By H. I. Aaronson

THE TTT-curve for the beginning of transformation in hypoeutectoid steels containing appreciable amounts of relatively strong carbide-forming alloying elements often exhibits a "bay" at intermediate temperatures. In many of these steels, proeutectoid ferrite is the initial product of the decomposition of austenite not only at temperatures above the bay but also in an appreciable temperature range below the region of the bay. Hultgren has postulated that ferrite formed above the bay, termed "orthoferrite", contains the equilibrium concentration of alloying element at temperatures above the eutectoid range, and the extrapolated metastable equilibrium concentration at lower temperatures. The ferrite formed below the bay, on the other hand, termed "paraferrite", was assumed to inherit completely the bulk alloy content of the austenite without regard for the compositional requirements of equilibrium. As shown schematically in Fig. 1, the two types of ferrite were taken to have different Ae3 temperatures and different C-curves on a TTT-diagram. Their different kinetic behaviors were thus considered responsible for the bay in the TTT-curve for the proeutectoid ferrite reaction in this type of alloy steel.

Jan 1, 1962

By T. Federighi, S. Ceresara, C. Panseri

The results of an exploratory investigation by means of resistivity measurements at -195ºC, on the aging characteristics of a set of Al-Mg alloys with a maximum content of 7 pct Mg, are reported. Whereas for dilute alloys (Mg < 1.5 pct) only a decrease in resistivity is observed at about 100°C (due to the elimination of quenched-in vacancies), for more concentrated alloys such a decrease is preceded by an increase in resistivity in the range between -60ºand +40°C. Following some previous suggestions, this increase is considered as good evidence for clustering of solute atoms @reprecipi-tation process). From the analysis of the results it appears that, although the process is substantially similar to that observed in other Al-rich alloys, it is characterized by a strong interaction between vacancies and zones. THE process of formation of Guinier-Preston zones, i.e., preprecipitation,1&apos;2 which occurs during the aging at about room temperature in many supersaturated aluminum-rich alloys, has been extensively investigated in the past few years by several workers.2,3 owever, a very interesting question arises when the case of Al-Mg alloys is considered: although it is very easy to supersaturate Al-Mg alloys, just in the same way as for many other aluminum alloys showing preprecipitation, only very little experimental evidence was available until a short time ago in the literature supporting the existence of "natural" aging in supersaturated Al-Mg alloys (see, for example, Refs. 4 to 6). On the other hand, as is well known, the X-ray method is not useful in this case because the X-ray scattering factors of magnesium and aluminum atoms are about the same. Recently, however, Cordier and Detert7 have stressed that during the aging at about room temperature of a supersaturated Al-Mg 10 pct alloy it is possible to detect an increase in resistivity; since, as is well known, such an increase is observed also in most alloys showing preprecipitation, the above authors have interpreted their results as evidence for the formation of magnesium-rich clusters (or Guinier-Preston zones) during the aging. In the course of or ientative investigations on preprecipitation in several aluminum-rich alloys, we also could detect a similar phenomenon in more dilute Al-Mg alloys, see Instituto Sperimentale Metalli Leggeri, Annual Report, 1959, and also Ref. 8. Since the details of our observations, although of a preliminary nature, differ from those of Cordier and Detert and allow one to draw a more advanced picture of the preprecipitation process in Al-Mg alloys, we have thought it useful to report our results in this paper and to comment on them briefly.

Jan 1, 1963

By P. K. Foster, C. M. Payne, A. McNabb

Some measurements of the rate of loss of hydrogen from cylinders of iron and steel are analyzed in terrns of a trapping theory. The apeement is encozcraging and gives rise to estimates for the density of traps in the metal. Furthermore, the results appear to be consistent with the assumption that the diffusion constant D for the steady flux of hydrogen through iron lies on the extrapolation of the linear curve (log D us 1/T) obtained at higher temperatures. IT has been shown in a previous paper1 that the literature relating to hydrogen diffusion in steels contains sufficient evidence to invalidate the application of Fick&apos;s laws to hydrogen diffusion in steel at low temperatures. To account for the deviations from simple diffusion behavior a trapping theory was developed, and the fundamental laws modified accordingly. In the present paper, new data on the evolution of hydrogen from long cylinders are presented, and together with some published data are examined in terms of the requirements of the theory.&apos; Properties of solutions of the basic equations derived previously1 and appropriate to the present experimental conditions are outlined in the first section as they determine the form in which the experimental data must be presented for a comparison of theory and experiment. Two new solutions not previously reported have been derived as described in the Appendix. The experiments and treatment of data are then given in Sections 2 and 3 and the results are discussed in Section 4. 1) THEORETICAL CONSIDERATIONS The hydrogen-diffusion theory1 applied in this paper postulated that lattice-dissolved hydrogen at a concentration C diffuses randomly in accordance with Fick&apos;s first law, but that the lattice contains a uniform density N of traps which can capture and delay hydrogen atoms. kC atoms are trapped per second in a region containing unit concentration of vacant traps while p are released per second in a region containing unit concentration of occupied traps. On this basis it was shown (Eq. [30] of Ref. 1) that, when local changes in the lattice-dissolved concentration C are slow enough for equilibrium to be established with the traps, the system is represented in dimensionless form by the equation:

Jan 1, 1965

By Gerhard Bockstiegel

Kuczynski&apos;s formula has been derived for the case of nonspherical particles. TWO formulae of Kuczynski&apos;s type have been derived, one describing the increase in tensile strength, the other describing the progress of shrinkage of a powder compact. It has been strength,shown that the exponents of all three formulae each contain two magnitudes of different physical characters, viz, the geometrical factor a and the kinetic factor ß. The interrelationships between the three exponents are stated. SOME years ago Kuczynski1 experimentally showed that the radius, x, of the area of contact between very small spherical metal particles and a metallic block is related to the time of sintering, t, by the following equation x = constant tk [11 where k has the value 1/5 or 1/7. Assuming that the metal particles were perfect spheres and the metallic block was perfectly flat, he derived the foregoing equation from theoretical considerations of the process of material transport in metals, and he showed that exponent k is different for different mechanisms of transport, e.g., k = 1/2 for viscous flow (according to Frenkel2), k = 1/3 for evaporation and condensation, k = 1/5 for volume diffusion, and k = 1/7 for surface diffusion. From this Kuczynski concluded that the mechanism of transport was either volume diffusion or surface diffusion, depending on whether the value of k, as found in his experiments, was 1/5 or 1/7. Subsequently. Cabrera8 corrected Kuczynski&apos;s calculations with regard to surface diffusion, showing that the theoretical value of exponent k is 1/5 for both volume and surface diffusion. He supposed that the different experimental values of k were due to slight differences in the shape of the metal particles. An exponential relationship similar to the aforementioned was found by Okamura, Masuda, and Kikuta,4 Masuda and Kikuta, and Takasaki8 when studying the rate of shrinkage on powder compacts during sintering. The authors measured the shrinkage by means of the fraction w = Vp — V./Vp — V,,,, where V,, is the volume of the green compact, V, is the volume of the sintered compact, and V,,, is the volume of the compact in its densest state. This fraction, w, they found, is related to the time of sintering, t, by the equation w == constant tm. [21 Further, Bockstiegel, Masing, and Zapf7 observed that the tensile strength, s, of sintering iron powder compacts can also be related to the time of sintering, t, by an equation of the foregoing type, i.e., s = constant tn. [3] For exponent n the values 0.28 (S=2/7) and 0.35 ( 2/5) were obtained, and the authors pointed out that there might exist a simple interrelation between exponent n as found in their experiments and exponent k in Kuczynski&apos;s equation. The authors supposed that 2k = n, since the strength of adhesion between a metal sphere and a block (as in Kuczyn-ski&apos;s experiments) must approximately be proportional to their contact area, p. x2. Theoretical Considerations This paper is an attempt to correlate the fundamental experiments of Kuczynski&apos;s type with the results obtained with powder compacts as represented by Egs. 2 and 3. In particular, the paper is to show how the rate of sintering is influenced by the geometry of the sintering particles and by the type of material transport. As the geometry of particles conglomerating in a powder compact is very complex, some simplifying assumption has to be made, of course, in order to adapt the problem to mathematical treatment. In the following paragraph a suitable simplification is introduced, and Kuczynski&apos;s formula is derived for the case of nonsphcrical particles. Relation Between Area of Contact and Sintering Time—As the face of contact between two particles in a sintering powder compact is not necessarily a circle (as in the case of spheres sintering to a block), Kuczynski&apos;s formula is modified as follows: Let the perimeter of the face of contact be described by means of polar coordinates R, 4, as shown in Fig. la, so the area of contact, f, is determined by f= 1/2 . S112p[R(Æ) ]2 dÆ [4] Then, let the two particles be intersected by a plane perpendicular to area f. The intersection is shown in Fig. lb. According to the nomenclature in this figure, the distance, h, between the surfaces of the two particles is a function of T and Æ: h = h(r,Æ). For the particular case of spherical particles, as in Kuczynski&apos;s theory, this function becomes: h = constant r2. It shall be assumed here that in the close neighborhood of their

Jan 1, 1957

By H. W. Paxton, G. M. Pound

A method is outlined for taking into account variation in chemical potential of both components in evaluating capillary effects at growing interfaces. The results are compared with experiment, and seem to be in reasonably good accord for Widman-statten ferrite growing in austenite. ENERY pointed out that during the steady-state growth of phases with a rather small radius of curvature at their advancing edge capillarity cannot be neglected. By proper application of the Laplace equation a correction must be made to the activity gradients down which diffusion occurs. Subsequent workers have concerned themselves with attempts to evaluate specific cases by the use and modification of the principles laid down by Zener.2-5 To solve the problem in its simplest form it is necessary to assume thermodynamic equilibrium at the interface and to select some criterion which will allocate the available free energy between reversible and irreversible processes. Zener chose to assume that the division should be made such that the new phase grew at the maximum rate. Other workers have used the same2,3 or different assumptions, e.g., maximum rate of free-energy dissipation,4 minimum rate of entropy production.5 Li6 has proposed that the "thermokinetic potential" should be a minimum at steady state. The purpose of this presentation is to note that most prior treatments have considered variations due to capillarity only in the chemical potential of the mobile constituent, and that a more consistent treatment must involve a consideration of the variation of chemical potentials of both solute -and sol- vent in a binary system.* As an example, the way in which this arises for ferrite growing from austenite may be illustrated by reference to Fig. l(a). The line OABC shows a typical variation of carbon activity with composition at one atmosphere pressure (at a transformation temperature below A3). In the tip of a growing ferrite plate with a hemi-cylindricab leading edge of radius ?, the pressure due to capillarity is*

Jan 1, 1963

By Toshimi Yamane

The internal friction of cold-worked titanium iso-thermally annealed at temperature below the recrystallization temperature was measured. The internal friction was calculated from the half width of a resonance curve of the specimen which was vibrated transversally by the electromagnetic method. The experimental results were as follows: 1) The specimens annealed for a long time at temperature below the re crystallization temperature after cold working have the strain-amplitude dependent internal friction. 2) The internal friction increased by the cold working was decreased during the isothermal annealing. The reason of decrease of the internal friction is considered to be caused by the annihi-lation of lattice defects. 3) There is a linear relation between logQt-1/Q0-1 and (1/T)2/3 below the recrys-tallization temperature, where Q0-1 is the internal friction standing 24 hr at the room temperature after cold rolling, Qt-1 is the internal friction annealed at T°K for t min. 4) The hardness of the cold-worked titanium does not change by the annealing at 300°C for a long time but decreases by annealing at 400ºand 460°C. METALS, when cold worked, show sharp changes in physical and mechanical properties&apos; The internal friction of cold-worked metals increases sharply and has a maximum value1,2 connected with working de- grees. The increased internal friction of cold-worked metals is recovered by annealing. This phenomenon is the well known effect called Köster effect. The recovery of the internal friction occurs earlier than the changes in tensile properties, hardness, or X-ray diffraction, and is very sensitive to the structure of a metal. The mechanism of the recovery at a temperature lower than the recrystallization temperature is being considered variously by many investigators: there are such views as the annihilation of dislocations by smith,&apos; the rearrangement of dislocations mentioned by Nowick,4 and interaction of dislocation with point defects.5 Smith and Nowick also considered the interaction but it is so difficult for them to explain the rearrangement mechanism systematically, it being not considered a special model; therefore, we do not explain it quantitatively. Experiments measuring the recovery of the internal friction of cold-worked metals were performed by Gordon and Nowick6 on NaCl, and by Smith on copper. In addition, there are many studies, particularly those of measurements on copper by other investigators. There are comparatively many investigations on aluminum and iron which are the cubic system,&apos;-&apos; but only a few on metals of the hexagonal system.10 In view of this, I investigated cph titanium at room temperature and measured the internal friction after annealing isothermally at temperature lower than the recrystallization temperature. SAMPLES AND EXPERIMENTAL METHOD samples for the experiment were cut from a 6-mm titanium plate. The long direction of samples was

Jan 1, 1963

By Rollin E. Hook, Attwell M. Adair

The yield and fracture behavior of recrystallized chromiztm have been studied in order to gain an understanding of the recrystallization embrittlement-rheotropic recovery phenomenon. The duc tile-brittle tensile transition temperature of recrystallized chromium was found to vary from 225 ° to -80°C as the ratio of specimen diameter/mean planar grain size decreased. The applicability of this observation to other bcc metals is briefly discussed. Brittle fracture in recrystallized chromium was found to be initiated predominately from intercrystalline rupture nuclei. Single crystals exhibit a high degree of ductility at 23 "C. The experimental data indicate that grain boundaries play a significant part in the yield and fracture behavim. Pres training significantly reduces the transition temperature, and high temperature aging does not result in re-embrittle-ment until complete recovery or re crystallization occurs. SEVERAL theories have been used to explain the recrystallization embrittlement-rheotropic recovery phenomenon in chromium. Wain, Henderson, and ohnstone&apos; propose a Cottrell dislocation locking mechanism due to nitrogen, and Weaver and Gross and weaver 3 propose a strain-induced precipitation mechanism involving a chromium nitride precipitate. The researches of many investigators seem to leave little doubt that brittleness in chromium is promoted by interstitial impurities. Smith and seybolt4 have shown that the ductile-brittle transition temperature is lowered as the interstitial content is reduced. weaver3 provides evidence for a 150°C reduction in the tensile transition temperature as the nitrogen content is reduced from 20 to 5 ppm. Maykuth and affee&apos; have suggested that the amount and orientation of grain boundary impurities may be responsible for the brittle nature of recrystallized chromium. This suggestion was based on their findings that wrought iodide chromium possessing a fiberous grain structure is ductile in tension at room temperature while a recrystallized grain structure is completely brittle. Previous investigations have not studied this phenomenon sufficiently to determine its cause. Perhaps this has been largely due to previous experimental findings that brittle fracture observed in chromium has been almost entirely transgranular.&apos; In addition McNeil and imb,&apos; who investigated coarse-grained as-cast chromium, describe the point of initiation of fracture as cleavage, close to the (100) plane, near or at grain bound-daries, or at included particles or voids. However, Hook, Adair, and ipsitt found that fracture in coarse-grained recrystallized chromium is initiated by intergranular rupture and then propagates nearly entirely by cleavage. This result, together with their finding that room temperature ductility in bending is observed for single crystals and coarse-grained polycrystalline specimens for which the number of grains through the specimen diameter is small, suggests that grain boundaries may play an important role in the brittle behavior of chromium. The recrystallization embrittlement problem can be resolved into two questions. These are, whether the controlling mechanism is predominately one of crack initiation or crack propagation, and whether brittle fracture is initiated predominately by slip or twin induced intergranular rupture or by cleavage. The following research was designed to study the role of grain boundaries on the brittle fracture of chromium in an effort to resolve these questions. EXPERIMENTAL PROCEDURES, RESULTS, AND DISCUSSION General Procedure. All tensile specimens (except 0.04 in. diam wires) were prepared from 1/4 in. diam swaged rod fabricated from one ingot. Details of fabrication are given elewhere. The results of impurity analysis for the swaged rod and for the

Jan 1, 1963

By Y. C. Liu, W. R. Hibbard

An analysis of the relationship between the deformation and recrystallization textures in face-centered-cubic metals is presented. The analysis assumes that orientations of the secondary as well as the primary textures are related to the deformation texture. The effect of alloying elements on the recrystallization texture of copper-base alloys is also discussed. ROTATIONAL relationships based on prior orientations have been used to derive both the primary and secondary recrystallization textures."" This similarity suggests that, if the secondary texture arises from grains formed during primary recrystallization, as proposed by Dunn: and if primary recrystallization derives its lineage from the deformation structure, then the orientations obtained in secondary recrystallization .as well as those obtained in primary recrystallization should be related to the deformation texture. The following discussions are

Jan 1, 1956

By Dogan E. Gücer

In the following note, with the help of a new parameter of strain hardening, the attention is drawn to the close relationship between the relative performances of steels under plastic range cycling and their strain hardening characteristics. If a cantilever beam of rectangular cross section is tested with the arrangement shown in Fig. 1 in reversed bending between constant deflection limits at the lever head, the longitudinal strain-deflection hysteresis shown in Fig. 2 is obtained. There is no lateral strain due to constraint at the rectangular test section.&apos; If the absolute value of strain undergone between a maximum state of tension and maximum state of compression is called A, it will be seen that A decreases with cycling rapidly due to the strain hardening in the test section and the ensuing change in the bent beam profile. It will also be seen that A reaches an approximately stable value around 10th cycle. If we call the first cycle strain range, A,, and that of 10th cycle, A,,, then is an index of the strain hardening capacity at a particular deflection level. A plot of n vs ? is reproduced in Fig. 3 for two ASTM steels: A-302 and A-201. A-302 is a low alloy structural steel, A-201 a low-carbon steel. The specimens were first normalized at 1650°F for 75 min then grooved with a milling cutter; and the notches were ground to 50G finish. The final operation before testing was a stress relief at 1150°F for 75 min. The behavior of the two steels changes around ?1 = 0.8 pct or A,, = A, -n = 0.7. If these curves are compared with the endurance life curves given in Fig. 4, it will be seen that the relative performance of the two steels also change around A,, =. 0.70 pct. The steel with lower strain hardening capacity (7) at a certain strain level shows a longer endurance life, irrespective of their strength levels. Since the exponent governs strain hardening at lower strain levels than the Modulus, the relative values of both parameters also coincide with the change in n values and the relative performances of the two steels at different strain levels. These two observations indicate to the close relationship be-

Jan 1, 1962

By Carl Wagner

This paper contains solutions of the differential equation of diffusion in binary alloys if the diffusion coefficient is an exponential function of the concentration of one of the components. THE general differential equation for one-dimensional diffusion in a binary system can be written as: where c is the concentration of one of the two components in any suitable units; x, the distance from a reference plane; t, time; and D, the diffusion coefficient. Hartley and Crank&apos; have pointed out that eq 1 with conventional length units for measuring the distance x holds only if the alloy can be regarded as a rigid framework. In general, this is not the case, especially if the lattice parameter varies appreciably with composition. If a modified coordinate system is used instead of an orthodox system based on the centimeter a:: length unit, eq 52 is obtained, which has the same general form as eq 1 and is generally valid. The necessary transformations are presented in the appendix. If&apos; D is independent of concentration, analytical solutions of eq 1 are known for numerous boundary conditions. If D depends on concentration, solutions based on known analytical functions are not available. Among others, Boltzmann2 and Matano3 have shown that the concentration c depends only on (x/t1/2) in the case of diffusion between two semi- infinite spaces with uniform initial concentrations: c = c, for x < 0, t = 0, i.e., x/tl/2 = — x [21] c = c2 for x > 0, t = 0, i.e., x/tl/2 = + a Moreover, Boltzmann and Matano have shown how D may be calculated as a function of concentration over the whole range of composition from c -c, to c = c2 if c as a function of (x/t1/2) for the initial conditions stated in eq 2 has been determined experimentally. Thus, for instance, in principle, the diffusion coefficient in silver-gold alloys may be calculated as a function of concentration for the whole range of composition from only one diffusion experiment with a couple of pure silver and pure gold welded together. If the diffusion coefficient D as a function of concentration c is known, a solution of eq 1 for boundary conditions as stated in eq 2 with arbitrarily chosen values of c, and C2 may be wanted. For instance, if the diffusion coefficient in an alloy A-B as a function of concentration has been derived from an experiment with a diffusion couple involving 0 and 30 pct B as initial. concentrations, the calculation of the concentration distribution in a diffusion couple involving other initial concentrations, e.g., 5 and 20 pct B, may be desired. This problem may be solved by numerical or graphical integration of eq l. The solution of an ordinary differential equation of second order, which results from using (x/t1/2) as an independent variable, can be computed quite rapidly if two conditions for the same value of the independent variable are given. In eq 2, however, two conditions are given for two

Jan 1, 1953

By G. E. Tardiff, A. A. Hendrickson

THE objectives of this communication are to present the solid-solution strengthening data for silver-base zinc single crystals and to evaluate the importance of strength contributions from several mechanisms through the use of this data combined with that for the silver-base aluminum case.&apos; Some features of the yield point behavior of silver-base zinc crystals were previously reported.&apos; Silver-base zinc alloys were prepared by induction melting 99.99 pct Ag with 99.9 pct Zn in high-purity graphite crucibles contained in argon-filled quartz tubes. After the first melting, the ingots were cut into short lengths, redistributed in the molds, and remelted in order to reduce solute-concentration variations. Alloy single crystals were then grown from the melt through the use of a modified Bridgeman technique which consisted of lowering the graphite crystal mold through a hot zone at a rate of 3/8 in. per hr. As in the melting operation, the molds were contained in argon-filled quartz tubes. Gage lengths 2 cm in length were introduced by both spark machining (circular cross sections) and abrading and acid etching (rectangular cross section) followed by electropolishing (a comparison of the critical resolved shear-stress values prepared by the two techniques showed no differences in strength values). The final cross-sectional areas of the crystals were approximately 5 sq mm. Prior to testing, the crystals were annealed at 600°C for 20 hr in argon atmospheres, furnace-cooled, and lightly electropolished. Crystal orientations were determined using the back-reflection method. The tensile testing was done on a Model FM Instron at a strain rate of 1(T4 per sec. Test temperatures of 77", 200°, and 400°K were attained by immersing the specimens in liquid nitrogen, dry ice-acetone mixtures, and silicone oil, respectively. The critical resolved shear-stress (CRSS) values for silver-base zinc crystals as a function of composition and testing temperature are given in Fig. 1. It will be noted that the CRSS for silver-base zinc solid solutions, as in the silver-base aluminum1 case, depends on temperature in a manner typical of fcc solid solutions: at high temperatures (-300°K and above), the CRSS is relatively temperature-independent but becomes strongly dependent on temperature at lower testing temperatures. A reasonable picture of solid-solution strengthening for silver-rich solutions at room temperature based on "direct" strengthening mechanisms3 is as follows. Since silver alloys have low stacking-fault energies, extended dislocations are expected and it is possible that Suzuki locking4 makes the major contribution to the room-temperature solute strengthening. This provides essentially temperature-independent strengthening since thermal motions of the dislocation line are not large enough to aid the dislocation in escaping the solute atmosphere extending over the fault width. An estimate of the

Jan 1, 1964

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,&apos; who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.&apos;" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.&apos; (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By J. Mote, P. Ward Flynn, J. E. Dorn

The effect of strain and strain rate on the critical resolved shear stress for prismatic slip in specially oriented single magnesium crystals was determined over a range of temperatures in an effort to identify the thermally activated strain-rate controlling dislocation process. Below about 450°K prismatic slip was preceded by twinning and fracturing. Above 450°K extensive prismatic slip was obtained followed by fracturing. Neither the Peierls&apos; mechanism nor the dislocation intersection mechanism can account for the observations. The data, however, are in good agreement with the dictates of Friedel&apos;s theory for cross slip to the prismatic plane. PREVIOUS investigations on single and polycrys-talline magnesium have resulted in the identification of the mechanisms of plastic deformation summarized in Table I. The-only well-confirmed mechanisms are {0001}, (1010}, (1011) slip plus (1012) twinning. The other twinning modes were only tentatively established and additional investigations are required to further confirm their operation. As noted in Table I, slip in this hexagonal close-packed metal invariably occurs in the direction of greatest atomic density, revealing that the Burger&apos;s vector for-active slip dislocations is always given by b = a/3<1210>. Slip is easily induced on the basal plane, and recent investigations have shown that the strain-rate controlling mechanism at low temperatures is the thermally activated intersection of the glide dislocations with dislocations threading the basal plane. In contrast, very little is known about prismatic slip. It has been reported to be active at points of stress concentration in polycrystals below

Jan 1, 1962

By Jim D. Mote, Eugenia M. Howard, Willis L. Barmore, John E. Dorn

The effect of stress and temperature on the creep rate of Ag-33 at. pct A1 and Ag-33 at. pct Al-1 at. pct Zn for prismatic slip was determined over a range of temperatures from 440º to 700°K. The alloys exhibited a brief initial inverted transient creep over which the creep rate increased slightly to a steady-state value which depended only on the stress and temperature, regardless of the previous strain history. The steady-state creep rates were found to be given by: where the activation energy is independent of the stress and strain and agrees fairly well with that estimated for diffusion. The observed creep behavior was shown to be in qualitative agreement with a model based on the stress-induced local disordering in the vicinity of a dislocation. OVER the past fifteen years, considerable progress has been made in correlating the experimen-entally observed plastic behavior of pure metals over each temperature range with one or more of a series of theoretical strain-rate controlling dislocation mechanisms. Despite the current interest in the plastic behavior of intermediate phases and inter metallic compounds, however, very little has been done in identifying the operative dislocation mechanisms in these materials. It is anticipated that the plastic behavior of intermediate phases can be rationalized in terms of the same dislocation mechanisms that are appropriate to pure metals and a solid solutions, provided the additional complexities arising from crystal structure, bonding, long-range order, short-range order, and defect lattices are taken into account. As part of a more extensive investigation on the plastic behavior of intermediate phases, Mote, Tanaka, and Dorn1 recently reported on the effect of temperature on the yield strength for prismatic slip in the hexagonal Ag-33 at. pct A1 intermediate phase as recorded in Fig. 1: Over Region I the deformation was observed to take place as a result of the thermally-activated Peierls mechanism, and over Region II the athermal disordering mechanism applied. The experimental data at that time, however, were not sufficiently extensive to identify the thermally activated mechanisms operative over Region III. It is the purpose of this investigation to attempt to identify the mechanisms that are operative over this high-temperature region. It will be shown that the same mechanism operates all over Region Ill, although the activation energy for this mechanism is in good agreement with that for diffusion, the process cannot be attributed either to the motion of jogged screw dislocations or the climb of edge dislocations. The results, however, are in good qualitative agreement with stress-induced disordering localized at dislocations. EXPERIMENTAL PROCEDURE The alloys studied in this investigation were prepared from silver, aluminum, and zinc (each of purity greater than 99.995 pet) by induction melting under an argon atmosphere and chill casting in a copper mold. Rectangular bar single crystal specimens (1/4 by 1/8 in. in cross-sect ion) of Ag-33 at. pct Al were grown in vacuum by a modified Bridgman technique. Similar Ag-33 at. pct Zn specimens were produced by an identical technique employing an argon atmosphere. The specimens were so oriented that the angle 90-Xo between the tensile axis and the normal to the prismatic plane and the angle A, between the tensile axis and the slip direction were 45 ± 1 deg. The effect of a change in temperature on the creep rate and a change in stress on the creep rate were determined over the temperature range

Jan 1, 1963

By B. W. Howlett, M. B. Bever, Somnath Misra

The heats oj- formation at 0°C of the compounds AuSn,, AuSn2, AuSn, and the £ phase were measured in a metal -solution calorimeter with liquid tin or a liquid Sn-Bi alloy as solvent. The melting point, heat of fusion, and heat capacities near the melting point of- the compound AuSn in the solid and liquid state were measured in a constant temperature gradient calorimeter. The free energy and entropy of formation of the compound AuSn at its melting point and at 298 °K were calculated from the experimental results and published data. The heats of formation are discussed in relation to the nature of the compounds. The heat capacity below the melting point, heat of fusion, and entropy of fusion of AuSn are interpreted in terms of processes oc-curring before melting. The atomic arrangement in liquid Au-Sn alloys and the bonding in the intermediate phases of. the Au-Sn system are discussed in the light of the measured thermodynamic properties. THE available thermodynamic information on the intermediate phases in the Au-Sn system consists of the heats of formation of the compounds AuSn4, AuSn2, and AuSnly2 and of one composition of the < phase2 besides values of the heat content of the compound AuSn from 0" to 635".&apos; However, the heats of formation refer to different temperatures ringing from 90" to 450°C. Also, the reported error limits of some of the values are large and several inconsistencies are apparent. In the investigation reported here the heats of formation of the compounds AuS-, AuSnz, and AuSn and of three compositions of the < phase were determined for a single reference temperature of 0°C by liquid metal-solution calorimetry. The compound AuSn, which is the only congruently melting intermediate phase in this system, was further investigated in a constant temperature gradient calorimeter by measuring its heat of fusion, melting point, and heat capacity in the solid and liquid states near the melting point. From these data and published free energies of the liquid of composition Au~n,&apos; the free energies of formation of the compound AuSn at the melting point and at 298°K were calculated. The results shed light on the solid-liquid transition of AuSn and on the atomic bonding and state of association of gold and tin in the solid and liquid phases. 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Samples. Stoichiometric amounts of gold and tin, each 99.99+ pct pure, were melted in evacuated Vycor capsules (12 mm ID). The melts were maintained approximately 150°C above the liquidus for about 12 hr and shaken repeatedly. Samples of the compound AuSn were cooled slowly to room temperature. Melts of the other phases, all of which solidify by peritectic reactions, were transferred to the narrow end (5 mm ID) of the capsule, which was then quenched into iced brine. The solidified samples were annealed in the unopened capsules for 10 days at 30" to 50° C below the respective solidus temperatures. The absence of microsegregation and second phases was confirmed by metallographic examination. At least two batches of each composition were prepared. 1.2) Solution Calorimetry. The heats of formation were determined by liquid metal-solution calorimetry. In this technique, the difference between the heat effects on dissolution in a liquid metal, or alloy bath, of the compound and a mechanical mixture of its annealed components, adjusted for changes in composition of the bath, is the heat of formation of the compound at the temperature from which the samples are added. Details of the equipment and technique have been described."&apos; A tin bath at 300" or 350°C was used with the compounds AuSn,, AuSnz, and AuSn. The high gold content of the £ phase would have caused it to dissolve with an appreciable exothermic heat effect. In order to achieve thermal compensation, the samples were added from 0°C to a bath at 350°C consisting of 66.2 wt pct Bi (99.999+ pct pure), balance Sn (99.99+ pct pure). This solvent gives thermal compensation because gold dissolves exothermically in tin and endothermically in bismuth. The calorimeter was calibrated by adding from 0°C approximately 0.015 g-atom of the solvent.

Jan 1, 1965

By B. D. Cullity, S. S. Hsu

The stress distribution at the surface of a twisted cylinder is analyzed along the boundary of a slip plane of arbitrary orientation and this analysis is applied to the torsion of cylindrical crystals of magnesium. A criterion for slip is developed and the critical resolved shear stress of magnesium in torsion is found to be 0.038 kg per sq mm. The mechanism of torsional deformation in magnesium and aluminum is described, as well as the relaxation of a twisted crystal at elevated temperatures. THERE has been considerable fundamental study A of the mechanism of slip occurring during deformation in tension and compression but comparatively little attention has been paid to the mechanism of torsional deformation. This paper is concerned with the way in which a single crystal deforms in static torsion and with the phenomenon of untwisting which a twisted crystal undergoes during annealing. Particular attention is paid to the application of the critical resolved shear stress law to torsional deformation. Probably the most likely mode of torsional deformation that can be imagined consists of rotation of one part of the crystal relative to another on the active slip plane. Here the most interesting feature is the slip direction. If a cylindrical single crystal is twisted about its axis and if, to consider the simplest case, the active slip plane is normal to the specimen axis, then the direction of gross slip at any point must always be at right angles to the radius drawn to that point. It follows that the crystallographic direction of slip must be continually changing, in sharp contrast to slip in tension which occurs in a crystallographically constant direction. Extensive investigations of slip in torsion have been made by Gough and his associates.&apos; They made torsional fatigue tests on metal single crystals belonging to a number of different crystal systems and observed, with a microscope, the appearance of slip lines on the surface and of strain markings on the transverse cross section of cylindrical specimens. They concluded that the critical resolved shear stress law was just as valid in torsion as in tension, in the sense that slip occurred on that plane and in that direction in which the resolved shear stress was a maximum. They also established that the operative slip planes and directions were the same as in tension. They did not, however, measure the critical resolved shear stress in torsion nor, in fact, did they establish that a critical value of the resolved shear stress was necessary for the initiation of slip. Their investigations were, moreover, restricted to torsional fatigue tests which necessarily involve small strain amplitudes. Wilman,&apos; studying crystal growth and the abraded surfaces of crystals, observed crystal fragments

Jan 1, 1955

By R. L. Fullman, J. W. Cahn

A method is derived for obtaining the distribution of sphere diameters and plate thicknesses (or pearlite spacings) from size distribution functions obtained along randomly oriented lines. The method described offers several advantages over existing methods. IT is often of interest to measure not only the average particle size but also the distribution in sizes of particles dispersed in an opaque material, such as an alloy. Particles of a single size will exhibit a range of apparent sizes on the plane of polish. If the sample contains a distribution of particle sizes, the distribution of observed sizes on the plane of polish is related to the distribution of actual particle sizes by an integral equation, For example, a distribution of sphere sizes, N(r),

Jan 1, 1957

By R. W. Heckel, J. H. Smith, H. W. Paxton

The habit plane of proeutectoid cementute precipitated from austenite was studied using a two-trace surface (analysis coupled with a direct X-ray back-reflection determination of the orientatzon of the parent Matrix. The results were the same as those obtained by earlier workers1 - 2 who used Indirect methods to determine the orientation of the matrix. The data indicate that a range or habit planes in the parent phase is operative which is not in agreement with accepted existing theories. In 1933, Mehl, Barrett. and smith1 obtained a non-unique result in a study of the Widmanstätten habit plane of proeutectoid cementite. Their data are shown in Fig. 1. These results were verified by Greninger and Troiano,2 although they did not pre-sent any data. Both of these investigations relied upon indirect methods of determination of the matrix lattice orientation. Theoretical considerations of Widmanstatten precipitates have usually proved or assumed an orientation relationship between matrix and precipitate; the habit plane expressed relative to the matrix is generally unique, although it may be irrational.3 Opinion is divided as to the factors influencing the choice of habit plane. Mehl4 felt that a nucleus which was plate shaped to minimize strain energy and surface energy during its formation could maintain this shape by the point effect of diffusion; the

Jan 1, 1961

By N. S. Stoloff, R. G. Davies

A study has been made of the efject oj different dislocation-precipitate interactions upon the temperature dependence of the flow stress of aged Ni-14 at. pct A1 alloy. It is observed that when the dislocations bow between widely spaced (-20004 coherent Ni3Al particles the flow stress decreases with increasing temperature in the normal way. However, when the dislocations cut closely spaced (-5004 particles the flow stress is independent of temperature from -100 to 600°C, due to a balance between softening of the matrix and an increase in strength of the particles with increasing temperature. The retention of strength at high tempera-tures of commercial nickel-base alloys, which are strengthened by the precipitation of a phase based upon Ni3Al, is thought to be due to the unusual strength properties of Ni3Al. The flow stress of Ni3Al increases continuous1y from -196"C to a maximum at -600"C. It is concluded from a series of thermal-mechanical tests that the sevenfold increase in flow stress over this temperature interval is due to a lattice effect and is not diffusion-controlled. The flow stress of precipitation- or dispersion-hardened materials depends on the resistance to dislocation motion within the matrix and the extra energy required for dislocations to bow between or to cut particles. If the dislocations bow between the particles or if the strength of the cut particles is constant with temperature, then the flow stress of the precipitation-hardened alloy must decrease with increasing temperature due at least to the decrease in elastic modulus of the material. There will be softening also from thermally activated cross-slip or climb, offering an additional degree of freedom for dislocations to avoid particles. For example, in the case of nickel containing a dispersion of thoria,&apos; which most probably deforms by dislocations bowing between particles, the flow stress decreases by about 50 pct between 25" and 650°C. In A1-Cu alloys2 aged to produce the 8" precipitate, dislocations cut the particles, and the flow stress decreases by about 20 pct between -269" and 25°C. However, many commercial high-temperature nickel-base alloys, for example Inconel-X and Udimet-700, exhibit little or no decrease in flow stress with increasing temperature up to about 700°C. A characteristic feature of these alloys is that they are strengthened by the precipitation of a phase based upon Ni3A1. Guard and westbrook4 and flinn&apos; have shown that Ni3Al (and alloys in which a third element such as molybdenum or iron is substituted for part of the aluminum) is unusual in that the hardness and flow stress increase with temperature to a maximum at about 600°C. For the flow stress of a precipitation-hardened alloy to be independent of temperature we propose that the particles must be cut by dislocations moving through the matrix and that the strength of the particle must increase with increasing temperature. Theories of precipitation hardening do not take into account the flow stress of the dispersed particles that are cut during deformation; the only dissipative process usually considered7 is the creation of interface within the particle and between the precipitate and matrix. The purpose of the present investigation has been to study in detail the temperature dependence of the flow stress of a nickel-base alloy strengthened by the precipitation of Ni3Al in two structural conditions such that when deformation occurs it does so by dislocations a) bowing between the particles and b) cutting the particles, respectively. A simple binary Ni-14 at. pct A1 alloy was chosen because considerable information is already available for this system concerning phase equilibria and precipitation reactions and rates.&apos; Dislocation-precipitate interactions in the binary alloy should be similar to those in the more complex commercial alloys. In addition, the mechanical and physical properties of NisAl were studied in detail in the hope of elucidating the mechanism by which the strength increases with increasing temperature up to 600°C. EXPERIMENTAL PROCEDURE For the study of the effect of precipitation of Ni3A1 upon the temperature dependence of the flow stress, an alloy containing 14 at. pct A1 was utilized; a Ni-8 at. pct A1 solid-solution alloy was employed as a comparison material. Vacuum-cast ingots were hot-rolled at 1000°C and cylindrical compression samples, 0.20 in. diam by 0.40 in. high, were prepared from the 1/4-in.-diam rod. Specimens were recrystallized and solution-treated at 1000°C for 1/2 hr and then water-quenched. A preliminary study revealed that, when the Ni-14 at. pct A1 alloy was aged for 1 hr at 700°C, significant precipitation hardening was obtained, and that the structure was free from grain boundary discontinuous precipitation; an overaged condition was produced by annealing the aged specimens at 850°C for 1 hr. To circumvent the difficulties involved in the hot rolling and swaging of Ni3A1, compression samples,

Jan 1, 1965

By R. S. Craig, W. E. Wallace, G. S. Kamath

The destruction of long-range order in Mg-Cd, has previously been thought to occur as a second order process. In the present work a variety of X-ray diffraction techniques are employed to show that in this case and in Mg-Cd alloys containing frorn 20 to 33 1/3 at. pct Mg the process more nearly resembles an ordinary first order phase transformation. It is found that the ordered alloy, which occurs as a single phase at lgw temperatures, transforms with increasing temperature into a Cd-enriched disordered (P) phase and an Mg-enriched ordered (a) phase. The interval over which these two phases coexist under apparently equilibrium conditiovs extends from 25" to 87°C content. At 33 1/3 at. pct Mg the two-phase region has disappeared. Measurement of the long range order parameter, s, for the ordered phase in MgCd, (from superlattice line intensities) shows that it disorders only very slightly before it is transformed into the p form. Kinetic experiments reveal that when the a phase is formed frorn the p phase by suitably quenching so as to suppress phase segregation, the transformation is essentially complete and the a phase has acquired its equilibrium value of S in less than 1 min. In an earlier investigation carried out in this Laboratory1 the rate of disordering of the MgCd3 superlattice was determined over an extensive range of temperature. The process was found to be first order and the rate constant, k, was established. At the lowest temperatures studied k was found to increase exponentially with temperature. At higher temperatures, however, it passed through a maximum and for the 100 deg interval below the point at which the superlattice was destroyed k was observed to decrease with increasing temperature. The various theoretical treatments1-3 of order-disorder phenomena lead to a negative temperature coefficient for k near the superlattice critical temperature but this region for MgCdB seemed unusually wide. Detailed analysis of the point indicated&apos; that either the long-range order parameter, S, for MgCda varied with temperature in an anomalous way or the disordering in this instance is more complex than in the cases which have been treated theoretically. The original objective in the present work was simply to determine S vs temperature for MgCda to ascertain whether the disordering was in conformity with theoretical expectations.2° In an early stage of the work it was noted, however, that under equilibrium conditions ordered (a) and disordered (0) phases coexist in MgCd, over a considerable range of temperature. Since on thermo- dynamic grounds the coexisting phases must differ in composition, the investigation was enlarged to permit the compositions of the two phases in MgCd3 to be determined and to establish the extent of the two phase regions for alloys containing from 20 to 33 1/3 at. pct Cd.

Jan 1, 1963