By Jesús Contreras

Within its programme for continuous improvement and cultural change, Atlantic Copper has installed the Six Sigma methodology as a basic tool for the improvement of management techniques in all its production centres. Following an implementation period, the methodology is widely used for analysis and improvement, not only in the fields of production and maintenance, but also in other areas of the business such as supplies or energy management. The present paper describes, phase-by-phase, the project that was developed to improve the quality of converter slag through the application of Six Sigma techniques, from the initial set up to the final results obtained.

Jan 1, 2005

By Liow Jong-Leng

A survey of the interactions of large gas bubbles formed from top and bottom injection of gases into melts was carried out. Spherical cap bubbles were found not to produce much splash when they break through the bath free surface except for that formed by plunging of the-spout at its edges. In contrast, the bursting of balloons produces cavities which give rise to liquid jets being ejected from the bath free surface. The position of the balloons relative to the bath free surface is an important parameter in the formation of the liquid jet. It is found that the interactions of multiple bubbles close to the free surface is important in determining the splash behaviour of gas injected systems.

Jan 1, 1996

By Dieter Neuschiitz, Pengfu Tan

"In order to understand the sintering phenomena during iron ore sintering process, a CFD model of iron ore sintering has been developed, combining with the kinetics of 15 relevant chemical reactions with the aim of describing the temperature fields and the gas flow patterns in the sintering bed. This CFD model can be used to simulate the concentrations of the gaseous and solid species, temperatures of the gas and solid, melting and molten fractions of the mixture, gas velocities, temperature zones and residence times of the gas in each temperature zone. IntroductionThe off-gas analyses clearly revealed that the off-gas of a sinter strand does not have a composition corresponding to thermodynamic equilibrium, for example, the CO, CO2 and O2 concentrations are not the mutually consistent equilibrium values. Apparently the chemical reactions in the sinter bed are controlled kinetically. Therefore kinetic modeling of sintering reactions combined with CFD modeling is necessary to understand the sintering phenomena during iron ore sintering process.Several models of iron ore sintering have been developed since 1970 [l-l 4l, each being more refined than its predecessor. The models were formulated as a series of differential equations to describe chemical and physical changes occurring at a point in the bed. These equations were solved numerically in a vertical plane along the strand. The present CFD model, based on the Nath's model [14], has been published in the reference [15]. In this work, some new chemical kinetic models of gas-solid reactions are incorporated in the present CFD model. The concentrations of gaseous and solid species, temperatures of gas and solid, melting and molten fractions of solid, velocity of gas, and residence time of gas in each combustion zone can be calculated by this model."

Jan 1, 2004

By Dean Ilievski

Mathematical modelling of the precipitation process requires that the kinetics of crystal growth, nucleation and agglomeration be known: This paper reviews the current state of knowledge on these precipitation sub-processes (ie. growth, nucleation and agglomeration) and describes a number of experimental techniques for estimating their kinetics. The experimental methods used to generate the precipitation data and the data analysis techniques used to extract the kinetics information from the data are discussed separately. There is no universal "best" technique for determining the kinetics. However, studies on multi-crystal systems are more reliable for modelling purposes than are single crystal studies. The selection of a technique will depend on which sub-processes are present. A problem with all kinetics studies is that there is generally a large uncertainty in the estimated kinetic parameters. This stems from the scatter in the experimental data being further propagated by the mathematical techniques used to extract the kinetic parameters.

Jan 1, 1996

By R. Altman

A Brookfield viscometer fitted with a stainless steel bob was used to measure the viscosity of industrial lead blast furnace slags between 1126 and 1298°c. Slag oxidation state was characterized by first annealing the? slag samples at 750°c in sealed copper tubes in order to precipitate magnetite crystals. The magnetite concentration was then measured on an Outokumpu Saturated Magnetic Analyzer. Using an Arrhenius-type equation, a viscosity model was developed by regression. The equation below accounted for 75% of the variability in the data used to generate the regression coefficients and, on average, could predict viscosity within ± 12% of the measured value. The greatest difficulty encountered in measuring viscosity was due to the occasional presence of solids in the slag which caused, at times, erroneously high viscosity measurements. Precautions to minimize this problem are outlined in the text.

Jan 1, 1985

By S. Seetharaman, Du Siehen

"In the processing of molten metals, it is extremely important to monitor continuously the concentration levels of various minor elements. In the production of common metals like copper, iron and aluminium electrochemical sensors involving solid as well as liquid electrolytes are being increasingly used to measure the concentrations of minor elements. The present paper deals with the electrochemical principles underlying these measurements and the possible errors involved. One of the major difficulties in the case of the solid electrolytes is to correct for the consequences of the electronic contribution to the conduction of the electrolyte.The application of the electrochemical sensors for molten metals processing involves designing of these probes to withstand the industrial operating conditions. In this respect, significant achievements have been made with respect to the design of oxygen probes for liquid metals in general and liquid copper in particular. Some of the salient design features are discussed in the paper. The application of auxiliary electrodes for impurities in molten metals like phosphorus in copper and silicon in iron are taken up. The development of oxygen sensors for slags is given special attention. Recent developments in the field of sensor technology, as applied to metals processing are highlighted.1. IntroductionThe rapid technological advancement today require precise control of the process parameters and the impurity levels. Most of the molten metals processing in industrialized countries are often steered by suitable computer models, either phenomenological or simulations based on theoretical principles. These models often require that the process parameters are continuously monitored so that the progress is followed and modified suitably as and when required. It is common practice to measure temperatures by incorporating temperature sensors at the various strategic points of the reactor. In the case of monitoring the composition changes in the various phases, the method of sampling followed by routine chemical analysis involves a time lag as well as uncertainties in sampling and analysis. In this respect, electrochemical sensors have the advantage of generating accurate data when properly applied and increasing attention is being paid in the development of electrochemical sensors for various common species in molten metals processing. In the present paper, the developments in this area over the years are outlined and typical process applications are discussed. A greater emphasis will be laid on sensors based on oxygen conducting electrolytes and their application to the production of common metals like iron and copper."

Jan 1, 1996

By J. P. Bellot

During the non-ferrous metal processing, the melting step under vacuum or under rarefied gas leads to volatile metal losses. It is the case of the metallurgical processing of the nickel-based, titanium-based or zirconium-based alloys where the evaporation losses don't allow a sufficient control of the alloy chemical composition. A theoretical approach has been carried out involving both a continuum description in the liquid phase and a molecular approach in the rarefied gas phase. The finite volume method is used in order to solve the coupled transport equationsin the liquid, whereas the Boltzmann equation is modelled by using a Monte Carlo method. At the liquid metal and metallic vapor interface, the volatilization and recondensation fluxes link up the two calculations. Simulation results are given for the melting and refining of reactive metals such as titanium alloys where the control of the chemical composition remains a major difficulty. The validity of the kinetic Langmuir's law is discussed for different operating conditions.

Jan 1, 1996

By Stephanie Trant

Montana Tech has been engaged in fundamental research on the processing of critical materials for more than a decade. Efforts include examining novel reagents for the flotation of Rare Earth Minerals (REMs). For this paper, research results on a collector, salicyl hydroxamic acid (SHA), are presented. Various REMs were examined and include the rare earth oxides (REOs), carbonates (RECs), and phosphates (REPs) of a suite of Rare Earth Elements (REEs). Differences are attributed to solution and surface chemistry, coordination number, and ionic diameter. SHA adsorption follows an ion-exchange process that leads to chemisorbed and surface-precipitated states, depending mostly on pH. Many effects are directly attributed to lanthanide contraction. Results should also be applicable to other REM/collector systems and further suggest that REM flotation should consider dual collectors.

By Asmo Vartiainen

Background of Direct-to-Blister Flash Smelting is discussed; especially slag chemistry relating to copper solubility, slag fluidity and impurity behavior. In December, 2000, Mini-pilot Flash Smelting test runs were carried out at Outokumpu Research Oy to produce blister copper from Chilean concentrate and white metal and from a mixture of them. Tested slag types were iron silicate slag, ferrous calcium silicate slag and calcium ferrite slag with different slag compositions and different concentrate/white metal ratios. The test runs were successful. The fluxing effect of copper oxide was clearly demonstrated and ferrous calcium silicate slags remained fluid on a very wide liquidus range. The distribution of arsenic between ferrous calcium silicate slag and blister copper is much higher than between iron silicate slag and blister copper. This successful test run with the new slag type offer new possibilities in Direct-to-Blister process design.

Jan 1, 2003

By Kenji Matsuzaki

A mathematical simulation model of the Imperial Smelting Furnace operation has been developed for purpose of improving the furnace operation. The model consists of top, shaft and bottom regions, Analysis in the shaft region is based on differential heat and materials balances taking account of reaction kinetics and heat transfer rates, and those in the top and the bottom regions are based on heat and materials balances under a steady-state condition, Longitudinal distributions of process variables such as temperatures of gas, sinter and coke, gas composition and fractional conversion under a practical operating condition were calculated, With this model, the furnace performance under various operating conditions also can be shown reasonably predicted,

Jan 1, 2003

By R. L. Nyirenda

One of the problems with ammoniacal-ammonium carbonate leaching of EAF carbon steelmaking flue dust is that zinc present in spinel phases is not leached. This paper presents results of test work in which prior to leaching, EAF dust was reduced with CO containing gas to decompose the spinels into zinc oxide and iron bearing phases, mainly metallic iron and wustite. From such reduction products, the amount of zinc leached increases but the iron co-leached becomes extensive. The effect of various leaching parameters such as liquor concentration and redox potential on zinc and iron dissolution has been investigated. Supplementary experiments utilizing pure zinc oxide and pure iron phases were also carried out. Results show that the co-dissolution of iron from severely reduced EAF dust cannot be prevented. This is because the wustite phase contains zinc which can only be leached when iron also dissolves. Further, the zinc bearing wustite phase is not totally soluble so that the residue cannot be made zinc free. In the absence of air, dissolution of metallic iron hardly occurred, though in leaching experiments of a long duration its transformation to a spinel structure was observed.

Jan 1, 1992

By Alessandro Blasi, Massimo Morgana, Corradino Sposato, Pietro Garzone, Giuseppe Devincenzis

A comparison among (2-ethylhexyl)-mono (2-ethylhexyl) ester Phosphonic acid (P507), Secondary-octyl phenoxy acetic acid (CA-12) and Bis(2,4,4-trimethylpentyl) phosphinic acid (Cyanex272), in heavy rare earths separation via hydrometallurgical processes has been investigated. The separation coefficients, , were obtained and the extraction selectivity has been evaluated using a mixture of heavy rare earths from Samarium to Ytterbium. The experimental results indicated that P507 and Cyanex 272 display a greater affinity for heavier rare earths while CA12 proved to be more effective for the lighter rare earth metals.

Jan 1, 2014

By Edward Rosenberg

The synthesis and characterization of silica polyamine composites modified with a variety of sulfur containing ligands is described. The two most successful ligands in terms of sulfur in-corporation and mercury capture are ethylene sulfide and carbon disulfide. The ethylene sulfide forms either an amino mercaptane or a polysulfide upon reaction with amino groups on the composite. The carbon disulfide undoubtedly forms a dithiocarbamate functional group upon reaction of the amino group under basic conditions. Both materials posses excellent capture kinetics and capacities for mercury, Once captured, the mercury is extremely difficult to remove from the composite materials, even with concentrated acids, and they easily pass the TCLP test. The materials are compared with related thioether modified silica polyamine composites and appropriate potential applications are discussed.

Jan 1, 2003

Proposed by outstanding electrochemist and electrometallurgist Prof. Raphael Agladze (191 1- 1989), process of copper and manganese co-electrowinning was enhanced to the pre- electrowinning stages: low,temperature co-leaching of copper and manganese containing materials, and to high-temperature co-roasting of the same materials with consecutive leaching. The report presents results of experimental investigations of the processes mentioned above, as well as results of thermodynamic investigations of co-roasting processes, and co- leaching processes computer modeling.

Jan 1, 1997

By J. P. Hager

The formation of the vapor complex AgFeC14 (g) baa been identified and its thermodynamic properties determined. The vapor pressure of silver chloride can be enhanced by a factor of 15-20 due to the formation of the vapor complex. The vapor pressure of both AgCl (g) and AgFeC14(g) were measured using a double-zone transpiration .technique. Gibbs free energies have been determined for the vapor transport reactions. Laboratory kiln tests were conducted to confirm the enhanced recovery of silver through the formation of the AgFeC14(g) vapor complex and to indicate the opportunities for process development using this new vaporization chemistry.

Jan 1, 1985

By Ken-ichi Machida

"Surface modification of R-Fe-N intermetallic compounds was made to improve their magnetic property and nitrogenabsorbing ability, arid high-performance resin-bonded magnets and nitrogen storage materials were developed: Surface coating for Sm2Fe11Nx by the zinc metal produced via photodecomposition of Zn(C2Hs)2 was effective to avoid the further oxidation in the molding process of the fine powders for bonded magnets and the resulting (BH)max values were improved to -186 kJm-3. Meanwhile, R2Fe17 as the mother compounds for RzFe11Nx was highly active for decomposition of NH3 molecule and subsequent nitrogen absorption as metal nitrides. Furthermore, even inert Nz molecule was dissociated on them by impregnating Ru metal and the resulting nitrogen atoms were absorbed in the crystal lattice of R2Fe17. These results demonstrated that the nitrogen storage system was established by cycling the nitrogenation and hydrogenation of RzFe11/R2Fe11Nx materials.IntroductionProcessing for rare earth metals and intermetallic compounds requires well-controlled conditions in order to avoid the oxygen contamination involved in it due to their high reactivity, as causes the serious damage for materials such as magnets, metal hydride for hydrogen storage, and so on. Rare earth-iron intermetallic compounds, R2Fe17, provide the corresponding metal nitrides (R2Fe11Nx) by heating in N2 or a mixed gas stream ofNH3-H2 [l] and, among them, Sm2Fe11N3 has been particularly noted as one of the promising materials for high-performance permanent magnets such as bonded ones [2- 6]. Usually, the nitrogenation for Sm2Fe17 is made in Nz, but it needs the much more hard conditions of reaction pressure (-10 MPa), temperature (-550°C) and time (-72 h) than the nitrogenation in the NH3-H2 mixture [l]. In the latter case, a significant amount of nitrogen can be interstitial introduced in· the R2Fe17 crystal lattice (x=-7) under the more moderate conditions than in N2 (at 0.1 MPa and -450°C for -3 h) [3-6] and then, in a similar manner as metal hydride systems [7], the excess nitrogen in RzFe1 7Nx (x>3) is reversibly desorbed by heating at a temperature around 500°C in Ar to form the RzFe11N3 compounds. This behavior of nitrogen absorption and desorption has a close relation to the sites for nitrogen in the crystal lattices."

Jan 1, 2000

By K. Moriyamo

Operation improvement efforts at Hyuga Smelting Co., Ltd. have focused on calcining capacity in the reduction rotary kilns ("the kilns"), whose limited feed rate capacity had capped production at around 18,000t-NiN since 1995. To improve the kilns' feed rate capacity of 80 wet t/hr, attempts were made to increase the gas flow in the kilns by increasing the capacity of the off-gas fans. However, as the increased gas flow resulted in only limited improvement of the kilns' feed rate, a scoop feeder was installed on each kiln to add coal to the middle of each kiln's interior to gain a higher efficiency of thermal supply and conversion. With these gas flow and coal charge addition operations, the kilns' feed rate capacity increased up to 120 wet t/hr, with burner fuel efficiency increasing by approx. 10% (approx. 5% in total with the additional coal included). As a result, production was raised to a level of 22.000t-Ni/Y Keywords: reduction rotary kiln, scoop feeder, additional coal charge.

Jan 1, 2004

By F. Kongoli

Viscosity is an important parameter of copper smelting and converting processes. It affects the settling of matte or metal droplets in the slag, distribution of elements etc. Despite this importance, confusion exists on the viscosity of copper smelting slags as a result of disagreements found among the measured viscosity data of several authors especially in the slags of high ferric iron content and close to magnetite precipitation. In this work a critical review of the existing data on the viscosity of copper smelting slags has been first carried out and the effect of oxygen potential on the viscosity of copper smelting slags has been clarified through a coupled quantification of viscosity and liquidus temperature. The confusion in the literature has been clarified and the importance of the relation between the viscosity and the liquidus temperature is discussed.

Jan 1, 2003

By Gaballah I.

Elimination of arsenic, mercury and zinc from synthetic solutions containing H;\A.sD4. HgCI2 and ZnCI2 using modified barks was investigated. The pH range was varied from ?1 to 10. The initial concentrations of individual element were 10,100 and 1000 ppm. More than 99 % of mercury and 65 % of zinc cations were removed by the modified bark .. In this case, the modified bark reacts as a cation exchanger leading to the release of ' two protons for every HgII or ZnII fixed by this material. About 30 % of arsenic was eliminated from the solution. This 'low efficiency could be attributed to? the presence of arsenic ,as. anion. Decontamination of a treated industrial effluent containing 4 ppm of ion? metals was performed on a pilot plant scale by the modified bll(k. More than 70'% of these ion metals were eliminated.

Jan 1, 1995

By Young-Dae Kim, Dong-Sic Kim, Jong-Jin Pak, Kyung-Hyo Do

"Sulfur is one of the most harmful elements in stainless steel (SIS) products and the specification of sulfur content is getting more severe for high grade SIS. In order to accurately control the desulfurization reaction in high chromium containing SIS melts, it is important to know the thermodynamic interaction between chromium and sulfur in Fe-Cr melts over a wide range of chromium content. In this study, the equilibrium sulfur distribution, Ls, between a Ca0-Alz03 slag and Fe-Cr-C,.,-S melts were measured under CO atmosphere in the temperature range of 1823-1923 K. The specific effect of chromium on the activity coefficient of sulfur in the melts was determined with the consideration of carbon effect on sulfur. A separate experiment was carried to determine. Ls between a slag and FeCr- S melts (Cr: 0-30 mass%) at 1873K to check the validity of the thermodynamic parameter determined in the present study.IntroductionFerritic stainless steels containing chromium (Cr) up to 30 mass% have been developed for a good corrosion resistance and a high formability to replace austenitic SIS. Especially, Sulfur (S) causes a reduction of high-temperature strength and the hydrogen induced cracking (HlC) in stainless steel for line pipes. [l]Many studies on the desulfurization of hot metal and liquid steel have been carried out for several decades and they used HzS-H2 gas equilibrium technique for measuring the effects of many alloying elements on the activity coefficient of S in liquid iron. However, the study on desulfurization of Fe-Cr melts was very scarce.[2] In order to accurately control the desulfurization reaction of high Cr stainless steel, it is essential to know the thermodynamic relation between Cr and S in Fe-Cr melt over a wide range of Cr content and temperature.In the present study, the thermodynamic interaction between Cr and S in liquid iron was determined by measuring the equilibrium distribution ratios of S between Fe-Cr-C,.1-S melts containing a wide range of Cr up to 30 mass% and a 55 mass%Ca0-45 mass%Alz03 slag of which the sulfide capacity was pre-determined using Fe-C,a1-S melts in the temperature range of 1823-1923 K. The validity of thermodynamic parameter determined in the present study was checked by measuring the S distribution between a Ca0-Alz03-Mg0 slag of known sulfide capacity and liquid Fe-Cr-S alloy at 1873 K. Using Wagner's formalism, the results of experiment were thermodynamically considered to determine the effect of a specific concentration of Cr on the activity coefficient of S in liquid iron."

Jan 1, 2014