmission technique. Moreover, intensities are much greater, an advantage when surveying crystal planes of poor reflecting power.

Jan 1, 1954

By I. Havenaar

EXPERIMENTAL DATA In an article by C. K. Ferguson and J. A. Klotz,1 experiments on the filtration of drilling muds under borehole conditions are discussed. Experimental data on mud filtration through the wall and the bottom of the hole are presented. From the data on bottom-hole filtration it was concluded that the filtrate does not flow freely into the formation, but that the pores of the formation are plugged by the mud. A quantitative interpretation of the data can be civen, by using a formula for bottom-hole filtration, dehved below. This formula is based on the following assumptions, 1. Each time a blade of a drag bit, or a cone of a roller bit, moves along the bottom of the hole, the mud cake is completely removed. 3. A new mud cake is immediately formed on the freshly produced surface, and losses of "whole" mud into the formation are negligible (this is equivalent to an immediate plugging of the pores). 3. The filtration of the mud on the bottom of the hole follows the classic law: V = A +1—(Eq. I), where t is the time required to yield a volume of filtrate V, A is the surface area of filter cake, and C is a constant. The application of this equation means that any eroding effect of the mud stream on the mud cake is neglected. The formula for the calculation of the volume of filtrate, Q,, flowing in one second through the hole bottom (diam. d cm), when using a bit with n cones or blades rotating at a rate of rn revolutions per second, is derived as follows: The mud cake is formed on the bottom of the hole in the time t =1; the filtrate volume V which passes n through the bottom In this time 1s given by Eq. 1: After1/nmsec the mud cake is removed. In one m second this process takes place nm times. Therefore the volume of filtrate, obtained in one second is given by This equation has now been applied to the experiments of Ferguson and Klotz. The constants C were derived by means of Eq. 1 from the API filter losses of the muds used by the authors (t = 1,800 sec; A = 45.16cm2). A three-cone bit was used (n = 3) at 90 rpm (m = 1.5). The calculated figures are compared with the experimental data in the table below. The calculated values of Q, are usually lower than the experimental values. This may be due to the following causes. 1. The value of C used in the calculation is based on the API filter test (filtration pressure of 100 psi), whereas the experimental data were obtained with a filtration pressure of 200 psi. Although the effect of the pressure on C is not large, C decreases somewhat with increasing pressure, and this leads to a higher filtration rate. 2. Mud losses and the eroding action of the mud stream on the cake are not entirely negligible. 3. The values of Q, derived by Ferguson and Klotz from their experiments are too high, because of their assumption that all pore liquid within the formation drilled is picked up by the drilling mud. It is found, however, that the calculated values of Qf, except in the case of oil base muds, are of the right order of magnitude. ACKNOWLEDGMENT The author wishes to thank the management of the Koninklijke/Shell-Laboratorium, Amsterdam, for permission to publish this note.

Jan 1, 1957

By A. J. Teplitz, J. K. Rodgers, E. M. Pohoriles

This note is presented in order to call attention to a newly developed laboratory apparatus that appears to have interesting possibilities for the study of lost circulation of the pressure-parting type, for a more realistic evaluation of sealing materials for this type of loss, and for investigation of other aspects of hydraulic fracturing. A study of lost circulation, conducted jointly by operating divisions of the Gulf Oil Corp. and the Gulf Research & Development Co., has been in progress for the past few years. Earlier phases of the study dealt with mechanical factors contributing to loss of returns in laminar type sediments.' One aspect of this type of loss which has been widely discussed in the literature and elsewhere concerns the geometry of the fractures into which such losses occur. This subject is not merely a philosophical one, but has an important bearing on procedures for combating lost circulation difficulties and on other well operations. The further course of the collaborative studies previously mentioned has produced some information on this subject which, though limited in amount, is believed to be significant. In several typical cases of lost circulation in laminated shale and sand formations, the wells have been surveyed with instruments2,3 capable of detecting the points of loss with considerable accuracy. These wells were located in the Gulf Coast of Texas and Louisiana, in the Texas Panhandle, and in the Rocky Mountain area. In each of these instances the loss was shown to be occurring at some distance removed from the bottom of the hole and sharply confined to a very narrow interval, less than 1 ft in thickness. It is rather difficult to imagine that fractures of a vertical nature' would be of the limited extent indicated by the surveys in these wells. Furthermore, the high rates of loss at relatively low pressure differentials observed in some of these instances together with the narrow intervals involved would appear to require the radial flow pattern which would be associated with a more or less horizontal fracture plane. In view of the foregoing observations and records of successful squeeze cementing operations, in attempting to construct a laboratory apparatus For simulating pressure induced lost circulation, it was decided that the design should be based on a horizontal type of fracture. It was realized that5,6 Vhe production of horizontal fractures in a formation with non-penetrating fluid requires some mechanism for transmitting vertical components of the hydraulic forces to the plane of parting. This was accomplished, as will be evident in the description of the apparatus that follows, by providing recesses in the wall of the borehole which are believed to be representative of wellbore configuration found in Gulf Coast wells. The possible influence of such borehole irregularities on both pressure fracturing and the treatment of lost circulation appears to have been neglected in many studies of these subjects. It is believed that the present apparatus, incorporating features that take into account some of the factors mentioned, will provide means of gaining a further understanding of pressure induced fracturing and possibly for more realistically evaluating the numerous sealing agents, particularly the non-time-setting materials employed in treating the pressure-parting type of loss. DESCRIPTION OF APPARATUS The test cell used in the laboratory investigations is shown in Fig. 1. A schematic diagram of the entire system is shown in Fig. 2.

Jan 1, 1956

By Kehsin Kuo

DIE steel with 1.47 pct C, 0.42 pct Mn, and 8.22 pct W contains Fe,C and WC in the annealed state and WC embedded in a martensitic matrix in the hardened state (quenched from 800°C). The presence of a large amount of undissolved angular WC carbide particles makes this steel extremely wear-resistant. However, the WC carbide begins to dissolve in the austenite when the heating temperature is raised above 1000°C, but this solution process is still not complete at 1250°C although partial melting has already taken place at the austenite grain boundaries. At 1325 C, this steel contains austenite and liquid metal but no WC carbide, Fig. 1. On quenching into brine, the liquid metal solidifies into a constituent which etches differently from the austenite-martensite matrix. This constituent appears lighter than the matrix at the 1250°C stage when etched with 2 pct nital but darker in Fig. 1 when etched with Murakami's reagent. Such a constituent has also been found in burnt tungsten high speed steels. This constituent has been isolated from the matrix by anodic dissolution in a 5 pct HC1 electrolyte and was found by the X-ray powder method to be iso-morphous with &manganese, Table I. The agreement in line intensity between these two phases indicates that there is no ordering in this new phase. The calculated cube edge of this phase is 6.395A, somewhat larger than that of ß-manganese (6.30A). Besides this phase, the anodic residue also contains free carbon from the matrix and amorphous WO,, although the X-ray powder pattern of the residue shows the presence of only this phase. This makes it impossible to determine directly the composition of this phase from the residue. Attempts to prepare an alloy containing only this phase have hitherto been fruitless. The following experiments serve to show that this phase can only be obtained by drastic quenching from the liquid state and that its tungsten and carbon contents must be lower than those in the Fe,W,C carbide. On air cooling from 1325oC, the liquid metal solidifies into a eutectic consisting of austenite and the Fe3W3C carbide. The nature of this dark-etching Fe3W3C has also been ascertained by X-rays. This eutectic becomes coarser on furnace cooling. The solidification of a specimen cooled for 5 min from 1325" to 1200°C and water quenched is still not complete and the fine eutectic is formed during the quenching. Since this new phase can be replaced by a eutectic of austenite and the Fe,W,C carbide, its composition must lie somewhere between the latter two phases. The special features of this phase are: 1—it can only form directly from the liquid state by drastic quenching and 2—it is a ternary phase of iron, tungsten, and carbon. The ß-manganese structure of this phase is also interesting. In the Periodic Table, iron and tungsten lie on opposite sides of manganese; a certain combination of these two elements, in the presence of carbon, may have average properties similar to those of manganese. It has already been established that the x phase, a ternary one of iron, chromium, and molybdenum, has the a-manganese structure."' A similar phase has also been found in the ternary system Fe-Cr-W and in the following binary systems: Re-Cb, Re-Ta, Re-Mo, and Re-W.6 References 1 G. D. Preston: Philosovhical Magazine 11928) 5. 7th Series, p. 1207. - K. W. Andres: Nature (1949) 164, p. 1015. 35. G. McMullin, S. F. Reiter, and D. G. Eberling: Trans. ASM 11954) 46, p. 799. ' J. S. Kasuer: Acta Metallurgica (19541 2, p. 456. • H. J. Goldschmidt: Trans. ASM (19541 46, p. 807. P. Greenfield and P. A. Beck: Private communication.

Jan 1, 1957

By N. E. Grosvenor

Several methods have been proposed for determining the tensile strength of rock. These have been tried out over the past several years, but the results have been erratic and of doubtful value. The tensile strength of rock is its weakest property, and this property apparently enters into all failure phenomena, whether underground or on the slope of an open pit. Therefore, it is essential that detailed quantitative information is known about the tensile strength of rock if the design engineer is going to select the proper pit slope, pit orientation, or orientation of underground workings so as to give the most economical and safest mining condition. This quantitative information may be used to orient the pit in such a manner as to allow steep slopes along two sides. This information possibly may be used to orient the direction of either underground workings or open pits so as to decrease powder consumption and to increase blasting efficiency. Hence it is of prime importance that a method of determining accurately the tensile strength of rocks be developed. The U. S. Bureau of Mines states' that no standard methods have been proposed by the ASTM for testing the tensile strength of rock. The method described in the Bureau publication is said by them to be unsatisfactory. A similar test that has been used in our laboratory in place of the USBM test is shown in Figs. 1 and 2. h this test the core is placed in a set of grips that has been designed for one particular size core. The grips are designed to distribute the stress around the core if they are tightened correctly. A universal joint or a flexible cable may be used in conjunction with the apparatus to prevent bending or twisting of the specimen. The main difficulty encountered with the system shown is the failure of the specimen within the grips. The possible cause of the failure within the grips may be due to a stress concentration set up by the uneven tightening of the grips. This method can be used only for tests on cores, and even then has been found to be totally unsatisfactory because of the failure within the grips. The U. S. Bureau of Reclamation has been using a test similar to the sketch shown in Fig. 3. Sulfur is cast around each end of the specimen to form a bearing surface and then a ring grip is used to apply a tensile stress. The grips are in contact with the sulfur cast and do not touch the specimen. This method is unsatisfactory, apparently because a large number of the specimens appear to break within the sulfur cast. Professor Wuerker of the University of Illinois uses the test shown in Fig. 4.' Professor Wuerker states2 that this method has given definite and reproducible results with the weakest as well as with the strongest rocks. The test is a supplement in all cases where cores cannot be obtained. The principle and equipment are the same as for the test for tensile strength of hydraulic-cement mortar. Soft

Jan 1, 1961

By P. Levesque

IN the process of alloying two metals to obtain a single-phase alloy, the end product is nearly always a cored structure. The mechanism of solid-

Jan 1, 1955

By D. Moskowitz

IN the course of a general investigation of boride systems, sponsored by the Office of Naval Research, various vanadium boride powders of relatively good purity were prepared which could be used for a determination of the phases present. The X-ray pattern of one of these lots showed, in addition to the known VB1 and VB22 phases, an additional phase, almost certainly of composition V3B4, isomorphous with Cr3B4, Cb3B4, Ta3B4, and Mn3B,. Its pattern fitted in well with the indices worked out by Kiessling for Mr3B4.3 The unit cell for this new compound is orthorhombic, with the dimensions a = 3.030A, b = 13.18A, c = 2.986A7 V=119.2A.' Table I lists the X-ray diffraction data for V.3,.

Jan 1, 1957

By W. C. Winegard, C. Elbaum, T. Ojala

NONOCTAHEDRAL slip was observed in poly- crystalline aggregates of aluminum by Boas and Ogilvie.&apos; These authors indicate that the non-octahedral slip takes place on (100) or (110) planes. Ogilvie2 studied the continuity of slip lines across grain boundaries in polycrystalline aluminum. Non-octahedral slip was observed by him, but it was not reported to occur in the continuous slip lines across the grain boundaries, which were identified as octahedral slip in all cases. The present note reports the observation of non-octahedral slip in the grain boundary region of an aluminum bicrystal and tricrystal, both deformed in tension at room temperature. An analysis is made, which leads to a probable identification of the non-octahedral slip planes as (110) and (331). The specimens used were of rectangular cross section, approximately 5x10x200 mm. They were prepared by growth from the melt, using aluminum reported by the manufacturer to be 99.994 pct pure. The grain boundaries were in a plane perpendicular to the wider face and parallel to the long dimension of the specimens. The axis of tension was also parallel to the long dimension of the specimen. The orientations of the specimens studied were determined by the Laue back-reflection method and are given in Fig. 1. The nonoctahedral slip was first observed after about 6 pct extension in the bicrystal, and after about 2 pct extension in the tricrystal. The micrograph, Fig. 2, of the grain boundary region of the bicrystal shows two active slip planes throughout each of the two crystals, with a third plane active at the grain boundary in each crystal. Two major sets of slip traces observed in grain No. 1 are consistent with the operation of the slip systems (ill) [oil] and (111) [011]. The nonoctahedral slip takes place on a plane belonging to a <111> zone, as determined by drawing trace normals. Assuming that slip will take place only in the <110> direction, the planes in the <111> zone, which do not contain that direction, need not be considered. Among the remaining prominent planes of that zone, the (011) plane has a common slip direction—the [011]—with the (111) plane, which acts as one of the octahedral slip planes. In grain No. 2, a similar situation to that in grain No. 1 is observed. As indicated previously, the (oil) plane in the <111> zone, to which the nonoctahedral slip plane belongs, has a common [Oil] slip direction with the acting (ill) slip plane. Also, the orientation of the (oil) plane in grain No. 2 almost coincides with the orientation of the acting (111) slip plane in grain No. 1. Similarly, the orientation of the (oil) plane in grain No. 1 almost coincides with the orientation of the acting (111) slip plane in grain No. 2. It is, therefore, possible that the nonoctahedral slip was induced, in both cases, by octahedral slip in the neighboring grain. It is important

Jan 1, 1957