AARONS, J. BOYD, Major. AGNEW, FRANK VANS. ALLEN, HERMAN H., Private, D Co., 8th -Reserve Engineers. BAINS, THOMAS M., Major, Engineer Officers' Reserve Corps. BANKS, H. R., Lieutenant, Canadian Engineers, B. E. F. BARBOUR, PERCY E., Deputy Supt. (Captain), New York State Troopers; Captain, 22d Regiment, N. Y. N. G. BARLING, H. B., Ist Lieutenant', Engineer Officers' Reserve Corps. BIGELOW, BRAXTON. BLOOMFIELD, E. C., Lieutenant. , BORROW, F. K. BROCK, R. W., Major, 19th Reserve Battalion of Canadians. BROOKS, ALFRED H., Captain, Engineer Officers' Reserve Corps. BROWNE, DE COURCY, 1st Lieutenant, Ordnance Dept., Fortress Monroe, Va.

Jan 9, 1917

By John Chipman, Peter J. Koros

The distribution of copper between liquid silver and liquid iron, Fe-C, and Fe-C-Si alloys was studied at 1600°C. From the data and the activity of copper in silver obtained from the phase diagrams, the activity coefficients of copper in iron up to 3 atomic pct are log y, = 0.90 — 2.4 N, and y": = 8.0. The effect of carbon up to saturation is expressed as log y = 1.8 Ni. The effect of silicon up to 11 atomic pct is insignificant. SLOWLY rising copper content of steel being produced is focusing attention on the lack of information on the behavior of copper in liquid steel. Chou' measured the activity coefficient of copper in liquid iron through its distribution between liquid silver and iron. He obtained a value of 9.12 at infinite dilution. Chipman' calculated the activity coefficient of copper in liquid iron at 1600°C from the phase diagram and obtained a value of 12. Ameiln and Pfeiffer- investigated the possibility of removing copper from liquid steel through the use of lead, silver, and bismuth as solvents. They also calculated that the activity coefficient of copper in liquid iron would be increased five or sixfold by addition of 4 pct C. Langenberg and Lindsay' are investigating the effectiveness of lead and sodium sulfide in removing copper from liquid iron. The experimental method was similar to that used by Chou' and Chipman and Floridis." Silver, copper, and iron were melted together, the copper distributing itself between the two layers so that at equilibrium a,.,, (in Ag) - a,.,, (inFe) and N,.,, (in Ag) yc,, (inFe) (in Ag). [21 N,.,, (inFe) Thus, from the concentration of copper in each layer and the activity coefficient of copper in liquid silver, the activity coefficient of copper in liquid iron can be calculated. The effect of an alloying element such as carbon on the activity coefficient of copper can also be determined from its effect on the distribution, provided the new element is essentially insoluble in silver. The one serious limitation of this method is the increasing mutual solubility of silver and iron in the presence of a third component. The mutual solubilities of pure iron and silver are negligible, but increase with increasing copper concentration beyond the range investigated. Ag-Cu System—The activity coefficient of copper in silver at 1600°C had to be estimated, since direct experimental data are not available. Kawakami" measured the heat of mixing of Ag-Cu alloys at 1200°C by a calorimetric technique. Scheil' calculated the heat of mixing in this system by use of the phase diagram, assuming that the solution is random and that the heat of mixing is independent of temperature. The terminal solid solution may be assumed to obey Raoult's law within the requirements

Jan 1, 1957

By M. C. Flemings, F. R. Mollard

Two-phase Pb-Sn alloys, ranging in compositiotz from 12 to 26 at. pct Pb, were unidirectionally solidified in a convection-fvee system, with thermal gradients in the liquid of up to 480°C per cm. Plane front solidification Loas achieved in all alloys at sufficiently steep gradient and slow growth rate. Conditions causing breakdown of the interface to a cellular or dendritic structure were roughly as predicted by a sinlple constitutional supercooling criterion. Structures of alloys of near-eutectic composition, solidified with plane front, exhibited a lamellar structure; the alloys furthest from the eutectic exhibited a rod-like morphology. Assumptions used in a previous paper for calculations of solute redistribution in two-phase plane front growth are shown to be reasonable for Pb-Sn alloys. Results of calculations are in good agveement with experiment. These show that variations in growth rate during solidification of the composite produce marked changes in average composition of the solid. IN a previous paper, Part I,' conditions necessary for plane front solidification of two-phase alloys were discussed and calculations given on solute redistribution in this type of solidification. This paper, Part 11, describes experiments on Pb-Sn alloys, designed to check the assumptions of the analyses presented, and to demonstrate their applicability to a given alloy system (Pb-Sn). APPARATUS AND PROCEDURE General. A vertical crystal growing unit was built for the study as described below, and "normal solidification" employed throughout (i.e., the ingot was completely melted except for a portion near the bottom end and then solidification initiated). The furnace was designed to permit achieving very low interface velocities, and steep gradients, in essential absence of convection; it is sketched in Figs. 1 and 2. Simple heat flow considerations indicated choice of a small-diameter specimen (ingot) to achieve high thermal gradients; ingot size chosen was 0.3 cm in diam. The ingots were held inside silica tubes 0.06 cm wall thickness. The requirement for an essentially convection-free system was met by use of the vertical furnace with the heat source over the heat sink, as well as by use of the small diameter ingots. In addition, by selection of tin-rich Pb-Sn alloys, the diffusion boundary layer (lead-rich) was denser than the bulk liquid and would not cause convection. The only apparent driving force for convection in this system was the small transverse temperature gradient resulting from heat flow into the samples from the furnace. Such convection must have been small, however, since 1) no temperature fluctuations in the melt were noted in the recordings, which would have indicated turbulent convection, and 2) experimental results obtained and described below could not have been achieved in presence of significant convection. Ingot Preparation. Pb-Sn alloys ranging from 12 to 26 at. pct Pb were prepared from high-purity lead and tin (99.9999 pct pure metal). Each alloy was prepared by first melting the pure metals in the proper ratio in air, in a Pyrex container. The melt was then stirred thoroughly with a graphite rod and cast into a preheated graphite mold. Ingots were then prepared from these castings for use in the actual experiments; each ingot consisted of a rod of alloy, 15 cm long in a 25-cm-long transparent fused-silica tube, 0.3 cm ID and 0.06 cm wall thickness. One chromel-alumel thermocouple, made with 0.004-in.-diam wire and protected by a two-hole alumina tube, was inserted into each ingot. The 1.5 cm of the thermocouple nearest the bead were protruding from the alumina tube and were coated with a very thin layer of boron nitride paste which provided electrical insulation while allowing good heat conduction. The electrically welded junction size was about that of each wire and the cross section of the two wires represented about 0.3 pct of the sample cross section. Including the coating, the thermocouple cross section still represented less than 0.5 pct of the ingot cross

Jan 1, 1968

For the year ending February, 1920 PRESIDENT HORACE V. WINCHELL MINNEAPOLIS, MINN. PAST PRESIDENTS PHILIP N. MOORE ST. LOUIS, Mo. SIDNEY J. JENNINGS NEW YORK, N. Y. FIRST VICE-PRESIDENT A. R. LEDOUX NEW YORK, N. Y. TREASURER GEORGE D. BARRON. . . . ' NEW YORK, N. Y SECRETARY BRADLEY STOUGHTON NEW YORK, N. Y

Jan 6, 1919

By F. M. F. Cazin

Some twenty years ago the author of a book,* by which, for the first time, molecular action was made to account for nearly all phenomena in hydrodynamics, began his preface as follows: " It is contrary to all experience, that any branch of science should suddenly cut short its own line of reasoning, and drop all connection with its past, and yet as quickly re-establish itself on an entirely new basis. It is, therefore, not without justification that this book should be met with caution and even distrust." When the newly-discovered natural facts and laws presented in this paper were, in 1891, first laid before the officers of the American Institute of Mining Engineers, they might have been preceded by a preface to the same effect; and the expression would have found its justification by the actual experience these facts and laws met with. Since then, as the result of their publication in one of the most prominent

Jan 1, 1895

By G. Birkbeck, T. C. Wells

Pearlite morphology in three commercially produced, low-carbon steels has been studied using optical and electron microscopy. A reduction in the cooling rate from 600° to 6°C per hr increased the interlamellar spacing but had little effect on pearlite content. The form of the lamellae was also assessed in terms of a new parameter, the ratio of lamellae length to interhmellar spacing. The variation of this parameter with cooling rate depended on steel composition. For each steel, it would appear that an optimum cooling rate exists at which lamellar pearlite can be produced to the greatest extent, though not necessarily the same extent in different steels. PeARLITE morphology depends principally on steel composition, prior austenite grain size, and either cooling rate or isothermal transformation temperature. Alloying with manganese,'" fine grain size,374 and slow cooling rates reduce the likelihood that a well-developed lamellar structure will be produced. Instead, imperfect structures usually consisting of partly globular carbides are formed in a ferrite matrix. Such structures have been described as granular.1,2,5 degenerate,6 or semi4-pearlite. Manganese additions also progressively lower the eutectoid temperature and the carbon concentration at the eutectoid so so that, for a given carbon content. the pearlite fraction is increased as manganese is added. While the effects of manganese are understood in a general way, quantitative studies of pearlite morphology have been carried out mainly on steels of eutectoid composition;9 little quantitative data is available for low-carbon steels. Certain anomalies exist in the behavior of steels containing -1.5 pct Mn, however. The pearlite morphology in niobium-treated steel differs from that which is generally accepted as typical of low-carbon/manganese steels in that a reasonably well developed lamellar structure is sometimes observed. In the present work, the effects of changes in cooling rate from 600° to 6°C per hr on the pearlite morphology in three commercially produced, low-carbon steels have been studied by both optical and electron microscopy. I) MATERIALS The steels were of the following types: 1) 0.1 pct C, 0.4 pct Mn steel (En 2, a composition similar to specification SAE 1010); 2) niobium-treated, 0.2 pct C, 1 1/2 pct Mn steel (BS 968:1962); 3) silicon-killed 0.2 pct C, 1 1/2 pct Mn steel (En 144, a composition similar to SAE 1320). The chemical analysis for each steel is given in Table I. To facilitate the comparison of pearlite morphology in the three steels, steels 1 and 3 (which were obtained as 1/2-in. plate and 1-in.-diam bar, respectively) were hot-rolled in the laboratory to $ in. thickness, finishing at around 850°C. The BS 968:1962 was received as 1/8-in. plate finished at 885°C and was not further worked. Specimens from each steel were heat-treated in vacuo at 950°C for 1 hr and cooled at rates of 600°, 60°, and 6°C per hr. 11) EXPERIMENTAL Pearlite contents were determined by point counting (500 points) on longitudinal sections mechanically polished and etched in 2 pct nital. Pearlite morphology is usually considered in terms of interlamellar spacing. For pearlite colonies randomly distributed in space and having a true, constant interlamellar spacing So Pellissier et al.9 determined the distribution curve for the apparent spacings of the lamellae on a random section plane. The areal fraction fs of the pearlite colonies occupied by apparent spacings up to a limiting value S is given by:

Jan 1, 1969

By W. Wanjokow, H. O. Hofman

In the metallurgical treatment of most metallic sulphides it is usually necessary to carry on a roasting-operation. In some cases the raw ore will have to be roasted; in others the intermediary product, matte, produced in smelting the ore; again, both ore and matte may have to be subjected to oxidation at elevated temperatures. Most metallic sulphides, when given an oxidizing-roast, pass through the state of sulphate before they are converted into oxides. All metallic sulphates are completely decomposed by heat, with the exception of those of lead and bismuth, but the temperatures at which decompositions take place vary with the metals. Some metallic sulphates are converted directly into oxides, others first form basic salts. Alkali-earth sulphates show a behavior similar to that of metallic sulphates, while alkali sulphates do not part with their sulphur trioxide even at elevated roasting-temperatures. The older data on the decomposition of metallic sulphates by heat are only approximations. Thus Kerl' gives the order in which metallic sulphates are decomposed with increasing temperatures as (Ag2, Fe, Cu, Zn, Ni, Co, Mn, Pb) SO,. More recent statenlents give definite temperatures and modify the formerly accepted order of decomposition. But the temperatures given by various observers do not agree. The reasons for this are to be found mainly in the method and manner of carrying out experiments. Four methods have been used: 1. Heating in an evacuated tube; 2, heating in a tube closed at one end, without air-cur-

Jan 1, 1913

By K. J. Rosengren

INTRODUCTION Mount Isa Mines Limited operates a major mining complex at Mount Isa in northwest Queensland, Australia. The location is arid and remote, some 600 miles distant from the nearest port of Townsville on the eastern coast (Fig. I). Current mine production is 6 million long tons per annum comprising 3.8 million tons of copper ore and 2.2 million tons of silver-lead-zinc ore. Copper ore production is scheduled to increase to 5.8 million long tons per annum by 1973 and a new silver-lead-zinc mine is being developed at Hilton, 13 miles north of Mount Isa. The Mount Isa and Hilton orebodies occur in a single stratigraphic member, termed the Urquhart Shale. This shale is conformable with several other sedimentary formations striking north-south and dipping approximately 65º west. The silver-lead-zinc orebodies occur in bands conformable with the shale bedding and tend to be of tabular shape, varying in width from a few feet to nearly 200 ft. The copper orebodies occur in breccia bodies, locally known as "silica-dolomite", within the Urquhart Shale and tend to be more irregular and massive with widths up to several hundred feet. The detailed geology is described by Bennett (1 2). At present, production comes almost entirely from underground operations with only about 25,000 tons per year of carbonate ore from open pit operations. The mining method used in the copper orebodies is sublevel open stoping with pillar recovery by pillar blast before stope filling or by sublevel caving after stope filling. A large primary sublevel caving operation was also carried out until recently in one of the orebodies. The wider lead orebodies are mined by sublevel open stoping, with or without pillar recovery, while cut and fill stoping is used in the narrower orebodies. Details of the mining methods are given by Davies (3). The company's interest in open pit mining stems from a large open pit which was mined out in 1965 and a further large open pit planned for future production. In addition, the company is currently evaluating several large ore deposits in Australia and New Guinea. All of these orebodies would be mined by open pit methods and rock mechanics studies of slope stability are now a standard feature of all open pit evaluations.

Jan 1, 1972

ALTHOUGH iron ores occur in many parts of Sweden the two principal deposits are those at Grängesberg (see accompanying map) and at Kiirunavaara-Gellivare. Both of these deposits are con-trolled by a holding company, Trajikaktiebolaget Grängesberg-Oxelösund, which sells annually about one-half of, the iron in ore traded in world markets and has a fleet of 24 seagoing ore boats, with a total dead weight capacity of 172,500 tons. Because of its pre-eminence in international iron ore trade a brief outline of its operations will be of interest. ORE DEPOSITS OF GRÄNGESBERG The Grängesberg deposits have been known since the Middle Ages, but up to the middle of the nineteenth century the ore was transported from the mines to the furnaces in winter in. sleighs. Railway building began in 1853, and in 1873 the complicated structure of capital investment was tottering, but the basic bessemer process created a demand for ore high in phosphorus, as this is, and refinancing on the initiative of Sir Ernest Cassel put the principal operation on a firm footing. There are numerous property owners in the district, but they are all controlled by a joint administration board, and 90 per cent of the ore is produced by a subsidiary of the Grängesberg company from proper-ties which it either owns or leases. The ore, a mixture of magnetite and specular hematite, is in lenticular bodies, dipping about 70 E. in. fine-grained gneiss, and contains about 61 per cent Fe and 1 per. cent. P. There are two principal veins; the total ore reserves to a depth of 500 meters are estimated at 150,000,000 tons. As seen in the accompanying illustration, the ores were first worked in open cuts, but eventually underground shrinkage stoping was adopted. Difficulties were encountered in the support of the workings and from the freezing of the ore in the stopes, so slicing was adopted, although block-caving is used in one place. Most of the mining is now done at a depth "of 150 to 190 meters. The present annual output is about 1,400,-000 tons of crude ore, which yields about 1,000,000 tons of concentrate after being subjected to magnetic con-centration and jigging.

Jan 1, 1927

By S. M. Purdy

Under certain conditions of hot rolling and air cooling from the hot-rolling temperature, bars of a high carbon (0.40 pct C) chrome-nickel austen-itic alloy were found to show magnetism even though no ferrite or martensite could be detected by microscopic or X-yay methods. The appearance of magnetism in such alloys may come from chromium impoverishment of the austenite grains near the precipitated carbide particles. SPORADICALLY, hot-rolled bars of Silchrome 10, an exhaust valve steel, have been found to be magnetic. Because of the analysis of the alloy—0.40 pct C, 18 pct Cr, 8 pct Ni, 3 pct Si —magnetism is unexpected. Preliminary investigation showed neither martensite nor ferrite to be present; only austenite and Cr23C6. Since a literature search was fruitless, a brief study was made of the appearance of magnetism in this alloy. The only basic difference between the two heats is the nitrogen content. Permeability was measured using a Severn magnetic gauge. This instrument consists of a magnet mounted on a counterbalanced arm. A set of calibrated plugs is placed in contact with one pole of the magnet. The specimen is placed close to the other pole of the magnet. If the specimen pulls the magnet away from the plug, it has a permeability greater than that marked on the plug. This technique is swift and reproducible. Previous experience has shown that the permeabilities obtained corresponded to those obtained on a permeater with a field strength of 100 oe. Specimens from both heats were annealed at temperatures between 1700 and 2300°F. One set of specimens was water cooled and another furnace cooled. All the water-quenched specimens were non-magnetic; the furnace cooled ones were magnetic as shown in Table I with no difference being observed between the two heats. Microstructural examination of the specimens showed the expected increase in carbon solubility with increasing temperature. Carbide solution was complete at 2200°F. The specimens heated to 1900°F or below showed some carbide precipitation from the hot-rolled structure. A furnace cooled specimen from a given temperature showed less carbide out of solution than the water-quenched specimen from the next temperature below; e.g., the specimen furnace cooled from 2100°F showed less carbide out of solution than the water-quenched specimen from 2000" F. These studies indicated that the appearance of magnetism was not related to the quantity of carbon in or out of solution and it was related to precipitation at temperatures below 1700" F. A set of samples annealed and water-quenched from 2100° F was aged for 4 hr at temperatures between 1000" and 1600°F; all were non-magnetic. A second set of samples, similarly annealed, was aged 1 to 24 hr at 1200°F with the results shown in Table II. None of the latter set of specimens showed magnetism until they had been aged about 8 hr. Magnetism was quite strong after aging 24 hr. X-ray diffraction studies on several of the magnetic specimens showed that the austenite had a lattice parameter of 3.58A and that the carbide was Cr23C6. Several of these samples were electrolytically digested in 10 pct HCl in ethanol, with a current density of 0.1 amp per sq cm. None of the particles in the residue were magnetic. Accidentally, one cell was run at 1 amp per sq cm; e.g., magnetic particles were found in this residue. After careful separation, the magnetic particles were mounted on a quartz fiber and their diffraction pattern determined using a 5.73-in. Debye-Sherrer camera with CrK radiation. These particles showed a fcc structure with a lattice parameter of 3.57A. Prolonged exposure, up to 16 hr, produced no other lines on the film. The following facts seemed to be established at this time: 1) Austenite was the magnetic phase. 2) Neither ferrite nor martensite could be detected. 3) Magnetization could be produced by aging at 1200°F. One explanation of these data is that the carbide precipitation impoverishes the region immediately around the carbide particle of carbon and chromium and increases the proportion of nickel. All of these serve to increase the Curie temperature of the region around the carbide particle. If the composition change is enough, the Curie temperature will rise above room temperature. If the volume of the affected region is great enough, the magnetism will become detectable. At low aging temperatures, composition changes are great enough but the overall volume of impoverishment is quite small

Jan 1, 1962

By F. J. Plecity, J. T. Michalak, W. C. Leslie

Isothermal recrystallization and grain growth in zone- and vacuum-melted irons and Fe-Mn alloys, up to 0.60 pct Mn, were studied in the range 480° to 650° C, after 60 pct cold reduction. In initial stages, rate of grain growth and rate of recrystallization of iron decrease with time. The recrystallization is typical of a growth-controlled process, and rate of growth is determined by the extent of recovery. Mn decreases rates of growth and of recrystallizatzon. The recrystallization process changes at about 0.30 pct Mn and nucleation may become time-depetzdet~t. In recent years, considerable effort has been expended in determining the effects of solute elements on recrystallization and boundary migration in fcc metals. The results have indicated that the effects produced by single solute additions are dependent upon both the element added and its concentration.'-' In contrast, there have been very few attempts to determine the characteristics of recrystallization and boundary migration in high-purity bcc metals, especially after heavy deformation, and the effects thereon of single solute elements.9-11 This study was undertaken to determine the recrystallization characteristics of various "high-purity" irons and the effects of manganese additions at two levels of base purity. It was hoped that the information obtained would improve our understanding of the recrystallization of pure metals and aid in formulating a theory for the effect of solute elements. The interest was not entirely academic, for the annealing of low-carbon steels, which is of very great commercial importance, is but poorly understood. MATERIALS The compositions of the irons and iron-manganese alloys used are listed in Table I. The zone-melted iron and Fe-Mn alloys were made by Battelle Memorial Institute. Iron S-1 was arc-melted in a water-cooled steel mold in an argon atmosphere. The ingot was forged into a bar, then given two horizontal zone-refining passes in an alumina boat. Iron V-4 was treated in a similar manner, but was not zone-refined. The iron for the zone-melted Fe-Mn alloys was induction melted in vacuum in MgO crucibles and cast into alumina molds. The ingots were forged into bars, machined to shape, and a groove milled down one side of each. The best available electrolytic Mn was placed in the grooves, and the bars were zone melted. The vacuum-melted Fe-Mn alloys were induction melted in this Laboratory in MgO crucibles and poured into cast-iron molds. Iron V-5 was purchased from National Research Corp. in the form of a small vacuum-cast ingot. The low-carbon steel was made by induction melting in air at the U.S. Steel Corp. Applied Research Laboratory. The history of the materials prior to the final cold reduction differed; these details are given in the Appendix. The penultimate grain size of the principal materials was kept in the range ASTM 2 to 4, except for the low-carbon steel. PROCEDURES The cold work prior to the final recrystallization anneal was kept constant at 60 pct. It is known that rolling procedure can influence the kinetics of recrystallization of ironI2; therefore, all specimens were rolled in one direction only, between clean,

Jan 1, 1962

Jan 1, 1939

By Gerhard Derge

A series of studies of the corrosion of tin is under way in the Metals Research Laboratory at the Carnegie Institute of Technology. The complete program includes examination of the corrosion properties of high-purity tin and the changes produced in these properties by the addition of varying amounts of alloying elements. Other studies of this subject have been made recently under the sponsorship of the International Tin Research and Development Council, but these researches have been confined largely to the weakly acid environments commonly encountered in the canning industry.' There is little information available regarding the corrosion of tin under alkaline conditions, but such data would be of value, for a large amount of the metal is used under such conditions. The potential measurements to be described were made because they seemed to offer the most rapid method for obtaining a general view of the conditions to be encountered in such service. These experiments will also serve to establish a technique that will be of value in further studies. It must be emphasized that the results reported are those of controlled laboratory experiments and that the conclusions drawn cannot yet be applied to service conditions; rather, they point to the directions in which more exhaustive experimental work may be done to best advantage. Experimental Procedure The first work was devoted entirely to the problem of obtaining reproducible results from a series of potential measurements. Only the methods finally adopted as standard will be described here, except when the variations from these have furnished results of interest. The cell used is shown schematically in Fig. 1. The electrolyte is contained in the vessel A (an inverted bell jar), whose ground top is fitted to the transite-board lid B. The controlled atmosphere can be admitted

Jan 1, 1938

Large equipment for quarrying and for the various stages of crushing and grinding are the trend for new and existing operations. Included are large size haulage units, fast drilling equipment, impact crushers and large mills capable of high tonnage rates for metallic and nonmetallic minerals. In grinding, large-size mills continue as the choice in industries where grinding constitutes a major portion of the processing. Typical is a 10 x 34 ft two-compartment mill in closed circuit with an 18-ft diam air separator for cement. Other cement mill sizes are in the order of 12 x 36 ft, 2500 hp; 10 x 37 ft ball and rod (wet), 1400 hp; 13 x 36 ft, 3000 hp; 13 x 40 ft (wet), 3000 hp. Several installations of combination ball and rod mills have been made, and one of the largest is 12 x 45 ft. In connection with the wet grinding of raw materials, the DSM 270-degree screen has been installed in several cement plants with the intention of producing a material finer than 50 mesh. In ore processing, large autogenous mills (121/2 x 20 ft) are being installed.

Jan 2, 1964

By C. W. Parmelee

THE ideal fuel for burning ceramic wares is the one that, among other characteristics, has little or no sulfur. For that reason wood was long considered the most desirable fuel but its high cost has practically eliminated its used except in regions where it is very abundant or other circumstances warrant its choice. The fuels commonly employed are natural and producer gas, oil, and coal. The last named is undoubtedly the most important, not only in this country but abroad. Occasionally anthracite is used but the larger part is bituminous. The quality of the coal used depends on the kind and the value of the products being manufactured. For some materials, such as common brick, hollow block, etc., the quality of the coal is of less importance than in the manufacture of polychrome terra cotta, pottery, porcelain, etc. It is obvious that in burning clays that contain notable amounts of pyrite, marcasite or gypsum, as is the case with many common clays, the sulfur content of the fuel is of much less importance. The permissible amount of sulfur in the coal used will depend on the kind of product being manufactured. "A good sample' of coal commonly used in pottery ovens has something like this quantity of sulfur." PER CENT. Total sulfur 1.20 Sulfur in the ash 0.11 Volatile sulfur a 1.09

Jan 9, 1919

The Midvale Plant of the United States Smelting, Refining and Mining Company, situated twelve miles south of Salt Lake City, consists of mills for concentrating lead-zinc ores and a custom lead smelter. The milling department includes a 475-ton gravity mill for ores from the United States Mines at Bingham, a 100-ton Huff electrostatic zinc plant and a 60-ton pilot flotation mill for differential separation of lead and zinc. The gravity mill and electro- static plant are being replaced by a 600-ton differential flotation plant, now under construction, for differential separation of lead, zinc and iron. This new mill will have capacity for treating custom ores in addition to ores from the company's mines at Bingham.

Jan 1, 1925

By T. F. Witherbee

IN the sections, Figures 1, 2, and 3, are shown three crucibles that have been applied to substantially the same furnace, all the conditions having been the same except a variation of one foot of bosh, and a slight variation in the angle of the same. The bosh of No. 3 was originally the same as No. 2, the additional foot in diameter being the result of three months' cutting. Beginning with No. 1, which was 5 feet 6 inches diameter, with tuyeres 5 feet 4 inches high, and cinder-tap four feet from bottom, great trouble was found in holding iron a proper length of time, four hours being the outside limit when working well, and two hours or less if working badly. "Break-outs" through the iron

Jan 1, 1880

Owing to circumstances which are entirely unavoidable, the cost of rendering to Institute Members the services which they have been ac-customed to expect from the Institute has increased enormously, especi-ally during the past year. The cost of printing has increased 20 per cent. and another 30 per cent. is expected. There is no recourse; the Institute must pay this or cease publishing. The increase for supplies and office force will be very great. Justice to our employees, whose cost for living expenses has risen by leaps and bounds, demands an increase in. wages, wholly aside from the fact that the employees need not and will not stay. The Institute is, therefore, faced with the alternative of greatly re-ducing its service to the members or else of asking from them a small increase in clues. An amendment to the Constitution has been offered by the members increasing the clues to $15 per year, which cannot become effective until 1921. This still leaves us as the engineering society with the lowest annual clues, except only one, whose dues are $15 per year. To help meet the immediate emergency, the Directors have exercised the authority vested in them by the Constitution and By-Laws and requested the members to pay $3.00 for the Transactions to be issued during the year 1920, which is very much less than the cost of publication. It is the opinion of the Board that the members will prefer to pay this slightly additional expense rather than to have the Institute take a backward step in respect to the services which it is rendering, and which has been increasing constantly in amount, as well as in unit cost, during the past seven or eight years.

Jan 12, 1919

By S. Vela, R. M. McKinley, L. A. Carlton

Johnson et al. have described a new well-testing technique that measures formation flow properties between wells.' The technique, called pulse-testing, requires a sequence of rate changes in the flow at one well and measzcrement of the re.rulting pressure changes at an adjacent well with a very sensitive differential pressure gauge. This paper describes an extensive application of the technique in a producing oil field. Pulse-tests on 28 of 45 possible well pairs in the field provided a picture of the areal distribution of reservoir hydraulic diffusivity, trans-missibility and storage. The primary objective in presenting these data is to demonstrate the potential of the methcid for reservoir description. A second objective is to show in three ways the qualitative and quantitative accuracy of reservoir parameters determined from pulse-tests: (I) pulse-test data show a nonuniformity in the field, closely correlating with the oil-water distribution as given by production data: (2) pulse-test values for permeability are comparable with core va1ue.s; and (3) perhaps most important, the field responds to a conventional interference test in the manner in which pulse-test data predict it should. The pulse-testing technique by Johnson et al.' is an ideal source of data for purposes of reservoir description, for it provides a measurement of formation storage S = +ch, hydraulic diffusivity 91 = k/+cp and transmissibility T — This paper describes an application of this method in a producing oil field. Results were analyzed to give numerical values for the parameters 7, T and S. These values were compared with oil-water production data (for the effect of fluid saturation), with core data and with data from an interference test. The reservoir in which the pulse-test survey was run is the result of a structural trap formed by a fault along the east side of a north-south trending anticline. A down-structure aquifer providcs a natural flank water drive for the pool. The producing formation is a dolomitic lime- stone having mainly vugular permeability; the formation oil has a gravity of 29" API with negligible dissolved gas. The field contains 19 wells, all on pump, arranged on 40-acre spacing along the top of the anticline. Fig. 1 shows the location of all these wells except two at the south end of the field. The dashed line on the right-hand side of the figure represents the approximate location of the fault with respect to well positions. Pulse-Test Survey and Analysis of Data A pulse-test requires a pulsing well and a responding well. In the field, changes were made in the rate of flow at the pulsing well by stopping and starting the pump periodically and measuring the corresponding pressure

Jan 1, 1969

By H. R. Reed

THE cost of hoisting with electricity in deep mines is a matter about which little information has been published. This paper makes a detailed study of such costs and presents the information in a series of curves. In particular the curves show the cost of hoisting ore from depths varying from 500 to 7000 ft. Vertical with the shaft at 70° incline for the double cylindroconical and double cylindrical drums, the hoists operating balanced, using Ward Leonard and Ilgner-Ward Leonard control, and designed for most economical operation from each depth. Operation with the double cylindrical drum is expanded to cover hoisting from 2000 to 5000 ft. using equipment designed for 5000 ft. and from 4000 to 7000 ft. using equipment designed for, 7000 ft. Additional curves are included to show the ratings of the necessary hoist motors, energy input per hoisting cycle and size of flywheel in tons for complete equalization when the Ilgner-Ward Leonard system is used, also hoisting efficiency. The duty imposed on a mine-hoist motor fluctuates between wide limits during a cycle of operation. The demand on the motor may vary from a large horsepower value' near the beginning of the cycle to a small or a negative demand near the end of the cycle. Such factors as tonnage to be raised per hour, depth of shaft, and balanced or unbalanced opera-tion have such a marked effect on the operating cycle and vary to such an extent for different mines that no set of rules can he formulated for quickly determining the size of the motor required. The duty cycle from which the motor rating is (derived must he determined for each case according to the conditions of the proposed hoisting operations. The motor torque required at the cardinal points of the duty cycle is determined from the moment or torque in pound-feet necessary to raise and lower the load and ropes, accelerate and retard the load, ropes, drum, etc. The torque diagram depends largely upon the type of drum. Two different types of drums, if used on exactly the same duty cycles, may have widely different peak demands and capacities of hoist motors. The essential feature in the design of hoisting drums and in determining

Jan 1, 1937