By W. McA. Johnson

The work of J. E. Johnson, Jr., on the effect of small amounts of oxygen in cast iron in increasing its strength and resistance to shock, is of interest from the technical and scientific standpoints. The following exposition of the theory carries Mr. Johnson's explanation further and, in my opinion, will disclose certain related phenomena and perhaps shed further light on the subject. Some facts, so novel in character as to excite incredulity, have been accepted finally by many metallurgical authorities. One of these is that oxygen to the amount of 0.060 per cent. in cast iron gives it a breaking strength of 3,500 Ib. per square inch, compared with a breaking strength of 2,500 lb. per square inch in cast iron of the same composition with respect to elements other than oxygen, but having only 0.010 per cent, oxygen. The "oxygenated" cast iron, even if made in a coke furnace, has properties equivalent to the best charcoal pig iron. Mr. Johnson has also established the fact that the variations in combined carbon cannot account for the results. By microphotographic evidence he has shown that in oxygenated cast iron the graphite particles are dense and spherical, while in well-deoxidized cast iron the graphite particles are flaky and leaf-like. It is just a matter of common sense that iron of the latter structure is much weaker than the former. The analytical and microscopical work has been done with care and there is no doubt in my mind about the accuracy of the experimental results. In this paper then, we shall consider it as accepted that small amounts (0.060 per cent.) of oxygen increase the strength of cast iron by producing a structure in which the round and solid particles of graphite are surrounded firmly by a principal matrix of ferrite. The purpose of this paper is to show that the reason why the graphite particles are round is founded on the fact that the particles of any precipitate are made denser and harder by the presence of a reagent having a solvent action on the precipitate. This can be stated as a law, although I have never seen it so given in any textbook. Let us then, for purposes of illustration, give a concrete example and develop the theory of such mechanical and chemical actions as occur: It is well known that, by a soluble sulphate, a barium salt in solution is precipitated in a dense and easily filtered body when the solution is

Jan 1, 1916

By Walter Bonsack

THE CHAIRMAN.-This is the third and last session of the Institute of Metals Division's Symposium on Secondary Metals, and certainly the best of those that I have attended in the last few years. I would say that the increase in interest in secondary metals is quite noticeable by the steadily increasing attendance at these meetings. We have heard about the necessity of utilizing salvaged materials, but we still speak about them as low-grade, or down-graded materials. We still have the wrong perspective. We must willingly admit that these materials are valuable; we cannot go on using the choicest primary metals as morsels for our economic diet in a war of such unbelievable dimensions. This brings up the question-why are we so selective. The answer certainly is not that we know nothing else will do, but rather that we do not know what else will do. To be honest, we should admit our lack of knowledge concerning our complex alloys. Compared to the organic chemists, we metallurgists are very conservative, and the sooner we realize this and start to overcome it the better, because if we do not eliminate this difference, many customers of the metals business will go over to the plastics. If we take for example the development of aluminum alloys, you will see what I mean. From the binary aluminum alloys of 1920, we have progressed to ternary and quarternary alloys in the 1930's. We are only now beginning to use more complex alloys as we are forced to learn more about the effect of various elements on existing alloys. The effects of these elements should be studied now. They can be studied by two methods of approach. The usual method is to start from the base alloy and add various elements one by one in increasing amounts and study the resultant changes in properties. This is a tedious, long way. The other method which the smelters frequently use is to take the off-grade heats and study their characteristics. While the producer of primary alloys often has difficulties in alloying certain elements with the alloy under investigation, the smelter often finds them well alloyed in his raw materials and has no difficulties at all. Elements such as lead are difficult to alloy with aluminum and they tend to segregate severely. However, the amount which will remain alloyed in the metal is usually found in some "secondary" aluminum alloys. If one considers such concentration as the saturation, then by dilution with the same type of alloy, but free of such element, one can produce numerous intermediary alloys for investigation. In this fashion one is fairly certain to get uniformly spaced concentrations of the element under investigation. Similar cases probably exist with other metals. Nevertheless, the amount of work necessary to study all possible combinations is still tremendous. Necessity forces us now to utilize alloys which contain more elements than we are accustomed to. It is, therefore, necessary to study carefully the more complicated alloys. In secondary aluminum we are working and using the alloys which contain as many as 6 to 10 elements and we have learned over a period of several decades to balance

Jan 1, 1943

By G. E. Agar

The energy required for dry grinding of phosphate rock in ball and roller mills has been analyzed by the method suggested by Charles and others. The findings are not wholly in agreement with Charles' predictions; but, nevertheless, the method of analysis is shown to be sound. Some of the deviation is probably attributable to the characteristics of a dry grinding system. Many laboratory and pilot plant scale experiments have been made to determine the energy requirements for size reduction. This topic was recently reviewed by Agar and Brown' and it was apparent that very little if any data exists in the literature which permits one to apply the Charles 2-Holmes3 analysis to industrial size systems. More recently, the idea has been put forward that the postulate of comminution by impact used by Charles and others was not sufficient to explain size-reduction throughout the grinding operation. The opportunity exists in the grinding operations of International Minerals and Chemical Corp. (IMC) to analyze the energy-size relationship for dry grinding phosphate rock in both ball and roller mills. This situation arises because the mills are used for custom grinding and make products from 50% to 85% minus 200 mesh. BACKGROUND A correlation of particle size in a comminuted material with the energy expended in size reduction was proposed by charles2 to be of the form

Jan 1, 1965

By Edward Griffith

The anthracite industry, which produces about 50 million net tons of coal annually, has been talked of as being able to last for another century; but if the water record of the past century continues into the expected century, this expectation of many years production still to come out of the remaining reserves will not be attained. The industry will be a submerged one in fact as well as in name. A recorded forecast of what has since occurred appears on page 34 of the Mine Inspectors' reports of 1897: It should also be noticed that bodies of water had accumulated in parts of abandoned mines before duplicate surveys of the same were required by law; and as a result we have today to contend with bodies of water, the exact location and position of which are not correctly known. Since that date, 47 years ago, the implications of the foregoing comment have grown enormously. This is shown in Fig. I and in the following table showing flooded and partially flooded areas that have come into existence since the early 1930's in the northern anthracite field: Number of Year Flooded Areas 1932...................... 2 1933...................... 3 1934..................... 3 1935...................... 5 1936...................... 7 1937...................... 9 1938.................... 11 1939...................... 11 1940...................... 11 1941...................... 14 1942...................... 14 1944...................... 26 Similar conditions exist in other fields in the anthracite region. In the period between 1923 and 1940, abandonment of collieries in the southern field resulted in the flooding of approximately 60 sq. miles (30 per cent) of the field. The ahandonment of collieries in this field has imposed additional expense for pumping on the collieries still operating. This condition will be aggravated by the extension of developments and cause suspension of operations if economic conditions do not justify the assumption of additional pumping costs. During the years, the region's rainfall has not altered, but the quantity going inside the mines through breakages in the surface, brought about by extraction of the coal, has increased materially, as indicated by the ratio of tons of water pumped to tons of coal produced underground for one of the large companies in the northern anthracite field: Year Ratio 1920................. 8.4:1 1925.................. 10.6:I I930.................. II.4:I 1935................. 26.2:1 1940.................. 32.7: I 1942.................. 30.3:I The data in Table I shows the total amount of water pumped and its ratio to underground production for one of the large companies in the southern anthracite field, and shows a rapidly growing serious situation. Rainfall quickly affects the workings in all the fields. In mine inspection district 7 of the southern field the rainfall in 1935 was 92,083,000,000 gal. The total water pumped was 36,274,000,000 gal. (39.4 per cent of the rainfall). The operating mines

Jan 1, 1947

Recently the Colorado Engineering Council was formed "to coördinate the work of various technical, scientific, and engineering organizations, promote the welfare and professional standing of their members, and foster a more general recognition of the engineer in civic matters." The membership consists of local associations of members of the national engineering societies and other local engineering, scientific, or technical associations.

Jan 8, 1919

By T. O. Anderson, E. J. Stahl

Tests to increase knowledge concerning the process of hydraulic fracturing have been performed on three wells in the Allegheny field in western New York. The fracture orientation and its physical appearance at the well-bore was determined by impression packers run at appropriate times throughout the program. Fract~tre azi171uth and its dimensions thus determined were compared to the rock properties and treatment conditions. Logs to provide data concerning rock properties and to improve identification of vertical fractures were run before each step of the fracture treatment. Pressure osc~illu~iot~s were studied after each phase of tile treatments surface pressures during treatment. These measurements show that subsurface pressures exhibit many of the same characteristics as surface pressures during treatment of a well; however, transient pressures are dampened and deelayed in time at the bottom of the well when COmpared with surface pressures. Data obtained from this study provides a means to help locale and determine orientation of vertical fractures made in the open wellbore. Although these rests were performed in only one area, much of the information gained may be applied to fracturing programs in orher areas. INTRODUCTION In this study, various tests were made to provide data to better understand formation fracturing in situ. The reservoir studied is the Richburg oil sand which is a part of a series of predominantly grey sandstones and shales with occasional brown sandstone layers, known as the Caneadea unit of the Canadaway group of Upper Devonian age. Average physical characteristics of 12 cored wells in this area are 13-ft thick gross sand formation, 12-ft thick net sand. 1.7 md permeability, 11 percent porosity, 44 percent oil saturation (before secondary recovery) and 16 percent water saturation (before secondary recovery). This particular area of the Allegheny oil field was originally drilled prior to 1890. The first waterflood secondary recovery attempt was made in 1929. The present sustained waterflood development began in 1951 and is being carried out on a 4.5 to 5-acre spacing. Objectives of these tests were to (I) study fracture azimuth and dimension in relation to rock properties and treating conditions, (2) improve fracture identification techniques, (3) compare surface and subsurface pressure during all phases of treatment and (4) compare the periods of the fluid column oscillations occurring after each phase of treatment. Although the areas of investigation listed appear divergent in purpose, the program was designed primarily to increase knowledge of down-hole conditions leading to rock failure and extension of the fracture thus created. TEST PROCEDURES Wells upon which tests were conducted are designated as Wells 1 through 3. Well 2 was located 440 ft north of Well 1, and Well 3 was located approximately 880 ft west of Well 1. Wells 1 and 2 were completed with cable tools, while the producing interval of Well 3 was rotary cored using fresh water as the drilling fluid to obtain oriented cores. Tests were divided into separate phases on each well as the fracturing program progressed and consisted of measurements performed prior to treatment, during and after the formation breakdown operation. during fracture treatment and after treatment. To verify location and azimuth of the fracture created, and to obtain an impression of wellbore irregularities, a packer was used (Fig. 1). This packer was lowered on tubing into the wellbore opposite the interval under study and inflated in stages to allow the impression material to conform to the wall of the wellbore. A magnetic compass was attached to the tool for orientation reference. Impressions made prior to treatment showed no existing fractures in the wells under study. Impressions made after both formation breakdown and treatment pro-

Institute of Metals Division Ferrous and Nonferrous Physical Metallurgy Established as a Division April 26, 1918 (Bylaws published In the 1944 TRANSACTIONS Volume of the Division) A A SMITH, JR, Chairman E A ANDERSON, Past-Chairman F N RHINES, Senior Vice-Chairman W A DEAN, Vice-Chairman H A MALONEY, Treasurer ERNEST KIRKENDALL, Secretary 29 West 39th Street, New York 18, N Y Executive Committee R M BRICK 2 W A JOHNSON 1 H I DIXON 2 E W PALMER 1 M GENSAMER 2 J H SCAFF 3 J D HANAWALT 1 J D SULLIVAN 3

Jan 1, 1952

By H. M. Howe

On commencing the construction of the Orford Company's copper smelting works, at Bergen Point, N. J., I endeavored to convince our President, Mr. W. E. C. Eustis, by actual tests, that at the pressure of from 15 to 18 ounces per square inch, employed by us in smelting, less power was consumed in delivering a unit of blast by a Baker blower than by a fan blower. I attempted to prove this in the following manner: Across the mouth of a No. 5) Baker blower I firmly fastened a board with two round holes, 6 inches in diameter, cut in it. The board was fastened so tightly that no air could escape except through the holes. I then drove the blower at several differerent speeds, observing the pressure at which the air excaped through the two openings for each different speed of the blower, and also indicating the engine, whose only work at that time was to drive the blower. From this I calculated the quantity of power required to deliver, with a Baker blower, sufficient air to keep the pressure at a given point, while it escaped freely through the two six-inch apertures into the open air; or, in other words, to deliver air at a given pressure through these two openings. From the total power so consumed it was, of course, necessary to deduct the power which was required to drive the engine itself. This was ascertained by removing from the engine the belt which drove the blower, and then noting the quantity of power consumed in simply turning the engine over without any

Jan 1, 1882

By V. B. Kurfman

Grain refinement of Mg-Al melts by carbonaceous additions has been attributed to nucleation by aluminum carbide. The effects of process and alloy variables are interpreted and predicted in terms of the dispersion and chemistry of this phase. The grain coarsening action of Be, Zr, Ti, R.E., chlorination, temperature extremes, and prolonged holding times is described. Measures necessary to insure an adequate dispersion of the catalyst are discussed. CARBON inoculation treatments have become fairly well known and used for grain refinement of magnesium alloys containing Al. Although there is general agreement that a nucleation process occurs, the process is not understood and the inoculants are used in a rather empirical fashion. The treatment is applied to the class of alloys containing 3 to 10 pct Al, i.e., AZ31A to AM100A. Typical methods involve melting, alloying, and adjusting the temperature to 1400° to 1450°F. Then 0.01 to 0.5 pct C as CaC2, C6C16, or lampblack is added by any convenient means, and the melt poured within 10 to 30 min. Investigators generally have been impressed by an assumed similarity of this refinement process to superheat grain refinement, which depends on heating approximately the same alloys to a temperature in the range of 1550" to 1650°F, then pouring promptly after the melt is cooled to the pouring temperature. Various predictions have been made that carbon refinement would replace superheating in commercial practice due to reduced process costs, but this replacement has not fully taken place because of production difficulties and conflicting observations. Davis, Eastwood, and DeHaven1 agree with Nelson2 and wood3 in suggesting that an excess of inoculant may be harmful. Wood however says that overtreat-ment is not a problem in production use of hexa-chlorobenzene inoculation, and Hultgren and Mitchell4 claim no evidence of harm from excess additions. Various grain coarsening reactions are known to occur, including the possibility of overtreatment mentioned above. Trace amounts of Be,2 Zr, and Ti may prevent refinement by either a carbon treatment or a superheat. Occasionally treatment with cl25 may cause coarsening, although the Battelle refinement process' uses a CC14-C12 blend. Grain coarsening also tends to occur on holding at temperatures below 1350°to 1400°F, especially after a superheat treatment, and for this reason Nelson2 stresses the desirability of a refinement method useful at lower temperatures for open pot melting practice. Since a carbon treatment can be made to work at temperatures below 1400°F, it seems desirable to investigate the mechanism of the refinement and the mechanisms of the coarsening reactions in order to establish control conditions for use in commercial production. The identity of the nucleating phase must first be established and then the factors affecting its chemistry and physical dispersion must be determined. THE IDENTITY OF THE NUCLEATING PHASE Davis, Eastwood, and DeHaven suggested that the nucleating phase in this system is Al4c3,1 but Mahoney, Tarr, and LeGrand8 disagree, largely because they found no evidence of the compound in alloys after carbon treatment and because there is no indication that aluminum carbide should be unstable over the temperature range used in the superheat treatment. This latter objection is based on the assumption that both the carbon treatment and the superheat treatment introduce the same nuclei. Electron diffraction studies have been made to identify the nucleating phase. Samples of grain refined A292 have been selectively etched SO that clean surfaces are obtained and so that secondary phases are in relief. Electron diffraction patterns from these surfaces have established that the carbon treatment of A292 introduces into the metal a large number of small, plate-like particles with a structure very similar to Al4C3. In most cases, the plate-like nature of the particles prevented positive identification but in the cases where the identification could be made the particles proved to be AIN A14C3. However, enough variation in lattice constants was observed so that all compositions from pure A14C3 to the 50:50 solid solution A1N.Al4C3 were probably present.14 In A14C3 and especially AlN.Al4C3 the A1 atoms occur in layers within which they have the same hexagonal symmetry and spacing as the Mg atoms in a single basal plane of a magnesium crystal. The solid solution spacing lies between the 3.16 of AIN and the 3.3? for Al4C3, in satisfactory agree-

Jan 1, 1962

By Raymond Dugdale, Fathi Habashi

There has been a recent interest in studying the action of anhydrous sulfur trioxide on ores to convert the metal values into a water-soluble form as a substitute for leaching by sulfuric acid. For example, Svenke1 converted the small amounts of uranium in slate ash into a water-soluble form by treating the material with SO, at about 600°C. Chao and Sun found that a variety of aluminum-bearing minerals could be sulfatized by SO, in the temperature range 400° to 600°C usually in the presence of a catalyst such as sodium sulfate. Kruse3 patented a process for beryllium recovery from the low grade ore in Utah by first reacting it with SO, at 560° to 750°C then leaching the product with water. In the present report, the action of SO, was examined in the temperature region 100°-300°C which was not investigated by those workers. Experimental Tests were conducted on a beryllium ore sample from Utah, the analysis of which is given in Table 1. It corresponds closely to a saponite ore type as given by Crocker et al. It was in powder form 45% passing a 400

Jan 1, 1973

Jan 1, 1923

By Klaus Schwerdtfeger

The equilibria in the Cr-N system have been investigated in the temperature range 1100° to 1310°C by reacting chromium powder with Nz-Hz gas mixtures. The solubility of nitrogen in chromium in equilibrium with chromium subsitvide ("Cr,N") is given by Chromium subnitride is nonstoichiotnetric; its nitrogen content is always less than that corresponding to the formula CrzN. The lattice paranzeters of quenched samples have been measured; c, and a. parameters are found to increase with increasing nitrogen content. The growth rate of the subnitride layer on chromium plates was measured by a thermogravimetric technique, using a silica spring balance. The self-diffu-sivity obtained from the theoretical analysis of the parabolic rate constant is found to decrease with increasing nitrogen content, i.e., with decreasing vacancy concentration in the nitrogen sublattice. The intrinsic nitrogen diffuivity is derived from another series of rate measurements using "CrzN" plates; the intrinsic diffusivity, DN = 3.2 X 10-a cmZ sec-' at 1200 C, is found to be essentially independent of- the subnitride composition. The concentration gradient was measured in a chromium subnitride layer by the X-ray method and found to be consistent with the derived diffusivity value. TWO chromium nitrides are known to exist:' the nonstoichiometric subnitride "CrzN" and the nitride CrN. In the present work the kinetics of the formation of chromium subnitride from chromium and nitrogen have been investigated at 1100" and 1200°C. In additional experiments the relevant equilibria have been measured. The data are used to evaluate the diffusivity of nitrogen in chromium subnitride. Since chromium nitrides are often found in chromium-containing steels, the results are expected to be helpful in the interpretation of the chemical reactions between chromium steels and nitrogen. Equilibria in the Cr-N system have been determined by several investigators.2"3 The rate of nitriding of chromium was measured by Arkharov et a1 .' in ammonia in the temperature range 800" to 1200°C. The parabolic rate law was observed. Due to the undefined nitrogen activity of the ammonia atmosphere, it is dif- ficult to interpret these rate data theoretically. An additional difficulty arises from the fact that the two-layer scale consisting of CrN and "Cr2N" was formed at the temperatures below 1030°C. The rate of nitriding of technical chromium (95 pct) was measured by Zaks in nitrogen at -1 atm in the temperature range 800" to 1300°C. EXPERIMENTAL METHODS The chromium samples were reacted with Nz-HZ gas mixtures in a vertical tube furnace, wound with Pt-10 pct Rh resistance wire. The gas-tight reaction tube was of high-purity recrystallized alumina. In nitrogen solubility measurements the nitrogen content of chromium was determined by the Kjeldahl method, on samples quenched in the cold part of the furnace. The nonstoichiometry of the subnitride and the nitriding rates were measured thermogravimetrically using a sensitive (+0.1 mg) silica spring balance. For the equilibrium measurements samples of 1 g of chromium powder contained in high-purity alumina crucibles were used. In order to remove most of the oxygen and nitrogen impurities from the chromium, the samples were initially annealed in purified hydrogen until a constant weight was obtained. The chromium plates (approximate dimensions 2 by 1 by 0.08 cm) used for the rate measurements were machined from ingots obtained by arc-melting of iodine-processed chromium. According to manufacturers' specifications the purity of the chromium powder was 99.9 pct Cr and that of the iodine-processed chromium 99.99 pct Cr. Our own spectroscopic analysis of the chromium powder yielded 0.02 pct Fe, 0.05 pct Mn, 0.05 pct Si, and 0.02 pct Ti as major impurities with all the other detectable elements below 0.005 pct. The nitrogen partial pressure of the gas phase was controlled by mixing prepurified hydrogen and nitrogen with constant pressure head capillary flowmeters. Oxygen and water vapor were removed from the mixed gas by passing it through columns of platinized asbestos (450°C) and anhydrone. The gas flowed upward in the furnace with flow rates of 300 to 500 cu cm per min (25"~). Gas tightness of the furnace system was ensured by pressure checks at regular intervals. The furnace temperature was controlled electronically in the usual manner. The reported temperatures were measured with a Pt/Pt-10 pct Rh thermocouple and are estimated to be accurate within ±$C The X-ray measurements were made with a Debye-Scherrer camera and a diffractometer using chromium radiation {\Ka = 2.29092A). EQUILIBRIUM MEASUREMENTS The experimental results of the equilibrium measurements are contained in Tables I to In. Fig. 1 shows the solubility of nitrogen in solid chromium in the temperature range 1100" to 1310°C. In Figs.

Jan 1, 1968

By P. M. Robinson, M. B. Bever

THE heats of formation at 273°K of the compounds InBi, In2Bi, and TIBi2 have been determined by metal solution calorimetry with bismuth as solvent. The published information on the thermody-namic properties of these compounds is limited. The structure of the compound InBi (mp, 383°K) is tetragonal of the PbO (B10) type.1 The compounds In2Bi (mp, 362°K) and TIBi2 (mp of highest-melting composition, 486°K) are now believed to have structures of the NizIn (B8) type273 and not the A1B2 (C32) structures reported earlier.4, 5 The compounds In2Bi and TIBi2 have limited homogeneity ranges at room temperature, while the compound InBi has no detectable homogeneity range.' Samples of the compounds were prepared from 99.99 pet Bi (Mallinckrodt Chemical Works), 99.999 pet in (American Smelting and Refining Co.), and 99.99 pet Tl (Amend Drug and Chemical Co.) by melting the components in sealed, evacuated Vycor tubes. The compounds InBi and in2Bi were of the stoichiometric compositions. The compound TIBi2 contained 40 pet T1; this composition was chosen because at room temperature the alloy of stoichiometric composition does not lie within the homogeneity range.' The melts were held approximately 50°C above the liquidus for 8 hr and then quenched into iced brine. The samples were homogenized for 48 hr at temperatures 20°C below the temperature of complete solidification. Metallographic examination of sections taken from the center and the ends of the ingots did not reveal second phases or segregation . The heats of formation were determined as the difference in the heat effects on solution of a compound and of a mechanical mixture of its components added from the reference temperature of 273°K to liquid bismuth at 623°K. The details of the calori-metric procedure and method of calculation have been described elsewhere? The calorimeter was calibrated by adding bismuth at 273°K to the bismuth bath at 623°K. The calculated values of the heats of formation of the compounds, listed in Table I, are based on a value of 4.96 keal per g-atom for the difference between the heat contents of bismuth at 273" and 623oK7 No published values are available for the heats of formation of the compounds InBi and In2Bi. Hultgren et a1.7 have calculated a value of -0.50 i 0.10 keal per g-atom for the heat of formation at 423°K of the compound TIBi2 containing 40 at. pet T1 from heat-content measurements in the range from 398" to 700°K and the heats of formation of the liquid alloy. The difference between this value and the value of -0.66 * 0.01 keal per g-atom at 273°K is too large to be attributed to a difference between the heat capacities of the compound and the components over the temperature range 273o to 423oK7 However, the direct determination of the heat of formation by a calorimetric method should give a more accurate value. The heats of formation at 273°K of the compounds InBi and In2Bi lie on a straight line when plotted as a function of composition, Fig. 1. The compound In2Bi, therefore, appears to be barely stable with respect to its neighboring phases. In order for the free energy vs composition curve to be concave towards the composition axis, the entropy change on formation of In2Bi must be more positive than that on formation of InBi. As the compounds are ordered,2, 3, 8 there is no configurational entropy change on formation. The difference between the entropy changes on formation of the two compounds, therefore, is probably associated with the vibrational entropies. In view of the low heats of formation, the changes in vibrational entropy, due to changes in bond strength on formation of the two compounds, are likely to be small. Owing to the volume contractions on formation of the two compounds,5 the vibrational entropies probably decrease slightly but the decrease of the vibrational entropy of InBi is expected to be larger than that of In2Bi.

Jan 1, 1965

By Robert C. Emmett, Donald A. Dahlstrom

FOR many years gravitational classification has been employed as a basic tool in beneficiation of minerals and coal. While improvements have been made to increase efficiency and fields of application, the basic flow pattern has remained relatively unchanged in most gravitational classifiers. Feed slurry is introduced into a settling pool wherein the coarser solids settle against either an upward or horizontal fluid current, or a combination of both, and are withdrawn in a concentrated underflow stream. The finer solids below the classification point possess too low a settling velocity and thus are primarily swept out through a weir overflow by the bulk of the fluid. Because of its simplicity, efficiency, and low power and maintenance costs, gravitational classification finds a wide acceptance for separations in the range of 20 to 325 mesh.

Jan 10, 1953

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

Eighty-four quaternary titanium-base alloys from the following systems were investigated: 1. Titanium-chromium-carbon-nitrogen. 2. Titanium-chromium-carbon with copper, vanadium, molybdenum, manganese, iron, or nickel. 3. Titanium-chromium-nitrogen with vanadium, molybdenum, or nickel. The tensile properties, minimum bend radii, hardnesses, response to heat treatment and aging treatment, and phase relationships of these alloys are reported. HIS paper is the third in a series describing J- titanium-base alloys. The first paper describingdescribed titanium binary alloys, and the second contained data on a large number of titanium ternary alloys. Eighty-four heats, comprising three groups of quaternary titanium-base alloys, are described in this paper as follows: 1. Titanium-chromium-carbon-nitrogen alloys. 2. Titanium-chromium-carbon alloys containing copper, vanadium, molybdenum, manganese, iron, or nickel. 3. Titanium-chromium-nitrogen alloys containing vanadium, molybdenum, or nickel. The methods of preparing, fabricating, and testing the alloys are described in the paper Binary Titanium Alloys. Quaternary Titanium - Chromiurn - Carbon -Nitrogen Alloys The properties of titanium-chromium-nitrogen and titanium-chromium-carbon ternary alloys have been described in the paper Ternary Alloys of Titanium. Because small amounts of nitrogen and carbon both appear to be somewhat beneficial, these additions have been investigated fairly completely in quaternary alloys containing chromium at the following levels of composition: 2.5, 3.5, and 5.0 pct chromium 0.25 and 0.5 pct carbon 0.1 and 0.2 pct nitrogen Mechanical Properties: The mechanical properties of these alloys are listed in table I. Fig. 1 and 2 show graphically a comparison of the tensile properties and hardnesses of quaternary alloys with those of the titanium-chromium binary alloys. Fig. 1 shows the comparison at 0.25 pct carbon, whereas fig. 2 shows the comparison at 0.5 pct carbon. It is concluded from these data that 0.25 pct carbon and 0.1 pct nitrogen are desirable additions to the 5 pct chromium-titanium base. It is further concluded that most of this improvement is produced by the nitrogen and that carbon is either harmless or mildly beneficial, at least up to 0.25 pct. Structure and Transformation Range: The effects of carbon and nitrogen on the transformation range of the titanium-chromium alloys were determined as part of the routine investigation. Additions of 0.25 pct carbon and 0.1 pct nitrogen had no appreciable effect upon the transformation range. However, the addition of 0.25 pct carbon and 0.2 pct nitrogen definitely raised the beta solvus temperature, as shown by fig. 3.

Jan 1, 1951

By H. L. Marcus, P. W. Palmberg

As can be seen from the phase diagram A1-W1 the equilibrium solubility of tungsten in aluminum is practically nil at room temperature. By quenching from the liquid state (50,000°C per sec), Varic, Burov, and Kolesnicenko2 obtained A1-W solid solutions up to 0.15 at. pct W. The quenched alloys were in the form of foils, 0.2 to 0.3 mm thick. Considering the results of Duwez and Willens,3 it is obvious that this thickness, which makes impossible a sufficiently rapid quenching, was the main reason for the relatively low content of tungsten dissolved in aluminum found by Varic.2 he present note shows that the metastable solubility of tungsten in aluminum can be appreciably extended in aluminum-rich A1-W alloys. The quenching technique and the procedure employed for the preparation of the alloys have been described previously.475 The resulting quenched flakes varied in thickness from 1 to 20 µm from experiment to experiment. However, the measurements of the lattice parameters were carried out only with flakes thinner than 5 µm. The areas of quenched flakes were between 0.1 and 15 mm2. The quenched flakes were placed into a 0.3-mm glass capillary tube which was then mounted in a 114.6-mm-diam Debye-Scherrer camera. Straumanis asymmetric film position and nickel-filtered CuKa radiation were used. The lattice spacings were computed taking X(CuKa1) = 1.54050A for resolved and ?(CuKa) = 1.54178A for unresolved doublets. All specimens were rotated at room temperature, 26" +2°C. The lattice parameters were estimated from extrapolation against the Nelson-Riley function. It was estimated that the error in the lattice parameter of the measurements on a single film lies within +0.0004A for lower and about +0.001A for higher concentrations of tungsten. The lattice parameters of the metastable solid solutions A1-W are plotted vs the concentration of tungsten in Fig. 1 together with the parameters measured by previous investigators.' Each point of the present measurements represents a determination of the lattice spacing on different quenched flakes, for a given concentration of tungsten. With experimental accuracy, the lattice parameters of the metastable solid solutions fall on the straight line passing through the already known data.' As estimated from the uncertainties in the lattice spacings of the solid solutions, the alloys were homogeneous within 0.1 at. pct W. The solubility of tungsten in aluminum-rich A1-W solid solutions obtained by a very rapid quenching technique is increased to about 0.95 at. pct W. This value is 6 times greater than the amount known up to now. -he lattice parameters of the resultant aluminum solid solutions with higher concentrations of tungsten than 0.95 at. pct W did not remain constant AUGER electron spectroscopy has been used to clarify the role of impurities in the embrittlement of AISI 3340 steel. Analysis of fracture surfaces has shown that the embrittled condition is correlated with appreciable antimony segregation at grain boundaries. The low temperature (400" to 600°C) temper embrittlement of low alloy steels containing various combinations of Cr, Ni, Sb, Mn, P, Sn, and As has been examined extensively for many years. General reviews of the area have been made by McMahon1 in 1968, LOW' in 1959, woodfine3 in 1953, and Holloman4 in 1946. Recent work by Low, Stein, Turkalo, and LaForce5 has done much in separating the alloy and

Jan 1, 1970

By E. Gregory, A. Coucoulas

Carbm dioxide, which exists metastably as a constantly subliming molecular solid in a normal room-temperature environment, has been shown to exhibit many microstructural features which are similar to those observed in metals and ceramics at temperatures approaching their melting points. An examinution has been made of some of the factors affecting a brittleness condition known as "smzdiness" which occurs in solid carbon dioxide. It has been shown to be highly dependent on manufacturing and storage conditions and is thought to be a marked intergranu-lay brittleness which results from a combination of excessive grain growth and a concentration of gas-filled pores at the grain boundaries. In the course of an investigation carried out to explain certain physical and mechanical properties of solid carbon dioxide, observations were made of the microstructure and fragmentation of samples after fabrication and storage under varying conditions. Many similarities between the structures of solid carbon dioxide observed under ambient conditions and those existing in metal and ceramic systems at temperatures approaching their melting points have been observed. There are, however, important differences between solid carbon dioxide and the common metallic and ionic solids which result primarily from the differences in the nature of the bonding forces. Despite these differences, the relative ease with which certain microscopic observations can be carried out, may make solid carbon dioxide a useful material model for the physical metallurgist and the ceramist. It could also prove a valuable material for educational purposes where it is required to illustrate grain phenomena which normally can only be seen with the aid of a high-temperature microscope, and after prolonged chemical or thermal etching.

Jan 1, 1963

By D. Turnbull, R. E. Cech

FISHER, Hollomon, and Turnbull have developed a theory for the nucleation of martensite. They first tested the theory on Fe-C alloys and low alloy steels. The major factor influencing nucleation of martensite was considered to be statistical composition fluctuations occurring in small regions at high temperature and frozen-in on quenching. These local regions of varying size and composition serve as nucleation centers. They become supercritical, one by one, as temperature is progressively lowered, resulting in temperature-dependent or athermal transformation. Fisher next applied nucleation theory to substi-tutional solid solution alloys. Detailed predictions were made for Fe-Ni alloys because of the availability of free energy data on this system. It was shown that composition fluctuations that were significant energy-wise did not occur, and nucleation frequencies could be calculated from average properties of the system. Nucleation was predicted to occur as time-dependent and having the functional relationship to give a C curve of nucleation frequency vs temperature. The analysis further predicted that the nucleation frequency was extremely sensitive to composition. Experimentally, it would be found that the transformation in some compositions is so slow that measurable amounts will not form in a reasonable length of time. With other compositions, only slightly different, the nucleation frequency becomes so great that the material becomes transformed while still distant in temperature from the maximum nucleation frequency. On quenching an alloy of such composition, the observed transformation kinetics would be similar to those found in Fe-C alloys. Cech and Hollomon repeated experiments of Kurdjumov n which the kinetics of transformation were similar to those predicted by Fisher for Fe-Ni alloys. The alloy studied in this investigation contained 73.3 pct Fe, 23.0 pct Ni, and 3.7 pct Mn. Fisher,' using an idealized model for the extent of transformation as a function of the number of martensite crystals per grain of parent phase, derived nucleation frequencies from the transformation curves of Cech and Hollomon. Complicating influences such as coupling effects between grains in the polycrystalline specimens were neglected. Nevertheless, excellent agreement was found between the theoretically and experimentally derived nucleation frequencies. These experiments, however, could not provide a critical test of the theory. Experimental nucleation frequencies could vary widely from those calculated, depending upon the extent of deviation from ideal partitioning and the extent of coupling effects. Further, since the compositions of material theoretically analyzed and experimentally determined were different, the free energy changes involved in the experimental work could only be estimated. Also, the effect of heterogeneities on the transformation kinetics was not considered. For these reasons, it was decided that experiments designed to test the validity of the Fisher analysis must be conducted on binary Fe-Ni alloys, which were the ones considered theoretically by Fisher. The martensite transformation in Fe-Ni alloys has been the subject of considerable study. Machlin and Cohen have shown that transformation proceeds in a manner quite unlike that in any other ferrous alloy system. They found that single crystals would transform to a large extent in a single burst. In large grain polycrystalline specimens, frequently more than one grain and sometimes the whole specimen would transform at the same instant in this manner. Results on filings indicated that different particles would undergo the burst transformation at widely different temperatures. These results support the conclusion that the transformation behavior could not be described by a single nucleation frequency as would be the case if the nucleation were homogeneous. It appeared that further work was necessary to define the factors responsible for burst-type transformation, so that the conditions could be altered to favor homogeneous nucleation of martensite if such could be accomplished. This report summarizes the results of some experiments conducted with powdered Fe-Ni alloys for this purpose and the re-

Jan 1, 1957

By Hertha R. Freche

The diffusion of magnesium and silicon from the core into the high-purity coating of Alclad sheet is important commercially, and led to the use of a duplex product for the study of diffusion by means of spectro-graphic analysis of successive layers. It has been found that in the duplex materials the diffusion of magncsium from an undersaturated aluminum-magnesium alloy into its high-purity aluminum coating is approximately of the same order of magnitude as the diffusion of silicon from a saturated aluminum-silicon alloy into its high-purity aluminum coating. However, if magnesium and silicon are both present in the alloy in the ratio of Mg2Si, they appear to diffuse in the approximate ratio of this compound. Finally, if the alloy contains silicon in excess of the amount required by magnesium silicide, the amount of diffused silicon in the high-purity aluminum coating will also be in excess. The interdiffusion of metals in the solid state is of both scientific and technical interest, because it is helpful in the study of the alloy structure and in the solution of problems pertaining to the strength and surface condition of the fabricated product. W. C. Roberts-Austenlt carried out the first quantitative determination of the coefficient of diffusion of gold into lead. This classical experiment was followed by a series of investigations on the diffusion of metals and nonmetals in iron and steel and in nonferrous metals and alloys. Recently the diffusion of copper in coated strong aluminum alloys was investigated by A. Burkhardt2. This appeared to be the first published investigation on the diffusion of metals into aluminum. The present investigation was the direct result of a technical question in connection with alloy fabrication and is a summary of some preliminary work pertaining to the diffusion of magnesium and silicon into aluminum. The results necessarily will be subject to some variations, since this is the first attempt to evaluate the coefficients of diffusion of magnesium and silicon into aluminum according to this method of procedure. This

Jan 1, 1936

By Clarence E. Sims, Donald W. Williams, George A. Moore

INTRODUCTION DURING the past several years the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture and the ductility values often can be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Some hundreds of previous investigations, largely qualitative in nature, have established beyond reasonable doubt that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, the Steel Founders' Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-ductility effects and porosity. In order that these investigations might proceed on a quantitative basis, hydrogen analyses of a precision considerably higher than any previously reported in the literature were necessary. The method chosen was selected entirely on the basis that it had the highest probability of freedom from uncontrollable errors and will be described in detail in another publication.1 Briefly, the method used consisted of the hot extraction of solid pieces of steel weighing from 45 to 50 g in a highly evacuated quartz tube maintained at 1050°C (1925°F) for a period 0f approximately 40 hr. The greatest precautions were taken to eliminate blanks and insure a sound gas-collection system. Vacuum and temperature conditions were maintained automatically. Mercury-filled risers were used for the introduction of samples in order that the system could be degassed thoroughly in

Jan 1, 1948