By J. H. Swisher

When an Fe-Mn alloy is internally oxidized, the inclusions formed are MnO which contains some dissolzled FeO. In the internal oxidation reaction, not all of the manganese is oxidized; some remains in solid solution as a result of the high Mn-0 solubility product in iron. Taking these factors into consideration, the rate of internal oxidation of an Fe-1.0 pct Mn alloy is computed as a function of temperature, using available thermodynanzic data and recently published data for the solubility and diffusivity of oxygen in iron. The predicted and experimentally determined rates for the temperature range from 950 to 1350°C are in good agreement. ThE rates of internal oxidation of austenitic Fe-A1 and Fe-Si alloys have been studied extensively.1"4 Schenck et al. report the results of a few experiments with Fe-Mn alloys at 854" and 956C, and Bradford5 has studied the rate of internal oxidation of commercial alloys containing manganese in the temperature range from 677" to 899°C. When Fe-Mn alloys are internally oxidized, the inclusions formed are solutions of FeO in MnO, the composition depending on the experimental conditions. Since the thermodynamics of the Fe-Mn and FeO-MnO systems have been investigated,6"9 and since the solubility and diffusion coefficient of oxygen in y iron have been determined recently,' it is possible to predict the rate of internal oxidation from known data. The calculations used in predicting the rate of internal oxidation will first be outlined, then the results of the prediction will be compared with the experimental results of this investigation. PREDICTION OF PERMEABILITY FROM THERMODYNAMIC AND DIFFUSIVITY DATA Oxygen is provided for internal oxidation in these experiments by the dissociation of water vapor on the surface of the alloy. The dissociation reaction is: + H2(g) + [O] [1] where [0] denotes oxygen in solution. The equilibrium constant for this reaction is known as a function of temperature:' log As oxygen diffuses into the alloy, oxide inclusions are formed which are MnO with some FeO in solid solution. The reactions occurring are: [Mn] + [0] = (MnO) [31 and [Fe] + [0] = (FeO) [41 where [ Mn] is manganese dissolved in iron and (FeO) is iron oxide dissolved in MnO. The overall reactions may be written as follows: [Mn] + HOte) = (MnO) + H2(£) [5] and [Fe] + H20(g) = (FeO) + Hz(R) [61 The standard free-energy changes and equilibrium constants for Reactions [5] and [6] are known.6 Therefore the equilibrium constants for Reactions [3] and [4] may be obtained by combining known thermodynamic data for Reactions [I], [5], and [6]. For Reactions [3] and [4]: K = and For the present purpose, both the Fe-Mn7,8 and FeO-~n0' systems can be considered to be ideal, i.e., [amn] = [NM~] and (aFeO) = (NM~~) = 1 - (NFeO) where the Ns are mole fractions. These relations, together with Eqs. [I] and [8], permit us to compute both the oxide and metal compositions as a function of temperature and oxygen potential at any point in the specimen. For cases where the oxygen concentration gradient between the surface and the subscale-base metal interface is linear, the kinetics of internal oxidation is an application of Fick's first law: where dn/dt is the instantaneous flux of oxygen into the specimen, g-atom per sq cm sec; 6 is the instantaneous thickness of the subscale, cm; Do is the diffusion coefficient of oxygen in iron, sq cm per sec; p is density of iron, g per cu cm; h[%O] is the oxygen concentration difference between the surface and sub-scale-base metal interface, wt pct. B6hm and ~ahlweit" derived an exact solution to the diffusion equation for systems in which there is a stoichiometric oxide formed. They showed that the oxygen concentration gradient is given by a rather complex error function relation. For the Fe-Mn-0 system and for most other systems that have been studied, however, variations in oxide compositions are small and rates of internal oxidation are sufficiently slow that the deviation from linearity in the concentration gradient of oxygen is negligible. The mass of oxygen transported across a unit area of the specimen for the total time of the experiment is given by the mass balance equation:

Jan 1, 1969

By R. V. Mrazek, F. E. Block, S. B. Knapp

The mixed homogeneous and heterogeneous kinetics of the thermal decomposition of tungsten hexacarbonyl were studied by employing a batch reactor. The system was such that a sample of tungsten hexacarbonyl could be injected into the preheated reactor, and the progress of the reaction followed by a simple pressure measurement. Both the homogeneous and heterogeneous reactions were found to be first order, and approximate activation energies were determined for each reaction. It is shown that the dis-proportionation of carbon monoxide to give carbon and carbon dioxide cannot be the source of carbon in tungsten deposits prepared by this reaction. The kinetics of the thermal decomposition of tungsten hexacarbonyl have been investigated as part of a continuing study by the U.S. Bureau of Mines on the decomposition of organometallic compounds. Reactions involving the thermal decomposition of metal carbonyls have a potential application in the preparation of pure metals and fine metal powders. Indeed, it was these applications which provided the impetus for much of the early work involving the carbonyls of nickel1 and iron.' The relative lack of study of other metal carbonyls can be traced to the comparative difficulty in synthesizing these compounds. The most common use for tungsten hexacarbonyl has been as an intermediate in vapor-phase plating.7'8 However, attempts to obtain a carbon-free deposit of tungsten by this method have not been successful, and some investigators have taken advantage of the carbon contamination and used this process to form tungsten carbide deposits.lo Other investigators have studied the thermodynamic properties11"14 and molecular structure of tungsten hexacarbonyl. However, very little is known about the kinetics of this thermal decomposition, the mechanisms involved," or the source of carbon in the resulting plate. In contrast, studies have been made of the kinetics of the thermal decomposition of nickel tetracarbonyl, iron pentacarbonyl, and molybdenum hexacarbonyl.'l It has been found that these thermal decompositions occur by a mechanism which is partially heterogeneous in nature. Information available on the equilibrium constants for the decomposition of tungsten hexacarbonyl was used to determine a temperature range, 500" to 560°K, in which the reaction could be expected to be essentially complete. APPARATUS The apparatus used allowed the injection of a sample of tungsten hexacarbonyl into a preheated batch reactor and the use of a simple pressure measurement to follow the progress of the reaction in the sealed reactor. The pressure was sensed by means of a pressure transducer (Consolidated Electrodynamics Corp., 0.3 pct)* capable of operating at the *Reference to specific products is made to facilitate understanding and does not imply endorsement of such brands by the Bureau of Mines._______ reaction temperature. This type of sensing element was chosen to avoid the problem of condensation of the sublimed carbonyl in the capillary tubing leading to any type of remote pressure-sensing device. stirring was provided by rotating the entire apparatus. Glass beads placed in the reactor provided a pulsating agitation. To minimize thermal gradients in the reactor walls, the reactor was constructed of aluminum. The support tube which held the reactor in the furnace was thin-walled stainless steel to minimize heat conduction out of the reactor. As a result of these measures, a nearly uniform temperature (°C) was maintained throughout the reactor. Fig. 1 is a schematic diagram of the apparatus. The small gear motor rotated the entire apparatus at about 200 rpm. The bearings shown at the ends of the air cylinder were perforated to allow air to be fed to the charging piston and to allow inert gas to be fed to the reactor during the preheating period. The sample was simultaneously injected and sealed inside the reactor by operation of the air piston. Fig. 2 shows a cross section of the air cylinder and the adjoining portion of the support tube leading to the reactor. The sample carrier is shown in place at the right-hand end of the injection rod extending from the air piston. The piston is shown in the retracted position, as it would be prior to the start of an experiment. The small Teflon gasket which encircled the sample carrier at the end of the injection rod sealed the reactor when the sample was injected. This seal was maintained throughout the test by maintaining air pressure on the piston. The sample carrier was a 2-in. section of thin-walled, -in.-diam nickel tubing with an internal blank about 1 in. from the base and with the base end sealed.

Jan 1, 1969

By Hsun Hu, R. S. Cline

The annealing behavior and the mechanism of re-orientation during recrystallization of iodide titanium cold-rolled 94 pct have been studied in detail. Results indicate that recrystallization occurs by the nucleation and growth of new grains, as in other common metals. Recrystallization nuclei form by the coalescence of subgraim, and the change in texture as a result of recrystallization is largely due to selective growth among the nuclei formed. The annealing of titanium is characterized by a wide range of overlap of the various stages of the annealing process, which may be responsible for a range of activation energies observed, and for the apparently gradual change in the annealing texture as a function of time or temperature. The deformation and recrystallization characteristics of titanium and zirconium are very similar. In cold-rolled strip, the deformation texture consists of two symmetrically oriented components, each having the basal plane laterally tilted at about 30 deg from the rolling plane and the [1010] direction parallel to the rolling direction. Upon annealing for recrystallization, the change in texture can be described, for simplicity,* as rotations around [0001].2'6'8 According to McGeary and Lustman,' recrystallization occurs in zirconium through normal growth of the subgrains, which they called "domains", without the nucleation of new grains; and the magnitude of rotation around the [0001] axis increases gradually during the progress of recrystallization. If these conclusions were true, the mechanism of recrystallization in zirconium would be basically different from that in most metals, since it is commonly known that recrystallization with reori-entation always involves the migration of high-angle boundaries. In an attempt to clarify the situation, the mechanism of reorientation during recrystallization in iodide titanium cold-rolled 94 pct was studied in detail. The structural and textural changes upon annealing at various temperatures were examined by optical and transmission-electron microscopy, X-ray pole figures, pole density distribution measurements, and micro-beam techniques. EXPERIMENTAL PROCEDURE Material and Specimen Preparation. An iodide titanium crystal bar was are-melted and solidified in a cold-hearth crucible under a purified argon atmosphere. The solidified ingot had dimensions of approximately 3 by 1/2 by 3 in. One face of the ingot was somewhat uneven, but was as clean and shiny as the remaining parts of the ingot. Large grains with a Widmanstatten internal structure were clearly shown on the shiny surfaces, indicating the occurrence of P — a transformation upon rapid cooling from the melt. Analysis of the are-melted ingot indicated C 0.033, N 0.010, H 0.013, 0 0.002 in weight percent, and traces of iron, copper, and silicon as detectable impurities. The ingot was cold-rolled -40 pct to 0.300 in. thick with a reduction of 0.005 in. per pass. The defects on the uneven side of the ingot were then removed by machining. This reduced the thickness to 0.285 in. The piece was then recrystallized by annealing at 800°C for 1 hr in a fused silica boat charged into a fused silica tube furnace under a vacuum of 10~5 mm Hg. To refine the grain size, the recrystallized metal was again cold-rolled 40 pct to 0.170 in., then annealed at 700°C for 1 hr. These treatments yielded a strip with a uniform equiaxed grain structure, having a penultimate average grain diameter of 0.04 mm and a hardness of approximately 90 Dph. Final rolling reduced the thickness from 0.170 to 0.010 in., corresponding to a reduction of 94 pct. The strip was rolled in both directions by reversing end for end between passes. Surface lubrication was provided by oil-soaked pads attached to both rolls. Specimens of 1 in. length (for X-ray examinations) and +in. length (for hardness and microstructure examinations) were cut from the rolled strip, and a width of & in. was cut from the edges of each specimen by a jeweler's saw. These specimens were then etched in a solution of 10 cu cm HN03, 5 cu cm HF, and 50 cu cm H,O to 0.008 in. thick to remove the surface metal, as well as the distorted metal at the saw cuts, prior to annealing or measurements. To minimize any surface reaction with the atmosphere, all specimens were kept in an evacuated desiccator. Isothermal Anneals. All annealing treatments were conducted in vacuum in a fused silica tube furnace as described earlier. The temperature of the furnace was controlled to within *2"C. The specimen was placed in a fused silica boat, then pushed into the hot zone of the furnace. It took about 5 to 6 min for the specimen to reach the furnace temperature. After the specimen was held at temperature for a desired length of time the boat was pulled to the cold zone of the furnace; the heating-up period was excluded from the isothermal annealing time. Thus, the uncertainty in annealing time is higher for very short anneals, but negligible for long anneals.

Jan 1, 1969

By H. Conrad, V. V. Damiano, G. J. London

The slip mode activated during the c axis compression of single crystals of commercial-purity ingot SR beryllium, high-purity (twelve-zone-pass) beryllium, and Be-4.4 wt pct Cu and Be-5.2 wt pct Ni alloys in the temperature range of 25° to 364°C was determined using two-surface slip trace analysis, slip-step height analysis, and electron transmission microscopy. All three techniques indicated the occurrence of copious pyramidal {1 122) (1123) slip in the alloys over the entire temperature range, the amount increasing with temperature. Pyramidal slip was also indicated in the high-purity beryllium by slip trace analysis and electron transmission microscopy, but the amount was somewhat less than in the alloys. For the commercial-purity ingot crystals, only a very small number of pyramidal slip lines were observed, and these were in the immediate vicinity of the fracture surface. No pyramidal dislocations could be detected by electron transmission microscopy in this material. Dislocatransmissiontions with Burgers vectors [0001] and +(ll20) were identified by electron transmission microscopy inthe (1122) slip bands, as well as those with the j (1123) vector. This was interpreted to indicate that the edge components of the 3(1123) vector dislocations activated during c axis compression dissociate upon unloading according to the reaction i (1123) — [0001] + 3(1120) THE microstrain c axis compression of single crystals of commercial-purity ingot SR beryllium (99.6 pct), high-purity twelve-zone-pass beryllium (99.98 pct), Be-5.24 pct Ni and Be-4.37 pct Cu alloys was described in a previous paper.1 This paper covers in detail the analysis of slip traces observed on two mutually perpendicular lateral surfaces of these specimens, and a detailed description of transmission electron microscopy studies performed on foils cut from the bulk crystals after they had been deformed to fracture in the c axis compression. Observation of slip traces on single surfaces of deformed single crystals are generally insufficient to positively identify slip or twinning modes. The use of two carefully cut and oriented perpendicular surfaces can greatly aid in the positive identification and index- ing of slip traces, although even this technique may be quite inadequate if more than one type of slip system operates and if an insufficient number of traces are observed on the surfaces. The problem is greatly simplified for symmetric cases like that for c axis compression of an hep crystal such as beryllium, in which the operating slip systems are all equally inclined to the direction of the applied stress, and each slip system of a given slip mode has an equal chance of operating. For such cases, the traces of any given slip mode observed on the surfaces cut parallel to the c axis are symmetrically tilted about the c axis. It is therefore possible to quickly determine whether one or more slip modes are operating. Confirmatory evidence in support of the observations made on the external surfaces can be obtained from foils cut from the deformed crystals and examined by transmission electron microscopy. This latter technique serves to identify not only the operating slip plane but also the Burgers vector of the dislocations which participate in the slip. For this purpose, a simplified technique based upon a double tetrahedron notation is used in the present paper. The planes and directions in the hep lattice are all designated by letters rather than indices and extinction conditions are easily determined if the Burgers vector lies in the plane contributing to the diffraction. RESULTS 1) Slip Trace Analysis. The standard (0001) stereo-graphic projection of beryllium is shown in Fig. 1. The two mutually perpendicular, lateral surfaces of the compression specimen are represented by the diametrical planes AA' and BB', also referred to as surface A and surface B. For the specific case represented (a Be-5.24 pct Ni specimen deformed by c axis compression at room temperature), the A surface is tilted 5 deg to the (10i0') plane and the B surface is tilted 5 deg to the (1120) plane. Two surface trace analyses may be facilitated by examining in turn the intersection of various great circle traces of specific pyramidal planes with two surfaces and comparing the angles made with the (0001) plane with those actually observed on the two surfaces. One then identifies the slip traces by trial and error on a best-fit basis. The (1122) type planes (it was found that slip occurred on these planes) are shown plotted on the stereographic projection in Fig. 1. One obtains directly the angles between the (0001) plane and the {1122) traces by measuring the angle from the periphery to the point of intersection along the lines

Jan 1, 1969

By H. Conrad, V. V. Damiano, G. J. London

A method is described for producing single crystals of high-purity beryllium, Be-4.37pct Cu, and Be-5.24 pct Ni. These crystals were prepared for testing in compression parallel to the [0001] by orienting and lapping to within ±3' of arc of the (0001). Microstrain testing apparatus is described along with c axis compression results for ingot purity beryllium, twelve-zone-pass material, and the above-mentioned alloys. Results show no measurable plasticity for the ingot purity material from -196" to 400°C, although some surface traces of (1122) slip was observed at 200°C and above. The twelve-zone-pass material shows substantial microstrain plasticity at 220°C with slip on (1122). Both alloys show significant plasticity at room temperature and above with slip also on (1122) planes. THE two slip systems which normally operate during the plastic deformation of beryllium in the vicinity of room temperature are:' basal slip (0001)(1120) and prism slip . Pyramidal slip with a vector inclined to the basal plane has been reported for elevated temperatures,'-a but occurs near room temperature only at very high stresses.~ A summary of the available data on the effect of temperature on the critical resolved shear stress for slip on these systems has been compiled by Conrad and Perlmutter.~ It has been postulated6'7 that one of the principal factors contributing to the brittleness of poly crystalline beryllium at temperatures below about 200°C is the difficulty of operating pyramidal slip with a vector inclined to the basal plane. Hence, detailed information on the operation of such a slip system is important to understanding the brittleness of beryllium. The operation of pyramidal slip with a vector inclined to the basal plane is best accomplished in beryllium by compressing single crystals in a direction parallel to the c axis. In such a test the resolved macroscopic shear strzss on the basal and prism planes is zero and (1012) twinning which is favored by tension along the c axis does not occur. Hence, in c axis compression of beryllium the normal deformation modes are inhibited and the operation of pyramidal slip with a vector inclined to the basal plane is favored. In the present investigation, c axis compression tests were performed on beryllium single crystal as a function of temperature (77" to 700°K), purity (commercial and twelve zone pass), and alloy content (4.37 wt pct Cu and 5.24 wt pct Ni). Presented here is a description of the test techniques employed and the gross mechanical behavior observed. A detailed analysis of the slip traces developed on the surfaces of the deformed specimens during these tests and the results of electron transmission studies of the deformed crystals are given in a separate paper.B PROCEDURE 1) Materials and Preparation. Single crystals about 1 in. diam were prepared of the following materials: commercial-purity beryllium, high-purity beryllium, and two beryllium alloys, one with 4.37 wt pct Cu and the other with 5.24 wt pct Ni. The commercial-purity single crystals were obtained by cutting specimens from large-grained ingot of Pechiney SR material, which is approximately 99.98 pct pure. The high-purity crystals were prepared by floating-zone refining (twelve passes) a rod (7 in. by 1 in, diam) of Pechiney SR grade cast and extruded beryllium. Although an absolute chemical analysis of the zone-refined material was not established, mass spectro-graphic analysis, emission spectrographic analysis, and y activation analysis indicated that it contained in atomic fractions about 5 to 10 ppm each of carbon and oxygen, 1 to 5 ppm each of nickel and iron, and about 1 to 2 ppm of copper, with the remaining residual impurities being less than 1 ppm. Further indication of the purity of this material is provided by the critical resolved shear stress for basal slip, which was approximately 300 psi. The starting material for the alloy single crystals was 1-in.-diam floating-zone-refined (six passes) rod of Pechiney SR grade beryllium. Two such rods were wrapped respectively with sufficient weight of wire of high-purity copper (99.999 pct) or nickel (99.999 pct) to yield a 5 wt pct alloy. A seventh floating-zone pass was then applied to each of the rods to accomplish the initial alloying and an eighth pass for homogenization. Analytical samples were taken from regions of the rod immediately adjacent to where the mechanical test specimens were cut; these indicated 4.37 wt pct Cu and 5.24 wt pct Ni. 2) Crystal Orientation. To avoid the occurrence of basal slip during c axis compression testing, it is necessary to load the crystals as nearly parallel to the c axis as possible. Preliminary c axis compression tests indicated that plastic flow and/or fracture occurred at stresses of the order of 300,000 psi; hence on the basis of a critical resolved shear stress for basal slip of 300 to 400 psi, the maximum crystal misorientation permitted is about 4 to 5' of arc. Since this accuracy cannot be obtained using the usual back-

Jan 1, 1969

By H. Biloni, R. Morando

The surface structure and substructure of Al-Cu alloys solidified as conventional ingots and under particular conditions such as those used by Bower and Flemings are studied. The influence of lampblack coating on the mold walls is especially considered and the results compared with those obtained in copper and graphite molds where no coatings exist. When high heat extraction conditions exist the observations show that mechanism of copious nucleation is responsible for most of the chill zone. When the heat extraction through the mold walls is low, a coarse grain structure with dendritic morphology arises, with a size that depends on the degree of convection present, analogous to that analyzed by Bower and Flemings. In both cases the effect of the convection on the macroscopic and microscopic appearance is discussed. The ingot macrostructure consists of one or more of three zones: "chill zone", "columnar zone", and central "equiaxed zone". The mechanism of the columnar-equiaxed transition has been subject of considerable interest and at present at least three theories exist about the formation of the equiaxed region: 1) the constitutional supercooling theory1 maintains that the equiaxed crystals nucleate after the columnar zone has formed, as a result of the constitutional supercooling of the remaining liquid; 2) chalmers2 pointed out, however, that there were several objections to this proposal, and that consideration should be given to the possibility that all the crystals, equiaxed as well as columnar, originated during the initial chilling of the liquid layer in contact with the mold; 3) Jackson et aL3 and O'Hara and ~iller~ suggested that a remelting mechanism of the dendrite arms is responsible for the formation of the equiaxed region. After the work of Cole and Bolling and other authors6 it became evident that convection (natural, reduced, or forced) plays a very important role in the transition from columnar to equiaxed and on the size of the resultant equiaxed structure. Until recently the accepted explanation of the chill zone was that it occurs as a result of copious nucleation in the liquid layer in contact with the mold walls.798 The columnar region is a subsequent result of the growth of favorably oriented grains and, as a result of a selection mechanism studied by Walton and Chalmers,9 elongated grains with marked texture are formed. Recently, however, Bower and Flemings" using an ingenious laboratory experiment introduced the idea that the "copious nucleation" mechanism is not responsible for the formation of the chill zone and that the presence of convection, introducing some form of "crystal multiplication", plays a decisive role in the formation of the chill zone. Unfortunately, it is important to consider that for their conclusions Bower and Flemings extrapolated the results obtained in their special experiments to the case of conventional ingots, and that these authors only analyzed the macrostructures of the specimens. Let us consider the work by Biloni and chalmers" concerning predendritic solidification. These authors were able to show that a study of the segregation substructure of A1-Cu gives information about the nucleation and growth of crystals formed in contact with a cold surface. A spherical predendritic region characterizes the first part of every grain nucleated in contact with the surface as a result of the chill effect. The aim of this paper is to elucidate through the observation of the segregation substructure the conditions under which (in the Bower and Flemings type of experiments and in conventional ingots) either the nucleation or the multiplication mechanism gives rise to the structure in contact with the mold walls. I) EXPERIMENTAL TECHNIQUES The experiments were performed on two alloys: Al-1 wt pct Cu and A1-5 wt pct Cu. The purity of the aluminum was 99.99 pct and the copper 99.999 pct. The results obtained with both alloys were similar. In the Bower and Flemings type of experiments the apparatus employed to obtain rapid solidification against a surface was similar to that used by those authors. The liquid was drawn by partial vacuum into the thin section mold cavity. Plate casts were 5 cm wide and usually 7.5 cm high. The thicknesses of the cast were 0.1 and 0.3 cm. Two different materials were used for the mold, copper and nuclear-grade graphite. The internal mold surfaces were polished and left uncoated for some experiments. In other experiments, the copper or graphite surface was coated with a thin film of lampblack material. In some of these particular experiments one of the mold walls was left with an uncoated region (usually in the form of a cross). The conventional ingots were cast in graphite or copper molds. In different experiments the mold walls were sometimes uncoated or coated with lampblack material. The results obtained in conventional and Bower and Flemings copper molds were compared with those obtained with copper molds coated with a very thin film of graphite; the results obtained were essentially similar. The size of the conventional ingots was 5 cm diam and 7 cm high in all cases. The cast surfaces produced by the Bower and Flemings type of experiments and conventional methods were observed macroscopically and microscopically without any metallographic preparation. As Biloni and Chalmers showed," the observation of the chill surface can give considerable information about the structure and segregation substructure.

Jan 1, 1969

By G. W. Healy, L. F. Sander

was investigated by reacting thin discs of calcium oxide with gas mixtures of CO2, CO, and Son. Its value was 19,300 * 300 cal independent of temperature in this range. No solid solubility of sulfur in calcium oxide was detected within the limits of the experimental method and it is estimated to be below 0.025 pct by weight. The importance of lime in desulfurization is well-established but complete information on the pure phase equilibrium: CaO + 1/2 s2 = CaS + +02 [11 is not yet available. The goal of this work was to evaluate solid solubility of CaS in CaO and to determine the free-energy change associated with Reaction [I] at temperatures of 1400" to 1650°C. The equilibrium constant for Reaction [1] can be written: It is convenient to rewrite Eq. [2] in the form: where A = {Ps /PqJ1'2 has been referred to' as the "sulfurizing power' of a gas mixture. In this work, thin discs of CaO were suspended in a vertical tube furnace and exposed to CO + CO2 + SOz gas mixtures having known values of A. The samples were then analyzed for sulfur. As expected, X-ray diffraction confirmed that CaS was the only sulfur-bearing phase formed at the relatively low oxygen pressures used. EXPERIMENTAL PROCEDURE Reagent-grade CaCO3 was pressed in a 3/8-in.-diam pill die and prefired in air to produce CaO discs weighing between 0.004 and 0.01 g. Several discs were used to provide a suitable weight for chemical analysis while maintaining a large surface area to react with gas mixtures. These were placed in a platinum mesh basket and suspended in the gas stream in the hot zone of a vertical tube furnace. Desired gas mixtures were prepared from cp grade CO and CO2 and anhydrous grade SO2. The method of soap bubble displacement was used to calibrate capillary flow meters. While this gave excellent results with CO and Con, some problems with bubble insta- bility and soap film "drag" arose with the use of SO2 at low flow rates. Hence, frequent sampling and analysis of gas mixtures was carried out to insure proper control of the ingoing SOZ. The furnace used for gas:solid equilibration was a vertical mullite tube externally wound with 60 pct Pt-40 pct Rh wire having a diameter of 0.028 in. An inner tube of $ in. ID served as the reaction chamber having Pyrex ground joints sealed to the mullite to provide gas-tight connections at top and bottom. A Pt-Pt 10 pct Rh thermocouple was inserted into a protection tube adjacent to the sample basket to measure sample temperature during a run. Constant-temperature control to 2C was observed at any desired set point within the range of this investigation. This was accomplished by a control thermocouple imbedded in the furnace windings which served to actuate an electronic controller wired for high-low operation. The sulfur analyses of the solid samples were carried out using a stoichiometric combustion technique based on the method of Fincham and Richardson. Some analyses were done using a modified evolution method3 but these were used primarily to check the results of the combustion method. The results were in good agreement but the combustion technique of-ferred an advantage in economy of time and material. CALCULATION OF GAS EQUILIBRIA Heating a given mixture of CO + CO + SO2 to high temperatures gives rise to a large number of product species. The details of calculating the partial pressures of these products of interaction and dissociation can be found in several references4,5 and need not be repeated here. The thermodynamic data selected for the major species in the gas mixtures are shown in Table I. Equilibrium constants from these reactions were combined with oxygen, carbon, and sulfur balances and a computer program written to facilitate the calculations. Some early difficulties in reproducing experimental results were finally traced to the effect of atmospheric pressure changes. No reference to consideration of this question had been found in the

Jan 1, 1969

By R. D. Schoone, J. T. Michalak

Recovery, recrystallization, and texture development of a cold-rolled aluminum-killed steel have been studied during simulated box annealing. Two different initial conditions existed prior to cold rolling: 1) essentially all of the nitrogen in solid solution and 2) most of the nitrogen precipitated as AlN. The combined effect of nitrogen and aluminum in solid solution before annealing was to inhibit recovery and sub-grain growth at temperatures above about 1000°F and to raise the recrystallization temperature range on continuous heating at 40°F per hr from 1000"-1050°F to 1065"-1085°F. For the material with nitrogen and aluminum initially in solution there was an inhibition in the nucleation of the (001) [110] texture component and an enhancement of the (111) [110] texture component. The differences in annealing behavior mzd texture development are attributed to preprecipitation clustering of aluminum and nitrogen at subboundary sites developed by prior cold working. THE annealing of cold-worked aluminum-killed steels has been the subject of numerous investigations.'-'2 These studies have been concerned with kinetics of recrystallization, with microstructure and texture development, and with the individual and combined effects of composition, thermal history prior to cold rolling, and heating rates during subsequent annealing. It has been shown that the inhibition of recrystallization, and the development of the pancake-shaped grain and recrystallization texture characteristic of aluminum-killed steels, can be associated with the precipitation of A1N particles during a recrystallization anneal involving heating rates in the range 20" to 80°F per hr. If the AIN is precipitated before cold rolling or if more rapid heating rates are employed, the cold-rolled steels recrystallize more rapidly to an equiaxed grain structure and texture comparable to that of rimmed low-carbon steel. The retardation of recrystallization, the development of the elongated grain structure, and the pronounced (111) texture have been attributed to: 1) precipitation of A1N at prior cold-worked grain boundaries to form a mechanical barrier to grain boundary migration;' 2) precipitation on the boundaries of the growing recrystal-lizing grains as well as on cold-worked grain boundaries;'" and 3) preprecipitation clustering or precipitation on subboundaries to retard recovery, nucleation, and growth. The present study was undertaken to study in more detail recrystallization and texture development during commercial box annealing of cold-rolled aluminum-killed steels. Comparison of the annealing be- havior after cold rolling, for two different conditions prior to cold rolling, was made in an attempt to define more clearly the role of aluminum and nitrogen in forming the recrystallization texture. A) MATERIAL AND PROCEDURE The material used in this investigation was a commercial low-carbon aluminum-killed steel which was hot-rolled with a finishing temperature of about 1565"F, then coiled at about 1020°F. The composition, in wt pct, was: 0.050 C, 0.30 Mn, 0.007 P, 0.019 Si, 0.03 Cu, 0.02 Ni, 0.02 Cr, 0.045 Al, and 0.004 N. Two 4.5 by 13 by 0.078 in. sections were cut from the center section of a hot-rolled panel and one of these was reheated to provide two different conditions prior to cold rolling: low AlN: as commercially hot-rolled, with aluminum and nitrogen in solid solution; and high AlN: as commercially hot-rolled, then reheated at 1300°F for 3.5 hr to precipitate most of the nitrogen as AlN. ~etallc&a~hic examination indicated that the reheating did not change grain size nor carbide distribution (some spheroidization of pearlite was noted). Texture analysis at half-thickness level showed that both sections had the same substantially random as-hot-rolled texture. The results of check chemical analysis of each sample are given in Table I. Both sections were cold-reduced 65 pct on a laboratory rolling mill to a final thickness of 0.027 in. Cold rolling, in one direction only, was in the direction of the prior hot rolling. Specimens 1.0 by 1.25 in. were cut from the cold-rolled sheets and given a simulated box anneal in an atmosphere of 2 pct HZ-98 pct He. Specimens were heated at a constant rate of 40°F per hr from room temperature to various temperatures in the range 750" to 1300°F and cooled immediately by withdrawal to the water-cooled end of a tube furnace. The temperature in the 6-in. uniform hot zone of the furnace was controlled within 3"F. Selection of the individual specimens was made to give a random distribution of annealing temperatures with respect to location in the cold-rolled sheet. At least two specimens of each condition were annealed to the same temperature and smaller specimens for light microscopy, transmission electron microscopy, and X-ray studies were prepared from each of these. Rolling-plane sections for each of these studies were taken at half thickness. Light microscopy and transmission electron micro-

Jan 1, 1969

By W. H. Herrnstein, F. H. Beck, M. G. Fontana

Sulfur solubility in a iron was measured in the 750 to 890°C temperature range and was found to be insensitive to ferrite purity within a limited composition range. The permeability of sulfur in ferrite was determined from the internal sulfidation of Fe-Mn alloys. From the solubility and permeability results, the diffusivity of sulfur in ferrite could be calculated. These results are summarized as follows: Dissolved sulfur decreased the lattice parameter of ferrite. The effect of dissolved sulfur on the tensile properties of ferrite at low temperatures was also determined. SINCE sulfur is an important residual impurity in commercial irons and steels, effects associated with the presence of sulfur as a solute in iron are of considerable practical interest. Unfortunately, certain basic information relative to the Fe-S system appears to be lacking in the literature, e.g., the effect of dissolved sulfur on the lattice parameter and mechanical properties of ferrite. In addition, discrepancies exist in previously reported results for the solubility of sulfur in ferrite. These discrepancies raise questions regarding the sensitivity of sulfur solubility to the purity and microstructure of iron. This study was undertaken primarily in an effort to obtain reliable data on the solubility of sulfur in ferrite. Additional objectives included determination of the permeability and diffusivity of sulfur in ferrite by the internal sulfidation method and determination of the effect of dissolved sulfur on the lattice parameter and tensile properties of ferrite. EXPERIMENTAL METHOD Three grades of iron, encompassing a range of impurity levels, were employed in the study. The grades were designated VME (vacuum-melted electrolytic), SPZR (single-pass zone-refined), and MPZR (multipass zone-refined). The composition of each grade is given in Table I. Poly crystalline and single-crystal strip specimens were employed in the solubility experiments. Uniform grain size strip (ASTM 3 to 5) of 0.005 to 0.020 in. thickness was obtained by alternate cold reductions of 60 thickness 60 to 80 pct and recrystallization at 650°C for i hr in pure, dry argon. Single-crystal specimens were produced in 0.010-in.-thick SPZR iron strip by the strain-gradient anneal technique. Recrystallized strip 0.25 in. wide was strained until a Luders band or bands had propagated over the length of the strip; the strip was then annealed by drawing it through a 150°C per in. gradient (890°C peak temperature) at 1 in. per hr in an atmosphere of pure, dry argon. Laue photographs of the crystals produced exhibited no discernible asterism. Specimens were equilibrated with H-H, atmospheres at temperatures between 750" and 890" by one of two methods, each of which makes use of the reaction: The encapsulation sulfurization method was employed in the majority of the solubility experiments. A strip

Jan 1, 1969

By L. F. Bryant, J. P. Hirth, R. Speiser

The surface, gain boundary, and twin boundary energies, as well as the surface diffusion coefficient, of cobalt were determined from tests at 1354°C in pure hydrogen. A value of 1970 ergs per sq cm was calculated for the surface energy, using the zero creep method. It was possible to measure the creep strains at room temperature because the phase transformation was accompanied by negligible irreversible strain and no kinking. Established techniques based on interference microscopy were used to obtain values for the other three properties. The gain boundary and twin boundary energies were 650 ad 12.7 ergs per sq cm, respectively, while a value of 2.75 x l0 sq cm per sec was determined for the surface dufusion coefficient. In the course of a general study of cobalt and cobalt-base alloys, information was required about the surface energy of cobalt. Hence, the present program was undertaken to measure the interfacial free energy, or, briefly, the surface energy, of the solid-vapor interface of cobalt. The microcreep method was selected for this measurement because other surface properties could also be determined from the accompanying thermal grooving at grain boundaries and twin boundaries. A brief summary of the methods for determining the various surface properties follows. At very high temperatures and under applied stresses too small to initiate slip, small-diameter wires will change in length by the process of diffu-sional creep described by Herring.1 The wires acquire the familiar bamboo structure and increase or decrease in length in direct proportion to the net force on the specimen. For a specimen experiencing a zero creep rate, the applied load, wo, necessary to offset the effects of the surface energy, y,, and grain boundary energy, y b, is given by the relation: where r is the wire radius and n is the number of grains per unit length of wire. The first results obtained from wire specimens were reported by Udin, Shaler, and Wulff.' udin3 later corrected these results for the effect of grain boundary energy. The grain boundary energy is determined from measurements of the dihedral angle 8 of the groove which develops by thermal etching at the grain boundary-free surface junction. For an equilibrium configuration: Measurements of the angle 8 can be made on the creep specimens4'5 or on sheet material, as was done in this investigation by a method employing interference microscopy.= If the vapor pressure is low, the rate at which grain boundary grooves widen is determined primarily by surface diffusion and, to a lesser extent, by bulk diffusion. The surface diffusion coefficient, D,, is obtained from interferometric measurements of the groove width as a function of the annealing time, t. As predicted by Mullins~ and verified by experiment, the distance, w,, between the maxima of the humps formed on either side of the grain boundary increases in proportion to if grooving proceeds by surface diffusion alone. For this case: where fl is the atomic volume and n is the number of atoms per square centimeter of surface. When volume diffusion also contributes to the widening, the surface diffusion contribution can be extracted from the data by the method described by Mullins and shewmon.8 Where a pair of twin boundaries intersects a free surface, a groove with an included angle of A + B (using the groove figure and notations of Robertson and shewmong) forms by thermal etching at one twin boundary-free surface junction. If the "torque terms", i.e., the terms in the Herring10 equations describing the orientation dependence of the surface energy, are sufficiently large, an "inverted groove" with an included angle of 360 deg-A'-B' develops at the other intersection. The angles A + B and A' + B' are measured interferometrically. When the angle, , between the twinning plane and the macroscopic surface plane is near 90 deg, the twin boundary energy is calculated from the relation: 1) EXPERIMENTAL TECHNIQUES Five-mil-diam wire containing 56 parts per million impurities was used for making ten creep specimens. These specimens had about 15 mm gage lengths with appended loops of wire and carried loads (the specimen weight below the midpoint of the gage length) ranging from 3.7 to 149.8 mg. The wires were hung inside a can made from 99.6 pct pure cobalt sheet. Beneath the wires were placed small specimens of 20-mil-thick, 99.9982 pct pure cobalt sheet from which the relative twin boundary and grain boundary energies and the surface diffusion coefficient were measured. All the specimens were annealed at a temperature of 1354" i 3°C which is 92 pct of the absolute melting point of cobalt. The furnace atmosphere was 99.9 pct pure hydrogen that was purified further by a Deoxo catalytic unit, magnesium perchlorate, and a liquid-nitrogen cold trap. As a precautionary measure the gas was then passed through titanium alloy turnings which were heated to 280" to 420°C and replaced after every test period. The hydrogen was maintained at a

Jan 1, 1969

Jan 1, 1969

By R. L. Pober, L. Kaufman, E. V. Clougherty

Composite structure of hafnium, zirconium, and titanium diboride with additions of metals and/or compound phases were prepared by reactive high-pressure hot pvessing and evaluated in air and in mixtures of oxygen and helium at temperatures up to 2400°K and at linear flow rates of 0.1 to 0.2 ft per sec stp. Oxidation characteristics, principally depth of conversion of diboride to dioxide, were determined by a gas analysis method and by postoxidation metallo-graphic analyses. The best oxidation resistance was observed for hafnium diboride-silicon carbide composite which exhibited a 6-mil conversion to dioxide for a 1-hv oxidation in air at 2200°K compared to a 20-mil recession for hafnium diboride with no additive. Analogous improvements in oxidation resistance were observed for the addition of silicon carbide to zirconium. EARLIER investigationof the oxidation behavior of the diborides of the transition elements of Groups IVA and VA in flowing gas mixtures have produced a ranking of these compounds according to which HfB2 is the most oxidation-resistant followed in turn by ZrB2 > TiB2 > TaBz > NbB2. Other ~tudies~-~ have examined the physical, thermal, and thermodynamic properties of these diborides to provide a sound basis for the more detailed and specialized investigations which are required to generate the information needed to assess the usefulness of such materials in high-temperature oxidizing environments. Recent oxidation studies7 have examined the effect of variations of metal and boron content on the oxidation characteristics of zirconium and hafnium diboride in flowing gas mixtures including air and helium plus oxygen. Results obtained in the latter investigation confirmed the superior oxidation resistance of HfB2 over ZrB2. Moreover, metal-rich compositions of hafnium diboride showed improved oxidation resistance over boron-rich compositions at temperatures up to 2000°K; at higher temperatures the differences are not distinguishable. In particular HfBI.7 exhibited a diboride to dioxide conversion depth of 4 mils in 1 hr at 2000°K; HfB2. 2 exhibited a conversion depth of 16 mils for the same exposure.~ Specimens for the study of metal and boron stoichiometry on the oxidation characteristics of HfB2 and ZrB2 were prepared by high-pressure hot pressing, a specialized type of fabrication which produced dense crack-free bodies of the desired compositions with no significant impurity introductions. The purpose of the present investigation was to explore the possibility of further improving the oxidation resistance of the metal-rich ZrB, and HfB2. The plan to accomplish this objective was based in the formulation of several diboride compositions containing other compounds and phases which are generally known to have good oxidation resistance in one or more types of test environment. Ideally, such additives would also enhance or at least not diminish other boride property values principally mechanical strength and those parameters related to thermal stress resistance. The additions selected for HfBz included zirconium, aluminum, and (Ta + TaB2) designed to produce ternary metal diborides, hafnium to form a discrete HfB phase, chromium to provide a metal skeletal phase, (Hf + Si) to form a discrete hafnium silicide phase, and Sic to provide a discrete second phase. Additions to ZrB2 included A1 + B designed to produce a ternary metal diboride, Zr + Si to form a discrete zirconium silicide phase, and Sic to provide a discrete second phase. All the specimens were prepared by high-pressure hot pressing which was used to advantage to fabricate billets of the variety of compositions desired and suitable for oxidation testing. The present investigation also included the evaluation of high-pressure hot-pressed TiB2and TiB2-20 vol pct Sic, conventionally hot-pressed Boride 2,' and KT silicon carbide. Boride

Jan 1, 1969

By D. O. Hobson

Zirconium single crystals of various specific orientations were fabricated by rolling or drawing. The resulting textures were determined and are discussed with respect to the deformation modes that produced them. The crystals deformed in a predictable manner by combinations of up to third-order twinning with three twinning modes and by slip. Twinning was found to play a major role in initial texture formation. Texture changes produced by slip occurred only at the higher reductions. The twinning sequences that produced each intensity peak during the initial reductions could be identified. Schmid factor criteria were found useful in predicting which deformation modes to expect for each crystal orientation and fabrication procedure. The possible application of these data to poly-crystalline material is discussed. PREFERRED orientation or texture has a significant effect on the properties of most materials, causing anisotropy in fabricated cubic metals and enhancing the natural anisotropy of noncubic metals. This study evaluates the effects of several fabrication methods on the textures formed from specific starting orientations of zirconium single crystals and, it is hoped, gives an insight into the effects of the same operations on poly-crystalline material. BACKGROUND In fcc and bcc metals, texture changes take place by gradual lattice rotations caused by the operation of one or more slip systems. Deformation twinning plays an insignificant role in the deformation of such metals. In zirconium and its alloys, however, and in many other hep metals the ability to twin allows very rapid texture changes to be made with very small amounts of deformation. The deformation systems found in zirconium and its alloys are prism slip and three twinning modes.1 Slip occurs on the {1010}< 1120) system. There is little or no appreciable basal slip in zirconium. The twinning planes, illustrated in Fig. 1, are {1012}, {ll2l}, and {1122}. Two twinning modes, the {1012} and the {ll2l} operate for a tensile stress along the basal pole. A compressive stress parallel to the basal pole is required for {ll22} twinning. These twinning operations cause a 35- to 85-deg reorientation of the basal pole. The {1012} twin is the predominant tensile twin at room temperature. The twinning shears, S, are shown in the figure. A criterion for predicting which deformation system will operate when a grain is subjected to a known stress state is the Schmid (orientation) factor. This factor gives the fraction of the applied stress that computer program was written2 to calculate the Schmid factors for the four deformation modes in zirconium. It assumed three orthogonal stress axes and considered ninety-one different orientations of the basal pole in one octant of this stress space. At each basal pole position the Schmid factors were calculated for seven positions of rotation at 10-deg increments of the unit cell about the basal pole. Schmid factors were determined for a total of 637 orientations and for twenty-four deformation systems in each orientation. The program listed the Schmid factors for uniaxial stress parallel to each axis and, to approximate rolling, or-thonormal biaxial stress was also considered. Fig. 2 shows the range of orientations over which the various types of deformation would tend to predominate in biaxial plane strain with the stresses, equal magnitude. The exact boundary position between regions of different deformation modes depends, however, on the relative values of the critical shear stress for each deformation mode. Fig. 2 is drawn on the assumption that they are equal and it therefore may be only approximately correct. It is also recognized that the biaxial stress analysis may not be applicable in certain crystal orientations. EXPERIMENTAL PROCEDURE Single crystals of zone-refined zirconium, produced by Wilson of this Laboratory,3 were electrical-discharge-machined to form specimens for rolling, tube-drawing, and rod-drawing studies. Specimens were rolled at room temperature on 2-|--in.-diam hand-powered rolls from three different starting orientations: 1) the basal plane parallel to the rolling plane and the [1120] in the rolling direction, (0001)[ll20]; 2) the (1120) plane parallel to the rolling plane and the basal pole in the rolling direction, (1120)[0001]; and 3)_the (1120) plane parallel to the rolling plane and the [1100] in the rolling direction, (1120)[ll00]. Drawing specimens were cut with the [0001] direction as the drawing direction in the tube blank and [1120] as the drawing direction in the rod specimen. The drawing

Jan 1, 1969

By Rees D. Rawlings, C. W. A. Newey

The aging characteristics of an Fe-11 at. pct Mo alloy have been studied by means of light metallography together with density, Young&apos;s modulus, and hardness measurements. The results were consistent with the precipitation of a single intermetallic compound during aging; overaging was slow relative to that in other iron-based binary alloys. The solution treatment temperature had a small effect on the rate of hardening whereas deformation prior to aging had a marked effect on both the rate of hardening and the peak hardness. The density data indicate that the compound precipitated is Fe3MO2 and not the Laves phase Fe2Mo. Analysis of the modulus and density results gave values for the time exponent for precipitate growth of approximately 1.0 and 1.5 for the alloy aged with and without prior deformation, respectively. DETAILED studies of precipitation hardening in bcc matrices have been confined largely to the effects of carbides and nitrides. In view of this and the growing technological interest in intermetallic compound strengthening, e.g., in maraging steels, a study of precipitation in iron-based alloys with a low interstitial content has been undertaken. This paper is concerned with the aging behavior of an Fe-11 at. pct Mo alloy; the mechanical behavior of the alloy will be reported later. The early work of sykes on Fe-Mo alloys showed that precipitation of the intermetallic compound was accompanied by an increase in hardness and a decrease in volume of the material. More recent surveys of the strengthening associated with precipitation have been made3-5 and, in particular, Elsen and wassermann4 showed that deformation prior to aging increased the rate of hardening. These latter workers also followed the precipitation process by means of dilatometry, electrical resistivity, and lattice parameter measurements. Their results confirmed that there is a decrease in volume on aging. Except for the work of Hornbogen on an Fe-20 at. pct Mo alloy, neither clustering nor the precipitation of a nonequilibrium phase has been observed in Fe-Mo alloys. Studies of alloys of lower molybdenum content475 indicate that the equilibrium intermetallic compound is precipitated during aging. However, there is some doubt concerning the nature of the equilibrium precipitate phase. According to the phase diagram constructed by Hansen,8 the phase should be precipitated. This phase has a rhombohedra1 crystal structure which is characterized by the formula Fe706,&apos; although the composition of the molybdenum-rich boundary corresponds approximately to Fe3Mo2. The version of the diagram proposed by Sinha, Buckley, and Hume-Rother indicates that the A phase, a Laves phase Fe2Mo, should be precipitated. Their observation of a Laves phase supports the earlier findings of Bechtoldt and Vacher,13 although, in a recent study of the system by means of diffusion couples, Rawlings and Newey did not detect the phase. The work presented here describes the effect of solution-treatment temperature, aging temperature, and prior deformation on the aging characteristics of the alloy as revealed by light metallography together with hardness, density, and Young&apos;s modulus measurements. In addition the density data are used in an attempt to determine the compound precipitated during aging. EXPERIMENTAL PROCEDURE A 29-kg ingot of the alloy was cast at R.A.R.D.E., Fort Halstead, from deoxidized, Japanese electrolytic iron and sintered molybdenum. The ingot was homogenized for 6 hr at 1473°K and then worked, with intermediate anneals, into 6- and 16-mm-diam rods and 6-mm plate. Chemical analysis of the alloy gave, wt pct: Mo, 17.5 (11 at. pct); C, 0.003; Si, 0.002; S, 0.005; P, <0.002; and02, 0.0098. Solution treatments were carried out under a dynamic argon atmosphere in a vertical, "crusilite" element, furnace which had a facility for rapid quenching into iced water. Except for the study of the effect of solution treatment temperature, all specimens were solution-treated at 1573" * 2°K for 1 hr. Salt baths were used for the aging treatments. Specimens for hardness, density, and Young&apos;s modulus measurements were produced, after heat treatment, from the stock rod or bar using a precision silicon carbide slitting wheel. As described later, the quenching treatment produced local plastic strain in the stock material; consequently, care was taken to ensure that the specimens were not prepared from these regions. Those specimens used in the studies of the effects of prior deformation on the aging behavior were strained in compression in a Denison universal testing machine. Specimens for light metallographic observations were mechanically polished on successively finer grades of diamond paste down to and then etched in either alcoholic ferric chloride or in a 2 pct nital solution. Vickers diamond pyramid hardness data were obtained using a 30-kg load. At least five impressions were averaged for each determination. Density measurements were made using a displacement technique in which each specimen was weighed in air and in dibromoethane at 296°K. The specimens were cylindrical and weighed 3 to 4 g; all weighings were made on a balance reading to 1 x 10"5 g. For each specimen the mean value of five weighings was used to calculate the density. The density of the dibromoethane was determined using the displacement procedure and a standard nickel specimen. The error in an absolute density value was estimated to be HI.01 pct. To obtain the density as a function of aging time a single specimen was used and the density meas-

Jan 1, 1969

By John C. Gifford, Charles L. Thomas

A unique and reproducible method is presented for the determination of water vapor in tough pitch wire bar copper. The procedure involves reduction of the water vapor with molten aluminum to form hydrogen, which is subsequently measured by mass spectroscopy. Average water vapor pressures within the porosities of the wire bar samples are calculated. Correlation is to exist between the specific gravities of the samples and their measured water vapor contents. The method should find application as a very sensitive means of detecting hydrogen embrittlement in copper. The nature and quantity of gases evolved and retained during the horizontal casting of tough pitch wire bar copper have long been of interest to the metallurgist. Considerable work has been done at this laboratory on the determination of these gases. The work has involved not only qualitative but also quantitative analysis, so as to provide a basis for a total accounting of the porosity which is associated with the cast product. From a knowledge of the gas-forming elements within the copper, and the practice of melting and protecting it with a reducing flame followed by contact with a charcoal cover in the casting ladle, the gases which one might expect to find in the pores of the cast product are sulfur dioxide, carbon monoxide, carbon dioxide, hydrogen, and water vapor. Hydrogen sulfide, nitrogen, and hydrocarbons would be other possibilities; however vacuum fusion-mass spectroscopy techniques employed at this laboratory have shown that no hydrogen sulfide and only traces of nitrogen and methane are present. It is highly improbable according to phillipsl that any sulfur dioxide could be evolved in wire bar copper with 10 ppm or less sulfur under normal freezing conditions. Mackay and smith2 have noted that porosity due to sulfur dioxide only becomes noticeable at concentrations above 20 ppm S. Investigation of carbon monoxide and carbon dioxide by a variation in the method of Bever and Floe showed that these two gases could only account, at 760 mm and 1064°C (Cu-Cua eutectic temperature), for a maximum of about 25 pct of the total porosity in a wire bar having a specific gravity of 8.40 g per cu cm. phillips&apos; has noted that no normal furnace atmosphere is ever sufficiently rich in hydrogen to cause porosity in copper from hydrogen alone. In addition, using a hot vacuum extraction technique for hydrogen,4 values have never been observed in excess of 10 ppb in tough pitch wire bar. On the basis of the preceding considerations of gases in tough pitch wire bar, only water vapor is left to account for the major portion of the porosity. Direct determinations of water vapor are virtually impossible at low concentrations by any presently known technique, due to adsorption and desorption within the walls of the apparatus used.5 The present investigation deals with a method for the determination of water vapor by an indirect procedure, using molten aluminum as a reducing agent to form hydrogen according to the reaction: 2A1 + 3H2O — A12O3 + 3H2 The evolved hydrogen can then be measured quantitatively by mass spectroscopy. EXPERIMENTAL A 10-g piece of 99.9+ pct A1 was charged into a porous alumina crucible (Laboratory Equipment Co., No. 528-30). Fig. 1 shows the crucible in place at the bottom of an 8-in.-long quartz thimble. A funnel tube with two l1/8-in.-OD sidearms extending at a 90-deg angle from each other was attached to the top of the thimble. One of the sidearms was joined to the inlet system of the mass spectrometer (Consolidated Electrodynamics Corp. Model 21-620A) via a mercury diffusion pump situated between two dry-ice traps. The copper samples were placed in the other sidearm, followed by a glass-enclosed magnetic stirring bar for pushing the samples into the crucible. All ground joints were sealed with vacuum-grade wax. The entire system was evacuated and the aluminum was heated with a T-2.5 Lepel High Frequency Induction Furnace for 21/2 hr at a temperature visually estimated to be 900°C. The temperature was then lowered and the hydrogen was monitored on the mass spectrometer until it was given off at a constant rate of about 4 to 5 1 per hr. This rate corresponded to a slope of 2 to 3 divisions per min on the X3 attenuation of a 10-mv recorder at a hydrogen sensitivity of approximately 100 divisions per 1. A micromanometer (Consolidated Electrodynamics Corp. Model 23-105)

Jan 1, 1969

By J. Szekely, Robert G. Lee

Calculations are presented for the prediction of the combined radiative-convective heat loss from molten steel held in a ladle, covered by initially molten slag. A mathematical formulation is given and numerical solutions are presented of the resultant partial differential equation. It is shown that a slag layer of about 2 to 3 in. thick would prevent any significant heat loss from the top metal surface for Periods of up to 1 hr. For thinner slag layers (or in the absence of the protective slag) appreciable heat losses would occur; plots given in the paper allow the quantitative evaluation of the fall in the metal temperature due to this heat loss. The ironmaking-steel processing operation involves several intermediate steps where the molten metal is held or transfered in ladles. The quantitative assessment of the heat losses occurring under these conditions is of considerable importance in process design considerations since the temperature of the metal may have to meet rigid specifications in any given part of the processing sequence. While the metal is held in a ladle, heat is lost by two mechanisms: i) by conduction into the ladle walls; ii) by radiation and convection from the top surface. Calculations relating to the conductive heat loss, are readily made and information may be found in the literature both on data pertaining to metallurgical situations and on the techniques that are available for performing additional computations.&apos;-3 The evaluation of the combined convective-radiative heat loss is less straightforward, especially when there exists a protective slag layer covering the metal. In this latter case, as the top slag surface loses heat partial solidification may occur and the latent heat thus given up by the slag may represent an effective barrier to the heat loss from the metal. A semiquantitative assessment of the role played by the slag in preventing heat loss from the metal has been made in a previous paper,4 where it was shown that a slag layer 6 in. thick would act as a near-perfect insulator for periods of up to 2 hr. However, this first paper reported on an essentially preliminary investigation that considered only one slag layer thickness; furthermore, the boundary conditions used for the calculations were somewhat restrictive since no allowance was made for changes in the metal temperature. The purpose of this second paper is to extend the scope of the preliminary investigation previously reported by: i) considering several slag layer thicknesses; ii) allowing for variations in the metal temperature; and finally iii) by performing calculations on the net loss from the metal rather than from the slag surface. FORMULATION Consider a slag phase extending from y = 0 to y = L1, covering a metal phase that occupies the region extending from y = Ll to y = L, as illustrated in Fig. 1. Denote the slag and metal temperatures by TS and Tm and assume that initially both slag and metal are molten, having a uniform temperature Ti. At time = zero the surface represented by the y = 0 plane (top slag surface) is brought into contact with cold air, the temperature of which is given as T Thus for time > zero, heat will be transfered from the slag to the air by natural convection and thermal radiation; as a result of this heat loss the slag temperature will fall and after some time a solid phase is formed and a solidification boundary (more realistically described as a zone) will move progressively from y = 0 toward y = L1. Once the region of temperature gradients, moving ahead of the solidification zone, reach the slag-metal interface (y = L1) there will be a net transfer of heat from the metal through the slag to the cold air, across the y = 0 plane. In the formulation of moving boundary problems, involving phase changes that require computer solution, it is convenient to represent both phases by a single equation, making allowance for the latent heat of solidification by assigning an appropriate temperature dependence to the specific heat content. Thus the energy equation for the whole of the slag may be written as follows:

Jan 1, 1969

By J. D. Hunt, D. T. J. Hurle

A uariety of eutectic structures are formed in faceted/nonfaceted eutectics. The various structures are explained in terms of the absence or presence of small facets in the liquid groove. Regular structures are produced when, for purely geometric reasons facels cannot form. The presence of a facet in the liquid groove leads to the formation of an irregular or a cell-like complex regular structure, due to the relative immobility of the groove. A classification of eutectics was proposed by Hunt and jackson, based on the presence or absence of facets on the primary phases (the absence of facets may be predicted from the dimensionless entropy of melting2). Eutectics were divided into three groups: 1) eutectics in which both phases grow in a nonfaceted manner; 2) eutectics in which one phase grows faceted, the other nonfaceted; 3) eutectics in which both phases grow faceted. It was suggested that regular1 rodlike or lamellar structures1 should be formed in the first group, that irregular or complex regular structures1 should be formed in the&apos; second, and that irregular structures1 should be formed in the third. Recently it has been shown that the structural classification is incomplete. Regular rodlike structures (InSb-NiSb eutectic3), or broken lamellar structure (Bi-Zn eutectic, Fig. 8), are formed in alloys of the second group when the faceted phase has a large volume fraction. Hunt and jackson&apos; argued that regular structures could form in faceted/nonfaceted systems, but that such structures would be unstable in the presence of microfacets on the lamella of the faceting phase, because the growth rate at a point on such a facet would depend on the kinetic undercooling at the point of nu-cleation on the facet, and not on the local kinetic undercooling. In these circumstances it would not be possible to consistently balance the compositional and kinetic undercooling over a lamellar structure and thus obtain a stable isothermal interface. In this paper we discuss in detail the origin of the various structures formed in faceted/nonfaceted systems, pointing out that the most important factor promoting the formation of a regular structure is the absence of a facet in the liquid groove. 1) FACET FORMATION IN SINGLE-PHASE MATERIALS Facets form when there is an energy barrier for the addition of a new solid layer on an existing solid. When a barrier is present,2 growth proceeds by the lateral movement of steps across a crystallographic plane. The rate-controlling stage of the process occurs when the step is first formed. Hulme and Mullin6 have shown that faceting in single-phase materials can only occur when both interface curvatures are convex with respect to the solid and when the surface is tangential to the facet plane. When even one of the curvatures is concave a facet does not form because new layers of solid from adjacent regions can always feed the facet plane, Fig. 1. Growth under these conditions is then as easy as elsewhere. Similar considerations will apply to eutectic growth; consequently the shape of the faceted phase is extremely important. 2) LAMELLAR SPACING CHANGES IN EUTECTICS Jackson and Hunt7 have shown that the interface undercooling AT of a growing lamellar interface (neglecting kinetic undercooling) is related to the lamellar spacing, A, and growth velocity, v, by an expression of the form: where m, Ql, and nL are constants of the system given in Ref. 7. Eq. [I] is plotted for fixed v in Fig. 2. Jackson and Hunt postulate that a regular eutectic grows near, but to the right of the minimum in the AT vs A curve. They argue that the spacing cannot be to the left of the minimum because the interface is then unstable to fluctuations in A. It cannot grow too far to the right, because when the spacing becomes too wide an isothermal interface can no longer be maintained over the large-volume-fraction phase.7 It is argued that during any change in growth rate the lamellar spacing remains in the permitted range by the movement of lamellar faults. When the spacing is too wide, the fault, shown in Fig. 3, moves to the left; when the spacing is too narrow it moves to the right. The faults, however, have to be formed. heir formation has been shown to occur when local regions deviate considerably from the spacing defined by the lamellar When the spacing is locally too narrow (it passes to the left of the minimum, Fig. 2), pinching off of the narrow phase occurs. When the spacing is locally too wide, the interface on the large volume-fraction phase can no longer be maintained as an iso-

Jan 1, 1969

By M. G. Benz

The superconducting performmce of diffusion-processed Nb3Sn is influenced by its micro structure. High isotropic transverse current density may be achieved in this material by a process which forms a precipitate of ZrO, within the Nb3Sn. FOR an ideal type-I1 superconductor, little or no transport current can be carried in the mixed state; i.e., little or no transport current can be carried above the lower critical field H,,, where the field penetrates abruptly in the form of current vortices or fluxoids, even though full transition to the normal state does not occur until the upper critical field H,,.&apos; Fortunately, nonideal type-I1 superconductors can be readily obtained and these carry large transport currents up to the upper critical field H. Both theoretical and experimental investigations have attributed this current-carrying capability for nonideal type-I1 superconductors to pinning of the fluxoid lattice by heterogeneities in the microstructure of the superconducting material. These heterogeneities may take the form of dislocations or dislocation clusters,2"5 grain boundaries: structural imperfections introduced by phase transformations; radiation damage,8"10 or precipitates.11"15 Nb3Sn formed by diffusion processing is a type-I1 superconductor. Heterogeneities are needed for high superconducting critical currents above H,,. This paper will cover: a) what the microstructure of diffusion-processed NbSn looks like; b) what changes in the microstructure take place when the system is doped with precipitates, and c) how these changes in microstructure influence the superconducting critical currents. EXPERIMENTAL Preparation of Samples. Diffusion processing was used to form the Nb3Sn. The procedure used was as follows: a) coat the surface of a niobium tape with tin; b) heat-treat this tape at a temperature above 930°C to form a layer of Nb3Sn at the Sn-Nb interface. Such a layer of NbsSn is shown in Fig. 1 The thickness of the NbsSn layer formed was controlled by the time and temperature of the heat treatment. The same general procedure was used for preparation of both undoped samples and samples doped with a precipitate. An additional step was included in the preparation of the doped samples which consisted of internal oxidation of zirconium to form ZrOn. The details of the doping process will be reported in a later paper. Sample Testing. The Nb3Sn tape samples were soldered to a copper or brass shunt. Current and voltage leads were then attached to the sample in the usual four-probe resistance measurement configuration. The sample was cooled to 42°K. In some cases it was cooled in the presence of a high magnetic field and in other cases with the field turned off. The results were the same for both cases. The samples were oriented in a configuration with field transverse to current but could be rotated such that the angle between the field vector and the wide side of the tape sample could be changed. Measurements up to 100 kG were done in a superconducting solenoid and measurements above 100 kG in a water-cooled copper magnet at the MIT National Magnet Laboratory. Once the test field was reached, the current in the sample was increased until voltage was detected across the sample. The critical current was taken as the current at which voltage was first detected in excess of background noise. In most cases this was 1 to 2 x 10~6 v for a— in.-wide sample carrying several hundred amperes with a in. separation between voltage leads and with a 10 "-ohm shunt resistance. RESULTS AND DISCUSSION Microstructure. Examination of the microstructure of the undoped Nb3Sn shows rather large-diameter (1 to 2 columnar grains growing outward from the niobium surface toward the tin surface. As the layer is made thicker by longer diffusion times, these grains grow longer. Few new grains are started. Transmission electron microscopy shows little or no second-phase material within the bulk of the Nb3Sn layer. The microstructure of a diffusion-processed NbsSn layer changes quite drastically when the system is doped so as to form a precipitate within the NbsSn layer. Instead of large-diameter columnar grains of NbaSn forming, smaller-diameter (0.5 to 1 ) equiaxed grains of Nb3Sn decorated with the precipitate form. Fig. 2 shows a transmission electron micrograph of a Nb3Sn layer doped with zirconium oxide. This layer has been etched so that one may look between the grains

Jan 1, 1969

By P. Chiotti, J. T. Mason

Thermal, X-ray, metallographic, and resistivity data were obtained to establish the phase diagram for the Yb-Zn system. Six intermetallic compounds and five eutectics have been identified. The compounds position at 695°C. No evidence for the compound YbZn,, was observed. Whether this compound is stabilized or inhibited by small amounts of impurities is uncertain. SEVERAL aspects of the Yb-Zn system have been reported in the literature. Much of this work deals with the crystallographic identification of some of the compounds. The YbZn compound has been reported by Iandelli and palenzonal and the YbZn, structure and thermal data for the composition range between YbZn and Yb3Znll have been reported by Michel et al. A compound of uncertain stoichiometry in the range 60 to 68 wt pct Zn with a cubic structure has been reported by Kuz&apos;ma et aL4 The YbzZn17, YbZn,,, and YbZn13 compounds have been reported by both Kuz&apos;ma et a1 and Iandelli and Palenzona.&apos; YbnZn17 has also been identified by Laube. This investigation was undertaken to establish the phase diagram of this system. Ytterbium in many respects behaves as an alkaline earth rather than a rare earth metal6 and it is of interest to note the resemblance between the Yb-Zn system, the Ca-Zn,&apos; and typical rare earth-zinc systems.g&apos;10 MATERIALS AND EXPERIMENTAL PROCEDURES The materials used in this investigation were Ames Laboratory ytterbium and Bunker-Hill slab zinc, 99.99 pct pure. Analyses of the ytterbium showed 38 ppm Ta, 82 ppm 0, and 15 ppm N with Ca, Cu, C, Mg, Al, Si, Cr, Fe, Ni, Sc, Y, Er, Tm, and Lu all less than 50 ppm. The ytterbium was dehydrogenated by heating in tantalum under vacuum for 8 hr at 900°C. The metal was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys in the composition range between ytterbium and Yb2Zn17. With higher zinc concentrations the tantalum was penetrated by the alloy and failed after several days at temperatures of 600" to 700°C. Approximately 20 g of zinc and ytterbium metal were sealed under argon in *-in.-diam tantalum cruci- bles equipped with thermocouple wells. The crucibles were in turn sealed in stainless-steel jackets. The alloys were equilibrated in an oscillating furnace and given various heat treatments in a soaking furnace. The steel jackets were removed and differential thermal analysis data were obtained under an atmosphere of argon. The thermal analysis apparatus was calibrated against the melting points of pure zinc, aluminum, silver, and copper and found to give thermal arrests within 1°C of the accepted melting temperatures for these elements. The thermal analysis apparatus has been described in an earlier paper.g Alloys were further heat-treated as necessary and subjected to metallographic examination and X-ray diffraction analysis. Most alloys were etched with Nital (0.5 to 10 pct nitric acid in alcohol). EXPERIMENTAL RESULTS The results of the thermal analysis are summarized by the points on the phase diagram, Fig. 1. Six compounds and five eutectics were observed. The eutectic temperature and compositions in weight percent zinc are 491°C and 12 pct, 645°C and 32 pct, 687°C and 54 pct, 742°C and 67 pct, and 750°C and 77 pct. The compounds YbZn, YbZn2, Yb2Zng, Yb2Zn17, and YbZnll melt congruently at 650°, 751°, 75Z°, 754", and 755"C, respectively. The compound Yb3Znll undergoes a peritectic decomposition at 695°C. The transformation and melting temperatures for the ytterbium were observed to be 797" and 817°C. re-

Jan 1, 1969

By M. J. Duggin

Structural similarities between the E, X, and iron carbides are illustrated. Experimental evidence regarding phase transformations occurring during ternpering reactions in finely divided carbides, thin-film carbides, and carbides which occur in steels is considered and possible mechanisms for the E — x and x — 9 transformations proposed. HOFER1 has shown that within the appropriate temperature ranges carbon monoxide will react with finely divided a iron to form either iron carbide or x iron carbide. He has shown that at an elevated temperature the E iron carbide will transform to the x iron carbide (Hagg carbide) which, upon further elevation of temperature, will transform to 9 iron carbide (cementite). Jack,2,3 using X-ray diffraction methods, has observed that during the tempering reactions occurring in steel the E iron carbide formed in the first stage of tempering passes into two-dimensional platelets of 0 iron carbide during the second stage of tempering. The three-dimensional form of the 0 carbide is formed during the third stage of tempering. Jack suggested2 that the two-dimensional platelets of 0 carbide could be related to the faulted x iron carbide. Okada and Arata4 investigated a Swedish steel containing 1.05 wt pct C and approximately 1.0 wt pct Mn using permeability measurements at low field strength. A Curie point of 360°C was observed in the quenched steel, which indicated the presence of E iron carbide. On tempering at 400°C the specimen developed a Curie point at 230°C, indicating the presence of x iron carbide, and on tempering at 700°C the specimen developed a Curie point at 190°C which was assigned to 0 iron carbide. The carbides were extracted electro-lytically and the use of X-ray diffraction techniques4r5 indicated the carbide with a Curie point of 230°C to be x iron carbide. The Curie points of the carbides are 10 to 22°C lower than the accepted values which is probably due to the presence of manganese in the carbides, since it has often been observed (e.g., Ref, 6) that a partial substitution of manganese for iron in cementite will lower the Curie point of this carbide. Hofer&apos; summarizes additional evidence of the tempering reactions in steel in which E iron carbide, formed during the first stage of tempering, transforms to x iron carbide during the second stage of tempering. During the third stage of tempering, the x carbide disappears as the 0 carbide is formed. By carburizing thin iron films in a CO gas stream, ~a~akura&apos; has been able to produce the E, X, and 0 iron carbides. He found that below 250°C the E iron carbide was formed; between 250" and 350°C the x iron carbide was formed and above 350°C the 0 iron carbide was formed. He has shown that the E iron carbide transforms to form x iron carbide at 380" to 400°C and that the x ir°n carbide transforms to form the 0 iron carbide at approximately 550" C; both of these phase transformations are irreversible. Hofer&apos; presents a review of evidence to show that the sequence of reactions occurring during tempering processes subsequent to the formation of E iron carbide formed by the direct carburization of finely divided a iron is the same as the sequence of reactions which occur during the tempering processes subsequent to the formation of E iron carbide in steel during the first stage of tempering. It is evident from Nagakura&apos;s work that identical tempering reactions are found in thin films of iron which have been carburized to form iron carbide. The purpose of this paper is to discuss the structural similarities between the E, X, and 0 carbides and to suggest a possible mechanism by which regions of the E carbide, formed during the first stage of tempering, may transform to the x carbide during the second stage of tempering. For the finely divided or thin film carbides a mechanism will be proposed for the transformation of the x carbide to the 0 carbide during the third stage of tempering, although it will be suggested that there is evidence that such a transformation may not occur in steels. STRUCTURAL DATA OF THE E, X, AND 0 IRON CARBIDES € Iron Carbide. It is evident from X-ray diffractions and electron diffraction&apos;, investigations that the metal atoms in the E iron carbide form an hcp structure with lattice constants ah = 2.752A, ch = 4.3534, using electron diffraction, reports the lattice paramet$rs of the superlattice cell to be a = 4.767A, c = 4.354, c/a = 0.9134. He finds that the carbon atoms occupy the octahedral voids in the metal atom structure so as to form a hexagonal stacking sequence with its basal plane parallel to that of the metal atoms. Considerable long-range disorder occurs in the positioning of the carbon atoms, however, which is in agreement with the possible range of composition Fe2C-Fe3C discussed by Hofer.&apos; Barton and ale" have made X-ray diffraction measurements on a sample of E iron carbide extracted from a catalyst in an organic process. Although there were few reflections recorded on the obtained X-ray powder diffraction pattern, they have proposed that the structure could belong to one of the three possible space groups p3m1, P63/mmc, or Pbcn if one assumed the composition to be Fe2C. Nagakura, using electron diffraction data, suggests a space group of P 6322 for a specimen of c iron carbide of apparent composition Fez.&. x Iron Carbide. The x iron carbide has been studied by Duggin and Hofer" and by Jack and wild,&apos; who

Jan 1, 1969