Search Documents

By Gerald Edmunds

THE liquidus line on the phase diagram for temperature versus composition of a binary alloy system, representing the boundary between the homogeneous melt and the heterogeneous melt plus solid, besides showing the minimum casting temperature, is useful in determining eutectic compositions and the presence of phase changes such as peritectic transformations and intermetallic compound formation. The liquidus often is determined by the cooling curves of thermal analysis, but supercooling frequently occurs, so that the temperature values are low. An alternative method, the one employed here, consists of determining the com- position of samples of the melts from heterogeneous alloys that are at equilibrium. With meticulous attention to fundamentals, this method is capable of yielding values limited in precision only by the temperature control and measurement and analyses. APPARATUS By starting, on the one hand, with a supersaturated solution and allowing the excess solute to precipitate, and on the other hand with an undersaturated solution and allowing more of the solute to be dissolved, both processes being carried out at the same temperature, equilibrium may be said to have been approached from both directions; that is, from above and from below. If the analyses show the solutions to contain the same fraction of solute when equilibrium has been approached from above and from below, one is assured that equilibrium has been reached in both determinations. In order to carry out such determinations, it is necessary to have equipment for obtaining and maintaining the proper temperatures; for holding the melt, measuring its temperature, and stirring, sampling and analyzing it. The present work required temperatures from 420° to 900°C. The equipment consisted of: A furnace, which was a vertical alundum tube, 1 ¾ in. diameter inside and 18 in. long, wound with Nichrome resistance wire, surrounded by a 3-in. i.d. alundum tube wound for 5 in. of length near each end, for compensation of end losses. This muffle was contained in an iron shell with Transite end plates, the intervening space being packed with Sil-O-Cel. The outside dimensions of the furnace were 12 in. in diameter by 18 ½ in. in height. Heating current was supplied by three independent variable-voltage transformers (Variac), one connected to each end compensator winding and manually controlled, and one connected to the main winding through a series resistance of 5 ohms. This resistance was short-circuited for

Jan 1, 1944

By R. A. Vandermeer, Paul Gordon

On the basis of a unified concept, theoretical erPressions for grain boundary migration in recrys-tallization are derzved for impurity-controlled and impurity-independent migration. The expression in the former case is analogous to that Previously derived by Lucke and Detert, and in the latter is shown to be equivalent to that usually obtained on the basis of absolute reaction rate theory. The equations are tested with quantitative experimental data for boundary migration obtained for the recrystallization of poly crystalline zone-refined alumimnz and for binary "alloys" of this aluminum with 0.00021, 0.00043, 0.0017, 0.0034, 0.0068, 0.0124, and 0.0256 at. pct Cu, respectively. All the essential characteristics of the e@erimentally determined boundary migration rates check both qualitatively ard quantitatively with the predictions of the theoretical equations. THE rates of transformations are customarily analyzed phenomenologically in terms of the two component rates—N, the rate of nucleation and, G, the rate of growth of the nuclei. The scientific aim of both theory and experiment is to describe the fundamental atomic phemmena involved in these two component processes with the hope that parameters calculated from theoretical equations will check those found experimentally. In solid state transformations, the theoretical and experimental problems are both generally of almost prohibitive complexity, for in addition to changes in composition and in such properties as density which may accompany transformations in amorphous, nonrigid materials, transformations in crystalline substances also involve structural changes, crystal reorientations, and the development of stresses. In studying such transformations it thus becomes; highly desirable, if not essential, to focus on a transformation and a set of conditions which minimize the number of active variables. This principle has been applied with considerable success by Cohen and his associates' in their evaluation of nucleation theories using the martensite transformation as the basis of study. A similar possibility exists for the evaluation of growth theories by the use of recrystallization after cold-deforming. If an unalloyed metal is employed as the subject of investigation, the recrystallization transformation involves basically only a change in strain-conditions and orientations. In spite of this possible simplilfication, however, until recently little quantitative success has attended attempts to correlate recrystal1ization parameters measured experimentally with those calculated theoretically. It seems highly probable that this lack of success may be attributed, both in the experimental and theoretical treatments, to one or more of the following factors: a) conditions have usually been studied under which apparently* both nucleation and growth are active;

Jan 1, 1962

By Hiram B. Woon

Uranium ore deposits in the Lisbon Valley area are in an arcuate belt, 15 miles long by one-half-mile wide, on the southwest flank of the Lisbon Valley anticline. They range in size from 500 to 1,500,000 tons and by mid-1965 had yielded 6,147,000 tons containing 48,530,000 pounds of U3O8. Ore bodies average 6 feet thick, are tabular, amoeba-shaped masses, concordant to the bedding, and are in the thickest, lowest sandstone unit of the Moss Back Member of the Chinle Formation of Triassic age. The host rock is predominantly a fluviatile, calcareous, fine-grained to conglomeratic sandstone. Uraninite, the principal ore mineral, fills the pores in the sandstone and partly replaces sand grains and fossil wood fragments. During Late Permian and Early Triassic time pre-Chinle Formations were arched to form the ancestral Permian anticline. Moss Back streams truncated Moenkopi and Cutler beds which capped the ancestral anticline and then covered it with fluviatile elastics, which were subsequently covered by thousands of feet of Triassic, Jurassic, and Cretaceous sediments. Uranium, probably derived from the Chinle Formation by diagenetic processes, was transported in connate ground waters, was moved by compaction or hydrostatic forces, and was deposited under reducing conditions. Uranium was emplaced around the crest of the ancestral anticline, prior to the Laramide orogeny. During the orogeny, the Tertiary-Lisbon valley anticline was super induced on the Permian anticline and, penecontemporaneous with uplift, was faulted parallel to its longitudinal axis. The Big Indian ore belt on the southwest flank footwall block was elevated to approximately its present position, and the northeast flank hanging wall block was elevated only slightly. An extension of the Big Indian ore belt around the northeast flank of the ancestral Permian anticline may exist in the Moss Back sandstone in the downthrown block northeast of the Lisbon Valley fault.

Jan 1, 1968

By E. C. Dominguez, H. B. Scharf

The Sparrows Point plant of Bethlehem Steel Co., southeast of Baltimore, is the largest Bethlehem plant, with an annual rated capacity of 6.2 million ingot tons. There is considerable diversity of product, but a high percentage is sheet, tin plate, galvanized sheets, and rod and wire. The large amount of light-weight end product requires a number of pickling installations that necessarily consume large quantities of sulfuric acid. In the coking operations sulfuric acid is also consumed in recovery of ammonia as ammonium sulfate and in treatment of recovered light oil derivatives. Total sulfuric acid consumption in the plant is currently approaching 10,000 tons per month, of which 55 to 60 pct is required for pickling. In 1951 the acute sulfur shortage caused grave concern as to future sulfuric acid supply for the Sparrows Point plant. Raw materials for acid making were already at hand in the form of hydrogen sulfide and pyrites sufficient to produce nearly half the sulfuric acid required at that time. It was also known that the Bethlehem mining activities would produce additional pyrites in the future. Late in 1951 Bethlehem management decided to build a 250-ton sulfuric acid plant at Sparrows Point to utilize these raw materials. The plant was built and put in operation in May 1953. The steel plant has expanded considerably since 1951, and it is now necessary to operate the acid plant far over rated capacity in order to supply plant demand. Production of acid in 1954 amounted to 93,000 tons.

May 1, 1956

By Walter E. Heinrichs

Before covering the separate methods used in mining geophysics, it may be well to mention some current basic geophysical prospecting concepts. As in most fields, a better understanding and means of studying these fundamentals usually provides the more common improvements, rather than new principles being discovered. The relative detail and complexity of most mining geology often results in the use of geophysics in problems it cannot solve. On the other hand, suitable applications are often ignored or left unrecognized. To minimize this, it is important to consider geophysics as a phase, or additional tool, in geological or exploration engineering.

Aug 1, 1956

By Stanley M. Jarrett

Operating one of the world's largest underground copper mines, Braden Copper Co. has been able to reduce its total accident frequency rate per million manhours by 84 pct, from 27.4 pct in 1945 to 4.45 pct for the first ten months of 1958. It has also won the Inter-American Safety Trophy for 12 consecutive years. The record may seem to indicate a secret formula, but there is none. The results stem only from hard work, and more and more of it.

Jan 11, 1959

By R. G. Aspden

The cold rolling and annealing textures were studied for 3 pct Si-Fe grains initially (001) [hkl]. A concentration of (001) [loo] primaries were observed only in the annealing textures of crystals initially having [loo] within 8 deg of the rolling direction. Eke annealing textures of the (001) [I101 cold rolling textures were sensitive to the initial orientation of the grains. Single crystal data were used to explain the formation of (001) [loo] in poly-crystalline malerial. CUBE texture formation in 3 pet Si-Fe sheet occurs during the final high temperature anneal. Its formation is dependent on the proper distribution of (001) plane primaries with reference to the rolling direction&apos; and on the growth of these primaries by secondary recrystallization. The selective driving force for these primaries with (001) within 7 deg of rolling plane is derived from the difference in surface energy between the annealing atmosphere and the crystallographic planes exposed at the surface of the sheet.&apos;-= The alignment of [loo] directions of (001) secondaries with the rolling direction is required for optimum magnetic characteristics7 and is dependent on processing.&apos; A high degree of alignment has been observed when the final cold rolled texture has a strong (111) [ll2] type component3 and the normal grain growth texture prior to secondary recrystallization has components with a [loo] parallel to the rolling direction and planes from (001) to (110) parallel to the rolling plane.1,3,8,9 Generally, this (001) component is much weaker than the (110) component. The growth rate of (001) plane primaries to secondaries has been found to be independent of the orientation of the primaries with reference to the rolling direction, i.e., the secondaries have the same degree of alignment of [loo] directions with the rolling direction as the (001) primaries.&apos; Hence, the rolling and annealing textures of individual grains or single crystals are of interest in understanding the development of the (001) [loo] secondary recrystallization texture. (001) components have been observed in the annealing textures of cold rolled grains initially having a [loo] parallel to the rolling direction and an (001) rotated up to 30 deg from the rolling plane. Crystals initially near the (001) [loo] orientation when rolled under the influence of constraints imposed by neighboring grains form deformation bands and ro- tate in both directions toward (001) <110>.10,11 Deformation bands have been reported also for crystals initially with an (001) within 1 deg of the rolling plane and a [loo] within 1 deg of the rolling direction when rolled as a free single crystal.12 These crystals have weak recrystallization textures and contain near an (001) [loo] component.10-12 When near (001) [loo] crystals are rolled as free single crystals no deformation bands form and the crystals rotate by a single rotation toward (001) [110]. Recrystallization after a 70 pct cold reduction yielded near an (001) [loo] component13 and after a 90 pct cold reduction an (001) [I201 component." Crystals initially near (210) [001] had a texture after a reduction of 70 and 84 pct which was similar to the (111) [li2] but rotated 10 to 15 deg in the transverse direction. These crystals recrystallize to (210) [OOl] or (410) [001] and contain an (001) [loo] component.10,13 An (001) component has not been detected in the normal grain growth textures of other single crystals. Crystals initially having orientations between (110) [001] and (111) [ll2] have a cold rolled texture of principally (111) [ll2] .10>16 Other crystals with a [I101 parallel to the cross direction rotate to (111) [112] and/or (001) [110] stable end orientations. Crystals initially having from (001) [110] to (111) [lie] retain this orientation after cold rolling.15 The cold rolled textures having [I101 directions parallel to the rolling direction had components in the annealing textures related to the deformation textures by 25 to 30 deg rotations about common (1 10) poles. Cold rolled textures of the (111) (112) type recrys-tallized to (120) [001] or (110) [00l]. The purpose of the present work was to further the understanding of the alignment of [loo] directions of (001) secondaries with the rolling direction. The cold rolling and annealing textures of grains initially (001) [hkl] were studied. These data were applied to the formation of (001) [loo] by secondary recrystallization. PROCEDURES AND EXPERIMENTAL TECHNIQUES The (001) poles near the sheet normal and rolling direction are given in Fig. 1 for the 10 grains studied. Each of these grains was located in the center of a polycrystalline specimen approximately 25 mm wide and 50 mm long. The lower case lettered grains, a through dl were about 1.2 mm in diam and near the (001) [loo] orientation. Specimens containing these grains were from a commercial 3 pct Si-Fe alloy with the principle orientation of (110) [001] as obtained by impurity inhibition of growth with manganese sulfide inclusions.17,18 Upper case lettered grains, A through F, were about 6 mm in diam and had (001) planes near the rolling plane and [hkl] di-

Jan 1, 1963

By W. E. Lamont, G. V. Sullivan

As part of its program to conserve domestic mineral resources through advancing mineral resources technology, the US Department of the Interior, Bureau of Mines, conducted investigations to determine the feasibility of recovering high-grade barite concentrates, suitable for use as well-drilling mud, from current and old waste pond materials and materials bypassed in present mining operations. Flotation studies of waste pond samples from Missouri and Nevada yielded barite concentrates containing over 95% Bas04 with recoveries of 86% and 96%, respectively, of the barite in the flotation feed. Flotation studies of a hard-rock sample from Georgia, currently bypassed in mining, yielded a barite concentrate containing 97% Bas04 with an attendant recovery of97% of the barite.

Jan 1, 1982

By Leonard Grimshaw

THE idea of bonding two dissimilar ferrous metals, and making use of both, is an old one. Tips have been brazed onto tool shanks for many years. The bonding of larger pieces to form whole bars and sheets has also been accomplished, but has received little attention in the technical literature, although a number of patents have been issued covering various methods for its accomplishment. There are three main motives behind the manufacture of composite steels. One is that the physical properties of one steel may supplement those of another; a useful, but at the same time, hard, brittle steel may be backed by a soft ductile one, or a stainless steel may be backed by a steel possessing greater strength. Another motive is direct lowering of cost; an expensive steel may be backed by a less expensive one, bringing down the cost of the piece as a whole. The third motive is an indirect lowering of cost, as when a useful steel is backed by a steel that is easier to machine, so that machining cost on a finished product is lowered considerably. Often more than one of these motives lead to a decision to use a com-posite steel.

Jan 1, 1936

By H. R. Stahl

THE disseminated lead district of Southeast Missouri lies 70 miles south of St. Louis. The only metal of economic importance in the ore is lead, but minor amounts occur of iron, zinc, copper, cobalt, nickel, silver and cadmium. These minor metals, as might be expected, tend to concentrate in both the flotation and table middlings. In the past, some zinc has been recovered by differential flotation. The silver and cadmium tend to associate with the zinc, and some recovery is made of these two metals at the smelter. The lead occurs as galena, or lead sulphide. The minor metals are also present as sulphides. The presence of oxidized lead is suspected, but has not been definitely proved. The gangue is chiefly dolomitic limestone, with small amounts of sandstone and shaly glauconitic and chloritic minerals. The ore contains about 3.25 per cent lead, occurring as galena disseminated through the gangue. Some of the galena is very finely disseminated, and the mineral in the gravity tailings, or chat, is seldom or never in the free state. The method of treatment of the ore has been evolved over a period of 75 years; hence probably is not far from correct. The milling processes have tended toward simplification during the past 15 years, but recoveries have never been sacrificed for the sake of simplicity. In many cases, simplification of flowsheets has led to better recoveries and operating economies. A simplified flowsheet is shown in Fig. I. The St. Joseph Lead Co. operates four mills in the Flat River district, with a normal total capacity of about 21,000 tons per day, divided as follows: Federal mill, 11,000 tons; Leadwood mill, 4500 tons; Desloge mill, 3400 tons and Bonne Terre mill 2400 tons. The methods of concentration used at these plants are similar in principle; they differ mainly in details and in the type and size of the equipment used. The process of concentration may be divided into five main steps; i.e., dry crushing, wet grinding, classification with its attendant desliming, tabling and flotation. A brief description of these processes will be given, noting important differences in the various plants, and also noting the more important changes or developments of the past few years. DRY CRUSHING The run-of-mine ore is hoisted in skips, the capacity of these skips ranging from 2 ¾ tons to 8 ¼ tons. At the Desloge plant, the ore is hoisted in 2-ton mine cars on self-dumping cages. All ore is hoisted at shafts adjacent to the various crushing plants, no ore being transported on the surface. Primary breaking at all the mills is accomplished with 9E Telsmith breakers. Preliminary screening is provided ahead of most of these crushers, either by station-

Jan 1, 1943

By S. J. Matas, R. F. Hehemann

The existence of two distinct forms of bainite—upper and lower bainite—in hypoeutectoid steels is confirmed by a systematic study of the structure of the product resulting from this mode of austenite decomposition. The transition between these two forms occurs at about 650° F regardless of the alloy content of the steel and their structural differences can be interpreted in terms of the kinetics of carbide precipitation from supersaturated ferrite. In the past few years, a renewed interest has been displayed in the kinetics and mechanism of the bainite reaction in steels. Several rather divergent models for the transformation mechanism have evolved from these studies,&apos;-&apos; however, it is difficult to evaluate these models critically on the basis of the existing experimental data. In particular, a more detailed knowledge of the structure of bainite should be helpful in providing a framework for the construction of an appropriate model. Metallographic studies7-l4 have led to a recognition of at least two distinct forms of bainite—frequently termed upper and lower bainite. Although the morphology of bainite changes with reaction tem- perature, there appears to be a relatively sharp transition between the two forms. This occurs in a narrow temperature range near 650° F. Transformation at temperatures below about 650° F results in the presence within the bainite of small plates of carbides oriented at an angle of 60 deg with respect to the direction of growth of the plate, while at higher temperatures carbides are oriented parallel to the growth direction. There is no generally accepted view regarding the significance of this structural transition. Some authors feel that carbides precipitate from austenite at all reaction temperatures1&apos; while others claim, at least for low-temperature bainite, that carbides precipitate from supersaturated ferrite.14.15 It was recognized many years ago that the nature of the carbide in bainite depends on the reaction temperature. The carbide hase in upper bainite is unmistakenly cementite.16-19 The exact nature of the carbide in low-temperature bainite is less certain. Magnetic measurements of lower bainite reveal no cementite Curie point21&apos;22 and dilatometric studiesz0 produce total expansions which are larger than those predicted on the basis of a ferrite-plus cementite structure. These effects have been attributed to the

Jan 1, 1962

By Donald W. Gentry, John F. Abel

This paper presents some of the results of a rock mechanics instrumentation program designed for, and implemented at. longwall panel 4N at the York Canyon Mine near Raton, New Mexico. The objective of this particular instrumentation program was to determine the response of the rock mass to longwall mining of a thick coal seam utilizing shield-type supports. Measurements were made in the rock along the ground surface, above the coal seam, in the coal seam, and immediately below the coal seam. Longwall test panel 4N had a total developed length of 762 m (2500 ft) and a face width of 168 m (550 ft), [Fig. 1]. The seam mining height in the panel area was approximately 3 m (10 ft). The average depth of overburden above the panel is 107 m (350 ft) although it ranges from 73-134 m (240-440 ft). Roof support at the face was provided by 116 Hemscheidt 320 HSL shields. These shield-type supports weigh 11.4 metric tons each.

Jan 1, 1979

By W. B. Devereux

The special mriditions under which gold occurs in the Potsdam formation of the Black Hills prew~lt features worthy of a more systematic pesentation than they have heretofore received. The notes

Jan 1, 1882

By P. H. Dudley

IN giving a brief account of the experiments in progress to inquire into some of the facts in regard to "railway resistances," recently commenced upon the Lake Shore and Michigan Southern Railway, with the dynagraph (which is essentially an instrument recording upon paper the force required to draw a train, at all speeds, marking the time in short intervals, so that the force absorbed due to any

Jan 1, 1876

By E. H. Dix

During an investigation of high-strength manganese bronze by til Engineering Division of the Air Service, at McCook Field, Dayton, Ohio, particles of a "blue constituent" were noted in the microstructure of most of the bronzes examined. The constitution of the simple copper-zinc base alloy is still a matter of dispute in spite of the fact that the copper-zinc series is one of the oldest industrially important groups of alloys, and has received thc carly co~l+itlcl-ntio11 of scirntific rcsc:trch. Thc diagram, according to the rnost rcrent \vork.&apos; IS shown in Fig. 1. The disputed questions involve the tcrmi~r:~tiorl of the beta field and the lint at 470&apos; C. The parliest expc~imc>ntcr, Rol)erts--~1~11stcri, detectrd an arrest in some of his cooling curves :it approximately this temperature and ascribed them to the formation of a cutectic; it has since been proved that there arc no eutectics in this series. Shepherd? was unable to detect any thermal arrests at this temperature, his. diagram was essentially as shown in Fig. 1, except that the line at 470" (&apos;. was omitted and the beta phase carried down to normal temperature. 1,:ttcr. carpenter and Edwards, by a very painstaking research, definitely established the authenticity of the line but attributed it to the breakdown of the BETA constituent into a cutectoid of alpha and gamma. microscopic evidence of the formation of the cutectoid is doubtful and it seems more likely to he due to an allo-tropic change in the beta constituent as shown by Fig. 1. At least for practical purpose?, it is more convenient to think of the structure of a 60-40 brass as a mixture of alpha and beta prime crystals rather thin alpha plus an unresoluble eutectoid of "apparent beta" as it has often been called. * Chief, Metals branch, Engineering Division, Air Service. 1 0. F. Hudson: Jnl. Inst. of hlvtals (1913) 12, 2 E. S. Shepherd: Jnl. Phys Chrm. (10141 8, 421. H. C. H. Carpenter and O. A. Edwards: Jnl, Inst. of Metals (1911) 5, 127.

Jan 1, 1923

Jan 1, 1931

By Lawrence K. Jetter, Robert F. Mehl

SOME advances have been made recently in the theory of the kinetics of precipitation from metallic solid solution despite the complexities of the problem, but there is surprisingly little quantitative information available on rates of precipitation with which to test present theory or upon which to build new theory.‡ Attempts to measure rates of precipitation have been beset with difficulties which originate both in the anomalies that attend the changes in the properties selected for measurement, as, for example, in electrical conductivity or mechanical properties, and also in the complexities in the structural changes in some systems, as in the aluminum-copper system. If the functional relationship between the quantity of precipitate and the value of the selected property is uncertain, measurements of that property are obviously of uncertain utility in determining absolute rates of precipitation. If the precipitating system passes through one or more transition stages, the interpretation of measured rates lacks definiteness; in such cases, it is necessary to measure the rate of reaction in each separate stage, if the rate measurements are to have any significance from the kinetic point of view.* These difficulties cannot be wholly avoided, for at least in some measure they are characteristic of the process of precipitation from solid solution, but they can be minimized both by the selection of a simple system and by the use of a method of measurement relatively free from anomalous behavior. The present paper reports dilatometric measurements on the rate of precipitation of silicon from the aluminum-rich solid solution in the aluminum-silicon system-a study that approaches the desiderata of simplicity. The aluminum-silicon system offers advantages from these points of view: there are no known anomalies in the property changes accompanying precipitation; 2.3,4 there are no known transition stages; the precipitate is an element, not a compound, and both matrix and precipitate are cubic, and while the structures are not identical (the solid solution is face-centered cubic and the precipitate is diamond cubic), the system at least approaches the ideal case of a crystal precipitating from a matrix of the same crystal type-the ideal case which Becker5 assumed in treating the precipitation process theoretically. The dilatometric method, while not free from disturbing effects, as the subsequent dis-

Jan 1, 1942

By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InAs and GaAs were measured over the temperature range 400°K to temperatures above the melting points using a di-phenyl ether drop calorimeter. Smoothed values of the thermal properties have been derived and tabulated at even temperature interuals . The heats of fusion of InAs and GaAs were determined as, respectively, 8790 ± 200 and 12,590 ± 300 cal per g-atom at the respective melting points of 1210º ± and 1513º ± 1°K, yielding entropies of fusion of 7.26 * 0.16 and 8.32 ± 0.20 cal perºK per g-atom, respectively. A general discussion of the thermal properties of III-V com-pounds is given. THE low-temperature heat capacities of InAs and GaAs have been determined by Piesbergen.1Using a dynamic temperature modulation technique, Miller2 has determined the heat capacities of the compounds as well as GaSb and Ge between room temperature and 650°K; however, it has been observed that values determined by drop calorimetry for GaSb3 and for germanium4 are consistently about 5 pct lower than Miller&apos;s results. Cox and Pool10 report values for the heat content of InAs and GaAs and the heat of fusion of InAs. No value for the heat of fusion of GaAs appears to have been previously reported. This paper reports results of high-temperature heat content investigations of InAs and GaAs measured in the range 400" to above 1500°K employing a diphenyl ether drop calorimeter. These results, together with our previous results on III-Sb compounds3 as well as heat-content measurements5 of solid InP and Gap, are used in a general discussion of these compounds. EXPERIMENTAL PROCEDURES High-purity samples of the compounds, stoichio-metric to ±0.1 at. pct, were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories. The sample preparation, description of the calorimeter, and details of the heat content measurement have been previously described.3 Samples were sealed in evacuated silica capsules and suspended by a Pt-Rh wire in a Pt-wound vertical tube furnace, heated to temperature

Jan 1, 1970

By Reed W. Hyde

Some information has been published on the sulphur dioxide concentration of gases from D wight-Lloyd machines sintering lead ores but most of this relates to the customary practice in which the charge is relatively high in lead and is sintered in two passes Over the machine. It is thought, therefore, that the following observations on sintering in one pass a low-lead, low-sulphur charge may be of interest. The data were obtained in sintering lead sulphide notation concentrates mixed with minus 20.mesh oxide ore, the mixture carrying 16,8 per cent Pb and 5.3 per cent S. No returns were used because of the limited amount of sulphur available as fuel, but the mixture pelletized readily. to make a satisfactorily permeable bed on the sintering machine. As there was a possibility that the SO z might be utilized, a series of runs was made to determine the concentration ofSO2 in the gases at different points along the wind box, and the effect on this concentration of changes in the wind-box vacuum. Several runs each were made with vacuums (as measured in inches of water at the wind box) of (1 2 to 1 in., (&apos;1 4 to 3% in. and (3) 6 to 5% in. The averages of the determinations from each series are platted On the graph (Fig, 1). The vertical scale shows the percentage by volume of SOz (as determined by the Reich method), and the horizontal scale shows the time e~pressed as percentage of the total sintering time. Sintering was considered to be complete when no SOz could be detected in the gases. In all cases the depth of bed was 4 1/2 in. and the weight of dry charge per square foot of hearth area was 45.2 lb. Other data are given in the table. The volume of gases corresponding to the several points along the wind box at which SO2 determinations were made could not be measured, but has been calculated from the SO2 Content and sulphur elimination on the assumption that the volume is uniform throughout the sintering period. This is not strictly true, as with a given vacuum the volume usually will drop slightly toward the middle of the period and increase toward the end. However, this made is a reasonable approximation. several interesting features are brought out by these data. In general, the published data on SO 2 concentration in sintering under ordinary conditions show a high SO2 concentration in the early stages followed by a rapid decrease in concentration and with relatively little SOz in the gases from the last half or third of the operation. In other words, the greater part of the sulphur elimination is obtained in the first third or half of the period. In these runs, the 6-in. vacuum, which approximates the usual operating condition, gives a curve that follows this customary pattern. Maximum SO2 concentration is obtained 234 min. after

Jan 1, 1944

By J. Birkinbine

Extended discussions, by inviting attention to problems affecting the conservation of natural resources, have encouraged investigations as to their sufficiency, with the general result that the more thorough the examination, the less cause appears for anxiety as to the exhaustion or serious depletion of these resources.

Jan 1, 1915