By M. Metzger, J. C. Bilello

Microyielding in 99.999 pct Cu occuwed in two distinct parabolic microstages and was substantially indeoendent of grain size at the relatiz~ely large grain sizes stzcdied. The strain recouered on unloading was a significant fraction of the forward strain and was initially higher in a copper-coated single crystal than in poly crystals. Results were interpreted in terms of cooperative yielding and short-range dislocation motion activated otter a range of stresses, and a formalism was given for the first microstage. It was suggested that models involving long-range dislocation motion are more appropriate for impure or alloyed fcc metals. THERE are still many unanswered questions concerning the degree and origin of the grain size dependence of plastic properties. In the microstrain region, a theory of the stress-strain curve proposed by Brown and Lukens,' based on an exhaustion hardening model in which the grain boundaries limit the amount of slip per source, accounted for the variation with grain size of microyielding in iron, zinc, and copper.' This theory assumes N dislocation sources per unit volume whose activation stress varies only with grain orientation. Dislocations pile-up against grain boundaries until the back stress deactivates the source, which leads to a relationship between the axial stress and the strain in the microstrain region given by: where G is the shear modulus, D the grain diameter, a the flow stress, and a, is the stress required to activate a source in the most favorably oriented grain.3 If this or other grain-boundary pile-up models are correct, then the reverse strain on unloading would be much larger for a polycrystalline specimen than for a single crystal. Also, the microplasticity would become insensitive to grain size if this could be made larger than the mean dislocation glide path for a single crystal in the microregion. These questions are examined in the present work on polycrys-talline copper and a single crystal coated to provide a synthetic polycrystal. EXPERIMENTAL PROCEDURE Tensile specimens 3 mm sq were prepared from 99.999 pct Cu after a sequence of rolling and vacuum annealing treatments similar to those recommended by Cook and Richards4-6 to minimize preferred orientation. Grain size variation from 0.05 to 0.38 mm was obtained by a final anneal at temperatures from 310" to 700°C. Dislocation etching7 revealed pits on those few grains within 3 deg of (111). For all grain sizes dislocation densities could be estimated as -107 cm per cu cm with no prominent subboundaries. The single crystals, of the same cross section, were grown by the Bridgman technique with axes 8 deg from [Oll] and one face 2 deg from (111). An anneal at 1050°C produced dislocation densities of 2 x 106 cm per cu cm and subboundaries -1 mm apart in these single crystals. A Pb-Sn-Ag creep resistant solder was used to mount the specimens, with a 19 mm effective gage length, into aligned sleeve grips fitted to receive the strain gages. All specimens were chemically polished and rinsed8 to remove surface films just prior to testing. The synthetic polycrystal was made by electroplating a single crystal with 1 µ of polycrystalline copper from a cyanide bath. Mechanical testing was carried out on an Instron machine using two matched LVDT tranducers to measure specimen displacement, the temperature and the measuring circuit being sufficiently stable to yield a strain sensitivity of 5 x 107. At the crosshead speeds employed, plastic strain rates were, above strains of 10¯4, about 10¯5 per sec for polycrystalline specimens and 10-4 per sec for the single crystals. Plastic strain rates were an order of magnitude lower at strains near l0- '. A few checks at strain rates tenfold higher were made for reassurance that the initial yielding of polycrystalline copper was not strongly strain-rate dependent. Test procedures followed the general framework outlined by Roberts and Brown.9,10 An alignment preload of 8 g per sq mm for polycrystals, and 2 to 4 g per sq mm for single crystals, was used for all tests. These gave no detectable permanent strain within the sensitivity of the present experiments; although at these stress levels, small permanent strains are detectable in copper with methods of higher sensitivity.11 12 stress and strain data are reported in terms of axial components. RESULTS General. The initial yielding is shown in the stress vs strain data of Fig. 1. For polycrystals, cycle lc, the loading line bent over gradually without a well-defined proportional limit, and almost all of the plastic prestrain appeared as permanent strain at the end of the cycle. The unloading curve was accurately linear over most of its length with a distinct break indicating the onset of a significant nonelastic reverse strain at the stress o u, indicated by the arrows. The yielding in subsequent cycles, Id and le, had the same general character. The single crystal behavior, shown to a different scale at the right of Fig. 1, was different in that initially the nonlinear reverse strain was unexpectedly much greater than for polycrystals. It should be noted that these soft crystals had a small elastic

Jan 1, 1970

By R. R. Vandervoort

The creep behavior of Nb(Cb), Ta, Mo, and W was determined under conditions of constant atomic dif-fzisivity, constant stress to elastic modulus ratio, and nearly equivalent grain size, and the steady-state creep rates obtained from these tests were correlated with calculated stacking fault energies for the metals. These results, in conjunction with similar data for several fccMetals,13 suggest that stacking fault energy may influence the creep strength ofbcc metals. The interrelationship between steady-state creep rate, subgrain size, and stacking fault energy was examined. It was found that the subgrain size for a given creep stress, increased as stacking fault energy increased, but that this relationship did not cormpletely account for the effect of stacking fault energy on creep rate. The crystallography and energetics of stacking fault formation in bcc metals has been discussed by a num-ber of authors,1-5 and impurity stabilized stacking faults on (112) planes have been observed in Nb,6,7 w,8,9 Fe,] and V" by transmission electron microscopy. However, a crucial question is whether or not stack-ing faults influence the mechanical strength of bcc metals. Potentially, stacking faults could increase strength by reducing the mobility of the partial dis-locations bounding the fault, by acting as barriers to slip dislocations, and by retarding the climb of dislo-cations during high-temperature deformation. The objective of this study was to seek a correlation be-tween creep strength and stacking fault energy for several bcc metals; namely, Nb, Ta, Mo, and W. The creep behavior of most polycrystalline metals and alloys at high temperatures and moderate stresses can be described by the following relation:11,12 im=Af(s) where i, = minimum creep rate, A = constant, j(s) = a function involving metallurgical structure, a = applied stress, E = average elastic modulus at the test tempera-ture, w = constant (equal to 5 for most pure metals), D = diffusion coefficient. One factor in the structure function F(s) which sig- R. R. VANDERVOORT, Member AlME is Research Metallurgist, Process and Materials Development Division, Chemistry Department, Lawrence Radiation Laboratory, University of California, Livermore, Calif. Manuscript submitted February 28, 1969. IMD nificantly affects the creep resistance of fcc metals is stacking fault energy, and creep rate has been shown to vary directly with stacking fault energy to the 3.5 power." In the latter investigation, four fcc metals of widely different stacking fault energies (Ag, Cu, Ni, and Al) were creep tested at a constant stress to modulus ratio of 1.21 x 10-4, at a constant diffusivity of 2.7 x 10-12 sq cm per sec, and at nearly equivalent grain sizes of about 0.7 mm. The creep data were then correlated with stacking fault energies. In the present study, a similar procedure was followed. All materials used in this work were consolidated by powder metallurgy techniques. Impurity contents in the as-received materials are listed in Table I. Chemical analyses showed that no measurable contamination of the test specimens occurred during pretest annealing treatments or creep testing. Specimens with a gage section 0.75 by 0.125 by 0.050 in. were creep tested in tension in a vacuum of less than 10-9 torr. Deformation at temperature was measured by tracking fiducial marks on the gage section of the specimen with an optical comparator. Optical deformation measurements also permitted observation of the macroscopic characteristics of the deformation Table I. Typical Specimen Impurity Content, ppm Nb Ta Mo W C 45 10 155 6 O 185 30 4 10 N 30 6 3 2 H 5 I 1 <1 als 3 10 2 15 Ca <5 I3 5 Cr 5 <3 10 <5 Cu 10 50 2 15 Fc 10 10 150 35 Ni 2 150 20 <5 Si <I0 1 3 <10 Ta 100 Ti 10 8 1 Zi 15 50 1 3 Table II. Test Conditions for Constant Stress-Modulus Ratio of 6 X 10.&apos; and Constant Diffusivity of 2.7 X 10-12 sq cm per see, and Grain Size Values for the Given Pretest Annealing Treatments Literature references Pretest Annealing for E and D Treatment Stress, Temperature, ___"&apos;Values__ Grain Tempera-Metal psi "C E D Size, mm ture, .C Time hr Nb 745 1525 14 15 to 17 0.83 1650 I Ta 1220 1770 18 19.20 O.91 1800 I Mo 1975 1630 18 21 0.77 2200 I W 2140 2265 18 22 040 2400 5

Jan 1, 1970

By W. O. Philbrook, K. Natesan

The oxidation kinetics of spherical pellets of zinc sulfide made from Santander concentrates were studied using a thermogravimetric technique. The experiments covered a temperature range-. of 740" to 102O°C, 0-N mixtures varying from 20 to LOO pct O2, and pellet diameters between 0.4 and 1.6 cm. Mathematical models were formulated to Predict the reaction rate on the assumption that a single transport or interface reaction step was rate -controlling. Analysis of the data indicated that the process of oxidation was predominantly controlled by transport through the zinc oxide reaction-Product layer. ROASTING processes, which are reactions between solids and gases, are very important because they are employed in the production of a number of basic metals. These processes are highly complicated, and one needs to consider the transport phenomena of heat and mass between the solids and gases in addition to the kinetics of various chemical reactions involved. Because of such complications there is a lack of knowledge concerning the rate-limiting factors, which may strongly depend on temperature, particle size, gas composition, and solid structure. The oxidation of zinc sulfide, which is of commercial importance in zinc production, falls into this class of reactions. The major goal of this work was to elucidate the roles played by different process variables, such as reaction temperature, gas composition, pellet size, and pellet porosity, on the kinetics of oxidation of single pellets of zinc sulfide. Roasting of zinc sulfide single particles has been a subject of both experimental and theoretical investigations.&apos;-&apos; The reaction is exothermic and may be considered to be irreversible. Such a reaction has been found to proceed in a topochemical manner. In other words, as the reaction proceeds, a progressively thicker outer shell of zinc oxide is formed, while the inner core of unreacted sulfide decreases. It has been found experimentally, both in the present work and in the previous investigations,1-9 that the particle retains its original dimensions and the process requires transport of gaseous oxygen across the porous product layer for continued reaction. The reaction may be represented by ZnS(s) + 3/2 O2(g) = ZnO(s) + SO2(g) [1] The solid product considered here is only zinc oxide, since the diffraction patterns of zinc sulfide pellets oxidized partially at &apos;798" and 960°C showed K. NATESAN, Junior Member AIME, formerly St. Joseph Lead Fellow, Department of Metallurgy and Materials Science, Carnegie-Mellon University, Pittsburgh, Pa., is now at Argonne National Laboratory, Argonne, Ill. W. 0. PHILBROOK, Member AIME, is Professor of Metallurgy and Materials Science, Carnegie-Mellon University. This paper is based on a them submitted by K. NATESAN in partial fulfillment of the requirements for the Ph.D. degree in Metallurgy and Materials Science at Carnegie-Mellon University. Manuscript submitted December 2, 1968. EMD lines corresponding to original zinc sulfide and the newly formed zinc oxide. OXIDATION MODEL The generalized model for gaseous oxidation of zinc sulfide is illustrated in Fig. 1. This depicts a partially oxidized sphere of zinc sulfide in a gas stream surrounded by a laminar film of gas. The spherical sample of zinc sulfide of unchanging external radius r0 is suspended in a flowing gas stream of total pressure PT and composition specified by the partial pressures of the individual components. Partial pressures of the gaseous species in the bulk gas phase, at the exterior surface of the pellet, at the ZnS/ZnO interface, and at equilibrium for Reaction [I] are identified by the superscripts b, o, i, and eq, respectively. The overall reaction involves the following ~te~s:&apos;~&apos;~&apos; Step 1. Transfer of reactant gas (oxygen) from the bulk gas stream across the gas boundary layer to the exterior surface of the pellet and the reverse transfer of the product gas (sulfur dioxide). Step 2. Diffusion and bulk flow of oxygen from the pellet surface through the product shell (ZnO) onto the ZnS/ZnO interface and the reverse transfer of sulfur dioxide. Step 3. Chemical reaction at the interface, which results in consumption of oxygen gas and generation of sulfur dioxide gas and heat; at the same time the _________ PARTICLE SURFACE / x^^^^n^X / MOVING INTERFACE core-----/ sJSNxy " /T^T^02 \ V\V$\ ^NWX/ "*/— GAS BOUNDARY x. \\ZnO SHELLV/ / \^ . / &apos; ^ BULK GAS --------N_______ _____,------p£ w \ P« / (f> \ / a \ <i) / <----------------- _(o) ^^--------------(b) °- pso, pso2 ro ri 0 ri ro RADIAL POSITION Fig. 1—Generalized model for oxidation of a sphere of zinc sulfide.

Jan 1, 1970

By K. P. Mukherjee, K. P. Gupta, J. Bandyopadhyaya

Even though a lot of work has been done in the past to establish phase equilibrium in the Cu-Si system a re cent investigation casts some doubt about the existence and crystal structure of some of the phases that form in the composition range of 15 to 25 at. pct Si in Cu. The present investigation was carried out using high temperature X-ray diffraction technique along with other standard techniques to study the phases in this composition range. The high temperature 6 phase appears to be tetragonal with parameters a,, = 8.815A, c, = 7.903A, and co/ao = 0.896. The reported bcc E phase exists at room temperature and at least up to 780°C and appears to undergo a transformation near 600°C. The phase appears to be cubic but not of the bcc type. The ? phase appears to undergo a transformation, as has been indicated by earlier investigators, and the low temperature form of .? phase is tetragonal with parameters a, = 7.267A, co = 7.8924, and co/ao = 1.086. THE Cu-Si binary system has been investigated by several investigators1" and several intermediate phases,?,e,?&apos; at lower temperatures and ?,ß,0,e, and ? at higher temperatures, were observed between terminal solid solutions of copper and silicon. Even though the existence of the e phase and the transformation in the ? phase were reported in many early works, in a recent study of this system Nowotny and Bittner6 doubted the existence of the e phase and phase at 550°C. Among the high temperature phases, the 6 phase was reported to have a complex cubic structure with parameter a, = 8.805A.7 Nowotny and Bittner, however, suggested that the structure of the 6 phase might be of CsCl type. In order to check these contradictory reports the present study was taken up to investigate the Cu-Si binary system in the composition range of 17 to 25 at. pct Si. EXPERIMENTAL PROCEDURE Weighed amounts of copper (99.99 pct) and silicon (99.9 pct) were induction melted in recrystallized alumina crucibles under argon gas atmosphere. The alloys containing 17, 18, 20, 21, 21.2, 22, and 24 at. pct Si were annealed in evacuated and sealed quartz capsules at 700°C for 3 days and subsequently water quenched. Other than this annealing, the 21.2 at. pct Si and 24 at. pct Si alloys were annealed at 550°C for 10 days, the 17 at. pct Si alloy was annealed at 750°C for 3 days, and the 22 and 24 at. pct Si alloys were annealed at 780°C for 2 days. All annealing temperatures were controlled to within *l°C. Alloys after quenching were subjected to metallographic and X-ray diffraction investigation. A solution containing 5 g FeC13 + 10 cc HCl + 120 cc H2O diluted with six times its volume with water was used as etching reagent. A 114.6 mm diam Debye Scherrer camera was used for obtaining diffraction patterns. The 17, 21.2, and 24 at. pct Si alloys were subjected to high temperature diffractometry using a Tempress Research High temperature attachment and a GEXRD VI diffractometer. For the 6 phase (17 at. pct Si alloy) powder specimen from a 750°C annealed alloy was reheated to 750°C in the high temperature attachment for 1½ hr before taking a diffraction trace. A 550°C annealed and slowly cooled phase (24 at. pct Si) alloy was first reheated to 550°C. a diffraction trace was made after annealing it for 2 hr, and subsequently it was heated to 716OC and kept at this temperature for 2 hr before taking a diffraction trace. For the e phase (21.2 at. pct Si alloy) a 550°C annealed and slowly cooled specimen was heated first to 425°C and annealed at this temperature for 2 hr before taking a diffraction trace. Subsequently, the specimen temperature was raised to 495", 540°, 603", 635", 682", 720°, and 748°C and homogenized at each temperature for 1 hr before taking diffraction traces. The powder specimen temperature was controlled to within +2oC at each temperature and argon gas, purified by passing it at slow rate through a fused CaC12 column, hot (800°C) copper and titanium chips and finally through a P2O5 column, was used to prevent oxidation of the powder. For all X-ray work copper-radiations at 25 kv, 15 ma (for Debye Scherrer technique), and 40 kv, 20 ma (for diffractometer tech-nique) were used. RESULTS AND DISCUSSION At 700°C the alloys containing 17 to 21 at. pct Si showed two phases while the 21.2 at. pct Si alloy was found to be single phase. The X-ray diffraction patterns of the two-phase alloys were consistent with the phase (ßP-Mn type structure) and the phase (21.2 at. pct Si) patterns. The diffraction patterns of the 17 at. pct Si alloy quenched from 750" and 700°C were identical. According to the accepted Cu-Si phase dia-gram4,5,10 the 17 at. pct Si alloy at 750°C should be in the (k + 6) two-phase region and very close to the -phase boundary. The identical patterns possibly resulted from the decomposition of the 6 phase on

Jan 1, 1970

By F. I. Grace, L. E. Murr

The mechanical responses and residual defect structures in 70/30 brass and type 304 stainless steel following explosive shock loading and cold reduction by rolling have been studied. A distinct relationship was observed to exist between the residual mechanical properties and micro structures observed by transmission electron microscopy. Shock-loaded brass deformed primarily by the formation of coplanar arrays of dislocations and stacking faults at lower pressures, and twin-faults (deformation twins and €-martensite bundles) at higher pressures (> 200 kbar). The micro -structures of cold-rolled brass were characterized by dense dislocation fields elongated in the rolling direction. Stainless steel was observed to deform by the formation of dense arrays of stacking faults at lower shock pressures and twin-faults at high shock pressures (>200 kbar). Lightly cold-rolled stainless steel deformed similar to low Pressure shock-loaded stainless steel, but transformed to a&apos; martensite in heavily cold-rolled stainless steel. Discontinuous yielding was observed for the heavily cold-rolled stainless steel, and stress reluxution in the weyield region for cold-rolled and shock -loaded stainless steel was interpreted as an indication of the ability of twin-faults and stacking faults to act as effective barriers to dislocation motion. A simple model for the formation of the planar defects and a&apos; martetnsite is presented based on the propagating of Shochley partial and half-partial dislocations. A considerable effort has been expended over the past decade in an attempt to elucidate the response of metallic-crystalline solids to the passage of a high velocity shock wave (e.g., smith,&apos; Dieter,2 and zukas3). While it has been possible to obtain relevant information pertaining to the residual defect structures and mechanical properties, there have been few rigorous attempts to draw a direct comparison between these structures and properties. In addition, numerous investigators have recently observed the occurrence of deformation twinning in shock deformed fcc metals (e.g., Nolder and Thomas,4 and Johari and Thomas5), but little attempt has been made to elucidate the mechanisms of formation of these defects. Comparative data for metals deformed by shock-loading and the same metals deformed by more conventional modes of deformation such as cold-reduction by rolling is also generally lacking. The present investigation therefore has the following objectives: 1) to examine the mechanical properties of some explosively shock loaded and cold-rolled fcc metals of low stacking-fault energy as a function of their residual substructures; 2) to present a simple model for the formation twin-faults and related defect structures in the low stack-ing-fault energy materials of interest (70/30 brass, ySFg= 14 ergs per sq cm; and 304 stainless steel, ySF = 21 ergs per sq cm); 3) to make some deductions with regard to the residual characteristics of dislocation and planar defect substructures in cold rolled and shock loaded 70/30 brass and type 304 stainless steel. In particular, it was desirable to characterize the residual hardening effects of particular deformation substructures. I) EXPERIMENTAL PROCEDURE Sheet samples of 70/30 brass (0.005 and 0.15 in. thick; annealed at 659°C for 2 hr) and type 304 stainless steel (0.007 in. thick; annealed 0.25 hr at 1060°C) of nominal compositions shown in Table I were cold-rolled in one direction only to produce reductions in thickness of 15, 30, 45, 60, and 75 pct in the brass; and 5, 15, 25, 35, and 45 pct in the stainless steel. Identical sheet samples in the annealed (unrolled) state were subjected to plane compressive shock waves to various peak pressures ranging from 0 to 400 kbar in the brass and 0 to 425 kbar in the stainless steel; and with a constant peak pressure duration of approximately 2 microseconds. A detailed description of the shock loading technique has been given previously.6 Tensile specimens 1.0 in. in length and 0.125 in. in width were cut from the cold-rolled sheets (tensile axis parallel to the rolling direction), and the shock-loaded sheet specimens. Stress (load)-strain (elongation) measurements on the tensile specimens were made on a Tinius-Olsen load-compensating tensile tester using a strain rate of 2.7 x 10-3 sec-1. Tensile tests were repeated at least twice, giving essentially the same results. Stress relaxation measurements in the preyield region were also made using an initial strain rate of 5.4 x 10-4 sec-1. In addition to tensile and stress relaxation measurements, Vickers microhardness measurements were made on all samples. A total of 100 microhard-ness readings were obtained for each specimen following a light electropolish to ensure uniform surface conditions for all tests. The hardness averages ob-

Jan 1, 1970

By C. F. Jenkins, G. V. Smith

Serrated plastic flow in stable austenitic alloys based on Fe/Ni has been shown to be related to the presence of carbon and/or chromium in the systems. Strength peaks and plateaus in the serrated-flow temperature region for a commercial alloy correlate with an increased dislocation content, arising, presumably, from enhanced multiplication as a result of a strong interaction between dislocations and solute atoms. The data generally support a mechanism controlled by migration of vacancies, with the energy for vacancy motion being modified by the presence of chromium. Chromium atom -dislocation interaction is responsible for effects above 500°C, whereas the defect interacting with dislocations between 200" and 500°C is suggested to be a carbon-vacancy Pair. ThE phenomenon of jerky flow, serrated flow, or the Portevin-le Chatelier (P-C) effect in austenitic stainless steels is usually attributed to substitutional at1,2 mospheres1,2 or to precipitates&apos;-4 which form at dislocations during plastic deformation. On the other hand, evidence exists which supports a direct inter-stitial-dislocation interaction mechanism for serrated flow in fcc Ni-C,5,6 Ni-H7-9 and in nickel-austenites containing carbon." The present work consists in a study of serrated plastic flow in stable austenitic al-loys. The effects of carbon and of chromium were investigated separately, and a commercial stainless steel with different levels of interstitial impurity concentration was studied in an attempt to delineate the combined effects of the alloying elements. EXPERIMENTAL TECHNIQUES a) Materials and Fabrication. A commercial AISI 330 stainless steel and several specially prepared aus-tenitic alloys have been studied. The experimental alloys were prepared by arc melting the constituents under purified argon. Analyses of the materials are given in Table I. The commercial alloy was obtained as 5/8 in. bar stock and rolled to 0.092 in. sq, with several intermediate anneals. At this stage some of the material was annealed in Pd-purified hydrogen at 1100°C to establish different levels of interstitial content. All other heat treatments were in vacuum (10-5 torr). The "pure" alloy ingots were swaged to 0.120-in. rod and annealed in Pd-purified hydrogen at 1100°C. The analyses for these conditions are also contained in Table I. Following the above treatment, the final wire sizes Table I. Chemical Analyses of Test Materials Hrin Hydrogen at Cr, Ni, Alloy 1lOO°C wt pct wt pct C, ppm* N, ppm* Type 330 As-received 14.78 33.25 430 300 Type 330 64 14.78 33.25 40 50 Type 330 200 14.78 33.25 27 21 Fe/35 Ni 72 - 35.10 <10 62 Fe/35 Ni 200 35.10 <I0 44 Fe/35 Nil15 Cr 72 14.95 34.94 <I0 61 Fe/35 Ni/15Cr 200 14.95 34.94 <10 45 Fe/35 Ni/C $ 35.OM 380 *Sensitivity: N t 5 ppm Ct10ppm. f Nominal Ni content. % A master NiC alloy was used in preparation of this material; courtesy of D.E. Sonon. were obtained by either swaging or cold drawing. The test results did not vary with these techniques. b) Specimen Preparation. Two sizes of specimen and two gripping systems were used. i) 0.070-in. wire with a chemically milled gage section: 0.75 in. long, 0.060 in. in diam. These were fastened into grips containing tapped grooves. ii) 0.050 in. wire, gage length 1.5 in. Ball bearings were welded to the ends of the wires and the gage length was taken to include all material between the welds. Socket-type grips were used with these specimens. With specimens of type ii), joining was performed in a specially constructed brass jig, under argon, and automatic timing was utilized in the procedure. No adverse effects of welding were noted. Specimens were encapsulated and solution treated for 1 hr at temperatures selected to produce the same average grain size, -50 µ. Annealing twin boundaries as well as normal crystal boundaries were counted. The temperatures used are listed in Table 11. Table 11. Specimen Size. Temperature of Heat Treatment and Resulting Grain Diameters for Test Materials Recrystallization Resulting Material Condition Temperature Grain Sue AISI 330 Not H purified 0.070 120O°C 45 to 55µ in, wire AlSl 330 H , pure, 0.070 in. 1150°C 45to55µ wire Fc/35Nil15Cr Pure, 0.070 in. wire 1000°C 45tossp Fe/Ni Pure. 0.070 in. wire 775°C 45 to 55µ Fe/Ni/C Pure, 0.050 in. wire 850°C 10 to 20p AlSl 330 Not purified, 0.050 1150CC 45to55p in. wire AlSl 330 ti, pure, 0.050 in. 1150°C 45to55p wire

Jan 1, 1970

By F. George, W. Tice, M. Salkind

It was found that Al-A13Ni could be readily cold rolled perpendicular to but not parallel to the whiskers. Reductions of more than 98 pct were achieved without cracking by rolling perpendicular to the whiskers, whereas extensive edge cracking was noted after only 15 pct reduction when rolling parallel to the whiskers. The longitudinal and transverse tensile strengths were nearly doubled, and the longitudinal yield strength more than tripled by cold rolling 50 pct in a direction perpendicular to the whiskers. The whiskers exhibited some waviness (elastic bending) as a result of cold rolling, but at very high reductions (greater than 75 pct) whisker fracture and misalignment became significant. A fine dislocation substructure in the matrix consisting of cells attached to the whiskers was pro -duced by cold rolling. Most of- the substructure was readily removed by a 1-hr anneal at 500°C. Cold rolling was found to substantially reduce the thermal stability of the microstructure at 610°C but did not affect the stability at 500°C. FIBER and whisker reinforced composite materials promise significant improvements in properties over conventional materials. Before they find wide use, however, it will be necessary to understand the response of these highly anisotropic materials to common metalworking processes. Most of the nonmetal-lic fiber reinforced materials have very low elongations (a few pct or less) in the direction of fiber alignment. Thus, metalworking techniques such as rolling and forging would not be as broadly applicable to these materials. This investigation was initiated to determine how a composite system consisting of Al3Ni whisker reinforced aluminum responded to rolling, what changes in the microstructure occurred, and the effect of deformation on the mechanical properties. The composite material studied was produced by unidirectional solidification of the A1-Al3Ni eutectic alloy&apos;-7 and consisted of 10 pct by volume of aligned whiskers of Alai in a matrix of aluminum. It should be pointed out that this system is not representative of all composite materials, and the results will therefore not be universally applicable. The A1-Al3Ni system is characterized by: 1) A strong fiber-matrix interfacial bond 2) A ductile matrix 3) A sufficiently low fiber content to allow significant plastic flow between fibers 4) Strong, completely elastic whiskers (tensile strength 400,000 psi, elastic modulus = 20 X 106 psi.1 These factors allow the material to be readily rolled perpendicular to the fibers. If the fiber-matrix bond were not strong, such a weak interface could fail during rolling. A measure of the ability of a composite to be rolled in the transverse direction can be obtained from noting the transverse tensile behavior. In the case of Al-Al3Ni,2 there is considerable ductility (15 to 30 pct). In the case of boron filament reinforced aluminum, for example, the transverse elongation is less than 1 pct,8 and the material could probably not be cold rolled as readily in that direction. EXPERIMENTAL PROCEDURE 3-in. diam ingots of A1-A13Ni eutectic were unidi-rectionally solidified in graphite crucibles. The starting materials consisted of 99.99+ pct pure nickel and aluminum, and the pure eutectic ingots were made with 6.2 wt pct Ni. The unidirectional solidification process (described in detail elsewhere1-3) consists of preparing a master heat of eutectic composition, remelting, and withdrawing the ingot vertically downward through the heat source at a controlled rate so that plane front solidification proceeds upward at a constant velocity. The resulting microstructure consists of 10 pct by volume of whiskers of very high aspect (length to diameter) ratio. The fiber lengths have not been measured because of the difficulty of detecting fiber ends9 but exceeds 104. There is some possibility that the fibers may be continuous within one grain. Flat sheet specimens 2¾ in. sq and approximately 0.2 in. thick containing whiskers parallel to the plane of the sheet and to one edge were used for this study. A1-A13Ni exhibits either a rod-like (high solidification rates) or a blade-like (low solidification rates) whisker morphology,1,3 and both types were studied. Rolling was accomplished using a two-high rolling mill at a speed of approximately 10 fpm. The rolling direction was either parallel to or perpendicular to the direction of growth (direction of whisker alignment). Reductions of from 0.002 to 0.03 in. per pass were used with the most common value being 0.005 in. per pass. Cold rolling of Al-Al3Ni to more than 98 pct reduction in thickness was accomplished with no intermediate anneals. In addition. a series of speci-mens was cold rolled 97 pct with a 1-hr, 500°C anneal in air after each 50 pet reduction. Tensile testing was accomplished using a Tinius-lsen four screw testing machine. Flat sheet specimens + in. wide and between 2 and 2; in. long with the thickness dependent upon rolling reduction, were used. The gage section was in. wide and 1 in. long. Strain was measured using a clip-on LVDT extensome-

Jan 1, 1970

Jan 1, 1970

By H. B. Bell, P. C. Lidster

A study has been made of the use of ThO2-Y2O3 solid electrolytes to determine activity of chromium in Fe-Cr and Ni-Cr alloys in the temperature range 1300° to 1700°K. This method has been shown to give results which agree with the best vapor pressure measurements. SEVERAL investigations1"5 have been made of chromium activities in Fe-Cr alloys. Most of these have been made by vapor pressure measurements using knudsen cell techniques while one has been made using gas equilibration with H2/H2O gas mixtures. In the present investigation electromotive force measurements have been made on this system using a thoria yttria solid electrolyte. This system was -chosen to establish the technique of measurement at low oxygen potentials, before extending it to Fe-Ni-Cr alloys. The cell used was Pt Cr • Cr2O3 ilThO2 • Y2O3 llalloy • Cr2O3 IPt Since the oxygen pressure of the chromium-chromic oxide mixture lay in the range 10"19 to 1027 atm in the temperature range investigated, thoria yttria electrolytes were used. It was soon found during the investigation that considerable care was required to prepare satisfactory electrolytes and a study was made to find the best method of preparing pellets of TI1O2-Y2O3 solid solution of as near theoretical density as possible. Various compositions in the range 2 to 15 mole pct Y2O3 were studied but the experimental measurements were made with electrolytes containing 4 to 5 pct Y2O3. The method of preparation finally adopted was to use thorium oxalate and yttria as raw materials. The thorium oxalate was decomposed at 900°C for 6 hr to give a reactive powder. This powder was then mixed with the appropriate amount of yttria and ground in an agate mortar for about 4 hr. The powder was moistened with absolute alcohol as a lubricant and pressed in a metal die at a pressure of 7 tons per sq in. The pellets were then heated at 1100°C for 24 hr followed by 24 hr at 1250°C. After this firing cycle the material was reground and repelleted and again fired at 1100° and 1250°C followed by heating for 7 days at 1600°C. It was found in later experiments that a further firing of 4 hr at 2000°C improved the density further and gave pellets of only 2 pct porosity. After firing, the pellets were polished on emery paper and finally with the 2 µ diamond paste. The polishing was followed by a final firing of 24 hr at 1500°C. Investigation showed that this final treatment minimized reaction between the electrolytes and chromium oxide. It was believed that this was because of a lowering of the surface energy of the electrolyte surface. Two types of investigation were carried out to check that the pellets were satisfactory oxygen ion elec-

Jan 1, 1970

By A. V. Bradshaw, R. I. L. Guthrie

The behavior of large bubbles in the size range 4 to 25 cm3, rising through molten silver, has been studied. It was found that rising velocities were equivalent to those in aqueous systems of low viscosity. Mass transfer coefficients for oxygen bubbles dissolving in silver were found to be 0.036 ± 0.007 cm sec-1, being close to those predicted for transfer through the front surface of the spherical cap bubble only. It is suggested that the surface active nature of oxygen in silver could account for the relatively low coefficients obtained. MANY metallurgical processes involve interactions between gas bubbles and liquids. Examples include the removal of carbon monoxide in Open Hearth Steelmak-ing, the removal of sulfur by blowing air through copper matte during converting, and the removal of hydrogen from steel during vacuum degassing or inert gas flushing. The steps involved in such refining processes include; transport of the dissolved species to the bubble interface, adsorption and chemical reaction of the species at the interface, desorption of product molecules from the interface, and transport of product gas into the bulk gas phase of the bubble. It has been concluded1 that all the interfacial steps involved proceed so rapidly at steelmaking temperatures that transport of the solutes, present in the metal, become the important rate controlling factors provided nucleation phenomena are not restrictive. The O-Ag system was chosen for the investigation into gas bubble-molten metal interactions due to the relatively high solubility of oxygen that enables rates of oxygen transfer to be measured from changes in bubble volume. Other advantages of this system include the absence of a stable oxide phase at an oxygen pressure of 1 atm and the relatively low melting point of the metal which permits the use of a metallic container, providing that it is resistant to oxidation. In those metallurgical processes where bubbles have an important influence, bubble volumes are usually greater than 5 cm3. For this reason the present study relates specifically to single large bubbles of oxygen rising in silver. These bubbles adopt the characteristic spherical cap shape similar to that shown in Fig. 1 for a 30 cc bubble rising in water. After an initial investigation to determine the velocities of inert (nitrogen) bubbles rising in molten silver, experiments were carried out with oxygen and the rates of mass transfer between the oxygen bubbles and the silver were measured. EXPERIMENTAL Apparatus. The apparatus, Fig. 2, for containing molten silver, was constructed from "Nimonic 75" Alloy (75 pet Ni, 20 pet Cr, 5 pet Fe, Mn) and provided for the release of single bubbles from an hemispherical cup, situated at the bottom of the column. The cup was turned by translating the rotation of the drive shaft through 90 deg. This was accomplished by the use of a bevelled gear system, and a smooth drive was provided by the lubricating action of the silver on the gears. Since reliable high temperature seals at 1000°C were found to be impracticable, the filling and drive shaft tubes were extended outside the 3.5 kw resistance wire tube furnace, where connections were made using easily accessible O-ring seals. The apparatus remained gas tight to the atmosphere at pressure differentials far in excess of those used. The filling tube was connected via a small bore tube to the differential pressure transducer. Gas could be bubbled into the inverted cup from two i-in. tubes which passed down the inside of the column to preheat the gas. The temperature of the silver was maintained at 1020°C during all experiments. Measurement of Bubble Volume. In order to calculate mass transfer rates, it was necessary to obtain a continuous record of the bubble&apos;s volume during its passage through the column of molten silver. The method adopted for measuring the bubble volume involved closing off the top gas space to the atmosphere prior to each experiment, and recording the variation in gage pressure of this space during the formation and rise of the bubble. Since any change in bubble volume results in an equal change in top space volume, Boyles Gas Law may be applied (for isothermal con-

Jan 1, 1970

By R. F. Steigerwald

The effects of heat transfer on the corrosion behavior of type 304 stainless steel in boiling water have been studied. Heat transfer conditions increase the tendencies of the stainless steel toward stress-corrosion mucking when the water is contaminated with Cl-. Surface preparation is the most important variable in determining the severity of the stress-corrosion problem in water with a given Cl- content. Heat treatment, chemical cleaning, and degree of wet film boiling also affect the corrosion of stainless steels used as heat transfer surfaces in boiling water. An up-paratus for corrosion testing under controlled heat transfer conditions is described. THE principal objective of this investigation was to study the corrosion behavior of AISI Type 304 stainless steel in boiling high-purity water under conditions of heat transfer. The principal variables in the study were: a) boiling conditions: limited boil, agitated boil; b) metallurgical structure: annealed or sensitized; c) surface condition: rolled, pickled, or ground. The results of the study should elucidate the role of heat transfer in the corrosion of stainless steel in boiling high-purity water and provide a base line from which to assess the severity of this type of corrosion. Although there has been an investigation of the effect of heat transfer on the corrosion behavior of stainless steels in alkaline waters,&apos; work on the corrosion of stainless steels under heat transfer has been largely confined to various acid solutions.&apos;-4 Furthermore, the study of the corrosion of stainless steels in high-purity water has been generally restricted to auto-clave and instream testing in superheated (e.g., 300°C) water and steam.5&apos;6 Cooling water problems led to this study of the corrosion behavior of type 304 stainless steel in high-purity water at its atmospheric boiling point. In addition to the effects of heat transfer, this study also considered the influences of the type of boiling,7 metallurgical structure, and surface condition on the corrosion behavior of stainless steel in high-purity water. Two boiling conditions were investigated in this study: a) limiting boiling, i.e., when the heat-transfer surface had just reached the boiling point and boiling nucleated randomly over the specimen surface and b) agitated boiling, i.e., when a mild degree of superheat had been achieved on the specimen surface and boiling occurred generally over the specimen surface. Both boiling conditions are broadly classified as wet-film boiling. Originally, this program included the study of a third type of boiling, dry-film conditions. At dry-film boiling the temperature of the heat transfer surface is high enough so that it is covered with a continuous film of steam. Experimental difficulties made it impossible to study this kind of boiling with the available apparatus. Since surface condition affects heat transfer rates, three typical surfaces were chosen for study: a) as-rolled, the 2B finish received from the supplier, b) as-pickled, 30 min in 8 pct HNO3-1 pct HF, and c) as-ground on 120 grit paper. In order to evaluate the effect of improper heat treatment or welding on hot wall corrosion, both annealed and sensitized mi-crostructure were included in this study. EXPERIMENTAL Test Apparatus. The particular problems of interest in this investigation required a knowledge of the thermal gradient through the test specimen. From this gradient, the heat flux to the surface and the surface temperature could be determined. In order to satisfy this need, an apparatus similar to the boiling-disk apparatus of Fisher and whitney2 was designed. The solution is contained in a thermally-insulated, steel pipe lined with TEFLON resin. A stainless steel _______;________________________________________

Jan 1, 1970

By Charles Stein

The effects of several different prior treatments an the creep behavior of 99.9995 pct aluminum at 260°C and 1000 psi canstant stress are compared with annealed specimens. Quenching from 538oC, irradiation with 2 mev electrons, and tension-compression room temperature fatigue damage were used to change the substructure of the specimens prior to their creep testing. The quenched and the irradiated specimens showed a larger primary and transient stage contribution to the creep curve than those specimens which were only annealed prim to creep testing. The specimen receiving prior fatigue damage at room temperature showed no first stage or transient creep when tested under identical conditions as the above specimens and had an average creep rate seven orders of magnitude lower than that of either the annealed, the quenched or the irradiated creep specimens. In a previous electron transmission microscopy investigationl of the substructure developed during the creep of pure aluminum at 0.57 Tm, it was noted that a large concentration of vacancy loops and dislocation loops were present in and near the subboundaries while the interior of the subgrains contained few of these defects and had a low dislocation density, see Fig. 1. Yim and Grant2 and Hazlett3 have shown that the presence in nickel of a substructure developed by prior cold work effectively reduces the primary and transient contributions to the creep curve. Hultgren,4 McLean,5 Gervais, Norton, and Grant,6 Chang and Grant,7 and others have shown the same effect with the higher stacking fault energy material, aluminum. However, the specific defect responsible for the change in the creep behavior developed by the prior cold work was not established. Specifically, what effectively interfered with dislocation motion in these materials at elevated temperatures? Was it jogs on dislocations produced by their interaction with other dislocations or with vacancy or dipole loops, see Fig. 1, or did the subgrain walls determine the mean free path for glissile dislocations? This would be a realistic possibility only if subgrain boundaries are effective barriers to dislocation motion. The ability of a subgrain boundary to act effectively against glissile dislocations depends on the number and the arrangement of dislocations in the subboundary,8 which in turn is a function of the creep strain.&apos; This paper compares the creep rate of specimens possessing a large vacancy concentration to that of annealed specimens and with specimens having a stable subboundary wall containing Lomer locks produced by prior fatigue damage. EXPERIMENTAL PROCEDURE Vacancy Loops. Aluminum creep specimens, 99.9995 pct pure, were machined from zone refined rod to a 2-in. gage length and a cross-sectional area of 0.025 in. These specimens were annealed at 538oC, 1000°F, for 10 min and quenched into ice water. They were then reheated to the creep test temperature of 260°C, 500°F, and held at this temperature for 18 min to al-low for vacancy condensation and loop formation. The specimens were subsequently creep tested at 1000 psi constant stress at 260°C. The temperature along the gage length was monitored by three Pt-Pt, 13 pct Rh thermocouples, two embedded in the upper and lower shoulders of the specimen and one attached to the mid-point of the gage length- The temperature gradient was held to ± l°C or less throughout the Creep test. Elongations were measured by two LVDT&apos;s &apos;connected in an averaging &apos;On-figuration, with quartz extension arms placed against the specimen at the extremes of the 2-in. gage length. i K 3J?--&apos; * *H - >^> - &apos; ^L r 77 . *y J OJL, J Fig. 1—Transmission electron micrograph of pure aluminum strained 8.2 pct at 260°C and 1000 psi constant stress. Note the presence of numerous loops near the light dislocation tangle

Jan 1, 1970

By J. L. Tomlinson, B. D. Lichter

Electrical resistivities 01 liquid Cd-Bi, Cd-Sn, Cd-Pb, In-Bi, and Sn-Bi alloys were measured using an electrodeless technique. The resistivities ranged from 50 to 160 microhm -cm, temperature dependences were positive, and no sharp peaks in the composition dependence of the resistivity were observed. On the basis of these observations, it was concluded that the alloys are typical metallic liquids. The electron con-cent9,ation was calculated from the measured resis-tizlity and available thermodynamic data using a model which attributes electrical resistivity to scattering by density and composition flzcctuations. A correla-tion was shown between the departure of the electron concentration from a linear combination of the pure component valences and the value of the excess integral molar free energy. Calculation of the temperature dependence of the electrical resistivity showed a need for more detailed thermodynamic data in these systems and led to suggestions for improvement in the concept of residual resistivity in the fluctuation scattering model. THE electrical resistivity of liquid metals provides information regarding interatomic interactions and their effects upon structure. In this experiment an electrodeless technique was used to measure the electrical resistivities of liquid alloys of Cd-Bi, Cd-Sn, Cd-Pb, In-Bi, and Sn-Bi, and the results were used with thermodynamic data to calculate a parameter which reflects the tendency toward localization of electrons due to compositional ordering. It was found that the resistivities of these alloys are generally metallic in magnitude and temperature dependence. The electrical and thermodynamic properties are discussed in terms of the fluctuation scattering model&apos;22 which supposes that the electrical resistivity arises from scattering due to a static average structure and departures from the average due to fluctuations in density and composition. Further, this model is compared with the pseudopotential scattering model of Ziman et al.3-5 EXPERIMENTAL PROCEDURES Alloy samples were prepared from 99.999 pct pure elements obtained from American Smelting and Refining Company (except tin which was obtained from Consolidated Smelting and Refining Company.) J. L. TOMLINSON, Member AIME, formerly Research Assistant Division of Metallurgical Engineering, University of Washington, Seattle, Wash., is now Physicist, Naval Weapons Center, Corona Laboratories, Corona, Calif. 0. D. LICHTER, Member AIME, is Associate Professor of Materials Science, Department of Materials Science and Engineering, Vanderbilt University, Nashville, Tenn. This work is based on a portion of a thesis submitted by J. L. TOMLINSON to the University of Washington in partial fulfillment of the requirements for the Ph.D. in Metallurgy, 1967. Manuscript submitted May 31, 1968. EMD Weighed portions were sealed inside evacuated silica capsules, melted, and homogenized before the resistivity was measured. The resistivity of a liquid alloy was measured by placing the sample inside a solenoid and noting the change in Q. According to the method of Nyburg and ~ur~ess,~ the resistivity of a cylindrical sample may be determined from the change in resistance of a solenoid measured with a Q meter as T7--5--W =R7JT^ =&apos;Kc-lm(Y) [1] where L, R, and Q = wL/R are the inductance, series resistance, and Q of the solenoid. The subscript s refers to the solenoid with the sample inside; the subscript 0 refers to the empty solenoid. Kc is the ratio of the sample volume to coil volume and y = 2 [bei&apos;0(br)-j ber&apos;o(br)~\ br\_bero(br) +j bei0 (br) expressed with Kelvin functions which are the real and imaginary parts of Bessel functions of the first kind with arguments multiplied by (j)3&apos;2. The argument of the function Y is hr where r is the sample radius and b2 = po~/p, i.e., the permeability of free space times 271 times the frequency divided by the resistivity in rationalized MKS units. Since Eq. [I] cannot be solved explicitly for p, values of Kc. lm(Y) were tabulated at increments of 0.1 in the argument by. A measurement of Q, and Q, determined a value of Kc . lm (Y) and the corresponding value of br could be read from the table. From the known r, uo,, and w, the resistivity, p, was determined. The change in Q was measured after letting the encapsulated Sample reach equilibrium inside a copper wire solenoid. The solenoid was contained in an evacuated vycor tube in order to retard oxidation of the copper while operating at high temperatures and heated inside a 5-sec-tion nichrome tube furnace capable of obtaining 900°C. Temperature was determined with two chromel-alumel thermocouples, one in contact with the solenoid 30 mm above the top of the sample and the other inserted in an axial well at the other end of the solenoid and secured with cement so that the junction was 2 mm below the bottom of the sample. Temperature readings were taken with respect to an ice water bath junction, and the voltage could be estimated to the nearest thousandth of a millivolt. The lower thermocouple was calibrated by observing its voltage and the Q of the coil as the temperature passed through the melting points of samples of indium and tellurium. The upper thermocouple reading was systematically different from the lower thermocouple reflecting the temperature difference due to a displacement of 60 mm axially and 6 mm radially. Calculations show that the gradient over the sample was less than 2 deg. Q was measured by reading a voltage related to Q from a Boonton 260A Q meter with a Hewlett Packard

Jan 1, 1970

By H. E. Cline

Calculations of the formation and growth of faults caused by a variation in lumellar widths were made for a two-dimensioml three-plate problem. The angle between the a-ß boundary and the growth direction was allowed to vary and the time evolution was studied using a quasisteady state approach. At spacings smaller than a critical spacing given by X V = AO variations in the larrlellar widths grow in time to produce faults that coarsen the structure, while at spac-ings larger than this critical spacing, variations in the lamellar widths decay in time. If small plates are introduced into the structure they may grow only at large spacings to refine the structure. The time evolution and shape of faults were calculated for the three plate-problem and then the three dimensional problem and rod-like eutectic were qualitatively discussed. UNDERSTANDING of the mechanism by which the spacing of directionally solidified eutectics is determined may allow one to control their structure better. Steady state solutions for the growth of lamellar structures have been found for a range of lamellar spacings A and growth velocities V. To obtain a unique solution for the isothermal growth of pearlite, Zener1 assumed that growth occurs at a maximum velocity, while Tiller2 assumed that a eutectic alloy, grown under an imposed velocity, will choose a spacing corresponding to minimum undercooling. These assumptions are equivalent and have been referred to as "extremum growth". The extremum condition predicts the observed relation between velocity and spacing as given by V = constant [I] but does not provide a mechanism for changing the lamellar spacing. Jackson and Hunt3 calculated the interface shape by using solutions to the diffusion equation for a planar interface and a relation of the interface composition to the local curvature. If the spacing is much larger than the extremum spacing, the interface breaks down catastrophically to form forked plates. However, the catastrophic breakdown cannot account for the small adjustments in spacing that must occur in practice..3 Direct observations during the growth of organic eutectics4 and the Pb-Sn eutectic5 show that spacing changes occur by the formation of faults. A fault in a plate-like eutectic is the edge of a plate. Once the faults form, they may move to make small adjustments in the spacing.6,3 The motion of faults intersecting the growing interface was shown by an approximate analysis to give Eq. [I].6 A perfectly regular lamellar structure should be able to persist over a range of lamellar spacings. However, during growth small perturbations in the structure may occur. If the amplitude of the perturbation increases in time the structure is unstable, while if all possible perturbations decrease in time the structure is stable. In a previous paper7 variations in the shape of the solid-liquid interface were considered, while this paper considers only variations in lamellar widths while maintaining a macroscopically planar solid-liquid interface. Previously, theories of lamellar growth1"3 have artificially contrained the growth to give a regular periodic structure. To allow for a variation in spacing, the three phase intersections and groove angles were allowed to change with time as determined by assuming local equilibrium. THREE-PLATE PROBLEM Since the spacing changes in eutectics by local formation of faults,4&apos;5 it is suggested that local variations in spacing are responsible. The interaction between neighboring plates will be greatest because they have the smallest diffusion distance. For simplicity, as a nearest neighbor approximation, a three-plate problem will be considered, as illustrated in Fig. 1. The structure consists of a periodic array in which all the plates are allowed to vary in width. As in steady state growth it is assumed that the average composition in the solid remains constant. A variation in plate widths, that maintains the composition in the solid, was introduced by making the first a-phase plate thinner by an amount A, keeping the width of the second B-phase plate constant, and increasing the width of the third a-phase plate. If the structure were not perturbed, as in the regular two-plate problem previously described,&apos; then the groove angles at the three-phase junctions are the equilibrium angles, 0, and ? B, and the solid-solid boundary is normal to the interface. In the three-plate problem with a variation in plate widths the phase boundaries are assumed to be related to the three-phase junction by equilibrium angles, but the a/B boundaries may be rotated by an angle 0 from the growth direction. The angle H be-tween the tangent to the a/B boundary and the growth direction may vary during growth and determine the —> — — —.A_ Q-0 / 0 x, X2 Fig. 1—Schematic of the three-plate problem showing a variation in the spacing and the effect on the angles at the three phase intersections.

Jan 1, 1970

By R. E. Miner, J. K. Jackson, T. L. Wilson

A study has been made of the transformation kintetics and morphology in gas-quenched Fe-5 pct Ni alloys. Massive ferrite or nlurtensite was found to form at temperatures in agreement with earlier results. Surface Preparation appeared to have the greatest effect in determining the type of transformation Product formed. Grain size change, subgrain morphology, and dislocation densities of massive ferrite were essen-tinlly invariant functions of cooling rate. The mar-tens~tic structures were typical of transformation in austenite grains of the order of the sample thickness. BY introducing the idea of a massive transformation in dilute iron-base alloys, Gilbert and Owen in 1962 served to stimulate a closer inspection of phase transformations in ferrous systems.&apos; A wealth of literature has followed concerned with the morphology,2-5 transformation mode,2&apos;3&apos;6-8 and thermodynamics of transformations.2,5,9 interesting controversies have resulted from the experimental observations; closer attention has been paid to the definition of massive transformations and still to be resolved is the Ms temperature of pure iron. The purpose of this note is to report some observations made in a detailed kinetic and metallographic examination of the transformations that occur in gas quenched Fe-5 pct Ni. The results are pertinent to the Ms extrapolations that have been made for pure iron and the observed substructure of massively transformed alloys. PROCEDURE The material used in this investigation was cast as a 5 lb vacuum induction melted, carbon deoxidized heat. The ingot was hot worked to a strip 0.10 in. thick, decarburized, and cold rolled to final thickness. Specimens were punched to sample shape and decarburized in wet hydrogen at 600°C. The chemistry of test specimens is indicated in Table I. Samples 1 by $ in., by thickness were resistance heated and rapidly cooled in an apparatus as illustrated in Fig. 1. Similar helium quenching apparatuses have been described previously;2,6&apos;10 the distinguishing feature of this apparatus is the nozzle geometry. Twin nozzles with three convergent-divergent, sonic ports were mounted perpendicular to the specimen for quenching purposes. The specimen temperature was monitored with an intrinsic 3 mil chromel-alumel thermocouple spot welded to the specimen and con- nected to an oscilloscope. A single switch stopped the current flow through the specimen, opened a gas flow solenoid valve, and initiated an oscilloscope sweep. Cooling rates were read directly from a photograph of the oscilloscope trace and the quenching rates quoted later were made at a point immediately prior to transformation on the trace. All quenching studies were conducted either under a vacuum of 10"-5 torr or a helium atmosphere. The sample geometry was chosen large enough to permit optical and electron microscopy to be performed on samples. The samples were electropolished for both types of examination in a perchloric-acetic solution. Electron microscopy was conducted on a HU 11A microscope operated at 100 kv. Dislocation densities were determined at the same general operating reflection (110) on foils thick enough to produce Kikuchi patterns. RESULTS AND DISCUSSION Transformation Temperature Observations and OD-tical Microscopy. The quenching results of this study are illustrated in Fig. -2(a). Samples which were treated in the as-decarburized condition transformed in a manner similar to that reported previously—a decrease in transformation temperature occurred as the quenching rate increased until a plateau region was reached. Within the scatter of the results obtained here, there was no break in the transformation temperature-quenching rate plot. This suggests no change in transformation mode. Further metallographic examination confirmed this observation. A martensitic transformation was obtained for similarly treated samples except that the surface was first electropolished. The Ms temperature was approximately 85°C below the plateau determined for the unpolished samples and cooling rates as slow as 2000°C per sec were adequate for producing marten-site. The transformation temperatures are in gen- / STRIP SAMPLE / COPPER I SAX/-/}&apos; / CONNECTOR-----A f, SON|C poRTS AC LEADS 3j ]j"I rofe[ \ Mf/yinK/iKj&apos;&apos;^ THERMOCOUPLE X-(^—iie"s*c? &apos; LEADS 1 INCH Fig. 1-—Schematic scction of gas quenching apparatus

Jan 1, 1970

By W. O. Philbrook, R. S. Kaplan

Rates of oxidation were studied for levitation-melted samples of Fe-C, Fe-Si, Fe-C-Si, Fe-C-P, Fe-C-Mn, and Fe-C-S alloys oxidized by mixtures of either 5 or 10 pct O2, in helium at several temperatures in the range 1850o to 2050°C. The concentrations of the oxidized elements decreased linearly with time. Mass transport in the gas phase was found to be the rate-controlling step. Ilowever, a mulliple -film model was necessary to account for the flux of iron and manganese vapor counter to the oxygen flow. THE advent of the basic oxygen and spray-refining processes of steelmaking has generated considerable interest in the kinetics of reactions between oxygen-bearing gases and liquid iron alloys. The object of this research was the determination of the role of mass transport in the gas and metal phases and of surface chemical reactions in the overall oxidation process. Of the reactions for elimination of elements dissolved in liquid iron, the oxidation of carbon has been investigated most extensively. Studies by Fuji and Ura,1 Fuji,&apos; and Gunji et a1.,3 done with pilot-scale basic oxygen furnaces, indicated that mass transport of gaseous oxygen was rate controlling when the metal carbon content was greater than 0.15 to 0.30 pct. When the carbon content was less than this critical amount, diffusion of carbon dissolved in the iron was thought to be rate limiting. L. A. Baker et a1.4,5 levitated samples of iron-carbon alloys and oxidized them in CO-CO2, CO-C02-He, and O2-He atmospheres at 1660°C. These investigators found that the metal carbon concentration decreased linearly with time and their samples exploded when the carbon content fell below about 0.8 pct. They concluded that the rate-limiting step was the transfer of oxidant to the gas-metal interface. A model based on this rate-limiting step predicted decarburization rates within a factor of two of those experimentally observed. The explosion of the samples was attributed to a shift in rate-controlling step from gas-phase mass transport to transport of carbon dissolved in the metal. L. A. Baker and R. G. ward6 and R. Baker7 used freely falling droplets to investigate oxidation kinetics. In both papers, the authors speculated that flame fronts may have been partially responsible for the lack of better agreement between experiment and theory. Swisher and Turkdogan8 oxidized liquid iron having an initial carbon content of 0.97 pct with CO-CO2 and CO-C02-Ar mixtures at 1580°C. They concluded that a surface reaction was the rate controlling step. Iron-silicon alloys have been oxidized by R. Baker7 and Filipov and Martynov.9 R. Baker 7 also studied iron-carbon-silicon alloys falling as liquid droplets through oxygen. He found that the rate of both carbon and silicon oxidation varied inversely with the drop radius. When the initial silicon concentration was greater than 6 pct, the samples cooled during their fall. Manganese oxidation has been studied by R. Baker,7 and by Filipov and Martynov.9 ward10 investigated the loss of manganese from liquid iron under vacuum. He found that mass transport of manganese vapor was rate limiting in argon atmospheres of 0.02 torr to 700 torr pressure. Iron-sulfur alloys were desulfurized with H2-He and H2-Ar mixtures by Peters et al.11 A model based on the transport of H2S from the gas-metal interface into the bulk gas gave fair agreement between the predictions of the model and the experimental results. EXPERIMENTAL TECHNIQUE Essentially, the technique consisted of using helium-oxygen gas mixtures to oxidize levitated samples of liquid binary and ternary iron-base alloys. The fused silica reaction tube is shown in Fig. 1. The coil design is similar to that of L. A. Baker et al.4&apos;5 A Tef-lon-sheathed, ferritic stainless steel lifter (B) and an alumina pedestal (C) were used to support the sample in the coil prior to levitation and for the recovery of the sample. Samples were inserted into

Jan 1, 1970

By John Campbell

An approximate theoretical model is proposed to quantitatively predict freezing ranges Tf and hydrostatic tensions P developed within solidifying binary alloys, allowing for a certain amount of diffusion of solute in the solid during solidification. The maxima in ATf and AP as functions of composition are shorn to occur at smaller solute concentrations than would be expected from the equilibrium diagram, and are found to correspond closely to experimentally observed maxima in microporosity. THE freezing range of simple binary alloys appears to have been little studied, except for certain indirect observations on the defects, particularly microporosity and hot tearing, arising in long freezing range materials. Two theories relating to the freezing range of alloys and its effect upon porosity are reasonably well established, and appear to have been held in isolation from each other: a) From purely equilibrium considerations early researchers expected that an increase in solute content of an alloy should increase the freezing range (defined here as the equilibrium freezing range ?Tf = Tl-Ts where TL and Ts are the liquidus and solidus temperatures, respectively) and thereby increase the width of the pasty zone for a given set of conditions. This in turn should increase the difficulty of feeding the residual liquid through the dendrite mesh to compensate for the contraction on solidification, and consequently tend to increase the observed amount of porosity. From qualitative observations on steels Czikel1 reports an increase in porosity with increasing carbon content up to 0.46 pct C. More careful measurements by Whittenberger and Rhines2 on fourteen different alloy systems showed an approximately linear relation between ?Tf and pct porosity (although unfortunately the precise experimental data is not given). b) Conversely however, other authors3"5 propose that porosity is reduced by the presence of increased amounts of eutectic present at the final solidification temperature. Lees7 and Bochvar6 claim that the hot tearing of alloys is similarly reduced. Scheuer8 has put forward a theory to explain this effect, Fig. 1. The argument is basically that solidification progresses on a plane front through a relatively open dendrite network and is thus (the argument is not developed more explicitly) easier to feed. One would expect effect a) to operate at low solute contents, and b) to be important at higher solute contents, so that at some critical composition a max-

Jan 1, 1970

By E. W. Dewing

The solubility of A14C3 in cryolite melts has been determined by holding the melt with aluminum in a graphite crucible for 4 hr at temperature, quenching the crucible in water, and analyzing the frozen salt by CH4 evolution. The solubility is given by log(wt % Al4C3) = 1.298 -1.l74 (wt ratio NaF/AlF3) independent of temperature in the range 985" to 1080°C. Additions ofA1203, .NaCl, CaF2, or LiF up to 10 wt pct do not affect the solubility, provided that LiF and CaF2 are replaced by equivalent NaFin calculating the ratio. The variation with ratio can be accounted for quantitatively on the hypothesis that the Mechanism of solution is Al4C3 + 2AIF3 = 3Al2CF2 since the solubility varies as (aAIF3) 2/3; Mechanisms involving C", C2- , AlC- , A12C2+, and Al2CF+are re-jected. At ratios above 1.5 truces of c;- are also present. It was noticed some years ago in this laboratory that carbon specimens made cathodic in a cryolite bath decrease in diameter over a period of time.&apos; It was also found that cryolite which had been melted with aluminum in a graphite crucible was sometimes yellow, and that A14C3 could be seen intimately embedded in the cryolite crystals. CH, could be recovered by acid attack. There was thus reason to believe that A14C3 had a genuine solubility in molten cryolite, and the object of this work was to measure it. EXPERIMENTAL AND RESULTS A graphite crucible, 2 in. ID and 2.5 in. deep with a close-fitting lid, contained about 150 g of cryolite (plus additives) and about 20 g of 99.99 pct pure Al. It was placed in a vertical Inconel furnace tube, covered with refractory brick to provide thermal insulation, and the top of the tube was roughly sealed with disks of asbestos paper. An alumina tube led argon down to the level of the top of the crucible to expel air, and an alumina sheath with a Pt-10 pct Rh ther-mocouple inside was positioned between the crucible and the wall of the Inconel tube. The tube was heated in an electrical resistance furnace for the desired length of time; the refractory bricks were then removed, and the crucible was lifted out with tongs and quenched in water. After such a crucible was broken open it could be seen that its inner surface was yellow owing to the presence of A1,C3, and sometimes needle-like crystals could be observed (at X75 magnification) growing out into the nielt. It was concluded that Al,C, had been present as a separate phase when the crucible was at tenlperature and that the melt had been saturated: in

Jan 1, 1970

By A. S. Venkatadri, H. B. Bell

The equilibrium sulfur distribution between molten iron and Ca0-Mg0-Al203 slags containing iron oxide was investigated at 1550°C. The results were used to derive the iron oxide activities at low iron oxide concentrations in the slag by combining the sulfide capacity data obtained from gas-slag work with the free energies of both the sulfur solution in iron and the iron oxide formation in slag. The derived ferrous oxide activities were compared with values based on Tem-kin&apos;s kin&apos;s and Flood&apos;s ionic models. One difficulty in using these models is that the nature of the aluminate ion in slag is uncertain. Nevertheless, such indirect methods, in particular, those described in the present paper, are of value because of the difficulty of measuring small amounts of oxygen in liquid iron in equilibrium with slag. It is shown that these methods confirm the consistency of thermodynamics data on liquid iron and slags. It is well established that decreasing the iron oxide activity in the slag increases the desulfurization of molten iron at constant slag basicity. This effect is most pronounced at the very low iron oxide activities, characteristic of blast furnace slags. Yet a precise quantitative determination of the significance of low iron oxide contents in slag in blast furnace desulfuri-zation is not possible for the following reasons: a) difficulty of separation of iron "shots" from the slag, and b) errors in chemical analysis of small amounts of iron oxide in slags. In view of these obstacles, one must resort to indirect methods of calculating iron oxide activities. EXPERIMENTAL TECHNIQUE The apparatus for providing the sulfur equilibrium data has been described previously1 and was similar to that used by ell&apos; in connection with the study of slag-metal manganese equilibrium. The procedure consisted of: a) melting about 50 g of Armco iron in a magnesia crucible in a platinum furnace, b) adding a mixture of about 15 g of lime-alumina slag and varying amounts of Fe2O3 and CaS, and c) maintaining the temperature at 1550°C for more than an hour in an atmosphere of argon to enable the sulfur equilibrium to be attained. Several melts were made using lime-alumina slags with basic composition 55, 50, and 45 pct lime. During the experiment the temperature was controlled manually using a Pt/10 pet Rh-Pt thermocouple. After the experiment, the Power was shut off and the flow rate of argon was increased to freeze the melt as quickly as possible. The analysis of sulfur in the metal was carried out by the oxygen combustion method3 using uniform drillings from the top and bottom of the metal button. After crushing and grinding and removal of any iron particles with the aid of a hand magnet, the slag was analyzed for sulfur by the CO2 combustion method.4 The E.D.T.A. method was employed for the analysis of lime5,6 and magnesia,= the ceric sulfate method7 for the analysis of slag iron oxide, and the perchloric acid dehydration method5 for the analysis of silica. The remaining amount was taken to be Al2O3 precipitation with ammonium hydroxide in several preliminary melts had confirmed the propriety of using this simple procedure. RESULTS The activity of iron oxide in binary, ternary, and more complex slags has been the object of numerous investigations, and the two experimental methods for its determination are: 1) Equilibrating the metal with the slag in question and measuring the oxygen content of the metal. The ferrous oxide activity is then given by aFeO L%OJSat where [%0]sat is the oxygen content of the metal in equilibrium with pure iron oxide slag. This method was used by Chipman et al.8,9 2) Equilibrating the slag in iron crucibles with known partial pressures of H2/H2O or CO/CO2 mix-tures.10-12 This method is limited to temperatures between 1265" and 1500°C. The very low oxygen content of the melts in this investigation made it impossible to derive the ferrous oxide activity by the first of these methods. Therefore, the iron oxide activities were computed by means of: Sulfide capacity data from the gas-slag work" Temkin&apos;s concept14 Flood&apos;s approach15 a FeO from Sulfide Capacity. The method of calculating the aFeO involves the sulfide capacity of the slag (c,), the sulfur distribution coefficient (Ls), the free energy of dissolution of sulfur in iron, and the free energy of formation of iron oxide in the slag. Bell and Kalyanram13 have investigated the sulfur absorption characteristics of lime-alumina slags containing magnesia by the Carter-Macfarlane method16 (based on comparing the sulfide capacity of the slag in question with that of a standard slag of unit lime activity) and have derived lime activity values. The relation between sulfide capacity and their lime activity a&apos;CaO is given by: Cs= 3—: Xa&apos;CaO at 1500°C

Jan 1, 1970

By A. H. Larson, T. P. McNulty

RECENTLY, an investigation of the absorption of sulfur dioxide gas in molten binary copper alloys was conducted. A Sieverts-type apparatus, consisting of a mercury-filled gas dispensing buret and a mercury manometer, was used initially for determining the volume of gas absorbed as a function of pressure. The equilibration behavior of the alloys studied indicated that the mercury in the gas measuring system was absorbing sulfur dioxide. Owing to the widespread use of mercury as a displacement medium in absorption studies, an investigation was made to determine the nature and magnitude of the mercury - sulfur dioxide absorption effect. The gas measuring system was modified by substituting a Worden Quartz Products Type PDHV fused-quartz-spiral pressure gage for the mercury-filled dispenser and manometer. The dispensed gas volume at known temperature and atmospheric pressure was measured by evacuating a Pyrex vessel of known volume and by admitting sulfur dioxide into the vessel until the attached quartz pressure gage registered atmospheric pressure. Atmospheric pressure was measured concurrently with a separate mercury barometer. The volume of the empty sample chamber and its attendant apparatus was determined by measuring the equilibrium pressure accompanying the addition of a measured volume of sulfur dioxide into the initially evacuated system. The volume of the mercury sample was calculated from the density of mercury at the temperature of the study (25°C). Measured volumes of sulfur dioxide were then dispensed into the system and the equilibrium pressure accompanying each gas addition was determined. From the difference between the system volume and the mercury volume, the number of moles of gaseous sulfur dioxide remaining in the system at each pressure was calculated. The difference between the number of moles of gas dispensed into the system, denoted Enso2: and the number of moles of gas remaining in the system after absorption equilibrium had been attained, denoted nso2(g), was equal to the number of moles of absorbed gas, denoted nSO2. The number of moles of absorbed gas was then converted to absorbed volume, denoted VSo2, in cu cm at stp conditions of (PC and 760 mm Hg. Table I contains calculated values of Snso2, nSo2(g), and VSo2 for different sulfur dioxide pressures. In the original system, denoted Run I, volume limitations of the gas dispensing system prevented absorption studies at equilibrium pressures near atmospheric pressure, so a different gas dispensing system, denoted Run 11, was used for determining the last pressure reading in Table I. The data in Table I are expressed in terms of the absorption of sulfur dioxide in 49.68 cu cm of mercury. In Fig. 1, these data are expressed in terms of the absorption of sulfur dioxide in 100 cu cm of mercury. Since the absorption data plotted in Fig. 1 show a linear relationship, the volume of sulfur dioxide absorbed in mercury is a function of the first power of pressure. The absorption reaction is So2(gas) = SO2 (in Hg) The first-power pressure dependence, coupled with the fact that the sulfur dioxide could be removed from the mercury by applying vacuum, indicated reversible

Jan 1, 1967