The recent developments on the concentration and recovery of gold from leached gold thiosulfate solutions by solvent extraction, reduction-precipitation, and electrochemical deposition are reviewed in this paper. Alkyl phosphorus esters have been found to extract gold only in alkaline thiosulfate solutions, The recovery of gold increases with thiosulfate concentration in the aqueous phase and with alkyl phosphorus esters concentration in the organic phase with aliphatic hydrocarbon diluents. The addition of ammonia improves the extraction. The extraction of gold with amines in either aliphatic or aromatic diluent decreased in the following order: primary>secondary>tertiary amines. Increase in the extractant concentration at high pH increased the extraction of gold. At pH < 9, the primary amine, RR&apos;CHNH2 with 1&apos;9-23 carbon atoms is the main extractant with TBP as the synergistic reagent and at pH >9, the primary amine shows a synergistic effect on the extraction of gold&apos; with TBP. TheAu(I) ions in thiosulfate solution are reduced by sodium borohydride (SBH) to metallic gold, with particles in the sub micron range, At an SBH/ Au ratio of 6.25, pH = 6, and at room temperature, the I e ppm Au(I) in a solution of ] 0 gil thiosulfate was completely reduced to metallic gold in about 60 minutes.

Jan 1, 1999

By Wenbin Liu

A novel route for rapid synthesis of ultrafine WC-Co cemented carbides with homogeneous binder phase distribution is reported. The composite powder is produced by in situ reduction-carbonization reactions by using WO2.9, Co3O4 and carbon black as raw powders. The reaction equilibrium and phase stability are studied by thermodynamic calculations. The WC-Co composite powder is condensed by spark plasma sintering (SPS) to obtain the cemented carbides bulk. The sintering temperature is lower than that in the conventional sintering methods by 1500C, while the sintering time is remarkably reduced by 3-5 times. The high performances of the hardness and the fracture toughness are obtained. The experimental results confirm that the present processing scheme of in situ reduction-carbonization reactions and subsequent SPS sintering is an efficient way to prepare WC-Co cemented carbides, and is apparently superior to the conventional long-period techniques of preparing composite powder and cemented carbides bulk.

Jan 1, 2008

By Renato G. Bautista

The chemistry of the separation of metals from each other and from the other undesirable components involve multiple simultaneous chemical reactions. In the case of leaching, the heterogeneous chemical reactions between the solid and the liquid phase may be limited to a few reactions. In the homogeneous liquid phase, the number of simultaneous chemical reactions could be double or triple that of the number of heterogeneous reactions:. The rate of dissolution becomes very dependent on the changing concentrations of the significant chemical species taking part in the multiple reactions in both the heterogenous and homogeneous phase. The rate expression developed for the process must take into account the mechanism of chemical reactions in order to best represent the actual process. This paper also examine the role of mass transfer with chemical reaction in the develpoment of the rate equations for dissolution, liquid-liquid extraction, membrane separation, precipitation, and electrodeposition.

Jan 1, 1996

By Y. F. Liang

Fe-6.5wt.%Si alloy has excellent soft magnetic properties compared with conventional silicon steel. It is very brittle at room temperature due to appearance of ordered phases, like B2 and DO3. In this paper, we investigate the effect of ordering on cold workability of this alloy. Methods of rapid quenching and hot rolling were utilized. It is found that rapid quenching and proper heat treatment of the hot rolled sheet could decrease the degree of order due to the very high solidification rate and high cooling rate. The rapid quenched sheet and hot rolled sheet after proper heat treatment could be cold rolled without crack. Microstructure, phase ordering, micro hardness, and cold rolling properties were investigated by Optical Microscope, X-ray Diffraction, Micro Hardness Indenter and Four-high Mill.

Jan 1, 2009

By Susumu Okabe

Mitsubishi Continuous Copper Converter employs the top blowing lance system for the continuous supply of reaction gases into the molten bath. In order to avoid the excessive refractory wear caused by the melt splash without loss of the reaction efficiency, the furnace design and the blowing condition should be optimized. Empirical equations which correlate the splashing rate on the&apos; side wall with the dimensions of the furnace, lance position, lance size, gas velocity and bath properties were obtained by by the physical model study, and compiled into a computer program. The computer program is effectively utilized for the analysis of the actual operation and for the optimum design of new furnaces.

Jan 1, 1998

By R. W. Bartlett

The extensive central Idaho black sand placer deposits are a potential source of rare earth elements, particularly the heavy rare earth elements that are not prevalent in commercial bastnasite deposits. These placers derive from the Idaho batholith. The geology, occurrence, and extent of these deposits are reviewed and the diverse mineral assemblages and complex mineral chemical compositions of these sands are described. Niobium, yttrium and thorium are also present in significant concentrations. The results of prior mining practice, including concentration and separation of the heavy minerals are reviewed. Technical approaches to extraction of rare earths from Idaho black sand concentrates are discussed.

Jan 1, 1992

By Alysson Tadeu Pereira Almeida

Steels with low concentrations of nitrogen, hydrogen and carbon have been in large demand lately. The RH process is a secondary refining process that can simultaneously attain significant levels of removal of these interstitial elements from liquid steel. In the RH process, the melt circulation rate plays a very important role in determining the productivity of the equipment, since it affects the decarburization rate. In the present work, a physical model of a RH degasser in a 1:5 scale of an industrial reactor has been built and used in the study of the circulation rate and of the kinetics of decarburization. The effects of the gas flow rate and of the configurations of the nozzles used in the injection of the gas have been analyzed. The decarburization reaction of liquid steel was simulated using a reaction involving CO2 and caustic solutions. The concentration of CO2 in the solution was evaluated using pH measurements. The experimental results indicated that the kinetics of decarburization can be described by a first order equation. Based on the results, it was possible to determine the contributions of the decarburization in the upleg snorkel and in the vacuum vessel.

Jan 1, 2006

By Niloy K. Nath

Two layer sintering by charging green sinter mix with normal coke rate in the upper layer and reduced coke rate in the lower layer, can substantially reduce the coke rate and also improve the sinter quality by producing more uniform thermal profile through out the bed height. The two-layer sintering process have been analyzed by numerical simulation of the process by a detailed CFD based model, considering all the important phenomena like gas-solid reaction, melting and solidification, flow through porous bed, heat and mass transfer etc. Optimization techniques like genetic algorithm, differential evolution is then applied to evaluate the optimum coke rate in the two layers of the bed to produce the ideal thermal profile and melting fraction in the sinter bed for optimum sinter quality. Through this optimization method both high quality sinter with minimum return fines can be achieved along with reduced coke rate. Application of a genetic algorithm for this type of process optimization has several advantages over the traditional optimization techniques since it can identify global optimum condition and perform multi-objective optimization much easily for complex industrial process like iron ore sintering. Keywords: Two-layer Sintering, Iron Ore Sinter Quality, Ergun&apos;s Equation, Gas-solid reaction, Melting Fraction, Multi Objective Optimization, Pareto Set, Genetic Algorithm

Jan 1, 2003

By Rudolf Keller

"EMEC Consultants is developing a process to extract oxygen, aluminum and silicon from lunar anorthositic soil. The process will provide oxygen in space for propulsion, aluminum as a structural material, and possibly silicon for the construction of solar cells.The evolution of the process concept in the course of our present NASA-sponsored SBIR effort is discussed. A molten salt electrolysis producing aluminum and oxygen is the central step; inert anode technology is to be employed. Silicon will be produced by reducing the anorthite, CaAI2Si20S' with aluminum. In a steady-state operation, all components of the ore added have to be removed from the process, and the removal of calcium is a major topic of our experimental studies.Utilization of Lunar ResourcesUtilization of lunar resources may play an essential role in the exploration of the solar system and the conquest of space. High costs are involved in overcoming Earth's gravity to supply missions in space. Even at a low projected cost of $ 300 for transporting a pound of payload into Earth orbit -- today's costs are many times higher -- it appears attractive to use resources in space to produce needed materials. Processing of lunar resources on the lunar surface is an obvious possibility.Oxygen is a product of major interest. It is required for support of human life in space. Even greater quantities may be needed for propulsion, to conduct further missions into space. To satisfy this demand for oxygen through lunar processing requires a quite different solution than to supply oxygen on Earth, where oxygen gas is abundant and easy to extract from air or water. On the lunar surface, solid oxide materials have to be used. Hydrogen reduction of ilmenite and subsequent electrolysis of the resulting water is being studied [1]. Other suggestions include fluorination of lunar soil [2], reduction with lithium and electrolytic decomposition of the resulting lithium oxide [3], and aqueous HF leaching [4]."

Jan 1, 1988

By Denise Cristina Oliveira Nascimento

Environmental considerations in addition to technical, economical and societal benefits are increasingly promoting the substitution of natural fibers for glass fiber in polymer matrix composites. However, natural fibers are heterogeneous in their dimensions, specially the cross section, which plays an important role in their mechanical strength. It has been found that the equivalent diameter of fibers such as sisal, ramie, pineapple and curaua correlates to different levels of tensile resistance. Piassava is a promising stiff natural fiber for composite reinforcement. In this work, a statistical analysis of tensile strength of piassava fibers using the Weibull methodology was performed. An attempt to correlate the fiber strength, obtained in tensile tests, with the diameter, precisely measured by means of a profile projector, was carried out. The results revealed an inverse dependence between the piassava fiber diameter and corresponding tensile strength. Fracture tip observation by SEM suggested a possible mechanism that could justify this inverse correlation.

Jan 1, 2010

By Ying-Chu Hoh

The extraction of cerium(IV) by valence change with two-phase electrolysis was studied experimentally. The results show that the electro-oxidation extraction depends mainly on the distribution of the solute between the two phases, the reaction on the electrode surface and the diffusion of the reactant and product between the electrode and aqueous interphases. The effects of various parameters on cerium extraction were also studied. The selected parameters were background current, catholyte acidity, agitation speed, operation current and voltage and surfactant addition. The electro-oxidation extraction mechanism can be divided into eight steps. In addition, Wee the rate of extraction is quite fast, the percentage extraction Ce+4 can be taken as an index to show the conversion rate of Ce+3 J to Ce+4.

Jan 1, 1989

By Marco Olper

After two years of extensive research a new and innovative modification to the CX-EW process has been exploited. This process, called CX-EWS, avoids completely all the critical aspects of the previous process which affected the cost of the energy, of the chemicals and of The maintenance of the insoluble anodes. All these benefits reflect a saving of about 30% of The operating costs compared to the present traditional production and allow for a total operating costs of less than 6.5 cts/lb. lead (net of raw material cost). With this new technology it is allowed for the first time the treatment in the same plant facilities of both primary lead sulphide concentrate and spent batteries. The paper describes the technical and economical aspect of the new process with a feasibility study for 150,000 t/y spent battery facility throughput.

Jan 1, 1995

By Guo Xueyi

The morphological characteristics of the nickel particles electrodeposited from chloride dominant aqueous solution was investigated. The effects of the electrolyte constituents, the parameters for the electro-deposition on the morphology of the nickel particles were addressed. It is evidenced that not only the particle size but also the morphology of the deposited nickel particles strongly depend on the electrolyte constituents and technical operation conditions. The electro-crystallization mechanism of the metallic nickel particles deposited at high current density was elucidated. The ultra-fine nickel particles with flake, nodular or dendrite shape may be produced by controlling the duration for electro-deposition.

Jan 1, 2003

By Jasper Kwong

The recycling of MgO-C refractories as a slag conditioner in EAF (electrical arc furnace) foaming slags have been evaluated by the Albany Research Center. The amount of MgO in the slags is critical for the foaming quality. Good foaming slags provide the benefits of high energy efficiency and low refractory consumption and require saturation with MgO. A computer model predicting the chemistry of MgO saturated foaming slags was designed to predict suitable amounts of MgO additives from MgO-C spent refractories. This model can also help to reduce the amount of slags and to improve the economics of producing steel. The implementation of this recycling program is underway at steel plants and the experience of recycling spent refractories will be discussed.

Jan 1, 2002

By T. B. Braun

Cathode contamination is the principal factor affecting the quality of electrorefined copper. It is commonly accepted that annealability is unfavorably affected by the following elements, in decreasing order of adverse effect: tellurium, selenium, bismuth, antimony, and arsenic. Silver in cathodes has importance as it represents a nonrecoverable loss of silver to the refinery. Mechanisms for the contamination of cathodes by these elements are examined and the effect of operating variables on contamination, including anode composition, electrolyte composition, electrolyte temperature, addition agent practice, and electrolyte discard rate, are discussed.

Jan 1, 1976

By Dhanesh Chandra

In this symposium, research in the area of energy conversion is presented. This symposium has special significance, as we honor three prominent scientists from hydrogen storage research and development field. In this symposium, the majority of papers presented by international scientists and engineers are in the area of hydrogen storage. Other energy conversion papers include magnetic materials, superconductors, and thermal energy storage materials. Recent developments in light-weight high gravimetric hydrogen density hydrides have led to potential use of hydrides for onboard automobile and other applications. This, of course, is significant from environmental concerns of CO2 and other emissions from the current use of carbon based fuels in automobiles. Thus, it is becoming increasingly important to switch to cleaner alternative fuels such as hydrogen [1]. The Challenge of Vehicular Hydrogen Storage as potential hydrogen energy carriers for vehicular applications, with a driving range of approximately 300 miles, require ~5-13 kg of hydrogen stored on-board. In the United States, Centers of Excellence have been established in metal hydrides, chemical hydrides, and carbon-based materials, and abundant scientific and industrial research is being carried on metal hydrides; only some of the current research from the Centers will be reported here. The European commission, Japan Institutions, and others also have numerous hydrogen storage programs in progress. Several international collaborations have also begun between IEA and IPHE scientists to accelerate the progress of development of practical hydrides. A summary of the abstracts is included in this overview.

Jan 1, 2006

By Jean Goldschmidt

Recycling of fine oxidized particles of non-ferrous metals usually cannot be carried out by pyrometallurgical methods. &apos;Hydrometallurgy provides an alternative technology to reintroduce? the resulting products as secondary raw materials into the industrial cycle, thereby saving resources and energy while keeping the environment a little cleaner. The paper summarizes the methods employed by Hydrometal to achieve these objectives and? stigmatizes the latest counterproductive international regulations which create ever more obstacles to environmentally sound recycling.

Jan 1, 1995

By R. David Prengaman

During the past several years a new insoluble lead anode has been developed for copper electrowinning. The new anode consists of a rolled lead-calcium-tin alloy sheet attached to a slotted copper bus bar by a soldering process which produces a complete metallurgical bond between bar and sheet. The metallurgical bond greatly reduces the resistance between the bus bar and the lead sheet and the high conductivity does not deteriorate during the life of the anode. The rolled anode thins uniformly and does not suffer preferential grain boundary or internal corrosion commonly seen in cast anodes. The lead-calcium alloy containing a high tin content corrodes slowly because the rolling process produces a uniform, fine grained structure. The wrought product is very strong and ductile; and contains no internal defects, segregation, cracks, or pores which can reduce the life of the anode. Because the anodes corrode uniformly, a high percentage of the anode thickness can be utilized thus extending the life of the wrought anodes. The anode alloy composition which is stable only in wrought form, produces exceptional resistance to passivation during current interruptions. First introduced into liberator cells, the new electrowinning anodes have been specified as the anodes of choice for every new SX-EW tankhouse constructed in the last two years. This paper describes the new anode, its method of construction, service history, and how it differs from present copper electrowinning anodes.

Jan 1, 1987

By V. L. Stolyarova

As part of an effort to develop the fluoride electrolysis route for the production of rare earth metals and alloys, a study of the thermodynamic properties of DyF3 has been carried out by Knudsen cell mass spectrometry. A quadrupole mass spectrometer QMS 420 was used in conjunction with the Knudsen cell arrangement. The experiments were carried out in the temperature range 1280-1440 K. Vaporization was carried out from platinum, molybdenum and tantalum cells. The Dy*, DyF+, DyF2+ fragment ions and the DyF3 parent ion were identified in the mass spectrum of the DyF3 vapour. The DyF, vapour pressure was obtained by the complete isothermal vaporizadon method as well as the ion current comparison method, and the enthalpy of sublimation of DyF3 was evaluated. From the DyF3 vapour pressure data obtained at different temperatures, the enthalpies of formation of DyF3 in the gaseous as well as condensed phases have been evaluated. The experimental data are compared with the thermodynamic information available in literature.

Jan 1, 1995

By Marko Suput

Titanium is a high-strength, low-density metal nearly immune to corrosion, but limited in use by its high price. The high price is due to the cost of smelting and processing the ore. The research on titanium production using the Solid Oxide Membrane (SOM) process aims to consolidate most of the processing steps required for conventional titanium production into a single step making it an energy-efficient and cost-effective method for producing CP billet and ingot and possibly also powders used to make titanium alloys. In the SOM process experiment, a steel crucible contains MgF2-CaF2-TiO2 flux; an inert metal/carbon rod serves as the cathode; an oxygen-ion-conducting yttrium-stabilized-zirconia (YSZ) membrane in the form of a one-end-closed tube contains either a liquid metal that acts as the anode or liquid MgF2-CaF2 ionic flux that connects the YSZ membrane to an anode. During electrolysis, when the voltage between anode and cathode is higher than the reduction potential of titanium oxide, titanium ions are reduced at the cathode and the oxygen ions pass through the YSZ membrane and are oxidized at the anode. The oxygen ions are oxidized at the anode by a reducing agent, hydrogen gas or carbon, forming steam or CO(g), respectively. To date, a suitable MgF2-CaF2-TiO2 flux has been selected and the operating temperature for the SOM process has been determined. Several electrolysis experiments have been performed. As expected, lower valence deposits of titanium oxides have been witnessed at the cathode prior to depositing pure titanium. Continuing work will aim to extend the electrolysis time in order to pass enough charge to produce a significant amount (100 g) of titanium at the cathode.

Jan 1, 2006