By R. E. Pray, M. C. Fuerstenau, J. D. Miller, B. F. Perinne

Quartz cannot be floated with potassium amyl xanthate as collector at any pH. Complete flotation is achieved with certain minimal additions of amyl xanthate and Pb from pH 5.8 to 8.5 and with amyl xanthate and Zn from pH 7.5 to 8.1. The active species of these metal ions responsible for activation are shown to be PbOH and ZnOH No flotation was effected when Cu and Mg were added as activators. Previous work1,2,3,4,5,6,7 has shown that quartz may be floated in the presence of sulfonate or soap when the following two criteria are met: 1) some portion of the added metal ion has hydro-lyzed to its first hydroxy complex, and 2) a precipitate of the metal-collector has formed. Since sulfonate and soap, two substantially different anionic collectors, conform to these criteria, this phenomenon may well be expected to be of a general nature. In this view then, it would appear that any anionic collector, including xanthates, should also float quartz when these two criteria are met. The object of this paper is to demonstrate the conditions under which quartz will respond to flotation in the presence of potassium amyl xanthate. EXPERIMENTAL MATERIALS AND TECHNIQUES Quartz was prepared by leaching the sized sample (48 x 150 mesh) with HC1 until no iron could be detected in the leach liquor. Conductivity water, made by passing distilled water through an ion exchange column, was used in the investigation. Potassium amyl xanthate was selected as collector. Purification of this reagent was effected with the following method: 1) a laboratory sample of potassium amyl xanthate was dissolved to saturation in hot ethyl alcohol and filtered several times while still hot, 2) the filtrate was cooled, during which time potassium amyl xanthate crystallized out of solution; the xanthate was then separated from the solution by filtration, 3) the amyl xanthate was dissolved in fresh hot ethyl alcohol and filtered, 4) step (2) was repeated, 5) the crystalline potassium amyl xanthate was washed with ethyl ether five times, and 6) the xanthate was dried for 24 hours under continuous vacuum. Inorganic impurities are insoluble in hot ethyl alcohol whereas dixanthogen is soluble in ethyl ether. Five-gram charges of 48x150 mesh quartz were conditioned for 3 min in 125 cc of solution containing the reagents and were floated with the small-scale cell and procedure described in previous papers.478 Reagent grade HCl and NaOH were used for pH adjustment, while reagent n-amyl alcohol was added as frother. Frother addition is necessary with this technique, but it should be mentioned that data, similar to those shown in Fig. 2 for 1 x10-4 mole per liter Pb++ and 1 X 10-4 mole per liter AX-, were also obtained with a Hallimond cell in the absence of frother. EXPERIMENTAL RESULTS Clean quartz could not be floated with amyl xanthate at any pH. Flotation was achieved under certain conditions, however, when various metal ions were added to the system. The activating ions used were lead, zinc, copper and magnesium, added as reagent grade chloride salts. Lead as Activator: The effect of Pb++ as activator was examined at five different additions of amyl xanthate (Fig. 1, 2 and 3). When 1x 10-5 mole per liter xanthate was added in the presence of 1 x 10"4 mole per liter Pb ++, no flotation was obtained at pH 6.5 or below, while a recovery of about 60% was effected at pH 7. When the pH was increased to 7.8, no flotation was again obtained, Complete depression was noted from pH 7.8 to about 10, at which point a recovery of about 30% was achieved. At about pH 11, the precipitate of lead amyl xanthate which was present below this pH dissolved and complete depression occurred. When 2.5x 10-5 mole per liter xanthate was added with the same lead addition, no flotation was obtained at pH 5.8 and below, whereas a recovery of

Jan 1, 1965

By W. F. Hosford

A series of aluminum single crystals was subjected to axially symmetric flow by drawing through dies. The orientation dependence of the drawing stress, which indicates the resistance to this type of flow, compares reasonably with predictions of Taylor and of Bishop and Hill. Measured lattice rotations likewise are generally consistent with theory. The most successful analyses of the plastic behavior of polycrystalline metal and its relationship to single crystal behavior are those of Taylor1-3 and of Bishop and Hill.4-6 The purpose of this paper is to provide a critical test of some of the basic assumptions involved in these theories. Both treatments apply to fcc metals and assume the shape change of each grain in a polycrystal to be the same as that of the polycrystal as a whole. Thus for a randomly oriented polycrystal extended under uni-axial tension each grain is assumed to undergo axially symmetric flow. dey = dez = -1/2dex, deyZ = dezx = dexy = 0 [l] where x, y, and z are a set of orthogonal axes, x being the tensile axis. Although [011.] oriented grains in bcc and fcc metals may depart markedly from this ideal behavior,7,8 the assumption is probably quite reasonable for most grains. Under a uniaxial tensile stress, ox, the work dW per unit volume expended in producing an increment of axial strain dex is, dW=oxdex [21 Since this work is expended in slip, dw =STi dyi 131 where Ti and yi are the shear stress and shear strain on the active slip systems. In both analyses Ti is taken to be the same on all slip systems, and dependent only on the total prior shear strain on all systems, so dw = Tdy [41 where t is the shear stress required for slip and y is the sum of the shear strain yi on all slip systems. Combining 121 and [4] and defining M = oX/T The ratio M is a generalized Schmid factor. It relates the tensile stress required for axially symmetric flow, ox, to the basic shear stress, 7, and it also expresses the ratio of crystallographic strain, y, to the tensile strain, Ex It depends only on the orientation of the crystal. Taylor evaluated M for various orientations by finding the least value of dy/dEx which could satisfy the shape change. Bishop and Hill, on the other hand, found M by considering the relative work (1/T)dW/dEx expended by stress states which could activate enough slip systems to produce the shape changes. The results of both methods appear to be equivalent, although certain omissions were made in Taylor's original work. The orientation dependence of M, calculated by the second method,9 is shown in Fig. 1. Taylor used the average 2= 3.06 for all possible orientations to predict the tensile stress-strain curve (oxvs Ex) for a random polycrystal from the shear stress-strain curve (t vs y) of a single crystal. Changes in M from lattice rotation were neglected so points on the ox vs ex curve were simply taken at ox = 3.06t and e = y/3.06 from corresponding points on the t vs y curve. Recent extension of the analyses of Taylor and of Bishop and Hill to crystallographically textured metals has been used to relate plastic anisotropy to textures, and to predict the potential texture hardening that could result from texture control.9 Unfortunately there have been relatively few experimental tests of the underlying theory. Taylor found that the tensile stress-strain curve of polycrystalline aluminum did agree reasonably well with that predicted from a single-crystal T-y curve. Had the single crystal undergone easy glide, how-

Jan 1, 1965

By J. W. Galpin, R. H. Allen

Controlled pre-grouting is a technique developed during a period of more than ten Years experience, in an effort to produce safer, drier and more economical mine shaft sinking. The technique involves a knowledge Of hydro-mechanics, both static and dynamic, and a series of specially formulated grout mixtures to obtain several desired results through precontrolled setting time. In general, the following procedures have been used to secure the best results in controlled pre-grouting: I. Before drilling is commenced, One Of two decisions is made: one procedure, a modified form of the Francois method, is to stage drill and grout, that is, drill a limited portion of the hole, then grout and redrill that section which has been grouted, progressing in stages until the required depth is reached. We prefer this method because no casing Or grouting packers are required in the bore hole. This eliminates the risk of losing them in the bore hole due to packer failure, which might result in the expense of drilling a new grout hole. Another feature Of this approach is that smaller drill holes may be effectively used, further reducing the costs. One drawback, however, is that because of the open and small size hole, it is impractical to attempt water draw-down tests. The second alternative is to drill the bore hole, (generally NX size), to the re-quire~ depth. he casing and grouting packer are placed in the bore hole at the lowest packer setting. A small, portable, power driven, swabbing device is used in the grouting casing to test the packer and remove mud or cuttings from the bore hole below the packer. The hydrostatic level is recorded and a close estimate or test is made of the quantity of water at each packer setting. Grouting progresses upward in a series of packer settings to the surface. Occasionally, casing is inserted in the bot-tom of the bore hole from within the mine, and water pressure and volume can be obtained in this manner. This is usually dangerous because of the unknown quantity of water. 2. The grouting, mining and geological engineers at the drill location make a detailed examination of the cores and also locate proper and firm grouting packer locations. A competent driller,s opinion should be given due consideration as to the character and condition of the bore hole. 3. Several samples of formation water

Jan 1, 1949

The Development of Research and Quality Control in the Modern Steel Plant. By Leo F. Rein-artz. (Metals Technology, April 1943) Blast Furnace and Raw Materials Essential Considerations in the Design of Blast Furnaces. By A. L. Foell. (,Metals Technology, December 1942) Results Obtained from Surveys of Gas at Furnace Tops. By James M. Stapleton. (Metals Technology, January 1943) Physical Aspects of the Dust Catcher, Gas Washer and Precipitator on No. 3 Furnace at Carrie. By C. P. Clingerman and C. J. FleiscH. (Metals Technology, January 1943) Slag Control by Introduction of Flux through Blast-furnace Tuyeres. By Carl G. Hogberg (Metals Technology, January 1943) The Electrical Conductivity of Molten Blast-furnace Slags. By A. E. MaRtin and GerRard Derge. (Metals Technology, August 1943) Some Physical Characteristics of By-product Coke for Blast Furnaces. By CEarles C. Russell and MichaeL Perch. (Metals Technology, December 19+2) Pyrometry at the Coke Oven. By Robert B. Sosman. (Metals Technology, December 1942) Calcination Rates and Sizing of Blast-furnace Flux. By T. L. Joseph, H. M. Beatty and Gust Ritsianes. (Metals Technology, December 1942) The Low-temperature Gaseous Reduction of a Magnetite. By M. C. Udy and C. H. Lorig. (Metals Technology, October 1942) Steelmaking Problems of Total Operation in Steelmaking. By William C. Marshall and Frank G. Norris. (Metals Technology, April 1943) Silicon-oxygen Equilibria in Liquid Iron, By C. A. ZapFFe and C. E. Sims. (Metals Technology, September 1942) Equilibria of Liquid Iron and Simple Basic and Acid Slags in a Rolating Induction Furnace. By C. R. Taylor and John Chipman. (Metals Technology, September 1942) Rapid Analysis of Oxygen in Molten Iron and Steel. By Gerhard DeRGe. (Metals Technology, January 1943) Silver Chloride as a Medium for Study of Ingot Structures. By Karl L. Fetters and Margaret Dienes. (Metals Technology, August 1943)

Jan 1, 1943

By Albert Sauveur

SOME writers believe that when austenite transforms completely into pearlite on slow cooling through the thermal critical range, such transformation does not imply the formation of any of the so-called transition constituents: martensite, troostite and sorbite. Might it not be claimed with as much justification that when water freezes it does so suddenly, solid ice being obtained without passing through the intermediate stages of ice and water? Obviously, regardless of the speed of solidification, this would be erroneous. Before reaching the completed solid condition, this must of necessity pass through an unbroken series of stages when the system consists of mixtures of water and of ice, the former decreasing and the latter increasing in amount. Are not these "transition" stages in the freezing of water similar to the transition stages occurring in the transformation of austenite into pearlite? To clarify, let us consider in Fig. 1 the mechanism of the transformation of eutectoid steel from its austenitic to its pearlitic condition as it cools slowly through its thermal critical range. It is generally admitted that this transformation is the result of two distinct phenomena: (1) the allotropic change of gamma iron into alpha iron and (2) the crystallizing out of solution of the carbide Fe3C. Whether this crystallizing of Fe3C implies also its formation is immaterial for our purpose. In other words, whether it is the carbon in atomic dispersion which is present in gamma iron or molecules of Fe3C has no bearing upon the matter to be discussed. The transformation of gamma iron into alpha iron cannot take place suddenly. It must of necessity be progressive, regardless of the speed with which it may take place. At A, for instance, there would be present AB gamma iron and BC alpha iron. The distance MN does not refer to falling temperature, but to the passage of time. It may be assumed that the transformation takes place at a constant temperature (the Ar321 point). In a similar way, the crystallization of Fe3C out of the austenite solid solution must be progressive as depicted between M and N. At A there would be present AB gamma iron, BC alpha iron, CD carbon dissolved in gamma and in alpha iron and DE Fe3C. This condition may be described according to individual preference as martensite or troostite. To sum up, can the metal pass from condition

Jan 1, 1931

By F. W. Bryan, D. H. Lynch

Introduction This paper is a general description of current central Florida phosphate mining, beneficiation, and product transportation. It is directed and believed to be of interest to engineers not familiar with this industry. Deposit: The phosphate deposits of central Florida are generally located in a five county area which includes Polk, Hillsborough, Hardee, Manatee, and DeSota counties. Geologically, the deposit is of marine origin and is identified as the Bone Valley formation. This formation is Pliocene to Recent in geological age and overlies a Miocene limestone formation known as the Hawthorn. The Bone Valley formation sediments are regionally characterized by equal proportions of apatite, quartz, and clay. The clay is predominantly of the mont-morillonite family. On a local scale, however, the proportions of these three major constituents vary considerably. The phosphate occurs as the apatite mineral (Ca 10F2(PO4)(6) and with the clay and sand, the minable ore is commonly referred to as matrix. This matrix is overlain by unconsolidated overburden of sand and sandy clays, ranging in depth from 10 to 45 ft. The matrix usually occurs in fairly horizontal continuous beds from 3 to 25 ft in thickness. The bedded limestone formation lies directly below the matrix and is generally well defined. The phosphate particles range from 3/4 in. to 200 mesh (Tyler) in size. The phosphate particles coarser than 14 mesh are called pebble phosphate and those less than 14 mesh are termed flotation feed which, when beneficiated, subsequently become concentrates. Through mining and beneficiation, phosphate quality is measured in BPL percent which stands for bone phosphate of lime units. In subsequent chemical manufacturing, the quality is indicated by P205 content. The deposit is economically characterized by various ratios such as tons of product per acre and cubic yards handled per ton of product. Magnesium, iron, and aluminum content are also considered in evaluating ore reserves. These elements are often critical to the chemical fertilizer processes. Presently, an ore body is considered economically minable if it meets the criteria shown in [Table 1]. These, of course, are general guidelines and specific costs and returns on investment must be considered in each case for acquiring reserves. On a new grass-root venture, a 20-30 year life is generally expected with a mineral recovery of 80%. History and Uses Phosphate mining in central Florida began around the turn of the century. However, in the early days, only pebble phosphate was produced until about 1930 when technology was available to beneficiate the -14 + 150 mesh particles. The -150 or -200 mesh material was discarded as it is today. The basic processes for beneficiation are washing, scrubbing, desliming, sizing, and flotation. These basic unit processes are essentially the same today although many improvements have been developed since the early days. Phosphate is used primarily in the production of high analysis fertilizer chemicals, typical of which are triple superphosphate, monoammonium phosphate (MAP), and diammonium phosphate (DAP). Phosphate is also used in the production of food preservatives, dyes for cloths, vitamin and mineral capsules, steel hardeners, gasoline and oil additives, toothpaste, shaving creams and soaps, bone china dishes, plastics, optical glass, photographic films, light filaments, water softeners, insecticides, soft drinks, road fill, and livestock feed supplements. Florida produces over 80% of the nation's marketable phosphate rock and one-third of the world production, according to the US Bureau of Mines. This amounted to approximately 35 million tons in 1975. Exports of Florida phosphate rock were to such countries as Canada, Japan, West Germany, Italy, and India, with Canada and Japan being the major users. Almost 95 o of all outbound cargo shipped through the port of Tampa is phosphate rock or related products. Beneficiation Following is a description of Agrico's new Fort Green beneficiation plant which is typical of the newer large capacity plants being built in the field. Agrico's Fort Green mine was completed in 1975 and is located in the southwest corner of Polk County and is directly adjacent to Manatee, Hillsborough, and Hardee Counties. With some minor differences, Fort Green is typical of a modern central Florida plant. The rated capacity is 3,000,000 plus tons of product per year and this varies according to the richness of the ore being handled. A simplified flowsheet is presented in [Figs.1 and 2]. This plant is served by three draglines of the 40-cu-yd class. The phosphate beneficiation is usually divided into three major functional steps: (1) washing and screening to produce a pebble product and flotation feed, (2) feed preparation and (3) flotation to produce concentrates. The typical plant is similarly divided into these three functional areas. Washer: Briefly, the slurried matrix is pumped from two draglines simultaneously at a combined rate of about 20,000 gpm at 2000 tph (solids) to rotary trommel screens sized to make a 7/8-in. separation. ([See Fig. 1]-) The trommel oversize is sent to hammermills where it is crushed and returned to the trommel screens, or pumped to tailings if minor impurities (Fe203, A1203, MgO) are too high. The trommel undersize is pumped to 14 mesh stationary (static) flat screens. The flat screen over¬size is subjected to three stages of 14 mesh vibrating screening and two stages of log washing in order to produce a final pebble product. The pebble product (+ 14 mesh material) is conveyed by belt conveyor to a large on-ground storage pile. Pebble product is reclaimed through a tunnel and loading system below

Jan 1, 1980

By E. O. Wagner, V. F. Parry

This paper summarizes investigations during 1949 on three pilot plants for drying low-rank fine coal by entrapment in hot gases. Detailed operating results on processing seven coals having moisture ranging from 24 to 62 pet, formulas and data for calculating performance of large units, and general conclusions on the problem of drying fine coal are presented. THIS paper presents a summary of investigations by the Coal Branch of the Bureau of Mines during 1949 on the removal of internal moisture from low-rank coals by processing them in the entrained and fluidized state. A paper on this subject, giving a summary of the early work, was presented at the 1949 AIME annual meeting1 and gave a the- oretical discussion of the time and heat required to dry various sizes of low-rank coal. The investigations on two pilot plants were presented in the foregoing paper. During 1949, three additional pilot plants were built to study phases of the drying problem and to investigate different techniques of handling fine coal in the entrained and fluidized state. The present paper gives operating data on the new units and presents detailed data on the drying of seven coals having bed moisture ranging from 62 to 24 pct. The problem of removing surface moisture from fine coal is principally one of heat exchange and dispersion of the coal particles so that heat can reach the liquid moisture to permit evaporation, and it does not involve the factors of size and time of contact to any great extent. If enough heat can reach the surface of the particles at temperatures higher than 250°F, moisture evaporates almost instantly, and the factors of time and size are of secondary importance compared with the factors of heat balance and dispersion of the coal. Therefore, it does not appear to be necessary to employ a fluidized bed when removing surface moisture, and the most efficient process would be one in which the coal particles are entrained in a hot gas stream of optimum temperature traveling at a velocity that causes the particles to disperse into a low-density phase. When low-rank coals are dried, the fluidized bed is necessary to provide control of time of contact. This is done by adjusting the superficial velocity which controls the density or dispersion of the particles. The density of beds having fluidized properties suitable for drying low-rank coals appears to range from about 5 up to about 15 lb per cu ft. When the density is below 5 lb per cu ft, which represents a low-density phase, optimum conditions for removal of surface moisture should be found, and this requires superficial velocities of about 15 fps. The problem of removing bed moisture from low-rank coals involves consideration of size of coal, temperature, mass flow, heat balance, pressure, time of contact, and method of dispersing the coal in the heating mediums. The experimental work presented here gives data on these factors. Coal sizes up to 1/2 in. x 0 were dried with hot gases having initial temperatures ranging from 1900° to 2400°F. Coal

Jan 1, 1951

By A. J. Jacobs, J. W. Spretnak, R. Speiser

The activities of nickel in liquid iron-nickel solutions containing from 10 to 90 at. pct Ni were measured over the temperature range .1510° to 1600°C. A special function was devised whereby activities can be computed by a graphical integration using the results of chemical analyses on the vapor phase alone. The liquid solutions studied exhibit negative deviation from Raoult's law, but they approach ideality as the temperature is raised from 1510° to 1600°C. The maximum heat of solution is less than -8.0 kcal per mole. The entropy of solution is less than —2.5 kcal per mole deg at 1510°C, and changes negligibly as the temperature is raised. The liquid iron-nickel solutions do not follow regular solution behavior. THE activities of the components of a liquid alloy system can be determined in favorable cases from the partial pressure of the vapor in equilibrium with the liquid alloy.' Assuming that the vapor over the alloy behaves as an ideal gas, the activity of component i is given by the expression, Where the superscripts 1, v, and o signify the liquid, the vapor, and the pure component, respectively; the f's are the fugacities, and the P's, the pressures. The quantities Pi and Pi can be determined by the

Jan 1, 1960

Jan 1, 1967

By Harry H. Angst, Reuel A. Cochrane

The successful exploitation by opencut methods of the low-grade porphyry copper deposits is due to the economical handling of large tonnages. Large tonnages are possible only if the rock material is broken so that the large power shovels can operate with minimum delays. This is particularly true at the New Cornelia mine, where the dense, hard, tough rock material creates problems not encountered in most of the porphyry copper mines. The introduction of churn drills at the New Cornelia for primary drilling, in 1936, necessitated a complete change in the methods of breaking ground as formerly air drills had been used. The blasting operations are of particular interest because of the handling of great quantities of high explosives in safely and efficiently fragmenting the hard rock material. Rock Formations At the New Cornelia mine the rocks are quartz monzonite with a diorite border facies intruding a rhyolitic series. Overlying these formations is a fanglomerate formation composed of boulders of monzonite, diorite, rhyolite, and other types of rock of unknown derivation. (The word "fanglomerate" is used in this paper in referring to the local conglomerate type of rock formations.) The ore body is approximately 4800 ft. long and 2800 ft. wide, and is of the disseminated type. Mineralization occurs principally in the quartz monzonite and to some extent in the adjacent diorite and rhyolite. The principal ore minerals are chalcopyrite, bornite, and a small amount of chalcocite. Over a considerable area the quartz monzonite is extremely hard and siliceous in character, owing to pegmatitic zones of alteration. The hardness of the ground depends on the intensity of the silicification. In a small area in the pit, the monzonite contains an abundance of pyrite accompanied by sericitization and is soft and easily fragmented. This is true also in the remaining oxidized portion of the ore body. The diorite and rhyolite formations, like the monzonite, vary from extremely hard to very soft material, but on the whole are easier to fragment than the monzonite. Jointing is prevalent in all the rock formations and plays an important role in the blasting efficiencies. In the fanglomerate formation, numerous well-defined joints, widely spaced, tend to make the ground blocky when blasted. This is a deterrent to good fragmentation. In the other rocks the joints are more numerous and are closely spaced, except in localized areas where the formations are extremely hard. These descriptions indicate that the lowest blasting efficiency will be obtained in the harder formations, from which the major portion of the mine production is obtained; namely, the monzonite and rhyolite. All rock formations mined at the New Cornelia pit are so hard that excavation

Jan 1, 1943

By A. B. Hildebrandt

P. B. Baxendell is to be complimented for an exccllent piece of work. To our knowledge there has been no previous publication of field data on the flow of oil and gas through the annulus of a well. It is certainly gratifying to see this work on annular flow confirm the previous published correlation procedure on tubing flow. It extends considerably the range under which reliable gas-lift calculations can be made. Baxendell discussed this work with us about a year ago and was kind enough to send a large scale plot of his correlation. We had been designing gas-lift installations on flow through the annulus, assuming that the original correlation of the f factor based on tubing flow' was valid as long as we stayed within the same mass velocity range on which the correlation was based. Doing this work necessitated the use of an equivalent diameter for the annular flow. The equivalent diameter is defined as area' of stream cross section wetted perimeter and for the case of an annulus is D, — D,. Substituting this in the basic equation correlating energy loss along with the area to flow required to convert the velocity, to volumetric flow rate, D (Baxendell's Eq. 7) becomes dell's expression, D,). Similarly, the D in 1.4737 X 10 (M&/D) becomes (D, + D;) for annular flow. On receipt of Baxendell's data, we. of course, recalculated it to put it into the form we were using, and to see how well it agreed with the correlation based on tubing flow. Fig. 1 shows the results, which were certainly gratifying. For low values of (D, - D,) pv, the data coincide with the data on flow through tubing, whereas at high values the data on flow through the annuli appear to be leveling off to a constant value. For very high rates of flow where the turbulence is very high, one might expect the value f to level out and become constant. A bulletin published in 1914 by the U. of Wisconsin presented results of a large number of laboratory teats in air lifting water through short lengths of 1.25-in. tubing. It was possible to correlate a random sampling of

By J. S. Vanick

AN extremely hard, tough, and strong, white or chilled cast iron has been applied for the past several years to industrial and mining services in which its unusual properties have been confirmed by its ability to deliver in many instances much better performance than plain chilled iron, or other wear-resistant materials. It is being produced regularly by alloying a good base composition of chilled or white cast iron with essentially 4 to 6 per cent of nickel and 1 to 2.5 per cent of chromium. Such a material can attain a hardness exceeding 600 to 750 Brinell as against 380 to 530 for corresponding grades of plain chilled iron. The strength is approximately doubled and the toughness significantly increased. These properties make it especially useful for many applica-tions requiring a high hardness for resistance to wear, abrasion, attrition, deformation; to some extent to high compressive loading and to a lesser but important degree to corrosive action. A wide variety of commercial castings is being successfully produced from this iron, ranging in size from the small-grain grinding plates or burrs through medium-sized castings such as sand pumps up to large, heavy castings such as rolls for metal rolling or cement grinding. The composition of this white cast iron may be roughly bracketed within the range shown in Table 1.

Jan 1, 1933

By Carl F. Floe, John Chipman

THE system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or C02 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modem metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100° to 1500°C., and pressures from about 20 mm. of mercury to somewhat above atmospheric. REVIEW OF PREVIOUS WORK The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as 02, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: [2M -}-G2 = 2MGK =G) IYf X[I]] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: [MG = Ki Pa,[2]] Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: [6Cu + S02 = Cu2S + 2Cu20[3] K Cu2S X (Cu20)2(Cu)e(Psm)[4]] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: [K1 =or Vdo,= K2/PBO [5] PsO]

Jan 1, 1941

THE composition and quality of finished steel depend upon selection and proportioning of the raw materials of the charge as well as on control of furnace practice. This chapter deals only with those raw materials of the basic open-hearth process which are important in determining the composition of the steel or slag. They are the metallic charge, oxygen-bearing materials, fluxes, and alloying and deoxidizing additions. Refractories, which may also affect the slag composition, are discussed in the previous chapter. Wide variations are possible in the type and composition of charged materials, but in all cases certain fundamental relationships among the elements of the charge must be maintained. Since the process consists essentially of refinement by oxidation of undesired elements, a balance must be established between the sources of oxygen and the elements in the charge that are subject to oxidation (see Chapters II and VII). For example, if it is desired to use a high ratio of blast-furnace hot metal to scrap, it is necessary to add an oxygen-bearing material such as ore or mill scale to eliminate the excess carbon and silicon that are present in the hot metal. An example of the opposite extreme would be the use of a metallic charge composed entirely of steel scrap. With this type of charge, it is common practice to substitute burnt lime for limestone as a flux and to charge some carbonaceous material such as coke to avoid an excess of oxygen in relation to the elements of the charge that are subject to oxidation. Elements such as copper and nickel, which are not subject to oxidation or other reactions resulting in their elimination, may be introduced into the charge only to the extent to which they are permissible in the finished steel. An example of adjustment of the charge for elements of this type would be found in the use of steel scrap high in copper. In this case, metallic components of the charge other than the scrap should below in copper, or a sufficiently high ratio of pig iron to scrap should be charged to dilute the copper from the scrap, so that the average copper content of the melt will be below the required maximum.

Jan 1, 1944

By J. E. Cannaday, R. J. Austin, R. K. Saxer

PREVIOUS investigators have determined activation energies and have postulated various controlling mechanisms for creep.'-' Recently Barrett et 01.I5 have suggested, as the result of their work with cadmium, that the apparent activation energies for creep (AHc) above 0.5 T, could be correlated by means of activation energies for self-diffusion (AHSD) and modulus of elasticity functions: AHC = AHSD - (5RT/E) dE/dT. The wide disparity of apparent activation energies previously obtained with nickel compared to those reported for other fcc metals and the desire to test the postulate of Barrett el al. prompted this study. The as-received 17.5-mil nickel wire used during this work assayed 99.87 pct pure, Table I. X-ray analysis indicated that the wire was in a stress-re- lieved state and metallographic examination revealed an equiaxed grain size of approximately 0.01 mm. Specimens degreased in acetone and cut to 1-1/2 in. lengths were tested in a cam-mechanized constant-stress creep machine. A vacuum of at least lo-5 mm Hg was maintained during all tests. Stresses were applied when thermal equilibrium was established. When a measurable (at least 0.5 pct) secondary creep was observed, the temperature was pulsed to a higher temperature. Pulsing time varied from 30 sec at 480°C to 2 min at 1300'C and above. Slopes of creep curves were determined after the initial acceleration in the strain rate had subsided and steady-state creep was achieved. To confirm the results obtained, additional tests were performed incorporating a temperature pulsing method suggested by sherby. In this method the load was removed during temperature pulsing and reapplied after thermal expansion had occurred. No appreciable differences in results were obtained. Tests were performed over a wide range of temperature (470" to 1310°C) and stresses (250 to 17,000 psi). The expression was used to calculate activation energies. In this expression T1 and T2 are the initial and final temperatures, and el and i2 are the creep rates at T, and T2. The variation of the apparent activation energies with the mean test temperature calculated by means of Eq. [I] are shown in Fig. 1. The mean test temperature (Tmean) was calculated from the relationship

Jan 1, 1967

By Victor A. Phillips

A series of strips of a Ni-12.7 at. pct A1 alloy were Prepared containing cubical y'(NisAl) precipitates with edge lengths from 60 to 500A. A particle-free solution-tveated strip was included for cornparison. They weve cold-rolled 95 pct and the effects of particle size on the isochronal (1/2 hr) annealing behavior between 300° and 950°C studied (by hardness and light and electron microscopy). It ulas inferred that the particles deformed with the lnatvix becoming lamellae which remained coherent. Comparison with published data fov pure nickel showed that aluminum greatly re-tavded softening and recrystallization, but it made little difference whether or not particles were present. The presence of pakticles led to a heterogeneous distribution of precipitates after annealing at 700" to 750°C. Recovery was not detected. Recrystallization occurred by the growth of new grains into unrecrys-tallized material. In a previous study by the author,' the growth of Ll2-type ordered yl(Ni3Al) precipitates was followed in Ni-12.7 at. pct A1 alloy as a function of aging at 600" and 700°C. The particles were showo to be cubical in shape in all sizes from 50 to 3000A and remained coherent. This work was used as a guide in preparing the starting structures for the present study of the effect of these particles on the annealing behavior of heavily cold-rolled strip. Another question of present interest was whether dislocation and particle hardening were additive, since the structures before rolling ranged from solution-treated to peak-aged to overaged. Also, precipitation might occur on annealing after cold-rolling. Reference may be made to other papers2"5 for previous work in this relatively unexplored field and only some recent work will be mentioned her:. phillips2 studied the effect of deformable 0 to 590A-diam cobalt particles on a Cu-3.23 pct Co alloy rolled 95 pct and found that the particles, which rolled out into thin lamellae, impeded softening and recrystallization. Tanner and servi3 likewise studied the annealing of cold-swaged Cu-2 pct Co alloy containing 150A-diam particles and found impeding effects. Haessner et a1.,4 on the other hand, found that incoherent 2-p-diam non-deformable particles of B4C (0.04 vol pct) tended to increase the rate of recrystallization of copper rolled up to 95 pct reduction. They attributed this to the formation of new grains at the particle interfaces. Humphreys and artin' found that nondeformable silica particles in copper rolled to 30 pct reduction accelerated recrystallization if the particle spacing was large and retarded it if the spacing was smaller. Haessner et a1 4 also studied a rolled Ni-Cr-A1 alloy; however, the particles of y'(Ni3Al)-type precipitate were not put in before rolling, but separated during the isothermal annealing at 750°C. No previous work appears to have been carried out on the effect of y' (Ni3A1) particles on the annealing of Ni-A1 alloy. Hornbogen and ICreye7 redetermined the solubility c of aluminum in nickel as a function of temperature T and showed that it was given by c = 32.6 exp(-1940/RT). This relation gives aluminum solubilities of 15.1, 14.2, 12.0, and 10.7 at. pct at 1000°, 900°, 700°, and 600°C, respectively. The phase precipitated from the nickel-rich solid solution is fcc y1 (Ni3A1) which has a Cu3Au -type ordered structure8 and remains ordered up to 1000°C.B EXPERIMENTAL PROCEDURE The alloy used was identical with that used before. Chemical analysis showed 6.27 wt pct (12.71 at. pct) Al, the principle impurities being 0.065 pct Fe, 0.022 pct Co, 0.020 pct Cu, and 0.004 pct C. Bar stock of 1 in. diam was cold-swaged to % in. diam, cold-rolled to 0.300-in.-thick strip, and annealed at 900°C in dry hydrogen. It was cold-rolled to 0.100-in. thickness and solution-treated for 1 hr at 1000°C while sealed in a quartz tube in argon, quenching in iced brine with the aid of a device to snap off the nose of the tube. Lineal analysis gave an average grain size of 0.055 mm. Pieces of strip were aged at 700°C in vacuo for 30 min, 51/4 hr, and 1 week to produce nominal average particle widths of 60, 150, and 500A, respectively, as known from the previous work.' The average diamond pyramid hardness was determined. The heat-treated strips were rolled from 0.100 to 0.005 in., a reduction of 95 pct, and the rolled strips stored at about -5°C. Small pieces were annealed within 1 week for 30 min at temperatures from 300° to 950° ±2°C in a horizontal vacuum furnace. Strips were withdrawn into a cooling zone, giving an estimated initial cooling rate from 950°C of about 50°C per sec. Average diamond pyramid hardnesses were determined on a lightly electropolished spot on the surface of each strip using 300-g load. Each point on the softening curves represents a separate annealed specimen. Sections containing the rolling direction were examined by optical metallography. Selected specimens were electrothinned to the center plane' and examined by transmission at 100 kv in a Siemens Elmiskop I electron microscope. It is well-known that changes in the structure tend to occur when a deformed strip is electrothinned below a thickness of a few hundred angstroms, although this is less serious with a material such as nickel which has a high melting point, and also is apt to be less serious when particles are present. Observations were nevertheless confined to thicker regions of the foils with estimated thicknesses over 1000A. No changes were observed due to beam exposure.

Jan 1, 1968

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960

By H. J. Ramey

The wellbore acts as a storage tank during drawdown and build-up testing and causes the sand-face flow rate to approach the constant surface flow rate as a function of time. This effect is compounded if non-Darcy flow (turbulent flow) exists near a gas wellbore. Non-Darcy flow can be interpreted as a flow-rate dependent skin effect. A method for determining the non-Darcy flow constant using this concept and the usual skin effect equation is described. Field tests of this method have identified several cases where non-Darcy flow was severe enough that gas wells in a fractured region appeared to be moderately damaged. The combination of wellbore storage and non-Darcy flow can result in erroneous estimates of formation flow capacity for short-time gas well tests. Fortunately, the presence of the wellbore storage eflect permits a new analysis which can provide a reasonable estimate of formation flow capacity and the non-Darcy flow constant from a single short-time test. The basis of the Gladfelter, Tracy and Wilsey correction for wellbore storage in pressure build-up was investigated. Results led to extension of the method to drawdown testing. If non-Darcy flow is not important, the method can be used to correct short-time gas well drawdown or build-up data. A method for estimation of the duration of wellbore storage effects was developed. INTRODUCTION In 1953, van Everdingen and Hurst generalized results published in their previous paper3 concerning wellbore storage effects to include a "skin effect", or a region of altered permeability adjacent to the wellbore. Later, Gladfelter. Tracy and Wilsey4 presented a method for correcting observed oilwell pressure build-up data for wellbore storage in the presence of a skin effect. The method depended upon measuring the change in the fluid storage in the wellbore by measuring the rise in liquid level. To the author's knowledge, application of the Gladfelter, Tracy and Wilsey storage correction to gas-well build-up has not been discussed in the literature. It is, however, a rather obvious application. Gas storage in the wellbore is a conlpressibility effect and can be estimated easily from the measured wellbore pressure as a function of time. Several approaches to the wellbore storage problem have been suggested. As summarized by Matthews, it is possible to minimize annulus storage volume by using a packer, and to obtain a near sand-face shut-in by use of down-hole tubing plug devices. Matthews and Perrine have suggested criteiia for determining the time when storage effects become negligible. In 1962, Swift and Kiel' presented a method for determination of the effect of non-Darcy flow (often called turbulent flow) upon gas-well behavior. This paper provided a theoretical basis for peculiar gas-well behavior described previously by Smith. Recently, Carter, Miller and Riley observed disagreement among flow capacity k,,h data determined from gas-well drawdown tests conducted at different flow rates for short periods of time (less than six hours flowing time). In the original preprint of their paper, Carter et al. proposed that the discrepancy in flow capacity was possibly a result of wellbore storage effects. Results of an analytical study of unloading of the wellbore and non-Darcy flow were recorded by carter.14 In the final text of their paper, Carter et al.!' stated that they no longer believed wellbore storage was the reason for discrepancy in their kgh estimates. In view of the preceding, this study was performed to establish the importance of non-Darcy flow and well-bore storage for gas-well testing. In the course of the study. a reinspection of the previous work by van Everdingen' and Hurst' was made, and the basis for the Gladfelter, Tracy and Wilsey' wellbore storage correction was investigated and extended to flow testing. WELLBORE STORAGE THEORY As has been shown by Aronofsky and Jenkins,11-12 Matthews," and others, flow of gas can often be approximated by an equivalent liquid flow system. The following developnlent will use liquid flow nomenclature to simplify the presentation. Application to gas-well cases will be illustrated later. First, we will use the van Everdingen-HursP treatment of wellbore storage in transient flow to establish (1) the duration of wellbore storage effects, and (2) a method to correct flow data for wellbore storage. DURATION OF WELLHORE STORAGE EFFECTS When an oil well is opened to flow. the bottom-hole pressure drops and causes a resulting drop in the liquid level in the annulus. If V. represents the annular volume in cu ft/ft of depth, and p represents the average density of the fluid in the wellbore, the volume of fluid at reservoir conditions produced from the annulus per unit bottom-hole pressure drop is approximately: res bbl-- (V, cu ft/ft) (144 sqin./sq ft) psi -(5.615 cu ft/bbl)(pIb/cuft) ........(I)

Jan 1, 1966

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members who registered at Institute headquarters during June: Ralph H. Sweetser, Columbus, Ohio. O. M. Bilharz, Rivermines, Mo. Etienne A. Ritter, Colorado Springs. Colo. Joseph A. Holmes, Washington, D. C. Dwight E. Woodbridge, Duluth, Minn. Francis Church Lincoln, Urbana, 111. Arthur Chippendale, Mexico City, Me'. William E. Saunders, Philadelphia, Pa. E. T. Miller, Louisville, Ky. E. P. Ross, Johnson City, Tenn. Jesse Scobey, Denver, Colo. H. M. Boylston, Cambridge, Mass. Charles Rhodes, Auckland, N. Z. Edward Keller, Perth Amboy, N. J. John W. Finch, Denver, Colo. F. G. Cottrell, San Francisco, Cal.

Jan 7, 1913

By S. W. Miller

DURING the examination of welds made in steel by the oxy-acetylene and electric-arc processes, the writer has met with some unusual structures, which he has not encountered elsewhere. They seem to be quite closely associated with the welding methods used, and characteristic of them, and would seem to be worth noting, especially as the references to them in the literature are few, and their explanation not clear or complete. An introductory word or two about fusion welding may not he out of place. The oxy-acetylene process is based on the great and very local heat generated by the burning of acetylene in the presence of commercially pure oxygen, the two gases being thoroughly mixed before combustion. The theoretical temperature is somewhat under 4000° C., but on account of various losses, the actual maximum temperature is probably about 3000° C. 1 The electric-arc process, using a metal electrode, which is also the filling rod, generates a still higher and more local temperature. The actual temperature of the positive crater of the carbon arc is given as 3500° C.2 No figures have been found for the temperature of the arc using a metal electrode, but it would probably not be very different from that of the carbon arc, and probably higher than that of the oxy-acetylene flame. The greater localization of the electric arc is due to the fact that it is not surrounded by a large envelope flame as well as to its higher temperature; while the oxy-acetylene white cone, or welding flame, in which the carbon of the acetylene is burned to CO, is surrounded and preceded by -a long envelope flame, itself of quite high temperature, in which the CO is burned to C02, and the hydrogen of the acetylene to

Jan 2, 1918