Search Documents

By J. P. R. deVilliers

A procedure is described whereby gold-containing calcined concentrates and leach residues from refractory gold ores are smelted with carbon to form a small amount of metal. The gold is liberated upon smelting, and is collected in the molten metallic phase, which is easily separable from the slag. The metallic phase consists of approximately 1 to 15 per cent (by mass) of the material after smelting, and the gold content is generally upgraded by a factor of greater than 6 compared with that of the original roasted material. Recoveries better than 95% have routinely been achieved. The quenched metal contains predominant Fe-Ni alloy, as well as minor Fe sulphides and Cu-Fe sulphides. Trace amounts of Fe-Ni arsenide and Au-Cu alloy are also present. The gold content of the metallic phase can be increased further by oxidation of the hot metal in the presence of silica or slag. This will reduce the amount of metal, and will concentrate the gold in a smaller volume. The metallic phase can then be treated hydrometallurgically to recover the nickel and the gold.

Jan 1, 1989

By Santo Ranieri

We will briefly review the nickel market in 2003 and look forward to the supply demand balance for the next few years focusing in on the key factors influencing future price dynamics. On the supply side we will examine slated brownfield and greenfield expansions including the Norilsk factor and the small to mid-range 'supply creep'. We will also review the cost side of the industry and what to expect going forward. On the demand side, we will discuss the stainless steel and non-stainless demand, the China factor and the stainless steel scrap supply cycle. We will conclude by pinpinting where the market is on the current price cycle, and where we believe the mid-term direction is headed.

Jan 1, 2004

By Sergey Komarov, Manuela Diaz, Sano. Masamichi

"Mixing time, bubble behavior and absorption rate of gas injected into a liquid bath through rotary L-shaped lances have been studied by cold models with an effort to improve refining characteristics of metallurgical processes. Two kinds of the rotary lances were tested, namely the single-hole lance and the multi-hole lance. The effects of gas flow rate, bath depth and rotation speed were examined.It is found that when gas is injected through the rotary lances, the mixing intensity and the gas absorption rate are larger than that for the gas injection through stationary lances. The effect of rotation speed decreases as the bath depth and the gas flow rate increase.The multi-hole lance produces much smaller bubbles, which lead to an increase in the volumetric mass transfer coefficient by 3-4 times as compared with the single-hole lance. However, the effect of rotation speed is smaller for the multi-hole lance. The obtained results are explained in terms of the bubble coalescence and fragmentation, the rate of which depends on the departure bubble size and the power supplied to the liquid bath.IntroductionIn recent years, there has been a growing interest in the development of gas injector for metallurgical processes. The majority of the previous work was focused on modification to the injector design to improve mixing and to increase the of chemical reaction rate. These two goals can not be necessarily achieved by the same way. Bottom nozzles and stationary immersed top lances, which have been widely applied to steelmaking processes, are effective for the bath mixing, but have a limit to decrease in the bubble size. This results from a vigorous coalescence occurring between the bubbles when they rise in the molten bath as a bubble swarm.One of the ways to ensure the small bubble size and the effective bath stirring is the gas purging through rotary injectors. A number of studies have been undertaken to improve the refining characteristics by using rotary injectors. All of them are related to aluminum refining. The SNIF equipment (The Spinning Nozzle Inert Flotation) has significantly improved the quality of aluminum products at National Luxemburg Aluminum [1]. Rotary injectors made in the form of a disc have been applied to the Alcoa 622 [2] and the GBF processes [3]. A study of the gas injection by a rotary impeller has been carried out by C. Leroy and G. Pignacelt [4]. All researchers note the significant improvement in removal of sodium, calcium, hydrogen and non-metallic inclusion."

Jan 1, 1996

By Lin Yang, Minjun Tang, Shuishi Liu, Jianfeng Zhou, Linjiang Qing, Xiaolei Song, Yufeng Guo, Tao Jiang

"The dynamics of oolitic hematite magnetic roasting was studied. The results show that oolitic hematite magnetic roasting was controlled by the internal diffusion, and the diffusion coefficient was 9.018x10-7 m2·s-1when the oolitic hematite was roasted at 650°C. Magnetic susceptibility improves when temperature increases and roasted time prolonges under the condition of roasting at 650°Cfor 50min, with the magnetic susceptibility is 39.88%. CaF2 and Na2C03 can significantly improve the magnetic susceptibility at the same roasting condition, and the magnetic susceptibility was 63.35% and 57.99% respectively, thus the reduction of oolimic hematite was promoted.IntroductionWith the continual depletion of free-milling iron ores and its rising price, developing the abundant resources of oolitic hematite has become one of the main research areas. The oolitic hematite accounts for 10% of China's iron ore reserve, and it also accounts for 30% of red ore reserve in China [1]. In order to exploit the oolitic hematite, there are many beneficiation research methods, including fine grinding/selective flocculation/high intensity magnetic separation or flotation, high-gradient magnetic separation, low intensity magnetic separation/high intensity magnetic separation/reverse flotation, chloridizing roasting/acid pickling, magnetic roasting/leaching process etc [2]. However, the oolitic hematite is easy to slim and the valuable mineral is covered by the slim, because of the tiny granule of value mineral, then the ooides are formed due to the state of layer morphology formed by iron ore and ganaue minerals [3, 4]. Fairly good separation indexes were hard to be obtained by traditional separation due to its structural features, so the magnetic property of the iron minerals will be changed with the use of the magnetic roasting [5, 6], which result in hematite variably altered to magnetite and simplified technological process so that a good separation indexes will be obtained by using the low intensity magnetic separation. Therefore, in order to provide theoretical direction of how to use the oolitic hematite effectively through the magnetic roasting, the oolitic hematite of GuiZhou province was studied, which emphasized on researching the dynamics of oolitic hematite magnetic roasting."

Jan 1, 2013

By Frank M. Kimmerle

Spent Potlining (SPL) contains recoverable chemical elements (C, F, Na and Al) which are lost in stabilization or immobilization processes primarily aimed at eliminating cyanides and reducing leach rates of soluble fluorides prior to landfiling. They can be recovered in a variety of mineral forms for recycling in the aluminum industry and elsewhere. Alcan has developed a cost-effective hydrometallurgical route, combining a number of proven unit processes to destroy cyanides, recycle the chemical values and provide a zero-discharge process. Pilot plant studies of this Low Caustic Leach and Liming (LCL&L) Process prove that the fluoride scan be converted to acid grade fluorspar, while the sodium and aluminum are recovered as a sodium aluminate and caustic feed to the Bayer Plant operations. The remaining brick and carbon fraction constitutes a high ash solid fuel which meets TCLP leach criteria and whose reduced sodium content enhances its value as a chemical reducing agent.

Jan 1, 1994

By W. G. Davenport

H20 is present in many flash furnace inputs. Examples are: (a) moisture in concentrate and flux (b) humidity in blast (c) moisture in hydrocarbon fuel, particularly coal, Appendix IV. H20 may also leak into the furnace from damaged water-cooling jackets. H2O, especially that it be included H2O, exerts a strong cooling effect on the flash furnace. It is important our calculations. As will be seen from the calculations, gaseous and liquid H2O both increase flash furnace industrial oxygen and oil requirements. This is because gaseous H2O (humidity in blast) must be heated from its input temperature to the flash furnace off gas temperature. Liquid H2O must be evaporated and heated.

Jan 1, 2001

By Rashmi Kumar, Amit Chatterjee, Sanjay Chandra

The practice of adding alloying materials to a molten bath is an integral feature of many pyrometallurgical operations. However, very little is known about the dissolution rate and solution mechanisms of solid additives in liquid melts. In foundries where large tonnages of liquid metals are handled, there is considerable interest in achieving optimum metal quality at minimum cost. This objective is influenced by several factors and the solution is often plant specific. Though the amount, sequence and mode of ferroalloy addition vary from plant to plant, various fundamental factors determine how quickly these additions dissolve in the bath. At the Ingot Mould Foundry (IMF) in TATA STEEL blast furnace hot metal is used to cast ingot moulds. The composition of hot metal desired for making ingot moulds demands addition of 20 kg each of Ferromanganese and Ferrosilicon in the 12 T transfer ladles into which the blast furnace metal is poured at the IMF. Owing to low temperature of hot metal at the IMF, casting commences immediately and complete dissolution of the ferroalloys is often not possible. To study this aspect in detail and to evolve suitable corrective measures, a mathematical model for the melting of a solid particle in a liquid metal bath was developed at TATA STEEL. The model was validated using the data available in literature. In keeping with published work, two separate dissolution periods were identified - a "shell period" and a "free dissolution period". The maximum thickness of the crust formed around a spherical particle shortly after immersion, can be obtained by using the mathematical model which has been developed. The model can also be used to investigate the effect of various parameters such as superheat of the bath, size of the particle, etc., on the maximum crust thickness and the particle melting time. On the basis of this study, the addition of ferromanganese and ferrosilicon was optimized at the IMF in Tata Steel.

Jan 1, 1996

By Di Yang

The influence of high density (104 -105 A/cm2) electric current pulses (70 us duration) and continuous DC (~103 A/cm2) on the flow stress and ductility in tension of a high carbon steel wire were determined at 204°, 427° and 649°C. Electropulsing (100 pulses per second) with an effective current density of 100-200 A/cm2 gave a 10% enhancement in the uniform elongation of the wire at 204°C, but had no effect at 427°C and 649°C. In contrast, continuous DC either had no significant effect on the ductility or gave a decrease. The electropulsing per se decreased the flow stress only slightly at 204° and 427°C, but gave a significant decrease at 649°C. Continuous DC increased the flow stress at all three temperatures. The present results along with those by others suggest that the enhanced ductility by electropulsing and the reduction in flow stress may be further increased by raising the effective current density through increases in either the pulsing frequency, maximum current density of each pulse or pulse duration. This could conceivably increase the reduction per pass during wire drawing or the number of passes between anneals.

Jan 1, 2001

By Roberto Parreiras Tavares, Frederico da Costa Fernandes, Guilherme Antonio Defendi, Vangleik Ferreira da Cruz, Júlio César de Sousa Pena

"Near-net-shape casting is an important area of research in the iron and steel industry today. Among the near-net-shape casting processes, the single-belt caster seems to be the most promising, since it is the only one that can achieve levels of productivity similar to those obtained with conventional continuous casting machines. One of the most important aspects in the single-belt casting is the feeding system used to deliver liquid metal over the belt. This system determines the velocity distribution and the levels of turbulence of the liquid metal and affects the quality of the strips. In the present work, a metal delivery system having a simple geometry was proposed. Using the CFD code CFX 5.6, a mathematical model to simulate three-dimensional turbulent fluid flow and heat transfer in that system has been developed. This model was used to analyze different configurations of the metal delivery system and the free surface shape of the fluid was also determined. A physical model of the feeding system was built and used to validate the predictions of the mathematical model. The fluid flow calculations have been validated by dye injection experiments and laser doppler anemometry. Measurements of the free surface levels have also been performed. These experiments provided supporting evidence for the predictions of the mathematical model.IntroductionTo maintain its competitiveness in the present market, the metallurgical sector, particularly the steelmaking companies, are developing new techniques of production. Some of these new processes are focussed on the strip casting technologies. Among these technologies, the SingleBelt process is considered the most interesting option, reducing the number of rolling steps and, consequently, the final cost of the product, especially the part associated to the energy consumption (fuel and/or electric energy). This process can also reach levels of productivity that can not be matched by other strip casting methods(1). One of the most important aspects concerning these new processes is related to the liquid metal delivery system. This system can have a significant effect on the final quality of the strips, since it determines the velocity distribution and the levels of turbulence of the liquid metal."

Jan 1, 2004

By Jin-yan TIE, Ke-xin JIAO, Qian Li, Hai-bin ZUO, Jian-Liang Zhang, Meng SHEN

This paper designs three factors such as temperature, pH, conductivity and three levels of orthogonal test. Temperature is a significant factor. However PH and conductivity are not significant through poor analysis. Further research is conducted on the temperature. Temperature stability is 50 . Suitable water velocity is 2.3m/s, which is calculated based on the largest part of the heat flux intensity and the corresponding water temperature should be controlled with 1.5. Meanwhile, water velocity increased has little effect on the heat transfer capabilities.

Jan 1, 2015

By Xue Ping

Sm2Fe17 alloy is an important precursor for the preparation of Sm2Fe17Nx magnet, which possesses a higher Curie temperature, larger anisotropy field, better resistance to oxidation and thermal stability. In this paper, the wet chemical co-precipitation was developed for synthesis of the Sm-Fe alloy oxide precursor. Based on the principles of simultaneous equilibrium and mass balance, a series of thermodynamic equilibrium equations of Sm(III)-Fe(II)-NH3-C2O4 2--H2O system at ambient temperature were deduced theoretically and the thermodynamic diagrams of lg[M2+]T (M=Sm, Fe) versus pH at different solution compositions were drawn. Then, the experiments were done to address the various effects on the wet chemical process, including solution pH value, reactant concentration, reaction temperature and aging time, etc. It is found that by precise control of the process, the Sm-Fe alloy oxide precursor was synthesized with fine crystallization and special size &size distribution.

Jan 1, 2008

By G. Gomathi, K. Asokan, K. Subramanian

An electrochemical reactor with anode and cathode chambers separated by a composite perfluoro polymer cation exchange membrane was designed, fabricated and used for the reduction of dissolved carbon dioxide under ambient conditions to formate. The flow reactor enhanced the mass transfer of carbon dioxide compared to the batch reactor. Experiments were conducted using two different perfluoro polymer membranes - Nafion 961. Efficacy of CO2 reduction on various cathode materials (Cd, Pb, Sn and Zn plated stainless steel woven mesh) were determined. Optimum values of flow rate and current density were evaluated for the energy efficient formation of formate in aqueous KHCO3 (pH 7.5-8.5) buffer solutions.

Jan 1, 2008

By Chikabumi Yamauchi, Masami Tashiro, Toshiharu Fujisawa, Hiroyuki Snano

"Rare earth metals usually contain large amount of oxygen because of their reactiveness, and therefore oxygen removal is one of the major problems on the purification of rare earth metals. In the present research work, halide flux treatment at high temperature under inert gas atmosphere was applied to the oxygen removal from neodymium. NdF3 was used as a halide flux. Deoxidation reaction and its mechanism were discussed based on the experimental results. Halide flux treatment is very effective for oxygen removal from rare earth metals.IntroductionSolid Sate Electrotransport (SSE) process has been successfully applied for the elimination of interstitial gaseous impurities from chemically active metals[l]-[5]. However, to achieve a higher effectiveness of the SSE process, it is required a very low initial impurity content in the metal. In case of rare earth metals, it is known that they usually contain large amount of oxygen that should be lowered as much as possible before applying the SSE process. In addition, if effective oxygen removal is achieved by simple process, it is significant also from the industrial viewpoint. In the present work, the application of a halide flux treatment is investigated to remove oxygen from neodymium by using NdF3 as a flux. At first, deoxidation reaction and its mechanism were discussed based on the phase diagram of the Nd-NdF3-Ndp3 quasi-ternary system. Based on the results, oxygen content in deoxidized neodymium was calculated theoretically and it was verified by deoxidation experiments."

Jan 1, 1998

By Jilai Xue, Jun Zhu, GermainKouma Ndong, Luxing Feng

High-temperature corrosion behaviors of Fe-Ni-Cr alloy as inert anodes for aluminum electrolysis have been studied. The effect of anodic overpotential on layer growth of anodic surface is specially considered. The corrosion layers on the anodes tested were analyzed using XRD and SEM-EDS to provide a fundamental understanding of the layers growth at metallic anode surface. The dissolution of the scale layers on the metal anode occurred with low overpotential, while AlxM3-xO4 spinel phase within the scale layers was found with an increased overpotential. A mixture of multiple MyO layers existed on the anode substrate. The results may be useful for understanding and controlling the corrosion behaviors of Fe-Ni-Cr anode for potential application in aluminum electrolysis.

Jan 1, 2015

By Mitsuhiro Ito

"To allow various wastes containing high levels of chlorine to be used as alternative raw materials for Portland cement, two practical methods of chlorine removal were developed. In the first method, chlorine is extracted from the wastes during the cement manufacturing process. In the second, ash-dust waste with high chlorine content is first washed and then dehydrated to cake before being introduced to the cement manufacturing process. This cake can be used as an alternative for some cement raw materials. By combining the two methods, various wastes previously considered unsuitable for recycling due to their chlorine content can often now be used in cement manufacturing plants. As such, these methods represent a major contribution to environmental protection as well as a solution to problems relating to the diffusion of heavy metals and dioxins from cement plants.1. IntroductionWaste generation levels have risen rapidly in recent years. in both the consumer and industrial sectors and today, the need for effective, efficient waste management is one of the most pressing and serious problem of today's society.The Japanese cement industry has reacted to the increase in waste generation by using certain materials as alternative raw inputs or fuels for cement production, in an effort to contribute to society and conserve energy resources.These wastes often contain non-negligible levels of chlorine and heavy metals, however, both of which are unsuitable for cement production. Depending on the element content, Heavy metals have a particularly negative effect -on cement quality; in addition, they can be released into the environment. Chlorine, on the other hand, is contained in large amounts in incinerated ash from household wastes as well as in certain plastics. Both substances are considered impediments in cement-production, not only because they reduce the quality of the cement produced but also because they impair operating safety on cement production lines.To address this problem, two practical technologies have been established for separation and recovery of chlorine components during cement pre-processing and production. This paper introduces the application of these technologies with a special focus on incinerated ash from urban wastes, a representative form of waste material having notably high concentrations of chlorine, heavy metals, and dioxins. We also outline the technologies enabling this material to be used as an alternative input to cement production."

Jan 1, 2000

By T. A. Larssen

The efficiency in production of manganese ferroalloys is dependent on the gaseous reduction of the higher manganese oxides in the ores used as raw materials. The materials, descending in the furnace, will meet the furnace gas that contains significant amounts of CO(g) and reduce in subsequent steps, the last step being reduction of Mn3O4 to MnO. This step may to varying extent occur at temperatures exceeding 800 °C, i.e. in the active region of the Boudouard reaction. The gas reduction of Assmang and Comilog manganese ores were investigated in CO-CO2-atmosphere at temperatures up to 1000 °C. It was seen that decreasing ore size correlates to a lower reduction temperature and increasing reduction rate. Similar effect was observed with increasing CO-content in the gas atmosphere. Further, it was found that Comilog ore obtained a complete prereduction at 600 °C, whereas reduction of Assmang ore was not complete at 800 °C for the majority of the experiments.

By R. M. Westcott

A two-electrode, direct current, slag resistance furnace (SRF) has been constructed and operated to selectively reduce the zinc and lead contents of non-ferrous slags. The experimental SRF is equipped with multiple methods of gas/solids injection for both mixing and reaction. A computer is used to position the electrodes and for data acquisition. A geometric factor correlation was previously developed at Columbia University for calculating the electrical resistance on the basis of furnace geometry and slag conductivity. The experimental SRF was used to test this correlation.

Jan 1, 1994

By William A. Hockings

Methods for the measurement of liberation of finely ground iron ores are described. The general method consists of separating a sample of the ground ore into a number of size fractions, followed by measuring the liberation of each fraction. The size separation has been done using electro-formed screens of 20-, 10-and 5-micrometer apertures, and also by air elutriation. Liberation (i.e., the distribution of compositions of individual particles) has been measured by optical microscopy. A computer pro-gram was used to adjust the raw count data so that it agrees with the chemical analyses of the size fractions. Various ways of presenting the results are given, and Some applications of the results to flotation processing are discussed.

Jan 1, 1981

By Philip Thompson

"Carefully planned laboratory test programs provide valuable data regarding the amenability of low grade gold ores to heap leaching. The most common laboratory test is the column leach test. The overwhelming problem associated with this type of test is the limit on the test column height. Most laboratories use a three (3) meter (10 foot) high column as a standard test due to building ceiling limitations, sample size limitations, etc. This paper presents a case study in which an ore sample was tested in a 1.5 meter, a three meter, and a six meter high column to determine the effect of column height on the test results. Other important factors such as sample preparation protocol, preliminary bottle roll testing to determine appropriate crush size, column diameter requirements, and leach solution analyses, are also discussed.IntroductionColumn leach testing has been used for years by many laboratories to determine the amenability of low grade precious metals bearing ores to heap leaching. However, the test work can be compromised by poor planning, misinterpretation of results, and extrapolation of data beyond the reasonable boundaries of the experiment. Preliminary test work should be performed prior to column testing. This preliminary work provides valuable information regarding the response of the ore to cyanidation and aids in the design of the column tests.The sample should be screened into various size fractions prior to testing. The fractions are assayed to determine the gold content of each size fraction and of the overall sample. The most valuable preliminary test is the bottle roll cyanidation test which is usually performed on five kilograms of coarse sample in a large rolling bottle which can accept material up to 50 millimeters top size. The residue from this test is screened at different sizes to determine the distribution of unleached gold in the residue. Comparison of the gold distribution in the leach residue with the distribution of gold in the feed at the same size intervals provides an indication of the appropriate crush size for the sample. The overall gold extraction from the sample at the crush size tested is also determined from these data. Lime and cyanide requirements can also be estimated from this test. The viscosity of the bottle roll pulp and the size distribution of the feed and leach residue can also suggest whether agglomeration of the ore will be required prior to column testing. Ores which contain significant amounts of clays (greater than 5 percent) will generally require agglomeration to prevent plugging of the test column."

Jan 1, 1997

By R. Padilla, M. C. Ruiz, R. Villa

"Bismuth is an impurity in copper minerals where it occurs mainly as the mineral bismuthinite (Bi2S3). In smelting of copper minerals, most of the bismuth reports to the white metal, as a result, a substantial amount of bismuth accompanies the copper to the electrorefined cathodes. Thus understanding the behavior of Bi2S3 at high temperatures is crucial to eliminate bismuth before electrorefining. In this paper, some experimental data on the decomposition/volatilization of bismuthinite in nitrogen- oxygen atmospheres is discussed. The results indicated that in nitrogen atmosphere, bismuth volatilization occurs through a fast decomposition of bismuthinite to metallic bismuth and sulfur with subsequent volatilization of bismuth in the range 850-1100 °C. Similarly, in the presence of oxygen, bismuthinite decomposes to bismuth too, followed by oxidation to the non-volatile bismuth trioxide at temperatures higher than 750 °C. Both, temperature and partial pressure of oxygen affect significantly the bismuth volatilization and the oxidation rates.IntroductionCopper sulfide minerals are the major source for the production of metallic copper by pyrometallurgical processes, which are the dominant processes in the production of copper by selectively oxidizing the sulfide sulfur to SO2 and the accompanying iron in the concentrates to iron oxide, which can be conveniently removed as a stable slag.Generally, copper concentrates contain some deleterious minor elements such as arsenic, antimony, bismuth and lead, which are present as sulfides. These elements depending on their concentration may originate problems in the copper smelting processes and they can ultimately lead to a final copper product with unacceptable high levels of impurities.During the treatment of these copper concentrates by smelting, the impurities generally distribute themselves in the condensed and gas phases and they are eliminated mainly through the gas phase [1-3]. Thus, smelter off gases contains substantial amounts of volatilized impurity elements. For example, in the case of bismuth, the estimated distribution of bismuth in flash furnace smelting [2] was 15 % in the matte, 5 % in the slag and 80 % in the gas phase, and recently, for Outokumpu flash smelting Davenport [3] reported the distribution of bismuth as 30-75% in matte, 5-30% in slag and 15 -65 % in the off gas."

Jan 1, 2011