Search Documents

By O. W. Ellis

The question of the influence of gases upon the properties of copper has received the attention of a number of investigators, among whom Sieverts,' Iwase,2 Lobley and Jepson3 stand preeminent. Solubility of Gases in Copper Sieverts and Iwasé concerned themselves with the solubility of a variety of gases in the metal in the solid and liquid states. They determined the absorption coefficients of these gases and in all cases found a sharp change in solubility at the melting point of the metal. In this respect they disagree with Lobley and Jepson, who have based their opinions upon the appearance of small ingots of the metal which had been fused in an atmosphere of one or other of three gases and had then been rapidly cooled, while surrounded by gas, to the freezing point (rate—possibly 30" to 60" C. per sec.). The ingots that had been fused and cooled under nitrogen and carbon monoxide were free from blowholes and it was assumed that these gases were not absorbed in amounts much in excess of those which would dissolve in the solid metal; the ingots similarly treated under hydrogen were full of blowholes and it was assumed in this case that gas was ejected on solidification of the copper. The effect of varying the rate of freezing upon the character of the test ingots was not examined by these investigators; otherwise, it is felt, their views might have been subject to modification. Sieverts' most important contribution is that the solubility of a gas in any metal is proportional to the square root of its pressure or concentration. Knowing then the absorption coefficients of the various gases in copper, it should be possible to determine the analysis of the

Jan 1, 1929

By O. W. Ellis

The question of the influence of gases upon the properties of copper has received the attention of a number of investigators, among whom Sieverts,' Iwase,2 Lobley and Jepson3 stand preeminent. Solubility of Gases in Copper Sieverts and Iwasé concerned themselves with the solubility of a variety of gases in the metal in the solid and liquid states. They determined the absorption coefficients of these gases and in all cases found a sharp change in solubility at the melting point of the metal. In this respect they disagree with Lobley and Jepson, who have based their opinions upon the appearance of small ingots of the metal which had been fused in an atmosphere of one or other of three gases and had then been rapidly cooled, while surrounded by gas, to the freezing point (rate—possibly 30" to 60" C. per sec.). The ingots that had been fused and cooled under nitrogen and carbon monoxide were free from blowholes and it was assumed that these gases were not absorbed in amounts much in excess of those which would dissolve in the solid metal; the ingots similarly treated under hydrogen were full of blowholes and it was assumed in this case that gas was ejected on solidification of the copper. The effect of varying the rate of freezing upon the character of the test ingots was not examined by these investigators; otherwise, it is felt, their views might have been subject to modification. Sieverts' most important contribution is that the solubility of a gas in any metal is proportional to the square root of its pressure or concentration. Knowing then the absorption coefficients of the various gases in copper, it should be possible to determine the analysis of the

Jan 1, 1929

By Samuel L. Hoyt

This paper gives a brief description of an investigation made several years ago on the diffusion of zinc into copper. The material for that study was furnished in the form of thin copper strips coated with zinc. The result was required rather quickly and at not too great an expense, and especially information was desired as to the rate at which zinc would diffuse from the zinc coating into the copper and the temperature at which the operation should be carried out. A study of the requirements of this problem indicated that the solution might be secured by means of six determinations. This is the smallest number that will give the information desired and, at the same time, furnish checks on the accuracy of the determinations which justify an abbreviated experimental program. This does not count a preliminary test which was designed to give some idea of the correct temperature to use. The minimum number of temperatures that can be used is two. Knowing the rates of diffusion of zinc into copper at two properly chosen temperatures, it is possible to calculate the rate for any other temperature, and also to check the accuracy of the determination by means of the heat of diffusion, which is calculated from the effect of temperature on the rate of diffusion. The minimum number of determinations at any one temperature is three. The amount of diffusion which occurs at a fixed temperature is definitely related to the time of diffusion, so that by determining the amount of diffusion for three different time intervals, this relationship may be established and possibly a check on the accuracy may be secured. This accounts for the six determinations or experiments, and suggests the logical plan of the work. The check used here is not generally applicable to diffusion phenomena, but it seems to hold closely enough for the limited amount of diffusion in this investigation to justify its use. The samples used were 5 to 6 mils thick and about 1 in. square. They were placed between iron blocks and set in the hot zone of a nichrome furnace which had been brought to the desired temperature Time was taken from the moment the samples reached the furnace

Jan 1, 1929

By Samuel L. Hoyt

This paper gives a brief description of an investigation made several years ago on the diffusion of zinc into copper. The material for that study was furnished in the form of thin copper strips coated with zinc. The result was required rather quickly and at not too great an expense, and especially information was desired as to the rate at which zinc would diffuse from the zinc coating into the copper and the temperature at which the operation should be carried out. A study of the requirements of this problem indicated that the solution might be secured by means of six determinations. This is the smallest number that will give the information desired and, at the same time, furnish checks on the accuracy of the determinations which justify an abbreviated experimental program. This does not count a preliminary test which was designed to give some idea of the correct temperature to use. The minimum number of temperatures that can be used is two. Knowing the rates of diffusion of zinc into copper at two properly chosen temperatures, it is possible to calculate the rate for any other temperature, and also to check the accuracy of the determination by means of the heat of diffusion, which is calculated from the effect of temperature on the rate of diffusion. The minimum number of determinations at any one temperature is three. The amount of diffusion which occurs at a fixed temperature is definitely related to the time of diffusion, so that by determining the amount of diffusion for three different time intervals, this relationship may be established and possibly a check on the accuracy may be secured. This accounts for the six determinations or experiments, and suggests the logical plan of the work. The check used here is not generally applicable to diffusion phenomena, but it seems to hold closely enough for the limited amount of diffusion in this investigation to justify its use. The samples used were 5 to 6 mils thick and about 1 in. square. They were placed between iron blocks and set in the hot zone of a nichrome furnace which had been brought to the desired temperature Time was taken from the moment the samples reached the furnace

Jan 1, 1929

By B. Egeberg, H. B. Smith

Britannia metal is a white alloy consisting primarily of tin and antimony, the tin greatly predominating. The alloy usually contains a small amount of copper and occasionally very small amounts of one or two other metals, such as bismuth, zinc, and lead. It is capable of being cold-rolled, it takes a high polish, and it is fairly noncorrosive; properties which make it a popular metal for many household and traveling utensils. Britannia metal is similar in many respects to pewter and has largely replaced pewter in the arts, but it should not be confused with that alloy, because pewter is essentially a tin-lead alloy, while Britannia is a tin-antimony alloy. In view of the fact that so little has been published concerning Britannia metal, the authors feel justified in presenting the results of their investigation, particularly since the behavior of this alloy under cold rolling and heat treatment differs so greatly from that of other metals and alloys. The old craftsman, engaged in the making of ornaments or tableware, heated the cold-rolled sheet metal or his finished product to a straw color corresponding to about 375" I?., claiming to produce thereby a harder and more rigid article. The fact that possibly led him to this heating was that a reheated article or sheet made from Britannia metal has a distinct metallic ring when struck a sharp blow, whereas an unheated article or sheet has a leady, dead note. No doubt he has associated the metallic ring with a greater rigidity and strength, and justly so, as will be seen later. The approximate analysis of the metal we investigated was 91 Sn, 7 Sb, 2 Cu, and the molten metal was bottom-poured into an iron mold yielding an ingot 7 3/4 in. wide by 11 in. long and % in. thick, the casting temperature being 800" F. The ingot was cold-rolled to a sheet 0.032 in. thick, sufficiently large samples for experimental purposes being cut from the sheet at intermediate stages. The samples were all tested for hardness with scleroscope and Brine11 machine, then heated to 212" F. for 30 min., and again tested after cooling to room temperature. The same samples were heated successively at 300°, 400°, and 440" F., followed

Jan 1, 1929

By H. B. Smith, B. Egeberg

Britannia metal is a white alloy consisting primarily of tin and antimony, the tin greatly predominating. The alloy usually contains a small amount of copper and occasionally very small amounts of one or two other metals, such as bismuth, zinc, and lead. It is capable of being cold-rolled, it takes a high polish, and it is fairly noncorrosive; properties which make it a popular metal for many household and traveling utensils. Britannia metal is similar in many respects to pewter and has largely replaced pewter in the arts, but it should not be confused with that alloy, because pewter is essentially a tin-lead alloy, while Britannia is a tin-antimony alloy. In view of the fact that so little has been published concerning Britannia metal, the authors feel justified in presenting the results of their investigation, particularly since the behavior of this alloy under cold rolling and heat treatment differs so greatly from that of other metals and alloys. The old craftsman, engaged in the making of ornaments or tableware, heated the cold-rolled sheet metal or his finished product to a straw color corresponding to about 375" I?., claiming to produce thereby a harder and more rigid article. The fact that possibly led him to this heating was that a reheated article or sheet made from Britannia metal has a distinct metallic ring when struck a sharp blow, whereas an unheated article or sheet has a leady, dead note. No doubt he has associated the metallic ring with a greater rigidity and strength, and justly so, as will be seen later. The approximate analysis of the metal we investigated was 91 Sn, 7 Sb, 2 Cu, and the molten metal was bottom-poured into an iron mold yielding an ingot 7 3/4 in. wide by 11 in. long and % in. thick, the casting temperature being 800" F. The ingot was cold-rolled to a sheet 0.032 in. thick, sufficiently large samples for experimental purposes being cut from the sheet at intermediate stages. The samples were all tested for hardness with scleroscope and Brine11 machine, then heated to 212" F. for 30 min., and again tested after cooling to room temperature. The same samples were heated successively at 300°, 400°, and 440" F., followed

Jan 1, 1929

By E. M. Wise

THe properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. General Requirements In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should he good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depi1atories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 Ib. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800" and 1200" C. Colored Golds The popular green and yellow golds are based on the gold-silver-copper alloys; in some cases modified by the introduction of zinc to improve the casting properties and to alter the color, and nickel to increase the strength. The properties of the Au-Ag-Cu system have been the subject of a very thorough investigation by Jänecke,l Sterner-Rainer12 and Carter."

Jan 1, 1929

By E. M. Wise

THe properties required of gold alloys for jewelry are not well standardized, due in part to problems peculiar to certain branches of the jewelry industry, in part to the individual preference of the fabricator and to his willingness to cope with certain difficulties in manufacture, which arise with the use of certain alloys. General Requirements In general, the properties desired may be classed as follows: 1. Color should conform to the dictates of good taste and smart style. 2. Corrosion resistance and tarnish resistance should he good. This is to a considerable extent determined by the carat. Resistance to such corrosive agents as mercuric chloride as well as certain depi1atories is unreasonable to expect and difficult to meet. 3. Strength and hardness must be adequate to maintain the delicate contours of finely modeled jewelry. 4. Wear resistance must be great enough to resist abnormal wear, such as is encountered by a wedding ring in a lifetime of wear. 5. Ductility must be sufficient to permit the fabrication of drawn shells, tubes and difficult shapes. Material having a yield point of not less than 60,000 lb. per sq. in., an ultimate strength of 100,000 Ib. per sq. in., and an elongation of 40 per cent. is desirable. 6. Melting point should be between 800" and 1200" C. Colored Golds The popular green and yellow golds are based on the gold-silver-copper alloys; in some cases modified by the introduction of zinc to improve the casting properties and to alter the color, and nickel to increase the strength. The properties of the Au-Ag-Cu system have been the subject of a very thorough investigation by Jänecke,l Sterner-Rainer12 and Carter."

Jan 1, 1929

By H. B. Pulsifer

This paper outlines a method for rapid production of flat,, granular surfaces on many of the medium hard alloys. Grinding wheels and fabrics on wheels are not used; the purpose is accomplished by rubbing on emery papers and on fine abrasives heaped on hand boards. The advantages of chromic acid in the solutions for etching nickel and copper alloys are explained. Steels may require an additional step in the mechanical smoothing owing to the lack of an ideal etchant. Chloric acid is a rapid etchant for steel. Thirty-six photomicrographs illustrate the steps in smoothing and the clearness with which structures can be rapidly exposed. New structures in low-carbon steels are announced. After a little practice, many materials can be finished within two or three minutes. CUPRONICKELS In the previous papers on the metallography of copper and magnesiurn which the author has presented to this Institute there has been an attempt to demonstrate the advantages of minimizing the mechanical work of surfacing and depending more on chemical means; the present paper continues the research into a still wider field. It is obvious that the success of a chemical method for smoothing and etching depends almost entirely on the use of a suitable reagent. The etchant must remove the surface granulations and outline the structures. A very special type of reaction between reagent and metal must be displayed. Promiscuous corrosion or the intensification of the attack about local couples formed by impurities or components must not be in evidence. There are several reagents that etch highly polished nickel and copper alloys very well. Acidified ferric chloride solutions, concentrated and dilute nitric acid solutions, and nitric and acetic acids in acetone have been used to good advantage for the purpose. However, if they are expected to etch rather deeply—that is, smooth as well as characterize— the results may be far from satisfactory. Advantages of Chromic Acid In a protracted series of experiments it has been found that the addit,ion of chromic acid may be of the most surprising benefit. The function

Jan 1, 1929

By H. B. Pulsifer

This paper outlines a method for rapid production of flat,, granular surfaces on many of the medium hard alloys. Grinding wheels and fabrics on wheels are not used; the purpose is accomplished by rubbing on emery papers and on fine abrasives heaped on hand boards. The advantages of chromic acid in the solutions for etching nickel and copper alloys are explained. Steels may require an additional step in the mechanical smoothing owing to the lack of an ideal etchant. Chloric acid is a rapid etchant for steel. Thirty-six photomicrographs illustrate the steps in smoothing and the clearness with which structures can be rapidly exposed. New structures in low-carbon steels are announced. After a little practice, many materials can be finished within two or three minutes. CUPRONICKELS In the previous papers on the metallography of copper and magnesiurn which the author has presented to this Institute there has been an attempt to demonstrate the advantages of minimizing the mechanical work of surfacing and depending more on chemical means; the present paper continues the research into a still wider field. It is obvious that the success of a chemical method for smoothing and etching depends almost entirely on the use of a suitable reagent. The etchant must remove the surface granulations and outline the structures. A very special type of reaction between reagent and metal must be displayed. Promiscuous corrosion or the intensification of the attack about local couples formed by impurities or components must not be in evidence. There are several reagents that etch highly polished nickel and copper alloys very well. Acidified ferric chloride solutions, concentrated and dilute nitric acid solutions, and nitric and acetic acids in acetone have been used to good advantage for the purpose. However, if they are expected to etch rather deeply—that is, smooth as well as characterize— the results may be far from satisfactory. Advantages of Chromic Acid In a protracted series of experiments it has been found that the addit,ion of chromic acid may be of the most surprising benefit. The function

Jan 1, 1929

By A. J. Lyon

The stability and permanence of any structural material used in aircraft are of paramount importance. The spontaneous hardening, or age-hardening, which takes place in some of the aluminum alloys under ordinary conditions of temperature and atmosphere, is accompanied by an increase in tensile strength and proportional limit and a decrease in elongation or ductility. Within the last few years the introduction of a number of strong and ductile casting alloys led to a study by the Materiel Division, Air Corps, of the permanence of the physical properties in several of these alloys. It has been found that even though some alloys have good properties directly after casting or heat treatment, they are not satisfactory for stressed parts that require a combination of strength and ductility. It has also led to the conclusion that all alloys that can be hardened by artificial aging—heating in a temperature range below 170" C. (340" F.)—will harden spontaneously if allowed to stand for a sufficient length of time. It follows that, in aircraft work where the factors of safety are limited on account of the necessity of keeping the weight of the structures as low as possible consistent with their safe operation, the properties of the alloys in the stable or final condition should be used as a basis for design rather than the properties obtained on the material directly after casting. The work of Wilm in Germany, Hanson and Gayler at the National Physical Laboratory in England, and Merica, Jeffries, and others in the United States, has shown that the spontaneous hardening is characteristic to a greater or less extent in all aluminum-base alloys in which the solubility in the solid state of the alloying constituents decreases with the temperature. It has been shown that, by heating to a temperature as near as possible to the melting point of the material and soaking at that temperature for a sufficient length of time and then quenching or cooling rapidly, a maximum amount of the soluble constituents can be retained in solution and the condition of maximum hardening effect upon aging can be obtained. Also, in ordinary sand and chill castings, without heat treatment, a sufficient amount of the alloying constituents is held in solution to cause important changes in the final physical properties.

Jan 1, 1929

By A. J. Lyon

The stability and permanence of any structural material used in aircraft are of paramount importance. The spontaneous hardening, or age-hardening, which takes place in some of the aluminum alloys under ordinary conditions of temperature and atmosphere, is accompanied by an increase in tensile strength and proportional limit and a decrease in elongation or ductility. Within the last few years the introduction of a number of strong and ductile casting alloys led to a study by the Materiel Division, Air Corps, of the permanence of the physical properties in several of these alloys. It has been found that even though some alloys have good properties directly after casting or heat treatment, they are not satisfactory for stressed parts that require a combination of strength and ductility. It has also led to the conclusion that all alloys that can be hardened by artificial aging—heating in a temperature range below 170" C. (340" F.)—will harden spontaneously if allowed to stand for a sufficient length of time. It follows that, in aircraft work where the factors of safety are limited on account of the necessity of keeping the weight of the structures as low as possible consistent with their safe operation, the properties of the alloys in the stable or final condition should be used as a basis for design rather than the properties obtained on the material directly after casting. The work of Wilm in Germany, Hanson and Gayler at the National Physical Laboratory in England, and Merica, Jeffries, and others in the United States, has shown that the spontaneous hardening is characteristic to a greater or less extent in all aluminum-base alloys in which the solubility in the solid state of the alloying constituents decreases with the temperature. It has been shown that, by heating to a temperature as near as possible to the melting point of the material and soaking at that temperature for a sufficient length of time and then quenching or cooling rapidly, a maximum amount of the soluble constituents can be retained in solution and the condition of maximum hardening effect upon aging can be obtained. Also, in ordinary sand and chill castings, without heat treatment, a sufficient amount of the alloying constituents is held in solution to cause important changes in the final physical properties.

Jan 1, 1929

By Cyril Stanley Smith

IsolatEd alloys of copper and silicon were prepared and examined by chemical methods more than one hundred years ago, but it was not until the work of Rudolfi l that the equilibrium relations were studied. The early history of the alloys was well described by Baradue-Muller 2 and need not be further discussed here. The diagram of Rudolfi, based entirely on thermal observations, showed sillcon to be soluble in copper up to 4.5 per cent. at 849" C., at which temperature there was a peritectic horizontal resulting from the formation of a ß phase with about 7.4 per cent. silicon from a and liquid with 7.85 per cent. silicon. The ß phase was believed to form a eutectic with Cu3Si at 820" C. and 9.8 per

Jan 1, 1929

By Cyril Stanley Smith

IsolatEd alloys of copper and silicon were prepared and examined by chemical methods more than one hundred years ago, but it was not until the work of Rudolfi l that the equilibrium relations were studied. The early history of the alloys was well described by Baradue-Muller 2 and need not be further discussed here. The diagram of Rudolfi, based entirely on thermal observations, showed sillcon to be soluble in copper up to 4.5 per cent. at 849" C., at which temperature there was a peritectic horizontal resulting from the formation of a ß phase with about 7.4 per cent. silicon from a and liquid with 7.85 per cent. silicon. The ß phase was believed to form a eutectic with Cu3Si at 820" C. and 9.8 per

Jan 1, 1929

By John A. Gann

The following investigation constitutes a brief réumé of the more important binary magnesium alloys from the standpoint of metallo-graphic technique, and the effect of heat treatment on structure and properties. The comparative newness of the subject justifies this procedure as a preface to a more detailed study of each individual series of alloys. The work was started with the idea of practical application in the industry rather than as a theoretical investigation. The alloy compositions studied were selected as those most likely to show whether heat treatment would produce beneficial results. Furthermore, it was considered satisfactory to use commercial 99.9 per cent. magnesium, the best commercial grade of alloying ingredients, and to limit the time of heat treatment at the expense of incomplete equilibrium. These facts must be kept in mind when examining the results obtained, and the conclusions drawn. Preparation of Alloys All melts were made in an oil-fired cast-steel pot, approximately 12 in. dia, by 12 in. deep. Approximately 15 lb. of flux and 50 lb. of magnesium were melted and the calculated amount of alloying metal was added. After thorough alloying and puddling, the metal was chill cast in a graphite mold with four 1/2 by 1/2 by 4 in. bars fed from a common sprue and runner. The next higher composition alloy in a given series was made by adding the calculated amount of metal to the heel from the preceding cast. The pot was thoroughly cleaned after each series and new flux then introduced, thus avoiding possible contamination from earlier melts. The percentage compositions given in Table 1 are the calculated values. While not all alloys were analyzed, enough were checked to indicate that the reported compositions are correct to a few tenths of one per cent. A more detailed description of the foundry methods employed has been given in a previous paper. 1

Jan 1, 1929

By John A. Gann

The following investigation constitutes a brief réumé of the more important binary magnesium alloys from the standpoint of metallo-graphic technique, and the effect of heat treatment on structure and properties. The comparative newness of the subject justifies this procedure as a preface to a more detailed study of each individual series of alloys. The work was started with the idea of practical application in the industry rather than as a theoretical investigation. The alloy compositions studied were selected as those most likely to show whether heat treatment would produce beneficial results. Furthermore, it was considered satisfactory to use commercial 99.9 per cent. magnesium, the best commercial grade of alloying ingredients, and to limit the time of heat treatment at the expense of incomplete equilibrium. These facts must be kept in mind when examining the results obtained, and the conclusions drawn. Preparation of Alloys All melts were made in an oil-fired cast-steel pot, approximately 12 in. dia, by 12 in. deep. Approximately 15 lb. of flux and 50 lb. of magnesium were melted and the calculated amount of alloying metal was added. After thorough alloying and puddling, the metal was chill cast in a graphite mold with four 1/2 by 1/2 by 4 in. bars fed from a common sprue and runner. The next higher composition alloy in a given series was made by adding the calculated amount of metal to the heel from the preceding cast. The pot was thoroughly cleaned after each series and new flux then introduced, thus avoiding possible contamination from earlier melts. The percentage compositions given in Table 1 are the calculated values. While not all alloys were analyzed, enough were checked to indicate that the reported compositions are correct to a few tenths of one per cent. A more detailed description of the foundry methods employed has been given in a previous paper. 1

Jan 1, 1929

By H. K. Work

The Bessemer process is one of the most interesting methods of making steel. At one time it was by far the most important. In recent years, however, it has steadily lost ground to the open-hearth process. The forces working against this method of stccl-making are partly economic and partly metallurgical.1 In this paper, dealing as it does with the control of the process, the metallurgical factors alone will be considered, although it is obvious that economic factors must play a part in determining the ultimate status of the Bessemer process. This discussion has been limited in another respect—it deals primarily with the acid Bessemer process in bottom-blown converters, although much of the information is applicable to basic and side-blown converters. The fact that open-hearth steel has superseded Ressemer steel to a large extent has tended to create an impression that Bessemer steel is inferior. As a matter of fact, Bessemer steel is actually superior to open-hearth for many applications.2 There are, however, definite metallurgical limitations to the use of Bessemer steel, resulting largely from two factors: (1) the physical properties conferred by nitrogen and phosphorus, and (2) the variability from blow to blow. These, of course, are not entirely independent, since some of the variability covered in the second item is undoubtedly due to nitrogen. But the variability is also caused by other factors. One of these is the relatively small size of the Bessemer heats. Because of this, a given shipment of Bessemer steel is more likely than a shipment of open-hearth steel to contain the product of several heats, each with its own distinctive and slightly different characteristics. Added to this is the fact that the refining of Bessemer steel proceeds so rapidly that the timing of the end point is limited to a matter of seconds, whereas the finishing period in the open hearth extends over a period of one or two hours and the timing of the end point may vary by several minutes without seriously affecting the product. There is no doubt that this has contributed to the variability of Bessemer steel and has led to the use of open-hearth steel in many optional applications. That Bessemer steel may vary is not necessarily objectionable, and it may even prove an advantage, providing a precise control is available to secure the desired qualities for any specific application. With this in mind, a comprehensive research program was undertaken, one phase of which was directed toward securing more accurate control of the blow. The results have been encouraging, and it is the purpose of this paper to describe a method in which modern scientific instruments, based on photocells, are currently being employed to assist the blower. The Control Problem In this day of scientific control of technical processes, where the operating

Jan 1, 1941

By H. K. Work

The Bessemer process is one of the most interesting methods of making steel. At one time it was by far the most important. In recent years, however, it has steadily lost ground to the open-hearth process. The forces working against this method of stccl-making are partly economic and partly metallurgical.1 In this paper, dealing as it does with the control of the process, the metallurgical factors alone will be considered, although it is obvious that economic factors must play a part in determining the ultimate status of the Bessemer process. This discussion has been limited in another respect—it deals primarily with the acid Bessemer process in bottom-blown converters, although much of the information is applicable to basic and side-blown converters. The fact that open-hearth steel has superseded Ressemer steel to a large extent has tended to create an impression that Bessemer steel is inferior. As a matter of fact, Bessemer steel is actually superior to open-hearth for many applications.2 There are, however, definite metallurgical limitations to the use of Bessemer steel, resulting largely from two factors: (1) the physical properties conferred by nitrogen and phosphorus, and (2) the variability from blow to blow. These, of course, are not entirely independent, since some of the variability covered in the second item is undoubtedly due to nitrogen. But the variability is also caused by other factors. One of these is the relatively small size of the Bessemer heats. Because of this, a given shipment of Bessemer steel is more likely than a shipment of open-hearth steel to contain the product of several heats, each with its own distinctive and slightly different characteristics. Added to this is the fact that the refining of Bessemer steel proceeds so rapidly that the timing of the end point is limited to a matter of seconds, whereas the finishing period in the open hearth extends over a period of one or two hours and the timing of the end point may vary by several minutes without seriously affecting the product. There is no doubt that this has contributed to the variability of Bessemer steel and has led to the use of open-hearth steel in many optional applications. That Bessemer steel may vary is not necessarily objectionable, and it may even prove an advantage, providing a precise control is available to secure the desired qualities for any specific application. With this in mind, a comprehensive research program was undertaken, one phase of which was directed toward securing more accurate control of the blow. The results have been encouraging, and it is the purpose of this paper to describe a method in which modern scientific instruments, based on photocells, are currently being employed to assist the blower. The Control Problem In this day of scientific control of technical processes, where the operating

Jan 1, 1941

By David Sinclair, Philip B. Bucky

The dimensions and shapes of mine structures may at present be determined by (1) field experience, (2) structural calculations, and (3) barodynamic tests. § None of these, however, provide information as to the stresses, their direction and distribution in a mine structure. For the design of pillars, the placing of openings relative to working places such as gangways, haulage levels, etc., this information is desirable. Photoelastic methods provide this and, while relatively new, their application in all engineering fields is assuming increasing importance. This paper, therefore, will present the method with a few applications to mining, and with sufficient reference for further study by the reader. PART I The Photoelastic Method The photoelastic method of stress measurement determines the stress distribution in a two-dimensional model by optical means. It makes use of the fact that when a piece of isotropic transparent material, such as glass, celluloid, or Bakelite, is stressed and viewed in polarized** light a picture is seen which indicates by its color bands of light, or fringes, the magnitude of the stresses, their direction and their distribution. General Explanation The stress at any point 0 in a structure (Fig. I), may be resolved into two components, P and Q, each a pure tension or compression, at right angles to each other, called principal stresses.' To fully identify the stress, the values of P and Q and their directions or angle F must be known.

Jan 1, 1940

By David Sinclair, Philip B. Bucky

The dimensions and shapes of mine structures may at present be determined by (1) field experience, (2) structural calculations, and (3) barodynamic tests. § None of these, however, provide information as to the stresses, their direction and distribution in a mine structure. For the design of pillars, the placing of openings relative to working places such as gangways, haulage levels, etc., this information is desirable. Photoelastic methods provide this and, while relatively new, their application in all engineering fields is assuming increasing importance. This paper, therefore, will present the method with a few applications to mining, and with sufficient reference for further study by the reader. PART I The Photoelastic Method The photoelastic method of stress measurement determines the stress distribution in a two-dimensional model by optical means. It makes use of the fact that when a piece of isotropic transparent material, such as glass, celluloid, or Bakelite, is stressed and viewed in polarized** light a picture is seen which indicates by its color bands of light, or fringes, the magnitude of the stresses, their direction and their distribution. General Explanation The stress at any point 0 in a structure (Fig. I), may be resolved into two components, P and Q, each a pure tension or compression, at right angles to each other, called principal stresses.' To fully identify the stress, the values of P and Q and their directions or angle F must be known.

Jan 1, 1940