By Dengfu Chen, Yunwei Huang, Mujun Long, Kui Lv, Pei Xu, Lin Bai

The surface temperature of continuous casting slab in the secondary cooling zone is a key parameter of production control. However, the accuracy of radiation temperature measurement of high temperature casting slab is greatly affected by the environmental factors, such as water vapor, spray, water film and other participational medias during continuous casting process. In this paper, the radiation characteristics of water vapor and its influences to radiation temperature measurement of continuous casting slab were investigated. Based on the database HITRAN 2004 and the measuring principle of monochrome thermometer & colorimetric thermometer, the measuring errors under different operating infrared spectral wavelength were compared. Results showed that spectral region with wavelength nearby 1.0μm or 1.6μm would be the optimum for high temperature infrared thermometer used under the conditions with moist steam, water spray and water film at the secondary cooling zone in steel continuous casting.

Jan 1, 2016

By Jiechao Liu, Lijian Luo, Yubao Ma, Bo Zhang, Yanfeng Yang, Xin Hong, Luming Liu, Jienan Liu

Reduction kinetics of stainless steel slag in iron bath smelting reduction was studied at the temperature of 1500℃ ~ 1650℃. It was concluded that the reduction process consisted of two parts. That is to say smelting reduction was controlled by stainless steel slag melting initially and by interface reaction later. In order to increase smelting reaction rate, the melting point of slag should be decreased at the first stage and adjust the liquidity of slag at later stage. Smelting reaction rate will be accelerated by means of optimize the slag content. The optimal reduction result that all most all of the chromium in slag been recovered was obtained in temperature was 1500℃, basicity of slag was 1.0~1.2, the value of Al2O3+MgO was 25%.

Jan 1, 2015

By Yapeng Zhang, Zhiwen Shi, Chaoquan Yao, Fei Wang, Xinyu Li, Jianliang Zhang

A great deal of iron ores which have special elements have been applied in the sintering process with the decreasing of high-grade quality iron ores resources. In this paper, the laterite nickel ores were added into three different kinds of iron ores respectively to make liquid phase formation research by software of Factsage and high temperature characteristic sintering experiments. The results showed that the adding proportion of laterite nickel ores should be less than 15% when the high temperature properties of the mixing ores were well. Increasing the mixing ration of laterite nickel ores in the sintering blending would play an important role in the reduction of the sintering cost.

Jan 1, 2015

By Cailing Zhen, Jian Pan, Deqing Zhu, Xianlin Zhou, Yanhong Luo, Guixiang Huang

The grate-kiln process has been widely applied for oxide pellet production with the quick development of steel industry in China, but ring formation takes place which adversely affects the productivity and properties of fired pellets. Rotary kiln at high temperature seems a black box, and ring formation is difficult to measure directly by current technology. It’s of great importance to monitor ring formation during firing of pellets. Therefore, a method for estimating the thickness of ring formation in rotary kilns was studied, based on working out theoretically the relationship between ring thickness and the outside surface of the kiln, according to steady-state heat transfer across a cylinder, which provides a soft-sensing technique for ring formation at high temperature, and achieves stable pellet production .

Jan 1, 2015

By Vinicius Alves Gomes, Jean Igor Margem, Frederico Muylaert Margem, Sergio Neves Monteiro, Marina Rangel Margem

The interface between the matrix and the reinforcing fiber plays an important role in the efficiency by which an applied load is transmitted through the composite structure. The shear stress at the fiber/matrix interface can be associated with this load transference and, consequently, affects the composite strength. In the present work, pullout tests were used to evaluate the interfacial shear stress of malva fiber in epoxy matrix composites. A small critical length was found for the malva fiber embedded in epoxy, which corresponds to a relatively weak fiber/matrix bond and lower interfacial strength.

Jan 1, 2015

By Gavin Lind

The Minerals Council of Australia (MCA), through its Minerals Tertiary Education Council (MTEC), builds capacity in higher education in the core disciplines of mining engineering, metallurgy and minerals geoscience. Over the past fourteen years, this all-of-industry approach in securing the long-term supply of these critical skills (which remain a chronic skills shortage for the Australian minerals industry) through nationally collaborative programs across sixteen Australian universities delivers spectacular and sustainable results for the industry. These unique, world-first programs are built on a healthy platform of dedicated industry funding and in-kind support and forms part of the MCA’s broader uninterrupted, sustainable education and training pathway to increase workforce participation, workforce diversity and workforce skills, regardless of the business cycle in the industry. This paper will highlight the origins, iterations and current successful programs of MTEC, including its future vision, and presents a mechanism for industry and academia to collaborate to address future professional skills needs in the minerals industry globally.

Jan 1, 2014

By M. Wenzel, Dang Thanh Tung, Nguyen Anh Duc, Nguyen Huu Luong, Dang Van Sy, N. Kelly, K. Gloe, K. Kretschmer, Phuc Nguyen Le, K. Schnaars, S. Robles M, L. Götzke, J. J. Weigand

The recovery of rare earth metals from secondary sources has attracted much attention due to their ever expanding demand in the high-tech industry. The studies reported here focus on the hydrometallurgical recovery of lanthanum and cerium from spent fluid catalytic cracking (FCC) catalysts in a two-step process: leaching with nitric acid and solvent extraction by tri-n-butyl phosphate (TBP) and di(2-ethylhexyl)phosphoric acid (D2EHPA). The experiments show a high dissolution yield of about 93% lanthanum and 42% cerium in a single leaching step with 2 M (126 g/L) HNO3 at 80 °C; only 11% aluminum has been dissolved simultaneously. In the subsequent solvent extraction step the best results for this leach liquor could be achieved using a 1:1 mixture of 25% (v/v) TBP (0.92 M) and 25% (v/v) D2EHPA (0.76 M) in n-decane without the need for any pH adjustment. In that case La(III) and Ce(III) can be extracted with 60% and 74% yield respectively in one stage from the majority of accompanying matrix elements. In particular no extraction of Al(III) could be observed under these conditions.

Jan 1, 2016

By Kenji Monden

A simple technique is presented to evaluate optical property of biomimetic microlens array (BMA) as an antireflective surface on a polydimethylsiloxane (PDMS) sheet. The integration of these structures is done by a thermoforming process. We have only UV-VIS spectrophotometer for optical evaluation apparatus. The transmittance of the sheet is measured with angled sample holder. The 50 deg. transmittance of 270nm pitch BMA on PDMS sheet increases from 87 to 92% after the moth-eye structure is introduced. The transmittance of 350nm pitch BMA on PDMS sheet increases from 87 to 96% after the moth-eye structure is introduced. The transmittance increases with increasing pitch of BMA. The results obtained using UV-VIS spectrophotometer with handmade sample holder.

Jan 1, 2015

By Joo Hyun Park, Soo Sang Park

The distribution behavior of Pb between molten copper and FetO-SiO2 (-CaO, Al2O3) slags was investigated at 1473 K (1200 oC) and p(O2)=10-10 atm in view of the reaction mechanism of Pb dissolution into the slag. The distribution ratio of Pb (LPb) decreases with increasing CaO content (~6 mass pct) irrespective of Fe/SiO2 ratio (1.4~1.7). However, the addition of alumina into a slag with Fe/SiO2=1.5 linearly decreases the LPb, whereas a minimum value is observed at about 4 mass pct Al2O3 at Fe/SiO2=1.3. The log LPb continuously decreases with increasing Fe/SiO2 ratio, and the addition of Al2O3 (5 to 15 mass pct) into the silica-saturated iron silicate slag (Fe/SiO2 < 1.0) yields the highest Pb distribution ratio. The log LPb linearly decreases by increasing the log (Fe3+/Fe2+) value. The Pb distribution ratio increases and the excess free energy of PbO decreases with increasing Cu2O content in the slag. However, from the viewpoint of copper loss into the slag, the silica-saturated system containing small amounts of alumina is strongly recommended to stabilize PbO in the slag phase at a low Cu2O content.

Jan 1, 2014

By Jiang Feng, Zhang Libo, Peng Jinhui, Guo Zhanyong, Ju Shaohua, Lei Ting

The clean utilization of the residue containing chloride, CuCl residue, produced from zinc hydrometallurgy is very important for the recycle of valuable metals. And drying is the main process in recycling. In this study, response surface methodology was used to optimize operating conditions of the drying of CuCl residue in a convection oven and desirability function used as the methodology for the optimization. Optimization factors were air temperature (80–100°C), material thickness (10–25mm) and process time (80–120min) while investigated responses was final moisture content. The optimum conditions were found to be the temperature of 95.48°C with the material thickness of 13.47mm for the process time of 89.48 min. Under optimum conditions, the predicted moisture content of CuCl residue was 4.11% while the experimental date was 4.13%. The experimental value after process optimization was found to agree satisfactory with the predicted value. After drying, XRD was used to analyze the main phases of CuCl residue. The CuCl residue is made up of CuCl,Cu2O, ZnS and other compounds.

Jan 1, 2015

By B. R. Davis, Neale R. Neelameggham, R. E. Brown

The element Calcium element has a unique place in the production of etals, intermetallics and other compounds. The unusualness arises from the fact that we have several possible reductants – metallic calcium, calcium carbide, calcium cyanamide and calcium hydride. A review of how metallic calcium is manufactured and utilized is presented. The difficulties involved in producing the metal in large quantities and price implications are noted. . Fundamental thermodynamics of how these act as reductants are shown, along with the historic application of these in metal production during the past century and a half. Alternate applications as to how to control the cost of the reductant is indicated, such as the numerous attempts in making low cost titanium utilizing direct or indirect calcium reductant.

Jan 1, 2014

By Guanyong Shi, Zhihe Dou, Cong Wang, Ting'an Zhang, Hongyan Zhang

We prepared the CuCr alloy by thermit reduction-electromagnetic casting. But there are the defects such as stomata and oxide inclusions in CuCr alloy. In this paper, the existing state and distribution of inclusions and stomata in CuCr alloy are systematically analyzed. The alloy was characterized via SEM, EDS and metallographic microscope, in which the existing state and micro-structural defects of inclusions are analyzed. The results show that: there are three distinct areas: copper-rich areas, chromium-rich areas and the inclusion areas. Inclusions are mainly in the form of stomata and Al2O3 phase, mainly locating in the copper-rich phase and the interface area of chromium-rich phase and the copper-rich phase. Then, the composition of phases of the smelting slags and alloy were characterized via XRD. The results show that: the slag consists of Al2O3 and a little of Cr, the alloy consists of Cr, Cu and a little of Al2O3.

Jan 1, 2015

By Shengfan Zhou, XUEWEN WANG, Bianfang Chen, Mingyu Wang

Vanadium was leached from roasted stone coal by NaOH solution, and the effect of leaching temperature, leaching time, addition of NaOH, liquid to solid ratio, the grinding fineness of stone coal, and stirring speed on the vanadium leaching rate was studied. The kinetics analysis for the process is presented by the shrinking core model. The results show that the vanadium leaching ratio of roasted stone coal can be beyond 75% at the 6% NaOH addition, leaching temperature of 95°C, leaching time of 7h, liquid to solid ratio of 1.2mL/g, and grinding fineness of 0.111mm. The leaching process is controlled by interfacial reaction kinetics and the apparent activation energy was 59.36kJ/mol.

Jan 1, 2016

By Shizhe Liu, Bing Li, Heng Wang, Zuxin Zhao

In this paper, cyclic voltammetry and chronoamperometry have been applied to investigate the effects of Nd2O3 concentration on the anode effects, critical potential for the anode effects and Nd2O3 reduction in LiF-NdF3-Nd2O3 melts at 950℃. The results show that the oxidation peaks in the potential of about 2.7V are attributed to the oxygen ions oxidation and the peak current density increases with Nd2O3 concentration increase from 0 to 0.5wt%. The critical potential caused the anode effects shifts to 0.3V more positive value as Nd2O3 content in the melts decreases from 0.01wt% to 0.5wt%. The cyclic votammograms on W electrodes in the LiF-NdF3-Nd2O3 melts present two pairs of reduction and oxidation peaks, indicating that the reduction of Nd ions in the LiF-NdF3-Nd2O3 melts in two steps rather than one step.

Jan 1, 2014

By Kai Kang, Jun Bao, Shouping Liu, Xiao Sun

Powder characteristics have a significant influence on selective laser melting (SLM) process. In this research, particle size, surface contour and the microstructure of IN718 powder used in SLM were tested, and the physical and chemical changes during heating process of the powder were investigated as well. The shape characteristic and fluid properties of IN718 powder were defined and measured. It is shows that most particles of IN718 powder exhibited nearly spherical shapes, and the particle size is about 22.95μm. On this basis, IN718 sample was fabricated by SLM process using the powder and the microstructure of the fabricated sample was investigated. The results indicated that the sample has a dense microstructure, no macro-defects but a few micropores and porosity. Compared with the powder, there was no new phase formed in the sample and melting point of the sample was little less than that of the powder.

Jan 1, 2015

By O. P. Pandey, Rama Arora, Gurmel Singh, Suresh Kumar

The tribological behavior of Dual Particles Size (DPS) rutile reinforced LM13 alloy composite was investigated under varying applied pressure from 125 kPa to 625 kPa at a constant sliding speed of 1.6 m/s. In the present studies, 15 wt.% of rutile particles of different sizes (50-75 μm and 106-125 μm) are reinforced in the Al-12Si alloy (LM13) by liquid metallurgy route. Microhardness of the prepared samples was measured in different phases. Microstructure, wear mechanism and surface morphology of the wear surfaces and debris was observed under optical and scanning electron microscope. The change in wear behavior has been explained with reference to the observed EDS analysis of the wear track and debris. However, an interesting change in wear feature, mild to severe wear transition at critical pressure was noticed in wear behavior of the composite. The Al-DPS composite has immense potential to be used as a component material for tribological applications.

Jan 1, 2015

By Zhengjie Chen, Wenhui Ma, Jijun Wu, Kuixian Wei

The gasification reactivity of PC (petroleum coke), strengthened by addition of different potassium carbonate proportions using different grinding medium, was investigated by using thermogravimetric analysis (TGA). Results showed that the gasification reactivity of PC not only increased with the increase of catalyst-loaded, but also showed the effective improvement by anhydrous alcohol. The PC was mixed with potassium carbonate [K2CO3] catalyst at 0.5%, 0.8%, 1.0% and 1.5%, and then ground wet with distilled water. The CO2-gasification rate of PC was only 77.35%, 80.55%, 84.07% and 85.88% under the gasification temperature 1100 °C and holding time 120 min, at different K2CO3 respectively. However, when the PC was ground in anhydrous alcohol at the same condition of catalyst-loading, the gasification rate of PC reached 95.43%, 96.63%, 95.50% and 95.61% at the holding time of 108 min, 101 min, 74 min and 35 min, respectively. It was shown by FTIR, SEM and EDX determinations that the anhydrous alcohol used as the grinding medium can further improve the gasification reactivity of PC when compared with the distilled water.

Jan 1, 2016

By Pertti Koukkari, Nagendra Tripathi, Karri Penttilä, Justin Salminen

A computational fluid dynamic model for a novel flash ironmaking process based on the direct gaseous reduction of iron oxide concentrates is presented. The model solves the threedimensional governing equations including both gas-phase and gas-solid reaction kinetics. The turbulence-chemistry interaction in the gas-phase is modeled by the eddy dissipation concept incorporating chemical kinetics. The particle cloud model is used to track the particle phase in a Lagrangian framework. A nucleation and growth kinetics rate expression is adopted to calculate the reduction rate of magnetite concentrate particles. Benchmark experiments reported in the literature for a nonreacting swirling gas jet and a nonpremixed hydrogen jet flame were simulated for validation. The model predictions showed good agreement with measurements in terms of gas velocity, gas temperature and species concentrations. The relevance of the computational model for the analysis of a bench reactor operation and the design of an industrialpilot plant is discussed.

Jan 1, 2014

By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

A novel ironmaking process is under development at the University of Utah aimed at producing iron directly from iron oxide concentrate in a flash reactor. This process will reduce hazardous emissions and save energy. The kinetics of magnetite reduction with hydrogen was previously investigated in our laboratory in the temperature range 1150 to 1400 oC at large temperature increments (~100 oC increments). Due to the significant melting that occurs above 1350 oC, the reduction kinetics was measured and analyzed in two distinct temperature ranges of 1150 to 1350 oC and 1350 to 1600 oC (~50 oC increments). Experiments were performed using magnetite concentrate particles of different sizes under various hydrogen partial pressures and residence times. Reduction degrees of more than 90 % were achieved in a few seconds at temperatures as low as 1250 ºC. Different rate expressions were needed to obtain reliable agreement with experimental data.

Jan 1, 2016

By M. Z. Quadir, M. A. Islam, P. J. Hazell, G. J. Appleby-Thomas, J. P. Escobedo

The mechanical response of closed-cell aluminium metallic foams subjected to low and high strain-rate loading has been investigated. A set of quasi-static and dynamic (shock) compressive tests have been conducted on closed-cell aluminium foams (CYMAT) with densities of 0.50 and 0.30 g/cc. Post-mortem characterization via optical microscopy and electron backscatter diffraction (EBSD) was performed on pristine and deformed specimens to elucidate the dominant deformation mechanisms in these materials. The combination of these techniques allowed for the assessment of critical deformation parameters such as changes in cell geometry and morphology, as well as microstructural evolution and deformation of the aluminium cellular network. These findings aim to aid in the design and development of optimized material structures for impact and blast protection.

Jan 1, 2015