By Junwei Han, Wenqing Qin, Dawei Wang, Fen Jiao, Wei Liu

The removal of iron impurity from zinc calcine was studied by magnetization roasting and magnetic separation. The effects of roasting temperature, magnetic intensity, ore grinding, and leaching pretreatment on iron grade and recovery were investigated. The results indicated that iron recovery increased with the increase of roasting temperature or magnetic intensity, while iron grade was always less than 22%, depending on the fact that the magnetite were not liberated completely. The good liberation was difficult to be achieved by ore grinding but was easier by acid leaching, since the magnetite grains were very fine. After the leaching pretreatment, the recovery of 76.31% with iron grade of 53.24% was obtained by one roughing and cleaning. The SEM/EDS analysis showed that a part of sphalerite, zinc ferrite and other gangues were mixed into the iron concentrate, while some of fine magnetite was reported to the tailing.

Jan 1, 2016

By QIE Jun-mao, DONG Fang, DENG Hao-hua

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.

Jan 1, 2015

By Alicia Esther Ares, Carlos Enrique Schvezov, Alejandra Silvina Roman, Claudia Marcela Méndez

In this paper the structure of aluminum based alloys and their corrosion behavior by using different electrochemical techniques as characterization methods are considered. Currently, it becomes imperative to know the role of the Al2Cu against the susceptibility to corrosion of these alloys. The present work aims to studying the electrochemical behavior of aluminum base alloys with the following compositions: Al-1wt.%Cu, Al-4.5wt.%Cu and Al-15wt.%Cu (with different grain structures), in 1M NaCl solutions, at room temperature. Cyclic potentiodynamic polarization tests were performed and were found that the alloys with more than 1wt.%Cu in the matrix have an unstable behavior and without tendency to reach passivity. The equivalent circuits derived from electrochemical impedance spectroscopy technique (EIS) generally showed two capacitive contributions. The susceptibility to corrosion becomes a complex function, not only of copper concentration and structure, but also with interdendritic spacings and distribution of phases in the alloys.

Jan 1, 2015

By Shaik Jeelani, Esperidiana A. B. Moura, Vijaya K. Rangari, Roberta A. Lima, Rene R. Oliveira

This work present the preparation and characterization of biodegradable nanocomposites based on aliphatic-aromatic copolyester (PBAT)/polylatic acid (PLA) blend reinforced by TiO2 nanoparticle. The biodegradable polymeric nanocomposites were prepared by melting extrusion process using a twin-screw extruder machine. The influence of the TiO2 nanoparticle addition on mechanical and thermal properties of PBAT/PLA blend was investigated by tensile and impact tests, SEM, DSC and XRD analysis and the correlation between properties was discussed.

Jan 1, 2015

By Manju Gurung, Birendra Babu Adhikari, Keisuke Ohto, Hidetaka Kawakita, Katsutoshi Inoue, Shafiq Alam

Novel bio-adsorbent gel was prepared by immobilizing functional groups of glycidyltrimethyl ammonium chloride, a kind of quaternary ammonium chloride, onto polymer matrices of persimmon extract for the recovery of precious metals such as palladium(II) and platinum(IV) from chloride media. It was found that this adsorption gel exhibits high selectivity to gold(III), palladium(II) and platinum(IV) over base metals such as copper(II) and iron(III) while crude persimmon extract, the feed material, exhibits high selectivity only for gold(III). From the adsorption isotherms study, the maximum adsorption capacities for gold(III), palladium(II) and platinum(IV) were evaluated as 3.30, 1.67 and 1.00 mol/kg, respectively. Those for palladium(II) and platinum(IV) are higher than those of simple quaternary ammonium chloride type of chemically modified persimmon tannin gel and commercially available anion exchange resin.

Jan 1, 2016

By Yi Tan, Kazuki Morita, Yaqiong Li

Molten Si-Al alloy, with the addition of Sn, was used for metallurgical grade Si purification by a low-temperature solidification method, with the aim of improving the recovery rate of Si. In this ternary melt, bulk Si was grown with a planar front by a directional solidification process under a well-controlled thermal gradient and growth rate conditions, thereby reducing the contamination of solvent metals. Effects of cooling rate, amount of Sn addition, and temperature gradient on the quality of bulk Si were determined. The criterion for constitutional supercooling for single-phase growth from multicomponent melts was employed to evaluate the growth process.

Jan 1, 2015

By Wan Entong, Xie Junlin, Jiann YangHwang, Yang Chengwei, Chen Junfu, Zhang Jianjun, Cao Tongyou, He Feng, Peng Zhugang, Fang De

During the solidification process of peritectic steel (PS), the peritectic reaction often causes volume contraction which associated with surface longitudinal cracks, and using mould flux with low heat flux density help for alleviating surface longitudinal cracks. New peritectic steel mold flux with Co2O3 doping reduced the heat flux density, and the optimal content was found to be 2.0 wt %. Furthermore, basicity and Na2O addition were designed, and the minimum heat flux density required basicity of 1.4 and 10.0 wt %. Na2O content. As a result, the optimal peritectic composition was CaO(35.67wt% ), SiO2(25.48 wt %)，Al2O3(3.7 wt %)， MgO(2.53 wt %)，Na2O(10 wt %)，CaF2(14 wt %)，Co2O3(2 wt %).

Jan 1, 2015

By Toshiyuki Nohira, Eiichi Takeuchi, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The Dy-Nd-Pr-Ni alloy sample was prepared by cathodic potentiostatic electrolysis at 0.65 V (vs. Li+/Li) for 1 h using a Ni plate in a molten LiCl-KCl-DyCl3-NdCl3-PrCl3 system at 723 K. The highest mass ratio (Dy/Nd+Pr) in the alloy sample was observed to be 50 at 0.65 V. Anodic potentiostatic electrolysis at 2.20 V for 12 h was conducted using the Nd-Fe-B magnet electrode in a molten LiCl-KCl system. All elements were almost dissolved from the magnet, and the original form of the magnet disintegrated. After anodic potentiostatic electrolysis at 2.20 V, cathodic potentiostatic electrolysis was conducted at 1.00 V for 5 h using a Mo plate in order to remove the dissolved Fe from the bath. Finally, cathodic potentiostatic electrolysis was conducted at 0.65 V for 12 h using a Ni plate. The mass ratio of Dy/Nd in the alloy sample was determined to be about 18.

Jan 1, 2015

By Huimin Lu, Liyuan Zhao, Zhijiang Gao

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.

Jan 1, 2015

By Larry Twidwell, Ed Rosenberg, Courtney Young, Sean Dudley, William Gleason, Maureen Chorney

Experimental and industrially produced polystyrene and silica resins are tested for recovery capabilities of Rare Earth Elements (REE). Testing regimes being used are typical of resin analysis. Inductively Coupled Plasma-AES results indicate that preferential separation and recovery is possible in the adjusted pH range of2 to 10, solution conditions, and resin type. Testing conditions are resulting in structure modification of the composite resin as indicated by X-Ray Diffraction, Differential Scanning Calorimetry, Scanning Electron Microscopy, Mercury Porisometry, and density analysis. Resin modification indicates both surface and internal structure alteration outside of reported standard behavior of resins. Structural changes have ramification for both Rare Earth Recovery RER and traditional resin operations. Analysis shows that the resin uptake of REE can be manipulated for concentration. Further analysis with SEM work indicates that widespread surface and interior modification is taking place as resins load with REE. This modification is leading to pore rupture and particle breakage. Further investigation is being performed to determine the mode of breakage.

Jan 1, 2015

By Itavahn Alves da Silva, Izabela Diniz Duarte, Carlos Antonio da Silva, Varadarajan Seshadri

Mathematical modeling using computational fluid dynamics has been employed to assess the thermal losses in a steelmaking ladle. Thermal losses lead to thermal stratification and convective flow inside the ladle. The effects of preheating, mineralogical and physical characteristics of the lining as well as thickness of slag cover have been studied and the results obtained from application of the model have been discussed.

Jan 1, 2016

By Naiyang Ma

High zinc concentration in basic oxygen furnace (BOF) steelmaking offgas (OG) cleaning system solid wastes is one of the main barriers for recycling of the solid wastes in sintering – blast furnace ironmaking process. One of the possible solutions is to utilize zinc-free scrap in BOF steelmaking so that the BOF OG solid wastes will not be contaminated with zinc and can be recycled through sintering – blast furnace ironmaking. This paper describes a model for helping to decide whether to use zinc-free scrap in a BOF process. A model computing marginal price increment of zinc-free scrap is developed. The marginal price increment is proportional to value change of the BOF OG solid wastes after and before using zinc-free scrap, to ratio of BOF solid waste rate to purchased galvanized scrap rate, and to price of galvanized scrap. Due to the variations of consumption rate of purchased galvanized scrap and home galvanized scrap, iron ore price, landfill cost, and price of purchased galvanized scrap, using zinc-free scrap in a BOF process might be economically feasible for some ironmaking and steelmaking plants or in some particular market circumstances.

Jan 1, 2015

By N. G. Azeredo

This work dealt with the evaluation of engineering structural clay brick samples that were sintered at estimated temperatures of 700 and 800°C. They were collected in a red-brick plant in Campos dos Goytacazes, RJ, Brazil. From a lot, a sample already sintered in its kiln at 700°C were collected and also a sample from the same lot only dried by the air, which were then sintered at 800°C controlled temperature. The samples were subjected to Brazilian Standard tests (ABNT NBR 15270:2005) to determine their geometric, physical and mechanical properties. In order to be classified as structural clay brick it is required minimum 3.0 MPa for the characteristic compressive strength (fbk) to be suitable for up to five floors structural building applications. We also used the Weibull Probability Plot and Weibull Maximum Likelihood Estimation to evaluate distribution parameters in order to compare the results of compressive strength obtained in the tests.

Jan 1, 2015

By Geoffrey A. Brooks, M Akbar Rhamdhani, Md Saiful Islam

A novel electrically-enhanced metal purification using slag has been developed. This was achieved by applying DC potential between liquid metal and slag phases. The concept was demonstrated through small-scale experiments at temperatures of 1500-1600oC for the removal of boron from Si-B melt using CaO-SiO2-16wt%Al2O3. Silicon (containing B) and slag were reacted in an alumina crucible in a resistance tube furnace. A circuit was produced by immersing graphite rods into the silicon bath and the slag layer. Electrical potential differences of up to 3.5 V were applied during the reactions. The reaction rates, the opencircuit voltages and short-circuit currents (in the case when the potential was applied) were then measured and determined for various slag to silicon ratio. It has been shown from this study that both the apparent rate and the boron partition ratio were increased by a factor of approximately 1.6.

Jan 1, 2014

By Dan Wang, Qian Xu, Guangshi Li, Xionggang Lu, Xingli Zou, Zhongfu Zhou, Hongwei Cheng, Changyuan Lu

The preoxidation of the ore has a profound significance to the concentration, separation and purification of nickel and copper from the lean complex ore. In this paper, the natural Ni-Cu sulfide mineral samples under the elevated temperature condition in air were investigated, as well as under isothermal condition at 600 oC in air. The mineralogical characterization was studied using XRF, ICP and the Rietveld method. The oxidation behavior and the element migration of the Ni-Cu sulfide ore were studied by XRD, SEM-EDS and TG. The XRD Rietveld method was successfully developed in the phase identification and quantification of this complex ore powder sample. The oxidative intermediates (Cu/Ni-ferrite) were detected by XRD, and the process of the element migration was obviously revealed by the line scans using SEM-EDS. It is the preoxidation of this mineral that provides guidance for the extraction of valuable metals from low-grade Ni-Cu sulfide ores in the future.

Jan 1, 2015

By Jilai Xue, Jun Zhu, GermainKouma Ndong, Luxing Feng

High-temperature corrosion behaviors of Fe-Ni-Cr alloy as inert anodes for aluminum electrolysis have been studied. The effect of anodic overpotential on layer growth of anodic surface is specially considered. The corrosion layers on the anodes tested were analyzed using XRD and SEM-EDS to provide a fundamental understanding of the layers growth at metallic anode surface. The dissolution of the scale layers on the metal anode occurred with low overpotential, while AlxM3-xO4 spinel phase within the scale layers was found with an increased overpotential. A mixture of multiple MyO layers existed on the anode substrate. The results may be useful for understanding and controlling the corrosion behaviors of Fe-Ni-Cr anode for potential application in aluminum electrolysis.

Jan 1, 2015

By Pedro A. Netto, Sergio N. Monteiro, Foluke S. de Assis, Rômulo L. Loiola, Frederico M. Margem

Banana fibers are among the lignocellulosic with great potential for use in polymer composites, such as the variety from the Musaceae family, due to its low density and good mechanical properties. In this work, epoxy matrix composites incorporated with continuous and aligned banana fibers were tested for their flexural behavior. Specimens with up to 30% in volume of fibers were bend-tested until rupture. The results showed an increase in both the composite mechanical strength and the stiffness with incorporation of these fibers. A fractographic analysis by SEM examinations a moderate adhesion mechanism between the banana fiber and the epoxy matrix. This mechanism is apparently responsible for the improved performance of the composites.

Jan 1, 2015

By Mao Chen, Tim Evans, Zhixing Zhao, Weidong Zhang, Baojun Zhao, Dongqing Wang

High temperature softening behaviours of iron blast furnace feeds (sinter, lump and pellet) have been determined under conditions simulated to the blast furnace. The industrial samples were packed with sandwich structure (coke / ore / coke) in graphite crucibles and 30 CO / 70 Ar gas mixture was blowing directly through the bottom of the crucibles. The displacement and temperature were continuously recorded simultaneously to construct the softening curves. Separated quenching experiments were also carried out at selected temperatures under the same gas atmosphere. The temperatures were selected corresponding to the turning points of the softening curves. The phase assemblages and composition of each phase in quenched samples were analysed by Electron Probe X-ray Microanalysis (EPMA). The proportion of the liquid formed at temperature was obtained from the backscattered electron images. The deformation characteristics of these complex multi-phase materials are shown to be related directly to the phase assemblages of the samples and the microstructures. FactSage was also used to assist the predictions of liquid / solid fractions and their compositions.

Jan 1, 2015

By Antoine Allanore, Guillaume Lambotte, Bradley R. Nakanishi

Current industrial methods used for rare earth element (REE) extraction involve: 1) ore enrichment, 2) separation of rare earth oxides (REOs), 3) chlorination or hydrofluorination, and 4) individual electrowinning of REEs from a molten halide electrolyte. The complexity of REE extraction is inherited from their electronic configuration. Recently, molten oxide electrolysis (MOE) has been used to produce reactive metals directly from their oxides, e.g. titanium. As a single-step alternative to processes 3) and 4), or laboratory has investigated rare earth extraction by MOE. A key challenge is to find a molten electrolyte more stable than REOs. One possibility is to use binaries of REOs directly as a solvent. We have, therefore, developed two experimental approaches for studying molten REOs at temperatures exceeding 2200oC. The present work reports the most recent experimental results obtained with La2O3-Y2O3. Those promising results demonstrate potential for operating with molten REOs and refine the underlying materials challenge for electrodes to enable metal recovery.

Jan 1, 2015

By Shaohua Ju, Feng Jiang, Chuanhua Li, Jinhui Peng, Libo Zhang

A T-junction microchannel is proposed to overcome the existing problems in conventional solvent extraction of indium from zinc hydrometallurgical process. Experiments were performed to separate In3+, Fe3+ and Zn2+ from sulfate solutions using Di-(2-ethylhexyl)phosphoric acid (D2EHPA) as the extractant. The effect of parameters such as pH, microchannel size and contact time on the extraction behavior of In3+, Fe3+ and Zn2+ was investigated. At contact time of 2.52 s and initial solution pH of 0.48, the extraction efficiency of In3+, Fe3+ and Zn2+ was 99.13%, 8.31% and 2.45%, respectively and separation factor of In3+/Fe3+ and In3+/Zn2+ were almost 1229.54 and 4864.98, respectively. Then, the loaded organic phase was stripped in T-junction microchannel. At contact time of 33.6 s, 99.64% of stripping efficiency of In3+ and stripping equilibrium were reached, while concentration of Fe3+ and Zn2+ was lower than 0.01 g/L with good separation of In3+ from Fe3+ and Zn2+.

Jan 1, 2016