Search Documents

By M. Abdellatif

"SynopsisCalcined basic nickel carbonate (BNC) concentrate was smelted in a pilotscale DC arc furnace to produce a nickel metal. The furnace was continuously operated for 12 days (24 hour/day), during which twelve different smelting conditions were investigated, with the major variables being reductant type and feed rate, flux composition and addition, and BNC feed rate.The 200 kW DC arc furnace was operated at power levels between 110 and 165 kW and at a total feed rate of 78 to 96 kg/h, resulting in an average slag and metal tapping temperature of about 1650°C. A total of 7.2 t of BNC were smelted, producing about 5.44 t of nickel metal and 2.94 t of slag. Nickel recoveries of 96.4% and higher were achieved, and the slag nickel content was as low as 0.1%. The major impurities in the metal were iron (mostly from oxygen lancing) and carbon. The calculated feed carry-over was less than 0.85% and the graphite electrode consumption was between 2.8–3.3 kg/MWh.IntroductionOne of the most distinctive advantages of DC open-arc smelting is the ability to process fine raw materials without any major issues with regard to the operability of the furnace, metal recovery, and metal quality. This has been demonstrated in Mintek’s DC arc pilot plant facilities over a period of about three decades (Curr et al., 1983). The materials that have been processed include laterite (Kotze, 2002), chromite fines (Curr et al., 1983), manganese fines (Lagendijk et al., 2010), PGM concentrates (Shaw et al., 2013), electric arc furnace (EAF) dust (Denton et al., 2005; Abdellatif, 2002a) and stainless steel (SS) dust (Denton et al., 2005; Abdellatif, 2002a; Goff and Denton, 2004), and petroleum fly ash (Abdellatif, 2002b). The top particle size of such materials can vary from a few millimetres (e.g. laterite) to micrometres (EAF and SS dust). Dusting, whether due to physical carryover of feed or to the arc side reactions, has been proven to be a non-issue. As such, the applications of DC open-arc furnaces have the potential to be extended to other raw materials such as particulate nickel oxide, which has a particle size much less than 100 µm.Nickel oxide is typically produced from laterite ore by sulphuric acid leaching, purification, and precipitation as basic nickel carbonate (BNC) (Rhamdhani, Jak, and Hayes, 2008) or as mixed hydroxide precipitate (MHP) (Mackenzie, Virnig, and Feather, 2006), and finally calcining at moderate temperatures (800–1200°C). The NiO product is very fine, with an average particle size in the range of 10–20 µm and a NiO content of more than 99%."

Jan 1, 2015

By R. Romano, E. Montalar, J. B. Serón

The SMR geomechanics classification system (adaptation of RMR for slopes) is reviewed with data from 87 actual slopes in Valencia. In a research project, SMR has been applied by a GIS system, as a method to forecast stability problems in future road construction. As a result of this work a methodology for GIS application has been developed. On revient sur la classification geomechanique SMR ( une adaptation du RMR pour talus et pentes) avec les dates de 87 talus existant autour de Valencia. Dans le cadre d’un projet de recherche SMR a été appliquée, avec un système GIS, comme méthode de prévision de stabilité problèmes dans la construction de futures routes. Une méthodologie pour l’application du GIS a été développe. Das Geomechanische Einteilungssystem SMR (eine Anpassung des RMR an Böschungen) wird an Hand der Daten von 87 Böschungen im Gebiet von Valencia überdacht. In einem Forschungsprojekt wurde das SMR in einem Geographischen Informationssystem (GIS) als Methode zur Vorhersage von Stabilitätsproblemen bei zukünftigen Straßenbauprojekten eingesetzt. Das Ergebnis dieser Arbeit ist die Entwicklung einer Methodologie für die GIS-Anwendung

Jan 1, 2003

By I. V. Filippova, Y. Foucaud, M. Badawi, O. Barrès, L. O. Filippov, S. Lebègue

Sodium silicate (Na2SiO3) is one of the most common reagents used in the froth flotation process, in which it is an efficient dispersant as well as a powerful gangue minerals depressant. Due to its high affinity with a lot of minerals, mostly silicates, it adsorbs on their surfaces and prevents the adsorption of the collectors, maintaining them hydrophilic. Hence, Na2SiO3 is widely used in the flotation separation of rare earth minerals, zinc minerals, iron minerals, scheelite, fluorite, apatite, and many other minerals. For decades, authors have demonstrated higher efficiency of Na2SiO3 when it is used in combination with sodium carbonate (Na2CO3), a common pH regulator. Among many well-known depressants, this system presented the best efficiency for many ores, including the Tabuaço scheelitebearing skarn studied herein. However, the mechanisms resulting in these strong positive synergistic effects are not well understood at the moment. Hence, the response surface methodology (RSM) was applied to this ore, considered as a case study, to optimize the depressing conditions and to study deeply the flotation behavior of this system. Strong synergistic effects between the two reagents were exhibited by the RSM, mostly affecting the scheelite, fluorite, and calcium-bearing silicates recoveries. This was attributed to surface carbonation of the minerals by Na2CO3, subsequently leading to a better depression by Na2SiO3. Overall, a 1:1 ratio between the two reagents displayed the best results in terms of WO3 grade and recovery. To gain understanding in the molecular mechanisms responsible for the aforementioned synergistic effects, FTIR studies were combined with state-of-the-art molecular modelling (Ab Initio Molecular Dynamics at 300 K) on fluorite, an archetype of calcium minerals. Keywords: Synergistic effects, scheelite, depressants, FTIR, DFT calculations

Jan 1, 2020

By P. W. van Deventer

?Soil quality is the capacity of a soil to function, within ecosystem and land use boundaries, to sustain biological productivity, maintain environmental quality, and promote plant, animal and human health?. In the long-term, vegetative rehabilitation of mining wastes aims at, as far as possible, the proper ecological integration of the reclaimed area into the surrounding landscape, which is sustainable and requires minimal maintenance. A certain succession pattern is therefore needed. Recent ecological concepts recognize the role of the substrate?s quality and nutrients in affecting the rates and directions of succession patterns. Although pedogenesis and eventually soil quality in mine waste are not well known, monitoring of soil quality parameters in kimberlite mine tailings reveal a remarkable establishment and or improvement of specifics oil quality indicators. During the same time the vegetative cover?s total functionality as well as reproductive ability improved. Functions of soil, and thus soil quality, can be assessed at the field, farm, ecosystem, pedosphere, and global scale. It is recognized, however, that management of soil becomes increasingly difficult at larger scales, but for demarcated mine waste sites it is possible to ameliorate and manage and assess soil functions and quality. Therefore the significance of the study is the following: soil functions and quality become inseparable from the idea of system sustainability, and are considered as key indicators of ecosystem sustainability on rehabilitated mine tailings material.

Jan 1, 2008

By I. Beukes, H. Kotze, B. Krause, R. P. Hattingh

Hillendale Mine is operated by Exxaro KZN Sands, and is situated on the north coast of KwaZulu-Natal in South Africa near the towns of Empangeni and Richards Bay, some 200 km north of Durban. During the mining operation the heavy minerals rutile, ilmenite, zircon and leucoxene are extracted for further beneficiation at a processing complex near the town of Empangeni. The deposit contains approximately 25% slimes (defined as the sub-45 micron fraction), and is mined using hydraulic monitoring. Run of mine is gravity fed down launders to pump stations, which deliver the material to a primary wet plant. Slimes is separated from the run of mine prior to the heavy minerals being separated from the sand. Sand tails containing approximately 2-5% slimes is pumped to the mining void. The slimes is thickened to a density of approximately 1.2, and most of the resultant material is pumped to a sub-aerial deposition site (residue dam). The area is characterized by an annual rainfall of approximately 1300 mm, which is relatively high by South African standards. From an agricultural perspective the soils are deep and well weathered. Dryland agriculture has been practised on an extensive scale in the area for the past 70 years. Sugar cane in particular is cultivated on and around the mine area. In terms of environmental approvals, the post-mining land use and objectives are defined as economically viable and sustainable sugar cane cultivation in the mined areas. During mining the soil profile is destroyed. In this paper the establishment of a reconstituted soil profile is discussed, with specific reference to the methodology that is being followed to achieve the homogeneous blending of sand and slimes. Defining the rehabilitation strategy and soil specification Strategically Exxaro KZN Sands divided rehabilitation into four aspects, comprising physical rehabilitation (restoration of soil structure), vegetative rehabilitation (restoration of vegetative cover), ecological rehabilitation (restoration of sustainable ecological communities), and sustainability (sustainable man/environment interface) (Hattingh and Viljoen, 2006). It is believed that the key to successful rehabilitation lies in achieving a substrate (soil) suitable for the establishment of the target vegetation. During the development of the rehabilitation strategy the key factor in the establishment of a suitable soil profile was shown to be the soil water retention of this material. Since dryland agriculture is practised, this aspect becomes critically important in ensuring that the post-mining land use is sustainable (Hattingh et al., in prep.). From a financial perspective, a closure certificate being issued implies that the state takes over financial liability for the rehabilitated land. This has significant implications for the state-the default position will be that all possible latent and residual impacts must be identified and known prior to a closure certificate being issued. From the mine's perspective this precautionary approach by the state implies that post-operational costs cannot be quantified exactly, and our approach is therefore to mitigate the risk of a long post-closure care and maintenance phase by means of addressing all potential latent defects during the operational rehabilitation phase. The financial viability of the soil reconstitution process itself is therefore not measured against other rehabilitation methods, but against the risk of not achieving closure. During a series of technical workshops comprising experts in the various disciplines in the rehabilitation of the soil profile were identified. These aspects include the re-establishment of a functional soil profile, soil physical characteristics, soil chemistry, soil biota, salinization potential, erodibility and soil weathering. The natural soils in the Hillendale area have been classified in terms of the South African soil classification system (MacVicar and co-workers, 1991) and consist of Hutton (orthic topsoils on red apedal subsoils) and Clovelly (orthic top soils on yellow apedal subsoils) soil forms. The topsoils consistently comprise medium to fine grained sand overlying heavier textured sandy clay loam to clayey subsoils. The topsoil structure consists of a single grain structure, whereas subsoils are apedal. These soils are typically deeply weathered and do not show secondary structures. During the mining process a layer of topsoil (300 mm) is stripped off, and the balance of the material down to the footwall is processed. Sand with 2-5% slimes (defined as the sub-45 micron fraction) is returned as backfill in order to re-establish the dune to approximate the previous landform. From an agricultural perspective this material is not suitable for the dryland cultivation of sugar cane. A capping of more suitable material therefore has to be provided. The most significant difference between the premining soil form and the backfill material is the percentage slimes, consequently a mixture of the sand and slimes is required as a capping over the backfilled sand. The required thickness of the cap is a function of specifically plant growth requirements, erodibility, weathering and runoff (Hattingh, et al.; in prep.). The percentage slimes required in the cap is a function of mainly soil water requirements (Hattingh and Viljoen, 2006). The conservative indications to date show that the reconstituted soil profile should consist of a homogeneously blended mixture of 70%-80% sand and 30%-20% slimes up to a maximum of 2 metres thick. This will be sufficient to ensure growth during dry periods.

Jan 1, 2007

By N. A. Sithole, S. A. C. Hockaday, P. J. A. Bezuidenhout

The Northern Cape Province in South Africa has high levels of annual direct normal solar irradiance and reserves of zinc (Zn) ores. The question arises as to the benefits of integrating renewable solar energy into the beneficiation routes of these reserves. The paper evaluates a novel flowsheet for the production and beneficiation of Zn in this region, maximising localised solar energy as a source for both electricity and process heat. Solar variability is discussed and the cost and benefits of thermal storage in the flowsheets are evaluated by its influence on the levelised costs of electricity and process energy over the project life-time at a possible implementation site. The results of the developed scoping model showed that solar photovoltaic integration to provide electricity for electrowinning without battery storage can lead to more than 10% cost saving on electricity over the lifetime of the project. Additional savings potential was identified when battery storage was included to enable the solar PV system to supply electricity during peak tariff periods. The solar thermal case showed the most promise with savings of 70% on heating costs for casting, while solar PV electricity without storage resulted in a 16% cost saving on heating for casting over the lifetime of the project. Solar PV electricity generation resulted in the avoidance of more than 20% of CO2 emissions from grid electricity use. Solar thermal heating can avoid up to 80% of the CO2 emissions associated with grid electricity use for remelting of Zn cathodes for casting. The CO2 emissions are indirect and not subject to South African carbon tax. Keywords: Solar process energy, zinc beneficiation, flowsheet evaluation

Jan 1, 2020

By M. Sibanda

The diffusion of carbon in Co-5% Fe alloy was studied in a belt-type pressure system at temperatures of up to 1330°C and press loads or nominal pressures of 7 020 tons or 42±3 kbar. Under these conditions, this alloy is in the solid state. Discs of graphite and prealloyed Co-5%Fe were used to make up the diffusion couple. The diffusion coefficient increased with increasing press load due to the tendency of the low density graphite to dissolve in the metallic phase reducing the overall volume and increasing the density of the system. Furthermore, inhomogeneous plastic deformation may have promoted diffusion by creating defects in the alloy. Diffusion couples treated at atmospheric pressure exhibited graphite particles in the metal, while those treated at high pressures exhibited carbide in the form of Widmanstatten laths. Carbon analyses indicated increased carbon solubility with increasing pressure. This was confirmed from calculated high-pressure phase diagrams.

Jan 1, 2005

By M. Reuter, C. Schuffeneger, T. Seppälä, L. Holappa

Reaction kinetics of solid-state reduction of chromite pellets (laboratory made and industrial) and lumpy ore was investigated by the thermogravimetric analysis (TGA) technique. Carbon monoxide was used as the reducing agent, with the presence of graphite in proximity to chromite. The experiments were carried out at both rising temperature and constant temperature in the range of 1450 - 1550°C. Scanning electron microscopy was employed to observe and analyse the structure and composition changes of the chromite samples. For the lab-made chromite pellets, the effects of particle size and bentonite addition on the reduction behaviour were studied. The pellet with smaller particle size gave a higher reduction rate. Bentonite addition had slightly negative effect on the reduction rate. When reducing industrial pellets, temperature and CO flow rate had positive influence on the reduction rate. Reduction of lumpy ore took place slower than reduction of a pellet. In all samples, chromite reduction proceeded longer in the outer part of the sample than in the centre part. The porosity of the chromite samples was determined before and after the experiments. The porosity of lumpy chromite increased significantly during the reduction. However, the porosity of lab-made chromite pellet decreases due to sintering effect. The reaction mechanism is discussed on the basis of experimental results and earlier investigations.

Jan 1, 2004

By T. Watanabe, S. Hayashi, M. Hayashi, K. Nagata, H. Fukuyama

Chemical states of fluorine in CaO-SiO2-CaF2glasses in a composition range of CaO/SiO2=0.5?1.3 and 5?25 mol%CaF2have been investigated by 19F solid-state NMR with and without MAS. The isotropic chemical shifts of the glasses are close to those of cuspidine crystal (59.4 and64.3 ppm with respect to C6F6) and CaF2crystal (58.6 ppm). The fluoride ions are coordinated with four or less than four calcium ions in this composition range. The chemical shifts move to the lower frequency with an increase in the CaF2content, whereas those are not affected by theCaO/SiO2ratio. The ionic distance between calcium and fluoride ions increases with an increase in the CaF2content. The chemical state of fluorine is not disturbed by the degree of polymerization of the silicate network. Comparing the MAS and static NMR spectra, the second moment attributed to 19F-19F dipole-dipole interaction has been estimated. The values of the glasses range over 3.1?7.3107Hz2andthose are larger than the calculated value of cuspidine crystal. This indicates that fluoride ions form Ca-F clusters in the glasses and that the size of clusters increases with increasing the CaF2content. Keywords: chemical state of fluoride ion, CaO-SiO2-CaF2glass, solid state 19F NMR spectroscopy

Jan 1, 2004

By C. S. Kucukkargoz, A. Bhalla

"The solid-state reduction of ilmenite concentrate with graphite was studied under argon atmosphere at temperatures between 1050°C and 1350°C. The rate of reduction increased with increasing temperature and decreasing particle size, with the maximum extent of reduction found to be 80% at 1350oC with a particle size in the range of -106 +90 µm. The activation energy for the reduction reaction was calculated to be 257 kJ/mole. The trivalent iron oxide was reduced first to divalent iron oxide and then to metallic iron. An annular ring of a partially reduced oxide phase containing metallic nuclei was formed around the core of ilmenite, which grew in size as the original ilmenite core shrank with progressive reduction. The reduction of titanium dioxide also took place during this stage, which produced the Magneli oxides in the form of TinO2n-1. The metallic phase had very high Fe and low Ti contents throughout the reduction, whereas the partially reduced oxide phase adjacent to the metallic phase was high in Ti and depleted in Fe. The metallic phase globules formed during this stage were small and are considered suitable only for leaching and not for other concentration processes. The core of the particle generally retained the composition of the original ilmenite. The purpose of this work was to remove iron and increase the titanium oxide content of the ilmenite to produce a high-titanium containing charge for subsequent smelting.IntroductionThe titanium-bearing minerals ilmenite (FeTiO3) and rutile (TiO2) are the primary natural raw materials used in industry to produce titanium metal and titanium-based products. The common titanium-bearing minerals are ilmenite, rutile, anatase, brookite, leucoxene, arizonite, and perovskite. Although the formula of ilmenite is commonly expressed as FeTiO3, the mineral can accommodate Mn and Mg, which are chemically bound in the form of (Fe,Mn,Mg)TiO3. Ilmenite concentrate can also contain Fe2O3 and Al2O3 in addition to the physically separable oxides such as SiO2 and CaO. The crystal structure of ilmenite is an ordered derivative of the corundum structure with a trigonal-rhombohedral symmetry. Fe2+ and Ti4+ ions occupy the octahedral sites, leaving the tetrahedral sites unoccupied. In each FeTiO3 unit, there are three O2- ions creating three octahedral sites, two of which are occupied by Fe2+ and Ti4+ (Wilson et al., 2005)."

Jan 1, 2017

By A. J. Jager, N. C. Joughin

The effects of extensive solid-waste packing as a support medium are described. It is shown that the waste packing resulted in excellent hangingwall conditions with only minor deleterious effects.

Jan 1, 1979

By S. L. George

The semi-solid metal casting process results in a unique solidification path. The microstructural features that were identified during the characterization of the as-cast microstructure, were used as evidence of the process history in order to determine the solidification path followed during the evolution of the microstructure. The morphology of the grains was characterized using SEM and the extent and distribution of the elemental segregation within the grain structure was analysed using EDS. Keywords Semi-solid casting, solidification path, segregation.

Jan 1, 2011

By M. C. Mulligan

Counter current decantation (CCD) thickener circuits are used to recover soluble metal as pregnant liquor solution from ore leach residue. The basis of CCD operation is to concentrate suspended solids thereby minimizing liquor content in underflow slurry that flow in one direction. Then the underflow slurry liquor is diluted with wash liquor that flows in the opposite direction and the suspended solids are concentrated again and again. The amount of liquor in the thickener underflow contributes to determining the number of CCD stages required to recover the desired amount of soluble metal. Furthermore, similar results could be achieved at a lower wash quantity, reducing the size of downstream equipment. High density thickeners (HDT) are designed to use gravity and compression, and minimize the amount of liquor in the underflow thus minimizing the number of CCD stages. This paper reviews the process used to select HDTs rather than high rate thickeners (HRT) for the Ruashi II copper-cobalt hydrometallurgical process in the Democratic Republic of Congo (DRC), using laboratory HDT simulations, to CCD simulations and thickener design details.

Jan 1, 2009

By R. Abela

In over ninety per cent of mineral sand plants, the most commonly used equipment is the spiral concentrator. The tonnage treated over typical spiral plants can range from as low as 200 ton per hour up to 6 000 tons per hour. Due to the limited capacity of each spiral, plants consist of multiple spirals assembled into banks. The mixture of minerals present in the sand feed requires several spiral stages to achieve the desired mineral recovery. Due to the complexity of the spiral circuits, there are always some design and operating problems that present themselves in plants. These range from slurry distribution, spirals operating at incorrect design parameters and feed variations. The material being treated is difficult to maintain in suspension due to its high density, resulting in segregation and preferential flow in pipelines, distributors and sumps. The objective of this paper is to highlight common problems associated with spiral installations to designers and operators of plants. Practical solutions are recommended in order to prevent and minimize these mistakes in the design. These solutions may be used to improve performance on operating plants.

Jan 1, 2003

By B. M. Munyungano

Rössing Uranium Mine operates a recovery circuit with continuous ion exchange followed by solvent extraction. Serious organic degradation problems were encountered during 1985/6, 2000 and 2005 in the solvent extraction plant. The preferential loss of the tertiary amine extractant was observed during the above-mentioned period. Previous investigations revealed that the tertiary amine was breaking down to nitrosamine, which cannot take part in the exchange reaction with U3O8. A reduction in the redox potential of the solvent extraction plant feed to below 500 mV halted this preferential loss. A lot of effort has been made to try and understand the actual mechanism for nitrosamine formation. Current understanding for the degradation is that formation is due to high nitrates on the strip side of the circuit emanating from nitrates from the precipitation process using ammonia. It is the current belief that pH lower than 3.7 on the strip side results in loading of nitrates onto the solvent. If oxidizing conditions prevail on the extraction side of the solvent extraction circuit, the tertiary alamine will then degrade into nitrosamine. This phenomenon is yet to be established and verified. It has, however, been established that the above process is brought about the following conditions ?High redox potential greater than 550 mV predominately caused by a high Fe3+/Fe2+ratio (4:1) ?Perception that if Fe2+<0.5 g/lit will contribute to high redox ?High concentrations of NO-3 in the conc eluate (feed to SX)/ammonium sulphate (NO-3> 4 g/l based on historic values) ?Presence of Mo as a catalyst ?Tests also have proved that the presence of nitrous acid in a concentration of 1 g/lat 550 mV leads to formation of nitrosamines from alamine.

Jan 1, 2007

By G. Bacon

The past decade has witnessed unprecedented growth in the development and implementation of solvent extraction technology in the extractive metallurgy of nickel and cobalt. Solvent extraction is proving to be a powerful tool, opening new opportunities for simpler, more cost efficient and environmentally sound metal refining processes. These advances, however, could not have been possible without the cooperative efforts between the nickel industry and the people and organizations involved with reagents, materials and equipment development and supply as well as solvent extraction research, aided by the accumulated knowledge and practical experience from the copper and uranium solvent extraction operations. This paper provides an overview of these developments and some of the challenges ahead.

Jan 1, 2002

By E. Robles

The Tati Activox® Project (TA®P) is the first step towards the implementation of the Norilsk Nickel Activox® process. The ultrafine grinding (UFG) and autoclave pressure leach process conditions are the heart of the Activox® patent. Low grade base metal sulphide concentrates are leached in the process to recover the base metals and to produce LME grade nickel and copper cathodes and cobalt carbonates. The downstream processing of the metal-containing liquor produced by this process includes solvent extraction circuits to extract and concentrate metal-rich solutions, before the various final products are obtained. This paper gives an overview of many of the relevant design aspects taken into consideration in the design of the Tati Activox® solvent extraction circuits. It addresses key design elements related to leach process conditions such as scaling, materials selection for corrosive solutions, pH control, crud formation and treatment, multiple SX trains designed to prevent organic cross-contamination, and design aspects related to the mitigation of fire risks.

Jan 1, 2009

By P. M. Cole

An unprecedented expansion of the global zinc industry is currently under way. While most new projects and plant upgrades remain committed to traditional processing technologies, recent advances in zinc solvent extraction (SX) have created opportunities for new process routes for both primary and secondary materials. The first commercial plant to use zinc SX for the mainstream processing of a low-grade ore is under construction and promises to become one of the lowest cost zinc producers. Several other oxide and sulphide projects in various stages of feasibility are considering the inclusion of SX in their process flowsheet. Zinc SX has also proved advantageous in the reprocessing of secondary materials, particularly for the treatment of zinc residues and furnace dusts. This review focuses on recent installations and projects underdevelopment that feature zinc SZ as the key separation step.

Jan 1, 2002

By Gerhard Nel, Huziel Masiiwa, Marthie Kotze, René du Preez, Simon Donegan

Tati Nickel is currently operating a hydrometallurgical demonstration plant in Botswana, using the Activox® process developed by LionOre Technology, to produce nickel cathode and a cobalt salt from a sulphide concentrate. Cobalt is extracted using Cyanex 272. This reagent also extracts all the iron, aluminium, copper, zinc, and manganese from the nickel stream. Versatic 10 carboxylic acid is then used as extractant to recover nickel from the stream, separating it from calcium and magnesium, and upgrading it to provide a suitable advance electrolyte for nickel electrowinning. However, the selectivity of Versatic 10 for nickel over calcium is limited, and gypsum formation in the extraction circuit is a problem when it is attempted to maximise the recovery of nickel. Mintek has developed a synergistic system with Versatic 10 for improved separation of nickel from calcium and magnesium. Laboratory test work was conducted on the raffinate of the cobalt solvent extraction circuit to optimise the Versatic 10/Nicksyn? (Mintek synergist) system to be employed. Extraction and stripping parameters suitable for this stream were optimised in the laboratory and then applied on the demonstration plant. A commercial batch (0.5 tons) of Nicksyn? reagent was produced for the demonstration plant. The laboratory test work results and the demonstration plant performance are discussed in detail in this paper.

Jan 1, 2007

By R. du Preez

Tati Nickel is currently operating a hydrometallurgical demonstration plant in Botswana, using the Activox® process developed by LionOre Technology to produce nickel cathode and a cobalt salt from a sulphide concentrate. Cobalt is extracted using Cyanex 272. This reagent also extracts all the iron, aluminium, copper, zinc, and manganese from the nickel stream. Versatic 10 carboxylic acid is then used as extractant to recover nickel from the stream, separating it from calcium and magnesium, and upgrading it to provide a suitable advance electrolyte for nickel electrowinning. However, the selectivity of Versatic 10 for nickel over calcium is limited, and gypsum formation in the extraction circuit is a problem when attempts are made to maximize the recovery of nickel. Mintek has developed a synergistic system with Versatic 10 for improved separation of nickel from calcium and magnesium. Laboratory testwork was conducted on the raffinate of the cobalt solvent extraction circuit to optimize the Versatic 10/Nicksyn? (Mintek synergist) system to be employed. Extraction and stripping parameters suitable for this stream were optimized in the laboratory and then applied on the demonstration plant. A commercial batch (0.5 tons) of Nicksyn? reagent was produced for the demonstration plant. The laboratory testwork results and the demonstration plant performance are discussed in detail in this paper.

Jan 1, 2007