Search Documents

By D. T. Goettge, E. L. Robinson

The phase changes occurring in low carbon steel during hot strip mill rolling are shown to be metallurgically significant when related to commonly used temperature control points, particularly finishing and coiling temperatures. In combination, these temperatures are shown to have an important influence on the level and uniformity of hardness, grain size, and carbide characteristics of the finished hot and cold rolled sheets. PRODUCTION of wide flat-rolled products ordinarily requires a number of operations in sequence to prepare the material for shipment to the customer. Most products are tailor-made for specific end uses, with each operation contributing certain properties to the finished material. Since the characteristics imparted to the semifinished product by a given step in processing carry through to the finished product in varying degrees, it is important that the intermediate stages of production of flat-rolled strip be carried out with the same care which characterizes the last or finishing operations. The step of hot strip mill rolling is common to the production of all of the various types of flat-rolled product; therefore, the hot strip rolling is an especially important point at which to recognize and control those variables which have an effect on the surface characteristics and metallurgical properties of the finished product and which influence the ease of conducting subsequent operations. Orders entered at a producing mill usually show an end use or describe an article or part into which the ordered product is to be fabricated. Applying his experience as to the properties necessary in a finished sheet to suit the end use and to perform successfully in the fabrication involved, the metallurgist selects a steel of suitable composition and deoxidation practice, and slabs of appropriate dimensions are produced for rolling on the hot strip mill. At this stage of processing, the metallurgist faces the problem of controlling hot strip mill practice in the light of his diagnosis of the properties necessary to meet the end use, paying due attention to the accompanying problem of producing a strip which can meet processing requirements on subsequent units in the mill. It is the purpose of this paper to describe some of the factors which he must consider in solving these problems and to indicate some of the principles which guide him. Equipment, Physical Requirements of the Strip, and Temperature Measurement The metallurgist must, of course, be familiar with the physical layout of the mill, the temperature-measuring equipment available, and the physical requirements of the hot strip product before he can apply his metallurgical knowledge to the problem; hence, the first section will consist of a brief discussion of these matters. The usual hot strip mill consists of reheating furnaces, five or six roughing stands including a scale-breaker, holding table, and second scalebreaker, six-stand finishing mill, runout table with spray cooling facilities, and coilers. A schematic diagram of a typical layout is shown in Fig. 1. Slab temperatures are primarily a function of heating time and furnace temperatures, while mill speeds, spray practice, drafting practice, available water pressure, temperature of the cooling water, cross sectional dimensions of the strip, coil size, and equipment limitations, either singly or in combination, determine what rolling temperatures are practical on a given hot strip mill unit. Thus, it is possible that a set of temperatures which can be utilized successfully on one mill cannot be used on another. However, adjustments in temperatures and rolling practice can usually be made to develop the desired metallurgical properties. In addition to the metallurgical properties developed through proper temperature control, the hot strip mill must also provide strip with certain physical attributes which may be summarized as follows: Strip Cross Section—The strip contour should conform to a section which will give the best results in the cold reduction operation. This is generally recognized as a strip with 0.001 to 0.003 in. crown or shoulder-to-shoulder convexity depending on width, and freedom from concave, flat, or wedge-shaped cross sections which cause metal buildup in cold reduction. Excessive drop off in thickness at the edges can also be very detrimental in cold reducing to light gages. Gage, Width, and Camber—All of these must be controlled. For example, rundown or increasing thickness from the front to the back of the coil results in nonuniformity in the thickness of hot-rolled sheet product and in added difficulty with gage and welds in cold reduction. Similarly, excessive width variation is the cause of guide trouble and excessive edge scrap at later stages of processing, while excessive camber is the source of a variety of processing troubles. Type of Oxide—Product intended for pickling should have a predominance of the type of oxide most easily removable in sulfuric acid. It is generally recognized that this type is obtained by use of maximum table cooling water and cold coiling

Jan 1, 1957

By D. J. Carney, E. Van Meter, J. J. Oravec

A study was made of combustion-air temperatures and factors affecting air temperatures in the open-hearth regenerative systems. Air-temperature surveys in the regenerative system revealed marked thermal gradients in the air above the checkers. The design of the fantail-uptake region plays a prominent part in increasing the heat recovery of the regenerative system. THE efficiency of the open-hearth regenerative system is one of the most important factors affecting open-hearth performance. Until recently, this factor has not received the attention in the literature given to many other items affecting performance, such as the type of charge, speed of charging, and the mechanical equipment of the open hearth. J. S. Marsh' emphasized the importance of the flame temperature and its dependence upon the combustion-air temperature. By means of measured air temperatures in open-hearth furnaces, data were presented which showed a remarkable degree of correlation between production rate and combustion-air temperature. This correlation was extremely good in view of the numerous factors, other than air temperature, which affect open-hearth production rates. In Marsh's work, a 100°F increase in air temperature reduced the heat time by approximately 45 min. Realizing the importance of combustion-air temperature, it is desirable to know which factors control the regenerative efficiency of the open-hearth furnace. B. M. Larsen recently discussed this subject.' The present paper illustrates a few of the more important items that affect regenerative efficiency and combustion-air temperature. In the latter part of 1951, a study of open-hearth combustion-air temperatures was begun at the South Works of the United States Steel Corp. In the initial work at open-hearth shop X, which produces low carbon steel products, temperatures were measured in the uptake in a manner similar to that used by Marsh' and the results obtained were very similar to the Bethlehem data. When it was decided to expand the study of combustion-air temperatures, open-hearth shop Y was selected because of the greater variety of furnace-design features, types of steel produced, and firing rates used. With the use of aspirating thermocouples, continuous gas analyzers, thermocouple and optical pyrometers, a study was made of: 1—effect of combustion-air temperature on open-hearth production rate, 2—thermal gradients present in various zones of the regenerative system, 3—effect of furnace-design variations on air temperature and heat recovery, 4-—effect of furnace-operating variables on heat recovery, and 5—variation in heat recovery with furnace age during the normal furnace campaign. Data collected on individual heats at 15 min intervals included air-flow rate, firing rate, checker temperature, combustion-air temperature, and furnace pressure. These data were collected on approximately 230 heats of steel. In addition, information was obtained at random on air infiltration and combustion-gas compositions. The data gathered have shown the desirability of closer control of open-hearth firing practices, a need for reducing air infiltration in the uptake zones, and a need for further study of design of checkers and of uptake-fantail areas. Equipment Air is practically a nonradiating medium. Consequently, in the measurement of air temperatures, the principle of heat conduction must be used rather than heat radiation. For this reason, aspirating-type thermocouple pyrometers normally are used to measure air temperatures. With these devices, air

Jan 1, 1956

By G. R. Fitterer

Trends in slag composition in acid open hearth practice, particularly the variation in iron and manganese oxides during refining, are reviewed. A procedure which is currently being used to control the refining reactions is described and partially explained through slag phase diagram considerations. In addition, the ionic nature of these slags is considered and it is proposed that silica combines with the oxide ion and forms a series of complex silicate ions. The effect of basic oxides such as FeO, MnO, and CaO is apparently additive in furnishing the oxide ion for this purpose. IT is now possible to control192 the refining of steel in an acid open hearth furnace to a surprising degree. This control has been brought about through the knowledge and use of several facts and tests. These are: 1—A planned charge analysis based on a knowledge of the type of fuel, the bath depth, etc. 2—Knowledge and control of rate of fuel input as well as its method of atomization, if any. 3—Determination of the slag fluidity. 4—Bath temperatures (use of the Pt-Pt-Rh thermocouple). 5—Periodic determination of carbon content (use of the Carb-analyzer or Carbometer). Through the use of these control methods, a heat may be made to "melt-in" with or without residual manganese and silicon. The rate of refining or carbon elimination may be controlled accurately, and the desired tapping (or "go-ahead") carbon may be approached at a rapid or slow rate according to preference and type of steel being made. Thus operating time may be predetermined and greatly reduced. Further, all of the refining can be done without any ore or other oxidizing additions, and the heat may be brought to the desired tapping temperature simultaneously with the attainment of the desired carbon analysis. This control procedure is being used in most acid plants in the United States today and has been de- scribed.', ' Although the slag metal relations are sufficiently well known to control the heat as stated, yet it is possible to account for only about two-thirds' of the 0, which must have been used for the elimination of the carbon and other metalloids. Phase diagram studies' of the slags, slag weights, the metal particle theory,' ore additions, limestone additions, etc., may all be taken into consideration; yet, the mechanism of oxidation and source of all the oxygen remain to be explained. This paper reviews some of the principles upon which the control methods were based and proposes other possibilities regarding the unexplained phenomena. Old and New Acid Open Hearth Practice Some of the recent statements in the literature regarding acid open hearth operation are based on old heat data which are not typical of modern American practice. These old heat logs have been responsible for many misconceptions regarding the acid hearth practice and represent heats which do not coincide with modern methods. In recent years, American practice has been altered materially and these changes will be briefly described. Modern American Practice: A typical log of a modern American acid open hearth heat' is shown in Fig. 1 which indicates that the refining time was only two hours, during which the carbon was eliminated rapidly and the bath temperature increased at a fast rate. The manganese and silicon contents of the metal were essentially eliminated and their oxides had become constituent parts of the slag at the "melt-down" period. During the course of the heat, the MnO content of the slag remained practi-

Jan 1, 1954

By Arnlf Muan, Bert Phillips

The quenching technique has been used for- a study of phase velntiorzs within the composition triangle 2CaO.Fe2O3-FeO.Fe2O3 Fe2O3 of the system Ca-Fe-O. Desired total compositions of sanzples were attained by weighing of starting materials in required proportions and keeping them in sealed 80 pct Pt 20 pct Rh tubes during equilibration .runs. The liquidus surface has been delineated. the existence of two ternary compounds has been established, and seven ternary inwariant situations have been determined. ONE unit within the research program on refractory oxides in progress in our laboratories is the study of phase relations in the system Ca-Fe-Si-O. The present paper deals with the ternary system 2CaOFe2O3-FeO.Fe2O3-Fe2O3, which is only a small part of the enormously complex quaternary system. Many of the phases occurring in iron ore sinter products have compositions which can be closely approximated within this ternary system, and a knowledge of stability relations existing among these phases may be expected to be a useful guide for improving sintering operations. Two fundamentally different experimental approach es are commonly used in studies of systems containing iron oxides, both permitting control of the oxidation state of Fe. One method consists in keeping constant the oxygen partial pressure of the gas phase in equilibrium with condensed phases (liquid and crystalline). In the other method, which is the one used in the present investigation, the total composition of condensed phases is kept essentially constant by keeping the samples in a gas-tight container. The details of this experimental procedure will be described in a later section. PREVIOUS WORK Extensive studies of phase relations in the bounding binary system FeOFe2O3-Fe2O3 have been reported by Greig, Posnjak, Merwin, and Sosman,' by Darken and Gurry,2, 3 and recently by Phillips and Muan.4 A diagram summarizing the results of these studies is shown in Fig. 1. Particular attention is

Jan 1, 1961

By M. V. Nevitt

In the systems Ti-Mn-O, Ti-Fe-O, Ti-Co-O, and Ti-Ni-O the bounda.r-ies of the Ti2Ni-type phases were determined at one or more temperatures and the variation of the lattice parameter with oxygen content was determined. Densities were calculated from the lattice parameters and compared with measured density values. The: results indicate that the occurrence of the phase in these systesms can be correlated qualitatively with valency electron concentration, and that the role of oxygen is that of an electron acceptor. The lower limit of oxygen solubility appears to be determined by the valencies of Mn, Fe, Co, and Ni, while the maximum oxygen concentration coincides with the filling of the 16 (c) positions of the O 7h - Fd 3m space group. THE suggestion has been made by several investigators'" that the phases having the cubic E9,-type structure, and known as 17-carbide-type, double-carbide-type and Ti,Ni-type, are members of a family of electron compounds. This concept has been given additional support by recent work8 in which new isostructural phases involving second and third long period combinations were found, and which provided further evidence of the regularity of occurrence of the phase in terms of periodic table relationships. In this laboratory attention has been focused on the isomorphs containing titanium, zirconium, or hafnium, and the role that oxygen plays in their occurrence. In some binary systems Ti,Nitype* phases occur having the formula A,B where A is the titanium group element. Based on previous workq and the present investigation, oxygen is known to be soluble in two of these binary phases, Ti,Co and Ti2Ni. It is probable that oxygen is also soluble in the other phases of this kind. In other binary systems the Ti,Ni-type phase does not occur, but does occur in the corresponding ternary systems with oxygen .3-5 The experiments described here were performed to determine whether the occurrence and composition of certain of the Ti,Ni-type phases could be related to an electronic effect and whether oxygen's stabilizing role is exerted through an influence on the electron: atom ratio. The ternary systems Ti-Mn-O, Ti-Fe-O, n-Co-O, and Ti-Ni-O were selected for study for two reasons: First, several schemes have been proposed for first long period elements which, although not in quantitative agreement, show a generally consistent trend for the variation of valency with atomic number. Although for a transition metal the term valency is difficult to define and is generally not a constant number which can be applied to all alloys, it is usually assumed to be an index of the number of electrons per atom involved in metallic cohesion. Second, the determination of the Ti2Ni-type phase boundaries was facilitated by the fact that the phase relations in several of these ternary systems have been investigated by other workers."' EXPERIMENTAL PROCEDURE___________________ The alloys were prepared by arc melting crystal-bar titanium, reagent grade TiO, and electrolytic manganese, iron, cobalt, and nickel. Each button was remelted at least three times. The metals had a minimum purity of 99.9 pct except the nickel whose purity was 99.4 pct, the major impurity in this instance being cobalt. The preparation of the manganese alloys was attended by the customary difficulties associated with the vaporization of manganese. The technique used in this case was to add approximately 10 pct extra manganese to the original charge and to continue remelting the button until the final weight was in agreement with its intended weight. At least three alloys in each system were analyzed chemically and the results, even for the manganese alloys, were in good agreement with the intended compositions. A few additional alloys in the Ti-Mn-O system were prepared by the sintering of mixed powders in evacuated quartz tubes followed in some cases by arc melting. For annealing, the alloys were wrapped in molybdenum foil and placed in fused silica tubes containing zirconium chips. The fused silica tubes were evacuated at room temperature to a pressure of 1 x l0-6 mm of Hg and sealed. These capsules were then annealed for 72 hr at an external pressure of 5 x 10-5 mm of Hg in a vacuum furnace whose temperature could be controlled to + 1°C. The success of this procedure in avoiding significant oxygen or nitrogen pickup was indicated by the bright, ductile condition of the molybdenum foil and by the complete absence of a microscopic reaction layer on the specimens. This method did not permit rapid quenching of the specimens but in no case did metal-lographic examination indicate that a solid-state transformation had occurred on cooling. Metallo-

Jan 1, 1961

By C. D. King

DURING the 30-year period spanned by these annual Howe Memorial presentations, many lecturers could proudly claim a kinship either as a student or an associate of the man whose memory we honor. Although it has been my good fortune to have attended many of these annual lectures, it was not my privilege to have known Henry Marion Howe personally. However, his great repute as teacher and scientist was known to all undergraduates of my day and the later years have enhanced my appreciation of his wisdom and foresight. Those who knew him well have said he derived particular pleasure from speculations on the future world of metallurgy. For this reason, I feel that perhaps he would not be unsympathetic to a lecture in his honor which departs from the highly instructive scientific presentations made in the past by so many able Howe Memorial lecturers, and which is concerned more with the practical phases of various steelmak-ing processes and some speculations on their future form and relative importance. The word "revolutionary" is frequently applied to each seemingly important improvement in the production of steel ingots, but in retrospect these changes, impressive as they appear at the time, are merely steps of progress. In the hundred years from the inception of tonnage steelmaking, only three processes can be truly classified as revolutionary. They are the pneumatic process, known in this country as the bessemer process; the reverberatory method called the open hearth process; and, the electric furnace process. There have been many variations and combinations of the three fundamental methods, but they remain truly the only revolutionary methods in steelmaking since its early history. Everything else has been evolutionary, in effect. doing the same things that we have done in the past but doing them better, correcting our errors through experience, and slowly but inevitably reaching a higher state of accomplishment. It has often been said that coming events cast their shadows before, and the production of steel ingots is no exception. As a result of the unrelenting demands of World War I1 and the years that followed, truly impressive progress has been made in steel ingot production. The incessant pressure for immediate results during this period required the employment of initiative and daring, as in few past decades, and many developments were brought to fruition. Of equal importance is the possible effect on future steelmaking methods of the many ideas initiated but still in formative stages. Fig. 1 portrays ingot production in the United States by the three fundamental processes over a period of 75 years and is interesting because it poses some questions as to future trends. The early ascendancy of the bessemer, its replacement in importance by the open hearth process, the amazing growth of the latter, and the recent challenge of the electric furnace are evident from the chart. Management is fully aware of these changes, but is even more interested in the future trends. Our concepts of the relative importance of the more recent developments and their possible effect on future processes may perhaps be best exemplified by a specific, hypothetical problem. Let us assume management is contemplating a new ingot producing plant with an output of 100,000 net tons per month, located in an area where some purchased scrap may be obtained but where by far the largest component will be own-produced blast furnace iron. Management requires a process or combination of processes which will yield highly uniform quality characteristics in the ingot form, and represent the soundest selection in investment and operating cost. Under these conditions, the obvious selection for the past four decades has been the open hearth process but, in view of more recent developments, management may believe that it is no longer permissible to disregard other possibilities with impunity. Accordingly, to be assured of the best possible selection, they request that you review not only the possibilities of utilizing the conventional open hearth, duplex, bessemer, and electric furnace methods, but also the more recent developments, such as the turbo-hearth, the Linz-Donawitz method, the Perrin modifications, and other possibilities. With this background, one might then appraise the relative importance of these methods to meet a specific need, and concurrently speculate on the forms that future ingot processes will assume and the relative importance of these processes.

Jan 1, 1955

By G. Sachs, A. W. Dana, C. C. Chow

A great number of the investigations on the plastic flow of metals have been concerned with the establishment of a "universal" stress-strain relation. In such a relation some stress function when plotted against a strain function should yield identical curves for the various stress states. In the first investigation of this type, Ludwik and Scheu1 plotted the maximum shearing stress as a function of the maximum principal strain. Later Ros and Eichinger2 introduced two universal stress-strain relations, the one relating the maximum shearing stress to the maximum shearing strain, and the other relating a stress invariant, suggested by von Mises and Haigh, to the corresponding strain invariant. (In more recent investigations the stress and strain invariants are frequently supplemented with some factor to render their meaning more lucid.) A further suggestion which has not attracted appreciable attention is that by Baranski³ who used stress and strain deviators. The most common means of experimentation to determine the relation between stress and strain consists in subjecting thin walled tubes to combined internal pressure and axial tension.4a,4b,4c This method allows the study of plastic flow under stresses which are variable in two directions. However, the plastic flow which can be obtained in this manner is comparatively small, being limited by either tension failure or instability. For copper,'. only the relation between maximum shearing stress and maximum shearing strain yielded good agreement. On the other hand, tests on a stee14b and on an aluminum alloy4c. resulted in systematic deviations if any of the discussed universal stress-strain relations were used. It would seem, therefore, that the agreement mentioned above for copper is only incidental and explained by its high rate of strain hardening compared to that of other metals. Much larger strains than experienced in the tube tests can be obtained by subjecting a thin membrane of a ductile metal, which is restrained at its periphery, to a uniform hydraulic pressure. The thin sheet forms a deep bulge before it fails. The stresses and strains in such a bulge increase with increasing distance from the edge of the clamping "die," the maximum stresses and strains occurring at the pole (crown) of the bulge. While the stress and strain states are determined by the contour of the bulge, the absolute magnitude of the stresses and strains depends upon the hydraulic pressure. The bulge contour is in turn correlated with the geometry of the die opening. The deformation and fracture characteristics of circular bulges, that is, bulges formed with circular clamping dies, have been the subject of numerous experimental and analytical investi-gations.5,6,7 It has been shown that plastically deformed circular bulges develop large and comparatively uniform strains before failure by instability"6b,6c,6d and closely assume a spherical shape.6d Also the distribution of strains across the contour of the bulge is dependent on the metal being investigated and is correlated with, but cannot be predicted from, the metal's stress-strain characteristics. On the other hand, oblong or elliptical bulges, that is, bulges formed with elliptical clamping dies, are not as susceptible to analytical analysis and have not been investigated to the extent that circular bulges have. The few available data6c,7c indicate that stress states are obtained at the poles of the bulges, varying between plane strain and balanced biaxial tension, depending upon the geometry of the die opening. In this paper, the strain state and curvatures exhibited by three bulge shapes, a circular and two elliptical bulges, Fig 1, are analyzed experimentally using methods described in previous publications.6a,6c An attempt is made to derive the stress-strain relations for these bulges, which represent strain states in which the ratio of the two positive principal strains varied between 1.0 and 0.35. In addition, tension tests yielded data for a value of —0.5 for this strain ratio. Such an analysis should indicate the applicability of the various laws correlating stress with strain to the stress and strain states occurring in bulged shapes. Definitions and Nomenclature The definitions of the major stress and strain quantities used in this paper are as follows: s1, s2, s3 = principal normal stresses Sl > s2 > S3 t = shear stress e = conventional (unit) strain e = In (1 + e) El, E2, E3 = principal natural strains 7 = shear strain The maximum shear stress: , _ S1 — S3 lmax = 2 Frequently, the flow stress, s1 — s3 = 2lmax rather than the maximum shear stress is used.

Jan 1, 1950

By John Henderson

FOR some time now the most commonly accepted description of liquid silicate structure has been the "discrete ion" theory, proposed originally by Bockris and owe.' This theory is that when certain metal oxides and silica are melted together, the continuous three dimensional silica lattice is broken down into large anionic groups, such as sheets, chains, and rings, to form a liquid containing these complex anions and simple cations. Each composition is characterized by "an equilibrium mixture of two or more of the discrete ions",' and increasing metal oxide content causes a decrease in ion size. The implication is, and this implication has received tacit approval from subsequent workers, that these anions are rigid structures and that once formed they are quite stable. The discrete ion theory has been found to fit the results of the great majority of structural studies, but in a few areas it is not entirely satisfactory. For example it does not explain clearly the effect of temperature on melt structure,3 nor does it allow for free oxygen ions over wide composition ranges, the occurrence of which has been postulated to explain sulfur4 and water5 solubility in liquid silicates. In lime-silica-alumina melts the discrete ion theory is even less satisfactory, and in particular the apparent difference in the mechanism of transport of calcium in electrical conduction8 and self-diffusion,' and the mechanism of the self-diffusion of oxygen8 are very difficult to explain on this basis. By looking at melt structure in a slightly different way, however, a model emerges that does not pose these problems. It has been suggested5" that at each composition in a liquid silicate, there is a distribution of anion sizes; thus the dominant anionic species might be Si3,O9 but as well as these anions the melt may contain say sis0:i anions. Decreasing silica content and increasing temperature are said9 to reduce the size of the dominant species. Taking this concept further, it is now suggested that these complexes are not the rigid, stable entities originally envisaged, but rather that they exist on a time-average basis. In this way large groups are continually decaying to smaller groups and small groups reforming to larger groups. The most complete transport data 8-10 available are for a melt containing 40 wt pct CaO, 40 wt pct SiO2, and 20 wt pct Al2O3. Recalculating this composition in terms of ion fractions and bearing in mind the relative sizes of the constituent ions, Table I, it seems reasonable to regard this liquid as almost close packed oxygens, containing the other ions interstitially, in which regions of local order exist. On this basis, all oxygen positions are equivalent and, since an oxygen is always adjacent to other oxygens, its diffusion occurs by successive small movements, in a cooperative manner, in accord with modern liquid theories." Silicon diffusion is much less favorable, firstly because there are fewer positions into which it can move and secondly, because it has the rather rigid restriction that it always tends to be co-ordinated with four oxygens. Silicon self-diffusion is therefore probably best regarded as being effected by the decay and reformation of anionic groups or, in other words, by the redistribution of regions of local order. Calcium self-diffusion should occur more readily than silicon, because its co-ordination requirements are not as stringent, but not as readily as oxygen, because there are fewer positions into which it can move. There is the further restriction that electrical neutrality must be maintained, hence calcium diffusion should be regarded as the process providing for electrical neutrality in the redistribution of regions of local order. That is, silicon and calcium self-diffusion occur, basically, by the same process. Aluminum self-diffusivity should be somewhere between calcium and silicon because, for reasons discussed elsewhere,' part of the aluminum is equivalent to calcium and part equivalent to silicon. Consider now self-diffusion as a rate process. The simplest equation is: D = Do exp (-E/RT) [I] This equation can be restated in much more explicit forms but neither the accuracy of the available data, nor the present state of knowledge of rate theory as applied to liquids justifies any degree of sophistication. Nevertheless the terms of Eq. [I] do have significance;12 Do is related, however loose this relationship may be, to the frequency with which reacting species are in favorable positions to diffuse, and E is an indication of the energy barrier that must be overcome to allow diffusion to proceed. For the 40 wt pct CaO, 40 wt pct SiO2, 20 wt pct Al2O3, melt, the apparent activation energies for self-diffusion of calcium, silicon, and aluminum are not significantly different from 70 kcal per mole of diffusate,' in agreement with the postulate that these elements diffuse by the same process. For oxygen self-diffusion E is about 85 kcal per mole,' again in agreement with the idea that oxygen is transported,

Jan 1, 1963

By Gordon H. Geiger, J. Bruce Wagner

Electrical conductavity and therrnoelectvic nzeasuretnents on synthetic hematite slabs with 0.01 to 0.90 at. pet Ti and with 0.30 at. pet Ca were made. Additions of titanium and of calcium both increased the electronic conductivity with titanium yielding greater n-type behavior and calciurn p-type behavior. Reduction studies of hematite to magnetite in CO-CO2 atmospheres between 600° and 900°C initially exhibited linear kinetics. These linear rates were increased by additions of titanium and decreased by calcium. IN recent years many studies have been reported in the literature on the kinetics of the reduction of hematite and magnetite to iron. In addition, Hansen and Josephl and Schenck and Schultz2 have reported studies on the reduction of hematite to magnetite, the first step in total reduction to iron. In order to evaluate the results of the studies of over-all reduction in terms of the actual mechanism of the reaction and to define further the important factors in the rate- controlling mechanism of the magnetic roasting reaction, the following experiments were undertaken. Specimens of undoped hematite and hematite containing titanium or calcium in solution as doping agents were reduced to magnetite in CO-CO2 mixtures. In addition, electrical-conductivity measurements were correlated with the reduction kinetics using concepts of defect solid-state chemistry. EXPERIMENTAL Fisher certified Fe2O3 powder was used to make specimens for both the electrical and kinetic studies (see Table I for analysis). Doping with titanium and calcium was accomplished by adding TiO2 and CaO powders to the Fe2O3 powder. The powders were mixed in a Waring blender for minimum times of 1/2 hr. Satisfactory blending was achieved based on comparison of analyses of individual specimens af- ter reduction. The specimens were formed in a steel die using opposed punches with a rectangular opening 10.0 by 40.0 mm. The Fe2O3-TiO, platelets were pressed cold at 16,000 psi. They were sintered for approximately 16 hr at 1075°C in air, in accordance with information in the literature3, 4 on the time and temperature needed to obtain solution of the titanium in the hematite. The Fe2O3-CaO mixtures were first cold-pressed at 20,000 psi and sintered for 3 hr at 1225°C to insure solution of CaO. This material was then ground to -325 mesh in a 6-in. ball mill and the resulting powder was used to make platelets in the same manner as above. The sintered platelets were usually between 1/16 and 1/8 in. thick. They were ground on a carborundum wheel and polished on 2/0 paper. Typical dimensions of the kinetic-study specimens were 1.6 by 0.8 by 0.05 cm, and a typical weight was 0.3 g. Conductivity and thermoelectric specimens were approximately the same size, but were subjected to further sintering in order to ensure maximum densification. Finally, all specimens were measured to the nearest 0.0005 in. and weighed on a Mettler H-15 balance to the nearest 0.0001 g and the density calculated. The average density of the specimens used for the reduction studies was 4.87 g per cc, or 7.1 pet total porosity. The standard deviation ranged from 0.14 to 0.063 g per cc within a composition group. In the present study, the apparent surface area as measured with a micrometer was taken as the true surface area. The chemical analyses for calcium and for titanium within a group showed maximum variations of 50.04 pet from the average values used in Figs. 9 and 11. In order to suspend the specimen from the balance for the kinetic studies, a hole, 0.03 in. in

Jan 1, 1965

By J. M. Dahl, L. H. Van Vlack

STAFF: Editor, Gerhard Derge Associate Editor, Paul G. Shewman Carnegie lnstitute of Technology Schenley Park Pittsburgh, Pa. 15213 Editorial Assistant, M. A. Redmerski Production Editor, Otto T. Johnson THE METALLURGICAL SOCIETY: Jack H. Scoff, President; Richard C. Cole, Post-President; Harold B. Emerick, President-Elect; Ralph L. Hennebach, Treasurer; Robert W. Shearman, Secretary; Donald A. Parks, Assistant Secretary; Leslie S. Wilcoxson, Assistant Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: R. E. Lund, Chairman; T. E. Dancy, H. B. Emerick, P. R. Gouwens, R. E. Grace, J. H. Jackson, H. H. Johnson, A. E. Lee, Jr., R. R. Nosh, R. D. Pehlke, and Paul Queneau. Review and selection of monuscripts is under the supervision of the following Publications Committees: Extractive Metollurgy Division: R. E. Grace, Chairman; G. M. Bell, D. W. Bridges, J. M. Cigon, G. W. Healy, T. A. Henrie, R. D. Holli-day, C. E. O'Neill, C. S. Sami s, A. W. Schlech-ten, and Charles Shull . Iron and Steel Division: R. D. Pehlke, Chairman; T. P. Floridis, Arnulf Muon, G. R. St. Pierre, E. T. Tuckdogon, L. H.Von Vlack, and J. M. Uys. Institute of Metals Division: H. H. Johnson, Jr., Chairman; J. B. Clark, Vice Chairman; M. R. Achter, G. F. Bolling, J. O. Brittain, G. P. Conard, II, L. A. Girifolco. G. T. Hahn, J.P. Hirth, L. Himmel, G. T. Horne, George Krauss, C. F. Leitton, Jr., J. D. Livingston, R. D. Monning, H. M. Otte, S. V. Radcliffe, R. E. Reed-Hill, H. C. Rogers, O. Sherby, M. T. Simnod, G. R. Speich, E. A. Steigerwold, R. A. Swolin, W. A. Tiller, W. R. Upthegrove, J. B. Wagner, Jr., Derek Walton, H. W. Weart, W. W. Webb, and D. WiIsdorf. Published monthly by the American lnstitute of Mining, Metollurgicol, and Petroleum Engineers, Inc., 345 East 47th Street, New York, N. Y. 10017. Telephone PLAZA 2-6800. Subscription $30 per year for non-AIME members in United States and North, South, and Central America; $32, foreign; $7.50 for AlME members. Single copies, $6.00, single copies foreign, $6.50. The AlME is not responsible for any statement mode or opinion expressed in its publications . . . Copyright 1965 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York . . . Indexed in Engineering Index, lndustrial Arts Index, and Chemical Abstracts . . Second class postage paid at New York, N. Y., and Ann Arbor, Mich. Volume 233, Number 1.

Jan 1, 1965

By J. M. Dahl, R. J. Warrick, O. K. Riegger, H. Van Vlack

A liquid which is rich in oxygen (and silicon) develops at steel rolling temperatures in resulfurized and plain-carbon steels. This liquid fluxes solid manganese sulfide. The composition of the liquid and the resulting microstructures vary with the manganese/silicon/oxygen ratios in the steel. The observations and conclusions zuhich are presented are used 1) to suggest a mechanism for MnS deformation in resulfurized steels, and 2) to rationulize hot-shortness anomalies between plain-carbon and resulfurized steels. 1 HIS is a summary of the dependence of sulfide inclusion microstructures upon steel composition, and an interpretation of the behavior of sulfide inclusions at steel-rolling temperatures. Sulfide inclusions are known to have several metallurgical effects upon steel. Their effects upon hot-shortness are best appreciated. Although hot-shortness is well known, it is questionable whether its mechanism is fully understood because there are several anomalies in our interpretation. For example, why should not high sulfur contents produce extensive hot-shortness in free-machining steels ? A second metallurgical consequence of sulfide inclusions appears because sulfide inclusions improve machinability. Furthermore, globular inclu- sions are to be desired over elongated inclusions. To date, we know that lower silicon contents (< 0.010 pct) favor the globular sulfides, but we do not know why this interrelationship between silicon content and inclusion shape exists. Finally, the evidence is strong that the surface quality of a hot-rolled steel is particularly sensitive to the sulfur content. SUMMARY OF PREVIOUS WORK The role of sulfur in hot-shortness was first suggested during the past century. It is uncertain who was the first to conclude that sulfur was less deleterious in the presence of manganese, and that manganese altered the sulfide phase from a liquid FeS to a solid MnS at steel-rolling temperatures. However, Urban and chipman&apos; emphasized that liquid FeS may accumulate as an interdendritic film during solidification. More recently, Keh and Van lack&apos; showed that the intergranular liquid does not completely surround the metal grains at all rolling temperatures. Rather, a small finite dihedral angle exists when geometric equilibration is attained at

Jan 1, 1962

By E. T. Turkdogan, L. S. Darken

Calcium ferrite melts were equilibrated with sulfur and oxygen-bearing gases at temperatures within the range 1290°C to 1620°C. The results show that at oxygen partial pressures below 10-4 atm the sulfide-reaction occurs and at higher oxygen pressures the sulfur dissolves in the melt principally as sulfate ion. It is also observed that when the product increases, sulfate ions are converted to pyrosulfate ions and the results permit the evaluation of the pyrosulfate/sulfate ratio. It is shown that the ratio y CaSO,/rCaO increases with decreasing concentration of calcium oxide in calcium ferrite, silicate and aluminate melts. Indications are that oxy-acids, e.g. silica, alumina and ferric oxide, increase yCaS0,. A few experiments were carried out within the sul-tide range and the results are in accord with those obtained by other investigators on aluminate and silicate melts. BECAUSE of the industrial importance and theoretical interest, many investigators have studied the reactions between molten oxides, silicates or alumi-nates, and gases containing oxygen and sulfur. The early work reviewed by Schenckl and studies made by Bardenheuer and Geller2 indicates that solution of gaseous sulfur in an oxide melt resulted in the replacement of the oxide ions by the sulfide ions. Measurements made by Grant and Chipman3 on the equilibrium partition of sulfur between molten iron and complex silicate melts also demonstrated that, for a given temperature and silicate composition, the distribution of sulfur between slag and metal increased with decreasing oxygen content of the metal. Fincham and Richardson4 studied the effects of temperature and partial pressures of sulfur and oxygen on the solubility of sulfur in simple silicate and alumino-silicate melts. They observed that at oxygen partial pressures below about 10-5 atm sulfur in the gas dissolved in the melt as sulfide ions, replacing an equal number of oxide ions of the melt. At oxygen partial pressures higher than 10-3 atm, sulfur entered the melt as sulfate ions. Similar studies were made by St. Pierre and Chipman5 using calcium ferrite and calcium silico-ferrite melts. The experimental data presented in this paper were obtained in this Laboratory about 10 years ago; this is the first formal presentation although a preliminary report was given previously.6 In each of these experiments, a pure synthetic CaO-Fe2O3 melt in a platinum crucible was equilibrated with a gas mixture (SO2-O2, SO,-air, SO2-CO, or SO2-CO2-CO) at a temperature ranging from 1296°to 1620°C. The experimental technique was essentially the same as that reported by Darken and Gurry,7 the main difference being that the atmosphere in the reaction chamber contained sulfur dioxide together with oxygen, or carbon dioxide-carbon monoxide

Jan 1, 1962

By George R. St. Pierre, John Chipman

METALLURGISTS have been studying the chem-ical behavior of sulfur in steelmaking for many years in order to have a better control of the sulfur content of finished steel. During the refining period in the open hearth, molten steel is separated from a gas phase by molten slag. Chemical reactions occur principally at the slag-metal interface and at the slag-gas interface. A need for physical-chemical investigations of reactions between sulfur-bearing gases and steelmaking slags was recognized some time ago.&apos;.&apos; From the early work, it can be qualitatively concluded that increased sulfur content and low partial pressure of oxygen in the gas phase favor the passage of sulfur from gas to slag. Using radioactive sulfur S Koch and Fink&apos; have demonstrated the rapid rate of exchange of sulfur between gas and slag in an open hearth furnace. Gurry and Darken and Darken and Shields (as reported by Derge and Marshall&apos;) have equilibrated lime-iron oxide slags with SO—O2 gas mixtures. The major conclusion from the reported results is that sulfur content increases with increasing lime content in lime-iron oxide slags equilibrated with a gas of high oxygen pressure (10-2). The data were interpreted as indicating the presence of SO, and S,O, ions. Richardson and Fincham&apos; have conducted the most extensive experimental study of sulfur equilibria between gas and slag. Their results confirmed many of the conclusions drawn from calculations of Richardson" and Withers. Richardson and Fincham&apos;s data fitted very well into the sulfur scheme represented by the reactions 1/2 s2 (g) + (0) melt - 1/202(g)+ (S) melt [II 1/2 S, (g) + 3/2 O (g) + (0) melt - (SO,) melt. [2] At oxygen pressures greater than 10 to 10 they found that reaction Eq. 2 was predominant while reaction Eq. 1 was controlling at oxygen pressures less than 10." to 10.". The slag compositions and gas mixtures used in their investigations were different from those used in the present study. Wherever possible, comparison has been made between their results and these, and agreement is excellent. It is evident that the distribution of sulfur between slag and gas depends upon the oxygen pressure of the gas. In FeO slags, a change in oxygen pressure produces a change in ferric oxide content, and a knowledge of this equilibrium is a prerequisite to studies of sulfur distribution. The data are found in the work of Darken and Gurry" on the FeO system and the more recent experiments of Gurry and Darken" and of Larson and Chipman" on FeO slags containing lime and silica. The effect of oxygen pressure on the ratio Fe /(Fe" + Fe ), the so-called j-ratio, reported by these investigators will be used in interpreting the results which follow. Experimental Method The purpose of the experimental program was to determine the equilibrium sulfur content in slags exposed to gases of known oxygen and sulfur pres- sures. The slag compositions selected for study were from the lime-silica-iron oxide system. Additions of magnesia were made to some of the slags. Apparatus—The apparatus used by Larson and Chipman was modified slightly to accommodate the addition of SO2 to the gas mixtures. As in their work, slag samples of 0.5 to 2.0 g were held at temperature (lcc) in platinum crucibles under a steady stream of gas, 100 to 200 ml per min, for several hours and then rapidly lowered to the bottom of the furnace where they were quenched in mercury. Preparation and Analysis of Gas Mixtures—Mixtures of SO,-CO were prepared from Virginia Smelting Co. Extra Dry liquid SO, and Pure Co. CO,. After removing traces of water vapor with an-hydrone, the CO, was passed over graphite at 1200°C, at which temperature the conversion to

Jan 1, 1957

By J. Chipman, G. G. Hatch

One of the important functions of the iron blast furnace is the desulphur-ization of pig iron before it enters the steelmaking furnaces. However, the increasing concentrations of sulphur in the metallurgical coke, source of approximately 90 pct of the sulphur present in the blast furnace charge, and demands for higher rates of production within recent years have increased the need for greater desulphurization within the iron blast furnace. Furnace operators are beginning to look for desulphurizing agents other than blast furnace slag to accomplish the desired degree of desulphurization. A considerable amount of work has been done on desulphurization outside the furnace with soda ash, calcium carbide and various synthetic slags. Whether the desulphurization of pig iron is accomplished wholly inside the furnace or partly inside and the remainder outside, will be determined by the economics involved. Regardless of which is the case, it is believed that it is necessary to have a better understanding of the physical chemistry of desulphurization by blast furnace slags. To this end, it is the object of the present investigation to attempt what is believed to be the first equilibrium study of the distribution of sulphur between liquid pig iron and a wide range of blast furnace slag compositions. Review of Literature There is a considerable amount of information in the literature concerning the desulphurizing power of iron blast furnace slags, the solubility of various sulphides in the slags, and the effect on desulphurization of temperature, of elements dissolved in the liquid iron, and of viscosity. However, there is nothing to indicate that the equilibrium distribution of sulphur between liquid iron saturated with carbon and iron blast furnace slags has been studied experimentally. Wentrupl has made probably the most detailed study of the desulphurization of pig iron to date. He considered that there are three distinct aspects involved, namely: 1. Desulphurization within the blast furnace (by lime and manganese). 2. Subsequent desulphurization by manganese. 3. The effect of subsidiary reactions on the desulphurization by manganese. The experimental work carried out by Wentrup was devoted mainly to obtaining a better understanding of how desulphurization by manganese was accomplished in the mixer and the ladle. Particular attention was given to the part played by carbon, silicon, and phosphorus associated with manganese in the iron, and the effect of temperature on desulphurization. The experimental results indicated that desulphurization by manganese is purely a process of crystallization of manganese sulphide. The addition of silicon to iron melts containing 3.5 pct carbon and less than 0.5 pct manganese had no noticeable effect on desulphurization, but with 1-2 pct manganese the silicon additions improved the desulphurization. Additions of phosphorus also resulted in improved desulphurizati011 by manganese, but the effect was not as marked as in the case of silicon. It was also found that desulphurization by manganese was further improved by lowering the temperature. In order to explain desulphurization inside the blast furnace, Wentrup considered the system iron, sulphur, calcium, oxygen, manganese. (silicon). The distribution of sulphur between the metal and slag was represented by the following equation: (SS) _ (S)Fe + (S)Ca + (S)Mn .... [S] = [s] [1] The parentheses and the brackets represent the equilibrium concentrations in weight per cent of the slag and metal constituents, respectively. Since FeS D (FeS) _ (FeS) (S)Fe LfeS - [FeS] [S] [2] (CaO) + S e (FeO) + (S)Ca _ (FeO)(S)Ca. (S)Ca _ (CaO) Kl = (CaO)[S] [S] ~K1(FeO) [3] Mn + S D (S)Mn (S)Mn (S)Mn K&apos; = [MnpT "1ST = *lIMnJ !4) Substitution of Eq 2, 3, and 4 into Eq 1 resulted in if = L- + *> (Sol + K^ (S) [51 Eq 5 was used to calcu1;lte -f^j and [S] at 1480°C for slags containing 30-50 pct lime, 0.1-2.5 pct iron oxide, 0-26 pct silica, 2 pct sulphur and iron analyzing 1.5 pct manganese. The value for LFaB at 1480°C was found to be equal to 4.5, based on the experimental work of Bardenheuer and Geller.2 The results of the calculations are shown in Table 1. Although the slags are hypothetical and do not represent the range of compositions found in ordinary blast furnace practice, the calculations indicate that lime is effective in controlling desulphurization only if the iron oxide and silica contents of the slag are kept low. Schenck3 did not claim K1 to be a true equilibrium constant, but an empirical value which varied with the silica content of the slag.

Jan 1, 1950

By J. Chipman, G. G. Hatch

T. ROSENQVIST*—It is a pleasure to see the excellent way in which the experimental part of this work has been handled. There seems to be little doubt that the distribution data obtained corresponds most closely to thermodynamic equilibrium under the prevailing reducing conditions, namely equilibrium with graphite and one atmosphere CO pressure. The desulphurization curves in Fig 10 show the same general feature as the curves given by Holbrook and Joseph, but the distribution ratios are from 20 to 40 times greater—undoubtedly due to a closer approach to true equilibrium. In the theoretical discussion, the authors calculate a theoretical distribution (S) ration -jg-. which they find to be about 50 times greater than the experimental. The deviation is so great that the basis for their calculation needs a more thorough examination. The authors base their thermodynamic calculation on free energy expressions where diluted solutions of FeS and CaS are used as standard states. (The activity coefficient in diluted solutions is taken to equal unity.) Such a standard state will change when the nature of the solvent is changed. Taking the free energy of the reaction [FeS] ? (FeS), Eq 2, which is derived from the distribution of sulphur between an iron and a FeO-melt, it is very unlikely that the free energy of this reaction will be the same for a distribution between pig iron and a calcium silicate slag. Therefore a more fundamental basis for the thermodyuamic calculations seems needed, where all thermodynamic equations are referred to unambiguously defined standard states. The most natural standard states for CaO and CaS are the pure solid substances at the same temperature. As standard state for sulphur in iron, pure liquid FeS can be used. This rules out Eq 2 [FeS] ;=s (FeS) because ?F° = 0. The standard equation will then be: FeS, + CaO6 + Cgraph ?Fei + CaS8 + CO. vFo1773 = 25,000 cal It would be more universal and also simpler to refer the escaping tendency of sulphur in liquid iron to the corresponding H2S/H2 ratio which can readily be determined experimentally. As standard state a gas mixture H2S/H2 = 1/1 can be used. (This corresponds at the temperature of liquid iron closely to one atmosphere S2 vapor.) Thus the standard equation for the sulphur reaction can be formulated as follows: H2S0 + CaO3 + Cgraph ?H2o + CaS8 + COg The standard free energy of this reaction has been calculated from the best available data to AF°m3 = —35,000 cal. This gives for the equilibrium constant at 1500°C Now, the solubility of CaS in blast furnace slags has been determined by McCafferey and Oesterle* and corresponds at 1500°C to about 10 pet S (varying somewhat with the composition of the slag.) If the activity of CaS is assumed linear between 0-10 pet as curve 1, (see Fig 11), then acaO = 0.1 (S); (S) being wt. pet sulphur in the slag. For a diluted solution of sulphur in an iron melt saturated with carbon, the ratio H2S/H2 is, according to Kitchener, Bockris and Liberman,f about 0.01 [S], [S] being wt. pet sulphur in iron. Substituting these values in the expression for Kp we find The value 2.103 is only 4 times greater than the experimental coefficient found by Hatch and Chipman, but the value is very sensitive to a small error in AF°. A better agreement with the experimental distribution coefficient can be obtained if one assumes the activity of CaS to run like curve 2 (Fig 11). This (S) will give a lower theoretical W, value, a value which varies with (S) exactly as Hatch and Chipman learned. Such a shape of the activity curve, which corresponds to a positive deviation from Raoult&apos;s law, is actually to be expected from the fact that liquid silicate and sulphide phases usually show incomplete miscibility. A closer agreement between experimental and theoretical data can not be expected before we have more complete data for the individual activities of CaS and CaO in the slag. The activities acaS and Ocao referred to the solid phases as standard states, are exact defined quantities contrary to the somewhat undefined expression "free lime," and they are independent of any theory for the constitution of liquid slag. J. CHIPMAN (authors&apos; reply)—The authors wish to thank Mr. Rosenqvist for his very interesting and useful thermodynamic addition. Curve 2 of his figure offers the needed basis for explaining the increase in the ratio (S)/[S] with increasing sulphur content. Attention is called to an error in the printed paper: Fig 2 and 3 are reversed. M. TENENBAUM*—In the figures showing the relationship between excess base and sulphur distribution (Fig 6, 7 and 9) the slope of the curve tapers off in the negative basicity range. Somewhat the same thing is observed with open hearth slags. In that case, the fact that some sulphur distribution between slag and metal is obtained with negative basicity is interpreted as indicating some dissociation of the lime silicate compounds whose existence in oxidizing basic slags has been used to explain various observed phenomena with regard to other slag-metal reactions. In the case of the blast furnace slags, the reduced slope of the sulphur distribution curve with decreasing excess base is attributed to the amphoteric effect of alumina. Has the possibility of other explanations been investigated ?

Jan 1, 1950

By R. E. Boni, G. Derge

Application of surface tension measurements has been made to molten silicates in order to determine the effect of sulphur upon the surface tensions of synthetic blast furnace slags. In melts with the same molar ratios of AI2O3 + SiO2 to the basic oxides BaO, CaO, and MgO, the surface tensions increase in the order of oxides listed. Sulphur lowers the surface tensions of the basic BaO, basic CaO, acid BaO, acid CaO, and acid MgO slags in that order; and the concentration of excess sulphur at the slag surface increases in this same order of slags. The rate and amount of desulphurization of iron by these slags is favored by a low excess surface sulphur in the slag. IN a previous paper,1 the authors discussed the applications of surface tension measurements of molten silicates to problems of metallurgical interest. Of major importance is the aid that such studies lend to forming a working concept of slag structure. Since the ability of a slag to desulphurize metal depends strongly upon its composition,2"4 fundamental information about the structural differences between various slags which contain sulphur should aid the development of better desulphurizing media. For that reason, the present investigation concerns the effect of sulphur upon the surface tensions of synthetic blast furnace slags. Experimental Procedure , The maximum bubble-pressure method was used to measure the surface tensions of synthetic blast furnace slags in the temperature range 1300° to 1600°C. The method is based upon the equation which was developed by Schrödinger5 from a consideration of the forces of hydrostatic pressure and surface tension of a liquid which oppose bubble formation when a gas is forced through a tube immersed in the liquid. where y is the surface tension between argon and slag in dynes per centimeter; g is the gravitational constant, centimeters per second2; H is the manometer reading in centimeters; s2 is the density of manometer fluid in grams per cubic centimeter; S1 is the density of the medium in grams per cubic

Jan 1, 1957

By T. J. Whalen, S. M. Kaufman

Surface-tension measurements for liquid Fe-C-Co and Fe-C-Ni alloys were performed by the sesszle-drop technique at 1350o and 1425°C. Cobalt was shown to he more effective than nickel in lowering the surface tension of Fe-C alloys A minimum value for surface tension of 1640 dynes per cm was found in the Fe-C-Co system at a concentration of 1.5 pet C and 12pet Co. Analysis of these measurements in terms of adsorption and desorption behavior indicated that cobalt and nickel lower surface tension in Fe-C alloys by replacing carbon at the liquid-vapor interface. Comparison of results to date for Fe-C liquid alloys has shown that most substitutional-type elements having about the same atomic diameter as iron also have relatively the same influence on surface tension when present in dilute amounts. It has been shown previously that surface-adsorption behavior in liquid Fe-C ternary alloys is related to the manner in which the ternary addition affects the activity of carbon in the bulk solution.&apos; Certain ternary additions, such as chromium, tending to decrease carbon activity cause adsorption of carbon and chromium to the liquid-vapor interface. Additions, such as silicon, increase the carbon activity, resulting in a desorption of carbon and an adsorption of silicon. Both cases were shown to cause a decrease in surface tension due to adsorption. It is the object of this paper, as part of the writers&apos; continuing interest in the effect of alloying additions on the surface tension of Fe-C alloys, to present and discuss surface-tension data on solutions in the ternary systems Fe-C-Co and Fe-C-Ni. Available activity measurements for these systems in the solid state indicate a strong increase in carbon activity when either nickel or cobalt is added to Fe-C alloys.2, 3 EXPERIMENTAL PROCEDURE The alloy compositions used are shown in Table I. These alloys were prepared by vacuum melting in stabilized zirconia crucibles and then vacuum casting into cold-steel molds. The nominal analyses for the alloys used in this investigation are given in Table I. Surface tensions and densities were measured by the sessile-drop method4,5 in conjunction with the tables of Bashforth and bdams.&apos; Specimens were prepared by slicing 1/4-in. cubes from the center of the vacuum-cast ingots and grinding the edges of these cubes until their shapes approximated spheres with flat bottoms. Proper handling techniques, including an acetone rinse immediately before use, assured minimum contamination from sources extraneous to the actual melting. For each experimental run a sample was placed on a BeO plaque and positioned and leveled inside a vacuum induction heating apparatus. The sample and plaque arrangement sat inside a molybdenum tube which acted as the susceptor. Diagrams of this apparatus may be found in the literature.= After heating to temperatures just above the liquidus at pressures of the order of 10-4 to 10- 5 mm Hg, photographs of the drop profile were made using its natural thermal radiation as a light source. Some measurements were made with partial pressures (-1 cm Hg) of a mixture of H2 and He gases. The H2-He atmospheres proved to be necessary at higher nickel contents to retard excessive vaporization losses. Chemical analysis for carbon and the ternary addition was performed for each alloy sample after completion of the experimental run.

Jan 1, 1964

By E. N. Silverman

Mixtures of&apos; MnS, ZFeO-SiO,, ZMnO.SiO, FeO, and MnO were prepared synthetically and used to study the planes ZFeO. Si0,-ZMnO.SiO,-MnS, FeO-MnO-MnS, and Fe0-MnO.Si0,-MnS in the quaternary system. Because the oxides and silicates studied flux MnS, inclusions in this system are partly liquid during rolling. Also, oxygen can modify subsurface inclusions through the reaction MnS + FeO—FeS + MnO during the soaking of ingots and the reheating of blooms and billets. NONMETALLIC inclusions in steel have long been a subject of study and conjecture because the properties of many steels are known to be affected by the the kind and amount of inclusions present. In free-machining steels, the type of inclusion present has a direct bearing on their machinability; in other steels, cleanliness is important and metallurgists direct their efforts at reducing the amount of non-metallic inclusions. Thus, the accumulation of knowledge about the formation and behavior of inclusions during all stages of steelmaking and processing should aid in improving the quality of steels and decreasing the production costs resulting from rejections. Previous studies of inclusions have contributed greatly to our understanding. The investigators have generally examined inclusions in finished steel. Boulger, Moorehead, and Garvey1 found that in Bessemer steels, low silicon contents results in globular sulfide inclusions with attendant high machin- ability ratings. Van vlack2 also found that low silicon contents favor inclusion morphology that contributes to high machinability ratings. Boquist and Stoll* found that silicon content affected sulfide inclusions and machinability of blooms, billets and bars more than did the finishing temperature in the range between 1775° and 2075°F. Carney and Rudolphy3 studied the distribution of sulfur, manganese, silicon, and carbon in a commercial ingot of resulfur-ized steel and found that silicon was concentrated near the bottom. This helped to explain why bottom cuts had poorer machinability. Klinger and Koch4 developed techniques for extracting inclusions from steel, and the technique devised by Gurry, Chris-takos, and stricker5 for extracting carbides can also be adapted to the study of inclusions. A different approach to the study of inclusions in steel consists of synthesizing the constituents that form inclusions and determining the phase eauilibria in the system that contains the constituents. The resulting phase diagrams can then be used to determine the effect of the various constituents upon each other. In this way, it becomes possible to under-

Jan 1, 1962

By S. L. Payne, J. P. Morris, R. L. Kipp, G. R. Zellars

The activities of iron and nickel in liquid Fe-Ni alloys were determined by measuring the vapor pressures of iron and nickel above the alloys and comparing with the vapor pressures of the pure metals. Nickel was found to deviate negatively from Raoult&apos;s law over the entire composition range. Iron behaves ideally down to 0.7 mole fraction but shows negative deviations at lower concentrations. At 1600°C the activity coefficients at infinite dilution are 0.40 for iron and 0.66 for nickel. 1 HE formulation of the conditions of chemical equilibrium between liquid metals and gases or slags is an important application of thermodynamics to pro- cess metallurgy. Usually the metal and slag phases are solutions of several components; and for accurate calculations, it is often necessary to use the activities of the components in place of their concentrations. Data concerning activities, however, are quite meager. The evaluation of the activities of iron and nickel, presented in this paper, is part of a project to determine activities in iron alloys at elevated temperatures.

Jan 1, 1960

By N. A. Gokcen, E. S. Tankins, G. R. Belton

Equilibrium in the reaction H2(g) + O[in liquid iron, cobalt, or nickel] = H2O(g) has been investigated over wide temperature and composition ranges. Oxygen has been found to obey Henry&apos;s Law in each of the three metals at 1550°C. The standard free-energy changes for the above reaction are given by: (1550° to 1700°C) ?Foco = -45,360(±290) + 16.16(±0.16)T (1490° to 1700°C) ?Fo Ni = -48,170(±220) + 16.12(±0.12)T (1465° to 1700°C) where the standard state for dissolved oxygen is the I wt pet solution. ThE thermodynamic behavior of dilute solutions of oxygen in molten iron has been the subject of many investigations over the last thirty years,&apos;-&apos;4 the majority of the investigators having utilized the reaction:

Jan 1, 1964