Search Documents

By R. L. Moment

The anisotropic elastic behavior of rolled beryllium sheet has been measured, using a pulse echo technique, and compared with X-ray diffraction data. Calculated elastic stiffness constants compared favorably with published values for beryllium single crystals which were attributed to the strong (0002) rolling plane texture. Variations of Young's modulus in the yolling plane could be associated with the velative distribution of (0002) planes out of their ideal position in the rollitzg pkule. WHEN a metal is subjected to cold working such as drawing, forming, or rolling, a crystallographic texture develops which can significantly alter its physical properties. One method for detecting this texture is X-ray diffraction, but Alers and Liu' have recently pointed out how the prediction of anisotropic physical properties from pole figures alone is not always accurate due to differences in interpretation. Variations in Young's modulus with orientation or, more completely, the values of the effective elastic constants of the worked metal, also serve to indicate the presence of a texture. In fact, as Alers and Liu' pointed out, calculated variations in Young's modulus for assumed orientations, when compared with experimental data, can be used to eliminate some of the uncertainty in interpretation of X-ray pole figures. Thus, elasticity measurements can serve not only to clarify any unusual elastic behavior of worked metal, but also to detect and in part determine the nature of its texture. X-ray determination of the texture of rolled beryllium has been reported by Smigelskas and Barrett,2 who found a strong texture of (0002) in the rolling plane with (1070) planes normal to the rolling direction. In the case of metal rolled at room temperature, they reported that [1010] directions also appeared at positions 60 and 120 deg from the rolling direction in the rolling plane, while in more recent work Keeler3 found these directions were also tilted towards the rolling plane. The texture for beryllium rolled at 80O0C, however, only showed (1010) planes normal to the rolling direction and the spread of (0002) planes out of the rolling plane was less. In looking for elastic anisotropy one might consider unidirectional rolling of a metal as introducing an or-thorhombic symmetry through reorientation of the grains, since the three deformations, compression, extension in the rolling direction, and extension in the cross direction, are orthogonal to each other and unequal in magnitude. Thus the rolled sheet could be treated like an orthorhombic single crystal and the nine stiffness constants of the elasticity tensor used to calculate the anisotropy of Young's modulus, the shear modulus and Poisson's ratio. In this case we could write: which is symmetric about its diagonal. Borik and Alers4 have recently used this approach on rolled die steel with very good results. They found, however, that instead of displaying orthorhombic elastic symmetry their specimens could be considered tetragonal in which case Cr1 = c22, c13 = Ca, and c44 =cjj. This conclusion was made solely on the basis of the measured tensor elements, and serves to point out the advantage of this method for studying the anisotropy of rolled metals. Their calculated values for Young's modulus as a function of angle in the rolling plane also checked very well with direct measurements made on different specimens using the resonance technique. In the present study, cross-rolled beryllium was used which had been unidirectionally rolled about 11 pct for the final reduction. This imparted a slight anisotropy in the rolling plane which was detected both by X-ray techniques and elasticity measurements. For purposes of discussion in this paper, the rolling direction is that direction in which the most reduction passes were made and cross direction is the normal to the rolling direction in the rolling plane. It was also decided to consider the rolled sheet as displaying orthorhombic symmetry for the purpose of obtaining elasticity samples with the direction defined as in Table I. Any change in the final symmetry attributed to the sheet would then be made on the basis of the measured elastic stiffnesses. The final data would then be compared with that expected from the X-ray study and that reported for beryllium single crystals. EXPERIMENTAL PROCEDURE Rolling Schedule. The samples used in this study were taken from a large sheet which, because of its size, had to be unidirectionally rolled for the final reduction. The resulting texture was that of cross-rolled metal with a slight unidirectional texture superimposed. A cast beryllium ingot, 9.500 in. sq by 3.325 in. thick, was cross-rolled to 81 pct reduction followed by unidirectional rolling for an additional 11 pct to give a total reduction of 92 pct. The thickness of the final sheet ranged from 0.265 to 0.280 in. Reduction up to 67 pct was done at 980°C and the final 25 pct at 870°C. Analysis for metallic impurities showed aluminum 0.06 pct, iron 0.19 pct, and silicon 0.11 pct, giving a beryllium purity of 99.64 pct.

Jan 1, 1968

By John F. Elliott, John P. Hager

The standard free energies of formation of the lowest stable sulfides of chromium, molybdenum, and tungsten in equilibrium with the corresponding metal hazle been determined by reacting the sulfide and metal with H2(g)/H2S(g) mixtures. The reaction is A method for estimating the standard ~nolav entropies and standard entropies of formation at 298°K of the sul-fides of refractory metals is presented. The standard free energies of formation of the lowest sulfides of the metals in group VIa of the periodic table are probably best determined with the reaction* is known with greater accuracy than is that property for any other sulfur-bearing compound or solution which might serve as a reference phase to establish the chemical potential of sulfur for the essential re- However, there still remain significant problems to the use of Reaction [I] in studying these sulfides. First, the equilibrium gas ratios (Ph2S/PH2) are very small, and with the most stable sulfides in the series the ratios tend to be at the limit of the range for precise chemical analysis (10-4); and second, the reaction rate for the formation or reduction of these sulfides appears to be relatively slow. A primary reason for the latter problem is that the gas phase near the equilibrium concentration has very little capacity for transport of sulfur. It is to be noted that the thermo-dynamic properties obtained from the experimental results by Eq. [I] apply for 1 g-atom of sulfur in the metal-saturated compound even though the exact composition of the compound has not been determined. The work reported here is a study of the standard free energies of formation of the lowest sulfides of chromium, molybdenum, and tungsten, and of copper, by Reaction [I]. In planning the experimental program, it was decided that the technique that has been used previously3"' could be used with modification and that an improved analytical method was needed for determining H2S in the gas phase. THE EXPERIMENT The once-through flow of gas was selected in preference to recirculating the gas, a) because of the low sulfur capacity of the gas, b) because of the relatively slow rate of reaction and the danger of the

Jan 1, 1968

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.' Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,' and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-' per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By J. H. Bucher

The effect oj strengthening by the precipitation of CbC on the toughness offerrilic steel (0.11 pct C, 0.74 pct Mn, 0.02 pct Cb) was stlrdierl. A g-veater degree of pvecij~itatiotz strengthning is ohtaznable by aging the so11ution-treated steel rtt velaticely Low temperature was (1050" to 1l0O3F) than at higher temperatures (I150" to 1200°F). Tlzis ),eslrlts because a finer dispersion of CbC is obtained. However, the ductile-brittle transition te~ripertltlo.e is raised approximately tlzjeee tirues as IFLIIC~ perv a given yield stress increase) by aging in the lower tempareture range, as opposer1 to the Irigher temperaturee range. This is proposed to result pl-iir~avily because different precipitation distributions ar-e associated with the different aging -treaments. For tile steel aged at 1050" and 1100 F, heavy: precipitation on disloccctions occurs resulting in a high degree of rlislocution pinningh tl~us lowevirzg- the toilguiess. in tll c(.rise of the steel aged at 1150 'a?zd 1300"F, Pvecipitatiol~ is irzove g-enerally distributed throughout the matrix rather limn preferentially on dislocations.; and Ike detlsitj, oj mobile dislocations is not sttyong-ly affected. THE most effective means of strengthening hot-rolled ferritic steels are grain refinement and precipitation hardening. It is well-known that grain refinement increases both the strength and the toughness. However, the upper limit of yield strength obtainable by grain refinement alone is about 60,000 psi,'12 i.e., without the formation of acicular structures of lower toughness. The most economical means of obtaining higher strengths is the addition of small amounts of elements such as columbium, vanadium, and titanium which form carbonitrides. These precipitates are very effective in increasing the strength, but the ductile-brittle transition temperature is is Although it is agreed upon that precipitation decreases the toughness, there has been little effort to isolate the causative aspects of embrittlement. The purposes of this research are to assess quantitatively the embrittlement associated with different precipitate distributions and morphologies, and to correlate the degree of the embrittlement with the microstruc-ture. In this manner, a more fundamental insight into the mechanism of embrittlement may be gained. The steel selected for this purpose was a low-carbon, columbium-bearing steel which, after solution treatment, was aged in various time-temperature cycles while attempting to hold all other microstructural variables constant. MATERIALS AND PROCEDURE The composition of the steel used in this investigation is given in Table I. Starting with commercially hot-rolled material 0.074 and 0.280 in. thick, tensile blanks were cut from the thinner material and sub-size Charpy blanks from the thicker stock. The steel had been rolled using a low finishing temperature and rapid cooling after hot rolling to produce grain refinement. Also, chemical-extraction analysis and electron-microscopic examination revealed that the cooling was rapid enough to suppress any significant precipitation of CbC. Therefore, the as-rolled steel is essentially in the solution-treated condition in terms of the precipitation reaction, and it was used as the base material in this investigation. The room-temperature tensile properties of the as-rolled steel aged at 1100", 1150", and 1200°F for various time intervals were determined, see Table 11. The ductile-brittle transition behavior was studied for smooth and notched tensile specimens, and longitudinal half-size (0.200 in. thick) Charpy V notch specimens aged at 1100" and 1150°F for various times, also Table 11. In addition, tensile specimens aged for single times at 1050" and 1200°F were evaluated with respect to their ductile-brittle transition. Only one 1050°F treatment was used because of the extremely slow kinetics of precipitation at this temperature and because no significant difference between 1100°F aging was observed. Only one treatment at 1200°F was used because aging at this temperature alters the shape of the grain boundary cementite particles present in this steel and complicates analysis. The design of the tensile specimens is given in Fig.1.

Jan 1, 1968

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of- liquid Mg-Pb allojs have been determined by an isopiestic method from 18 to 42 at. pct Pb and by a thevmodynumic analysis of the phase diagram frofiz 0 to 100 at. pct Pb. In the overlapping composition range the magneszupn activity values derived by the two methods are in excellent agreement, thus mutually supporting the correctness of the Mg-Pb phase diagram previously determined by the authors and of the acticitzes deriz~ed isopiestically. SEVERAL studies have been made of the thermody-namic properties of liquid Mg-Pb alloys. Wagner and Engelhardt,1 Lantratov,2 Knappwost,3 Sryvalin et al.* and Wilson5 used the electromotive-force method, Scheil and Wolf8 and Schmahl and Sieben" applied the transpiration technique, and the present authors8 utilized the phase diagram to determine the activity of magnesium in the Mg-Pb system. The results of these studies are not in very good agreement and could not be incorporated into a general systematic analysis of the thermodynamic properties of the homologous series of the Mg-Group IV B systems Mg-Pb,8 Mg-Sn,° Mg-Ge,10and Mg-Si.11 The thermodynamic properties of the Mg-Pb system were therefore re investigated by an isopiestic technique which has been developed for similar studies in the Mg-SnB and Mg-Ge10 systems- Lead specimens, contained in iron or graphite crucibles, were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure to form alloys of compositions which depended on their temperatures, the temperature of the magnesium vapor source, and the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE Magnesium (Dominion Magnesium Ltd., Toronto, Canada) of 99.99+ pct purity and lead (American Smelting and Refining Co.) of 99.999 pct purity were used. In the early experiments, Runs 2 and 3, the alloys were contained in uncovered high-purity iron crucibles. Alloys formed in the uncovered iron crucibles had to be chemically analyzed owing to the slight volatility of lead under the imposed experimental equilibration conditions. The compositions of these alloys were determined by a gravimetric analysis of lead as lead chromate. To avoid this problem, the remaining runs were made in covered graphite crucibles machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non- i reactivity of graphite with lead and magnesium has been previously established,' and the experimental procedure has been described in full detail.' In the runs using covered graphite crucibles it was found that the weight increases of the crucibles and their contents after equilibration equaled the magnesium contents of the alloys within the accuracy of the chemical analysis (i0.3 at. pct Pb). Clearly, the small lid openings of the graphite crucibles prevented significant lead losses during a run, and the weight increase was therefore taken as the magnesium content of the alloys. EXPERIMENTAL RESULTS At thermodynamic equilibrium the magnesium partial pressure of the specimens equaled that of the reservoir. Since the magnesium reservoir was always maintained at the temperature minimum of the system, the activity of magnesium of any specimen was given by the ratio of the magnesium reservoir pressure to the vapor pressure of pure magnesium at the specimen temperature. The standard state was chosen as liquid magnesium and the vapor pressure of liquid magnesium

Jan 1, 1968

By P. Chiotti, R. J. Hecht

Vapov pressure data of solid and liquid alloys along with phase diagram data WERE employed in calculating the thermodynamic properties for the Ca-Zn system. The relative excess partial molal free energy for zinc in the liquid alloys was fitted to the relation wnvre i is we tvmpvrutiirc in ucgrees neivtu ana in is the tr~ole fvaction. Relations for the standard free energy of fortnation for the eight cornpounds were developed. ThE phase diagram for the Ca-Zn system as determined by Messing et a1.' is reproduced in Fig. 1. Earlier work on the phase diagram has been summarized by Hansen and Anderko2 and the very limited thermodynamic information for this system has been reviewed by Hultgren et a1.3 The heat of fusion for the compound CaZn2 has recently been determined to be 9260 cal per mole.4 Solubility data for calcium in zinc for the temperature range of 650" to 725°C were fitted by the relation and reported by Johnson and Dilloon5 In the present investigation zinc vapor pressure data were obtained by both the dewpoint and Knudsen methods in order to calculate the thermodynamic properties for liquid and solid alloys. The dewpoint method as employed in this work requires that only one of the components be significantly volatile, in this case zinc, and that the vapor pressure of pure zinc be known. For calculation purposes the vapor pressure data for pure zinc3 were fitted to the relations; for temperatures below 692.7K, the melting point of zinc. The corresponding free-energy relations for vaporization and sublimation of pure zinc are respectively. Some of the calculations also required knowledge of the free energy of fusion of zinc and calcium and the free energy for the 721°K allotropic transformation of calcium. The free energy of fusion of zinc was taken to be the difference between Eqs. [4] and [5], or The free energy of fusion and transition for calcium were based on the enthalpy values of 2040 and 222 cal per g-atom, respectively, as reported by Chiotti et al. 4 and the heat capacity data given by Hultgren et a1.3 and are represented by the relations, In the latter expression the difference in heat capacity between the a and 0 forms of calcium was neglected. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in preparing the alloys were Bunker Hill slab zinc, 99.99 pct pure, and Ames Laboratory calcium. The average impurities in the calcium in parts per million by weight, ppm, were N-17, H—77, Ba—216, Mg-15, Si—7, C—157, and Fe—9. The zinc was cleaned in dilute nitric acid and the calcium was used as received. The calcium was stored and handled in an argon-filled glove box and when removed from the dry box it was kept in an argon-filled desiccator. Tantalum was found to be a suitable alloy container. The alloy components were contained in a 1-in.-diam cylindri-

Jan 1, 1968

By D. E. Peacock, B. Harris

Thermal-expansion and electrical-resistivity measurements have been carried out below 400°K on niobium and two niobium alloys containing tungsten. For anonaly in the expansion us temperature curve below aboct 300°K. This reslt is consistent with an earlier obsercation that Young's modilus joy Cb-132 lms an unusiully strong -tenperati-e dependence below roon temperature. No anonulous behavior was observed in the resistiuity vs temperature curve for either alloy or in the magnetic susceptibility us tenperature curve for Cb-132. These results are disclssed in terms of various electronic and bonding theories of the transition metals and their alloys, but it has not been possible to reach any definite conclusion as to the cause of the results obtained. ALONG with investigations of the low-temperature mechanical behavior of niobium and its alloys, some of the physical properties of these materials have also been studied. In the work described here, thermal expansion and electrical resistivity were measured below 400°K for niobium and two of its alloys, Cb-132 and D-43. In addition, the magnetic susceptibility of Cb-132 was measured over the same temperature range. The alloys are representative of two distinct tion-hardened alloy such as might find service as a turbine blade, while D-43 (Nb, 5.3 at. pct W, 1.1 at. pct Zr. and 0.08 at. pct C) is a solution- and dispersion-hardened alloy, of considerably lower strength than Cb-132. which is a potential vane material. Their significant common feature is the presence of tungsten as the principal source of solution hardening. EXPERIMENTAL TECHNIQUES Thermal-expansion measurements were made with a quartz-tube dilatometer using baths of liquid nitrogen, liquid bromoethane, and a liquid polyalkylene glycol derivative to cover the range 80 to 400 K. Results are recorded as expansion relative to that of quartz, and the probable maximum error in any value of relative expansion. All, is about il pct. The metallurgical condition of the specimens, which were in rod form. will be discussed in the section dealing with experimental results. Resistivity was measured on recrystallized wires 0.030 in. in diam using a potentiometric technique. The same baths were used for temperatures between 80' and 400°K as were used for the expansion measurements. and in addition the resistance of D-43 and Cb-132 was measured at 4.2 K by immersion in liquid helium. The maximum expected experimental error in any resistivity value is about 3 pct and that in any change in resistivity about i0.05 pct. Temperatures in both sets of experiments were measured with liquid-in-glass thermometers with an accuracy usually better than 1°K. EXPERIMENTAL RESULTS 1) Thermal Expansion. In Fig. 1 is shown the relative linear expansion of recrystallized niobium. D-43. and Cb-132. The curve for Cb-132 is composed of results from several runs on three different samples. Two of the samples were annealed for an hour at 1500°C to cause recrystallization and the third was annealed for an hour at 2000'C to remove some mi-crosegregation of tungsten which was known to be present in the wrought alloy received from the manu-

Jan 1, 1967

By L. R. Woodyatt, H. J. Beattie, C. T. Sims

Theories correlating the formation of u and related intermetallic compounds to the electron-per-atom density of binary and ternary alloys have appeared regularly in recent technical literature. These same principles can be modified and applied to complex precipitation-strengthened alloys such as the iron-, cobalt-, and nickel-base superalloys and the stainless steels. Since these complex alloys contain carbides and other phases that normally precipitate before the U-type phases, the nature and amount of the precipitated phases must be calculated first. The following general formula is then applied to the residual matrix composition of the alloy: element. The magnitude of the resulting number is indicative of whether the alloy will form a a -type phase. When these calculations (which are computerized) are systematically applied to alloys of knoun phase analysis, a breakoff in average electron-vacancy number is noted between U-free and U-prone alloys. Alloys with an average electron-vacancy number higher than the breakoff form a-type phases, while those with lower ones do not form these phases. This method could then be used to eliminate from consideration all experimental compositions that would precipitate undesirable phases. It also is useful in evaluating analyzed heats of alloys where minor heat-to-heat variations determine whether the alloy is o-free or o-prone. THE highly significant development of strong, ductile superalloys to provide reliable construction materials in the 1000" to 2500° F temperature range has been due principally to unremitting application of Edisonian techniques and logic by the dedicated physical metallurgists who have shouldered this responsibility. Tools such as the electron microscope, phase analysis, and computers to accomplish regression analyses have been used heavily, but the effort has been essentially practice of an art, rather than a science. The objective of this paper is to describe and illustrate application of some relatively fundamental principles to certain of these alloy systems in an attempt to remove some of the empiricism from the technology. Specifically, the work presented here deals with the use of periodic-group relationships to predict the formation of intermetallic phases which can occur in primarily austenitic (fcc) structures. Calculations that have been developed might be applied in the design of new alloys and the evaluation of known alloys, and thus have the potential of eliminating vast areas of unnecessary alloy preparation and evaluation. ALLOYING CONCEPTS AND STRUCTURAL FEATURES OF SUPERALLOYS Strength is produced in austenitic superalloys by three principle mechanisms: 1) precipitation of y'; 2) formation of carbides; 3) solid-solution hardening by soluble refractory metals. The first mechanism requires the addition of aluminum and titanium, the second requires carbon and carbide-forming elements, while the third calls for the addition of molybdenum and/or tungsten. A considerable concentration of chromium is usually maintained to resist oxidation/corrosion, but it is also an important carbide-forming element. Fig. 1 shows a sketch and electron micrograph of the structure of a typical wrought nickel-base super-

Jan 1, 1967

By V. Koump, T. F. Perzak, R. G. Olsson

The vate of dissolutioz of carbon in molten Fe-C alloys urns studied by votating- cylindrical g-vaphite sairlples in a stationary crucible containing the melt. The rate of dissolltion was determdined from the change in the bnth co)npositiorz. Alccss-tvansfev coeffi'cients, calcilated with the assurlption that the inte)yacial liquid ulas saturated with carbon, were found to be in agreement with an existing Correlation fov mass transfer jroni votating cylinders. It is corzcllrded tlat, itz the wnge of- Reynolds' numbers itzvestigated (790 to 18,000), the vate of dissolutio of carborz in Fe-C alloys is controlled by tile rate of carbon difirsion from the interface. The dissolution of carbon in molten Fe-C alloys has been the subject of a number of investigations. Most of these investigations have been inconclusive because of poorly defined experimental variables. Two of the more sophisticated studies are summarized below. Dahlke and Knacke' studied the phenomenon by, in part, immersing graphite rods into 0.5 pct carbon-steel for different lengths of time. Since the experiments were conducted in air or in CO atmospheres, the melt was strongly agitated by gas evolution. It was concluded that the change in bath composition as a function of immersion time was in agreement with the assumption that the dissolution process was transport-controlled. The hydrodynamic conditions in these experiments, however, were not well-defined and gave no indication of the nature of the dissolution process at higher fluid velocities. In a recent study Shurygin and ruk investigated the dissolution of carbon in molten Fe-C, Fe-Si, Fe-P, and Fe-Ni alloys. Small graphite disks were rotated in a crucible containing molten alloys under such conditions that only the lower face of the disk was exposed to the melt. The results of this investigation indicate that, over the range of velocities (100 to 1000 rpm) and bulk liquid concentrations (0.7 to 4.5 wt pct C) considered, the dissolution of carbon in the iron alloys is limited by the diffusion of carbon from the interface to the bulk liquid (a transport mechanism). For the particular geometry used by these authors, exact analytical solutions of hydrodynamic and diffusion problems are aailable. Hence the experimental results obtained by Shurygin and Kryuk permit the evaluation of diffusion coefficients of carbon in the four systems investigated. In the present investigation a series of experiments were conducted in which the rate of dissolution of carbon in Fe-C alloys was measured under conditions which permitted wide variation of the fluid velocity and the carbon concentration of the bulk liquid. Graphite cylinders were rotated at different speeds in a stationary concentric crucible containing various molten Fe-C alloys. THEORETICAL DEVELOPMENT In general, the resistance to mass transfer from a solid interface to a turbulent liquid is assumed to reside in a laminar boundary layer adjacent to the interface. If it is also assumed that the diffusion coefficient is independent of concentration, the steady-state rate of dissolution for the case of arbitrary liquid and solid densities can be obtained from the integration of the equations of continuity. The derivation is similar to that used by Lommel and chalmers4 for the case of pl = ps. The solution, expressed in terms where N = rate of diffusion of the solute from the interface. Exact analytical solutions of the hydrodynamic equation for the boundary layer thickness are available for only a limited number of geometries. Consequently, a mass-transfer coefficient, k, is usually

Jan 1, 1967

By Jack L. Taylor

Single crystals of tungsten grown from powder -metallurgy swaged rod by high-temperative annealing were deformed in tetzsion at temperatures from 2500 to 5000 OF. Orientation of specittzen tensile axis, strained ratrix, and defortnation bands was determined optically by reflections from {110} etch pits. Slip traces meve analyzed and slip directiorz determined. Results indicate that {110}(111) , {112){111}. and {123}{111} type slip occur in tungsten over the terpe,atuve rutge investigated. Slip is orientation-dependent occuvring on tCuzt cowzbitzation oj slip plane and direction which has the highest critical resolved shear stvess. Overshooting appears to be a general occurrence between 2500' and 5000°F. Dejornatiotz bands show rotation in a directiorz opposite to the yotation of tire tensile axis. DEFORMATION in bcc metals has been reviewed by Maddin and Chen,' Keh and eissman,' and most recently by Nabarro, Basinski, and olt. From these reviews it is apparent that some disagreement exists concerning the crystallography of plastic deformation in bcc metals. There is evidence of noncrystallo-graphic slip, the crystal slipping on or near a noncrys-tallographic plane in the (111) zone for which the resolved shear stress is greatest. There is also evidence to indicate that crystallographic slip occurs in the planes of the same zone. On the other hand, there is agreement that the close-packed direction ( 111) is the slip direction in bcc metals. Further, in pure bcc metals4 and alloys the operative crystallographic slip systems are strongly dependent on temperature. Both crystallographic and noncrystallographic slip have been reportede8 in tungsten, a group VIA bcc metal. The number of slip families which operate in the case of crystallographic slip, however, has been in question. The earliest study by oucher' of single-crystal tungsten tested at temperatures of 1800 to 5000°F led to the conclusion that only {112)( 111) type slip operated. Raymond and eumann recently reached the same conclusion studying deformation by rolling of plasma-flame single crystals at 1800°F; however, only [loo] and [110] orientations were studied. Work at high temperatures by Leber and Pughs on tungsten and Chen and Maddin9 on molybdenum suggests that conjugate slip on nonparallel (110) planes may account for the slip on (112) and (123) planes found by others working with bcc metals. The present paper presents evidence of three families or modes of slip in tungsten in the temperature EXPERIMENTAL PROCEDURE Material. Standard microtensile specimens, 0.160 in. diam by 0.640 in. gage length, were ground from commercial powder-metallurgy swaged tungsten rod, type MK. Specimens were heated for 10 min at 5150°F or 6 hr at 5400°F in vacuum of 1 x 105 Torr or less to produce single crystals. At the lower temperature an average of two out of seven specimens heated in a group developed single crystals throughout the specimen length as shown in Fig. 1, the rest remaining wholly poly crystalline. At the higher temperature, three or four out of seven specimens became single crystal. Other than to note that Laue X-ray photographs generally showed sharp, well-defined spots, no attempt was made to assess crystal perfection or measure dislocation density. Two tungsten single crystals grown from the melt by the plasma-arc process were also used for this study.

Jan 1, 1967

By D. A. Munro, G. P. Contractor

Fourteen 50-lb laboratory melts were investigated to determine the effect of uranium on the tenpering characteristics of loo-carbon (0.06 to 0.1 pct C) steels. It was found that uranium additions, particularly in the range 0.30 to 0.45 pct, enhanced the hardness and both ultimate and yield strength of the experivzental steels in the quenched and tempered condition. The structural and morphological chazges indicated that uranium retarded tempering of the tnartensite, thereby hindering the normal formation of polygonal ferrite formed in the late stages of tempering. The effect of this was to make possible the re-tension of the acicilar ferritic structure in the uranium-bearing' steels. The iraniuin-bearing steels also showed IVidnzanstatten-type growth of ferrite plates and had large prior austenite grains containing assenzblies of fine ferrite grains, mainly acicular in geometry. The fine-grained ferrite structure and the presence of more numerous and apparently smaller precipitates in the uranium-bearing steels are thought to he principally responsible for the itnproved tensile strength and hardness of the experinzental uranium-bearing steels. At ternperirzg temperatures above 455% (850'F) the ferrite in the higher-uraniun steels nzaintained acicularity and, hence, its strength and resistance to tempering. Uranium did not produce a secondary hardening peak. However, it retarded softening during the third stage of tempering because of its effect of inhibiting the grouth of cementite particles and of retaining the acicularity of ferrite plates. The resistance to coalescence accounted for the slow grocth of the ferrite grains in the uranium-modified steels and, hence, fov the persistence of the acicular ferrite structure. IT had been found previously1 that uranium additions up to about 0.45 pct had no significant effect on the tensile properties of low-carbon steel (0.06 to 0.10 pct C) in the as-rolled and normalized conditions, Fig. 1. On the other hand, it was observed that uranium in excess of about 0.30 pct had an embrittling effect as revealed by Charpy V-notch impact results. It was also noted that, as the uranium content increased, the morphology of pearlite changed from lamellar to feathery and the ferrite grains showed an etching effect resembling striated or dashed markings, suggestive of precipitation. The sharp drop in the impact properties shown in Fig. 2 warranted an assumption that the uranium content of about 0.30 to 0.45 pct may produce some secondary hardening reaction on tempering, analogous to that associated with a Cr-Mo-V steel, which shows very poor CVN toughness at the secondary hardness peak in the tempering curve.1' With this background and the reported findings of Hasegawa and noda that low-carbon uranium-treated steel showed signs of secondary hardening, the present investigation was undertaken to determine the effect of uranium additions on the mechanical properties of 0.10 pct C steels. No attempts were made to investigate in detail the mechanisms of hardening, although some suggestions based on the experiments are made. MATERIALS AND PROCEDURES A series of 50-lb induction-furnace melts was made using AISI 1008 rimming steel billets as the melting stock. The melting, forging, and rolling techniques proven satisfactory in previous projects'-3 were employed as a guide for this investigation. The steel was deoxidized with aluminum (2 lb per ton) prior to the addition of high-purity uranium. The analysis of each melt is given in Table I. Properties were evaluated as a function of heat treatment and are presented in terms of hardness and tensile strength vs tempering temperatures. The variation of hardness with the tempering temperature was studied on the quenched and tempered specimens, some of which measured 0.50 by 0.25 in. diam and the others 0.40-in. cubes. Before quenching, the specimens were vacuum-sealed in glass tubes and normalized at 900°C (1650°F) for 20 min. Following this treatment, the sealed specimens were hardened by austenitizing at 955°C (1750°F) for 20 min and water quenching, and then tempered for 1 hr in the range 150 to 730°C

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By Y. C. Liu, G. A. Alers

The anisotropy of Young's modules has been measured in a series of Cu-Zn alloys containing from 1 to 28 wt pct Zn and cold-rolled to 97.5 pct reduction in thickness. These modulus data show a transition in texture as a function of zinc content. In alloys containing 3 pct Zn or less, the texture is essentially that of copper. A transition is clearly seen to develop in 5 and 8 pct Zn alloys, and to have been completed in a 12 pct Zn alloy. Increasing the proportion of zinc to 28 pct does not produce any further changes in texture. The ease and clarity with which this texture transition can be seen in the modulus data is in great contrast with the inccertainty in the visual detertiination of the range of texture transition from a series of pole figures. It is also shown that the rolling texture of the high zinc content alloys cannot be a one-COIIIponenl texture, characterized by the (110)(112) ideal orientations, as usually assumed. A second, quite important component must also be present. Furthermore, the present data are inconsistent with matrix orientations on which the "oriented growth" hypothesis of the Formation of recrystallization textures is based. THE rolling textures of binary fcc alloy systems have generally been considered to lie between two terminal textures. One of these terminal textures is the copper type and the other is the 70:30 brass type. Alloys of intermediate solute content exhibit a texture which is said to be a transition between the two terminal textures. On the basis of efforts to correlate rolling and recrystallization textures, two concepts have been advanced in the literature on the nature of these transition textures. One school1 suggests that the addition of alloying elements, e.g., zinc, causes a gradual rotation about one of the (111) poles from the (358)( 523) ideal orientation of the copper-type rolling texture to the terminal {1 10)( 112) ideal orientation used to describe the rolling texture of 70:30 brass. This concept is depicted in Fig. 1 with the angle of rotation corresponding approximately to the zinc content and is designated here as the "rotational concept", since the ideal orientation of the transition textures varies continuously with alloy content. The other concept,' the "mixture concept", suggests that the copper-type rolling texture is a two-component texture. {358) (523) and {110)(112). The addition of alloying elements affects only quantitatively the relative amounts of these two components—a decrease in the amount of material in the {385}(523) orientation and an increase of that in the {110)(112) orientation with increasing solute content. An experimental distinction between these two concepts is essential to a better understanding of both the mechanism of formation of rolling textures and the subsequent formation of recrystailization textures in fcc metals. Because of the lack of resolution inherent in pole figures, it has not been possible to differentiate between the two concepts on the basis of this data. Both concepts, in fact, make use of the same set of pole figures but interpret them in a manner acco-rding to the view held.'" Experimental results obtained from inverse pole figures or selected-area electron diffraction3j4 simply -yield more refined pole figures but do not eliminate the ambiguity of interpretation. Quantitative measurement of an entirely different, orientation-dependent property must thus be considered

Jan 1, 1967

By D. R. Uhlmann, T. P. Seward, O. Chalmers

A magnetic field has been used to damp out liquid convection during the solidification of castings. Ingots of Al-2 pct Cu were poured from various sperheats (10" to 65°C) into a room-temperature graphite mold located between the poles of an electromagnet. The effect on ingot structure of varying the strength and time of application of the magnetic field was investigated, and the results are interpreted in light 01- current theories of ingot structure. In the solidification of alloy systems, thermal gradients in the melt and differences in density of the constituents are expected to produce convective motion in the liquid. The thermal convection caused by temperature gradients should be present during the freezing of both alloys and pure materials, while the solute convection caused by density differences should be of concern only for alloys. The possible influence of this natural convection on the structure of castings has been discussed by Ruddle,' Chalmers, and Tiller. More recently, an experimental investigation of such effects was carried out by Cole and Bolling. These workers took stationary molds containing lead- and tin-based alloys and. using a brine solution. quenched them from various superheats above their respective liquidus temperatures. When grids were placed across the mold diameter to suppress convection, the grid region was later observed to contain a larger percentage of columnar grains than other parts of the casting or than similar castings poured without the grids present. From thermocouple measurements, they found the temperature in the grid region to be higher than that in the region outside the grids throughout the freezing process, and concluded that convection should be an important mode of heat transfer in normal castings. In addition to such convection arising from thermal gradients or differences in density of the constituents, a further source of convective motion, which we shall call "momentum convection", may be particularly important in small (laboratory-size) castings. By this term we refer to the convective motion produced in the initial pouring process, a motion which is damped out as the linear momentum and angular momentum of the liquid are dissipated. Besides these sources of convection, which are present to some extent in all castings. external influences may also be effective in producing convective motion. Examples of such "forced" convection which have been discussed in the literature include stirring the melt, shaking the mold, rotating the mold, and so forth The purpose of the present study was to examine the effect of convection on the structure of castings poured into a cold mold. In this work, a magnetic field was employed to damp out the convective motions within the liquid, and hence control the extent of con- The effect of a magnetic field on convective currents in a conducting liquid is to induce eddy currents which oppose and damp out the convective motion. vection. The technique of magnetic damping was previously used by Utech and F1emings" in their study of convective effects on impurity banding and other substructure in alloy crystals grown unidirectionally from the melt. In their investigation, fields as small as 200 gauss were found to be effective in damping the convection currents which influence the banding. I) EXPERIMENTAL TECHNIQUE In the present study, alloys of A1-2 wt pct Cu were poured into a room-temperature graphite mold. The mold, in the shape of a circular cylinder, 2 in. ID, 2-3/4 in. OD, 5 in. inside height, and 5-1/2 in. outside

Jan 1, 1967

By Wei-Kao Lu, G. Bitsianes

An improved general rate equation for a one-ditnensional gas-solid system has been derived. Fov the veversihle interfacial chemical reaction, there are concentrations of gaseous reactant and product at the reacting zone to be considered. They have been calculated with the velations fuvnished by the constraints on the system, namely, quasi-steady state and equimolal counterdiffusion of the gases. The results of the diffusiori study of Evans, Watson, and ,Mason based on the "dusty gas" model have been applied here. The interfacial chemical reaction is taken as first-order with respect to the concentration of the gases involved. The equation has proper dependence on gas composition and on solid structure through the relative values of Knudsen and normal diffusivities. The existence of the total pressure gradient inside the specimen has been predicted and confirmed experimentally. In a previous communication' we introduced a general rate equation for gas-solid reactions by considering the contributions of chemical reaction at inter- phase boundaries and diffusion through the solid product layer simultaneously. These equations, for one-dimensional and spherical specimens, take care of the whole range continuously from purely diffusion control to purely chemical reaction control. In this paper we study only the one-dimensional system. The corresponding rate equation is reproduced here: Of the two terms on the right-hand side of Eq. [I], the first represents the contribution of interfacial chemical reaction and the second that of gaseous diffusion. The shortcomings of Eq. [I] are that in its derivation the interfacial chemical reaction was assumed to be irreversible and the diffusion rate of gaseous product was not considered. Any pressure effects building up within the porous media were also neglected. Evidently. these simplifying assumptions will limit the general applicability of these equations. The rate of reduction of iron oxide by hydrogen, for instance, is very sensitive to the concentration of water vapor in the main gas stream, as has been reported by cewan' and by Quets et a1.3 Furthermore, the gaseous phase at the reacting interface will contain an appreciable amount of the gaseous product of reaction. If this were not true, a sufficiently high concentration gradient for the outward diffusion of the gaseous product could not be maintained. With these shortcomings in mind, Eq. [1I cannot be rigorously ap-

Jan 1, 1967

By G. R. Love, M. L. Picklesimer

Aboue 950°C the Nb-Zr system consists of a completely miscible bcc solid solution, commonly called the phase. Between 950 and 600°C, and between 20 and 85 pct Nb, the phase deconlposes, after sunciently long times, into two bcc solid solutions. The pct Zr alloys are conveniently descibecl with T-T-T (time-temperature-transformation) curves having a nose at about 2 hr at 700°C. The reaction rate varies only slowly with zirconium content and negligibly with oxygen contanzination; it is speeded up by a factor of 10 to 15 by 90 pct cold ulork and slowed dou by n factor oj 10 to 30 by a two-hundrecljold increase in grain size. Nb-r alloys with compositions between 40 and 85 pct Nb have been the basis for the majority of commercially important superconducting materials. In part because of their commercial promise, more is known about these alloys than about most other high-field superconducting materials. At the same time, there is considerable disputed or incomplete metallurgical information. For example, although Rogers and tkins&apos; indicate a monotectoid reaction at approximately 600°C and a two-phase 01 + 0, field extending between 20 and 85 pct Nb and to a maximum of 95OGC, erhout&apos; has reported that this entire region would be a single homogeneous B were it not for oxygen contamination. Again, although it has been shown that relatively short-time heat treatments in the vicinity of 700CZ significantly improve the ability of short wire samples to carry high currents in high magnetic fields at 4.2K, these observations have never been fully correlated with the structural change or changes occurring during the anneal. We intend to investigate in detail the effect of metallurgical variables, including heat treatment, on the superconducting properties of hard superconductors. To verify that our experimental techniques are valid and to establish a relative standard against which other materials may be measured, we feel it advisable to know the behavior of the Nb-Zr alloys under a variety of processing conditions. As an initial step toward this goal, we have determined in detail the kinetics of the transformations in Nb-Zr alloys. EXPERIMENT A number of problems had to be solved before beginning any fruitful work on the reaction kinetics in this system. While solving some of these problems, either by chance or by design, small amounts of information were obtained about alloys containing 40, 50, 60, 65, 67, 70, and 75 pct Nb, bal. Zr. In addition, a large range of grain sizes and a range of temperatures considerably greater than the range indicated by Rogers and Atkins phase diagram were examined. We will, however, report in detail only the results obtained for the Nb + 33 pct Zr and Nb + 25 pct Zr alloys at three grain sizes, two levels of oxygen contamination, and the temperature range 550 to 950°C. These data are most complete, but the other data are sufficiently complete to indicate the kind and magnitude of the variation of the transformation kinetics outside this range. The first and most difficult problem encountered in this inquiry was one of sample homogeneity. When Nb-Zr alloys are arc- or electron-beam-melted on a cooled copper hearth, solidification is sufficiently slow that there is appreciable coring in the cast structure and a large variation of grain size across the button thickness. Both these factors significantly affect the apparent reaction rate in the system. A two-step solution to the problem was attempted; an arc-melting and drop-casting technique has been developed by conald that greatly reduces the as-cast grain size and virtually eliminates coring segregation. Ingots made in this way exhibited no detectable (3 pct maximum) zirconium segregation. Before it was evident just how good this technique was, we attempted to supplement it with rather long-time, high-temperature annealing of the cast ingots. This annealing was carried out in evacuated and sealed (seal-off pressures < 1.0 x 106 torr) quartz capsules lined with tantalum foil at 1400 to 1450 C for 8 to 72 hr. There were two principal effects of this treatment: the grain size increased to a fairly uniform 150 p, and the surface and all grain boundaries near the surface acquired a film of a second phase, tentatively identified as an oxide (possibly additionally contaminated with silicon). There was no evidence that this 1400 C treatment had affected the zirconium segregation. High-temperature annealing was subsequently used only for grain-size control, but anneals of longer than 4 hr at temperatures greater than 1000°C were performed in dynamic vacuums (pressure no greater than 1.0 x lo torr). Any contamination resulting from these treatments was well below the limits of detection of our techniques. All samples, as cast, were cold-swaged to at least 85 pct reduction in area. The samples called cold-worked were tested as swaged. The minimum re-crystallization anneal for these alloys was about 12 hr at 1050 C; this produced an equiaxed grain diameter of about 4 to 8 P. Annealing for 4 hr at 1450°C produced a grain size of about 80 to 150 p; and annealing for 4 hr at 1650aC, close to the melting point of many of these alloys, produced a grain size of 0.5 to 1.0 mm. At all temperatures, the larger grain size was

Jan 1, 1967

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid binary and ternary Fe-Ni-Co alloys has been measured by the Sieverts&apos; method between 1550°and 1700°C. Solubility data and standard free energzes and enthalpies of solution for nitrogen in the alloys are presented. Interaction parameters are discussed and presented for binary and ternary alloys. MOST of the studies of nitrogen solubility in liquid metals have been directed toward the dilute alloys of iron. Several of these investigations have included measurements of the nitrogen solubility in Fe-Ni al10s&apos;- and in Fe-Co alloys.435 There has been some work, however, that has extended across the e-i-" and F-CO" binaries. This investigation was undertaken to determine the nitrogen solubility in both binary and ternary alloys of the Fe-Ni-Co system. It was also hoped that the differences between earlier studies might be resolved. EXPERIMENTAL METHOD This investigation was made using a Sieverts&apos; apparatus described previously." The nickel (99.85 pct) and cobalt (99.9 pct) were obtained from Sherritt-Gordon Mines, Ltd., and the iron (99.95 pct) was Fer-rovac-E obtained from Crucible Steel Co. Recrystal-lized alumina crucibles were used throughout the entire investigation with no evidence of crucible-melt reaction. Melt temperatures were measured with an optical pyrometer and the temperature scale calibrated against the melting points of the three pure metals. The emissivity of the melt was assumed to be a linear function of composition for all alloys, as has been shown for Fe-Ni alloys.lZ The emissivity of the pure metals at 1600°C were taken as 0.43 for iron, 0.44 for cobalt, and 0.45 for nickel. Using these emissivities, the trans mis sivity of the system was found to be 0.51 i 0.01. The Sieverts&apos; method was used for this study and followed the procedures outlined previously.l&apos; The individual metals were weighed to give about 100 g of alloy. The alloys were melted in the crucible under a partial pressure of argon. The system was evacuated, and the "hot volume" was measured with argon. To avoid the errors caused by vaporization, the melt was held under vacuum only long enough to ensure that all of the gas in the system had been removed. The influence of any small amount of vaporization on the "hot volume" was shown to be negligible by measuring the "hot volume" after a run. This measurement agreed with that made at the start of the run within the implicit error, 0.2 cc, caused by the limitations in accurately reading the buret. The solubility-pressure relationship was measured in the pure metals and in several alloy compositions throughout the ternary system. These measurements were made by admitting measured amounts of nitrogen to the system, and then determining the equilibrium nitrogen pressure above the melt. This method has the distinct advantage of higher accuracy, particularly at lower pressures, than measurements made by withdrawing gas from the system to reduce the pressure after determining the solubility at 1 atm nitrogen pressure. This latter method has a practical lower limit of about 0.4 atm where an increased error is encountered because the buret must be emptied to permit further measurements at lower pressures. By determining the relation between apparent solubility and pressure, it was possible to make a good estimate of the initial nitrogen content of the metal from the intercept of the solubility curve extrapolated to zero pressure.11 DISCUSSION The solubility data corrected to 1 atm nitrogen pressure are summarized in Table I. The reported solubility has been corrected for the initial nitrogen content of the alloys. The initial nitrogen contents fell between 0.0002 and 0.0010 wt pct, and were lower in the iron and nickel than in the cobalt. Sieverts&apos; law was obeyed in all alloys at pressures up to 1 atm. Examples of this behavior are shown in Fig. 1. The reaction for solution of nitrogen is Taking the standard state as 1 wt pct N in the alloy and the reference state as nitrogen at infinite dilution in the alloy, and noting the adherence to Sieverts&apos; law, K becomes the solubility of nitrogen in the alloy at 1 atm pressure. Thus the solubility data of Table I were used directly to calculate the standard free energy for the solution reaction. These results are also presented in Table I. The enthalpy of solution is also summarized in Table I as calculated from a form of the van&apos;t Hoff relation: Iron-Nickel System. The data for the solubility of nitrogen in liquid Fe-Ni binary alloys is presented in Fig. 2 along the with data of aito, Schenck et al.,&apos; and Humbert and 1liott.l&apos; The data for studies of nitrogen solubility in Fe-Ni alloys containing less than 20 pc t i&apos;- are not presented in Fig. 2, although they are in good agreement with the present work. The results of this study are in good agreement with Schenck

Jan 1, 1967

By C. M. Sellars, F. Maak

Electvomotie -force measurements hazle been made on ten Au-Ni alloys at temperatures 7754 825O, 900O, and 935°C using galvanic cells with solid electrolyte. Partial and ivtegral thermodynamic functions are derived from the determined activities. which show la9,ge positive deviations jvom Raoult&apos;s law. The enthalpies of mixing- are in close accord with calorinletric data and are of comparable accuracy. The results are used to determine the miscibility gap and the spinoidal curL1e, and are qlalitaticely interpreted in terms of the large size difference and electvonic interactions between gold and nickel. Tabulated nalues of the actielities and partial and inteqal free energies, entropies , and enthalpies of mixing are given in the appendix. The Au-Ni binary alloys are of particular interest thermodynamically as despite the large size difference between gold and nickel atoms they have a simple phase diagram.&apos; This shows complete solid solubility above a miscibility gap with a maximum at about 71 at. pct Ni and 810°C. Activity measurements (over a range of temperature) have been made previously on this system using an electrolytic-cell method with a liquid chloride eletrolyte. The accuracy of this data has, however, been queried3&apos;4 as it leads to values for the enthalpy of mixing which are too high when compared with calorimetric measurements.46 Also, the entropy of mixing is too high when compared with the values derived from specific-heat measrements. It was therefore considered worthwhile redetermining the activity data using a galvanic cell with a solid electrolyte (0.85 ZrO, 0.15 CaO). This method is based on a technique introduced by Kiukkola and aner&apos;&apos; and has been used to determine the thermodynamic data for Cu-Ni alloys.&apos; THE ELECTROLYTIC CELL The cell used to determine the activity of nickel in Au-Ni alloys was: The cell reaction, which is discussed for a similar cell by Rapp and Maak, gives a direct measurement of the activity of nickel in the alloys as where aNi(alloy) is the activity of nickel in the alloy, 3 is Faraday&apos;s constant, E is the measured electromotive force, R is the gas constant, and T is absolute temperature. For the valid application of this type of cell the arrangement must be ther modynamic ally stable, which means that: 1) The free energies of formation of the oxides fulfill the relation 2) The vapor pressures or dissociation pressures of each component must be so small that during the time of the experiment the amount of any material transported by the gas is negligible. 3) Side reactions which change the alloy composition must be negligible. These reactions are possible both with the surrounding gas atmosphere and with neighboring solid material. The first two conditions are fulfilled by the above cell.&apos; The third condition is approached by care in the experimental technique. The factors which control the attainment of equilibrium in this type of cell have been considered by Rapp and aak, who conclude that metallic diffusion in the alloy is the rate-control ling step. A lower temperature limit for the practical application of this cell is therefore set by the condition that equilibrium must be attained in reasonable times. EXPERIMENTAL MATERIALS AND TECHNIQUE The starting materials were mint gold (99.99 pct Au) and Mond nickel (99.9 pct Ni). Alloys, nominally 5 at. pct Ni and then each 10 at. pct across the system, were produced by vacuum-levitation melting compacts of mixed drillings of the pure metals. The nickel used for the reference tablets in the cells was melted in a similar manner. The alloy ingots, cast in boron nitride molds, were cold-forged and

Jan 1, 1967

By V. B. Tare, H. Schmalzried

The use of solid electrolytes for determining kinetic paraneters at elevated tevnperatures is pointed out. The reaction rate constant k1 of the phase-boundary reaction during oxidution of iron to wiistite by CO2-CO gas mixtures has been deternined between 850 nnd 975C, using ZrOz(+CaO) as an electrolyte. Values are between 1.4 x 10-a and 5.2 x 10 ole per sq ctn atm. The tzain difficulty is due to mixed potentials arising from side reactions at the electrolyte inteyface. In a number of papers the calcium-doped zirconia electrolyte has been used for the determination of thermodynamic data from measured differences in oxygen activities (or potentials) between two electrodes. The purpose of this note is to suggest the use of this solid electrolyte for kinetic measurements as well. The principle can be seen from Fig. 1. A thin and compact phase II (electron conductor) is fixed on a plate of gas-tight, polished ZrO2(+CaO) (I), which separates two compartments with different oxygen potential. p, is a constant reference pressure of oxygen (1 atm). The electromotive force of this galvanic cell is given by E = RT5 In pep, and pe is the oxygen partial pressure at the interface electrolytephase 11. If phase I1 is in equilibrium with the surrounding gas phase, p, = DR. If pg changes sud- denly to a value pi, p, and therefore the electromotive force, E, change as a function of time according to the phase-boundary reaction rate at the gas phase I1 interface and the transport processes inside phase 11. It is assumed that local equilibrium is established at the boundary electrolytephase 11, that the gas phase shows no concentration gradients, and that the con-

Jan 1, 1967