By M. Furuta, M. Hasimoto, Y. Komoda, K. Haiki

"Tamano Smelter & Refinery started its operation in 1972 with high current density electrolysis (350Nm2 of maximum) applying PRC technology. After the start up, four times of expansion have been done, the cathode production capacity has increased from- 84,000 t/y to 191,000 t/y. However, recent refining technology with permanent stainless steel cathode enabled to increase current density up to 300 Nm2 or more without PRC method. In order to increase current density more than 350 A/m2 , experimental work using commercial size cell has been carried out at several conditions, such as current density, PRC conditions, electrolyte composition and electrode condition. As a result, it was found that high quality (LME A grade) cathode can be produced at such a high current density as 405 A/m2•IntroductionWhen considering the production increase of electrolytic copper, what becomes important is the improvement of productivity per unit of production facility. Conventionally, production had been expanded by increasing the number of cells but a huge investment required for this had a influence to the business profitability. Because of this, increase of current density, which is one of the methods to improve unit productivity, 'was expected and this method at the same time has another advantage of shortening the retention time of copper and other precious metals in the cells. At present, the average current density at Tamano during full capacity production is around 350 A/m2 and this used to be the limit throughout the world (1)."

Jan 1, 2000

By Michael L. Sorokin

The various methods of converter slag cleaning operation are analysed from the thermodynamk point of view: cleaning using coal, cleaning using combustion products of natural gas and cleaning in presence of matte. All calculations were done, applying the developing computer procedure based on the free energy minimisation algorithm. Three-suffix Margules equations were used to calculate thermodynamic properties of melts; The calculations resulted in recommendations for the practical appliance.

Jan 1, 1995

By María Cristina Ruiz

In the processing of copper concentrates by the conventional smelting-converting technology, complying with the increasingly severity of environmental legislation in some countries has become difficult, mainly due to severe fugitive emissions of gases produced during the batch PS (Peirce-Smith) converting step. In this work, the results of an investigation on the pressure leaching with sulfuric acid and oxygen of white metal (produced in a Teniente Converter reactor) are discussed. The study was carried out at laboratory scale and the main variables studied were temperature, concentration of sulfuric acid and partial pressure of oxygen. The experimental results indicated that most of the sulfur in the white metal was oxidized to sulfate in the whole range of temperature studied (105ºC to 150 ºC). The concentration of sulfuric acid over 0.05 M, and oxygen partial pressure over 6 atm had little effect on the dissolution of copper from the white metal. On the other hand, temperature had the most significant effect on copper dissolution; below 130 ºC copper dissolution was incomplete after 5 hours of leaching while at 150 ºC the dissolution was complete in 90 minutes and 10 atm of partial pressure of oxygen

Jan 1, 2006

By F. Garcia-Carcedo

This research aimed to develop a clean technology for the production of ZnO from residues generated by the steel making industry. Scientific and technologic parameters were both investigated in order to define an industrial methodology allowing the integral recycling of EAF dusts. A reengineering of the Waelz process was perform,~d, aiming to produce a clean fraction of ZnO, fluorine free, as well as a slag enriched in metallic iron, which can be recycled in electric arc furnaces. The technical conditions used to produce the ultra pure fraction of ZnO are described. The magnetic separation of the EAF dust allowing the production of a phase high in iron and recyclable to the electric arc furnace is also discussed. Thermodynamic of the volatilization of all the elements contained in the EAF dust was performed in order to better control the thermal process in the rotary kiln. Tests were run using different reducing agents, weakly or highly reactive, aiming to determine their specific efficiency.

Jan 1, 2000

By Andrew Campbell, Michael Reed

"WorleyParsons has used Discrete Event Simulation methods in conjunction with more traditional process models to assess the performance of copper smelting operations. This work was performed to determine the plant capacities and suitability of proposed debottlenecking options including accounting for the planned and unplanned (breakdowns) shutdowns in the various parts of the plant and supply chain. This paper outlines the methods used along with demonstrating the benefits of selecting a feasible option and minimizing capital and operating costs.IntroductionTraditionally for de bottlenecking studies of smelters and other process plants, a mass balance is performed based on continuous operating rates and expected operating hours. Smelters have several points of failure that will restrict, if not take the entire plant offline. By using a more detailed model, validated against plant experience, bottlenecks can be demonstrated and strategies to remove them to increase plant availability and economic.The modeling simulates the plant performance in real time, and by performing enough simulation the expected long run performance of the plant can be estimated. The models have been built using ExtendSim which is a powerful Discrete Event Simulation software package that is ideally suited to the batch and semi-batch processes and events that occur within smelter operating environments. The value of performing this work is that the operational performance of the plant can be assessed ensuring production targets are met, without using excessive capital outlay."

Jan 1, 2013

By Patrick R. Taylor

A non-transferred arc thermal plasma assisted cyclone reactor has been designed, built and operated to evaluate its use in vitrification of wastes. Simulated waste (liquid, slurry or fine particulate) is injected near the plasma flame, where nearly instantaneous dehydration and calcination reactions happen. A non-transferred arc plasma torch was attached tangentially to the cyclone and is utilized as both an enthalpy source and to provide the gas velocities required to generate the cyclonic gas flow patterns. The closed top cyclone flow sends the solid particulates to the wall, where they are captured by a thin film of molten glass that is injected as a powder at a position lower in the reactor. The molten glass is then collected in a crucible. The feasibility of simulant injection directly into the flame zone and its effect on electrode lifetimes has been studied. Several candidate refractory systems have been evaluated for their suitability for extended use under the demanding conditions present in the cyclone reactor.

Jan 1, 2002

By Niels Verbaan

NioCorp is developing the niobium/scandium/titanium Elk Creek carbonatite deposit. The probable reserve announced by the company in 2017 indicated significant niobium (0.79% Nb2O5), titanium (2.81% TiO2), and scandium (71 g/t), and is composed predominantly of calcite, dolomite, and ankerite. Niobium is mostly (80%) contained in pyrochlore with the balance in various Fe-Nb-Ti oxides, which also host most of the titanium. Scandium is primarily deported in dolomite, with lesser quantities in pyrochlore and biotite. The process flowsheet recovers separate niobium, titanium, and scandium products. Scandium is extracted from whole ore hydrochloric acid leach solutions using solvent extraction and is further refined through a re-leach and precipitation process. Scandium leach residues are treated in a sulphuric acid sulphation process to recover separate niobium and titanium precipitates as well as to solubilize the remaining scandium. Both hydrochloric acid and sulphuric acid reagents are recycled within the flowsheet. This paper will discuss key bench and pilot test results of the niobium extraction and recovery circuits and will present a conceptual flowsheet developed by the project team for NioCorp at SGS Minerals.

By S. G. Kumar, R. G. Reddy

"Niobium aluminides offer the advantage of higher high temperature capability compared to other intermetallic aluminides due to the refractory nature of niobium. However, the reaction sequence in Nb-Al system is sluggish and currently there is a great interest in the processing aspects of these materials. In the present study, a systematic investigation was undertaken to compare the effect of different powder metallurgy processing routes on the phase relations and microstructure of 66Nb-22AH2Ti (in atom percent) alloy. The three different process routes adopted were: (i) cold pressing followed by reaction sintering; (ii) cold pressing and hot pressing followed by sintering; and (iii) arc melting, hydride-dehydride process to make the alloy powder followed by cold pressing and then sintering. The samples are analyzed by XRD, Optical Microscopy, SEM-EDS and EPMA. The analysis showed that alloy pellets made from pre-alloyed powders i.e., arc melting followed by hydride-dehydride process, gave good densification and more Nb3Al formation.1. IntroductionTo improve the performance standards of turbine engines, materials scientists are challenged to develop materials that have· high thrust-to-weight ratio with high specific strength, high specific modulus and good environmental properties at elevated temperatures. The conventional high temperature materials like nickel based superalloys are high in density and hence many of the high temperature materials scientists have focussed their attention on intermetallic aluminides like Fe-AI, Nb-AI, Ni-AI and Ti-AI in recent years. The phase relations and properties of alloys based on Fe-AI, Ni-AI and Ti-AI are fairly well known whereas little is known about the alloys based on niobium aluminides."

Jan 1, 1996

By David N. Hanlon

The effect of high-temperature plastic deformation of the austenitic phase (y) on the subsequent phase transformation to ferrite (a) has been experimentally investigated, and modelled using a physically-based model. The effect is of importance for steel sheet, in view of me significance of the phase transformation with respect to the eventual properties of the material. In this paper the kinetics of the y ? a phase transformation has been studied after different degrees of prior deformation. The degree of deformation is varied by applying different deformation temperatures and strain rates, and by allowing a varying extent of recovery and recrystallisation. Consequently, both dynamic and static recovery and recrystallisation have been involved. The dilatometric observations on the phase transformation have been modelled using an interface-mobility model, in which the effect of the dislocation structure is introduced as an additional driving-force term. The effect of the stored energy on the nucleation process, which appears to be affected more strongly than the growth of ferrite, is examined in terms of the classical nucleation theory.

Jan 1, 2001

By V. Ramachandran

Over the past 20 years, water treatment plants have been built at various Asarco facilities to effectively handle the process waste streams that need to be bled from the system. The current paper review the several operations with reference to (a) waste streams processed, (b) process chemistry, (c) discharge options and recovery of treated water, and (d) sludge disposal.

Jan 1, 1994

By John Pilling

The concept of microstructure, its evolution through materials processing and its effect on the properties of the material is, perhaps, the foundation upon which the science of materials is built. PHAUST, a computer aided learning program, attempts to provide instruction in establishing the relationships between phase diagrams, thermal processing and microstructure. Using phase diagrams derived from a database or created by the user, the evolution of microstructure during processing is quantified using the lever rule and/or the Scheil equation and tracked through a doubly linked list (a form of binary tree). Microstructures, in the form of full colour cartoons are then drawn using the quantitative and logical information contained within the linked list using bitmapped templates and logigal operators such as NOT. AND, OR and XOR, giving the student a view of the structure as it would be seen under the optical microscope. The software provides complete diagnostics of student answers, locates errors and misconceptions as well as providing tutoring towards the correct solution method and answer.

Jan 1, 1991

By Gerardo Fuentes

The stoichiometry and kinetics of the hydrothermal reaction of enargite in copper sulphate solutions was investigated in the range 140–300 °C, and particle size under 15 and 50 μm. The stoichiometric experiment was performed at 300 °C, using one gram of sample (96% enargite, 4% tennantite) and 100 mL of copper sulphate solution (10 gpl) at 1.2 pH. Enargite reacted completely after 80 min. A solid product was obtained and characterized by XRD. The main product was chalcocite (M) and some traces of djurleite and chalcocite (Q). Tennantite did not react under these conditions. The kinetic experiments were conducted at 140 °C, 190 °C, 250 °C and 300 °C. From fitted data and Arrhenius equation the calculated activation energy (Ea) was 51 kJ/mol. According to the hydrothermal transformations studied, the reactivity of different phases found in the copper concentrates was bornite > chalcopyrite > covellite > sphalerite > pyrite > enargite > tennantite.

By Julian Johnson

The effect of changing redox potential (Eh) on the high temperature sulfuric acid leaching of Western Australian dry-land nickel laterite ores has been investigated. In particular, the effect of added reductant (sulfur, sodium sulfite) or oxidant (potassium chromate) on Eh, leaching kinetics, metal extractions, acid utilisation and leach residues has been determined. Three separate ores - nonhonitic ores from Murrin Mumn and Bulong, and limonitic ore from Cawse - were used in the study. Sulfur addition varied from 0 to 7.8 kg/t ore. The total acid loading was kept constant at 430 kg/t (Murrin Murrin ore) and 330 kglt (Cawse ore), whilst acid loading for Bulong ore was varied according to the presence of either reductant or oxidant. The extraction of both nickel and cobalt from limonite ore remained unaffected when small amounts of sulfkr were added, but addition of even small amounts of reductant to nontronitic ore decreased both nickel and cobalt extraction. Increased manganese and iron dissolution were observed as the levels of reductant increased, accompanied by a decrease in chromium dissolution. As the iron dissolution increased, free acidity decreased, with a subsequent decrease in nickel extraction. In contrast, addition of oxidant lead to reduced iron and manganese dissolution and slower extraction of nickel and cobalt. Keywords: Limonite, Nonhonite, Eh, Nickel Extraction

Jan 1, 2004

By S. C. Dhara

The recovery of Platinum Group Elements from various industrial scraps and spent materials in the form of high and low grade, such as, impure metals, matte, catalysts and other ceramic substrates, etc., has .been described by using high pressure reaction method. Nickel, Stainless Steel, Titanium and glass lined reaction vessels? are used in the reaction process. Primarily, the method involves either direct leaching of the substrates from the metal value or dissolving the precious metal from the substrate. Both acids and alkalies are used along with other reagents in the reaction process. The temperature and pressure of the leaching process are the main criteria for the reaction kinetics.

Jan 1, 1989

By W. -S. Hwang, R. A. Stoehr, P. Ingerslev

"The flow of molten metal entering complex two-dimensional foundry molds has been modeled using the Simplified Marker and Cell (SMAC) and Solution Algorithm (SOLA) techniques. The molds were for a series of four and three-spoke wheel designs. The computer calculations were compared to physical experiments in which molten cast iron was poured into C02-bonded sand molds. The metal was photographed with a high speed motion picture camera focused through a Pyrex glass window on one face of the mold. To get good agreement between the calculations and the experiments, it was necessary to accurately represent the velocity through the ingate. This was calculated by application of the Bernoulli equation to flow through the feed system. Some difficulties were experienced with mathematical instability, expecially in the three-spoke design with a narrow ingate. This was overcome by using 100% upwind differencing, and over relaxation parameter near 1.0 (i.e. no over relaxation), and variable mesh spacing.IntroductionModeling the flow of molten metal entering molds has the potential for making significant contributions to the design of feed systems. It will supply information to the computer-aided-design systems of the future that will enable the designer to optimize the placement of gates, dimensioning of passages, and designation of casting speeds. Such design criteria have generally been based on application of energy balance (Bernoulli equation) principles to flow in the sprues, runners, and gates. Indeed, this is the easiest way to determine the proper dimensions to give a suitable filling time for a casting of a given size. A number of computer programs, including one by some of the present authors, have integrated such calculations into CAD systems. l Modeling the flow of metal inside the mold cavity requires other techniques that will handle free-surface transient flow. Stoehr and Hwang reported on the application of the Marker-and-Cell (MAC) technique to mold filling problems at the previous conference in this series at Hennicker, N.H. in 1983. 2 Although considerable progress has been made since that time in improving the accuracy, stability, and convenience of these techniques, the shapes to which they were applied remained limited. Also, physical verification of the results of the calculations was limited to water models.The work to be reported in this paper was undertaken with two objectives: (1) to apply these techniques to more complex and realistic shapes, and (2) to verify the results by comparison with flow patterns observed in molten metal poured into actual sand molds."

Jan 1, 1986

By Doug Halbe

?Many are called, but few are chosen.? The biblical adage applies not only to life, but also to hydrometallurgical processes. There have been, in the past, many outstanding successes with new processes ? and also some dismal failures. What are the odds of success for a new process? When there have been problems, why? What can you do to make sure these problems don?t occur with your process? What effect will a slow startup have on project economics? How do financial institutions ? the people who loan your company money for the project ? feel about new processes and why? Is it possible to predict or estimate the time required to reach design parameters?and if so, how do you sell this estimate to management ? and financial institutions? Probably most important ? when do you start thinking about the answers to these questions?

Jan 1, 2003

By Xiao-hui Fan, Li-shun Yuan, Xu-ling Chen, Wei Lv, Min Gan, Yi Wang

"As the amount of ferrous scrap increases every year, it becomes more and more urgent to deal with this iron-bearing resource properly. This paper puts forward a method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing), and these cold-bonded pellets can be used as coolant in a converter. The influence on the pellets qualities by using different kinds of chloride as rust agents is studied, and results show that the strength of cold-bonded pellets increases significantly by using a combination of the three kinds of chloride -NaCl,MgClz,FeCh, their best dosages are 1.2%, 0.2%, 0.1% respectively. Other iron-bearing materials also have an effect upon the pellets strength, by adding 5% iron powder and maintaining for 48h, the compressive strength of the clumps surpass 2500N/A, dropping strength surpass 4 times/ A, and 10% iron slag or 20% steel slag can replace 5% iron powder while obtaining the comparative quality. The influence of different ratios of three ferrous scrap (converter mud, iron scale and dust) is further studied, and results show that when the ratio is 30% : 30% : 40%, the pellet strength reaches the maximum. After maintaining for 24~48h, the clumps can meet the mechanical as well as the physical-chemical requirements as BOF steelmaking refrigerant.IntroductionGreat amounts of converter mud, dust and iron scale are produced in steel production process. These materials are of great values, and their accumulation not only leads to environmental pollution, but also wastes the precious resources, which restricts the sustainable development of the steel industry [1,2] The main approach at present to dealing with the ferrous scrap is to add them into sintering. But in this way, the utilization factor of sintering and the quality of sinter decline while the energy consumption increases [3].Therefore, more advanced and efficient technology is needed to make the best of these iron resources. Cold consolidation of ferrous scrap is a simple process that has many advantages such as less investment, quicker effect, lower energy and lower cost [4-5] But the conventional maintaining period is too long, usually up to four-six weeks, and the pellet strength is low. Therefore, the key points of the cold-bonded pelletizing are to develop a new adhesive [4,5] to shorten the natural maintenance cycle and to improve the strength of the pellets. A method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing) is brought forward, and these cold-bonded pellets can be used as coolant in converter. After maintaining for 48h, these cold-bonded pellets can satisfy the mechanical requirements to replace the converter coolant [6]."

Jan 1, 2013

By B. Yalamanchili

Gerdau Ameristeel Beaumont presents its systematic approach for upgrade decisions that has developed over 30 years of ongoing capital projects for quality and cost improvements. This system serves to identify product needs, select process improvement strategies, justify them, and assist multi-department communications and decision-making. This is illustrated with Beaumont mills? last Stelmor upgrade and leads to a discussion of the need to consider Life Cycles of both products and technologies as we move to answer the challenges of the future.

Jan 1, 2006

By Michael A. Markowitz, Alok Singh

"Molecular self-assembly of phospholipids and other amphipathic molecules offers a versatile approach to form self-organized microstructures in various morphologies. Stabilization of microstructures in specific morphologies by polymerization renders them useful for practical applications in areas ranging from controlled release technology to template mediated synthesis of metals. Our efforts are focussed on the development of polymerizable biomembranes derived from phospholipids, their properties and utility e.g., as stable templates for studying chemistry at the lipid interface. Polymerized vesicles formed from mixtures of 1,2-bis(tricosa-1 O,12-diynoyl)-sn-glycero-3-phosphocholine, 1, with corresponding lipids having phosphohydroxyethanol,2, or -hydroxypropanol,3, headgroups have been used in electroless metal plating of vesicle surface with gold utilizing selective binding of Pd(NH3)4 2 + to 2 or 3. The surface bound palladium ion served as catalyst for metalization. Metalization of polymerized vesicles constructed from charge neutral diacetylenic phosphocholine,1, did not occur using this process. The headgroup structure of the negatively charged phospholipids and the degree of vesicle polymerization had an effect on the stability of the vesicles after metalization. Vesicles formed from a mixture of 1 with polymerizable diacetylenic phosphatidic acid, nonpolymerizable 1,2- dipalmitoyl phosphohydroxyethanol or 1,2-diacyl phosphohydroxyethanol (from soy lecithin) were not stable to metalization process. The metal coating of the vesicles was examined by electron diffraction and revealed that the gold metal on vesicles was polycrystalline and face centered cubic. The results demonstrate the utility of polymerized synthetic membranes as template for easy and efficient synthesis of nanoparticles. IntroductionPhospholipids, synthetic or natural, provide a simple and straight forward route to construct membranes in a variety of morphologies due to their inherent property of selforganization in the presence of water[1]. Vesicles are closed spherical structures comprised of concentric walls made from lipid bilayers. Vesicles are morphologically simple structures with enormous technological potential. Polymerizable phospholipids prepared by incorporating a polymerizable group in the molecules demonstrate physical properties comparable to their non-polymerizable counterparts and have the added virtue of providing enhanced physical and chemical stability to the membranes[2,3]. The size, shape and properties of the organized assemblies are dependent on the lipid structure and the nature of the aqueous environment[4,5]. The headgroup geometry, surface charge density, and spatial arrangement of the phospholipids are known to affect the surface behavior of the lipid membranes, which is evident through their interaction with other molecular (hormones, antigens, antibodies etc) or lomc species. Since phospholipid headgroup structure and charge can be modified either synthetically or by chemical perturbation of the aqueous medium (e.g., pH or ionic strength), phospholipid membrane surfaces offer a potential for developing novel strategies in those areas which involve the use of molecular reactive sites. One such strategy which could be envisioned explores the use of molecularly engineered phospholipid assemblies to design and prepare template structures to regulate formation of ordered materials [6]."

Jan 1, 1994

By Margarete Kalin

Mine abandonment is associated with the securing of access to underground workings, shafts, raises and adits. Waste rock piles and tailings are generally contoured and revegetated. When the waste materials contain pyritic material seepages can often emerge long after the physical reclamation work has been carried out. Their extent and origin has to be delineated to facilitate remedial measures. The depth to which the seepages extended can be determined with an electromagnetic (EM) survey. This paper reports on the experience gained using a winter and a summer EM survey correlated with measurements of specific conductivity at the sediment water interface. Lake sediments and ponds which represent a homogenous background material are good media, where specific conductivity and electromagnetic conductivity can be correlated. The origin of the seepage within the recontoured mine site requires detailed site knowledge, as many anomalies in heterogenous materials such as represented by a mine site are evident.

Jan 1, 1994