By A. L. Holley

The occurrence of this gas, in quite appreciable quantities, has been observed for many years in its escape along the creeks of Western Pennsylvania, and more recently, in much larger quantities, from the oil wells in and near Venango County. Within about five years several gas wells have been struck, from which the gas has escaped continuously in prodigious quantities and at great pressure. During the last year a systematic attempt has been made to utilize the flow of gas from one of these wells, and results have been reached which were quite unexpected. This well, near Leechburg, Armstrong County, is about twenty miles northeast of Pittsburgh, on one of the side tributaries of the Alleghany River. It had been drilled in search of oil to a depth of 1250 feet in 1871, but none was found. A great flow of gas was developed, however, accompanied by a slight spray of salt water, and this has continued with little or no diminution to the present time. The gas in its escape has been discharged through a 5-inch pipe, and at a pressure of from 60 to 80 Ibs. per square inch, but no exact determinations, either of the pressure or quantity, have been made. The rolling mill of Messrs. Rogers & Burchfield is on the opposite side of the river, and it has been for some years devoted to the production of fine grades of sheet iron from charcoal pig metal, by puddling and in knobbling fires. The usual weekly product of the mill has been 30 tons of No. 30 tin plates, and 50 tons of No. 24 to 28 sheets. The well was bought by this firm for $1000, and the gas is led across the river, a distance of about 500 feet, through a 3-inch pipe. It is distributed through half-inch pipes, and at a pressure of about 45 Ibs. per square inch, to several of the furnaces, but a large fraction of the total flow of gas is still wasted at the well. No essential alteration in any of the furnaces has been found necessary in the use of the gas fuel, except to brick up the firebridge and to put in the gas and air pipes. The old grate used for coal is loosely covered with bricks and cinder, so that a slight percolation of air may take place through them. The gas is admitted through a half-inch pipe, and blows toward the fire-bridge through 18 or 20 one-eighth inch jets. The air is blown in at about 2 lbs.

By T. A. Rickard

The interior of West Australia is an arid table-land, elevated 1400 feet above the sea. This plateau is flanked to the south by the Tertiary limestones which fringe the Great Australian Bight. It is bordered northward by the Carboniferous beds of the Fitzroy river and westward by the granite of the Darling hills, while to the cast this wide area, about 900 miles square, slopes downward imperceptibly into an undulating plain of sand, which stretches with dismal persistence across the boundary of South Australia. The waters of the ocean receded from this tract of land long ago; it is probably the oldest landsurface on the globe, and represents the basal wreck of a much larger continent. Fig. 1 is a map of this region. The Coolgardie and Kalgoorlie gold-fields are situated in the southwestern part of the region. The rock-formation consists of granite penetrated by diorites and andesites. The latter are occasionally associated with tuff's, which have been readily mistaken for sedimentaries. There are no fossil-bearing rocks, such as would afford a datum-line from which to measure the relative geological age of the prevailing formation. On the extreme edges of the mining territory there are, it is true, remnants of sand-rock which are considered identical with the " Desert Sandstone " of Queensland, determined by Daintree to be of Mesozoic age. But even this formation has evidently been laid down so long subsequent to the underlying rocks that it serves merely to emphasize their much greater antiquity. In their characteristics and in their relations to each other, the granite and the diorite of the Coolgardie region appear to me much to resemble the Laurentian granite and the Huronian

Jan 1, 1899

By B. E. Field

Cobalt is a silvery white metal with a slight bluish cast. It strongly resembles nickel in its appearance and properties, notably its resistance to corrosion, although its alloys with other metals differ decidedly in their properties from those of nickel. The name "cobalt" was derived from the German Kobold, meaning goblin, and this came to be applied to the cobalt minerals which, although they resembled ores, did not readily yield metal when smelted by the primitive processes available in the Middle Ages. Cobalt minerals were used as pigments by potters and glass workers before the Christian era. Cobalt blue glass was found in the tombs of the Egyptians and in the ruins of Troy, and many colors used by the ancient Greeks and Romans contained cobalt. The ancients were entirely unaware that the colors they used were caused by cobalt and the metal itself was not isolated until about the middle of the eighteenth century, by Brandt, although the preparation of cobalt compounds had been carried on in a small way ever since the opening of the silver-cobalt deposits at Schneeberg, Germany, in 1470.

Jan 1, 1935

By P. B. Bucky, R. V. Taborelli

This investigation was carried on by means of models and the application of the principles of similitude to determine the effects of props, props and cribs and sand filling in longwall mining. The geologic structure and rate of face retreat were kept constant and the only change introduced was in the method of support. It is not felt necessary to repeat a description of apparatus, or to explain the fact that a scalar model made in all parts of the same material as the prototype will behave similarly to the prototype when rotated at speeds such that the centrifugal force is as many times the gravitational force as the prototype dimension is a similar linear model dimension. The reader is referred to earlier papers1,2 for further information regarding these statements. All models were made of sandstone and were as in Fig. 6. They are composed of a 3/16-in. ore body bed A, overlain by a 3/16-in. bed B, a ?-in. bed C and two ?-in. beds D and E. The model was rotated at + 2350 r.p.m. equivalent to a model ratio of 1268. It was worked back ¼ in. at a time before being replaced in the centrifuge and again rotated. Table 1 gives model and prototype dimensions occurring in this discussion, the prototype dimensions being 1268 times the model dimensions. Figs. 1, 2, 3 and 4 were taken while the model was rotating at 2350 r.p.m. One was taken for each face retreat of 26.4 ft., but for obvious reasons all are not presented. Fig. 1 (A-E) shows the behavior of this type of structure with face retreats of 26.4 ft. and no artificial support. Fig. 2(A-E) shows the behavior of this type of structure where breaker and face props were used. The props were exceptionally strong, being of steel ? in. square in cross section, and capped with 1/16 in. ± of soft wood and paper, to allow for roof deflection. The face props were

Jan 1, 1940

By James A. McGurty, Walter J. Koshuba, Samuel G. Gordon, Gilbert E. Klein

ONE of the problems encountered in working with metals at elevated temperatures is the instability resulting from solid-solid diffusion at a -common interface. A determination of the nature and magnitude of this phenomenon is important as related to structural properties of materials potentially useful in high temperature applications. This paper is concerned with the solid state reaction between metallic molybdenum and beryllium at elevated temperatures. In the older literature,' there were no known inter-metallic compounds in the system Be-Mo, and the list of beryllium intermetallics was rather small. New compilations have been made by Smithells' and by Taylor," listing all the then known beryllium binary intermetallic compounds. In addition to these, some new phases have just been reported' in the system Zr-Be and some further compounds of the type MBe,3 have been currently described. The new compound MoBe,, which is reported upon in this paper differs considerably from the above mentioned MBe13 group, and will be discussed in detail. Diffusion Study The nature of the solid diffusion at a Mo-Be interface was determined by sealing a beryllium rod inside a molybdenum capsule and heating at a temperature of 2000°F' (1100°C) for 100 hr. The molybdenum capsule was fabricated from % in. swaged molybdenum rod obtained from the Fansteel Metallurgical Corp. The beryllium metal was obtained from Brush Beryllium Corp. as % in. cold-drawn rod. This material assayed 99.05 pct Be and contained as impurities 0.84 pct Be0 and 0.19 pct Be2C. The molybdenum capsule was % in. in OD x 2 in. long. To prepare it, a concentric hole 0.250 in. + 0.001 in. — 0.000 in. in diam was drilled and reamed in one end of a rod to a depth of 1 '/2 in. A 1 in. long beryllium rod 0.250 in. + 0.000 in. — 0.001 in. in diam was pressed into the molybdenum capsule. A molybdenum plug 0.250 in. & 0.001 in. in diam x 9/16 in. long was then used to seal the beryllium in place. The capsules were placed in a molybdenum resistance furnace and heated at 2000°F (1100°C) for 100 hr. On cooling, the specimens were cut and examined metallographically. Fig. 1 is a micrograph at X250 of a portion of the interface from a transverse section. Four phases are clearly visible, with sharp boundaries between them. Phase A is a section of the molybdenum capsule; phase B is the molybdenum-rich intermetallic composition MoBe,; phase C is the beryllium-rich compound MoBe13; phase D is a section of the beryllium rod. All phases were readily polished to a high metallic luster. The molybdenum-rich phase has a pronounced purple tinge. The beryllium-rich phase (C) is only slightly darker than the pure beryllium. In polarized reflected light, however, it shows striking birefringence between crossed Nicols. The black areas represent flaws or pores in the material. A small representative amount of powdered material from each of the phases was carefully removed under the microscope with a diamond tool. With this material, powder X-ray diffraction patterns were made for the identification of each phase. Table I lists the X-ray diffraction spacings and corresponding indexes characteristic of these intermetallic compounds. Synthesis To establish the formula of the new intermetallic compound, X-ray diffraction patterns were made from powders obtained from solidified melts of known composition. The syntheses were made by

Jan 1, 1952

By J. L. Gillson

In a brief summary of the many occurrences of fluorspar in our western states, it is not possible to go into detail in regard to the geology, mining and milling methods, and reserves about individual deposits. Rather a broad review is made of the occurrences and an analysis of how the western deposits may fit into our future domestic economy is presented. General Statement on Fluorspar Situation Fluorspar has been used for years as a flux in the manufacture of basic open-hearth steel, in foundry cupolas for melting pig iron, in the manufacture of opalescent glass and in the preparation of hydrofluoric acid. In 1880 the annual production of fluorspar in the United States was around 4000 tons per year. By 1900 it was up to 21,656 tons and between 1902 and 1908 it averaged about 40,000 tons annually. Prices were then so low, by present standards, that it seems impossible to believe now that mining could have been performed profitably at the price levels then prevailing. In 1890 fluorspar sold at the mines for $6.70 per ton, in 1901 for $5.81, in 1916 for 85.92. When the United States entered World War I, flyorspar production and price skyrocketed; the production reached 263,817 tons in 1918, with prices above $20.00 per ton, and prices were even higher in 1919 and 1920. After 1920, the domestic production fell from the 1918 level to about 125,000 tons annually and the average price dropped back to about $18.00 per ton. By 1935 the average price had fallen to $15.00, but in 1940 with a rising demand the average price of all grades had gone back up to $20.31. Today it is 75 per cent higher than in 1940 and presumably the price of acid grade at .least would be even higher if it were not for price ceilings. The first subsequent year that the domestic production exceeded that of 1918 was 1941, and the 1944 production is expected to exceed 400,000 tons, or over one and a half times that of 1918. In five-year periods, average production and imports were as are shown in Table I. Many people concerned with the consumption of fluorspar believe that the postwar period ahead will show a repetition of price trends of the last such period. They believe that imports will be again an important factor in the available supply and the price will fall back gradually toward the prewar level. The following basic factors are pertinent in analyzing this conclusion:

Jan 1, 1948

By A. H. Larson, L. G. Twidwell

DURING the roasting of zinc sulfide concentrates and by-product recovery from flue dusts, the zinc sul-fate phase may occur in various stages of the processes. In addition to zinc sulfide, other sulfide phases are usually present such as CdS, PbS, CuzS, and FeS. Consequently, the effect of these sulfides on the thermal decomposition of ZnS04 was investigated. Merck high-purity, anhydrous zinc sulfate was used as the starting material. The sulfate was heated under an argon atmosphere, at a rate of 10°C per min. With the first slight indication of decomposition as determined by gas analysis, the sample was removed from the furnace and allowed to cool. X-ray patterns showed no other phase present. It is estimated that less than 0.05 pct of the ZnS04 decomposed. The metal sulfides were also heated under an argon atmosphere to drive off any adsorbed water. The materials were then sized (-200 to +270 mesh), mixed in predetermined mole ratios, and pressed into pellets. The experimental measurement of the reaction rate consisted of purifying the argon carrier gas, continuous flushing of the heated reacting mixture with argon, and collection and analysis of the SOn product gas. The reaction system was heated to 600°C and al-

Jan 1, 1967

By M. Bevis, E. O. Fearon, P. C. Rowlands

Fe-Ni and Fe-Ni-C martensite specimens have been deformed in compression at room temperature and the habit planes of operative deformation twins determined by two-surface optical trace analysis. The full orientations of the martensite crystals were determined from divergent X-ray beam diffraction patterns. The experimental results are in excelled agreement with predicted twinning modes. In particular, the habit planes of some deformation twins in bcc martensites are consistent with a "Type XI compound'' twinning mode with Kl, Kz, 71, 77~ elements given by {5, 8, 11) {ioi}, (33) (ill) Tetragonal derivatives of this mode are operative in bct martensites. UnUSUAL deformation twinning modes have been reported by Richman' to occur in Fe-Ni-C martensites with bcc and bct structures. The twin habit planes were determined by single-surface trace analysis (pole locus method) and the remaining twinning elements were determined from the geometry of twin-twin intersections. The indices assigned to the observed habit planes are (3 101, "(089)" and "{0, 1,13)" or "{1,2,7} ", and only in the first case do the twinning elements correspond to a predicted twinning mode. This is mode 1.4 in the paper by Bevis et al. The results presented in Ref. 2 indicate that previously unpublished bcc and bct modes should be operative in preference to the (130) mode and anomalous modes reported by Richman. In view of these results and the uncertainties involved in determining habit planes from single-surface trace analysis and twinning elements from twin-twin intersections5 a two-surface trace analysis of deformation twins in Fe-Ni and Fe-Ni-C martensites has been carried out. EXPERIMENTAL PROCEDURES Two alloys with compositions Fe-23 pct Ni-0.6 pct C and Fe-30.4 pct Ni were prepared from 4N pure materials by induction melting under a vacuum of 10"5 mm Hg. The alloys were homogenized at 1350'~ for 5 days. Both of these alloys are austenitic at room temperature with M, temperature - — 50"C. The aus-tenite grain size of the Fe-Ni-C alloy was approximately 300 to 400 p. The Fe-Ni alloy was remelted in a vertical tube furnace and the melt lowered slowly from the hot zone of the furnace to produce s ingle -crystal austenite specimens. Specimens approximately 10 by 5 by 5 mm were cut from the ingots and quenched to various temperatures below the Ms temperature. The specimens were elec-tropolished in a 10 pct perchloric acetic electrolyte before being deformed in compression at room temperature. Martensite plates which exhibited profuse deformation twinning were selected for analysis and the specimen polished on a second surface such that the two surfaces which contained the martensite plate enclosed an obtuse angle of approximately 145 deg. The specimens were then electropolished to reveal the traces of the deformation twins on both surfaces. The full orientations of the martensite crystals were determined using a divergent X-ray beam technique (Kossel line technique) employing an AEI SEM2 electron probe microanalyzer. Details of this technique which include a detailed description of the Kossel camera attachment to the microanalyzer used in the present experiments have been discussed elsewhere.3 Only additional details relevant to this investigation are discussed here. The specimens were mounted with one surface normal to the incident electron beam as illustrated schematically in Fig. 1. The martensite plates to be analyzed were located using the normal scanning equipment of the microanalyzer. The position of the electron beam and hence the position of the source of divergent X-rays generated within the crystal could be located to within 1 p. Exposure times of approximately 8 to 10 min were required for back-reflection Kossel patterns and it was found that useful diffraction patterns could be obtained consistently from heavily deformed martensite plates. A reference line (carbon contamination mark) produced on the two surfaces of the specimen by scanning the electron beam in a direction having a known relationship with the reference !ine in the X-ray camera enabled the full orientation of the crystals to be determined. Martensite plates with widths as small as 8 p could be oriented using this procedure. The Kossel line patterns were interpreted using the charts developed by Rowlands and ~evis~ as generally

Jan 1, 1969

By Frank H. Macpherson

Few people realize the tremendously important part that Saline and Pulaski Counties in central Arkansas have played in the winning of the war The present favorable war situation might have been very different if we had not had the bauxite produced during the past two years from these two small areas, a total Of about 15 square miles. As a general statement, it can be said that the Arkansas bauxite deposits are, individually, relatively small, irregular in thickness, somewhat scattered and, therefore, compared with coal or iron-ore or open-pit copper deposits, relatively ill adapted to a rapid and drastic expansion in output. A few years ago it would have seemed an impossibility for these two counties to produce over six million long dry tons of bauxite in one year. However, with the cooperation of the operators, that is what happened in 1943, when the state of Arkansas achieved the seemingly impossible with a production of 6,020,684 1 long tons (dried equivalent) of bauxite ore during the calendar year, compared with an average annual production of 323,7252 tons in the period 1931 to 1941. It became apparent early in the year '94' that the united States soon might be drawn into the war, and, therefore, that an immediate study of the domestic metal situation was necessary. Aluminum is by far the most important metal used in the manufacture of aircraft and many other implements of war and it was evident that there would have to be a tremendous increase in the domestic production of bauxite, which is practically the only present source of this metal. AS more than 95 per cent of the known bauxite reserves of the United states was in Arkansas, careful preliminary studies were made in that state by representatives of the united States Bureau of Mines, the United States Geological survey and the War Production Board in the summer of 1941 Reserves in other states also were studied. The result of these studies was a recommendation by the War Production Board that mining in the bauxite.producing areas of Arkansas be geared for maximum production, in order to supply sufficient ore for this country's war requirements and, if necessary, to supply the war needs of Canada as well. The annual goal of eight million long tons (dry weight) set for Arkansas by the war Production Board was exceeded in 1943, when in August the output reached a rate equivalent to more than 8,300,000 long tons, dry basis. Because of the comparatively small tonnage of bauxite reserves, Congress appropriated funds for an extensive drilling program to be carried out by the Bureau of Mines in cooperation with the Geological Survey. Drilling began in May 1942 but owing to delay in delivery of drills, and trucks upon which the drills were mounted the program did not get into peak operation until early in 1943. By the end of July 1944, the Bureau of Mines records indicated an addition to the Arkansas reserves of 10,000,000 long tons (wet basis) in place,

Jan 1, 1946

Jan 1, 1965

By P. V. Faragher

A metal or alloy finds its place in commerce in proportion to its ability to serve certain purposes better and more economically than other materials. While there is some overlapping of the fields of application of the various metals under discussion in this symposium, each one has its uses for which it is especially adapted. While aluminum is the most recent of the metals to enter the field, the development of the industry has been based on its peculiar properties, by virtue of which new uses for non-ferrous metals have been created. There has been substitution of this new metal for other members of the group but there has been a far greater development in entirely new fields. In common with the other non-ferrous metals, aluminum is resistant to atmospheric corrosion. It also withstands the action of many of the common chemical reagents, strongly alkaline substances being the notable exceptions. The outstanding properties on which the application of aluminum is based are its low specific gravity and its ease of fabrication into the forms in which it is used. It is noteworthy that this property of specific lightness is retained in all the commercial aluminum-base alloys. This statement does not apply to aluminum bronze; this is more properly a copper-base alloy, since aluminum enters into its composition to the extent of only about 10 per cent. None of the commercial casting alloys of aluminum has a density exceeding that of the parent metal by more than about 10 per cent., and some are actually lighter. In the so-called "strong alloys" of aluminum in which strengths comparable to that of mild steel are developed by heat treatment, the greatest increase in density is only slightly more than 3 per cent., and one of these, also, is lighter than aluminum. This property of lightness combined with the desirable mechanical properties of the alloys, makes aluminum especially suited for parts of moving assemblies where saving in power, as well as a decrease in stresses resulting from inertia and vibration, are of importance.

PAUL D. FOOTE AND T. R. HARRISON, Washington, D. C. (written discussion *).-There are several methods for measuring the internal resistance of a battery, the line resistance in a circuit containing an e.m.f., or the true value of this e.m.f. The writers, however, were the first to em-ploy a simple principle whereby the total resistance of the circuit is ad-justed to a preassigned value for which the scale of the millivoltmeter is graduated, the only e.m.f. employed being that of the source measured. One of the simplest forms of these instruments is described on page 2842, September Bulletin. In papers now in the press we have described some twenty modifications of this simple design but all operating upon the same fundamentally new principle. The instrument devised by Mr. . Porter is of this general type but, unlike the designs we have recom-mended, is open to serious objections.

Jan 12, 1919

By B. K. Miller, George E. Moore

THE Missouri fire clays are here divided into plastic and semiplastic clays occurring as widespread bedded deposits in east central Missouri and flint and diaspore clays occurring as isolated "sink-hole" deposits in the north central Ozark region. Visual inspection was the first method used in clay prospecting. Thin overburden, hard sandstone "rimrocks," and the occurrence of diaspore float made this method particularly applicable in the flint and diaspore fields. The first drilling tool used was a hand auger. One man can drill 25 to 50 ft. per day at a cost of about 35 cents per foot. Holes can be drilled to a depth of 150 feet. Spud drills are often used where the over burden is hard. This drill uses a slotted earth socket bit. A two-man crew can drill about 100 ft. per day at a cost of about 35 cents per foot. Mechanically powered auger drills have been used extensively in wildcat drilling in the past few years. This type of drill furnishes a continuous set of cuttings. The practical depth limit with this drill is 50 to 60 ft. Two men can drill 300 ft. per day at a cost of about 20 cents per foot. Core drilling is used mainly to prove a known clay deposit. A two-man crew with a No. 22 Sullivan drill can drill about 30 to 40 ft. per day in soft clay, at a cost of about $1.25 per foot.

Jan 1, 1947

By Henry Rawdon

Cold-working is generally considered as a process of hardening metals. Diamet-rically opposite statements concerning the applicability of the scratch-hardness method in the testing of cold-worked metals, particularly after severe deformation, which exist in the technical literature led to the study of the results which are summarized in this paper. A series of metals, of which copper, iron and tin are used as illustrations here, were cold rolled to a definite degree without any intermediate annealing and the hardness determined by both the scratch and Brinell methods. The results indicate that the metal hardens rapidly during the initial stages of deformation; however, after a certain stage, which corresponds to a rather definite microstructure, the metal becomes softer and in its final form may be softer than the metal in its initial stage. As part of the study of the scratch-hardness method for metals and alloys in cooperation with one of the technical committees of the American Society for Testing Materials, the authors devoted considerable time to the study of the changes in hardness of metals when cold rolled. Various seemingly contradictory statements in the technical literature concerning the applicability of the scratch-hardness method to such cold-rolled materials were among the principal reasons for the investigation, the results of which are in part presented here. The effect of cold deformation, at least in moderate degrees, on the hardness as measured by the Brinell and other common methods is so well known that further reference is unnecessary. Concerning the scratch hardness of cold-worked metals, Martens and Heyn state' that hardness, whether measured by the ball-pressure method (Kugeldruck) or by the scratch method (Ritzverfahren), will be increased by cold deformation. Jeffries and Archer give a seemingly diametrically opposite view. They state,2 that "the sclerometer (indicating scratch

Jan 1, 1924

By W. R. Aufricht, E. H. Koepf

The theory, measurement, and application of capillary forces in reservoir rock have been treated ex-tensively in the various petroleum publications.1,2,3,4 These forces are of prime importance in oil production, and data on capillary properties are among the most important tools used in the study of reservoir mechanics. The principal application of measured capillary pressure data by the production and reservoir engineer is in the determination of the initial distribution and mobility of fluids in the reservoir. The distribution refers to the magnitude of the oil and interstitial water saturations under capillary equilibrium conditions and to their variation throughout the reservoir as a result of changes in rock properties and nearness to free water. The magnitude of the water (or oil) saturation, as well as the porosity, is required in volumetric calculations of oil in place. In low permeability reservoirs, where long transition zones are common, the magnitude of the oil content, even below the depth interval where commercial rates of flow of oil can be obtained, must be evaluated since this oil contains energy available to the production of the remainder of the reservoir. The mobility of the water phase is of particular importance in water-flood calculations since mobile water may condemn what would otherwise be a successful water flood. In reservoirs with predominantly small pores, high immobile water contents are possible. Conversely, reservoirs with predominantly large pores may contain mobile water even though the interstitial water contents are relatively low. This presentation reviews the distribution and mobility of interstitial water contents as determined from capillary pressure data and shows typical data for various types of carbonate reservoirs. A discussion of the variations found in different types of carbonate reservoirs is given. DISCUSSION Interpretation of Laboratory Data Fig. 1 is a typical laboratory capillary Pressure curve where water saturation as Per cent of Pore space is plotted vs capillary Pressure (psig) for an air-water system. This par- ticular curve was obtained by measurement on a sample of San Andres dolomite with intergranular-type porosity. The sample studied had a permeability of 10.0 md and a porosity of 18.8 per cent. The capillary pressure-saturation relationship illustrated is an inherent property of the rock (a function of the size and distribution of the pores) and represents the ability of this water-wet rock to retain water against the pressure differential exerted by a non-wetting fluid (oil or gas) to remove it. In the laboratory a known pressure differential is exerted from a pressure source; in the reservoir the pressure differential is controlled by the density difference between the hvdrocarbons and the water. The laboratory capillary pressure values may be converted into terms of equivalent height of water column using known values of reservoir oil and water density and measured or average values of interfacial tension

Jan 1, 1958

The papers presented at the International Congress, held in San Francisco, Cal., Sept. 20 to 25, 1915, are published in 11 volumes of Transactions. In addition, an index volume is published, containing .besides the author and title index, a report of the business meetings of the Congress, and a brief digest of each paper presented. The following is a schedule of the volumes: Index and Digest.-General proceedings, indexes and digests. Vol. I. Panama Canal. II. Waterways and Irrigation. III. Municipal Engineering. IV. Railway Engineering. V. Materials of Engineering Construction. VI. Mechanical Engineering. VII. Electrical Engineering and Hydro-electric Power Development. VIII. Mining Engineering. IX. Metallurgy. X. Naval Architecture and Marine Engineering. XI. Miscellaneous. Aeronautics; Refrigeration; Agricultural Engineering; Engineering Education; Heating and Ventilation. Remember the New York Meeting, Feb. 14 to 17, 1916.

Jan 12, 1915

By F. N. Rhines, A. S. Nemy

The mode of high-temperature tertiary creep of 523-0 aluminum alloy was found to be strongly stress dependent. The occurrence of necking and/or fissures during tertiary creep exhibited a sequence with varying stress, wherein fissures with no necking occur at a minimum stress and necking with no fissures occur at a maximum stress. At an intermediate stress, tertiary creep begins without necking but with fissures in a region just beneath the external surface, followed by necking and the development of fissures along the axis of the specimen. The results are interpreted in terms of grain boundary gliding and the hydrostatic stresses produced by restraints to grain boundary gliding. THERE appear to be two possible reasons for the existence of a period of accelerating elongation prior to rupture during high-temperature creep in metals; namely, 1) a change in the structure of the metal itself, leading to a change in its response to loading, and 2) a reduction in the cross section of the metal resulting in a higher unit loading. Howe,' by annealing and retesting broken low-temperature creep specimens, found that irreparable damage is done once a metal is subjected to creep. Andrade2 first pointed out the association between the reduction in cross section and the increase in creep rate. The present research was designed to investigate both of these factors by retesting specimens machined from material which had been subjected to high-temperature creep testing short of rupture. EXPERIMENTAL METHOD An aluminum alloy, 52s-0, was selected for these studies because it is constitutionally simple, is strong enough to be relatively insensitive to mechanical damage during machining,3 and undergoes accelerating creep in a convenient temperature range. This alloy is hardened by 2.6 wt pct Mg in solid solution and is not subject to overaging effects; it has a very small quantity of an insoluble impurity phase, Mg2Si, finely dispersed throughout its micro-structure. Creep specimens, similar in design to ASTM 0.252-in. tensile specimens, were machined from 3/4-in. round stock and the surfaces were electro-polished. A 24-hr anneal at 500°C was then applied to stabilize the grain size to an average diameier of 0.27 mm. Subsequent heating for as long as 700 hr at the intended test temperatures produced no change in the tensile properties, indicating a well-stabilized state of the material. Corresponding to each of the typical testing conditions listed in Table I, one creep specimen was tested to destruction and this test was employed as a guide in the selection of times for subsequent tests. Duplicate creep tests were then run to various points along the creep curve to produce specimens which were used to determine changes in mechanical properties and microstructures. The latter were examined at the midsections of the specimens. Other specimens were tested to various stages of tertiary creep, after which they were remachined to new cylindrical test specimens, electropolished and re-tested in creep. RESULTS The major findings of this investigation may be illustrated by a comparison of the results of three sets of creep tests. These were run at 400°C at three stress levels, namely 750, 1000, and 1500 psi. In presenting these results in Figs. 1, 5, and 8, the creep curves are given in pairs: That curve of each pair which is drawn through filled circles corresponds to the initial test, and the curve drawn through open circles (and designated by - R) represents the result of retesting the same specimen after machining to a new cylindrical surface. The load was readjusted to the original unit stress at the beginning of each retest.

Jan 1, 1960

By John T. Crawford

Much has been written of late regarding the flotation of coal as a means of reclaiming the valuable portion of the fines encountered in nearly all methods of coal preparation. Whether the process be wet or dry, whether the dust be sent through the entire process or removed prior to the cleaning by some such method as screening or aspiration, one of the final products consists of a considerable proportion of — 48-mesh material. The percentage of this —48-mesh material depends upon the mining method, transportation, storage, and method of preparation. The tonnage of this dust material ranges from 1 to 10 per cent of the total output of the cleaning plants. Four methods of disposal are available for this coal: 1. Disposal with the refuse from the plant. 2. Addition, after being reclaimed from the wash water, or dust collectors, without cleaning to the larger sizes. 3. Separate disposal as a pulverized fuel. 4. Cleaning so that addition to the larger sizes benefits the product as a whole. It is also true that flotation in one form or another is the only known way to effectively clean this material. While some processes do a reasonable cleaning job down to and including +l00 mesh, by far the greater majority stop at or short of the + 48-mesh size. Much of the literature on coal flotation passes by the fred pulp density and size by merely stating that the feed varies from 20 to 30 per cent solids and that the size range is from — 1/4 in. or — 1/8 in. to 0. Small wonder then that some operators with entirely different conditions, and not knowing the machine capacity, throw up their hands in despair when flotation is mentioned. Too much parallel is drawn between flotation methods as applied to ores and as applied to coal, to the detriment of the latter. In the flotation of metalliferous ores the feed pulp density ranges from 20 to 30 per cent solids, depending upon the amount of mineral to be floated and upon the size analysis. Thus where 2 to 5 per cent of the

Jan 1, 1936

By C. B. Dudley

IN the spring of 1877, the Pennsylvania Railroad Company became so dissatisfied with the average life and wear of the steel rails it was then able to procure, that it determined to make an investigation into the chemical composition and physical properties of steel rails, with a view, first, to answering the question why one steel rail has to be removed from the track after, perhaps, eight months' service, while another lasts ten years ; and, secondly, if this investigation succeeded in throwing light on this important subject, to use this information in securing better rails in the future. The results

Jan 1, 1879

By B. H. Bergstrom, C. L. Stevenson

In any process wherein materials must be pelletized, a crucial period exists during the interval between the manufacture of the green pellets and their subsequent heat treatment. The pellets must possess sufficient strength and plasticity to withstand conveying and sizing. Also, they must be neither excessively brittle nor excessively plastic when placed in a bed on a traveling grate for heat treatment. An acceptable pellet, in the event sufficient forces are applied to cause its fracture, will merely split into two or three large fragments which would not drastically alter the permeability of the pellet bed. However, when brittle pellets are broken, they shatter so that the resultant fine particles either decrease the perimeability of the bed or become entrained in the gas stream and thereby cause dust problems. On the other hand, excessively plastic pellets may not break at all but may merely flatten. This would seriously hamper bed permeability. In the past, pellet evaluation has usually been left to the creative and artistic talents of the balling operators. A multitude of techniques have evolved, of which the most common is the simple compression test. For this test a hand-operated device loads single pellets to fracture, but reliability is strictly operator- dependent. Probably the next most common test is the drop test, which is conducted according to several different procedures. This is an important quantitative test for estimating the amount of handling a pellet will withstand. There are many other tests, such as pinching a pellet between the thumb and index finger, but none are capable of producing reproducible results.

Jan 4, 1962