By M. J. Marcinkowski, A. S. Sastri

A detailed compressive stress-strain analysis and transmission electron microscopy investigation has been made of the deformation behavior occurring in a 50 at. pct Ni-Ti (hypoeutectoid) alloy and a 54.5 at. pct Ni-Ti (hypereutectoid) alloy. In the case of the hypoeutectoid alloy, three stages of work hardening are observed. Stage I occurs at a very low stress and is associated with plastic deformation via martensite formation. Stage 11 is characterized by very rapid work hardening and is due to difficulties in causing further deformation in the fine martensite aggregate produced in Stage I. Stage III which occurs at very high stress levels is characterized by smaller work hardening rates and is due to the plastic deformation arising from alternate reconversions of the original martensites to martensites of varying orientation. Rapid quenching of the hypereutectoid alloy leads to very high yield strengths and is related to a fine precipitate dispersion that such treatment brings about. The present investigation represents the final phase of a three-part study directed toward an understanding of the solid-state transformations in near equi-atomic Ni-Ti alloys as well as the deformation mechanisms associated with these alloys. In the first part,"2 to be henceforth referred to as I, it was found that alternate simple shears on {112} planes and in (111) directions convert the parent B2 structure in the equiatomic NiTi alloy into two distinct close-packed monoclinic martensites. All of the marten-sites were of this type, whether they were formed by cooling or by plastic deformation, whether induced to form in bulk samples or in thin foils, or whether examined in the electron microscope at room temperature or below. On the other hand, in the second part of this investigation,3 to be reffered to as 11, it was shown that upon slow cooling to about 640°C. alloys in the neighborhood of NiTi which possess the B2 structure transform eutectoidally into their equilibrium phases Ti2Ni and TiNi3. However, preceding the formation of these equilibrium phases a series of metastable intermediate phases are formed. This paper will set as its goal the elucidation of the remarkable deformation behavior exhibited by NiTi. In particular, Buehler and Wiley4 have found equiatomic NiTi to be surprisingly soft, while Buehler et al.5 have shown this alloy to possess a memory effect: i.e., upon bending at room temperature it will revert to its original shape when heated to above about 50°C. In I it was shown that NiTi was soft in the sense that the yield stress was low; nevertheless, the alloy work-hardened at an extremely rapid rate to very high stress levels. On the other hand, the hypereutectoid alloys with somewhat higher nickel, say 54.5 at. pct (60 wt pct) have enormously increased yield strengths compared to those of the equiatomic alloys. In order to determine the atomistic processes giving rise to the above behavior, it was decided to examine samples that were wafered from bulk specimens deformed in compression to various strains using the techniques of transmission electron microscopy. EXPERIMENTAL TECHNIQUE All of the alloys used in the present investigation contained either 50 at. pct Ni (55.06 wt pct) or 54.5 at. pct Ni (60 wt pct) and were arc-melted in the form of a finger using the same techniques described in I and II. The finger was capsulated in a stainless-steel jacket and swaged at 850°C into rods. Compression specimens 0.300 in, long and 0.200 in. in diam were machined from these rods. In order to completely re-crystallize the samples and remove residual stresses, all of them were capsulated in evacuated quartz, annealed for 1/2 at 1050°C. and then furnace-cooled. Compression tests were carried out in an Instron tensile testing machine covering a range of temperatures from —196° to 200°C using procedures described previously.6'7 In all cases crosshead speed was 0.02 in. per min. Wafers 0.015 in. thick were spark-cut from the cylindrical samples at 45 deg to the compression axes after they had been deformed to the desired strain. These specimens were then spark-planed to about 0.005 in. and then electrochemically thinned for examination by transmission electron microscopy as described in I.

Jan 1, 1969

By E. R. Russell, N. E. Richards

The current ejyiciency of aluminum cells was derived from the metal produced over a period of time and the theoretical faradaic yield. The difference in the actual amount of aluminum in the cathode at the beginning and end of the period must be determined. The weight of aluminum in the cathode was calculated from the dilution of an added quantity of impurity metal. Use of multiple indicator metals, copper, manganese, and titanium, demonstrated that the weight of aluminum in cells can be determined to within 1 pct with routine but careful chemical analyses. Over intervals of the order of 30 days, current efficiencies reliable to within 1 pct can be obtained. INVESTIGATIONS beginning with those of Pearson and waddington ,' through the most recent published work of Georgievskii,9-11 illustrate the direct relationship between the composition of the anode gas and the applicability of analysis of anode gases to the control of alumina reduction cells. McMinn12 noted the lack of an independent method for measuring cell production efficiency over the short term. There is no doubt that changes in the current efficiency are immediately reflected in the composition of anode gases. However, the accuracy of faradaic yields calculated from gas analyses depends upon the degree of interaction between primary anode gas and Carbon.6 A conventional industrial practice of obtaining long-term current efficiency for production units from mass balances and quantity of electricity is generally insensitive to the impact of planned control of any one or more of the influential reduction cell parameters such as temperature, alumina concentration, and mean interelectrode distance. Consequently, there is a real need in the aluminum industry for a procedure to obtain the absolute cell current efficiency over a short term—10 to 30 days—both for the calibration of values obtained from gas analysis6 and for evaluating the effect of controlling specific parameters in the reduction process. The amount of aluminum produced may be determined by considering the cathode pool as a reduction of an impurity metal in aluminum. Analyses over a period will show a decreasing concentration of the impurity due to the accumulation of aluminum solvent. The increase in aluminum inferred from analyses is the amount produced by the cell during the period. Combining weights of the cell aluminum in the cathode at the beginning and end of a specific period, weights of aluminum tapped and the quantity of electricity passed during the interval will yield the current efficiency. Smart,I3 Lange;4 Rempel,15 Beletskii and Mashovets,16 and winkhaus17 have used dilution techniques to determine aluminum inventory in alumina reduction cells. A technique for determining the weight of aluminum in production cells by addition of small amounts of copper to the aluminum cathode was described by smart.13 The precision in values of the aluminum reservoir through dilution of copper in the cathode ranged from about 1 to 3 pct depending upon the quantity of copper added in the range 0.2 to 0.01 wt pct, respectively. Because the method appears so direct and apparently simple, one would not anticipate difficulties in application to industrial cells. The objective of this study was to resolve this problem associated with the trace metal dilution technique for determining the amount of aluminum in a cell. The approach in evaluating trace metal dilution as a basic factor in determining the weight of aluminum in the cell reservoir, and the absolute current efficiency of the Hall-Heroult cell, was to dilute more than one trace metal in the aluminum cathode so that we could discriminate among complications arising from physical mixing, the possibility of separation of intermetallic compounds, loss of the added elements, and chemical detection. EXPERIMENTAL METHODS These experiments are not complex but require standardized procedures. The technique involves addition of the trace metals to the cathode, knowing when these metals are homogeneously distributed in the liquid cathode, timing of the sampling, employing accurate and precise analytical methods, using reliable procedures for monitoring the amount of electricity passed through the cell, and accurate weighing of aluminum removed from the cell during the particular period. More accurate results might be obtained if the increment in concentration of the added indicator metals were of the order of 0.1 to 0.2 wt pct. The method must be applicable to production units and, hence, the contamination of the aluminum minimized. For this reason, the concentration of trace metals in the cathode was kept below 0.07 wt pct and generally at 0.04 wt pct level. Trace quantities of copper, manganese, titanium, and silicon are already present in virgin aluminum and are suitable as additives from electrochemical and analytical points of view. Concentration of silicon is quite dependent upon the characteristics of the raw materials and was not used extensively in this work. Chemical Analyses. All instrumental analyses require calibration against an absolute technique such as a gravimetric, volumetric, or spectrophotometric method which represents the ultimate in sensitivity, precision, and accuracy. On review, the best methods for copper appeared to be optical absorption without

Jan 1, 1969

By Charles M. Packer, Oleg D. Sherby, Roy H. Johnson

Originally round tensile specimens of a eutectic Zn-A1 alloy develop elliptical cross sections during superplastic deformation. This observation, coupled with a detailed study of the microstructure and preferred orieniation, suggests that crystallographic slip and continuous grain boundary migration or re-crystallization are important processes during super-plastic deformation. In spite of the extensive activity in superplasticity1-15 and the numerous explanations proposed, no single model has had universal acceptance. It has been established, however, that the general requirements for superplastic extension of two-phase alloys include an extremely fine, stabilized grain size of the order of a few microns, a temperature about equal to or greater than one-half the melting point, a critical range of strain rate, and a similarity in the mechanical strength of the major phases. The proposed models can perhaps best be characterized in terms of the important phenomena associated with them. These phenomena include: phase instability,1 diffusional creep by volume diffusion3 or grain boundary diffusion4,5 slip and continuous grain boundary migration or recrystalliza-tion,= grain boundary Sliding,7-9,13,14 and dislocation glide.'5 In this paper, experimental observations will be reported which support a model involving slip and continuous grain boundary migration or recrystalliza-tion. Specifically, a correlation will be made between this model and the development of elliptical cross sections as originally round specimens are superplas-tically deformed. For the most part, superplasticity studies have been conducted with eutectic or eutectoid alloys. Probably the most thoroughly studied material has been the monotectoid Zn-A1 alloy.1,2,6,12,13,15 No attention to the eutectic Zn-A1 alloy has previously been reported, and the results discussed in this paper represent part of a general study of the superplastic properties of this alloy. MATERIALS The alloys used in this investigation were prepared by melting appropriate quantities of 99.99+ pct A1 and 99.999 pct Zn in air, mixing, and pouring into a water- cooled stainless-steel mold. Wet-chemical analysis was conducted with each heat of alloy prepared, using the procedure of Fish and smith.16 The composition of the eutectic alloy was 95.1 wt pct Zn. Ingots about 2 in. thick were rolled to 0.4-in. plate at about 300°C with a reduction of 5 to 10 pct per pass. Specimens were machined from the plate with the tensile axis parallel to the rolling direction. The specimens were round, with 0.150-in.-diam, 1.25-in.-long gage length, and 0.25-in.-diam threaded grip sections. EXPERIMENTAL PROCEDURE Specimens were mounted inside a uniform-temperature quartz tube which was surrounded by a double elliptical radiant furnace with a 12-in.-long uniform-temperature hot zone and a low thermal capacity. The tube extended through the top and bottom of the furnace and permitted rapid quenching of the loaded specimens when quickly filled with cold water at the conclusion of the test. The quench precluded any effects on specimen microstructure from a normal, slow cool. Constant stress was applied to test specimens by suspending a load on a constant stress cam of the type described by Hopkin.17 The design of this cam permitted application of a constant stress for elongations up to 200 pct. For greater elongation, approximately constant stress conditions were maintained by systematically reducing the load manually. RESULTS As part of an investigation of the superplastic properties of the eutectic Zn-A1 alloy, evidence was obtained for the development of elliptically shaped cross sections as originally round specimens were extended. For example, after an elongation of about 100 pct, a round specimen with an initial diameter of 0.150 in. became elliptical with major and minor axis of 0.128 and 0.88 in., respectively. Photographs are presented to illustrate the ellipticity developed during superplastic deformation, Fig. 1. The specimen shown was deformed at a stress of 500 psi, at a temperature of 285°C, and a strain rate of 2.28 x 10-2 min-1. The strain-rate sensitivity exponent* was measured at *The strain-rate sensitivity exponent, m, is defined as d In o/d In c where o is the steady-state flow stress and E is the strain rate. this temperature and in the strain rate range 10"3 to 10-1 min-1 was found to be about 0.5. This value is typical of those observed with superplastic materials. The material studied exhibited negligible strain hardening during superplastic deformation, the creep rate remaining constant under constant stress and temper-

Jan 1, 1969

By William C. Harrigan, William D. Nix

Dynamic measurements of Young's modulus have been made for poly crystalline Ni-W alloys from room temperature to 800°C. The alloys studied range in composition from pure nickel to Ni-10 at. pct W. The results indicate that Young's modulus decreases linearly with temperature above the Curie temperature. The rate of change of Young's Modulus with temperature mas found to range from 104 psi per "C for pure nickel to 0.82 x 104 psi per °C for Mi-10 pct W. At all temperatures the elastic modulus decreases with increcrsing tungsten content up to 1 at. pct W, and increases as the tungsten content is increased above that level. Young's modulus decreases slightly as the carbon content is increased from 0.002 to 0.09 wt pct C THE knowledge of the elastic modulus of metals and alloys is important for a number of reasons. The first and most obvious reason comes from the need to predict elastic deflections under given loading conditions. A second and somewhat more subtle reason comes from the fact that the elastic properties of an alloy must be known before a proper account of the mechanisms of plastic deformation can be made. This is especially true for high-temperature creep of crystalline solids. Sherby and his coworkers have shown that the high-temperature steady-state creep rates of crystalline solids are inversely related to the elastic modulus1,2 and that the temperature dependence of the elastic modulus must be taken into account if reliable determinations of the activation energy for creep are to be made. In addition, measurements of the elastic constants of solid solutions are needed to allow one to assess the modulus interaction contribution to solid-solution Strengthening.3-5 Pelloux and Grant6 have demonstrated that substantial solid-solution strengthening at room temperature and elevated temperatures occurs when refractory metal solute atoms are added to nickel. While the high-temperature elastic properties of pure nickel have been measured by a number of authors,7-10 the elastic properties of nickel-based refractory metal alloys have not been determined. The purpose of this paper is to report on measurements of Young's modulus of polycrystalline Ni-W alloys at elevated temperatures. It is expected that these measurements will be valuable to studies of the mechanical properties of nickel-based refractory metal solid solutions. I) EXPERIMENTAL Young's moduli of polycrystalline samples were determined by a dynamic method in order to reduce high- temperature anelastic and plastic relaxations. The samples were forced in transverse free-free vibration; that is, both ends of the sample were unrestrained and the vibration was transverse to the long axis. The fundamental resonant frequency was determined by the Forster method.11 The analysis of this type of vibration which was formulated by Rayleigh,12 Timo-chenko,13 and pickett,14 and reviewed by Fine," leads where fn is the resonant frequency of the nth mode, r is the radius of the circular cross section. L is the specimen length, ßn is 1.5056 for free-free vibration in the fundamental mode of vibration, 6 is the mass density, and E is Young's modulus in the axial direction. This equation can be transformed into: E = 9.17605 x 10-6(L/D)E/Lf2 [2] where E is Young's modulus in psi, L is the length in inches, d is the diameter in inches, W is the weight in grams, and f is the resonance frequency in cps. Eq. [2] was further modified in order to take account of the thermal expansion of the samples. The resulting correct term is: where the thermal expansion coefficients for nickel and tungsten, respectively. Xw is the atom fraction of tungsten in the sample and T is the temperature in "C. The treatment of the thermal expansion coefficient as a linear function of composition seems sufficiently accurate since an error of 25 pct in the expansion coefficient will result in only a 0.3 pct error in the modulus at 1000°C. A) Apparatus. The equipment for this investigation has been described by Lytton et al.16 Several modifications of the equipment have been made. The most significant change involved replacing the detector crystal transducer with a magnetic transducer. A phonographic magnetic transducer was employed as a sensing device since the contact pressure necessary to produce a stable signal is much less than that for a crystal transducer. This magnetic transducer is also not affected by conditions of high temperature and vacuum which are present in these experiments. The vacuum was 10-5 torr at room temperature and about 5 x 10-4 torr at 900°C. This was sufficient to prevent surface contamination of the samples during the tests. The samples were heated in an elliptical furnace with a quartz lamp at one focal line and the sample at the other, as described by Lytton et a1.16 The temperature of the sample was measured by monitoring the

Jan 1, 1969

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid iron alloys containing chromium and nickel has been measured in the temperature range 1550° to 1700°C at nitrogen pressures to 1 ah. The solubility surface has been determined for the iron corner of the liquid metallic ternary to 21 pct Cr and 11 pct Ni. The nitrogen solubility increases markedly with increasing chromium concentration. The effect of nickel and the bilinear effect of chromium and nickel are less pronounced. The solubility data are presented, and interaction coefficients are determined from them. THE solubility of nitrogen has been determined in liquid Fe-Cr-Ni binary and ternary alloys. The work in this laboratory has been directed toward a relatively limited composition range, that is to 20 pct Cr and 10 pct Ni. Humbert and Elliott1 studied the entire ternary; but their investigation was, understandably, limited in this region. The region considered here is of the greatest commercial interest. Knowledge of the solubility in these alloys is important for accurate control of the nitrogen levels in various stainless alloys. Also, the solution behavior is of theoretical interest because of its deviations from ideal dilute solution rules at moderate chromium levels. The nitrogen solubility in the iron binaries has been reviewed extensively by Pehlke and Elliott,2 particularly with respect to the dilute solution interaction parameters. More recently, there has been some interest in accurate descriptions of solute interactions in non-dilute solutions. Most of the investigators have adopted a power series fit to accommodate any non-linearity of the data. The Taylor series expansion is adopted here, using Scimar's notation3 for the interaction coefficients. An alternate method, instead of requiring higher-order expansions, is to restrict the range of the composition variables. A planar solubility surface may be fitted to the data and its range of validity determined. If the axes of this region are displaced from the usual origin—the solvent pure iron—a change in standard state is required for the solution reaction. The standard state for nitrogen in iron is commonly taken as the hypothetical 1 wt pct solution of nitrogen in pure iron. However, for an alloy of appreciable solute concentration, e.g., 13 pct Cr or 18 pct Cr-8 pct Ni, it would be convenient to use that base composition as the solvent and redefine the solution reaction in terms of that particular solvent. A brief derivation follows, defining the free energy of solution in an alloy solvent. Following the treatment by Darken and Gurry,4 for a nitrogen pressure of 1 atm: N (pure component) = N (1 wt pct in solvent) [l] AG=RT ln100/ wt pct N in solvent Taking this reaction for an alloy solvent less the same reaction for a pure iron solvent the relation between nitrogen in pure iron and an alloy is: N (1 wt pct in Fe) = N (1 wt pct in alloy) [2] AG = RT[ln(wt pct N in Fe) - ln(wt pct N in alloy)] Adding ½ N2(g) to each side and subtracting N (1 wt pct in Fe) = ½N2(g), the total free energy for solution of nitrogen in an alloy, referred to nitrogen at infinite dilution, is given by: ½N2 (g) = N (wt pct in alloy) L3] AG°3 = -RT ln(wt pct N in alloy )PN =1 atm Interaction parameters have their usual meaning when ?G°/RT is differentiated with respect to the proper composition coordinate. If desired, the dilute alloy treatment may be utilized with the new reference composition as the solvent. This has. indeed, been done by Small and pehlke5 in their analysis of nitrogen solution in liquid 18-8 alloys. The Sieverts' technique was used for this investigation on an apparatus previously described.6 The materials used in this program were: Ferrovac-E iron, 99.95 pct, Crucible Steel Co.: chromium, 99.95 pct, Union Carbide Metals Co.; nickel, 99.9 pct, International Nickel Co. Recrystallized alumina crucibles were used with no evidence of crucible-melt reaction. RESULTS The locations of the ternary compositions investigated are shown in Fig. 1. The data of Turnock7 and small8 have been alluded to in other papers.5'6 There were no departures from Sieverts' law observed for

Jan 1, 1969

By J. C. Williams, M. J. Blackburn

Several of the decomposition processes that can occur in supersaturated phases in a Ti:11.6 wt pct Mo and a Ti:20 wt pct V alloy have been studied by transmission electron microscopy. The deformation induced "marternsitic phase" in the Ti:Mo alloy has been found to have a bcc or bct structure rather than the previously reported hexagonal structure. The morphology of&apos; the transformed region is a rather complex asserrlblage of twins, twinning occurring in one or more systems; this internal twinning has been found to occur on (112). The w phase is formed in both alloys on aging and is present in the Ti:Mo alloy after quenching. The structure of this phase has been confirmed as hexagonal in both systems, however, differences in morphology and stability are found between the two alloys. Thus in the Ti-Mo alloy the w phase has an ellipsoidal morphology with the major axis lying parallel to <111>ß or [0001]w while in the Ti-V alloy the phase forms as cubes, the cube faces lying parallel to {100}ß or {2021}w Some observations on the particle sizes, volume fraction, and composition of the w phase in the Ti-Mo alloy are listed. The mode of formation of The a phase from the (ß + w) structures is also different in the two alloys. In the Ti-Mo alloy the a phase is formed by either a cellular reaction or by the growth of isolated needles, whereas in the Ti-V alloy the a phase is nucleated at an w:ß interface and grow to consume the w phase. Some of the difjerences in behavior of the w phase are attributed to the mismatch between it and the solute enriched ß matrix in which it forms. MaNY transition elements tend to stabilize the bcc or ß-phase when added to titanium. In general two types of phase diagrams are produced, either a ß-stabilized (ß-isomorphous) system, e.g., Ti:Mo, -Ti:V, Ti:Nb, or a ß-eutectoid system, e.g., Ti:Cr, Ti:Fe, Ti:Mn. In previous papers&apos;-4 the phase transformations in the a-phase and (a + ß)-phase alloys have been described and this work has been extended to ß-stabilized systems. Specifically, transformations in the alloys Ti:20 wt pct V and Ti:11.6 wt pct Mo have been studied; in both of these alloys the ß phase is retained at room temperature when quenched from the ß-phase field. A number of phase transformations can occur in such metastable ß phases and the two alloys were chosen to include most of the transformations reported for ß-stabilized systems. We list these possible phase transformations below. Ti:11.6 Mo quenched from >780°C to retain the ß phase: a) The w phase can form on quenching.5 b) Martensite can be produced by subzero cooling or deformation. Two martensite habit planes have been reported in Ti:Mo alloys; (334)ß and (344)ß=6 c) On aging at temperatures <-550° C the w phase is formed before the a-phase.5,7 d) On aging at temperatures >550°C the a phase is formed.7 e) The martensite can be tempered. It has been reported that the a phase rather than the ß phase is precipitated during tempering.&apos; Ti:20V quenched from >660°C to retain the ß phase:9 a) At aging temperatures <260°C separation into two bcc phases occurs. b) The w-phase is produced prior to the a phase on aging at temperatures <-400°C. c) At temperatures 2400°C the a phase is formed directly. T-T-T diagrams describing the temperature and time regimes for the formation of these phases have been published7,9 for a Ti:12 pct Mo and a Ti:20 pct V alloy. We have attempted to investigate these transformations using transmission electron microscopy, however thin foils undergo a spontaneous transformation in all conditions except the equilibrium (a + ß) structure. This transformation has been reported previ0usly10,11 and we will comment on its morphology and nature in the various sections of experimental results. EXPERIMENTAL The compositions in wt pct of the two alloys investigated were: Ti:11.6 Mo, 0.100 02, 0.006 N2, 0.0015 H2 Ti:20V, 0.0574 O2, 0.0111 N2, 0.005 H2 These alloys were cold-rolled to 0.020 in. thick sheet. Specimens were heat treated in vacuum or in inert gas at temperatures >500°C and in a circulating air furnace at temperatures <500°C. Thin foils were prepared using standard techniques, described in detail previously." Dark field micrographs were obtained using high resolution technique. RESULTS Martensitic Transformation in Ti:11.6 pct Mo. Detailed study of the deformation induced martensite is not possible due to a spontaneous transformation which occurs near the edge of thin foils as shown in Fig. 1. Similar transformations have been observed in iron-" and copper-base13 alloys as well as other titanium alloys, but some observations specific to the Ti:1l.6 Mo alloy are listed below. a) The boundaries of these transformed regions are glissile and move under the influence of the electron beam during examination. b) Selected area diffraction indicates the transformed regions have the same structure as the matrix, being separated by tilt boundaries. The misori-

Jan 1, 1969

By G. Nabi, W-K. Lu

Cylindrical specimens of natural dense hematite were reduced to magnetite at atmospheric pressure in H2-H2O mixtures of known composition over the temperature range 1084° to 1284°K. The rate of reduction was measured by the rate of movement of the interface between hematite and magnetite. The diffusion of gases through the gaseous boundary layer, the magnetite layer, and the interfacial chemical reaction were all considered in the interpretation of experimental data. The mass transfer coefficient through the boundary layer was calculated using accepted correlations. Values of the chemical reaction rate constant and the diffusivity of hydrogen in the magnetite phase were determined. THE present investigation is concerned with the reduction kinetics of natural hematite to magnetite by H2-H2O mixtures in the temperature range 1084" to 1284°K at atmospheric pressure. This reaction is the first step in the series of topochemical reactions in the process of reducing hematite to iron. Kinetic information of the simple steps such as hematite-magnetite transformation is necessary in order to have a better understanding of the complex processes of hematite reduction in iron-making. It also has direct industrial significance because magnetic roasting is one of the most important methods in benefication of lean ore.&apos; Although many technical papers have been published on the process of magnetic roasting and iron oxide reduction, very little information is available in the literature concerning the fundamental nature of hematite reduction to magnetite by reducing gases. Hansen et al.2 reduced the dense synthetic pellets of high-purity oxide in CO-CO2 mixtures and determined the reaction rate by weight-loss method. They were able to interpret most of their results by applying the interfacial area control theory developed by Mckewan.3 In contrast, Wilhelm and St. Pierre,4 who studied reduction of hematite to magnetite in H2-H2O mixtures by weight-loss method, stressed that the resistance of the porous magnetite layer to the diffusion of gases cannot be neglected in consideration of the overall reaction rate. In the present study the contributions of interfacial chemical reaction, diffusion of gases through the magnetite phase, and the gaseous boundary layer to the overall reaction rate will be considered. APPARATUS AND PROCEDURE Hematite Specimens Preparation. Natural hematite ore from Vermillon range of Northern Minnesota was selected for the present investigation because of its high purity and thermal stability. Chemical analysis of five samples gave the following average values: 67.52 pct total iron (96.62 pct Fe2O3, 0.28 pct FeO, 0.03 pct metallic iron), 2.53 pct SiO2, <0.07 pct MgO, 0.03 pct CaO, 0.05 pct combined mixture, 0.07 pct loss on ignition, and 0.34 pct other. Cylindrical specimens of 0.93 cm in diam and 2.7 cm in length were drilled from slabs of ore with a water-cooled diamond core drill. These specimens were heated to 1000°C and furnace-cooled. Specimens with silica pockets developed large cracks. The uncracked specimens were heated a second time, and their surfaces were carefully examined with a microscope. Those with hairline cracks or surface inhomoaenitv-- were rejected. Preparation of H2-H2O Mixtures. H2-H2O mixtures were prepared by the combustion of H2-O2, mixtures in a pyrex glass chamber in the presence of a catalyst. Alumina pellets coated with palladium, supplied by Englehard Industries, were used as the catalyst. Purified grades of hydrogen and oxygen were used which were repurified by usual techniques. Hydrogen before entering the combustion chamber was passed through an activated alumina H2O absorption bulb, with copper turning at the top. The cover of this bulb was not made pressure-tight so that any pressure development in the hydrogen line would cause the cover to blow off and also the copper turnings would act as a flame arrester in the case of a flashback from the combustion flame. Oxygen flow rates were measured with a bubble flow meter after purification with 1 pct accuracy. Hydrogen flow rates were measured by "precision wet test meter" and the amount of unburnt hydrogen was accurately measured by a bubble flow meter, after condensing water vapor in the gaseous stream. The Pyrex glass bulb contained concentric Vycor glass tubes as shown in Fig. 1. Oxygen was prevented from diffusing into the hydrogen line by threading platinum wire through pores at the combustion end of gas inlet tube. The glass bulb was heated with a Kanthal heating wire pasted in asbestos paper. The surface temperature of the bulb was measured with a thermocouple and adjusted to remain at approximately 350°C. The gaseous reaction chamber also served as a preheater for gases to avoid thermal segregation. The following sequence of operation was adopted. 1) Nitrogen was passed through the outer concentric tube to purge the catalyst bulb of oxygen. 2) Hydrogen was introduced through the inner tube until a steady flow was obtained. 3) Oxygen was then introduced into the nitrogen stream passing through the outer tube. 4) When combustion had commenced and a flame was visible over the platinum wire, the N2 was turned off.

Jan 1, 1969

By C. G. Bieber, J. R. Mihalisin, R. T. Grant

A growing demand for longer service life of gas turbines has placed increasingly rigorous requiret~rents upon superalloys employed for that application. Long-titne testing at high temperature has revealed that phase transformations occur in all superalloys. A common one of particular interest is o formation. Presented here are studies made to identify a and to characterize its formation and effect on properties in three cast nickel-base superalloys—IN 100 alloy, alloy 713C, and alloy 713LC. Methods are discussed by which o can be eliminated or inhibited in IN 100 alloy and alloy 713C. Evidence was obtained to indicate that some types of o may be more detrimental than others. Limitations in the electron vacancy approach to o prevention are pointed out, and it is shown how alternative approaches, such as reducing a complex superalloy matrix to the form of a pseudo-ternary system permitting equilibrium diagram treatment, lead to additional insights into the formation of in these alloys. AROUND 1960. Beiber1 developed IN 100 alloy, which still remains one of the strongest commercially available nickel-base superalloys. The principle used in the design of this alloy was to produce large quantities of y&apos; phase in a y matrix through the use of copious amounts of aluminum and titanium. In 1963, ROSS&apos; showed that when certain heats of this alloy were held for a long time at 1650°F they formed an acicular phase, subsequently identified as a.3 a is a hard and brittle phase first discovered in the Fe-Cr system by Bain and Griffiths.4 They termed it the "B" constituent. Subsequently this same phase was found in other systems, primarily those of the transition elements, and acquired the name "a" by which it is now known. The crystal structure of the a phase was first determined in the Fe-Cr system in 1950.5 It was shown to be tetragonal with a c/a ratio of about 0.52. as is the case with a found in other systems. This characteristic crystal structure is now the means by which a is identified. In superalloys, such as IN 100 alloy. large amounts of o impair the high-temperature creep strength and drastically reduce room-temperature tensile ductility. Discovery of o phase in some heats of IN 100 alloy quickly led to investigations of other superalloys for similar transformations. It was found that many of the stronger, more highly alloyed. super-alloys were indeed susceptible to o formation. This investigation has been concentrated on three commercial alloys: IN 100 alloy, alloy 713C, and alloy 713LC. J.R.MIHALISIN,MemberAIME, and C.G.BIEBER are with The International Nickel Co., Inc., Paul D. Merica Research Laboratory, Sterling Forest, Suffern, N. Y. R. T. GRANT, Member AIME, is with The International Nickel Co., Inc., Pittsburgh, Pa. Manuscript submitted May 22. 1968. IMD A detailed study has been made of the phase transformations and their relation to a formation along with a consideration of electron vacancy approaches for predicting a-forming propensity in these alloys. EXPERIMENTAL PROCEDURE Phase transformations were studied by light and electron microscopy, electron diffraction, microprobe investigations, and X-ray diffraction. Specimens for light micrographic examination were prepared by conventional grinding and polishing followed by etching with glyceregia (2:l HC1/HNO3 + 3 glycerine by volume). Photomicrographs of stress-rupture specimens were taken adjacent to the fracture unless otherwise noted in the text. Negative replicas for electron microscopy were taken from surfaces electropolished with a solution of 15 pct H2SO4 in methanol. For carbon extraction replication, a solution of 10 pct HC1 in methanol was used. A Siemens Elmiskop I was used for all electron microscopy. Selected-area diffraction studies were made at 80 kv using evaporated aluminum for standardizing the patterns. A nondispersive electron microprobe attachment was used to analyze the extracted precipitates chemically. The fluorescent X-rays were recorded using a flow counter containing P10 gas (90 pct Ar-10 pct methane) with a beryllium window and a single-channel pulse-height analyzer. The pulses from the analyzer were passed to a scaler-ratemeter and differential curves of counting rate vs pulse amplitude were obtained. The base line of the analyzer was driven with a synchronous motor at 0.5 v per min and a channel width of 0.5 v. The time for 105 counts was printed out for each 0.5-v increment. The microscope was operated at 80 kv with beam currents of 1 to 20 pa. This equipment detects elements from atomic number 13 to 40. X-ray diffraction studies were usually made on residues electrolytically extracted in 10 pct HC1 in H2O, although in one case a pattern was obtained from an etched surface of a metallographic specimen. A Siemens Crystalloflex IV was used with iron-filtered CoKa radiation. X-ray patterns were recorded using a goniometer speed of : deg per min. The scintillation counter and pulse-height analyzer operated at a channel height of 10 v and a channel width of 12 v. The equipment was calibrated with a powdered gold standard. The residues usually contained a number of phases. several of which could not be found in the ASTM card file. In addition, as is shown for the case of a phase in IN 100 alloy, other phases had a somewhat different lattice parameter from that reported in the ASTM card file, making it difficult to separate and identify constituents by comparison with ASTM d spacings. For these reasons, phases were identified on the basis of the lattice parameter obtained by indexing the ob-

Jan 1, 1969

By Ö. Valla, A. Muan, K. Grjotheim

The solid miscibility gap between CaO and "FeO" in the system CaO-"FeO" in contact with metallic iron gradually closes as MnO is added as a third component. On the liquidus surface of the system CaO-"FeO"-MnO, this situation gives rise to a boundary curve which originates in the bounding system CaO-&apos;&apos;FeO", proceeds a short distance into the composition triangle of the ternary system, and then vanishes. A new approach has been used to follow the course of this boundary curve. It is shown that the curve vanishes at a much lower temperature and at much lower MnO contents than has been inferred previously. The oxides CaO, "FeO", and MnO together with SiO2 are the major components of the slag phase formed in the basic oxygen process. Hence, the system CaO-"Fe0"-MnO is of considerable technological interest. In addition, the system is theoretically interesting. The three oxides above all have sodium chloride structure. The size differences among the cations are such that in the bounding "binary"* systems CaO-MnO and "FeO"-MnO complete solid-solution series are formed,1,2 whereas in the system CaO-"FeO" there is only limited mutual solubility in the solid state,3 see Fig. 1. Hence, a solid miscibility gap exists in a part of the "ternary"* system Ca0-"Fe0"-Mn0, and a liquidus boundary curve originates at the peritectic point, point a in the insert in Fig. 1, in the system CaO-"FeO", extends a certain distance into the ternary system, and then vanishes. Very little quantitative information on the system Ca0-"Fe0"-Mn0 is available in previous literature. Fischer and Feischer4 sketched isothermal sections at 1600° and 1700°C, and estimated that the vanishing boundary curve extends to approximately 1650°C and a composition of 42 wt pct MnO. The work to be described in the following was aimed at locating experimentally the "vanishing" liquidus boundary curve, determining its end point, and deriving representative isothermal sections below and above the temperature of the end point of this curve. EXPERIMENTAL METHODS The phase relations were determined by the well-known quenching method. (For a description of this method as applied to oxide systems, see the original paper of Shepherd, Rankin, and wright.5) Prereacted oxide mixtures of desired compositions were contained in iron crucibles and heated in a vertical tube furnace in an atmosphere of purified nitrogen. After equilibrium was judged to have been attained, the samples were quenched to room temperature, the phases present were identified by microscopic and X-ray examination, and total iron oxide contents were determined by chemical analysis. "Fisher Certified" reagents (MnCO3, CaCO3, Fe2O3, and Fe) served as starting materials. The calcium carbonate and ferric oxide were heated in air at 400° and 800°C, respectively, for 24 hr prior to use. Manganese oxide was prepared by decomposing the carbonate in a graphite crucible in hydrogen atmosphere at 1000°C. The product was ground under acetone to -100 mesh. The iron powder was used directly without any preparation. Dicalcium ferrite was used as a starting material for some mixtures. It was made by mixing some of the above prepared CaCO3 and Fe2O3 in proportions corresponding to the formula 2CaO. Fe2O3. This mixture was then fired in air for

Jan 1, 1969

By J. H. Swisher

The rate of internal sulfidation of austenitic Fe-Ti alloys in H2S-H2 gas mixtures is controlled primarily by sulfur diffusion, with counterdiffusion of titanium playing a minor role. At temperatures below 1100°C, enhanced diffusion along grain boundaries becomes important. The rate of internal sulfidation at 1300°C is approximately equal to the rate computed from the sulfur diffusion coefficient. The diffusion coefficient of titanium in y iron has been determined from electron microprobe traces in the base alloy near the subscale interface. The solubility of sulfur in Fe-Ti alloys has been measured in the temperature range from 1150° to 1300°C. The equilibrium sulfur content is found to increase with titanium content, due to the large effect of titanium on the activity coefficient of sulfur. The Ti-S interaction becomes stronger as the temperature decreases. TITANIUM as an alloying element in stainless steels is an effective scavenger for interstitial impurities, carbon in particular. Titanium is known to form stable sulfides; however extensive thermodynamic data on the Ti-S system are not available. Schindlerova and Buzek1 have shown that the Ti-S interaction in liquid iron is moderately strong. There have been no previous studies of the Ti-S interaction in solid iron. Internal sulfidation of Fe-Mn alloys was the subject of a recent investigation by Herrnstein.2 He found the rate of internal sulfidation to be an order of magnitude greater than predicted from available solubility and diffusivity data. A satisfactory explanation for the discrepancy could not be given. In the present study, the solubility of sulfur in austenitic Fe-Ti alloys was measured using a standard gas equilibration technique. Fe-Ti alloy specimens were also internally sulfidized. The rate of internal sulfidation was measured as a function of temperature and alloy composition. Supplementary electron micro-probe measurements were made to provide additional information on the nature of the internal sulfidation process. EXPERIMENTAL The starting materials were alloys containing 0.12, 0.24, 0.38, and 0.54 wt pct Ti. The alloys were made in an induction furnace by adding titanium to electrolytic iron that previously had been vacuum-carbon-deoxidized. The major impurity in the alloys as determined by chemical analysis was carbon. The carbon content of the alloys averaged about 100 ppm; metallic impurities were presented in concentrations of 50 ppm or less. Specimens were made in the form of flat plates, 0.03 by 2 by 4 cm for the equilibrium measurements and 0.5 by 1.5 by 3 cm for the rate measurements. The experiments were performed in a vertical resistance furnace wound with molybdenum wire and containing a recrystallized alumina reaction tube. In the gas train, flow rates of the reacting gases were measured using capillary flow meters. The source of H2S was a mixture of approximately 2 pct H2S in H2, which was obtained in cylinders from the Matheson Co. A chemical analysis was provided with each cylinder. The H2-H2S mixture was diluted with additional hydrogen to obtain the desired ratio of H2S to H2, and the resulting mixture was diluted with 30 pct Ar to minimize thermal segregation of H2S in the furnace. Argon was purified by passage over copper chips at 350°C and subsequently over anhydrone. Hydrogen was purified by passage over platinized asbestos at 450°C and then over anhydrone. The H2-H2S mixture was purified by passage over platinized asbestos and then over Pas. The samples used in the solubility measurements were analyzed for sulfur by combustion and iodometric titration. The subscale thickness in the internally sulfidized samples was measured on a polished cross section, using a microscope with a micrometer stage. Electron microprobe traces for titanium in solution were made on several samples that had been internally sulfidized. A Cambridge microanalyzer was used, and the known titanium content at the center of the specimen was used as a calibration standard. The procedure for the microprobe measurements will be described further when the results are presented. RESULTS AND DISCUSSION Equilibrium Data. Fig. 1 shows the sulfur concentration as a function of gas composition for three alloys equilibrated at 1300°C. The dashed line is based on data published by Turkdogan, Ignatowicz, and pearson3 for pure iron. The breaks in the curves are the saturation points for the alloys. The fact that the initial slope decreases with increasing titanium content indicates that titanium interacts strongly with sulfur in solution. To obtain information on the composition of the precipitating sulfide phase, the measurements described in Fig. 1 were extended to higher sulfur partial pressures. These results are shown in Fig. 2. (The initial portions of the curves are reproduced from Fig. 1.) The highest PH2s /pH2 ratio used is believed to be below the ratio required for the formation of a liquid sulfide phase. Time series experiments were used to study the approach to equilibrium in the samples. It was found that equilibrium with the gas phase was reached in less than 4 hr at 1300°C.

Jan 1, 1969

By A. Mitchell

An approximate phase diagram has been developed for the CaF2-CaC2 system, indicating a eutectic point at 1240°C, Ncac2 = 0.13, and no detectable solid solution in either phase. The liquidus line is shown to correspond to a simple c22- ion in solution. A thermo-chemical study of&apos; the reaction between carbon-saturated Ni-Ca alloys and CaC2-CaF2 liquids indicates that lhe Raoullian activity coefficient of CaC2 in dilute solution in Cap2 al 1500°C lies between 8 and 10. Some effects of the stabilily of Cap2-CaC2 solutions at high temperatures on electroslag remelting praclice are outlined. THE alkaline earth acetylides. MIIC2, have a reasonably high thermochemical stability at high temperature in the solid state,&apos; with the exception of magnesium, which forms an unstable acetylide at low temperatures (-500°C) and a carbide, Mg2C3, in the range 700&apos; to 1000°C. The acetylides of calcium and barium have been shown to have limited solubility in their respective chlorides,&apos; and further these solutions contain the acetylide as a C: ion.&apos; The equivalent magnesium solutions have not been studied. Although calcium "carbide" is used as a desulfuriz-ing reagent in steelmaking. and is possibly present as an acetylide-oxide phase in very basic electric arc practice slags, the acetylide ion appears to be substantially unstable in a silicate slag.* As a conse- *This instability arises from equilibria in the reaction: CaC2 + CO = (Ca0) + 3C where the low intrinsic solubility of CaC2 in silicate lattice, and the low activity of CaO in a silicate solution where CaO/Si02 < 1, combine to give a very small equilibrium concentration of CaC2 in solution in such silicate slags at temperatures in the region of I 500°c, even under carbon-saturated conditions. Under highly basic conditions, a liquid CaO-CaC2 phase may separate from the silicate system quence of this, the possibility that reactions involving CaC2 in silicate solutions are of importance to general steelmaking practice is remote. However, in operations involving a slag primarily based on a halide, or alkaline earth oxide, we must take into account the possibility that CaC2 will appear in quantities sufficient to significantly affect both the chemical and physical properties of the slag. The work outlined below presents a study of the CaF2-CaC2 system intended to provide sufficient data to allow an estimate of the importance of this system to electroslag remelting and welding practice. However, we should indicate at this point that there will be other processes, e.g., heat treatment, flux cleaning of castings, fused salt electrolysis, and so forth, where alkaline-earth halide fluxes are in contact with carbon, graphite, or carbides, and where halide-acetylide solutions must be taken into account. EXPERIMENTAL 1) Structural Studies. In view of the difficulty ex-perienced in handling CaC2 prepared from calcium turnings and propane gas at 700°C, it was decided to use solutions prepared directly in the equilibration apparatus, Fig. 1. The starting materials were: a) Ni-Ca-C alloy, prepared by adding calcium to liquid nickel held under calcium fluoride in an induction-heated graphite crucible; b) calcium fluoride, prepared by fusing calcium fluoride powder (British Drug House "EXTRA PURE") calcium fluoride in an induction-heated graphite crucible, in air, followed by electrolysis between graphite electrodes at 1 amp cm-2 density, for 10&apos; coulombs per g CaF2. This procedure decomposes the CaO produced by hydrolysis during the fusion step, replacing it by CaC2; Ca2+ + 2e-Ca*(l) Ca*(l) + 2C(gr)-(CaC2)caF2 O2- -2e-O*(g) O*(g) +C(gr)-CO(g) This results in a composition of between 2 and 5 wt pct CaC2 in CaF2. Fifty grams (in lumps) of this material were placed in a graphite crucible, together with Ni-Ca-C alloy (averaging 20 wt pct Ca), and the equilibration apparatus assembled. The alloy reacted with the crucible at high temperature to give CaC2, which dissolved in the calcium fluoride solution to give the desired composition. Cooling curves were plotted manually for these liquids, with rapid stirring and CaF2 seeding to minimize supercooling, and using a Pt/Pt 13 Rh thermocouple calibrated on the freezing points of nickel and copper. This gave a reproducibility of ±0.l°C. and an absolute accuracy of the thermocouple of ±l°C. An example curve is shown in Fig. 2, with the CaF2 end of the binary system in Fig. 3. The CaF2-CaC2 ingots were crushed, under dry nitrogen, and sampled for chemical analysis and X-ray examination. Analytical details are given in the Appendix. Powder diffraction data indicated that the only phases present in all samples examined were calcium fluoride and tetragonal (Types I and 111) calcium acetylide,4 with no evidence of solid solutions or compound formation. 2) Thermochemical Studies. The apparatus used to obtain activity data on CaC2 in these systems is shown in Fig. 4. It consists of an arrangement whereby the graphite crucible and its contents (CaF2-CaC2. Ni-Ca-C) can be rapidly cooled without exposure to air. Trial experiments to determine an equilibration time by ap-

Jan 1, 1969

By R. D. Pehlke, W. M. Small

The effect of added alloying elements on the solubility of nitrogen in a liquid alloy of 74 wt pct Fe. 18 wt pct Cr, and 8 wt pct Ni has been studied. At 1600°C and 1 atm nitrogen pressure, aluminum, chromium, columbium, manganese, molybdenum, tantalum, and vanadium increase the solubility of nitrogen in the liquid 18 Cr-8 Ni alloy, whereas additions of cobalt, copper, nickel, silicon, tin, and tungsten decrease the solubility. Interaction parameters based on a constant ratio of iron, chromium , and nickel have been used to quantitatively define the changes in nitrogen solubility. INVESTIGATIONS on the solubility of nitrogen in liquid iron have usually treated the pure metal, and often the influence of a single added element. Pehlke and Elliott1 carried out a comprehensive study on the influence of alloying elements on nitrogen solubility in liquid iron, and compared their results with previous studies. Turnock and pehlke2 have recently reported a study on the solubility of nitrogen in multicomponent liquid iron alloys. The original interaction parameter proposed by wagner3 was successfully employed in these studies. The need for obtaining information on the gas solubility in more complex alloys is indicated by the increasingly significant role played by dissolved gases in the processing of iron-based materials. The commercial stainless steels, for example, represent an area where data on nitrogen solubilities are required as a function of composition, temperature, and gas pressure. The nitrogen solubility in liquid Fe-Cr-Ni alloys has been studied by Humbert and Elliott.4 Their investigation covered the entire ternary system, and attempted to use data from binary alloys to predict nitrogen contents in liquid ternary alloys. Langenberg,5 using a method developed by Morris and buehl,6 calculated the nitrogen solubilities in multicomponent iron alloys from data available on binary iron alloys at 1600°C. Nelson,7 using a regular-solution model, extended this prediction to include the effect of temperature. Chipman and corrigan8 and Turnock and pehlke2 also employed empirical methods to calculate nitrogen solubilities in liquid multicomponent iron alloys. In order to provide a basis for predicting nitrogen solubility in liquid stainless steels, and to extend the data available for thermochemically modeling systems of this type, the following investigation was carried out. The study involved measupements of nitrogen solubility in a nondilute alloy and examination of the influence of a small addition of an alloying element on the nitrogen solubility. The study was focused on a very narrow range Of composition in the vicinity of 18 wt pct Cr-8 wt pct Ni (herein referred to as 18-8) with special emphasis on the change of.nitrogen solubility with the addition of a fourth metallic element. EXPERIMENTAL PROCEDURE A Sieverts&apos; apparatus, described previously,1,2 was used in this investigation. The charge materials were contained in a recrystallized alumina crucible and inductively melted. Additions were dropped from a glass side-arm. All materials were hydrogen-refined and vacuum-treated to eliminate or minimize the oxygen content. The source and purity of materials is given in Table I. The initial metallic charge was heated to approximately 1000°C and held under vacuum for 30 to 45 min as a means for removing hydrogen and adsorbed gases. Argon was used as the calibrating gas to determine the "hot volume". The average hot volume of the system was approximately 50 cu cm STP and a few experimental runs were made using a reaction bulb with a hot volume of 80 cu cm. The temperature range studied was from 1550° to 1700°C and the temperature was measured optically. THEORETICAL PRINCIPLES General Discussion. Nitrogen dissolves in liquid iron alloys according to the reaction: 1/2N2(g) = N (wt pct in solution) [l] The equilibrium constant, K1, for this reaction is written as:

Jan 1, 1969

By F. G. Jones, R. D. Pehlke, H. E. Gardner

The solubility of nitrogen in liquid Fe-18 pct Cr-8 pct Ni-0. 7 to 2.3 pct A1 alloys has been measured up to the solubility limit for the formation of aluminum nitride in the temperature range 1600° to 1700°C uszng the Sieverts&apos; method. The solubility of nitrogen in 18-8 stainless steel increases with increasing aluminum content. Based on a nitride composition, AlN, the standard free energy of formation of aluminum nitride from the elements dissolved in liquid 18-8 stainless-steel alloys has been determined to be: ?G° = -42,500 + 20. IT in the range from 1600° to 1700° C. EVANS and pehlke1 have measured the equilibrium conditions for the formation of aluminum nitride, AlN, in liquid Fe-A1 alloys. The present study extends that work to the more complex solvent, liquid 18 pct Cr-8 pct Ni (18-8) stainless steel. Recent work by Small and pehlke2 has dealt with the effect of fourth-element additions on the solubility of nitrogen in 18-8 base alloys. They found the effect of aluminum additions, up to 0.74 pct, on the solubility of nitrogen to be small. The present study covered the range from 0.74 to 2.28 pct aluminum, and by extending the composition range may be used to better define the effect of aluminum on the nitrogen solubility in these alloys. EXPERIMENTAL PROCEDURE The Sieverts&apos; method was used to measure the equilibrium solubility of nitrogen gas in liquid 18-8 stainless steel alloys containing 0.74, 1.49, 1.93, and 2.28 pct Al. The solubility was measured as a function of the nitrogen gas pressure at temperatures of 1600°, 1650°, and 1700°C. The apparatus used is the same as described by Small and Pehlke.2 The 100-g melts were made from Ferrovac-E high-purity iron, Crucible Steel Co.; 99.95 pct Cr, Union Carbide Corp.; 99.9 pct Ni, International Nickel Co.; and 99.99+ pct Al, Aluminum Co. of America. The aluminum was charged at the bottom of the crucible, surrounded by nickel and iron. The chromium was packed into the interstices to minimize vapor transport of the aluminum during initial melting. The hot volume of the system, measured for each melt with argon, ranged from 45 to 55 standard cu cm with a temperature coefficient of —8 x 10-3 cu cm per °C. The melt temperature was measured with a Leeds and Northrup disappearing-filament type optical pyrometer sighted vertically downward on the center of the melt surface. The temperature calibration of the system by Small and pehlke2 was assumed. Two problems are involved in determining the solubility product of a solid, metal nitride phase in liquid iron alloys. These are: 1) establishing the point of departure from Henrian behavior at the solubility limit of the metal nitride phase; and 2) determining the composition of the solid nitride which is precipitated. Determination of the solubility product of AlN was made by admitting small amounts of nitrogen into the reaction bulb until the deviation from Sieverts&apos; law was clearly evident in the form of a pressure halt. To obtain the solubility product at several temperatures during one run the following procedure was used: 1) add increments of nitrogen to determine the Sieverts&apos; law line at the lowest desired temperature; 2) continue to add nitrogen to precipitate a small amount of the nitride phase; 3) increase the melt temperature 50°C to dissolve the precipitated nitride; 4) repeat step 2 until either a nitride formed or the system reached ambient pressure; if a nitride formed at 1650°C, the sequence was repeated at 1700°C. The composition of the precipitated phase was checked by an X-ray diffraction pattern obtained from powder scraped from the surface of the solidified 1.93 pct A1 melt. RESULTS AND DISCUSSlON Solubility Measurements. Fig. 1 is a typical nitrogen-absorption curve obtained from measurements on a 1.93 pct A1 alloy. Since the initial absorption of nitrogen follows Sieverts&apos; law the nitrogen solubility is plotted as a function of the square root of the pressure of nitrogen gas in the reaction bulb. The results of the solubility measurements for all alloys studied are summarized in Table I. The slope of the Sieverts&apos; law line for each alloy was determined. Since this is also the solubility of nitrogen at 1 atm pressure of nitrogen gas, the latter designation is used for the data. It should be noted. however, that in most cases the value lies above the solubility limit for AlN. Fig. 2 shows the effect of aluminum on the solubility of nitrogen at this reference pressure and as a function of melt temperature. The solid portions of the lines represent attainable solutions; the dashed regions lie above the limit for precipitation of AlN.

Jan 1, 1969

By R. L. Bell, T. G. Langdon

A technique was developed- for determining the grain strain, and hence the grain boundary sliding contribution, occurring during the high- temperature creep of a magnesium alloy, from the distortion of a grid photographically printed on the specimen surface. The results were compared with those obtained from measurements of grain shape, both at the surface and interrwlly, and it was concluded that the grain shape technique may substantially underestimate the grain strain and overestimate the sliding contribution due to the tendency for migration to spheroidize the grains. ALTHOUGH a considerable volume of work has been published on the role of grain boundary sliding in high-temperature creep, many of the estimates of Egb (the contribution of grain boundary sliding to the total strain) have been in error due to the use of incorrect formulas or inadequate averaging procedures.&apos; One of the most easy and convenient measurements from which to compute Egb is that of v, the step normal to the surface where a grain boundary is incident. Unfortunately, this parameter is also the one associated with the treatest number of pitfalls. Values of v have been used to calculate Egb from the equation: egb =knrVr [1] where k is a geometrical averaging factor, n is the number of grains per unit length before deformation, v is the average value of v, and the subscript ,r denotes the procedure of averaging along a number of randomly directed lines. If the dependence of sliding on stress were assumed, it would be possible, in principle, to calculate k from the known distribution of angles between boundaries and the surface. This in itself is difficult because the distribution depends on the history of the surface,&apos; but the problem is even further complicated by the fact that v depends on other factors such as the unbalanced pressure from subsurface grains.3 However, the great simplicity of the measurement procedure for v makes it highly desirable that this problem of k determination should be overcome. In the present experiments, this was achieved by the use of an indirect empirical method in which the grain strain, eg, at the surface was determined by the use of a photographically printed grid. The assumption here is that the total strain, et, is simply the sum of that due to grain boundary sliding, egb, and that due to slip or other processes within the grains, eg. SO that: Et = Eg + Egb [2] Thus k is given by: In practice, it is customary to indicate the importance of sliding by expressing it as a percentage of the total creep strain; this quantity is termed y (= 100Egb/Et). The determination of Eg from a printed grid within the grains avoids the difficulties due to boundary migration which should be considered when the grain strain is calculated from measurements of the average grain shape before and after deformation. As first pointed out by Rachinger,4,5 however, this latter technique has the particular advantage that it can also be applied in the interior of a polycrystal. Recently, several workers have produced evidence on a variety of materials6-&apos;&apos; to support the observation, first made by Rachinger on aluminum,4,5 that 7 can be very high, 70 to 100 pct, in the interior, even when the surface value, determined from boundary offsets, is very much lower.10&apos;11 Although there have been criticisms both of the shortcomings of the grain shape technique&apos;&apos; and of the different procedures used to determine y at the surface,&apos; it seemed important to check whether measurements of sliding by grain shape gave values of y which were truly representative of the material. In the present experiments, grain shape measurements were therefore made both at the surface and in the interior for comparison with one another and with the independent measurements of grain strain using the surface grid technique. EXPERIMENTAL TECHNIQUES The material used in this investigation was Magnox AL80, a Mg-0.78 wt pct A1 alloy supplied by Magnesium Elektron Ltd., Manchester. Tensile specimens, about 7 cm in length, were prepared from a 1.27-cm-diam rod, with two parallel longitudinal flat faces each approximately 3 cm in length. The specimens were annealed for 2 hr in an oxygen-free capsule, at temperatures in the range 430° to 540°C, to give varying grain sizes, and, prior to testing, the grain size of each was carefully determined using the linear intercept method. This revealed that the grains were elongated -0.5 to 5 pct in the longitudinal direction. Testing was carried out in Dennison Model T47E machines under constant load at temperatures in the range 150" to 300°C. At temperatures of 200°C and below, tests were conducted in air with the polished flat faces coated with a thin film of silicone oil to prevent oxidation; at higher temperatures, an argon atmosphere was used. To determine v,, each test was interrupted at regular increments of strain and the specimen removed from the machine. At the lower strains, when v, was less than about 1 pm, measurements were taken on a Zeiss Linnik interference microscope;

Jan 1, 1969

By Erwin Pink

It has been pointed out in a previous publication&apos; that, for a given strain rate, serrated yielding can be observed only at certain test temperatures. Fig. 1 shows the results obtained for polycrystalline and re-crystallized tantalum, Va group in the periodic table of elements, where serrations in the course of deformation match the decrease of total elongation. However, there was no evidence of repeated yielding when testing molybdenum or tungsten, VIa group, at similar conditions, i.e., annealed and air-cooled samples (serrations have been found in quenched tungsten2). The reason for the observed serrations in the stress-strain curve are dissolved impurities on interstitial sites of the lattice. Of importance is the concentration of oxygen, carbon, and nitrogen, which are in random solution. Two methods to calculate the limiting concentrations for serrated yielding have been evaluated and applied with more or less success in estimating the role of carbon and nitrogen in mild steel.3 J. Friedel4 has given two equations, which determine the upper and lower strain rates i for the appearance of serrations at a certain test temperature: W denotes the binding energy of the interstitial atom, -1 ev for refractory metals;5 e&apos; the portion of continuous strain in the discontinuous stress-strain curve, measured as -3x10-3; b the Burgers vector, c the concentration, see Table 11, in atom fractions; p the dislocation density, -2 X l09 per cm2 at an average stress ?, -15 kp per mm2 at medium strain. k stands for the Boltzmann constant, T for the absolute temperature, and D for the diffusion coefficient. Table I. Eq. [1], for a given strain rate, determines the minimum temperature, and [2] the maximum temperature, below or above which no "dynamic strain-aging" can occur. According to the calculation, which uses the given quantities, serrations should only be observed within the cross-hatched temperature regions in Fig. 1, and this is in good agreement with the experiment. The effect of varying impurity concentrations is indicated schematically in Fig. 2: only Eq. [I] is affected. Setting Eq. [I] equal to [2], one can calculate the limiting concentration cmin which first causes serrations. The second method uses the aging condition by Cottrell and Bilby6,7 \£i/ \ n. a / where n(t) is the number of impurity atoms, which segregate at a dislocation line of 1 cm length after the time t (t in our case is the time between "repeated yield drops" in the serrated curve, or, the time until the above mentioned strain E&apos; is obtained, i.e., -1 sec for medium intensity or serrations). no is the number of impurity atoms in 1 cm3 and A = Qb4ep[(1 + v)/(l - v)], derived from equations given in Ref. 7. p is the shear modulus, 18,800 kp per mm2 for tantalum, 12,200 for molybdenum, AE the tetragonal distortion caused by interstitial impurities in a bcc lattice (approximately 0.4 for both tantalum and molybdenum) and v Poisson&apos;s ratio (0.35 for tantalum, 0.30 for molybdenum). From Eq. [3], combined with the condition for a pronounced yield drop as formulated by cottrel16 (at least one impurity atom segregated at the unit length of a dislocation), again a no min, and hence the concentration Cmin can be calculated.

Jan 1, 1970

By O. N. Carlson, D. G. Alexander

THE hardness anisotropy of metals and alloys has been of increasing interest in recent years but silicon ferrite,1 niobium,2 and tungsten3,4 are the only bcc metals about which this type of information has been reported. This investigation was carried out on vanadium and chromium single crystals in an effort to determine to what degree the hardness variations observed in these metals are due to orientation effects and to compare their behavior with other bcc metals. In earlier work the authors had observed a small angular dependence in the Diamond Pyramid Hardness of single crystalline vanadium on the (100) plane but no anisotropic effects were noted on either the (110) or (111) planes. At the suggestion of R. G. wheeler5 it was decided to investigate this effect in greater detail using the more asymmetric Knoop indentor. The vanadium metal used in the study was prepared by the aluminothermic reduction of V2O5 followed by electron beam melting.6 The principal analyzed impurities were 230 ppm C, 230 ppm O, 65 ppm N, 90 pprn Al, Cr not detected, 50 ppm Fe, 60 ppm Ni, and 200 ppm Si. The chromium was an iodide-refined product obtained from the Chromalloy Corporation. Analysis of this material showed the following amounts of impurities present: 10 ppm C, 9 ppm O, 2 ppm N, 0.4 ppm H, 3 ppm Al, 2 ppm Ca, 2 ppm Cu, 20 ppm Fe, 1 ppm Mg, 0.3 ppm Mn, 1 ppm Mo, 3 ppm Ni, 10 ppm Si, and 1 ppm V. Single crystals of both metals about 1 cm in diam and 10 cm in length were grown by an arc-zone melt- ing technique.7 The chromium crystal was annealed at 1600°C for 6 hr in a purified argon atmosphere to remove any strains or inhomogeneities, but the vanadium was tested in the as-grown condition. The crystals were oriented by the Laue back-reflection method and then sectioned with a spark cutter into individual specimens with a (loo), (110), or (111) plane parallel to the crystal surface. They were mounted in Lucite and carefully ground to a flat surface. The vanadium specimens were then electropolished in a 6 pct perchloric acid-methanol mixture while the chromium specimens were mechanically polished on a Syntron vibratory polisher using an alumina abrasive. The orientation of each crystal was then rechecked by the back-reflection X-ray method. All of them were found to lie within 2 deg of the desired orientation with the exception of the (110)-Oriented chromium crystal which was within 4 deg. Microhardness impressions were taken at 10 deg intervals from the common (110) direction by rotating the crystal in the plane of the crystal surface. A Knoop indentor was used with a 400-g load on the vanadium crystals and an 800-g load on the chromium. The hardness values are averages of 6 impressions and standard deviations were calculated for each set of data. The values reported for the (111) plane of vanadium are based on from 10 to 15 measurements for each point. The microhardness results for vanadium and chromium are plotted as a function of the angular rotation of the long axis of a Knoop indentor from the (110)

Jan 1, 1970

By S. S. Lisnyak, B. D. Lichter

An important question in the study of the "hot corrosion" phenomenon (i.e., accelerated oxidation of Ni-Cr-base and Co-Cr-base "superalloys" in the presence of sulfur) is the condition of formation and physico-chemical properties of different sulfides in the system Ni-Co-Cr-S. seyboltl has observed the presence of ((chromium-rich" sulfides of compositions M3S4, and M2S3 in the scales of superalloys after hot corrosion; however, as he points out, much confusion exists as to the identity of sulfides found on Ni-Cr and Co-Cr alloys. According to the literature,&apos; ternary sulfides, e.g., NiCr2S4, (monoclinic structure) and CoCr2S4 (spinel structure) exist in these systems. Therefore, it is likely that these compounds are found in the scale of alloys undergoing hot corrosion. At present this possibility has not been discussed in the literature. Accordingly, we have begun investigation on the properties of ternary sulfides and their mutual interaction. The magnetic and electrical properties of pure NiCr2S4 and pure CoCr2S2 have been previously determined."-&apos; In the present work we have studied the interaction between these sulfides at high temperatures by means of X-ray diffraction and magnetic susceptibility. The measurements were carried out at room temperature after appropriate thermai treatment of samples at high temperatures. For alloys containing the three elements nickel, chromium, and cobalt this interaction may be of importance in the study of the hot corrosion phenomenon. The compounds NiCr2S4 and CoCr2S4 were prepared from stoichiometric amounts of the elements and CoS in the case of CoCr2S4. Samples were mixed and sealed in evacuated silica tubes, slowly heated to 900&apos; to 100O°C, and held at temperature for a total of 120 hr (NiCr2S4) or 80 hr (CoCr2S4) with intermediate re-grinding~. X-ray diffraction showed a pure spinel structure for CoCr2S4 and a monoclinic structure for NiCr2S4. Samples of mixtures of the two ternary sulfides were prepared with different compositions, see Table I. Samples were heated for a total of 80 hr at 900&apos;C in evacuated silica tubes, with one intermediate regrind-ing. The capsules were slow-cooled to room temperature in the furnace. Samples for X-ray diffraction were prepared by placing powder on a glass slide with vaseline. Dif- fractometer traces were obtained on a G.E. XRD-5 diffractometer using a chromium tube and vanadium filter (40 kv and 31 ma). The size of the spinel unit cell was determined from the eight highest angle peaks (80 deg < 2b < 160 deg). Calculated lattice parameters were plotted vs cos B . ctn 0 and extrapolated to 6 = 90 deg. Measurements of the magnetic susceptibility were carried out at room temperature using the Faraday method in a magnetic field of 3000 G and using a Cahn RG automatic microbalance. The system was calibrated from the well-established susceptibilities of platinum and palladium: (Xpt = 0.968 x 10-6 g-1 and Xpd 7 5.04 x 10~6 g-1). The weight of samples were approximately 0.200 g. X-ray diffraction patterns for unsintered mixtures showed Bragg peaks from both the spinel (CoCr2S4) and monoclinic (NiCr2S4) structures. After sintering no monoclinic peaks were observed in samples containing up to 40 mol pct NiCr2S4. However, the spinel peaks were displaced to higher angles with increasing

Jan 1, 1970

By P. Niessen, S. J. Bercovici

RECENTLY Aust et al.&apos; proposed a model of non-equilibrium grain boundary segregation based on a vacancy gradient induced uphill diffusion process of solute to grain boundaries. According to their proposal, solute atoms which are attracted to vacancies would, during the cooling of a sample, migrate with vacancies toward grain boundaries (vacancy sinks) and thereby enhance the solute concentration in boundary regions. For solute atoms which are not attracted to vacancies no such boundary solute enrichment would be expected. These concepts were given experimental support by boundary and bulk mi-crohardness measurements of various thermally treated dilute zinc and lead alloys and also doped aluminum oxide. The underlying assumption in their work was that solute enrichment in boundary regions is indicated by higher microhardness values. From thermodynamic considerations1&apos;2 it appears that the solid-liquid solute distribution coefficient (K), defined as the concentration of solute in the solid to the concentration of solute in the liquid at equilibrium, indicates whether attractive or repulsive forces exist between vacancies and solute atoms. K < 1 indicates a solute-vacancy attractions, K > 1 indicates no, or a repulsive, vacancy-solute interaction. This note is to report on observations of different grain boundary etching phenomena in high purity zinc alloys. These phenomena appear to depend on whether a K < 1 or K > 1 solute is present. In experiments designed to measure directly the solute enrichment in grain boundary regions, samples of zone refined zinc with 0.1 at. pct solute additions were cooled from 380°C at a rate of 3°C per min. A surface layer of approximately 50 was then removed from the samples by chemical polishing. The samples&apos; surfaces were then protected by a chromating treatment such that in a subsequent etch only grain boundary regions were dissolved. The dissolved regions were approximately semicircular troughs, 10 µ in width. The grain boundaries were usually in the middle, i.e., at the bottom, of this trough. For zinc containing the K < 1 solutes cadmium and aluminum, the grain boundary was always indicated by a ridge as shown in Fig. 1. For pure zinc, and zinc containing the K > 1 solutes copper and gold, a groove at the bottom of the trough indicated the boundary position, Fig. 2., To test if these different grain boundary etching behaviors were possibly connected with the segregation process discussed above, the Zn-Cd alloy was again heated to 380°C and quenched into brine. After surface protection and etching it was found that this specimen no longer exhibited the grain boundary ridges but rather grain boundary grooves as shown in Fig. 2. It would appear, therefore, that the boundary ridge is a consequence of a process occurring during the slow cooling of the samples. From absorption spectrophotometric analysis it was found that for slowly cooled samples containing K < 1 solutes, the solute/zinc ratios of the material from the boundary trough were consistently considerably higher than the solute/zinc ratios of the bulk alloys. This boundary region solute enrichment was not observed in quenched samples. It is concluded therefore, that the boundary ridge shown in Fig. 1 is directly or indirectly connected with nonequilibrium solute segregation.

Jan 1, 1970

By R. G. Aspden, D. A. Colling

THE {120}(001) texture has been reported in near 50 pct Ni-Fe alloys <0.004 in. thick1,2 and in copper 0.014 in. thick.3 This texture is one of two types of secondary recrystallization textures observed to replace a cube texture matrix and is desirable in Fe-Ni alloys because of its unique magnetic characteristics.1,2 However, the conditions for and mechanism of the {120}(001) formation are not well understood.3 During an investigation of the influence of alloying elements on the magnetic characteristics of 49 pct Ni-Fe alloys with a sheet thickness of 0.014 in., we have observed the growth of {120}(001) secondaries when strong deoxidizers such as aluminum and calcium were present. It is believed that this observation in unique and provides additional insight with regard to the mechanism for {120}(001) texture formation. Three alloys were prepared with electrolytic iron and nickel and contained a nominal 49 wt pct Ni. Alloy A was a straight binary Fe-Ni alloy, whereas intentional additions of 0.013 wt pct Ca to alloy B and of 0.59 wt pct A1 to alloy C were made. Ingots were forged at 1100 C, hot-rolled to 0.150 in. gage, pickled, and cold-rolled to 0.014 in. Standard U-shaped magnetic test specimens were punched, deburred, sprayed with MgO, and annealed in ~50°C dew point hydrogen. Textures were identified with the aid of etch pits, the

Jan 1, 1970

By H. W. Kerr, B. Soutiere

THE possibility of using unidirectionally solidified eutectic alloys as high-strength composite materials has been investigated by several workers. Unidirectionally solidified lamellar and fibrous eutectics have been shown to have good short-time structural stability at temperatures close to the eutectic melting temperature.&apos;-4 Several investigations of both short-time high temperature tensile properties and creep properties of eutectic alloys have been carried out,3-" with promising results. Little work has been reported, however, on the thermal stability of eutectic alloys which have been unidirectionally solidified and subsequently deformed in compression. Since processes such as rolling and grinding introduce compressive stresses, and since the properties depend on the spacing and perfection of the composite structure10,11 this aspect is of definite importance if unidirectionally solidified eutectic alloys are to be considered for commercial use. A Cd-Zn alloy made from 99.999 pct starting materials was cast into a graphite boat and zone levelled12 to obtain a completely lamellar structure at one end of the bar. Sections from this region of the bar were removed, recast into 6.5 mm I.D. Pyrex tubing, and solidified unidirectionally upwards at a rate of 2.8 cm per hr. Specimens were cut from the solidified rods, heated in air at 200°C (0.88 of the eutectic melting temperature) for various lengths of time, and examined metal-lographically. Compression specimens were also cut from the solidified rod carefully machined to a length of & in., and deformed with the compressive axis parallel to the original growth axis to produce a total longitudinal strain of 12 pct. Some of these specimens were examined metallographically; others were heated in air at 200°C for various lengths of time and then examined. Metallographic examination of the deformed specimens showed the two types of deformation previously described; slip lines13 (smoothly bent lamellae) and kinks13,14 (sharply bent lamellae). Very close to the specimen ends there were a large number of deformation bands, but at a distance of about -re- in. the deformation was very localized, as shown in Fig. 1.

Jan 1, 1970