By O. J. C. Runnals

The intermetallic compounds NpAl2, NpAl3, and NpAl have been prepared, and examined by X-ray diffraction methods. The compounds are isostructural with the corresponding U-Al compounds. NpAl3 is face-centered cubic with a = 7.785A and has the MgCu2 structure. NpAl is simple cubic with a = 4.2624 and has the AuCU3 structure. NpAl4 is body-centered orthorhombic with a = 4.428, b = 6.268, and c = 13.71A. The published description for the atomic positions in UAl, applies also to NpAl4 THE U-Al system has been examined by Gordon and Kaufmann.1 They identified the following intermetallic compounds: UAI2, UAl3, and a third, tentatively identified as UAl5. A structure analysis of the latter compound by Borie2 proved that the formula UAl4 was more consistent with the X-ray data. The crystal structures of UAl2 and UA have been reported by Rundle and Wilson.3 UAl2 was found to be isostructural with MgCu. The atomic positions in the simple cubic UA1, cell were found similar to those in the AuCu3 structure. Three analogous compounds exist in the binary system Np-Al. X-ray data for the compounds NpAl2, NpAl3, and NpAl4 are reported below. The neptunium used in the investigation was supplied through the courtesy of the Argonne National Laboratory as neptunium (V) nitrate. It was stated to have a radioactive content of 99.25 pct Np237. The impurity limits had been established by a spectrographic analysis given in Table I. Any titanium, boron, or bismuth impurity should be effectively removed during the fluorination of NpO2 to NpF4, and sodium, lithium, magnesium or strontium during the alloying procedure. The oxalate ignition technique, described by Westrum for the preparation of finely-divided reactive PuO2, was used.The neptunium (V) nitrate solution, containing 100 mg Np, was evaporated to dryness on oxalic acid crystals. The resulting oxalate was calcined to NpO, by heating in platinum at 650°C for 2 hr. An equimolar mixture of anhydrous hydrogen fluoride and purified hydrogen was passed over the NpO2 for 2 hr at 500°C. According to Fried and Davidson" the above fluorination conditions should produce the purple-black fluoride, NpF3 However, the light-green product showed only NpF4 lines on an X-ray diffraction pattern and contained only an estimated 5 pct of finely dispersed black NpF3 particles on microscopic examination. NpAl3: An intimate mixture of 50 mg of neptunium fluoride and aluminum powder (99.99 pct pure, —28 to $60 mesh) was heated to 900°C in a BeO crucible in vacuum by a tungsten coil for 2 hr, to allow the following reaction to proceed: NPF4 + 7Al + NpAl, + 4AlF. [1] The formation and sublimation of aluminum mono-fluoride in this system was verified from an X-ray diffraction analysis of the sublimate. The diffraction pattern was similar to one obtained in the aluminum reduction of UF4 to UF3,6 showing both Al and AlF3 lines. The resulting alloy was sintered at 1100°C for 1 hr. A powdered specimen of the crystalline product was sealed in a thin-walled quartz capillary for X-ray examination. The photograph was taken on a 14.32 cm General Electric powder diffraction camera, using filtered copper radiation. The films were calibrated in terms of a NaCl standard pattern. The wavelengths used in the calculations were 1.5418A for Cu K and 1.5405A for Cu K The powder diffraction pattern showed that NpAl is simple cubic with a = 4.262 % 0.005A, and is isostructural with UA13 where a = 4.27A1 or a =

Jan 1, 1954

By R. A. Swalin, A. H. Geisler

THIS study represents an investigation of the effect of annealing temperature on the texture of drawn molybdenum, iron, and an iron alloy containing 14 pct Al. The effect of temperature on annealing textures has not been widely investigated in the past. One of the obstacles in making such a study using usual X-ray diffraction techniques results from the

Jan 1, 1957

By A. U. Seybolt

DURING the course of experiments involving oxygen equilibrations with a high-purity Pd-5 at. pct Rh alloy, the appearance of a subscale was noted. Most of the heat treatments in a pure oxygen atmosphere were performed at 900°C. The presence of the subscale was noted when the oxygen partial pressure was in excess of approximately 95 mm, up to 1 atm, the highest pressure used. According to available thermodynamic information' on the free energy of formation of Rh2O3 (the only reliably reported solid oxide of rhodium), this oxide should not be stable under these conditions, nor, of course, any oxide of palladium. Extraction of the subscale from the matrix was affected by treatment with aqua regia, and the resulting X-ray diffraction powder pattern is shown in Table I. This pattern is not that of Rh2O3, nor that of any known rhodium or palladium oxide. It can be indexed on a hexagonal lattice with a. = 5.22Å and co = 6.0Å. In addition to this unknown material, there was a weak Rh2O3 pattern. An X-ray fluorescence analysis of the powder gave 3214 palladium counts per sec and 5381 rhodium counts per sec, thus indicating the likelihood of a double oxide of palladium and rhodium. In view of the fact that the above result was obtained on a single sample, it is perhaps best not to insist upon the above ratio of about 0.6, but possibly to tentatively assume 0.5 or 1/1. The small amount of Rh2O3 in the X-ray pattern might have occurred on cooling, and it seems possible that the double oxide, below some temperature level, is not as stable as Rh2O3. To examine this point, some of the extracted double oxide was heated on a sheet of pure palladium in air at 900°C, and allowed to furnace-cool over a period of several hours. The X-ray diffraction pattern of the powder showed approximately the same intensity of Rh2O3 and the "hexagonal" oxide as before, but, in addition, a rather faint pattern of another crystalline species made its appearance. This finding again suggests partial transformation of the major (double) oxide to other oxides on cooling from 900°C. Application of the phase rule shows that only one equilibrium oxide (subscale) could have been present at temperature. Vacuum-fusion, oxygen analysis of the extracted subscale showed 7.7 ± 0.7 pct O. Combining this information with that of the X-ray fluorescence analysis suggests the formula PdRhO. This compound should have an oxygen content of 7.07 pct, which is within the range of error of the oxygen analysis. However, until a more careful stoichiometric study is made, it is suggested that the formula be written

Jan 1, 1965

By N. J. Grant, B. C. Giessen, Paul Predecki

ALLOYS of gold, silver, and aluminum with elements of the groups BII, BIII, BIV, and BV were prepared by a rapid quenching technique (splat) and were examined by X-ray diffraction. Five new intermediate phases were found and will be described briefly herein. For the gold and silver systems, the concentration ranges having an electron/atom ratio e/a of 1.4 to 1.5 ("3/2 Hume-Rothery phases") were studied primarily. Master alloys were prepared from high-purity metals (99.9+ pct or better) by melting either in evacuated fused silica capsules or by nonconsum-able-electrode arc melting in an argon atmosphere. Small pieces, 20 to 50 mg, of each alloy were blast-atomized to form a splat, by a technique similar to that described by Duwez and Willens.1 The technique used for this study is described in detail in Ref. 2; it utilizes a resistance-heated graphite crucible with a small hole at the bottom, directed toward a metal substrate or quenching plate. The prepared alloy rests over the fine hole, through which it is expelled by an explosion shock wave in the form of fine droplets (1 to 50 µ) of molten metal onto a copper or silver substrate, which is maintained at about -190°C. The resulting very high cooling rates (see Ref. 2 for quantitative measurements) can prevent the process of nuclea-tion and growth in many instances, resulting in the formation of metastable phases. The splat particles were transferred to a GE-XRD5 diffractometer and maintained at -190°C, where they were examined with CuKa radiation. The samples were then allowed to warm to room temperature or were heated to higher temperatures until the equilibrium structures formed. Of fifteen alloy systems considered, nonequi-librium structures were encountered in six; these are described below and summarized in Table I. In the system Au-Sb a metastable £ phase (A3 type, hcp, a = 2.898 + 0.002A; c = 4.731 * 0.004A; c/a = 1.633) was found in the concentration range Au + 13 to 15 at. pct Sb. This phase is isomorphous with the stable phases in the systems Au-Cd, Au-In, and Au-Sn, all at an average e/a ratio of 1.4 to 1.5. The concentration range of one-phase metastable was deduced from the small amounts of supersaturated gold solid-solution phase present in the splat product. It was found that ? could also be retained by splatting onto a substrate held at room temperature: however, decomposed into the equilibrium phases Au + AuSb2 after heating to 200°C for 1/2 hr, or on holding the powdered splatted alloy at 20°C for several months. Calorimetric measurements will be made in an attempt to decide the question whether ? is metastable at all temperatures or whether it is a stable phase at low temperatures. There is evidence that another phase, possibly also close-packed but with a different stacking sequence, can be obtained by rapid quenching of alloys with a different antimony content. Klement, Willens, and Duwez3 reported the existence of an amorphous phase on quenching Au-Si alloys (25 at. pct Si) to - 196°C. They found that on heating to room temperature another phase of unknown crystal structure was formed. This was confirmed (see Table I); however, the new crystalline phase, designated as ?, could also be formed simply by rapid quenching to room temperature, and even was found to exist already in the as-cast Au + 20 at. pct Si alloy. It was found that ? decomposed into Au + Si on the specimen surface at room temperature. This behavior, and the question whether or not there is an equilibrium-temperature region for ?, have not yet been resolved. It is probable that ? (Au + 20 to 21 at. pct Si) is cubic of the -brass type (D81-3) with a = 9.60, + 0.01A and N = 52 atoms per cell [compare 6 (CU-Sn)4]. Except for two very weak lines, the powder pattern of about thirty lines could be indexed on this basis; however, a determination of the atom positions has not yet been attempted. For Au-Ge the C phase was observed at about 21 at. pct Ge as reported by Luo et at.5 Lattice parameters a = 2.876A, c = 4.73,A, c/a = 1.64 were found. In the Au-Pb system, formation of a ? phase was not observed, but in the lead-rich region at 75 at. pct Pb, broad peaks belonging to an amorphous phase were found. The maximum diffracted intensity occurred at 28 = 32.4 deg which is about 1 deg larger than the position of the (111) line of lead (Cuka). For Ag-Pb, an amorphous phase analogous to the one found in the Au-Pb system was observed; this metastable phase exists probably at about 75 at. pct Pb. Since no lead-rich alloys were tested, all alloys consisted of silver + amorphous phase at -190°C. In A1-Ge alloys, line-rich and complex powder patterns were obtained at about 30 at. pct Ge; they bear similarities to those of aluminum and germanium, but are of lower symmetry; the existence of more than one intermediate phase is possible. The authors are grateful to the Kennecott Copper Corp. for Fellowship support, and ARPA (Contract

Jan 1, 1965

By P. G. Shewmon

A novel technique for determining the surface energy (?) and its derivative with respect to orientation, (?') is described. Essentially it involves the 'floating" of a wedge on the substrate, said wedge being made of a material which is not wet or only slightly wet by the substrate, i. e., as a greased needle "floats" on water. A thermodynamic analysis of a system in which the wedge is supported entirely by surface energy is given. If the original suyface is not at a cusp orientation, the surface tension is directly measurable from the groove angle formed. If the original surface is at a cusp orientation, there may or may not be a groove depending on the relative value of ?' and the weight of the wedge. Experiments primarily on copper and silver showed that sapphire, quartz and refractory metal wedges were wet while graphite wedges were not. The technique was demonstrated to work using graphite wedges, but the results obtained were not as eccurate as those obtained by other workers using the wire-creep experiments. It is concluded that the technique might prove most useful with non-metals where ?' is large and filament creep experiments would be quite difficult. If an absolute value of the surface free energy (?) of a metal is to be determined, the most reliable methods used to date measure an average over the various orientations exposed on a polycrystalline sample. For example, ? for silver, gold, and copper have been measured by determining the force required to just keep a thin wire,' or foil,' specimen from contracting under the influence of ?. Herring 3 has predicted and experiment confirms, that the sensitivity of this method is inversely proportional to the grain size.' Thus it cannot be used to measure ? for a particular orientation by using a foil single crystal or a very coarse-grained specimen. An accurate value if ? for tungsten averaged over a range of orientations has been determined using a field emission technique. The same techniques cannot or have not been used to measure ? for non-metallic solids, and as a result the values available are much less accurate.4 This Paper resents a means of making an absolute determination of ? for a particular surface orientation on any solid, as long as the given surface orientation does not break up into other orientations during an anneal. Experimentally ? is found to vary with orientation and at a few low index orientations it is found to have a cusped minimum, i.e., the derivative of ? with respect to the orientation of the surface changes discontinuously at the low index orientation, see Fig. 1. The slope of a plot of ? vs orientation (herein designated ?') is called the torque on the surface, since it tends to rotate the exposed surface toward the low index orientation, or if the surface is at the cusp orientation it opposes any force tending to rotate the surface out of the low index orientation. The ratio ?'/? has been determined for a few metals, but in cases where this ratio is high there is presently no means of determining either ?'/? or the absolute value of ?' for the orientations present on an annealed surface. The technique discussed herein also provides a means of determining an absolute value of ?' for those orientations which deviate only infinitesimally from a cusp orientation. It should work best on surfaces where ?'/? is large; that is, for cases where no other technique is available for measuring ?'. Aside from trying to learn more about surfaces through measuring ? and ?', the primary reason for wanting values of ? or ?' is to study adsorption. From measurements of the variation of ? for a particular orientation with the concentration of an impurity, one can obtain the number of impurity atoms adsorbed per unit area (Ti) on that orientation using the Gibbs adsorption equation.' where µi is the chemical potential of the adsorbed impurity. Thus, if absolute values of ? could be obtained for the free surface of a given surface orientation as a function of µi, ri could be determined for the given orientation. Furthermore, by equilibrating a grain boundary with the given surface at various values of ki, one could also determine ri for the grain boundary. Similarly Robertson 6 has pointed out that if y is taken to be a continuous function of and µi, then a2 ?/a @a µ2 = a2 ?/a pi a +. Thus, at all orientations away from cusps the following equation holds From a measurement of ?' vs ki, it is thus possible

Jan 1, 1963

By K. P. Gupta

In ternary systems containing silicon and transition elements, silicon was found to stabilize the a phase.1 At 1000°C a broad a-phase region was found in the Cr-Mn-Si system,1 which extends very close to the Mn-Si binary line (within about 3 at. pct Cr). Later investigation showed that, if chromium was replaced by small amounts (3 to 5 at. pct) of v,1 Ti, Nb, Ta, Mo, or w,1 the a phase or the R phase was again stabilized. Whether stabilization of complex crystal structures is possible by small additions of iron, cobalt, or nickel to Mn-Si is not known. Investigation of the Co-Mn-Si system4 shows the presence of several ternary phases, but at cobalt concentrations higher than 10 at. pct. In the present work the ternary systems Fe-Mn-Si and Co-Mn-Si were investigated at low iron and cobalt concentrations (< 7 at. pct Fe or Co) in search of phases of complex crystal structure. Experimental Procedure. The alloys were pre-pared by induction melting Co (99.8 pct), Si (99.9 pct), electrolytic Fe (99.88 pct), and Mn (99.9 pct) in recrystallized alumina crucibles under an inert atmosphere of argon gas. The alloy specimens were wrapped in molybdenum foil, sealed in argon-filled (at 1/2 atm) silica capsules and annealed for 72 hr at 1000" 1°C, and water-quenched. The use of argon-filled capsules was found to reduce the losses during annealing and the molybdenum foil prevented reaction of the manganese with silica. The total weight loss due to annealing and melting was found to be less than 1 pct for each alloy. The alloys were not analyzed chemically. A part of each annealed specimen was polished and examined metal-lographically using etching solutions, a) 0.1 to 0.5 pct oxalic acid solution in water, or b) 0.5 pct HNOs in methyl alcohol. Even though the etching solutions were quite dilute, the specimens were heavily etched and stained if the etching time exceeded more than 5 sec. Etching times found suitable were usually 1 to 3 sec. For X-ray diffraction work, a part of each annealed specimen was powdered by crushing after the exposed surface was ground off. X-ray diffraction patterns were taken with powder specimens using a 20-cm-diam asymmetrical focusing camera and Fe K radiation. These powder patterns were found quite satisfactory for the purpose of phase identification. However, X-ray diffraction patterns of single-phase alloy powder specimens were also taken using a Siemens diffractometer and filtered Cr-Ka radiation for greater resolution of the diffraction lines. Results and Discussion. In the Fe-Mn-Si system a new ternary phase was found at 1000°C between the p manganese and the MnsSi phase regions. The approximate phase relationships in this region of the 1000°C isothermal section are shown in Fig. 1. The new ternary phase, designated as the K phase, was found to occupy a narrow region about 1 at. pct in width and extending from Fee.oMn74.5Silg.5 to Fe.Mn.Silg.. At the high-iron content region, the K phase was found in equilibrium with the p manganese and the MnsSi phases but, at the low-iron content end of the K-phase region, the phases in equilibrium with the K phase were the p manganese phase, the MnsSi phase, and another new phase, designated in Fig. 1 as the v phase. The v

Jan 1, 1964

By K. G. Kreider, J. H. Brophy, J. Wulff

The technology of nickel-activated sintering of tungsten powder has been successfully applied to the densification of plasma-sprayed tungsten. Nickel was added by infiltration in a zinc solution followed by evaporation of the solvent. After sintering one hour at 1300°C density 95 pct of theoretical and transverse rupture strength of 74,000 psi were obtained. Shrinkage was found to be anisotropic and the mechanism of densification was comparable to that found in the nickel-activated sintering of tungsten powder. 1 HE use of a plasma spray gun for the fabrication of massive tungsten parts has become increasingly interesting. Applications now exist where a deposit in the as-sprayed condition is satisfactory. However, these deposits are generally characterized by a lamellar anisotropic microstructure containing 15 pct porosity of which, typically, two-thirds is open to the surface. Mechanically, the as-sprayed deposits fail at relatively low stress levels with a biscuit-like fracture. As a result of these problems the possibility of improving structure and strength by sintering treatments subsequent to spraying is particularly attractive. Preferably this sintering treatment should be adaptable to large bodies of sprayed metal. The similarity between the as-sprayed tungsten structure and that of a powder compact suggests that the relatively low-temperature activated sintering technique1 might be profitably employed in the densification of plasma-sprayed tungsten. It was the purpose of the present investigation to develop a technique for introducing the nickel-activating agent into the sprayed structure, to evaluate the amount and mechanism of densification obtained as a function of time and temperature, and to obtain an indication of the relative strength before and after sintering. EXPERIMENTAL PROCEDURE Powder used for spraying was purchased from the Wah Chang Corp. in several size fractions ranging from an average size of 4 to 150 . These powders were sized further for an explicit study of the influence of average feed size on densification. All powders were dried at 200°C before use. Spraying was accomplished with a Plasma Flame unit manufactured by Thermal Dynamics Corp. Several modifications of the unit were helpful in conducting the investigation. A variable speed auger feed mechanism coupled with the carrier gas mecha nism facilitated the use of fine particle sizes. A coil of ten turns of copper tubing in series with the arc power and concentrically would around the nozzle improved nozzle life and extended the range of operating currents available. The function of the auxiliary coil was to cause the arc to spin and to prevent impingement at only one point in the nozzle. Normally air sprayed deposits were made with an arc maintained at 400 amp at 50 to 70 v. The arc was blown by a gas mixture containing from 5 pct H, 95 pct N for the finest powder feed sizes ranging to 20 pct H, 80 pct N for the coarsest size. The flow rate was maintained at 100 cu ft per hr NTP through a nozzle of 0.25 in. ID. When apraying in air, the powder stream was directed toward an aluminum substrate for ease of mechanical removal of the deposit. The substrate was cooled by diverting the plasma flame with an air jet, and a second jet was directed on the deposit surface. In this configuration a gun-to-work distance of 2 to 3 in. was found to be satisfactory. Fig. 1 represents a typical as-sprayed deposit micro-structure. Laboratory studies of protective atmosphere spraying were carried out in cylindrical chamber 8 in. in diam by 18 in. in length. In operating the nozzle attached to such a chamber, particular care was required to avoid nozzle burn out due to reduced gas flow. The structure and density of the chamber sprayed deposits varied over wide ranges depending on substrate temperature. For the purposes of this investigation, flat deposits were made approximately 2 in. sq by 3/8 in. thick. From these deposits individual samples were cut an ground to a rectangular shape typically 1 1/2 in. by 1/8 in. sq such that the long dimension was perpendicular to the spraying direction. For the study of shrinkage anisotropy deposits up to one inch thick were produced. From these, rectangular samples were cut having a longer dimension parallel to the spraying axis. Prior to the addition of activating agent, the samples were deoxidized in hydrogen at 800°C for 20 min. No detectable dimensional or microstructural change was observed after this treatment. The addition of nickel was accomplished by infil-

Jan 1, 1963

By A. C. Fraker, H. H. Stadelmaier

WIENER and Bergerl reported the existence of the nitrides Fe3NiN and Fe3PtNwith a cubic L1&apos;2 structure. The present note shows that a similar nitride Fe3PdN can be observed and that the composition range between the iron nitride Fe4N and the nitrides Fe3NiN, Fe3PdN, and Fe3PtN is occupied by single-phase cubic nitrides with structures intermediate between L1&apos; and L1&apos;2. The materials used in this investigation were electrolytic iron of 99.9 pct purity, carbonyl nickel of 99.7 pct purity, sponge platinum of 99.95 pct purity, and palladium sheet of 99.8 pct. purity. Binary alloys of the transition metals were induction-melted in a crucible of fused alumina, powdered, and screened to a particle size of - 200 mesh. The powders were nitrided at 600°C in a gas mixture of ammonia and hydrogen, and the crystal structure was determined with the aid of a Wilson powder camera. The results are compiled in Table I together with information from the paper of Wiener and Berger.1 The compound at the nominal composition Fe3PdN has a diffraction pattern with prominent reflections of a face-centered cubic lattice (h2 + k2+l2 = 3, 4, 8, 11, 12, 16) and weaker superstructure lines (h2 + k2 + 12 = 1, 2, 5, 6, 9, 10, 13, 14). With decreasing palladium content the superstructure lines become weaker and approach the intensity of those of Fe4N. No analysis was made of the intensities, but it can be assumed that the structure is that found by Wiener and Bergerl in Fe3NiN and Fe3PtN, namely L1&apos;2 (perovskite structure) with both palladium and the interstitial nitrogen fully ordered. The dependence of the lattice constant upon the solute atom (Ni, Pd, Pt) content can be explained tolerably well by simple lattice expansion due to subsequent work confirms this suggestion, it will be of significance to order-disorder theory. The author is grateful to Lester Guttman for discussions on this topic.

Jan 1, 1961

By Mark J. Klein, A. H. Clauer

The Snoek peak induced by solute nitrogen in chromium was studied. A rapid quenching rate is required to maintain nitvogen in solution in sufficient concentrations to be detectable by internal-friction techniques. An expression for the tertninal solubility, c, of nitrogen in weight pevcent is log,,c = -4130/T + 1.05. The diffusion of nitrogen in zhromium determined by internal friction is SNOEK&apos;S theory1 of the stress-induced ordering of interstitial solute elements in the bcc lattice has been used to deduce information on the behavior of interstitials in a number of bcc metals. Under the proper conditions, internal-friction studies of "Snoek peaks" permit a determination of diffu-sivities, solubilities, and precipitation kinetics of interstitial elements. Internal-friction studies of this type have been reviewed by Nowick,&apos; Wert,= Powers and Doyle,4 and others. The behavior of interstitial atoms in Group V-A metals and iron has been rather extensively studied in this way, and results are reasonably self-consistent. However, the study of interstitial elements using internal friction in the Group VI-A metals—tungsten, molybdenum, and chromium—is much less clear. Thus far, internal-friction studies have revealed a peak in tungsten tentatively attributed to carbon5 and a peak in chromium associated with nitrogen. In chromium, Bungardt and Preisendanz6 observed a peak at 180°C for a frequency of -1 cps which they associated with nitrogen. More recently, de Morton7 determined the diffusivity of nitrogen in chromium from studies of a nitrogen peak at 160°c for a frequency of -1 cps and from elastic aftereffect measurements. The objective of this investigation was to study the nitrogen peak in greater detail, to obtain information on the behavior of nitrogen in chromium. This information is of interest because nitrogen is known to have an embrittling effect on chromium. However, efforts to deduce the role played by nitrogen in influencing the mechanical behavior of chromium are handicapped by lack of information on its behavior and distribution in chromium. EXPERIMENTAL PROCEDURES The chromium wires used in these studies were drawn from arc-melted iodide-chromium stock that had been extruded, swaged, and centerless-ground to 0.25 in.-diameter rods. Internal-friction measurements were made in an evacuated torsional pendulum similar to the one described by Kê,8 utilizing wires 0.048 to 0.030 in. in diameter. A series of analyses of the fabricated wires showed that the major impurities were approximately 100 ppm Fe and a combined interstitial content of 50 to 100 ppm C, O, N, and H. A typical interstitial analysis of the wires after processing is 15 ppm C, 2 ppm H, 50 ppm O, and < 5 ppm N. Interstitial concentrations were determined by vacuum-fusion, combustion-conductimetric, and micro-Kjeldahl analyses. In general, vacuum-fusion analysis yielded a lower nitrogen concentration than did micro-Kjeldahl analysis. For consistency, the nitrogen concentrations reported in this investigation were determined by the former method. Heat treatments were carried out by encapsulating the specimens in quartz tubes containing argon. The fabricated wires were annealed at 1150°C for 1 hr to produce uniform recrystallized grain size of about 0.015 mm. Nitrogen and carbon were added to the fabricated wires by encapsulating them in a quartz tube containing ammonia or methane, and annealing them at 1150°C for 48 hr. In some instances, carbon was also introduced by coating the wires with carbon black prior to annealing.

Jan 1, 1965

By Mark J. Klein

An internal-friction profile induced by nitrogen in Cr-35 at. pet Re was studied as a function of nitrogen concentration and heat treatment. From these studies, the solubility of nitrogen in this alloy was deduced. The equilibrium solubility of nitrogen in chromium does not appear to be substantially changed by the addition of 35 at. pet Re to chromium. However the precipitation kinetics of nitrogen from solution are significantly decreased. IT has been found that rhenium has a beneficial effect on the low-temperature ductility of Group VI-A metals. As part of a study to investigate the mechanism of this increased ductility, it was of interest to compare the concentration of interstitials retained in solution in one of these ductile bee alloys with the concentration retained in solution in its base metal. In this regard, a study of the solubility of nitrogen in ductile Cr-35 at. pet Re was selected for this phase of the investigation because the solubility of nitrogen in the base metal, chromium, has been determined over a fairly large temperature span.1-3 In addition, nitrogen is known to have an embrittling effect on chromium,4 but does not appear to have a comparable embrittling effect on Cr-35 at. pet Re.5 The experimental method selected for this study was the measurement of internal friction. This technique allows interstitial-concentration measurements to be made in bee metals that are sensitive to small changes in the concentration of a particular interstitial, even when other interstitials are present. When subjected to a cyclic stress, interstitial atoms in solid solution give rise to an internal-friction peak whose origin is the stress-induced ordering of interstitials into preferred lat- tice sites. These internal-friction peaks signify a dissipation of elastic energy which is greatest when the period of oscillation is comparable with the relaxation time for the attainment of an equilibrium interstitial distribution. For dilute interstitial binary alloys, the height of the internal-friction peak is proportional to the concentration of interstitial atoms in solid solutions. snoek8 has shown that the internal friction, Q-1, may be expressed by the equation where A is the relaxation strength, ? is the angular frequency, and 7 is the relaxation time. The relaxation strength, A, is proportional to the concentration of interstitials taking part in the relaxation if no interaction occurs between solute atoms. Thus values of peak height, which can be determined as a function of temperature, give a measure of the relative concentration of interstitial atoms in solution at various temperatures. If equilibrium has been attained, the peak heights will be proportional to the interstitial solubilities. The constant that relates A to the interstitial concentration can be determined experimentally from peak-height measurements as a function of concentration for specimens of constant crystallographic orientation. When this has been done, Q-1 measurements can be used to determine solubilities according to the equation C - KQ-1 where C is the soluble interstitial concentration and K is a constant that can be experimentally determined. It is possible, however, that lattice imperfections may bind interstitials to certain lattice sites. Internal friction does not measure these interstitial~, but does measure interstitials which are free to move in the normal lattice sites when subjected to an applied oscillating stress. On alloying the pure metal with a substitutional

Jan 1, 1965

By Huey-Lin Luo, T. R. Anantharaman, William Klement

Two new metastable phases have been obtained in Au-Ge alloys by rapid cooling from the melt. One is of the hep structure with near-ideal axial ratio and may be considered a Hume-Rothery phase. The other has a complex tetragonal structure (a = 11.627Å and c = 22.191Å for the Au60Ge40 alloy) and may be looked upon as a superlattice made up of forty-four fee unit cells. Alloys with the tetragonal phase are charactevized by marked preferred orientation. The metastable constitution of the Au-Ge alloys is discussed with reference to the rate of cooling from the melt. THE Au-Ge equilibrium diagram features a rather deep eutectic near 27 at. pet Ge with a maximum solid solubility of 3.2 at. pet Ge in gold and is similar to the Ag-Ge, Ag-Si, and Au-Si diagrams.&apos; The present study of the effects of rapid cooling from the melt on the structure of Au-Ge alloys constitutes an extension of similar investigations2-8 in this laboratory on alloys of noble metals with germanium and silicon. Nonequilibrium hep structures have so far been obtained by quenching Ag-Ge2, 3 and Ag-Si4, 5 alloys from the melt; an Au-Si alloy of approximately eutectic composition has been found6 to solidify in a noncrystalline state. EXPERIMENTAL PROCEDURES Twenty-nine alloys prepared from gold of 99.9+ pet and germaium of 99.999 + pet purity were investigated. The method of alloy preparation, the technique of rapid quenching from the melt, and the X-ray diffraction procedures were similar to those described previously.3, 4 Essentially, small sections (-20 mg) of thin alloy rods (-1 mm diam) were rapidly heated up to 1200°C in a graphite crucible under argon and the liquid alloy ejected by a helium blast onto a polished copper strip held on the inner periphery of a rotating wheel. The resulting thin foils were examined with or without the copper substrate in a G.E. X-ray Diffractometer or in a 114.6-cm-diam Debye-Scherrer camera. RESULTS Table I gives the constitution of liquid-quenched Au-Ge alloys, as estimated from intensities of X-ray reflections from the corresponding phases, viz., a (fee solid solution), ß (hep phase), ? (tetragonal phase), and diamond-cubic (dc) germanium. Despite unavoidable variations in the quenching rates, the proportions of the phases in different alloys were generally reproducible and stable at room temperature. There was no evidence of quenching strain, since the a doublets were well-resolved in high-angle Debye-Scherrer reflections in all cases except where stacking faults in the a fee and ß hep structures contributed to X-ray line broadening. The ß and ? metastable phases showed signs of decomposition to the equilibrium a phase and germanium only after a few hours annealing above 100°C. A few alloys around the eutectic composi-

Jan 1, 1965

By E. F. Adkins, R. I. Jaffee, C. T. Sims

The effect of oxide dispersions on mechanical proberties of cobalt and cobalt-base powder-metallurgy alloys was investigated. This study shows that oxide dispersions added to pure cobalt greatly improve the high-temperature creep resistance of the metal. Dispersions in powder-metallurgy .cobalt alloys were muck less effective. COBALT is extremely valuable as an alloy base for certain high-temperature applications. Important examples may be found in the widespread use of cast and workable alloys in aircraft gas-turbine engines. With the increases in cobalt production in recent years, greater use may be made of cobalt-base alloys for high-temperature applications, provided

Jan 1, 1960

By J. S. Kirkaldy, D. G. Fedak

The extra degree of freedonz introduced by a second independetzt concentration in a tenzary system gives rise to the possibility of unstable planar phase interfaces in semi-infinite diffision layer couples. Diffusion paths which pass continuously in and out of too-phase regions of the phase diagram but which are not coincident with tie-lines give rise to super saturated zones which may be either adjacent to or isolated from planar phase interfaces, with corresponding nonisolated or isolated precipitates. Nonisolated precipitates are equivalent to morphological development of the interface. Selected couples in the ternary systems Fe-Ni-Cr and Cu-Zn-Sn have been examined nzetallographically and ifz the latter case both isolated and uo~zisolated precipitates have been observed. The diffusion path in one of the couples showing interface morphological developtnent has been examitled using electron probe microanalysis. IGNORING the spurious effects of preferential grain boundary diffusion and anisotropic crystal growth7 it can be unequivocally stated that it is impossible for a binary isothermal diffusion couple constructed of two unsaturated phases to sustain a nonplanar phase interface. Consider for demonstrative purposes the schematic phase diagram of Fig. l(a). Given an initial flat phase interface, semi-infinite boundary conditions and the internal boundary condition fixed by the constitution diagram, xB = xB(T), the unique solution of the diffusion equation requires a persistent flat interface. No other solution is possible. If, however, we anticipate the involvement of surface tension, then the internal boundary condition must be written xB = xB (T,Y) where r is the radius of curvature of a hypothetical nonplanar interface. The introduction of a new parameter such as r can be equivalent to the release of an internal constraint, so that a stable nonplanar interface may be possible after all. Consider a perturbation to the interface as indicated in Fig. 1(b). According to the Ostwald-Freundlich equation: which is applicable to a system of this constitution, the solubility of A in the matrix ß ,xB (Y), at a point of curvature r is given by where Va is the molar volume of the a-phase, R is the gas constant, and a is the interfacial tension. Since the right hand side is positive, xB(r) >xB cm, as indicated in Figs. 1(a) and 1(c). Accordingly, the perturbation will carry the interface concentration in a direction which is opposite to that which would sustain local equilibrium. Such a perturbation is necessarily moderated and the system is returned to its initial condition. This result is general for all binary couples since we can regard an interfacial perturbation as an attempt to precipitate within un-

Jan 1, 1962

By R. I. Jaffee, F. C. Holden, H. R. Ogden, A. G. Imgram

The tensile and notch tensile properties of four refractory metals (molybdenum, tungsten, niobium (columbium), and tantalum) and one alloy (Mo-0.5Ti) were investigated. All the materials were evaluated in bar form, and the molybdenum and Mo-0.5Ti also were studied in sheet form. The notch sensitivity of each material was evaluated on the basis of several criteria, including the notch-unnotch strength ratio, the ductility transition, and the fracture transitions. USE of refractory metals as structural materials in aircraft and space vehicles may subject them to low-as well as high-temperature environments. At elevated temperatures, the usefulness of a material usually is limited either by strength considerations

Jan 1, 1962

By H. R. Ogden

The notch sensitivity of titanium alloys is affected by impurity content, microstructure, and heat treatment. Using notch tensile properties to evaluate notch sensitivity, three commercial titanium-base alloys were investigated over the temperature range of -320o to 390°F. The alloys studied were Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo. Six interstitial levels were studied for each alloy in four mi-crostmctural conditions. The ff- 0 alloys were studied in both the annealed and heat-treated condition. All tests were conducted using 1/4-in. diam round tensile samples. The notched samples had a 50 pct notch with a notch sharpness (a/r) of 53, corresponding to Kt 6.3. Notch sensitivity was increased by increased interstitial content, low temperature, and acicular-type microstructures. The heat-treated, high-interstitial content - 13 alloys were more notch sensitive than the same alloys in the annealed condition. In addition, minima in the notch tensile-temperature curves were observed at temperatures near 32°F. These minima became more pronounced with increasing interstitial content. 1 HE increaseduse of titanium alloys in high strength applications at subzero temperatures requires that a better under standing of the low-temperature behavior of the alloys be obtained. At low temperatures, metals generally exhibit increased strength with lowered ductility and tohness. Notch sensitivity and the factors which influence it become more important as the strength level is increased and the temperature is decreased. Some of the factor s which affect notch sensitivity in ti- tanium alloys are composition, interstitial content, microstructure, and heat-treatment condition. In this paper, the results of a study of these variables on the notch sensitivity of three titanium alloys at temperatures from —320o to 390o are reported. The notch geometry selected for this program was chosen to provide a severe test of notch sensitivity. The ability of the metal to flow without initiating fracture under these severe conditions is reflected in the notch-strength values. Since notch strength is, in part, determined by the constraint exerted by the combined tensile stresses, the behavior of notch specimens reflects the properties of the material under combined stresses. For example, a material with a high notch-unnotch strength ratio may be expected to withstand the biaxial stresses encountered in a pressure vessel better than a material with a low ratio of notch-unnotch strengths. This implies that maximum strength alone is not a sufficient criterion for applications of this type. It further may be concluded that the various conditions that promote poor notch behavior also will affect adversely the performance of materials under combined stresses. In the alloys studied, these included low temperatures, high interstitial levels, and hasformed microstructures. EXPERIMENTAL PROCEDURES Three alloys, Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo, were purchased from commercial producers as 2-in.-dam rod stock. Oxygen and nitrogen were added to these alloys by remelting to obtain a variety of interstitial contents as shown in Table I. In order to Compensate for the much more potent strengthening effect of nitrogen compared with oxygen, an oxygen equivalent content is used to describe the total oxygen plus nitrogen contents studied. It has been suggested previously1 thatnitro-gen is approximately twice as effective in strengthening as oxygen, and carbon, to the extent it is in so-

Jan 1, 1962

By N. J. Feola, E. P. Klier

NOTCH properties of titanium materials have been extensively investigated in the impact test.&apos;-" For the most part the impact strength meas- ured suggests a ductile-brittle transition that lies at relatively high temperatures, thus indicating a possible notch sensitive condition at ambient temperatures. Recently it has been shown&apos; that the impact strength for unalloyed titanium, as for aluminum alloys, may be a nonsensitive index of notch sensitivity as provided by the notch strength as measured in the notch tensile test. The notch strength for unalloyed titanium was found to depend on the nitrogen and carbon contamination levels. In the present work the levels to which oxygen, nitrogen, and carbon contaminants can be tolerated without leading to excessive em-

Jan 1, 1958

By W. Hume-Rothery

RECENT interest has been shown in utilizing solid-state techniques for obtaining large oriented grains in the Alnico Alloys.1-4 Unfortunately, due to the inherent brittleness of these materials it is difficult to introduce sufficient imperfections by deformation to support the nucleation and growth of new, recrystallized grains. As a result, recrystal-lization methods for obtaining large grains, such as the strain-anneal technique, do not appear to be feasible. Steinort et a1.2 used a combination of a thermal gradient and internal strains to obtain large single crystals of Alnico 5 from a poly crystalline casting by annealing at temperatures above 1200°C. It was suggested that the strains were the result of the precipitation of the y phase which exists between -850° and 1200°C. The purpose of the present study was to determine if the grain size of the cast Alnico alloys can be markedly increased by solid state techniques involv-

Jan 1, 1963

By P. Gordon, A. S. Iyer

IN a paper on the mechanical behavior of heat-treated steel, N. H. Polakowski&apos; put forward arguments to the effect that the stored energy resulting from the deformation of metals should be reduced during the inital stages of subsequent deformation carried out under conditions which produce work softening. At the time (1957) the only energy measurements available as indirect evidence on this point were the results of M. M. Degtyarev,2 some of which Polakowski reproduced in his Fig. 6, and which are again reproduced here in Fig. 1. The solid lines in the upper part of Fig. 1 are Degtyarev&apos;s, the dashed Lines Polakowski&apos;s prediction of the true trend of the stored energy in copper samples pre-strained in tension and then given various amounts of subsequent compression. The accuracy of this prediction has been borne out by some experiments carried out on American Smelting and Refining Co. copper (99.999&apos; percent Cu) by the present authors. Bars of this copper about 0.4 in. in diam and 12 in. long were prepared by vacuum melting and casting, followed by cold forging and swaging in several stages of about 40 pct reduction in area with intermediate recrystallization anneals. After the final anneal one bar was deformed in tension to 30 pct elongation; the gage length was then cut into several samples which were given axial compressions of various amounts. The hardness of

Jan 1, 1960

By E. Parthe, J. P. Pemsler

TWO references can be found in the literature concerning the ternary system uranium-tantalum -carbon. C. H. Schramm, P. Gordon, and A. R. Kaufmam reported in this Journal1 on the existence of the ternary carbide "UTa10C4." They also report a second face-centered-cubic carbide phase in the system U-Ta-C, which they denote as "white" phase. The publication includes a reproduction of a Debye-Scherrer powder photograph of "UTa10C4" and a list of the sin2 0 values of this compound. H. Nowotny, R. Kieffer, F. Benesovsky, and E. Laube2 report the complete solid solubility between TaC and UC with a B1 structure. Since the ternary phase "UTa10C4" lies very close to the binary system Ta-C, and the established phase Ta2C with a C27 structure had not been mentioned by Schramm et al., it was thought worthwhile to compare the patterns of "UTa10C4" with Ta2C. The strong lines of the given pattern were indexed on a hexagonal unit cell with the approximate cell parameters a = 3.09A and c = 4.93A. These are the values reported for Ta2C in the literature.3 The correspondence between reported and calculated sin2 8 values may be studied in columns 4 and 5 of Table I. The agreement is fair, but there remain weak lines which cannot be assigned to the hexagonal unit cell. The extinctions correspond to those of Ta2C, but a comparison of the calculated and observed intensities of the Ta2C lines (columns 2 and 3) with those of the corresponding lines of "UTa10C4" (column 6) show occasional deviations. To clarify this situation, four new samples were prepared. The compositions of these samples were chosen in such a way as to observe any existing ternary phase in the system TaC-UC-U-Ta. The samples were arc melted in an inert atmosphere and annealed at 1100°C for 36 to 72 hr. Compositions of the samples determined by chemical analysis are given along with the results of X-ray investigations in Table 11. The following conclusions may be drawn from these data: a) No ternary compounds occur in the section TaC-UC-U-Ta of the ternary system Ta-U-C. The "white" phase reported by Schramm et al. corresponds to a solid solution between TaC and UC. Only one three-phase field exists: C27-B1-A2. (Both tantalum and ? uranium have body-centered-cubic A2 structures.) The a uranium observed in sample 4 transformed from the high-temperature ? phase on cooling. b) The phase Ta2C with a C27 structure extends into the ternary system. "UTa10C4" is, therefore, a uranium-enriched Ta2C. Good agreement is ob-

Jan 1, 1960

By D. N. Seidman

In the course of a study of the electronic and thermodynamic properties of Pb-Se alloys it was found necessary to have an accurate knowledge of the phase diagram. However, the literature is in disagreement as to whether or not a monotectic reaction occurs in the lead rich portion of the phase diagram. Pelabonl reported only a two-phase region consisting of lead-rich liquid and solid PbSe extending from almost pure lead to the compound PbSe, and gave the melting point of PbSe as 1065°C. The data of Friedrich and Leroux2 are in general agreement with this type of diagram, with the melting point of the compound being 1088°C. However, Nozato and Igaki by inverse rate thermal analysis observed a monotectic reaction isotherm exlacing at 860°C with a monotectic composition of 20.5 at. pct Se. The miscibility gap in the liquid state extends from 7.5 to 20.5 at. pct Se. Hansen and Anderko4 accepted Nozato and Igaki&apos;s phase diagram in the region of the lead-rich monotectic. To reinvestigate this portion of the phase diagram, both thermal analysis and metallographic examination of various compositions were performed. The thermal analysis apparatus was constructed according to the specifications of the National Bureau of Standards. A t/t-l pct Rh thermocouple was calibrated against the melting point of copper (NBS), zinc (NBS), and antimony (A. D. Mackay), the emf being measured with a Rubicon Type B potentiometer sensitive to lpv. The absolute accuracy of the thermal analysis obtainable with this system is ± 0.5oC. Starting materials were semiconductor grade lead and selenium purchased from the American Smelting and Refining Co. Both elements were 99.999 pct pure with only trace impurities detected upon spectroscopic examination. One hundred galloys were sealed in quartz crucibles with a central thermocouple well under a vacuum of less than 1 p. This procedure prevented any composition change due to vaporization during the run. Cooling curves were obtained on the alloys listed in Table I. Data was taken by the direct method at cooling rates ranging between 1/2 to 2°C per min. The alloys were heated well above the liquidus and shaken vigorously to insure homogeneity. No evidence of an arrest indicative of the monotectic reaction was observed, and the two-phase region reported by Pelabonl and Friedrich and Leroux? was confirmed in general, although our data give higher liquidus temperatures than Friedrich and Leroux. The melting point of stoichiomet-ric PbSe determined for two different samples was 1080.7 0.5oC. The results of this investigation are compared with Nozato and Igaki&apos;s data in Fig. 1. To Complement the thermal analysis data, an 86 at. pct Pb specimen was examined microscopically. This composition was in the center of the miscibility gap reported by Nozato and Igaki.3 The alloy was heated to 1000°C, held for 1/2 hr, and water quenched. The specimen was polished using standard metallographic techniques for lead. The alloy was etched with an acetic-nitric acid etchant for 10 min at 45°C. Microscopic examination did not indicate the existence of two separate layers or solidified droplets imbedded in a matrix, as would be expected if a miscibility gap were present. The mi-crostructure shown in Fig. 2 consists of uniformly dispersed, dendritic PbSe in a lead-rich matrix.

Jan 1, 1962